Intrinsic ferromagnetic properties in Cr-doped ZnO diluted magnetic semiconductors

The Cr-doped zinc oxide (Zn_1−xCr_xO, 0≤x≤0.08) diluted magnetic semiconductors have been synthesized successfully by the sol-gel method. Investigations on magnetic, optical and structural properties of the produced samples have been done. Energy dispersive spectroscopy (EDS) shows the existence of Cr ion in the Cr-doped ZnO. The results of X-ray diffraction (XRD), the transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) indicate that the Cr ions are at least partially substitutionally incorporated into the crystal lattice of ZnO. The produced samples show good high-T_c (Curie temperature) ferromagnetism (FM) in Cr-doped ZnO nanoparticles with Cr concentration of less than 5 at%. The results of photoluminescence (PL) further testify that FM is an intrinsic property of the Cr-doped ZnO nanoparticles. And the occurrence of FM should mainly contribute to the Cr doping.     

Effect of Mg doping on morphology,photocatalytic activity and related biological properties of Zn1−xMgxO nanoparticles

The objective of this study is to synthesize ZnO and Mg doped ZnO (Zn_1−xMg_xO) nanoparticles via the sol-gel method, and characterize their structures and to investigate their biological properties such as antibacterial activity and hemolytic potential.Nanoparticles (NPs) were synthesized by the sol-gel method using zinc acetate dihydrate (Zn(CH₃COO)₂.2H₂O) and magnesium acetate tetrahydrate (Mg(CH₃COO)₂.4H₂O) as precursors. Methanol and monoethanolamine were used as solvent and sol stabilizer, respectively. Structural and morphological characterizations of Zn_1−xMg_xO nanoparticles were studied by using XRD and SEM-EDX, respectively. Photocatalytic activities of ZnO and selected Mg-doped ZnO (Zn_1−xMg_xO) nanoparticles were investigated by degradation of methylene blue (MeB). Results indicated that Mg doping (both 10% and 30%) to the ZnO nanoparticles enhanced the photocatalytic activity and a little amount of Zn0.90 Mg0.10 O photocatalyst (1.0 mg/mL) degraded MeB with 99% efficiency after 24 h of irradiation under ambient visible light. Antibacterial activity of nanoparticles versus Escherichia coli ( E. coli ) was determined by the standard plate count method. Hemolytic activities of the NPs were studied by hemolysis tests using human erythrocytes. XRD data proved that the average particle size of nanoparticles was around 30 nm. Moreover, the XRD results indicatedthat the patterns of Mg doped ZnO nanoparticles related to ZnO hexagonal wurtzite structure had no secondary phase for x ≤ 0.2 concentration. For 0 ≤ x ≤ 0.02, NPs showed a concentration dependent antibacterial activity against E. coli . While Zn_0.90Mg_0.10 O totally inhibited the growth of E. coli , upper and lower dopant concentrations did not show antibacterial activity.     

Structural and optical properties of ZnMgO nanostructures formed by Mg in-diffused ZnO nanowires

ZnMgO nanostructures with wurtzite phase were prepared by thermal diffusion of Mg into the ZnO nanowires. As ZnO light-emitting devices have been operated by using ZnMgO layers as energy barrier layers to confine the carriers, it is essential to realize the characterization of ZnMgO particularly. In this work, the Mg content in Zn_1−xMg_xO alloy determined by X-ray diffraction (XRD) and photoluminescence (PL) shows a good coincidence. The variation of lattice constant and the blueshift of near-band-edge emission indicate that Zn²⁺ ions are successfully substituted by Mg²⁺ ions in the ZnO lattice. In Raman-scattering studies, the change of E₂(high) phonon line shape in ZnO:Mg nanostructures reveals the microscopic substitutional disorder. In addition to the host phonons of ZnO, two additional bands around 383 and 510 cm⁻¹ are presumably attributed to the Mg-related vibrational modes.     

Effects of gold catalysts and thermal evaporation method modifications on the growth process of Zn1−xMgxO nanowires

In this paper, we investigate the roles of gold catalysts and thermal evaporation method modifications in the growth process of Zn_1−xMg_xO nanowires. Zn_1−xMg_xO nanowires are fabricated on silicon substrates with and without using a gold catalyst. Characterizations reveal that Mg acts in a self-catalyst role during the growth process of Zn_1−xMg_xO nanowires grown on catalyst-free substrate. The optical properties and crystalline quality of the Zn_1−xMg_xO nanowires are characterized by room temperature photoluminescence (PL) measurements and Raman spectroscopy, respectively. The Raman and PL studies demonstrate that the Zn_1−xMg_xO nanowires grown using the catalyst-free method have good crystallinity with excellent optical properties and have a larger band-gap in comparison to those grown with the assistance of gold.     

Influences of Co doping on the structural,optical and magnetic properties of ZnO nanorods synthesized by hydrothermal route

Pure and Co-doped ZnO nanorods have been synthesized by a hydrothermal process. The structure, morphology and properties of as-prepared samples have been studied using X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), photoluminescence (PL) spectrometer as well as by superconducting quantum interference device (SQUID). The structure and morphology analyses show that Co doping can slightly impede the ZnO crystallinity, influence the nanorods morphology, but cannot change the preferred growth orientation of ZnO nanorods. The amount of Co doping contents is about 3.0 at% in ZnO nanorods and dopant Co²⁺ ions substitute Zn²⁺ ions sites in ZnO nanocrystal without forming any secondary phase. The optical measurements show that the Co doping can effectively tune energy band structure and enrich surface states in both UV and VL regions, which lead to novel PL properties of ZnO nanorods. In addition, ferromagnetic ordering of the as-synthesized Zn_1?xCo_xO nanorod arrays has been observed at room temperature, which should be ascribed to sp–d and d–d carrier exchange interactions and presence of abundant defects and oxygen vacancies.     

Effect of Cr and Mn ions on the structure and magnetic properties of GaFeO3: Role of the substitution site

Effect of substitution of Cr and Mn in the Fe and Ga sites of GaFeO₃ on the structural parameters and magnetic properties has been investigated by preparing GaFe_1−xCr_x(Mn_x)O₃ and Ga_1−xCr_x(Mn_x)FeO₃ starting with appropriate oxide precursors. It is shown that, starting with Cr or Mn substituted Ga₂O₃, one obtains Ga_1−xCr_x(Mn_x)FeO₃, while reaction of Cr or Mn substituted α-Fe₂O₃ with Ga₂O₃ yields GaFe_1−xCr_x(Mn_x)O₃. The structural parameters and magnetic properties vary significantly with the substitution site of Cr showing a large decrease in the unit cell parameters as well as the T_C and other magnetic properties when the substitution is at the octahedral Fe (1, 2) site. Substitution of Cr at the octahedral Ga2 site results in marginal changes. Substitution of Mn in the Ga and Fe sites also show differences although the changes themselves are much smaller. First-principles calculations confirm such site-specificity and show how Cr substitution affects the properties differently when substituted at the Ga2 and Fe1 sites.     

Electronic structure and visible light photocatalysis water splitting property of chromium-doped SrTiO3

Cr-doped SrTi_1−xCr_xO₃ (x=0.00, 0.02, 0.05, 0.10) powders, prepared by solvothermal method, were further characterized by ultraviolet-visible (UV-vis) absorption spectroscopy. The UV-vis spectra indicate that the SrTi_1−xCr_xO₃ powders can absorb not only UV light like pure SrTiO₃ powder but also the visible-light spectrum (λ>420 nm). The results of density functional theory (DFT) calculation illuminate that the visible-light absorption bands in the SrTi_1−xCr_xO₃ catalyst are attributed to the band transition from the Cr 3d to the Cr 3d+Ti 3d hybrid orbital. The photocatalytic activities of chromium-doped SrTiO₃ both under UV and visible light are increased with the increase in the amounts of chromium.     

Structural,optical and photoluminescence properties of Zn<Subscript>1−x</Subscript>Ce<Subscript>x</Subscript>O (x = 0, 0.05 and 0.1) nanoparticles by sol–gel method annealed under Ar atmosphere

Ce doped ZnO nanoparticles (Zn_1−xCe_xO, x = 0.0, 0.05 and 0.1) have been synthesized by sol–gel method at annealing temperature of 500 °C for 1 h under Ar atmosphere. The synthesized samples have been characterized by powder X-ray diffraction (XRD), energy dispersive X-ray studies, UV–Visible spectrophotometer and fourier transform infrared (FTIR) spectroscopy. The XRD measurements indicate that the prepared nanoparticles have a hexagonal wurtzite structure and CeO₂ crystallites. The calculated average crystalline varied from 21.97 to 15.62 nm with increase in Ce concentrations. The increase in lattice parameters reveals the substitution of Ce into ZnO lattice. The presence of functional groups and the chemical bonding is confirmed by FTIR spectra. PL spectra of the Zn_1−xCe_xO system show that the shift in near band edge emission from 386 to 363 nm and a shift in blue band emission from 517 to 485 nm which confirms the substitution of Ce into the ZnO lattice.     

Preparation of ZnO:CeO2-x thin films by AP-MOCVD: Structural and optical properties

The growth of columnar CeO₂, ZnO and ZnO:CeO_2−x films on quartz and AA6066 aluminum alloy substrates by economic atmospheric pressure metal-organic chemical vapor deposition (AP-MOCVD) is reported. A novel and efficient combination of metal acetylacetonate precursors as well as mild operating conditions were used in the deposition process. The correlation among crystallinity, surface morphology and optical properties of the as-prepared films was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), transmission electron microscopy (TEM) and UV-vis spectroscopy. The synthesized films showed different crystallographic orientations depending on the ZnO and CeO₂ lattice mismatch, cerium content and growth rate. The CeO₂ films synthesized in this work showed plate-like compact structures as a result of the growth process typical of CVD. Both pure and ZnO:CeO_2−x films were obtained with a hexagonal structure and highly preferred orientation with the c-axis perpendicular to both substrates under the optimal deposition conditions. The microstructure was modified from dense, short round columns to round structures with cavities (“rose-flower-like” structures) and the typical ZnO morphology by controlling the cerium doping the film and substrate nature. High optical transmittance (>87%) was observed in the pure ZnO films. As for the ZnO:CeO_2−x films, the optical transmission was decreased and the UV absorption increased, which subsequently was affected by an increase in cerium content. This paper assesses the feasibility of using ZnO:CeO_2−x thin films as UV-absorbers in industrial applications.     

Fabrication and Optical Properties of Aligned Zn1-xMgxO Nanowire Arrays

Aligned Zn_1-xMg_xO nanowire arrays were successfully prepared on Si(111) substrates via the chemical vapor deposition (CVD) method with a mixture of ZnO, Mg, and activated carbon powders as reactants. The microstructures and optical properties of the synthesized Zn_1-xMg_xO nanowire arrays were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive analysis X-ray (EDAX), and photoluminescence (PL) spectrum analytic apparatus, respectively. While Mg content was achieved or less approximately 0.29 (x, atomic ratio) in ZnO lattice, the crystal lattice of the synthesized samples exhibited wurtzite structure. The Mg atoms were distributed into the ZnO crystal as the interstitial and displaced atoms, and there was no phase separation in preparing Zn_1-xMg_xO nanowire arrays. However, as the Mg content was up to 0.53 (x) in the fabricated Zn_1-xMg_xO samples, a clear phase separation phenomena appeared in the Zn_1-xMg_xO crystal. Compared with the PL spectrum of the pure ZnO nanowire arrays, the analytic results showed that a blue-shift of the near-band edge emission with increasing Mg content was observed in the Zn_1-xMg_xO arrays. And the relative intensities of green peak at ca 535 nm and UV emission peak at ca 376 nm were all restrained.     

Structures and optical properties of Zn1?x Ni x O nanoparticles by coprecipitation method

Nanocrystals of undoped and nickel-doped zinc oxide (Zn_1?x Ni _x O, where x?=?0.00?C0.05) were synthesized by the coprecipitation method. Crystalline size, morphology, and optical absorption of prepared samples were determined by X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), and UV?Cvisible spectrometer. XRD and SEM studies revealed that Ni-doped ZnO crystallized in hexagonal wurtzite structure. Doping of ZnO with Ni²⁺ was intended to enhance the surface defects of ZnO. The incorporation of Ni²⁺ in place of Zn²⁺ provoked an increase in the size of nanocrystals as compared to undoped ZnO. Crystalline size of nanocrystals varied from 10 to 40?nm as the calcination temperature increased. Enhancement in the optical absorption of Ni-doped ZnO indicated that it can be used as an efficient photocatalyst under visible light irradiation. Optical absorption measurements indicated a red shift in the absorption band edge upon Ni doping. The band gap value of prepared undoped and Ni-doped ZnO nanoparticles decreased as annealing temperature was increased up to 800?°C.     

Doping induced magnetism in Co-ZnS nanoparticles

Zn_1−xCo_xS nanoparticles with x=0, 0.1, 0.2, and 0.3 were synthesized by the co-precipitation method using thiophenol as capping agent. The effect of Co doping on the structural, optical and magnetic properties are investigated. The X-ray diffraction patterns show single phase with cubic structure and the images of Transmission Electron Microscopy indicate an average particle size of 39 nm. Significant blue shift in the optical absorbing band edge was observed with increasing Co doping. In the Co doped samples, room-temperature (RT) magnetic hysteresis is observed and the magnetization reduces with increasing Co content. However, these samples show paramagnetic resonance instead of ferromagnetic resonance at both 300 and 80 K, suggesting that the origin of RT magnetization in these Zn_1−xCo_xS nanoparticles involves with the frustration of antiferromagnetic interactions.     

Preparation of ternary metal chalcogenide (M1-xFexS, M = Cd and Zn) nanocrystallites using single source precursors

M_1−xFe_xS (M = Cd, Zn) nanocrystallites were prepared by pyrolysis and solvothermal decomposition methods using [M(Aftscz)₂] and [M(AftsczH)₂Cl₂] (M = Cd, Zn and AftsczH = monoacetylferrocene thiosemicarbazone) as single source precursors. The M_1−xFe_xS nanocrystallites were characterized by powder X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive X-ray analysis and UV-Visible spectroscopy. XRD patterns show that the Cd_1−xFe_xS and Zn_1−xFe_xS nanocrystallites prepared by pyrolysis and solvothermal decomposition routes have hexagonal phase. TEM images show presence of spherical and spherical plate-like morphology of M_1−xFe_xS nanoparticles. M_1−xFe_xS nanoparticles obtained by solvothermal decomposition in ethylene glycol are found to be capped with ethylene glycol as evident from IR spectra.     

First principles calculations of electronic structure and magnetic properties of Cr-based magnetic semiconductors Al1−xCrxX (X=N, P, As, Sb)

First principles calculations based on the density functional theory (DFT) within the local spin density approximation are performed to investigate the electronic structure and magnetic properties of Cr-based zinc blende diluted magnetic semiconductors Al_1−xCr_xX (X=N, P, As, Sb) for 0≤x≤0.50.The behaviour of magnetic moment of Al_1−xCr_xX at each Cr site as well as the change in the band gap value due to spin down electrons has been studied by increasing the concentration of Cr atom and through changing X from N to Sb. Furthermore, the role of p-d hybridization is analyzed in the electronic band structure and exchange splitting of d-dominated bands. The interaction strength is stronger in Al_1−xCr_xN and becomes weaker in Al_1−xCr_xSb. The band gap due to the spin down electrons decreases with the increased concentration of Cr in Al_1−xCr_xX, and as one moves down along the isoelectronic series in the group V from N to Sb. Our calculations also verify the half-metallic ferromagnetic character in Cr doped AlX.     

Enhanced visible light-driven photocatalytic degradation of crystal violet dye using Cr doped BaFe12O19 prepared via facile micro-emulsion route

The Cr ion doping effect on various properties of Cr doped BaCr_xFe_12-xO₁₉ nanoparticles was investigated, which were synthesized via a facile microemulsion approach and properties were studied using XRD, SEM, FTIR, Raman, photoluminescence and UV–visible techniques along with dielectric, optical and ferroelectric properties. The BaCr_xFe_12-xO₁₉ structure was hexagonal involving P63/mmc space group with average crystalline size of 9–18 nm. The NPs exhibited agglomerated platelet heterogeneous morphology. The presence of the Ba-O-Fe functional group was also confirmed by FTIR analysis. The PL analysis revealed that the doping reduced the recombination rate and charge (e^?-h⁺) separation is facilitated. The coercivity (H_c) and saturation polarization (Ps) increased with doping content and dielectric loss reduces with frequency and dopant concentration. The dopant contents also increased the AC conductivity and the optical bandgap found in 1.75–2.83 (eV) range. The BaCr_xFe_12-xO₁₉ exhibited a significantly higher photocatalytic efficiency versus BaFe₁₂O₁₉, and 91 % CV dye was degraded in 90 min under visible light irradiation. Additionally, a recycling experiment was conducted to confirm the stability of the prepared photocatalyst and Cr doped BaCr_xFe_12-xO₁₉ exhibited excellent stability and reusability. The Cr doping affected the dielectric, optical and ferroelectric properties and based on photocatalytic properties of BaCr_xFe_12-xO₁₉, it has potential applications for the destruction of dyes in wastewater under visible light exposure, which will make the process highly feasible for photocatalytic applications.     

Structural,optical and dielectric relaxor properties of neodymium doped cubic perovskite (Ba1−xNd2x/3)(Zr0.3Ti0.7)O3

Neodymium doped Barium Zirconate Titanate (Ba_1−xNd_2x/3)(Zr_0.3Ti_0.7)O₃ (x = 0.00, 0.02, 0.04, 0.06, 0.08, 0.10) ceramics were prepared using the solid state reaction route. Structural characterizations of the materials were done by using X-ray diffraction and Raman spectroscopy. XRD study suggested that all the compositions were of single phase cubic perovskite structure with space group Pm-3m while Raman spectra revealed that the replacement of the Ba²⁺ ions by Nd³⁺ ions significantly reduced the intensity of the Raman active modes and shifted them towards higher energy side. Room temperature optical property was analyzed by photoluminescence spectroscopy, which confirmed formation of shallow defects in the band gap. Photoluminescence property was attributed to the presence of polar [TiO₆] distorted clusters in the globally cubic matrix. As a result PL emission spectra of these materials were found to belong to violet–blue regions. Microstructural study of sintered pellets revealed that the grain sizes increase with increase in doping concentration. The temperature dependence of the dielectric properties was investigated in the frequency range 1 kHz to 1 MHz. The broadening in the dielectric constant peak around the phase transition temperature and shifting of the temperature maximum towards higher temperatures with increase in frequency indicated a relaxor type of behavior.     

Structural and magnetic properties of the Zn0.8−4xHoxOy (0.05 ≤ x ≤ 0.10) compounds prepared by solid state reactions

Zn_0.8−4xHo_xO_y (0.05 ≤ x ≤ 0.10) diluted magnetic semiconductors were prepared by the solid state reaction method. We have studied the structural properties of the samples by using the XRD, SEM, and EDX techniques. The SEM results clearly demonstrate that Ho³⁺ ions are quite well substituted for Zn²⁺ in the ZnO lattice, and the grains of the samples are very well connected to each other and tightly packed. From the XRD and EDX spectra of the samples, it has been concluded that the substitution of Ho causes no change in the hexagonal wurtzite structure of ZnO. According to our M–H and M–T measurements paramagnetism has been observed for all the samples from our attainable lowest temperature of 10 K to 300 K. Furthermore, the trend of the AC-susceptibility (χ) versus temperature curves, measured under an AC-magnetic field of 10 Oe, also support our conclusion about the paramagnetic contribution in the Zn_0.8−4xHo_xO_y compounds explored in this study. In order to clearly see the paramagnetic contribution, and whether there is also a ferromagnetic or antiferromagnetic contribution or not the inverse susceptibility (1/χ) against temperature curves are also plotted. Those curves indicate that, the substitution of Ho into the ZnO compound causes, in addition to the paramagnetism, a weaker antiferromagnetic (AFM) interaction.     

Bi_(4-x)Eu_xTi_(3-y)M_yO_(12)(M=Fe,Co,Ni)纳米颗粒的制备及光学和磁学性能

三层结构的Aurivillius相的Bi_(4-x)Eu_xTi_(3-y)M_yO_(12)(x=0~0.6;M=Fe/Co/Ni,y=0.01,0.02,0.04,0.06,0.08,0.10)纳米颗粒,是通过共沉淀法和后续的高温煅烧处理所制备的。利用XRD,SEM,PL,Raman,PPMS等方法对样品进行表征,研究了不同掺杂浓度下的产物的物相、形貌和性能等。实验结果表明,通过掺杂,发现纳米颗粒的粒径变小,形貌更均一,分散性也更好。通过对掺杂离子浓度的优化,发现Eu~(3+)离子的掺杂浓度为x=0.4时,发光强度是最强的。此外,对Ti位进行了磁性离子(Fe~(3+),Co~(3+)和Ni~(2+))的掺杂,实验结果发现随着掺杂的磁性离子浓度的减少,发光强度是逐渐增强,而且产物具有很好的铁磁性。     

Preparation and properties of amorphous titania-coated zinc oxide nanoparticles

Amorphous TiO₂-coated ZnO nanoparticles were prepared by the solvothermal synthesis of ZnO nanoparticles in ethanol and the followed by sol-gel coating of TiO₂ nanolayer. The analyses of X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the resultant ZnO nanoparticles were hexagonal with a wurtzite structure and a mean diameter of about 60 nm. Also, after TiO₂ coating, the TEM images clearly indicated the darker ZnO nanoparticles being surrounded by the lighter amorphous TiO₂ layers. The zeta potential analysis revealed the pH dependence of zeta potentials for ZnO nanoparticles shifted completely to that for TiO₂ nanoparticles after TiO₂ coating, confirming the formation of core-shell structure and suggesting the coating of TiO₂ was achieved via the adhesion of the hydrolyzed species Ti-O⁻ to the positively charged surface of ZnO nanoparticles. Furthermore, the analyses of Fourier transform infrared (FTIR) and Raman spectra were also conducted to confirm that amorphous TiO₂ were indeed coated on the surface of ZnO nanoparticles. In addition, the analyses of ultraviolet-visible (UV-VIS) and photoluminescence (PL) spectra revealed that the absorbance of amorphous TiO₂-coated ZnO nanoparticles at 375 nm gradually decreased with an increase in the Ti/Zn molar ratio and the time for TiO₂ coating, and the emission intensity of ZnO cores could be significantly enhanced by the amorphous TiO₂ shell.     

Bi4-xEuxTi3-yMyO12（M=Fe，Co，Ni）纳米颗粒的制备及光学和磁学性能

三层结构的Aurivillius相的Bi_4-xEu_xTi_3-yM_yO₁₂（x=0~0.6;M=Fe/Co/Ni,y=0.01,0.02,0.04,0.06,0.08,0.10）纳米颗粒,是通过共沉淀法和后续的高温煅烧处理所制备的。利用XRD,SEM,PL,Raman,PPMS等方法对样品进行表征,研究了不同掺杂浓度下的产物的物相、形貌和性能等。实验结果表明,通过掺杂,发现纳米颗粒的粒径变小,形貌更均一,分散性也更好。通过对掺杂离子浓度的优化,发现Eu³⁺离子的掺杂浓度为x=0.4时,发光强度是最强的。此外,对Ti位进行了磁性离子（Fe³⁺,Co³⁺和Ni²⁺）的掺杂,实验结果发现随着掺杂的磁性离子浓度的减少,发光强度是逐渐增强,而且产物具有很好的铁磁性。