铬和硫共掺杂二氧化钛催化剂的制备及其可见光催化性能

以钛酸四丁酯为前驱体,硝酸铬和硫脲为掺杂离子给体,通过溶胶-凝胶法成功制备了纯TiO2、不同浓度的铬掺杂和铬/硫共掺杂TiO2光催化剂.以靛红为目标污染物,进行了可见光催化降解活性测试实验.结果表明,共掺杂催化剂的活性高于未掺杂和单掺杂催化剂.当共掺杂催化剂含0.60%(原子比)的铬,1.2%(原子比)的硫,焙烧温度为500℃时具有最高的光催化降解活性.X射线衍射、N2吸附、X射线光电子能谱和紫外-可见漫反射吸收光谱表征结果显示,共掺杂催化剂为锐钛矿型,具有较高的比表面积,对可见光有较强的吸收能力.共掺杂TiO2具备较高可见光催化活性的原因可能是铬掺杂降低了TiO2的禁带宽度,拓展了可见光吸收区域,而硫掺杂能够维持体系的电荷平衡,增强催化剂对可见光的吸收.     

N掺杂TiO_2纳米粉体的制备及其可见光催化性能

首次以钛酸纳米管(NTA)为Ti的前驱体,以尿素为N源,采用水热法制备N掺杂TiO2纳米微粒,并用X射线衍射仪(XRD)、X射线光电子能谱仪(XPS)、紫外-可见漫反射光谱仪(UV-Vis DRS)、透射电镜(TEM)、傅立叶变换红外光谱(FT-IR)等技术对不同条件下制备的产物进行了表征.探讨了尿素的掺杂量、水热温度对N掺杂TiO2形貌和结构的影响,并以亚甲基蓝为模型反应物考察了其在可见光下的催化性能,结果表明样品UN-130-1/2催化活性最高.     

锌掺杂TiO_2的制备及其可见光催化性能

以钛酸纳米管[H2Ti2O2(OH)2,NTA]作为钛的前驱体、ZnCl2为锌源,采用水热法制备了锌掺杂的TiO2光催化剂;采用X射线衍射仪和透射电镜分析了催化剂产物的晶体结构和微观形貌;同时以亚甲基蓝为模型反应物,研究了锌掺杂量和水热温度对催化剂可见光光催化性能的影响.结果表明,水热温度为130℃,锌掺杂量为0.5%时,所得样品的光催化性能最佳.     

水热法制备铂掺杂二氧化钛及其可见光催化性能

以纳米管钛酸为前驱体,采用水热法制备了Pt掺杂TiO2样品.水热反应过程中,纳米管钛酸表面羟基与氯铂酸发生酸碱中和反应,导致反应后pH值升高;在130°C开始纳米管钛酸晶体结构由正交晶系转变为锐钛矿相TiO2.表面化学组成分析表明,掺杂的Pt主要以+2价形式存在.以丙烯为模型污染物,评价样品的可见光(λ≥420nm)光催化活性.结果表明,Pt-TiO2具有明显的可见光光催化降解丙烯的活性,其中160°C水热处理制得的Pt-TiO2活性最高.最后讨论了低温水热法Pt掺杂的形成机理及Pt-TiO2具有可见光响应的原因.     

LiF掺杂TiO2的制备及其光催化性能

采用溶胶-凝胶法制备了LiF掺杂的TiO2光催化剂,并采用X射线衍射、X射线光电子能谱和光致发光光谱等技术对样品进行了表征.以亚甲基蓝的光催化降解为反应模型,考察了LiF掺杂量、退火温度和溶液pH值对催化剂光催化性能的影响.结果表明,LiF的掺杂降低了金红石相的形成温度,同时在TiO2表面引入大量羟基氧并提高了TiO2表面氧空穴浓度,因此提高了TiO2的光催化性能.在LiF掺杂量为8%,退火温度为500℃和反应液pH值为6.6的条件下,LiF掺杂的TiO2的光催化活性是未掺杂TiO2的6倍.     

In离子掺杂二氧化钛纳米管可见光催化活性的研究

采用两步预掺杂方法制备出In离子掺杂二氧化钛纳米管可见光催化剂. 可见光催化降解对氯苯酚实验证明: 掺杂In离子量为3%的TiO2纳米管可见光活性最高, 是纯TiO2纳米管的2倍以上. X射线衍射(XRD), X光电子能谱(XPS)和表面光电压谱(SPS)结果表明: 当In离子掺杂浓度较小时, In离子取代晶格Ti的位置形成InxTi1－xO2取代式掺杂结构. In离子的掺杂能级与Ti离子的3d轨道形成混合价带, 使禁带宽度变窄, 增强了可见光响应. 随着In离子掺杂浓度的增加, 同时在InxTi1－xO2纳米管表面生成In2O3, 形成InxTi1－xO2/In2O3纳米管复合结构. 该复合结构有效地增加可见光响应, 促进了光生载流子的分离, 提高了光生载流子在固/液界面参加光催化反应的利用率, 使纳米管催化剂可见光催化活性显著提高.     

掺硼纳米TiO_2对农药毒死蜱的光催化降解作用

采用溶胶-凝胶法制备了掺杂硼的纳米TiO2,并用X射线衍射、红外光谱表征了产物的组成和结构.用制备好的掺硼纳米TiO2作为光催化剂对农药毒死蜱进行了光催化降解研究.结果表明:通过掺硼可以显著提高TiO2对毒死蜱的光催化效率.在硼掺杂量为3%,催化剂煅烧温度为500℃,煅烧时间为1 h,催化剂用量为15%时,毒死蜱的降解率最高.     

Ni^2＋／TiO2介孔材料光催化降解造纸废水影响因素的研究

溶胶-凝胶法合成了不同Ni掺杂量的Ni2 /TiO2介孔复合材料.用X射线衍射(XRD)、透射电子显微镜(TEM)、红外(FT - IR)光谱和N2吸附脱附等对产物结构进行了表征.考察了Ni掺杂量、催化剂的用量、初始pH、外加氧化剂等因素对光催化降解造纸废水的影响.结果表明: Ni2 /TiO2介孔复合材料光催化降解造纸废水的最佳反应条件为:Ni掺杂量为2%、催化剂用量1.5g/L、初始pH=4、通氧;光照4 h后,废水色度去除率达100%; 12 h后,废水CODCr去除率达到83.4%.     

Pt助剂对N掺杂TiO2可见光光催化性能的影响

考察了Pt促进的N掺杂TiO2(Pt/N-TiO2)催化剂对光催化降解有机污染物性能的影响及其作用本质.采用X射线衍射、透射电镜、X射线光电子能谱、紫外-可见漫反射光谱、光电化学和荧光光谱等手段对催化剂进行了表征,并考察了样品在可见光下光催化降解甲基橙(MO)的反应性能.结果表明,Pt的存在并未明显改变N-TiO2的晶...     

N掺杂富含(001)晶面TiO_2纳米片的制备及N掺杂浓度对可见光催化活性的影响(英文)

采用水热法制备了富含(001)晶面的锐钛矿型TiO2纳米片,并通过改变热处理过程中NH3流速制备不同N掺杂浓度的TiO2纳米片.运用X射线衍射、场发射扫描电镜、高分辨率透射电子显微镜、紫外-可见漫反射光谱、X射线光电子能谱和荧光光谱对光催化剂进行了结构和性能表征,并以罗丹明B为目标降解物,考察了N掺杂浓度对TiO2纳米片可见光催化活性的影响.结果表明,NH3流速为40ml/min时制备的N掺杂TiO2纳米片具有最低的光生电子-空穴复合速率,最高的OH产生能力并表现出最高的光催化活性.同时,讨论了N掺杂浓度对TiO纳米片可见光催化活性影响的机理.     

Fe掺杂对纳米TiO2薄膜的结构与光催化性能的影响

采用溶胶-凝胶法制备了Fe掺杂的TiO2薄膜,利用X射线光电子能谱、X射线衍射技术、显微共聚焦拉曼光谱、紫外可见光谱和原子力显微镜等对薄膜进行表征,以甲基橙为反应模型对光催化活性进行测试。 结果表明,在300~600 ℃焙烧时,TiO2以锐钛矿结构存在,700 ℃焙烧时出现金红石结构。 随掺铁量和焙烧温度的增加,Fe/TiO2薄膜的表面粗糙度和晶粒尺寸均逐渐增大;随镀膜层数的增加,Fe/TiO2薄膜光谱吸收向可见光方向移动;较低含量的铁掺杂改善了TiO2薄膜的光催化活性,而较高含量的铁掺杂则使TiO2薄膜的光催化活性下降,掺铁量为0.1%时Fe/TiO2薄膜的光催化活性最好。     

磁功能性TiO2光催化剂的制备及特性

采用溶胶-凝胶法以Fe₃O₄为磁核制备了磁功能性光催化剂,以甲基橙为模拟污染物,考察了掺杂Fe比例、催化剂煅烧温度以及煅烧时间对催化剂活性的影响.催化剂的最佳制备条件为:Fe₃O₄掺杂Fe含量为5%,煅烧温度为450 ℃,煅烧时间为2 h.通过TG-DTA、XRD、UV-Vis、TEM对催化剂进行了表征,结果表明:制备的催化剂具有明显的核壳结构,原Fe₃O₄磁核经过高温煅烧被氧化;TiO₂包覆在磁核表面;催化剂的吸收带边发生红移,在可见光区的吸收强度有所增强;催化剂颗粒的平均粒径为20 nm.     

Keggin型铬取代的磷钨杂多阴离子/二氧化钛纳米膜光催化剂的制备及可见光催化性能

以钛酸四丁酯Ti(OC₄H₉)₄为TiO₂前驱体,Keggin型铬取代的杂多阴离子PW₁₁Cr为可见光活性组分,采用溶胶-凝胶提拉法在玻片表面制备了PW₁₁Cr/TiO₂纳米膜光催化剂,并用UV-Vis DRS、IR、XRD、SEM和TEM等技术手段对催化剂的光吸收性质、化学组成、晶相和表面结构形貌等进行了表征;讨论了膜中PW₁₁Cr和TiO₂相互作用的方式;以染料模型污染物RhB的可见光催化降解为探针,评估了PW₁₁Cr/TiO₂光催化剂的可见光催化活性,讨论了光催化反应机理,并与TiO₂的光催化反应机理进行了比较;考察了焙烧温度、PW₁₁Cr剂量和溶液pH值对光催化活性的影响;最后用RhB的循环降解实验评估了催化剂的光催化稳定性。 实验结果表明,PW₁₁Cr/TiO₂光催化剂对可见光有明显吸收,较低焙烧温度(100 ℃)下得到的膜为无定形结构,而较高焙烧温度(500 ℃)为纳晶结构;前者的光催化活性较高,在200 W金卤灯照射下降解10 μmol/L RhB,120 min的降解率为95%,4 h的COD去除率为72%;羟基自由基是导致RhB降解的主要氧活性物质;低的膜处理温度,高的PW₁₁Cr负载量和溶液酸性有利于提高PW₁₁Cr/TiO₂膜的光催化活性;经循环重复使用10次,PW₁₁Cr/TiO₂膜的光催化活性仅有较少损失。     

Co掺杂对TiO2光催化剂结构与性能的影响

采用溶胶-凝胶法制备了Co掺杂的TiO2粉末, 利用透射电子显微镜、X射线光电子能谱、紫外可见光谱和X射线衍射技术对粉末进行了表征, 并利用环形光催化反应器对其光催化活性进行了测试. 结果表明, 随焙烧温度的增加, Co/TiO2粉末的晶粒尺寸逐渐增大, 升至873 K时, 钴元素以CoTiO3形式从TiO2中析出, 同时TiO2由锐钛矿型向金红石型发生转变, 相转变过程中晶格常数a和c以及晶胞体积发生收缩. 掺杂钴以后, 粉末的光谱吸收范围被拓展至可见光, 但是其光催化活性却明显降低.     

Synthesis, property characterization and photocatalytic activity of the novel composite polymer polyaniline/Bi2SnTiO7

A novel polyaniline/Bi(2)SnTiO(7 )composite polymer was synthesized by chemical oxidation in-situ polymerization method and sol-gel method for the first time. The structural properties of novel polyaniline/Bi(2)SnTiO(7) have been characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and X-ray spectrometry. The lattice parameter of Bi(2)SnTiO(7) was found to be a = 10.52582(8) ?. The photocatalytic degradation of methylene blue was realized under visible light irradiation with the novel polyaniline/Bi(2)SnTiO(7) as catalyst. The results showed that novel polyaniline/Bi(2)SnTiO(7 )possessed higher catalytic activity compared with Bi(2)InTaO(7) or pure TiO(2) or N-doped TiO(2) for photocatalytic degradation of methylene blue under visible light irradiation. The photocatalytic degradation of methylene blue with the novel polyaniline/Bi(2)SnTiO(7) or N-doped TiO(2) as catalyst followed first-order reaction kinetics, and the first-order rate constant was 0.01504 or 0.00333 min(-1). After visible light irradiation for 220 minutes with novel polyaniline/Bi(2)SnTiO(7 )as catalyst, complete removal and mineralization of methylene blue was observed. The reduction of the total organic carbon, the formation of inorganic products, SO(4)2- and NO(3-), and the evolution of CO(2) revealed the continuous mineralization of methylene blue during the photocatalytic process. The possible photocatalytic degradation pathway of methylene blue was obtained under visible light irradiation.     

铕掺杂TiO2的制备及其可见光光催化性能研究

采用溶胶-凝胶法制备了不同铕(Eu)掺杂量的TiO₂纳米颗粒(Eu-TiO₂),利用透射电镜(TEM),X射线光电子能谱(XPS),X射线衍射(XRD)及紫外可见漫反射(UV-Vis DRS)等方法对Eu-TiO₂进行了物理特性的初步表征.结果表明:与未掺杂纳米TiO₂比较,Eu-TiO₂禁带宽度变窄,具有可见光光催化活性.在可见光下(λ≥420 nm)照射下,以光催化降解染料罗丹明B(Rhodamine B,RhB)为目标反应,探讨了Eu-TiO₂不同制备条件对RhB降解光催化活性的影响,优化得到制备高活性Eu-TiO₂最佳pH为3、掺杂比例(n_Eu/n_Ti)为0.05%、煅烧温度为500 ℃.研究了可见光照射下Eu-TiO₂降解RhB和无色有机小分子水杨酸(SA)光催化反应条件及降解特性,RhB的12 h深度氧化矿化率为60.2%,SA的8 h降解率达到100%.通过跟踪测定可见光下Eu-TiO₂光催化反应过程中氧化物种的变化,研究了可见光激发Eu-TiO₂光催化反应机理,表明其光催化反应主要涉及羟基自由基(·OH)历程.     

铽负载介孔二氧化钛的制备、表征和协同效应

以嵌段共聚物P123为模板剂,采用蒸发诱导自组装法制备了铽负载介孔TiO2光催化剂,并利用XRD、N2吸附解吸和UV-Vis吸收光谱等技术手段对样品进行了表征。 制备的样品为锐钛矿和金红石混合晶相,以罗丹明B为模拟有机降解物,样品显示了良好的可见光催化活性。 研究发现0.7%的铽负载和380 ℃的煅烧温度是较佳的制备条件。 介孔结构所具有的高的比表面积、小的晶粒尺寸、铽负载诱导的电荷分离和可见光吸收增强协同提高了光催化活性。 同时,提出了铽负载二氧化钛诱导增强光催化作用的机理。     

Synthesis and structure of nanocrystalline TiO2 with lower band gap showing high photocatalytic activity

Nanocrystalline TiO2 was synthesized by the solution combustion method using titanyl nitrate and various fuels such as glycine, hexamethylenetetramine, and oxalyldihydrazide. These catalysts are active under visible light, have optical absorption wavelengths below 600 nm, and show superior photocatalytic activity for the degradation of methylene blue and phenol under UV and solar conditions compared to commercial TiO2, Degussa P-25. The higher photocatalytic activity is attributed to the structure of the catalyst. Various studies such as X-ray diffraction, Raman spectroscopy, Brunauer-Emmett-Teller surface area, thermogravimetric-differential thermal analysis, FT-IR spectroscopy, NMR, UV-vis spectroscopy, and surface acidity measurements were conducted. It was concluded that the primary factor for the enhanced activity of combustion-synthesized catalyst is a larger amount of surface hydroxyl groups and a lowered band gap. The lower band gap can be attributed to the carbon inclusion into the TiO2 giving TiO(2-2x)C(x) VO2**.     

离子液体-水混合介质中合成N、F共掺杂宽光域响应多孔TiO2光催化剂及性能

以TiCl4为钛源,离子液体-水为混合溶剂,采用液相水解-沉淀法制得浅黄色的N、F共掺杂宽光域响应多孔TiO2光催化剂(TiONF).以苯酚为模型物,考察了TiONF在紫外光区、可见光区及太阳光下催化活性.采用X射线光电子能谱(XPS)、紫外-可见漫反射光谱(DRS)、透射电镜(TEM)、X射线衍射(XRD)、傅里叶变换红外(FTIR)光谱及低温N2吸附-脱附等技术对TiONF的结构进行表征.结果表明,在离子液体-水混合介质中合成适量N、F共掺杂的TiO2在紫外光区、可见光区及太阳光下均表现出较高的活性,且高于纯水介质中合成TiONF的活性.离子液体-水混合介质有利于N、F进入TiO2晶格中;N、F共掺杂后在TiO2表面生成Ti―O―N键,形成新的能级结构,使催化剂的吸收红移至450-530nm,诱发TiO2可见光催化活性;同时,N、F共掺杂提高了TiO2表面羟基数量;还提高了TiO2相转变温度,减缓了相转变速率.另外,在离子液体-水混合介质中合成的TiONF较纯水介质中合成的TiONF粒子小、分散性好、比表面积大.     

溴化银/二氧化钛复合材料的可见光催化性能

将硝酸银的乙醇溶液与溶胶凝胶TiO2混合得到前驱体,随后经共沉淀-煅烧制备得到AgBr/TiO2复合材料;采用扫描电镜、X射线衍射仪、X射线光电子能谱仪分析了复合材料的形貌、晶体结构、Ag元素的价态,采用紫外-可见漫反射光谱仪测定了其光吸收性能;进而以甲基橙(MO)的可见光降解为探针反应测定了AgBr/TiO2复合材料的可见光催化性能.结果表明,当前驱体在不同温度下煅烧后,无定形TiO2颗粒逐渐增大,并逐渐转变为锐钛矿结构;担载的AgBr可明显拓展TiO2的可见光吸收范围;Ag物种主要以Ag+形式存在.当煅烧温度为300℃时,复合材料的光催化活性最高,MO的降解率在60min内达到90%以上;随着煅烧温度的增加,催化活性逐渐降低.