Barium(II)–2,4‐dinitrophenolate–18‐crown‐6 at 183 K

The title compound, bis(2,4‐dinitrophenolato‐κ²O,O′)(1,4,7,10,13,16‐hexaoxadecane‐κ⁶O)barium(II), [Ba(C₆H₃N₂O₅)₂(C₁₂H₂₄O₆)], is a 1:1 complex of barium(II)–2,4‐di­nitro­phenolate and 1,4,7,10,13,16‐hexaoxa­cyclo­octa­decane (18‐crown‐6). Its structure is located on a crystallographic inversion centre. The temperature dependence of the crystal structure has been studied. The monoclinic β angle of the P2₁/­n space group increases with increasing temperature. The packing structure of the complex is stabilized by intermolecular C—H?O interactions.     

Behaviors of the positive temperature coefficient of resistance of poly(styrene‐co‐n‐butylacrylate) filled with Ni‐plated core‐shell polymeric particles

Conductive composite films of poly(styrene‐co‐n‐butylacrylate) copolymers filled with low‐density, Ni‐plated core‐shell polymeric particles were prepared and their behaviors of positive temperature coefficient of resistance (PTCR) were investigated. When the conductive fillers in the composite film were loaded beyond the critical volume, 10 up to 25 vol %, composite films exhibited a unique electrical resistant transition behavior, which the electrical resistance rapidly increased by several orders of magnitude at the critical temperature. The PTCR transition temperature, in general, occurred before the glass transition temperature of polymer matrix. Further increased the conductive filler loading to 30 vol %, the overpacked conduction paths were formed in the entire composite and the PTCR effects became blurred. While the composite film treated with thermal cycle several times from room temperature up to 120 °C, the electrical resistivity increased accompanied with the shift of the PTCR transition to lower temperature. The reason might have been caused by the formed interfacial cracks within the composite film. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 322–329, 2007     

Singlewall carbon nanotubes covered with polystyrene nanoparticles by in‐situ miniemulsion polymerization

This work is to make carbon nanotubes dispersible in both water and organic solvents without oxidation and cutting nanotube threads. Polystyrene‐singlewall carbon nanotube (PS‐SWNT) composites were prepared with three different methods: miniemulsion polymerization, conventional emulsion polymerization, and mixing SWNT with PS latex. The two factors, crosslinking and surface coverage of PS are important factors for the mechanical and electrical properties, including dispersion states of SWNT in various solvents. The PS‐SWNT composite prepared via a conventional emulsion polymerization showed SWNT bundles entirely covered with PS, whereas the PS‐SWNT composite prepared via a miniemulsion polymerization showed SWNT partially covered with crosslinked PS nanoparticles. The method of mixing SWNTs with PS latex did not show the well dispersed state of carbon nanotubes because PS was not crosslinked and was dissolved in a solvent, and nanotubes separated from PS precipitated. So the PS nanoparticle‐SWNT composite had lower electrical resistance, and higher mechanical strength than the other composites made by the latter two methods. As the amount of SWNT increases, the bare surface area of SWNT increases and the electrical conductivity increases in the composite made by the miniemulsion polymerization. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 573–584, 2006     

Highly soluble and optically transparent poly (ether imide)s based on 2,6‐ or 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and aromatic bis(ether amine)s bearing trifluoromethyl groups

Two series of novel fluorinated poly(ether imide)s (coded IIIA and IIIB ) were prepared from 2,6‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride, respectively, with various trifluoromethyl‐substituted aromatic bis(ether amine)s by a standard two‐step process with thermal or chemical imidization of the poly(amic acid) precursors. These fluorinated poly(ether imide)s showed good solubility in many organic solvents and could be solution‐cast into transparent, flexible, and tough films. These films were nearly colorless, with an ultraviolet–visible absorption edge of 364–386 nm. They also showed good thermal stability with glass‐transition temperatures of 221–298 °C, 10% weight loss temperatures in excess of 489 °C, and char yields at 800 °C in nitrogen greater than 50%. The 2,7‐substituted IIIB series also showed better solubility and higher transparency than the isomeric 2,6‐substituted IIIA series. In comparison with nonfluorinated poly (ether imide)s, the fluorinated IIIA and IIIB series showed better solubility, higher transparency, and lower dielectric constants and water absorption. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5909–5922, 2006     

A cobalt(III)-salen complex with an axial substituent in the diamine backbone: stereoselective recognition of amino alcohols

A cobalt(III)-salen complex (3) with an axial substituent on the diamine backbone has been synthesized. Crystal structure reveals that the axial substituent (p-nitrophenyl group) is positioned in close proximity to the metal binding site. The stereoselectivity of the cobalt complex for binding amino alcohols increases with increasing steric bulk of the amino alcohol from alaninol (2.9) to valinol (6.2) and t-leucinol (36.0).