Preparation of Highly Stable and Photoluminescent Cadmium-Free InP/GaP/ZnS Core/Shell Quantum Dots and Application to Quantitative Immunoassay

Indium phosphide (InP) quantum dots (QDs) are ideal substitutes for widely used cadmium-based QDs and have great application prospects in biological fields due to their environmentally benign properties and human safety. However, the synthesis of InP core/shell QDs with biocompatibility, high quantum yield (QY), uniform particle size, and high stability is still a challenging subject. Herein, high quality (QY up to 72%) thick shell InP/GaP/ZnS core/shell QDs (12.8 ± 1.4 nm) are synthesized using multiple injections of shell precursor and extension of shell growth time, with GaP serving as the intermediate layer and 1-octanethiol acting as the new S source. The thick shell InP/GaP/ZnS core/shell QDs still keep high QY and photostability after transfer into water. InP/GaP/ZnS core/shell QDs as fluorescence labels to establish QD-based fluorescence-linked immunosorbent assay (QD-FLISA) for quantitative detection of C-reactive protein (CRP), and a calibration curve is established between fluorescence intensity and CRP concentrations (range: 1–800 ng mL⁻¹, correlation coefficient: R² = 0.9992). The limit of detection is 2.9 ng mL⁻¹, which increases twofold compared to previously reported cadmium-free QD-based immunoassays. Thus, InP/GaP/ZnS core/shell QDs as a great promise fluorescence labeling material, provide a new route for cadmium-free sensitive and specific immunoassays in biomedical fields.     

Nanocomposite hydrogel consisting of Na‐montmorillonite with enhanced mechanical properties

A new kind of nanocomposite (NC) hydrogel with Na‐montmorillonite (MMT) is presented in this article. The NC hydrogels were synthesized by free radical copolymerization of acrylamide and (3‐acrylamidopropyl) trimethylammonium chloride (ATC) in the presence of MMT and N,N′‐methylene‐bis‐acrylamide used as chemical cross‐linker. Due to the cation‐exchange reaction between MMT and ATC (cationic monomer) during the synthesis of NC hydrogels, MMT platelets were considered chemical “plane” cross‐linkers, different from “point” cross‐linkers. With increasing amount of MMT, the crosslinking degree enhanced, causing a decrease of the swelling degree at equilibrium. Investigations of mechanical properties indicated that NC hydrogels exhibited enhanced strength and toughness, which resulted from chemical interaction between exfoliated MMT platelets and polymer chains in hydrogels. Dynamic shear measurements showed that both storage modulus and loss modulus increased with increasing MMT content. The idea described here provided a new route to prepare hydrogels with high mechanical properties by using alternative natural Na‐MMT. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1020–1026     

不同杂环取代(E)-β-Farnesene类似物的合成及生物活性研究

为了寻求新型蚜虫控制剂,以蚜虫报警信息素(E)-β-farnesene(EBF)为先导,引入不同类型的杂环取代EBF结构中不稳定的共轭双键,设计合成了一系列不同杂环取代的EBF类似物.所有化合物结构均通过1H NMR、13C NMR、IR及HRMS确证.对化合物进行了生物活性测试及初步构效关系分析.结果表明,所有化合物均对桃蚜和大豆蚜表现出一定的生物活性,部分化合物的杀虫活性优于先导EBF,酯基的引入则对驱避活性有利.     

Preparation and gas sensing activity of La and Y co-doped titania nanoparticles

Journal of Sol-Gel Science and Technology - A novel gas sensing material, La–Y co-doped TiO2 nanoparticles, was synthesized by sol–gel method and applied to detect organic pollutants...     

烧结温度对Cao.9(NaCe)0.05Bi2Nb2O9无铅压电陶瓷性能的影响

采用传统固相反应法制备了Ca0.9(NaCe)0.05Bi2 Nb2 O9铋层状无铅压电陶瓷.采用XRD、SEM、EDS及相关电学性能测试系统表征了样品的晶体结构、断面形貌、元素组成以及介电、压电、铁电等性能,探究不同烧结温度对于陶瓷性能的影响.结果表明:当烧结温度为1150℃时,样品的晶体结构单一均匀,呈现片层状结构,致密性较好,压电常数高达17 pC/N,介电损耗仅为0.42;,居里温度为908℃,并且具有很好的温度稳定性,说明固相反应法制备的Ca0.9(NaCe)0.05Bi2Nb2O9压电陶瓷最佳烧结温度为1150℃.