N-3烷基取代嘧啶及其衍生物的合成

在室温条件下,经过三步反应,合成了一系列N-3烷基取代的嘧啶类化合物.该方法具有条件温和、操作简便、反应时间短、产率高等特点.目标产物经过了1HNMR,13C NMR和MS确证表征.     

Poly(vinyl alcohol)/melamine phosphate composites prepared through thermal processing: thermal stability and flame retardancy

Poly(vinyl alcohol)/melamine phosphate composites (PVA/MP) as a novel halogen‐free, flame‐retardant foam matrix were prepared through thermal processing, and then their thermal stability and flame retardancy were investigated by thermo‐gravimetric analysis, micro‐scale combustion calorimeter, cone calorimeter, vertical burning test, and limiting oxygen index (LOI) test. It was found that the thermal stability and combustion properties of the PVA/MP composites could be influenced by the addition of MP. Compared with the control PVA sample (B‐PVA), in the PVA/MP (75/25) composites, the temperature at 5% mass loss (T_5%) decreased about 10°C, the residual chars at 600°C increased by nearly 27%, the temperature at the maximum peak heat release rate (T_P) shifted from 292°C to 452°C, and the total heat released and the heat release capacity (HRC) decreased by 28% and 14%, respectively. Moreover, the PVA/MP composites could reach LOI value up to 35% and UL94 classification V‐0, showing good flame retardancy. At the same time, both Fourier transform infrared and X‐ray photoelectron spectroscopy spectra of the residual chars from the PVA/MP composites demonstrated that the catalytic effect of MP on the dehydration and decarboxylation reactions of PVA, and the chemical reactivity of MP during the chars‐forming reactions could be used to account for the changed thermal stability and flame retardancy of the PVA/MP composites. Copyright © 2012 John Wiley & Sons, Ltd.     

Effect of cholesteric liquid crystalline elastomer with binaphthalene crosslinkings on thermal and optical properties of a liquid crystal that show smectic A‐cholesteric phase transition

A side‐chain polysiloxane cholesteric liquid crystalline elastomer (ChLCE) with binaphthalene derivate as crosslinkings and cholesterol derivate as liquid crystalline monomers was designed and synthesized. A binaphthyl chiral dopant (CD) was synthesized as well. The chemical structures and liquid crystalline properties of the ChLCE and the CD were characterized by Fourier transform infrared spectroscopy, proton nuclear magnetic resonance spectroscopy, element analyses, differential scanning calorimetry and polarizing optical microscopy measurements. The helical twisting power of the ChLCE exhibited a turning point with changing temperature and was smaller than that of the CD. In addition, the effect of the ChLCE on phase transition temperatures and thermal‐optical properties of a liquid crystal that show smectic A (SmA)‐cholesteric (Ch) phase transition was studied. Worthily, the testing of the reflection wavelength with changing temperature suggested that the adding of the ChLCE in liquid crystals that show SmA‐Ch phase transition can expedite their SmA‐Ch transition. In addition, the network structure of the ChLCE may play a significant role in the accelerating of the transition. These properties provided theoretical and experimental foundations for applying ChLCE in thermally sensitive liquid crystal devices requiring fast response, such as thermally controllable windows, materials and displays. Copyright © 2012 John Wiley & Sons, Ltd.     

Fluorinated Porous Poly(spirobifluorene) Via Direct C‒H Arylation: Characterization,Porosity, and Gas Uptake

Considering intrinsic properties of conjugated polyfluorenes and special functions of porous polymers, synthesis of fluorinated porous poly(spirobifluorene) via direct C?H arylation polycondensation is explored. Owing to the contorted structure and cross-linking nature, the obtained polymer FPSBF shows permanent porosities with Brunauer–Emmett–Teller specific surface area up to 700 m² g^?1 and exhibits a narrow pore size distribution with the dominant pore size at about 0.63 nm, which is more suitable for adsorption of small gas molecules. Based on the measured gas physisorption isotherms with pressure up to 1.13 bar, the obtained polymer shows good uptaking capacities for hydrogen (1.30 wt% at 1.0 bar and 77 K) and methane (4.80 wt% 1.0 bar and 273 K). Moreover, FPSBF has significant adsorption selectivity for CH₄ against N₂ and the estimated ideal adsorption selectivity ratio is up to 30/1 at 1.0 bar and 273 K, which makes the material possess potential application in gas separation.     

Demulsification of Solids‐Stabilized Emulsions Under Microwave Radiation

Experimental data are presented to show the influence of solid particles on demulsification. It was found that the solid particles could effectively resist demulsification. Compared with conventional heating, microwave radiation can enhance the demulsification rate by an order of magnitude and increase the demulsification effectiveness. The demulsification effectiveness of the emulsions stabilized by graphite powder can reach 82%–89% in a very short time under microwave radiation, whilst that of the emulsions stabilized by barium sulfate can attain 100% under similar conditions.     

Anti‐static Agent Containing Zinc Oxide and its Modification for PA6 Fiber

A new anti‐static agent was synthesized from zinc oxide‐adipic acid‐polyethylene glycol and caprolactam by three‐step reactions. The antistatic agent (called poly(ether ester amide zinc oxide) or PEEAZ) was analyzed by IR and DSC. The results showed that zinc oxide existed in the main chain of PEEAZ. The glass temperature and melt temperature of poly(ether ester amide zinc oxide) (referred to as PEEAZ in the following) decreased with increasing poly(ether ester zinc oxide) increasing in PEEAZ. Antistatic PA6 fiber was obtained by adding PEEAZ 2–8% (wt/wt) to PA6 during blend spinning. The specific resistance and the static half‐value period of PA6 fiber was less than 10⁹Ω · cm and 60 sec, respectively. Excellent antistatic property remained after being washed 30 times.     

Preparation and Characterization of Polyhydroxyurethane/Attapulgite Nanocomposites Via In-Situ Surface-Initiated Polymerization

The polyhydroxyurethane/attapulgite nanocomposites (PHU/ATP) were prepared by in-situ surface-initiated polymerization of a five-membered cyclic carbonate, 2, 2-bis [p-(1, 3-dioxolan-2-one-4-yl-methoxy) phenyl] propane (B5CC) and hexamethylene diamine, from the surface of the aminopropyl attapulgite nanoparticles (APATP) for the first time. The chemical grafting of the polymer on the surface of ATP was confirmed by FTIR and the morphology of the attapulgite nanoparticles in the nanocomposites was examined by TEM. The thermal stabilities of the polyhydroxyurethane (PHU) and the polyhydroxyurethane/attapulgite nanocomposites (PHU/ATP) were compared with thermogravimetric analysis (TGA).The %G of the attapulgite nanoparticles was also calculated from the results of TGA after the free polyhydroxyurethane was washed off.     

Flammability and Thermal Oxidative Degradation Kinetics of Magnesium Hydroxide and Expandable Graphite Flame Retarded Polypropylene Composites

The flammability and the thermal oxidative degradation kinetics of expandable graphite (EG) with magnesium hydroxide (MH) in flame‐retardant polypropylene (PP) composites were studied by limiting oxygen index (LOI), UL‐94 test, and thermogravimetric analysis (TGA). The results show that EG is a good synergist for improving the flame retardancy of PP/MH composite and the effect is enhanced with decreasing EG particle size. The Kissinger method and Flynn‐Wall‐Ozawa method were used to determine the apparent activation energy (E) for degradation of PP and flame retarded PP composites. The data obtained from the TGA curve indicate that EG markedly increases the thermal degradation temperature of PP/MH composites and improves the thermal stability of the composites. The kinetic results show that the values of E for degradation of flame retarded PP composites is much higher than that of neat PP, especially PP/MH composites with suitable amount of EG, which indicates that the flame retardants used in this work have a great effect on the mechanisms of pyrolysis and combustion of PP.