SYNTHESIS OF POLYSTYRENE/TiO_2 CORE-SHELL MATERIALS

TiO_2-coated polystyrene nanoparticles were prepared in a simple way.First,functional PS particles were synthesized by copolymerizing one kind of polymerizable surfactant with styrene.Then the stable dispersions of polystyrene nanoparticles were used as templates,and polystyrene nanoparticles were coated with titania by in situ hydrolysis of tetra-n- butyl titanate (TBT).No surface treatment and centrifugation/redispersion cycle process were needed during the whole experiment.Isolated PS spheres with uni...     

SYNTHESIS OF POLYSTYRENE/TiO2 CORE-SHELL MATERIAL

 TiO₂-coated polystyrene nanoparticles were prepared in a simple way. First, functional PS particles were synthesized by copolymerizing one kind of polymerizable surfactant with styrene. Then the stable dispersions of polystyrene nanoparticles were used as templates, and polystyrene nanoparticles were coated with titania by in situ hydrolysis of tetra-n-butyl titanate (TBT). No surface treatment and centrifugation/redispersion cycle process were needed during the whole experiment. Isolated PS spheres with uniform coatings of titania were obtained when water concentration was lower than a certain level.     

Deposition of Oral Bacteria and Polystyrene Particles to Quartz and Dental Enamel in a Parallel Plate and Stagnation Point Flow Chamber

The aim of this paper is to determine to what extent (i) deposition of oral bacteria and polystyrene particles, (ii) onto quartz and dental enamel with and without a salivary conditioning film, (iii) in a parallel plate (PP) and stagnation point (SP) flow chamber and at common Peclet numbers are comparable. All three bacterial strains showed different adhesion behaviors, and even Streptococcus mitis BMS, possessing a similar cell surface hydrophobicity as polystyrene particles, did not mimic polystyrene particles in its adhesion behavior, possibly as a result of the more negative ζ potentials of the polystyrene particles. The stationary endpoint adhesion of all strains, including polystyrene particles, was lower in the presence of a salivary conditioning film, while also desorption probabilities under flow were higher in the presence of a conditioning film than in its absence. Deposition onto quartz and enamel surfaces was different, but without a consistent trend valid for all strains and polystyrene particles. It is concluded that differences in experimental results exist, and the process of bacterial deposition to enamel surfaces cannot be modeled by using polystyrene particles and quartz collector surfaces.     

Influence of nanobubbles on the adsorption of nanoparticles

A quartz crystal microbalance was used to study the influence of nanobubbles on the adsorption of polystyrene nanoparticles onto surfaces coated with gold, or coated with dodecanethiol or mercaptoundecanoic acid self-assembled monolayers (SAMs). Adsorption of the nanoparticles onto the surface causes the resonant frequency of the quartz crystal to decrease. We found that particles were adsorbed onto the gold-coated quartz crystal in air-rich water, but not in degassed water. This finding supports the long-standing hypothesis that nanobubbles play a key role in the long-range attractive force between hydrophobic surfaces in aqueous solutions. When the experiments were conducted using quartz crystals coated with a hydrophobic dodecanethiol SAM, the nanoparticles were adsorbed onto the surface even in degassed water due to the short-range hydrophobic interactions between the nanoparticles and the dodecanethiol molecules. In contrast, the nanoparticles were adsorbed to a lesser degree onto the hydrophilic mercaptoundecanoic acid-coated crystals due to electrostatic repulsive forces.     

An EQCM study on the influence of saccharin on the corrosion properties of nanostructured cobalt and cobalt-iron alloy coatings

Nanostructured cobalt (Co) and cobalt-iron (CoFe) alloy coatings were electrodeposited from sulfate solutions in the presence and absence of saccharin. The effects of saccharin on the corrosion behavior of Co and CoFe alloy coatings were investigated using the electrochemical quartz crystal microbalance (EQCM) technique coupled with cyclic voltammetry (CV) measurements. Saccharin was added to the electrolyte as a grain refiner and brightener. Interestingly, opposite corrosion behaviors were found for all nanostructured coatings in 0.1 M H₂SO₄ and 0.1 M NaOH. The use of saccharin as an additive in the plating solution accelerated the anodic reaction for all deposits in acidic medium. The mass decreases while dissolution rate increased with higher saccharin concentration. Meanwhile, formation of a thick passive film on the Co electrode surface were enhanced while a hindering effect was observed for CoFe alloy coatings deposited in the presence of saccharin in alkaline solution. The anodic and cathodic curves obtained from potentiodynamic polarization experiments were also in agreement with the EQCM results.     

Resolution of the vertical and horizontal heterogeneity of adsorbed collagen layers by combination of QCM-D and AFM

Collagen (type I from calf skin) adsorption on polystyrene (PS) and plasma-oxidized polystyrene (PSox) was studied, using a quartz crystal microbalance with energy dissipation measurements (QCM-D) and atomic force microscopy (AFM) in tapping mode. Radio-labeled collagen was used to measure the adsorbed amount and the ability of adsorbed collagen to exchange with molecules in the solution. The results show that the collagen adlayer consists of two parts: a dense and thin sheet in which fibrils are formed (directly observed by AFM) and an overlying thick layer (up to 200 nm) containing protruding molecules or bundles which are in very low concentration but modify noticeably the local viscosity. The thickness and viscosity of the semi-liquid adlayer both increase with adsorption time and collagen concentration. Fibril formation near the surface also increases with time and collagen concentration and occurs more readily on PS compared to PSox. Radiochemical measurements show that this may be related to the larger mobility of molecules adsorbed on PS, presumably owing to a smaller number of binding points.     

Reactivity and Coaggregation of p-Nitrophenyl Esters with Polymer Micelles at Solid Surfaces

The polymer micelle, poly[(N-(n-dodecyl)-4-vinylpyridiniumco-N-ethyl-4-vinylpyridinium) bromide], PDE, containing 30% dodecyl groups has been found to promote the adhesion of lipophiles to various surfaces including quartz, polystyrene, and poly(methyl methacrylate) cuvette surfaces from aqueous solutions. The adsorption of PDE/ester coaggregates to the surfaces was studied by hydrolysis of p-nitrophenyl esters in aqueous PDE(30) solutions. The extent of reaction of p-nitrophenyl myristate, an ester with a linear acyl carbon chain length of 14, can be viewed as a probe to study the adhesion of the PDE/ester coaggregates to the cuvette surfaces. The difference between initial concentration of ester and concentration of hydrolysis product, p-nitrophenoxide ion, gives the concentration of unreacted ester in the aggregates or film adhering to the solid surface. Up to 40% of p-nitrophenyl myristate was found unreacted on the surface of quartz cuvettes after apparent completion of the reaction. No adhesion of the related caproate ester with a linear acyl carbon chain length of 6 was detected. Copyright 2000 Academic Press.     

Quantitative SERS sensors for environmental analysis of naphthalene

In the investigation of chemical pollutants, such as PAHs (Polycyclic Aromatic Hydrocarbons) at low concentration in aqueous medium, Surface-Enhanced Raman Scattering (SERS) stands for an alternative to the inherent low cross-section of normal Raman scattering. Indeed, SERS is a very sensitive spectroscopic technique due to the excitation of the surface plasmon modes of the nanostructured metallic film. The surface of quartz substrates was coated with a hydrophobic film obtained by silanization and subsequently reacted with polystyrene (PS) beads coated with gold nanoparticles. The hydrophobic surface of the SERS substrates pre-concentrates non-polar molecules such as naphthalene. Under laser excitation, the SERS-active substrates allow the detection and the identification of the target molecules localized close to the gold nanoparticles. The morphology of the SERS substrates based on polystyrene beads surrounded by gold nanoparticles was characterized by scanning electron microscopy (SEM). Furthermore, the Raman fingerprint of the polystyrene stands for an internal spectral reference. To this extent, an innovative method to detect and to quantify organic molecules, as naphthalene in the range of 1 to 20 ppm, in aqueous media was carried out. Such SERS-active substrates tend towards an application as quantitative SERS sensors for the environmental analysis of naphthalene.     

石英晶体微天平用于微囊藻毒素在聚合物涂覆的金片表面吸附

合成了具有不同功能化的聚苯乙烯树脂,利用石英晶体微天平对树脂和微囊藻毒素相互吸附作用进行实时监测和研究．研究发现,吸附的pH和表面性质对于吸附量有重要的影响,而温度影响不大,中性pH氨基树脂对微囊藻毒素的吸附效果最好.     

Solvent Effect on the Sensitivity and Selectivity of Determining Aniline and Toluidines in the Air by Piezoelectric Microweighing

Batch conditions were optimized for the sorption of aniline and toluidines from the air on polystyrene, polyethyleneglycol-2000, and polyethyleneglycol succinate using piezoelectric microweighing. It was found that the analytical signal of a quartz crystal resonator depended on the mass of the modifier on the electrode surface and on the solvent. The selectivity of modifiers with respect to the compounds studied was estimated.     

Peptide-PEG amphiphiles as cytophobic coatings for mammalian and bacterial cells

Amphiphilic macromolecules containing a polystyrene-adherent peptide domain and a cell-repellent poly(ethylene glycol) domain were designed, synthesized, and evaluated as a cytophobic surface coating. Such cytophobic, or cell-repellent, coatings are of interest for varied medical and biotechnological applications. The composition of the polystyrene binding peptide domain was identified using an M13 phage display library. ELISA and atomic force spectroscopy were used to evaluate the binding affinity of the amphiphile peptide domain to polystyrene. When coated onto polystyrene, the amphiphile reduced cell adhesion of two distinct mammalian cell lines and pathogenic Staphylococcus aureus strains.     

Nanostructure protein repellant amphiphilic copolymer coatings with optimized surface energy by Inductively Excited Low Pressure Plasma

Statistically designed amphiphilic copolymer coatings were deposited onto Thermanox, Si wafer, and quartz crystal microbalance (QCM) substrates via Plasma Enhanced Chemical Vapor Deposition of 1H,1H,2H,2H-perfluorodecyl acrylate and diethylene glycol vinyl ether in an Inductively Excited Low Pressure Plasma reactor. Plasma deposited amphiphilic coatings were characterized by Field Emission Scanning Electron Microscopy, X-ray Photoelectron Spectroscopy, Atomic Force Microscopy, and Water Contact Angle techniques. The surface energy of the coatings can be adjusted between 12 and 70 mJ/m(2). The roughness of the coatings can be tailored depending on the plasma mode used. A very smooth coating was deposited with a CW (continuous wave) power, whereas a rougher surface with R(a) in the range of 2 to 12 nm was deposited with the PW (pulsed wave) mode. The nanometer scale roughness of amphiphilic PFDA-co-DEGVE coatings was found to be in the range of the size of the two proteins namely BSA and lysozyme used to examine for the antifouling properties of the surfaces. The results show that the statistically designed surfaces, presenting a surface energy around 25 mJ/m(2), present no adhesion with respect to both proteins measured by QCM.     

Physisorbed surface coatings for poly(dimethylsiloxane) and quartz microfluidic devices

Surface modifications of microfluidic devices are of essential importance for successful bioanalytical applications. Here, we investigate three different coatings for quartz and poly(dimethylsiloxane) (PDMS) surfaces. We employed a triblock copolymer with trade name F₁₀₈, poly(l-lysine)-g-poly(ethylene glycol) (PLL-PEG), as well as the hybrid coating n-dodecyl-β-d-maltoside and methyl cellulose (DDM/MC). The impact of these coatings was characterized by measuring the electroosmotic flow (EOF), contact angle, and prevention of protein adsorption. Furthermore, we investigated the influence of static coatings, i.e., the incubation with the coating agent prior to measurements, and dynamic coatings, where the coating agent was present during the measurement. We found that all coatings on PDMS as well as quartz reduced EOF, increased reproducibility of EOF, reduced protein adsorption, and improved the wettability of the surfaces. Among the coating strategies tested, the dynamic coatings with DDM/MC and F₁₀₈ demonstrated maximal reduction of EOF and protein adsorption and simultaneously best long-term stability concerning EOF. For PLL-PEG, a reversal in the EOF direction was observed. Interestingly, the static surface coating strategy with F₁₀₈ proved to be as effective to prevent protein adsorption as dynamic coating with this block copolymer. These findings will allow optimized parameter choices for coating strategies on PDMS and quartz microfluidic devices in which control of EOF and reduced biofouling are indispensable.     

Nanostructured films of amphiphilic fluorinated block copolymers for fouling release application

New amphiphilic block copolymers S nSz m consisting of blocks with varied degrees of polymerization, n and m, of polystyrene, S, and polystyrene carrying an amphiphilic polyoxyethylene-polytetrafluoroethylene chain side-group, Sz, were prepared by controlled atom transfer radical polymerization (ATRP). The block copolymers, either alone or in a blend with commercial SEBS (10 wt% SEBS), were spin-coated in thinner films (200-400 nm) on glass and spray-coated in thicker films ( approximately 500 nm) on a SEBS underlayer (150-200 microm). Angle-resolved X-ray photoelectron spectroscopy (XPS) measurements proved that at any photoemission angle, varphi, the atomic ratio F/C was larger than that expected from the known stoichiometry. Consistent with the enrichment of the outer film surface (3-10 nm) in F content, the measured contact angles, theta, with water (theta w > or = 107 degrees ) and n-hexadecane (theta h > or = 64 degrees ) pointed to the simultaneous hydrophobic and lipophobic character of the films. The film surface tension gamma S calculated from the theta values was in the range 13-15 mN/m. However, the XPS measurements on the "wet" films after immersion in water demonstrated that the film surface underwent reconstruction owing to its amphiphilic nature, thereby giving rise to a more chemically heterogeneous structure. The atomic force microscopy (AFM) images (tapping mode/AC mode) revealed well-defined morphological features of the nanostructured films. Depending on the chemical composition of the block copolymers, spherical (ca. 20 nm diameter) and lying cylindrical (24-29 nm periodicity) nanodomains of the S discrete phase were segregated from the Sz continuous matrix (root-mean-square, rms, roughness approximately 1 nm). After immersion in water, the underwater AFM patterns evidenced a transformation to a mixed surface structure, in which the nanoscale heterogeneity and topography (rms = 1-6 nm) were increased. The coatings were subjected to laboratory bioassays to explore their intrinsic ability to resist the settlement and reduce the adhesion strength of two marine algae, viz., the macroalga (seaweed) Ulva linza and the unicellular diatom Navicula perminuta. The amphiphilic nature of the copolymer coatings resulted in distinctly different performances against these two organisms. Ulva adhered less strongly to the coatings richer in the amphiphilic polystyrene component, percentage removal being maximal at intermediate weight contents. In contrast, Navicula cells adhered less strongly to coatings with a lower weight percentage of the amphiphilic side chains. The results are discussed in terms of the changes in surface structure caused by immersion and the effects such changes may have on the adhesion of the test organisms.     

Tensammetry with accumulation on the hanging mercury drop electrode: Part 6. Errors of determination caused by adsorption of non-ionic surfactants on the material of the measuring cell

The adosorptive loss of oxyethylated alkylphenols (Triton X-100 and Rokafenol N-3), oxyethylated alcohols (Brij-35, Marlipal 1618/40 and surfactant 18-10) and poly(ethylene glycol) of MW 9000 on cells constructed from quartz, glass, glassy carbon, PTFE, polyethylene, polypropylene, polystyrene and aluminium during the measuring process was investigated. In all instances very substantial losses were found, which completely changed the results of the determination. Apart from the vessel itself, very important losses on the ceramic frit located at the end of the salt bridge were found.The loss of all the surfactants tested on the quartz vessel is not very substantial and, after protection of the ceramic frit, a cell with such a construction gives minimum losses. The glass cell is very sensitivie to the manner of preparation of its surface. Cells constructed from PTFE and glassy carbon adsorb more specifically than others and can be used for the determination of oxyethylated alcohols but not for the determination of oxyethylated alkylphenols. Other materials used gave substantial losses of almost all the surfactants tested. Particularly bad results were obtained with polystyrene and aluminium cells.     

Comparison of stages in oil agglomeration process of quartz with sodium oleate in the presence of Ca(II) and Mg(II) ions

The oil agglomeration of quartz with sodium oleate in the presence of calcium and magnesium ions comprises three consecutive stages: adsorption of cations onto quartz surfaces, which leads to coagulation of the suspension, shear flocculation with sodium oleate and finally, agglomeration of flocs by kerosene. The effects of pH and cation concentration on these stages were investigated and the results were presented comparatively. It was found that all the stages of oil agglomeration of quartz exhibited sharp dependences on pH and cation concentration. That is, these stages generally took place in the pH and concentration ranges in which hydroxy complexes of the cations existed in the suspension. In the case of magnesium ion, the coagulation, shear flocculation and especially oil agglomeration of quartz improved after precipitation of hydroxide. These species of calcium and magnesium ions formed at high pH were adsorbed on the negatively charged surface of quartz, as a result of which the adsorption of sodium oleate became possible and thus the shear flocculation of the particles was achieved. Thereafter, the hydrophobic quartz flocs could be agglomerated by kerosene as bridging liquid. The increase in the shear flocculation efficiency depending on the increase of surface hydrophobicity enhanced the oil agglomeration of quartz with kerosene. The maximum recoveries for all the stages of the quartz were obtained in the presence of 10(-3) M magnesium and 5x10(-3) M calcium ions at pH 11. However, some differences in the behavior of shear flocculation and oil agglomeration of quartz suspension were observed above 10(-3) M concentration of magnesium ion.     

阳离子和两性表面活性剂对石英表面润湿性的影响

利用座滴法研究了阳离子表面活性剂十六烷基醚羟丙基季铵盐(C16PC)和两性离子表面活性剂十六烷基醚羟丙基羧酸甜菜碱(C16PB)溶液在石英表面上的润湿性质, 考察了表面活性剂类型及浓度对接触角的影响趋势, 讨论了黏附张力和黏附功的变化规律. 研究发现, 两种表面活性剂在高能的石英表面的吸附造成石英-水的界面自由能(γsl)增大. C16PB通过弱相互作用随机吸附到石英表面, 其增大γsl的能力与降低表面张力(γ1g)的能力相当, 接触角(θ)随浓度变化不大. C16PC 随体相浓度增大能够在石英表面通过静电作用形成定向排列的单分子层, 而后在临界胶束浓度(cmc)附近形成双层结构, 接触角随浓度变化的趋势可分为4个区域, 并通过一个极大值.     

Layer-by-layer fabrication of broad-band superhydrophobic antireflection coatings in near-infrared region

Broad-band superhydrophobic antireflective (AR) coatings in near infrared (NIR) region were readily fabricated on silicon or quartz substrates by a layer-by-layer (LbL) assembly technique. First, a porous poly(diallyldimethylammonium chloride) (PDDA)/SiO2 nanoparticle multilayer coating with AR property was prepared by LbL deposition of PDDA and 200 nm SiO2 nanoparticles. PDDA was then alternately assembled with sodium silicate on the PDDA/SiO2 nanoparticle coating to prepare a two-level hierarchical surface. Superhydrophobic AR coating with a water contact angle of 154 degrees was finally obtained after chemical vapor deposition of a layer of fluoroalkylsilane on the hierarchical surface. Quartz substrate with the as-fabricated superhydrophobic AR coating has a maximal transmittance above 98% of incidence light in the NIR region, which is increased by five percent compared with bare quartz substrate. Simultaneously, the superhydrophobic property endows the AR coating with water-repellent ability. Such superhydrophobic AR coatings can effectively avoid the disturbance of water vapor on their AR property and are expected to be applicable under humid environments.     

Effect of Cationic and Zwitterionic Surfactants on Contact Angle of Quartz–Water–Crude Oil System

The influences of four cationic surfactants hexadecyl glycidyl ether ammonium chloride and four zwitterionic surfactants hexadecyl glycidyl ether glycine Betaine solutions on contact angle of crude oil on a quartz surface were investigated using a captive drop method. The effects of surfactant type, structure, and concentration on contact angle were expounded. From obtained results it appears that the adsorbed surfactant at oil–water interface reduces the interfacial tension and the adsorption at quartz–water interface improves interfacial free energy, which results in reducing the stable value of contact angle and weakening dynamic behavior. At high concentration, the zwitterionic surfactant with branched-chain may form semi-micelle at quartz surface. As a result, the stable value of contact angle passes through a sharp minimum with the increasing concentration.     

Effect of anionic surfactant and short-chain alcohol mixtures on adsorption at quartz/water and water/air interfaces and the wettability of quartz

Measurements of the advancing contact angles for aqueous solutions of sodium dodecyl sulfate (SDDS) or sodium hexadecyl sulfonate (SHS) in mixtures with methanol, ethanol, or propanol on a quartz surface were carried out. On the basis of the obtained results and Young and Gibbs equations the critical surface tension of quartz wetting, the composition of the surface layer at the quartz-water interface, and the activity coefficients of the anionic surfactants and alcohols in this layer as well as the work of adhesion of aqueous solutions of anionic surfactant and alcohol mixtures to the quartz surface were determined. The analysis of the contact angle data showed that the wettability of quartz changed visibly only in the range of alcohol and anionic surfactant concentration at which these surface-active agents were present in the solution in the monomeric form. The analysis also showed that there was a linear dependence between the adhesion and the surface tension of aqueous solutions of anionic surfactant and alcohol mixtures. This dependence can be described by linear equations for which the constants depend on the anionic surfactant and alcohol concentrations. The slope of all linear dependence between adhesion and surface tension was positive. The critical surface tension of quartz wetting determined from this dependence by extrapolating the adhesion tension to the value equal to the surface tension (for contact angle equal zero) depends on the assumption whether the concentration of anionic surfactant or alcohol was constant. Its average value is equal to 29.95mN/m and it is considerably lower than the quartz surface tension. The positive slope of the adhesion-surface tension curves was explained by the possibility of the presence of liquid vapor film beyond the solution drop which settled on the quartz surface and the adsorption of surface-active agents at the quartz/monolayer water film-water interface. This conclusion was confirmed by the work of adhesion of aqueous solutions of anionic surfactants and short-chain alcohol mixtures to the quartz surface determined on the basis of the contact angle data and molar fraction of anionic surfactants and alcohols and their activity coefficient in the surface layer.