Anti‐static Agent Containing Zinc Oxide and its Modification for PA6 Fiber

A new anti‐static agent was synthesized from zinc oxide‐adipic acid‐polyethylene glycol and caprolactam by three‐step reactions. The antistatic agent (called poly(ether ester amide zinc oxide) or PEEAZ) was analyzed by IR and DSC. The results showed that zinc oxide existed in the main chain of PEEAZ. The glass temperature and melt temperature of poly(ether ester amide zinc oxide) (referred to as PEEAZ in the following) decreased with increasing poly(ether ester zinc oxide) increasing in PEEAZ. Antistatic PA6 fiber was obtained by adding PEEAZ 2–8% (wt/wt) to PA6 during blend spinning. The specific resistance and the static half‐value period of PA6 fiber was less than 10⁹Ω · cm and 60 sec, respectively. Excellent antistatic property remained after being washed 30 times.     

Preparation and Characterization of Polyhydroxyurethane/Attapulgite Nanocomposites Via In-Situ Surface-Initiated Polymerization

The polyhydroxyurethane/attapulgite nanocomposites (PHU/ATP) were prepared by in-situ surface-initiated polymerization of a five-membered cyclic carbonate, 2, 2-bis [p-(1, 3-dioxolan-2-one-4-yl-methoxy) phenyl] propane (B5CC) and hexamethylene diamine, from the surface of the aminopropyl attapulgite nanoparticles (APATP) for the first time. The chemical grafting of the polymer on the surface of ATP was confirmed by FTIR and the morphology of the attapulgite nanoparticles in the nanocomposites was examined by TEM. The thermal stabilities of the polyhydroxyurethane (PHU) and the polyhydroxyurethane/attapulgite nanocomposites (PHU/ATP) were compared with thermogravimetric analysis (TGA).The %G of the attapulgite nanoparticles was also calculated from the results of TGA after the free polyhydroxyurethane was washed off.     

Flammability and Thermal Oxidative Degradation Kinetics of Magnesium Hydroxide and Expandable Graphite Flame Retarded Polypropylene Composites

The flammability and the thermal oxidative degradation kinetics of expandable graphite (EG) with magnesium hydroxide (MH) in flame‐retardant polypropylene (PP) composites were studied by limiting oxygen index (LOI), UL‐94 test, and thermogravimetric analysis (TGA). The results show that EG is a good synergist for improving the flame retardancy of PP/MH composite and the effect is enhanced with decreasing EG particle size. The Kissinger method and Flynn‐Wall‐Ozawa method were used to determine the apparent activation energy (E) for degradation of PP and flame retarded PP composites. The data obtained from the TGA curve indicate that EG markedly increases the thermal degradation temperature of PP/MH composites and improves the thermal stability of the composites. The kinetic results show that the values of E for degradation of flame retarded PP composites is much higher than that of neat PP, especially PP/MH composites with suitable amount of EG, which indicates that the flame retardants used in this work have a great effect on the mechanisms of pyrolysis and combustion of PP.     

Highly sensitive detection of mercury (II) in aqueous media by tetraphenylporphyrin with a metal ion receptor

We provide a highly sensitive and selective assay to detect Hg²⁺ in aqueous solutions using a novel β-functionalised porphyrin-based chemosensor 5 at room temperature. The binding properties of the chemosensor 5 for cations were examined by UV–vis spectroscopy and ¹H NMR. The results indicate that a 1:1 stoichiometric complex is formed between chemosensor 5 and mercury (II) ion. The recognition mechanism between chemosensor 5 and metal ion was discussed based on their absorbance changes and the chemical shift changes when they interact with each other. Control experiments revealed that chemosensor 5 has a selective response to mercury (II) ion compared with other metal ions.     

Synthesis of Calix[4]arene Derivatives Containing a Nucleobase and their Interaction with Complementary Nucleosides at the Air–Water Interface

Amphiphilic calix[4]arene derivatives with a nucleobase on the lower rim have been synthesized in good yields by the condensation of calix[4]arenediamine {5,11,17,23-tetra-tert-butyl-25,27-bis(2-aminoethoxy)-26,28-dihydroxycalix[4]arene} with uracilo-N-acetic acid, thymino-N-acetic acid and adenino-N-propionic acid in the presence of CDI in DMF. Monolayers of the amphiphilic calix[4]arene-nucleobase derivatives on the surface of pure water, the aqueous subphases containing complementary nucleosides, were studied by film balance measurement and relaxation experiments. LB films deposited from all subphases were investigated by UV spectra and FT-IR spectroscopy. All the results indicate that the interaction between the nucleobases in the headgroup of amphiphilic p-tert-butylcalix[4]arene derivatives and the complementary nucleosides in the subphase takes place through multiple hydrogen bonding and the nucleosides can be transferred to solid substrates along with their monolayers.     

Hydrothermal synthesis, crystal structure, and photoluminescence of a new 2D cadmium(II) complex: {Cd(C8H5O3Cl2)2(C10H8N2)} n

One new cadmium coordination polymer, [Cd(2,4-Dcp)₂(4,4-Bipy)] _n (I) (2,4-HDcp = 2,4-dichlorophenoxyacetic acid, 4,4′-Bipy = 4,4′-bipyridine) with 2D layer structure, has been prepared by the hydrothermal synthesis and characterized by elemental analysis, IR, TGA and single-crystal X-ray diffraction. Complex I crystallizes belong to monoclinic system and has C2/c space group. Each Cd²⁺ ion is six-coordinated and located at an octahedral geometry. The Cd²⁺ ions are linked by bidentate 2,4-Dcp groups into a linear chain in which the benzene rings of 2,4-Dcp ligands point alternately up and down. These chains are further connected into a sandwich-like layer though 4,4′-Bipy ligands. Furthermore, the photoluminescence and life-time of I in the solid state have been studied.     

Preparation and characterization of an active catalyst

As an active catalyst to promote thermolysis of ammonium perchlorate (AP), potassium lead hexanitrocobaltate(II) complex (K₂Pb[Co(NO₂)₆]) was synthesized by the direct deposition method and inverse microemulsion method. Its submicron, size, cube morphology, and crystal structure were investigated by SEM, TEM, and XRD analysis, respectively. Thermal decomposition of K₂Pb[Co(NO₂)₆] was studied by the TG/DSC-IR online system and XRD analysis. The catalyst was decomposed at about 300 °C; its gaseous products were NO₂, NO, and N₂O and its solid products were Pb₃O₄, Co₃O₄, PbO, CoO, and KNO₂. Because thermal decomposition of the catalyst was synchronous with low temperature decomposition of AP, thermolysis of AP was promoted remarkably. In particular, the gaseous products (NO _x ) could directly oxidize the absorbed NH₃. As a result, compared to the data of pure AP, the integral heat of AP added 3.0 wt% of the catalyst multiplied by 280 %, the maximum rate of heat release increased by 634 %. The decomposition of catalyzed AP ended at about 317 °C, at which only less than 30 % of pure AP decomposed.     

Multi-walled carbon nanotubes coated by multi-layer silica for improving thermal conductivity of polymer composites

Silica has been non-covalently coated on multi-walled carbon nanotubes (MWCNTs) using the sol–gel chemistry, where tetraethoxy silane (TEOS) was used to form an inorganic silica layer immediately next to surface of MWCNTs and octyl triethoxy silane was coated over the TEOS. Transmission electron microscopy (TEM) measurements show that the diameter of MWCNTs increases with increasing the number of coating layer, indicating that the silica has been coated on MWCNTs. Quantitative analysis from thermogravimetric analysis (TG) also indicates that the inorganic and organic silica has been successfully coated on MWCNTs. Further, quantitative analysis found that the amount of silica measured by TG agrees well with the increase of thickness of coated MWCNTs obtained from TEM, indicating that little or no free silica exists in the system. The thermal conductivity of epoxy/MWCNTs composite was studied and the results show that the thermal conductivity of the composite is improved by coating MWCNTs in this manner and increases with increasing the number of coatings.     

Magnesium boride sintered as high-energy fuel

Boron was chosen as fuel owing to its excellent thermodynamic values for combustion. The difficulty of the boron in combustion is the formation of a surface oxide layer, which postpones the combustion process, reducing the performance of the rocket engine. In this paper, magnesium boride was sintered as high-energy fuel as a substitute for boron. The combustion heat and efficiency of magnesium boride and boron were determined using oxygen bomb calorimeter. The combustion characteristics of magnesium boride were investigated by thermal analysis, chemical analysis, XRD, and EDS. Results show that the combustion performance of magnesium boride are better than that of amorphous boron in oxygenated environments. The evaporation of magnesium in magnesium boride combustion process prevent the formation of a closed oxide layer, leading to higher combustion efficiency.