Nitrogen-Doped Porous Carbon Materials Derived from Graphene Oxide/Melamine Resin Composites for CO2 Adsorption

CO₂ adsorption in porous carbon materials has attracted great interests for alleviating emission of post-combustion CO₂. In this work, a novel nitrogen-doped porous carbon material was fabricated by carbonizing the precursor of melamine-resorcinol-formaldehyde resin/graphene oxide (MR/GO) composites with KOH as the activation agent. Detailed characterization results revealed that the fabricated MR(0.25)/GO-500 porous carbon (0.25 represented the amount of GO added in wt.% and 500 denoted activation temperature in °C) had well-defined pore size distribution, high specific surface area (1264 m²·g⁻¹) and high nitrogen content (6.92 wt.%), which was mainly composed of the pyridinic-N and pyrrolic-N species. Batch adsorption experiments demonstrated that the fabricated MR(0.25)/GO-500 porous carbon delivered excellent CO₂ adsorption ability of 5.21 mmol·g⁻¹ at 298.15 K and 500 kPa, and such porous carbon also exhibited fast adsorption kinetics, high selectivity of CO₂/N₂ and good recyclability. With the inherent microstructure features of high surface area and abundant N adsorption sites species, the MR/GO-derived porous carbon materials offer a potentially promising adsorbent for practical CO₂ capture.     

Fabrication of Phosphorus-Doped Cobalt Silicate with Improved Electrochemical Properties

The development of electrode materials for supercapacitors (SCs) is greatly desired, and this still poses an immense challenge for researchers. Cobalt silicate (Co₂SiO₄, denoted as CoSi) with a high theoretical capacity is deemed to be one of the sustainable electrode materials for SCs. However, its achieved electrochemical properties are still not satisfying. Herein, the phosphorus (P)-doped cobalt silicate, denoted as PCoSi, is synthesized by a calcining strategy. The PCoSi exhibits 1D nanobelts with a specific surface area of 46 m²∙g⁻¹, and it can significantly improve the electrochemical properties of CoSi. As a supercapacitor’s (SC’s) electrode, the specific capacitance of PCoSi attains 434 F∙g⁻¹ at 0.5 A∙g⁻¹, which is much higher than the value of CoSi (244 F∙g⁻¹ at 0.5 A∙g⁻¹). The synergy between the composition and structure endows PCoSi with attractive electrochemical properties. This work provides a novel strategy to improve the electrochemical performances of transition metal silicates.     

MWCNT Decorated Rich N-Doped Porous Carbon with Tunable Porosity for CO2 Capture

Designing of porous carbon system for CO₂ uptake has attracted a plenty of interest due to the ever-increasing concerns about climate change and global warming. Herein, a novel N rich porous carbon is prepared by in-situ chemical oxidation polyaniline (PANI) on a surface of multi-walled carbon nanotubes (MWCNTs), and then activated with KOH. The porosity of such carbon materials can be tuned by rational introduction of MWCNTs, adjusting the amount of KOH, and controlling the pyrolysis temperature. The obtained M/P-0.1-600-2 adsorbent possesses a high surface area of 1017 m² g⁻¹ and a high N content of 3.11 at%. Such M/P-0.1-600-2 adsorbent delivers an enhanced CO₂ capture capability of 2.63 mmol g⁻¹ at 298.15 K and five bars, which is 14 times higher than that of pristine MWCNTs (0.18 mmol g⁻¹). In addition, such M/P-0.1-600-2 adsorbent performs with a good stability, with almost no decay in a successive five adsorption-desorption cycles.     

Synthesis of Fe2+ Substituted High-Performance LiMn1−xFexPO4/C (x = 0, 0.1, 0.2, 0.3, 0.4) Cathode Materials for Lithium-Ion Batteries via Sol-Gel Processes

A series of carbon-coated LiMn_1−xFe_xPO₄ (x = 0, 0.1, 0.2, 0.3, 0.4) materials are successfully constructed using glucose as carbon sources via sol-gel processes. The morphology of the synthesized material particles are more regular and particle sizes are more homogeneous. The carbon-coated LiMn_0.8Fe_0.2PO₄ material obtains the discharge specific capacity of 152.5 mAh·g⁻¹ at 0.1 C rate and its discharge specific capacity reaches 95.7 mAh·g⁻¹ at 5 C rate. Iron doping offers a viable way to improve the electronic conductivity and lattice defects of materials, as well as improving transmission kinetics, thereby improving the rate performance and cycle performance of materials, which is an effective method to promote the electrical properties.     

静电自组装方法合成的具有多孔三维网络结构的Fe3O4/石墨烯复合材料作为高性能锂离子电池负极材料

采用静电自组装方法,分两步合成Fe（OH）₃/GO前驱体（GO：氧化石墨烯）,再通过水热反应和600 ℃高纯氮气气氛下煅烧,获得了Fe₃O₄/石墨烯复合材料. 通过X射线衍射（XRD）、扫描电镜（SEM）、高分辨透射电镜（HRTEM）、拉曼（Raman）光谱等多种分析,发现该复合材料具有三维多孔石墨烯网络结构. 把合成的这种Fe₃O₄/石墨烯复合材料作为锂离子电池负极材料,电化学测试结果表明其具有优良的电化学性能：首次放电容量为1390 mAh·g^-1,50次循环后容量为819 mAh·g^-1. 通过对比实验表明,三维石墨烯网络结构的形成对复合材料的电化学循环稳定性起着关键作用.     

Magnetic Nitrogen-Doped Porous Carbon Nanocomposite for Pb(II) Adsorption from Aqueous Solution

We report in the present study the in situ formation of magnetic nanoparticles (Fe₃O₄ or Fe) within porous N-doped carbon (Fe₃O₄/N@C) via simple impregnation, polymerization, and calcination sequentially. The synthesized nanocomposite structural properties were investigated using different techniques showing its good construction. The formed nanocomposite showed a saturation magnetization (M_s) of 23.0 emu g⁻¹ due to the implanted magnetic nanoparticles and high surface area from the porous N-doped carbon. The nanocomposite was formed as graphite-type layers. The well-synthesized nanocomposite showed a high adsorption affinity toward Pb²⁺ toxic ions. The nanosorbent showed a maximum adsorption capacity of 250.0 mg/g toward the Pb²⁺ metallic ions at pH of 5.5, initial Pb²⁺ concentration of 180.0 mg/L, and room temperature. Due to its superparamagnetic characteristics, an external magnet was used for the fast separation of the nanocomposite. This enabled the study of the nanocomposite reusability toward Pb²⁺ ions, showing good chemical stability even after six cycles. Subsequently, Fe₃O₄/N@C nanocomposite was shown to have excellent efficiency for the removal of toxic Pb²⁺ ions from water.     

多孔朵状Fe_3O_4纳米微球的制备及其性能研究

<正>众所周知,纳米材料的尺寸大小、晶型、形貌构型等结构特征对材料的化学物理性能有重要的影响[1],由于特殊形貌的新材料所具有独特、新颖、高效的化学物理等方面的性质以及在众多领域中的潜在应用[2],特别是3D花状空心纳米结构新物质[3-4],新形貌物质的纳米材料的制备方法和应用特性已经吸引了世界上材料领域的广泛兴趣和关注[5]。目前为止,合成3D纳米结构的方法有自组装法、三维导向连接法以及水热法等,即通过使用有     

Highly Porous Carbons Synthesized from Tannic Acid via a Combined Mechanochemical Salt-Templating and Mild Activation Strategy

Highly porous activated carbons were synthesized via the mechanochemical salt-templating method using both sustainable precursors and sustainable chemical activators. Tannic acid is a polyphenolic compound derived from biomass, which, together with urea, can serve as a low-cost, environmentally friendly precursor for the preparation of efficient N-doped carbons. The use of various organic and inorganic salts as activating agents afforded carbons with diverse structural and physicochemical characteristics, e.g., their specific surface areas ranged from 1190 m²·g⁻¹ to 3060 m²·g⁻¹. Coupling the salt-templating method and chemical activation with potassium oxalate appeared to be an efficient strategy for the synthesis of a highly porous carbon with a specific surface area of 3060 m²·g⁻¹, a large total pore volume of 3.07 cm³·g⁻¹ and high H₂ and CO₂ adsorption capacities of 13.2 mmol·g⁻¹ at −196 °C and 4.7 mmol·g⁻¹ at 0 °C, respectively. The most microporous carbon from the series exhibited a CO₂ uptake capacity as high as 6.4 mmol·g⁻¹ at 1 bar and 0 °C. Moreover, these samples showed exceptionally high thermal stability. Such activated carbons obtained from readily available sustainable precursors and activators are attractive for several applications in adsorption and catalysis.     

Ammonia-treatment assisted fully encapsulation of Fe2O3 nanoparticles in mesoporous carbons as stable anodes for lithium ion batteries

To improve the initial coulombic efficiency and bulk density of ordered mesoporous carbons, active Fe₂O₃ nanoparticles were introduced into tubular mesopore channels of CMK-5 carbon, which possesses high specific surface area (>1700 m²·g^?1) and large pore volume (>1.8 cm³·g^?1). Fine Fe₂O₃ nanoparticles with sizes in the range of 5–7 nm were highly and homogenously encapsulated into CMK-5 matrix through ammonia-treatment and subsequent pyrolysis method. The Fe₂O₃ loading was carefully tailored and designed to warrant a high Fe₂O₃ content and adequate buffer space for improving the electrochemical performance. In particular, such Fe₂O₃ and mesoporous carbon composite with 47 wt% loading exhibits a considerably stable cycle performance (683 mAh·g^?1 after 100 cycles, 99% capacity retention against that of the second cycle) as well as good rate capability. The fabrication strategy can effectively solve the drawback of single material, and achieve a high-performance lithium electrode material.     

SnO2 Quantum Dots Distributed along V2O5 Nanobelts for Utilization as a High-Capacity Storage Hybrid Material in Li-Ion Batteries

In this study, the facile synthesis of SnO₂ quantum dot (QD)-garnished V₂O₅ nanobelts exhibiting significantly enhanced reversible capacity and outstanding cyclic stability for Li⁺ storage was achieved. Electrochemical impedance analysis revealed strong charge transfer kinetics related to that of V₂O₅ nanobelts. The SnO₂ QD-garnished V₂O₅ nanobelts exhibited the highest discharge capacity of ca. 760 mAhg⁻¹ at a density of 441 mAg⁻¹ between the voltage ranges of 0.0 to 3.0 V, while the pristine V₂O₅ nanobelts samples recorded a discharge capacity of ca. 403 mAhg⁻¹. The high capacity of QD-garnished nanobelts was achieved as an outcome of their huge surface area of 50.49 m²g⁻¹ and improved electronic conductivity. Therefore, the as-presented SnO₂ QD-garnished V₂O₅ nanobelts synthesis strategy could produce an ideal material for application in high-performance Li-ion batteries.     

Supercritical Carbon Dioxide Assisted Deposition of Fe3O4 Nanoparticles on Hierarchical Porous Carbon and Their Lithium‐Storage Performance

A composite of highly dispersed Fe₃O₄ nanoparticles (NPs) anchored in three‐dimensional hierarchical porous carbon networks (Fe₃O₄/3DHPC) as an anode material for lithium‐ion batteries (LIBs) was prepared by means of a deposition technique assisted by a supercritical carbon dioxide (scCO₂)‐expanded ethanol solution. The as‐synthesized Fe₃O₄/3DHPC composite exhibits a bimodal porous 3D architecture with mutually connected 3.7 nm mesopores defined in the macroporous wall on which a layer of small and uniform Fe₃O₄ NPs was closely coated. As an anode material for LIBs, the Fe₃O₄/3DHPC composite with 79 wt % Fe₃O₄ (Fe₃O₄/3DHPC‐79) delivered a high reversible capacity of 1462 mA h g^?1 after 100 cycles at a current density of 100 mA g^?1, and maintained good high‐rate performance (728, 507, and 239 mA h g^?1 at 1, 2, and 5 C, respectively). Moreover, it showed excellent long‐term cycling performance at high current densities, 1 and 2 A g^?1. The enhanced lithium‐storage behavior can be attributed to the synergistic effect of the porous support and the homogeneous Fe₃O₄ NPs. More importantly, this straightforward, highly efficient, and green synthetic route will definitely enrich the methodologies for the fabrication of carbon‐based transition‐metal oxide composites, and provide great potential materials for additional applications in supercapacitors, sensors, and catalyses.     

Preparation of Bamboo-Based Hierarchical Porous Carbon Modulated by FeCl3 towards Efficient Copper Adsorption

Using bamboo powder biochar as raw material, high-quality meso/microporous controlled hierarchical porous carbon was prepared—through the catalysis of Fe³⁺ ions loading, in addition to a chemical activation method—and then used to adsorb copper ions in an aqueous solution. The preparation process mainly included two steps: load-alkali leaching and chemical activation. The porosity characteristics (specific surface area and mesopore ratio) were controlled by changing the K₂CO₃ impregnation ratio, activation temperature, and Fe³⁺ ions loading during the activation process. Additionally, three FBPC samples with different pore structures and characteristics were studied for copper adsorption. The results indicate that the adsorption performance of the bamboo powder biochar FBPC material was greatly affected by the meso/micropore ratio. FBPC _2.5-900-2%, impregnated at a K₂CO₃: biochar ratio of 2.5 and a Fe³⁺: biochar mass ratio of 2%, and activated at 900 °C for 2 h in N₂ atmosphere, has a very high specific surface area of 1996 m² g⁻¹ with a 58.1% mesoporous ratio. Moreover, it exhibits an excellent adsorption capacity of 256 mg g⁻¹ and rapid adsorption kinetics for copper ions. The experimental results show that it is feasible to control the hierarchical pore structure of bamboo biochar-derived carbons as a high-performance adsorbent to remove copper ions from water.     

Confined Nanospace Pyrolysis for the Fabrication of Coaxial Fe3O4@C Hollow Particles with a Penetrated Mesochannel as a Superior Anode for Li‐Ion Batteries

In this study, a method is developed to fabricate Fe₃O₄@C particles with a coaxial and penetrated hollow mesochannel based on the concept of “confined nanospace pyrolysis”. The synthesis involves the production of a polydopamine coating followed by a silica coating on a rod‐shaped β‐FeOOH nanoparticle, and subsequent treatment by using confined nanospace pyrolysis and silica removal procedures. Typical coaxial hollow Fe₃O₄@C possesses a rice‐grain morphology and mesoporous structure with a large specific surface area, as well as a continuous and flexible carbon shell. Electrochemical tests reveal that the hollow Fe₃O₄@C with an open‐ended nanostructure delivers a high specific capacity (ca. 864 mA h g^?1 at 1 A g^?1), excellent rate capability with a capacity of about 582 mA h g^?1 at 2 A g^?1, and a high Coulombic efficiency (>97 %). The excellent electrochemical performance benefits from the hollow cavity with an inner diameter of 18 nm and a flexible carbon shell that can accommodate the volume change of the Fe₃O₄ during the lithium insertion/extraction processes as well as the large specific surface area and open inner cavity to facilitate the rapid diffusion of lithium ions from electrolyte to active material. This fabrication strategy can be used to generate a hollow or porous metal oxide structure for high‐performance Li‐ion batteries.     

Graphitized carbon and graphene modified Fe2O3/Li4Ti5O12 as anode material for lithium ion batteries

Graphitized carbon (GC) and graphene (GE) modified Fe₂O₃/Li₄Ti₅O₁₂ (LTO) composites have been synthesized via a solid‐state reaction, respectively. The structure, morphology and electrochemical performance of the materials have also been characterized with X‐ray diffraction (XRD), scanning electron microscope (SEM) with an energy dispersive spectroscopy (EDS) system, X‐ray photoelectron spectrometer (XPS), Fourier transform infrared spectroscopy (FTIR) and electrochemical measurements. The discharge capacities of Fe₂O₃/LTO, GC/Fe₂O₃/LTO and GE/Fe₂O₃/LTO are 100.2 mAh g^?1, 207.5 mAh g^?1 and 238.9 mAh g^?1 after 100 cycles at the current density of 176 mA g^?1. The cyclic stability and rate capability are in the order of GE/Fe₂O₃/LTO > GC/Fe₂O₃/LTO > Fe₂O₃/LTO because of the synergistic effect between GC (GE) and Fe₂O₃/LTO. Copyright © 2016 John Wiley & Sons, Ltd.     

Synthesis of porous C/Fe3O4 microspheres by spray pyrolysis with NaNO3 additive for lithium-ion battery applications

In this work, we successfully synthesized porous C/Fe₃O₄ microspheres by spray pyrolysis at 700ºC with a sodium nitrate (NaNO₃) additive in the precursor solution. Furthermore, we studied their electrochemical properties as anode material for Li-ion batteries. The systematic studies by various characterization techniques show that NaNO₃ catalyzes the carbonization of sucrose and enhances the crystallization of Fe₃O₄. Moreover, an aqueous etching can easily remove sodium compounds to produce porous C/Fe₃O₄ microspheres with large surface areas and pore volumes. The porous C/Fe₃O₄ microspheres exhibit a reversible capacity of ~780 mAh g^–1 in the initial cycles and ~520 mAh g^–1 after 30 cycles at a current density of 50 mA g^–1. Moreover, a reversible capacity of ~400 mAh g^–1 is attainable after 200 cycles, even at a high current density of 500 mA g^–1. The wide range of pores produced from the removal of sodium compounds might enable easy electrolyte penetration and facilitate fast Li-ion diffusion, while the N-doping can promote the electronic conductivity of the carbon. These features of porous C/Fe₃O₄ microspheres led to the improved electrochemical properties of this sample.

Graphical Abstract

     

Synthesis and characterization of Fe2O3/SiO2 nanocomposites

Fe₂O₃/SiO₂ nanocomposites based on fumed silica A-300 (S_BET = 337 m²/g) with iron oxide deposits at different content were synthesized using Fe(III) acetylacetonate (Fe(acac)₃) dissolved in isopropyl alcohol or carbon tetrachloride for impregnation of the nanosilica powder at different amounts of Fe(acac)₃ then oxidized in air at 400–900 °C. Samples with Fe(acac)₃ adsorbed onto nanosilica and samples with Fe₂O₃/SiO₂ including 6–17 wt% of Fe₂O₃ were investigated using XRD, XPS, TG/DTA, TPD MS, FTIR, AFM, nitrogen adsorption, Mössbauer spectroscopy, and quantum chemistry methods. The structural characteristics and phase composition of Fe₂O₃ deposits depend on reaction conditions, solvent type, content of grafted iron oxide, and post-reaction treatments. The iron oxide deposits on A-300 (impregnated by the Fe(acac)₃ solution in isopropanol) treated at 500–600 °C include several phases characterized by different nanoparticle size distributions; however, in the case of impregnation of A-300 by the Fe(acac)₃ solution in carbon tetrachloride only α-Fe₂O₃ phase is formed in addition to amorphous Fe₂O₃. The Fe₂O₃/SiO₂ materials remain loose (similar to the A-300 matrix) at the bulk density of 0.12–0.15 g/cm³ and S_BET = 265–310 m²/g.     

Nanosized Fe3O4-modified activated carbon for supercapacitor electrodes

Nanosized Fe₃O₄-modified activated carbon composites for supercapacitor electrodes have been investigated. Structural and morphological characterizations of activated materials are carried out using X-ray diffraction and scanning electron microscopy, respectively. The electrochemical performances of the composite electrodes are evaluated by cyclic voltammetry, chronopotentiometry and electrochemical impedance spectroscopy. The experimental results show that the specific capacitances of the 10 wt % Fe₃O₄-modified activated carbon composite electrode (154.3 F g^?1) is highly improved compared with that of Fe₃O₄ (78.5 F g^?1) and AC (79.2 F g^?1) at the current density of 5 mA cm^?2, respectively. The charge/discharge tests show that it could retain 79.6% of its initial capacitance over 1000 cycles, suggesting its potential application for the fabrication of high-quality supercapacitors.     

Fe3O4/Graphene Composite Anode Material for Fast-Charging Li-Ion Batteries

Composite anode material based on Fe₃O₄ and reduced graphene oxide is prepared by base-catalysed co-precipitation and sonochemical dispersion. Structural and morphological characterizations demonstrate an effective and homogeneous embedding of Fe₃O₄ nanoparticles in the carbonaceous matrix. Electrochemical characterization highlights specific capacities higher than 1000 mAh g⁻¹ at 1C, while a capacity of 980 mAhg⁻¹ is retained at 4C, with outstanding cycling stability. These results demonstrate a synergistic effect by nanosize morphology of Fe₃O₄ and inter-particle conductivity of graphene nanosheets, which also contribute to enhancing the mechanical and cycling stability of the electrode. The outstanding capacity delivered at high rates suggests a possible application of the anode material for high-power systems.     

Removal of Cd(II) from Micro-Polluted Water by Magnetic Core-Shell Fe3O4@Prussian Blue

A novel core-shell magnetic Prussian blue-coated Fe₃O₄ composites (Fe₃O₄@PB) were designed and synthesized by in-situ replication and controlled etching of iron oxide (Fe₃O₄) to eliminate Cd (II) from micro-polluted water. The core-shell structure was confirmed by TEM, and the composites were characterized by XRD and FTIR. The pore diameter distribution from BET measurement revealed the micropore-dominated structure of Fe₃O₄@PB. The effects of adsorbents dosage, pH, and co-existing ions were investigated. Batch results revealed that the Cd (II) adsorption was very fast initially and reached equilibrium after 4 h. A pH of 6 was favorable for Cd (II) adsorption on Fe₃O₄@PB. The adsorption rate reached 98.78% at an initial Cd (II) concentration of 100 μg/L. The adsorption kinetics indicated that the pseudo-first-order and Elovich models could best describe the Cd (II) adsorption onto Fe₃O₄@PB, indicating that the sorption of Cd (II) ions on the binding sites of Fe₃O₄@PB was the main rate-limiting step of adsorption. The adsorption isotherm well fitted the Freundlich model with a maximum capacity of 9.25 mg·g⁻¹ of Cd (II). The adsorption of Cd (II) on the Fe₃O₄@PB was affected by co-existing ions, including Cu (II), Ni (II), and Zn (II), due to the competitive effect of the co-adsorption of Cd (II) with other co-existing ions.     

Sensitive electrochemical immunoassay for chlorpyrifos by using flake-like Fe3O4 modified carbon nanotubes as the enhanced multienzyme label

A highly sensitive electrochemical immunoassay of chlorpyrifos (CPF) was developed by using a biocompatible quinone-rich polydopamine nanospheres modified glass carbon electrode as the sensor platform and multi-horseradish peroxidase-flake like Fe₃O₄ coated carbon nanotube nanocomposites as the signal label. Due to the quinone-rich polydopamine nanospheres, the platform exhibited excellent fixing capacity by simple coating of sticky polydopamine nanospheres and subsequent oxidization. By coprecipitation of Fe³⁺ and Fe²⁺ on polydopamine modified carbon nanotubes (CNTs) with the aid of ethylene glycol (EG), the flake-like Fe₃O₄ coated CNTs (CNTs@f-Fe₃O₄) were synthesized and chosen as the carrier of multi-enzyme label due to the high loading of secondary antibody (Ab₂) and horseradish peroxidase (HRP) and also the peroxidase-mimic activity of Fe₃O₄. Under the optimum conditions, the immunosensor can detect CPF over a wide range with a detection limit of 6.3 pg/mL. Besides, the high specificity, reproducibility and stability of the proposed immunosensor were also proved. The preliminary application in real sample showed good recoveries, indicating it holds promise for fast analysis of CPF in aquatic environment.