Dispersion of Ni^（2＋） Supported on Carbon Covered Alumina Surface and Hydrogenation Performance

采用等体积浸渍法制备了以炭包覆氧化铝（CCA）为载体的Ni基催化剂.利用低温N2物理吸附、XRD、UV-Vis DRS、H2-TPR、H2-TPD等手段对催化剂进行表征,并考察了催化剂粗1,4-丁二醇加氢反应性能.结果表明,均匀分散在表面的炭可以有效阻止Ni2＋进入氧化铝表面四面体及八面体空位,Ni2＋以与载体具有中等强度相互作用的物种形式存在.随Ni含量的增加,镍物种晶粒尺寸发生明显变化,当Ni含量低于10%时,NiO以高分散状态存在于载体表面,Ni含量达到14%时催化剂中出现了NiO微晶,进一步提高Ni含量,NiO晶粒尺寸有所长大,但仍保持了较高的分散度.由于Ni的聚集程度较小,随着Ni含量增加,Ni的总活性比表面积增加,催化剂加氢活性提高,至Ni含量达17%时,催化剂表现出最佳的催化加氢活性.     

Ni/SiO_2、Ni/TiO_2-SiO_2催化剂上顺酐液相选择加氢合成γ-丁内酯

通过溶胶-凝胶方法结合超临界干燥技术制备了SiO2和TiO2-SiO2复合氧化物气凝胶载体,采用等体积浸渍法制备了Ni/SiO2和Ni/TiO2-SiO2催化剂,运用BET、H2-TPR、XRD、TEM及FT-IR等手段对催化剂进行了表征,并考察了催化剂在顺酐液相选择加氢合成γ-丁内酯反应中的催化性能.结果表明,Ni/TiO2-SiO2催化剂中Ti-O-Si键的形成增强了NiO与载体的相互作用,促进了NiO在载体表面的分散,得到了晶粒较小的活性Ni0物种,表现出高的加氢活性,在H2压力5.0 MPa、反应温度240℃、反应时间6 h的条件下,顺酐转化率为100%,γ-丁内酯的选择性达94.7%.     

助剂对Ni/SiO_2催化剂微观结构及二硝基甲苯催化加氢性能的影响

采用等体积浸渍法制备了负载型Ni/SiO2催化剂,研究了Ce、Zr、La、Co和Fe助剂对催化剂微观结构及其催化二硝基甲苯(DNT,C6H3CH3(NO2)2)加氢制备甲苯二胺(TDA,C6H3CH3(NH2)2)性能的影响。通过XRD,BET,H2-TPD、H2-TPR和XPS技术对催化剂进行了表征。结果表明,助剂的引入促进了Ni物种在载体表面的分散,减小了Ni晶粒的尺寸,使得NiO晶粒更易还原。添加La、Fe和Zr助剂增加了有效的Ni活性中心数,有利于催化活性的提高,其中,添加La助剂制备的催化剂催化性能最优,DNT转化率和TDA选择性分别为98.1%和99.1%。但Co和Ce助剂的加入降低了化学氢吸附量,使得有效的Ni活性中心数降低,降低了催化剂的催化活性。     

焙烧及还原温度对对硝基苯酚加氢合成对氨基苯酚Ni/TiO2催化剂性能的影响

采用等体积浸渍法制备了Ni/TiO2催化剂,考察了焙烧和还原温度对其结构及催化对硝基苯酚加氢合成对氨基苯酚反应性能的影响,利用X射线衍射、程序升温还原及H2化学吸附等方法对催化剂进行了表征.结果表明,923 K以下焙烧制备的催化剂中镍物种主要以与载体相互作用不同的NiO形式存在,随着焙烧温度的升高,催化剂中NiO与TiO2间的相互作用增强.经723 K还原后,随焙烧温度升高,催化剂的H2化学吸附量减小,而923 K焙烧的催化剂具有较佳的加氢反应性能,这与金属镍和TiOx(x<2)的协同作用有关.对于923 K焙烧的催化剂,当还原温度较低时,NiO还原不完全,金属镍与TiOx的相互作用较弱,催化剂活性较低;当还原温度过高时,镍晶粒发生烧结,并且催化剂的镍活性表面因镍与TiOx的相互作用增强而减小,从而导致催化剂活性降低,适宜的还原温度为673 K.当Ni/TiO2催化剂具有适宜的镍活性表面及适宜的金属镍与TiOx相互作用时,金属镍与TiOx的协同对-NO2的加氢活化最为有利.     

氮气气氛下焙烧的CeO_2载体负载Ni基催化剂的顺酐加氢性能研究

在氮气气氛中合成了具有较高氧缺陷浓度的CeO_2载体,采用浸渍法制备了Ni含量为10%的Ni/CeO_2-N催化剂,考察了其顺酐液相加氢性能,并与氧气气氛中制得的CeO_2载体负载Ni催化剂作了对比.N_2低温物理吸脱附,X-射线衍射,拉曼光谱,H_2程序升温还原等表征手段表明,在氮气气氛中合成的CeO_2具有较高浓度的氧缺陷位,在催化剂还原过程中可促进NiO物种的还原,同时在催化剂表面生成更多的氧缺陷位.该氧缺陷位可与活性金属Ni物种协同作用,显著提高催化剂的C=C及C=O加氢活性.     

Ni/HZSM-5催化剂的结构及其催化山梨醇水相加氢合成烷烃性能

采用浸渍法制备了Ni/HZSM-5双功能催化剂,考察了焙烧温度对催化剂结构及其催化山梨醇水相加氢合成C5～C6烷烃性能的影响.结果表明,在金属中心和酸性载体的协同作用下,通过山梨醇中C-O键加氢和异构化高选择性合成了C5～C6烷烃.经500°C焙烧的Ni/HZSM-5催化剂上山梨醇水相加氢的活性最高,山梨醇转化率为62.0%,戊烷和己烷的总选择性为76.4%,其中异己烷选择性达45.4%.对催化剂进行N2物理吸附、X射线衍射、NH3程序升温脱附和H2程序升温还原等表征后发现,经500°C焙烧催化剂的有效比表面积和孔体积均明显增大,HZSM-5负载的硝酸镍分解成较小晶粒的NiO,表面酸量适中,且Ni物种与载体相互作用较强,较易被H2还原,Ni还原度达100%.这是其催化活性最高的原因.     

负载Ni催化剂上1,4-丁炔二醇加氢反应的载体效应研究

制备了Ni负载量为15%的3种催化剂Ni/Al_2O_3、Ni/SiO_2、Ni/ZrO_2,考察了其在1,4-丁炔二醇加氢反应中的催化性能,结合XRD、H_2-TPR、H_2-TPD、N_2物理吸附等表征,研究了载体性质对催化剂1,4-丁炔二醇加氢性能的影响.结果表明,Ni/SiO_2催化剂上,由于Ni与SiO_2间弱的相互作用,Ni物种主要以大晶粒形式存在,产生大量弱吸附H_2物种,有利于低温下1,4-丁炔二醇加氢,在温度50℃,氢气压力1 MPa时,反应2 h可实现1,4-丁炔二醇的完全转化,1,4-丁烯二醇和1,4-丁二醇选择性分别达到68.1%与18.2%.Ni/Al_2O_3中Ni与载体间具有强相互作用,主要存在Ni-Al_2O_3界面或溢流到Al_2O_3载体表面的强吸附H_2物种,而Ni表面的弱吸附H_2物种较少,催化加氢活性明显降低.Ni/ZrO_2中由于还原过程中ZrO_2的迁移包裹作用,Ni表面低温吸附H_2物种最少,活性最低,1,4-丁炔二醇转化率仅为8.1%,主产物为1,4-丁烯二醇.     

柠檬酸添加方式对Mo-Ni-P/Al_2O_3催化剂加氢活性的影响

以Mo、Ni为活性组分,Al_2O_3为载体,采用不同柠檬酸添加方法制备了Mo-Ni-P/Al_2O_3催化剂.通过氢气程序升温还原(H2-TPR)、X射线衍射(XRD),透射扫描电镜(TEM)、XPS等表征方法研究催化剂的物化性质.结果表明:催化剂经柠檬酸的后处理,改善了载体氧化铝表面羟基基团的分布,促使Mo物种以八面体配位多核聚钼酸的形态存在,有效地减弱了载体与活性金属之间的强相互作用,提高了Mo物种的分散度与硫化度,使得催化剂形成更多"Mo-Ni-S"加氢活性相,提高了催化剂的加氢活性.与其他处理方法相比,柠檬酸后处理的催化剂对VGO具有更高的加氢脱硫、脱氮与芳烃饱和性能.     

残留Na对镍催化剂加氢性能的影响

采用共沉淀的方法制备了以镍为活性组分、镁为助剂、 SiO_2为载体的Ni-Mg/SiO_2催化剂,以大豆油加氢为探针反应研究催化剂中残留Na的含量对加氢活性的影响.分别用ICP-AES、 XRD、 H_2-TPR、 TG-DSC、 SEM、 BET等手段对不同催化剂进行了表征.结果表明:催化剂中残留Na对加氢活性有很大影响, Na含量为6.86%时,催化剂基本没有活性.随Na含量的降低,催化剂活性逐渐升高.这主要是由于Na对Ni的分散、颗粒尺寸和与载体相互作用有较大的影响有关.     

CrOx/SiO2催化剂对C10+芳烃加氢脱烷基反应的催化性能

 采用等体积浸渍法制备了一系列不同组成的CrOx/SiO2催化剂样品,并用XRD,FT-IR,UV-Vis,TPR和N2吸附等技术对催化剂样品进行了表征,考察了催化剂对C10+重芳烃加氢脱烷基反应的催化性能. 结果表明,CrOx/SiO2催化剂对C10+重芳烃加氢脱烷基反应的催化性能与催化剂的表面结构有关,脱烷基活性主要来自载体表面的CrOx物种. 当催化剂中n(Cr)/n(Si)=1%～2%时,CrOx在SiO2表面达到单层分散; 当n(Cr)/n(Si)=2%～20%时,表面CrOx物种含量的变化不大,催化剂的活性及选择性基本不变.     

流化床甲烷部分氧化制合成气Ni催化剂及助剂La的作用

在流化床中,考察了不同Ni担载量的Ni/γ-Al2O3催化剂对POM反应的催化性能,以8％Ni最佳,TPR结果表明。催化剂表面主要有两种化学状态的NiO。当镍担载量≤2％时,催化剂表面 仅存在一种高温下才能被还原的NiO,在Ni催化剂中添加La,可削弱NiO与载体间的相互作用,并且可减缓在CH4＋O2气氛下升温过程中NiO与载体发生强相互作用 生成NiAl2O4,因此添加La的Ni催化剂在750℃就能引发甲烷部分氧化（POM）反应,且反应引发后可获得与经700℃H2还原后的Ni^0催化剂相同的反应性能。     

Selective catalytic methanation of CO in hydrogen-rich gases over Ni/ZrO2 catalyst

Ni/ZrO2 catalysts were prepared by the incipient-wetness impregnation method and were investigated in activity and selectivity for the selective catalytic methanation of CO in hydrogen-rich gases with more than 20 vol% CO2. The result showed that Ni loadings significantly influenced the performance of Ni/ZrO2 catalyst. The 1.6 wt% Ni loading catalyst exhibited the highest catalytic activity among all the catalysts in the selective methanation of CO in hydrogen-rich gas. The outlet concentration of CO was less than 20 ppm with the hydrogen consumption below 7%, at a gas-hourly-space velocity as high as 10000 h-1 and a temperature range of 260 °C to 280 °C. The X-ray diffraction （XRD） and temperature programmed reduction （TPR） measurements showed that NiO was dispersed thoroughly on the surface of ZrO2 support if Ni loading was under 1.6 wt%. When Ni loading was increased to 3 wt% or above, the free bulk NiO species began to assemble, which was not favorable to increase the selectivity of the catalyst.     

Effect of Cu promoter on Ni-based SBA-15 catalysts for partial oxidation of methane to syngas

A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and H2-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ◦C the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.     

制备条件对Ni/ZrO2-SiO2催化剂煤气甲烷化的影响

采用浸渍法制备了ZrO₂-SiO₂复合载体和Ni质量分数为6%的Ni/ZrO₂-SiO₂催化剂,考察了载体制备时浸渍溶液pH值、焙烧温度和催化剂制备时的焙烧温度对Ni/ZrO₂-SiO₂催化剂煤气甲烷化反应性能的影响。采用X射线衍射、程序升温还原和扫描电子显微镜等方法对催化剂进行了表征。结果表明,载体浸渍溶液pH值为8.0～9.0, 载体焙烧温度为550 ℃,催化剂焙烧温度为450 ℃时,Ni/ZrO₂-SiO₂催化剂在煤气甲烷化反应中显示了最优的催化性能,CO转化率100%,CO₂转化率1.8%,CH₄生成速率16.6 mmol/(h·g)。进一步表征发现,制备ZrO₂-SiO₂复合载体时,增大浸渍溶液的pH值有利于形成粒径较小的亚稳态四方晶相ZrO₂,可见四方晶相ZrO₂更有利于甲烷化反应;载体焙烧温度会影响到NiO粒径的大小和其在催化剂表面的分散,温度过高和过低都会导致NiO粒径大小的不适宜以及分散性的降低;催化剂焙烧温度过高则会导致NiO与载体间的相互作用减弱,NiO分散性降低。     

Autothermal reforming of methane over Ni catalysts supported over ZrO2-CeO2-Al2O3

Ni catalysts supported on Al2O3, ZrO2-Al2O3, CeO2-Al2O3 and ZrO2-CeO2-Al2O3 were prepared by coprecipitation method, and their catalytic performances for autothermal reforming of methane to hydrogen were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. The relationship between the structures and catalytic activities of the catalysts was discussed. The results showed that the catalytic activity and stability of the Ni/ZrO2-CeO2-Al2O3 catalyst was better than those of other catalysts with the highest CH4 conversion, H2/CO and H2/COx ratio at 750 ℃. The catalyst showed a little deactivation along the reaction time during its 72 h on stream with the mean deactivation rate of 0.08%/h. The catalytic performance of the Ni/ZrO2-CeO2-Al2O3 catalyst was also affected by reaction temperature, no2 ： nCH4 molar ratio and nH2O ： nCH4 molar ratio. TPR, XRD and XPS measurements indicated that the formation of ZrO2-CeO2 solid solution could improve the dispersion of NiO, and inhibit the formation of NiAl2O3, and thus significantly promoted the catalytic activity of the Ni/ZrO2-CeO2-Al2O3 catalyst.     

Ni/Ce-Zr-Al-O催化剂的表面碱性和CO2＋CH4重整性能

用水热法制备了不同NiO含量的Ni/Ce-Zr-Al-O催化剂.用H2-TPD (程序升温脱附),DRIFTS(漫反射红外傅立叶变换光谱),CO2-TPD等方法考察了NiO的含量对催化剂表面碱性的影响,并和反应稳定性以及抗积碳性能相关联.H2-TPD结果表明,随NiO含量的增加,催化剂表面的Ni含量增加.DRIFT和CO2-TPD结果表明CO2的化学吸附主要是碳酸盐和碳酸氢盐形式.添加少量Ni能够使表面碱性位数量显著增加,碱强度减弱.Ni可能优先占据在催化剂表面较强的碱性位上,再增加Ni的含量则会使碱强度减弱,碱性位有所减少,降低CO2的吸附性能,从而减弱从CO2获得活动氧以消碳的能力.这种作用使NiO含量为7.0％(w)的样品活性随反应进行而减低,积碳量是NiO含量为4.0％(w)的样品的3.7倍.     

NiO/WO3/TiO2-Al2O3催化剂上正庚烷的临氢异构化

采用溶胶凝胶法制备了TiO2-Al2O3复合载体,用分步浸渍法制备了NiO/WO3/TiO2-Al2O3催化剂。 在常压连续流动固定床反应器上考察了NiO/WO3/TiO2-Al2O3对正庚烷临氢异构化反应的催化性能。 研究了催化剂中WO3含量、Ni含量、焙烧温度和还原温度及催化反应温度对临氢异构化反应的影响。 采用XRD和BET方法对催化剂进行了表征。 结果表明,当w(WO3)=25%、w(Ni)=10%时,所制备的NiO/WO3/TiO2-Al2O3催化剂对正庚烷异构化反应的催化性能最好,活性可达15.50%,选择性可达84.06%。     

溶胶—凝胶法制备NiO／SiO2催化剂研究

分别以正硅酸乙酯、硝酸镍为硅源和镍源,采用溶胶－凝胶法,经超临界流体干燥和普通干燥制备了NiO-A-SiO2、NiO-G-SiO2催化剂;以气凝胶和干凝胶为载体,采用浸渍法制备了NiO/A-SiO2、NiO/G-SiO2催化剂。并用XRD、TEM、BET、TPR等手段,研究了制备方法对催化剂织构、结构和Ni物种存在形态的影响,发现NiO-A-SiO2和NiO-G-SiO2催化剂上高度分散的NiO簇团与SiO2之间有较强的相互作用,其顺酐液相选择加氢转化率低于10％;NiO/G-SiO2催化剂上,以单一物种形态存在的NiO与SiO2相互作用弱,顺酐转化率为42％;NiO/A-SiO2催化剂上,以多种形态存在的微量NiO与SiO2间的相互作用较复杂,其顺酐液相选择加氢的转化率和丁二酸酐的选择性分别可达100％和98％。     

NiO/LaMnO3催化剂用于乙醇水蒸气重整反应

采用柠檬酸络合-浸渍法制备了NiO/LaMnO3钙钛矿型复合氧化物催化剂并将其应用于乙醇水蒸汽重整制氢反应, 考察了NiO含量、焙烧温度对催化剂性能的影响, 采用XRD、TPR和热分析等手段对催化剂进行了表征. 结果表明, 该催化剂具有高活性、高选择性和良好的稳定性. 催化剂中的NiO含量和焙烧温度对催化性能有显著影响. 在原料气体积组成为20%(体积分数, φ) C2H5OH 和水以及80%(φ)N2, 其中水醇摩尔比为3:1, 空速为80000 mL·h-1·g-1 cat, 反应温度为400 ℃时, 15%(质量分数, w)的NiO/LaMnO3上, 乙醇转化率接近100%. 关联催化剂活性和TPR及XRD实验结果, 发现催化剂的高活性源于由催化剂前驱体中进入钙钛矿型复合氧化物晶格中的镍离子被还原所得的金属镍.     

镁铝混合氧化物负载镍催化剂上液化石油气的预重整

采用共沉淀-浸渍法并在较低温度(400～700℃)下焙烧制备了镁铝混合氧化物(MgmAl)负载的Ni催化剂.X射线衍射和程序升温还原结果表明,Ni物种高度分散于催化剂表面,没有形成尖晶石NiAl2O4.在650℃可被还原成金属Ni纳米晶粒,在400℃和较低水/碳摩尔比(S/C=2)条件下表现出较好的催化液化石油气(LP...