导电聚苯胺与磁性CoFe2O4纳米复合物的制备与表征

在利用HNO3酸化处理CoFe2O4磁性纳米粒子使其表面离子化、分散性得到改善的基础上, 采用原位聚合法制备了具有电磁功能的聚苯胺/CoFe2O4 (PANI/CoFe2O4)纳米复合物. 借助TEM, XRD, FT-IR, TG, 四探针电导率仪、VSM(振动样品磁强计)等分析手段研究了复合物的形貌、结构、热稳定性及电磁性能. 结果表明, 处理过的CoFe2O4磁性纳米粒子可形成分散均匀的PANI/CoFe2O4纳米复合物, CoFe2O4以25 nm左右的粒子分散于聚苯胺基体中; PANI与CoFe2O4之间存在化学键合作用, 正是这种作用使复合物热稳定性得以提高; 复合物同时具有导电性和磁性能, 且随CoFe2O4含量变化而变化.     

配位-氧化聚合-水热法制备聚苯胺/CoFe_2O_4纳米复合物及其微波吸收性能

采用"配位-氧化聚合-水热法"制备了本征态聚苯胺/CoFe2O4二元纳米复合物,再以磺基水杨酸掺杂获得聚苯胺/CoFe2O4电磁复合物.考察了反应物配比及掺杂酸浓度对产物电磁性能的影响.通过透射电子显微镜(TEM)、X射线衍射(XRD)、红外光谱(FTIR)及电磁测量等手段对聚苯胺/CoFe2O4的形貌、结构及性能进行了表征.结果表明,复合物呈现多级结构,其中CoFe2O4为立方体状,平均粒径小于20 nm.当CoFe2O4的质量分数为8.86%时,复合物的电导率约为0.43 S/cm;当聚苯胺/CoFe2O4复合物厚度为2 mm时,在16.01 GHz处最大反射损耗为-16.71 dB,小于-10 dB的带宽达4.68 GHz;而当聚苯胺/CoFe2O4复合物厚度为3.2 mm时,在9.23 GHz处最大反射损耗达-51.81 dB,小于-10 dB的带宽为3.69 GHz,表明具有良好的吸波性能.     

导电聚苯胺与磁性CoFe2O4纳米复合物的合成及其电磁性能

在利用HNO3处理CoFe2O4磁性纳米粒子使其表面离子化、分散性得到改善的基础上, 采用苯胺在其表面原位聚合, 制备了具有电磁功能的聚苯胺(PANI)/CoFe2O4纳米复合物. 借助TEM、XRD、FT-IR、四探针电导率仪和VSM(振动样品磁强计)等分析手段研究了复合物的形貌、结构及其电磁性能. 结果表明, CoFe2O4以25 nm左右的粒子分散于聚苯胺基体中, 被其完全包覆, CoFe2O4与PANI之间存在化学键合作用; 复合物同时具有电性能和磁性能, 其导电率随CoFe2O4含量增加而降低, 饱和磁化强度随之升高, 而矫顽力在所研究的范围内则先增大而后又减小, 且均高于CoFe2O4的矫顽力.     

导电聚苯胺与磁性CoFe2O4纳米复合物的合成及其电磁性能

在利用HNO3处理CoFe2O4磁性纳米粒子使其表面离子化、分散性得到改善的基础上,采用苯胺在其表面原位聚合,制备了具有电磁功能的聚苯胺(PANI)/CoFe2O4纳米复合物.借助TEM、XRD、FT-IR、四探针电导率仪和VSM(振动样品磁强计)等分析手段研究了复合物的形貌、结构及其电磁性能.结果表明,CoFe2O4以25 nm左右的粒子分散于聚苯胺基体中,被其完全包覆,CoFe2O4与PANI之间存在化学键合作用;复合物同时具有电性能和磁性能,其导电牢随CoFe2O4含量增加而降低,饱和磁化强度随之升高,而矫顽力在所研究的范围内则先增大而后又减小,且均高于CoFe2O4的矫顽力.     

纳米复合材料CoFe2O4/SiO2的制备和表征

采用溶胶-凝胶法制备了(CoFe2O4)x/(SiO2)1-x纳米复合材料. 利用TG/DTA, XRD和Mssbauer效应研究了热处理过程中干凝胶的变化及样品的结构、晶粒尺寸和磁性. 结果表明, 随着SiO2含量的增加, 样品中CoFe2O4的晶粒尺寸和内磁场逐渐变小, 并从磁有序状态转变为超顺磁状态.     

磁性TiO2/CoFe2O4纳米复合光催化材料的制备

以磁性CoFe2O4为核,采用改进的溶胶-凝胶法,制备了磁性TiO2/CoFe2O4纳米复合光催化材料.利用VSM(振动样品磁强计)技术对其磁性能进行了研究,结果表明:由该法所得的TiO2/CoFe2O4纳米复合光催化材料的饱和磁化强度虽稍弱于纯CoFe2O4纳米材料,但其矫顽力则优于CoFe2O4.TEM、XRD、UV-Vis等的结果表明,该纳米复合材料中的TiO2为锐钛矿结构;与TiO2相比,纳米复合材料对光的吸收拓展到了整个紫外-可见区,且吸收强度大大增强.对染料废水光催化降解的模拟研究表明,该复合材料在紫外光下,6 h可以使亚甲基蓝染料溶液的脱色率达95%,且重复使用3次时染料溶液的脱色率仍能保持在90%,明显优于纯TiO2.     

CoFe2-xMnxO4纳米晶薄膜的结构、磁性及磁光效应研究

为了改善磁光材料CoFe2O4的磁学特性,本研究利用改进的溶胶-凝胶法在单晶硅衬底上制备了不同掺杂量的CoFe2-xMnxO4(x=0～2,0)纳米晶薄膜系列样品。并对其结构、磁性及磁光效应进行了研究。结果表明,Mn^3+的掺入可以有效地控制和降低CoFe2O4的居里温度,并可显著地增强薄膜的磁光效应。     

CoFe2O4/CdS纳米复合物的制备、表征及其声催化降解有机染料污染物

在低温(200℃)下采用一步水热分解CoFe2O4纳米粒子表面的镉二硫代氨基甲酸酯配合物制备了磁性CoFe2O4/CdS纳米复合物,运用X射线衍射、红外光谱、扫描电镜、X射线能量散射谱、紫外-可见光谱、透射电镜(TEM)、N2吸附-脱附、X射线光电子能谱和振动样品磁强计对所制样品进行了表征.TEM结果表明,CoFe2O4/CdS纳米复合物由几乎均一的约20nm球形纳米粒子组成.光吸收谱显示该样品的带隙为2.24 eV,很适合用于声/光催化降解有机污染物.在紫外光照射下评价了CoFe2O4/CdS纳米复合物的声催化H2O2辅助降解甲基蓝、罗丹明B和甲基橙反应活性.结果表明,该纳米复合物对这3种染料均表现出很好的声催化活性(5-9 min内完全降解).另外,比较实验结果表明,CoFe2O4/CdS纳米复合物是一个比纯CdS更高效的声催化剂.因此,纳米复合是一种非常好的提高CdS声催化活性的手段.该CoFe2O4/CdS纳米复合物表现出的磁性使其很容易从反应混合物中分离出来而重复使用.     

低热固相反应制备一维棒状CoFe2O4及其电磁特性

以草酸、硝酸铁、硝酸钴为原料, 加入不同聚合度的PEG, 采用低热固相反应法制备出草酸铁和草酸钴的混合前驱物. 在不同的温度(25, 60, 70, 75 ℃), 混合前驱物分别恒温反应2 h, 然后经450 ℃灼烧. 对获得的粉体用XRD, SEM, 激光粒度仪表征后证明: 加入PEG400在75 ℃反应获得了长径比约为6～15范围, 具有立方晶系尖晶石结构的棒状CoFe2O4铁氧体粉末. 经测试电磁学性质发现, 与粒状的CoFe2O4相比, 棒状的CoFe2O4磁导率虚部在高频15～20 GHz范围增加了近1倍, 各向异性常数Ku则增加了近5倍. 预示一维棒状结构的CoFe2O4作为吸波材料具有良好应用前景.     

纳米复合材料CoFe2O4/CD-SBA-15的制备与表征

为制备在磁性环境下容易分离的新型吸附材料,制备了CoFe2O4/β-CD-SBA-15纳米复合材料,采用X射线衍射(XRD)、红外光谱(FT-IR)、透射电镜(TEM)、比表面测定仪(BET)和振动样品磁强计(VSM)对纳米复合材料的结构与性能进行表征.研究表明:CoFe2O4分散在β-CD-SBA-15的骨架和孔道里...     

磁电CoFe2O4/BaTiO3纳米管的溶胶-凝胶模板法合成和表征

用溶胶-凝胶模板法合成了CoFe2O4/BaTiO3(CFO/BTO)复合纳米管, 管的直径约为100、200和300 nm, 其长度约为100 μm. X射线衍射(XRD)和选区电子衍射(SAED)都显示复合纳米管中同时存在尖晶石相的CoFe2O4 (CFO)和钙钛矿相的BaTiO3(BTO), 进一步的透射电子显微镜(TEM)研究证实合成的纳米复合物具有明显的管状结构. 磁、电研究表明, 该复合纳米管的磁性与纯CFO纳米管的磁性相当; 而铁电性与纯BTO纳米管的铁电性相当.     

Adsorption of cobalt ferrite nanoparticles within layer-by-layer films: a kinetic study carried out using quartz crystal microbalance

The paper reports on the successful use of the quartz crystal microbalance technique to assess accurate kinetics and equilibrium parameters regarding the investigation of in situ adsorption of nanosized cobalt ferrite particles (CoFe(2)O(4)--10.5 nm-diameter) onto two different surfaces. Firstly, a single layer of nanoparticles was deposited onto the surface provided by the gold-coated quartz resonator functionalized with sodium 3-mercapto propanesulfonate (3-MPS). Secondly, the layer-by-layer (LbL) technique was used to build multilayers in which the CoFe(2)O(4) nanoparticle-based layer alternates with the sodium sulfonated polystyrene (PSS) layer. The adsorption experiments were conducted by modulating the number of adsorbed CoFe(2)O(4)/PSS bilayers (n) and/or by changing the CoFe(2)O(4) nanoparticle concentration while suspended as a stable colloidal dispersion. Adsorption of CoFe(2)O(4) nanoparticles onto the 3-MPS-functionalized surface follows perfectly a first order kinetic process in a wide range (two orders of magnitude) of nanoparticle concentrations. These data were used to assess the equilibrium constant and the adsorption free energy. Alternatively, the Langmuir adsorption constant was obtained while analyzing the isotherm data at the equilibrium. Adsorption of CoFe(2)O(4) nanoparticles while growing multilayers of CoFe(2)O(4)/PSS was conducted using colloidal suspensions with CoFe(2)O(4) concentration in the range of 10(-8) to 10(-6) (moles of cobalt ferrite per litre) and for different numbers of cycles n = 1, 3, 5, and 10. We found the adsorption of CoFe(2)O(4) nanoparticles within the CoFe(2)O(4)/PSS bilayers perfectly following a first order kinetic process, with the characteristic rate constant growing with the increase of CoFe(2)O(4) nanoparticle concentration and decreasing with the rise of the number of LbL cycles (n). Additionally, atomic force microscopy was employed for assessing the LbL film roughness and thickness. We found the film thickness increasing from about 20 to 120 nm while shifting from 3 to 10 CoFe(2)O(4)/PSS bilayers, using the 8.9 × 10(-6) (moles of cobalt ferrite per litre) suspension.     

多级结构还原氧化石墨烯包覆的钴铁氧体的合成及电化学性能

以水滑石为前驱体合成微米花/纳米片多级结构过渡金属复合氧化物CoFe2O4,一种高性能锂离子电池负极材料。 通过X射线衍射仪(XRD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等技术手段对其进行结构表征,发现得到的复合氧化物为单一晶相,且具有多级结构。 电化学性能测试表明,得到的负极材料具有高比容量和倍率性能。 通过还原氧化石墨烯(rGO)对CoFe2O4进行表面包覆制备CoFe2O4/rGO,其循环稳定性得到大幅度提高。     

TiO2-CoFe2O4磁性复合材料制备及太阳光催化性能

以四氯化钛、三价铁盐和二价钴盐为前驱体,采用超声波技术一步合成了TiO2-CoFe2O4新型复合光催化剂,运用VSM、XRD、TEM和UV-Vis技术进行了表征,以甲基橙为模拟污染物在太阳光照射下研究其光催化活性。结果表明:所制得的样品具有良好的顺磁性,其饱和磁化强度为212 Gs;样品中TiO2和CoFe2O4分别以锐钛矿相和尖晶石结构存在,粒径尺寸在40～50 nm之间;样品在紫外-可见区有很强的吸收。光催化结果表明复合催化剂具有较高的太阳光催化活性,循环使用3次,仍能保持良好的催化活性。     

Well-dispersed bi-component-active CoO/CoFe2O4 nanocomposites with tunable performances as anode materials for lithium-ion batteries

CoO/CoFe(2)O(4) nanocomposites, derived from scalably prepared CoFe-layered double hydroxide (CoFe-LDH) single-resource precursors, exhibit tunable cycle performances and rate capabilities, which are supported by the homogenous dispersion of bi-component active CoO and CoFe(2)O(4) phases.     

Synthesis,characterization and application of pH-sensitive CoFe2O4/reduced graphene oxide (RGO) nanocomposite in a circulated photocatalytic reactor for Reactive Red 141 removal of wastewaters

Research on Chemical Intermediates - In the present study, CoFe2O4/reduced graphene oxide nanocomposite (CoFe2O4/RGO) has been synthesized, characterized and applied as a photocatalyst for Reactive...