A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Template synthesis of heterostructured polyaniline/Bi2Te3 nanowires

Heterostructured polyaniline/Bi₂Te₃ nanowires have been prepared by chemical and electrochemical reactions on a porous alumina template. Its morphology and structure have been studied by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and electron probe microanalysis. The microscope analysis reveals that Bi₂Te₃ is well enveloped in polyaniline tubules in pores of alumina template. This microscopic material shows possible application in microthermoelectric device.     

四角星形BiVO4/Bi2O3催化剂的制备及性能研究

采用水热法合成具有四角星形貌的钒酸铋,再将钒酸铋浸渍在碱溶液里二次水热,制备出BiVO₄/Bi₂O₃催化剂。采用X射线粉末衍射(XRD)、扫描电子显微镜(SEM),紫外-射(UV-Vis DRS)等方法征。可见光下,BiVO₄/Bi₂O₃复合物的光催化降解丹明B性能及光电优于纯BiVO₄。BiVO₄/Bi₂O₃复合材料形成了异质结构,有效抑制了光电子与空穴的复合效率。     

四角星形BiVO4/Bi2O3催化剂的制备及性能

采用水热法合成具有四角星形貌的钒酸铋,再将钒酸铋浸渍在碱溶液里二次水热,制备出BiVO_4/Bi_2O_3催化剂。采用X射线粉末衍射(XRD)、扫描电子显微镜(SEM),紫外-可见漫反射(UV-Vis DRS)等方法对样品进行表征。可见光下,BiVO_4/Bi_2O_3复合物的光催化降解罗丹明B性能及光电流响应均优于纯BiVO_4。这是由于BiVO_4/Bi_2O_3复合材料形成了异质结构,有效抑制了光生电子与空穴的复合效率。     

Bi/BiVO4&Bi4V2O11复合催化剂的制备及其光催化性能

经由溶剂热反应、光辅助还原过程制备Bi/Bi VO_4Bi_4V_2O_(11)纳米复合光催化材料。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、高分辨率透射电子显微镜(HRTEM)、X射线光电子能谱(XPS)、紫外-可见漫反射光谱(UV-Vis DRS)、N_2吸附-脱附等温线和光致发光(PL)等手段对该复合物进行表征。实验结果表明当金属Bi与BiVO_4Bi_4V_2O_(11)的质量比值为0.8,可见光照射30 min时,Bi/BiVO_4Bi_4V_2O_(11)复合催化剂对罗丹明B(RhB)的降解率可达95.6%。此外,Bi/BiVO_4Bi_4V_2O_(11)对四环素(TC)的降解也表现出增强的光催化性能。Bi/BiVO_4Bi_4V_2O_(11)复合材料提升的光催化性能可能归因于金属Bi的表面等离子体共振(SPR)效应、拓宽的可见光吸收范围和增大的比表面积。此外,提出了复合光催化剂可能的光催化机理。     

浸渍-分解法制备高可见光催化活性的Bi2O3/TiO2纳米管阵列

用浸渍-分解法将Bi₂O₃纳米颗粒沉积在TiO₂纳米管壁上, 制备了Bi₂O₃/TiO₂纳米管阵列. 用电感耦合等离子体发射光谱(ICP-AES)测定了Bi₂O₃/TiO₂ 纳米管阵列的化学组分, 利用X 射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)和紫外-可见(UV-Vis)吸收光谱表征了所制备的样品. 通过在可见光下(λ>400 nm)降解甲基橙(MO)水溶液来评价样品的光催化活性. 结果表明, Bi₂O₃纳米颗粒均匀地沉积在TiO₂纳米管中. Bi₂O₃/TiO₂纳米管阵列具有比纯Bi₂O₃膜和N-TiO₂纳米管阵列高得多的可见光催化活性. Bi₂O₃/TiO₂纳米管阵列活性的增强是其强可见光吸收和Bi₂O₃与TiO₂之间形成的异质结的协同作用的结果.     

Sol-Gel Template Synthesis of Highly Ordered LiCo0.5Mn0.5O2 Nanowire Arrays and Their Structural Properties

Highly ordered LiCo_0.5Mn_0.5O₂ nanowire arrays were prepared using porous anodic aluminum oxide (AAO) template from sol-gel solution containing Li(CH₃COO), Co(CH₃COO)₂, and Mn(CH₃COO)₂. Electron microscope results showed that uniform length and diameter of LiCo_0.5Mn_0.5O₂ nanowires were obtained, and the length and diameter of LiCo_0.5Mn_0.5O₂ nanowires are dependent on the pore diameter and the thickness of the applied AAO template. X-ray diffraction and electron diffraction pattern investigations demonstrate that LiCo_0.5Mn_0.5O₂ nanowires are a layered structure of LiCo_0.5Mn_0.5O₂ crystal. X-ray photoelectron spectroscopy analysis indicates that the most closely resembling stoichiometric layered LiCo_0.5Mn_0.5O₂ material has been obtained.     

Ultrasonic-assisted synthesis of PMMA/Ni0.5Zn0.5Fe2O4 nanocomposite in mixed surfactant system

PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite with superparamagnetic behavior was synthesized by in situ emulsion polymerization of methylmethacrylate (MMA) monomer in the presence of Ni_0.5Zn_0.5Fe₂O₄ colloidal suspension assisted by ultrasonic irradiation. The obtained samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectra (FT-IR), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). XRD and FT-IR spectra confirmed the formation of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite. TEM images showed that Ni_0.5Zn_0.5Fe₂O₄ nanoparticles with the particle sizes of about 12 nm were well dispersed in the polymer matrix. The nanocomposite at room temperature exhibited superparamagnetic behavior under applied magnetic field. The formation mechanism of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite was proposed as well.     

A facile two-step modifying process for preparation of poly(SStNa)-grafted Fe3O4/SiO2 particles

This article reports the synthesis of the poly(sodium 4-styrenesulfonate)-grafted Fe₃O₄/SiO₂ particles via two steps. The first step involved magnetite nanoparticles (Fe₃O₄) homogeneously incorporated into silica spheres using the modified Stöber method. Second, the modified silica-coated Fe₃O₄ nanoparticles were covered with the outer shell of anionic polyelectrolyte by surface-initiated atom transfer radical polymerization. The resulted composites were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive microscopy (EDS), Fourier transform-infrared (FT-IR), thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS) and vibration sample magnetometer (VSM). The XRD results indicated that the surface modified Fe₃O₄ nanoparticles did not lead to phase change compared with the pure Fe₃O₄. TEM studies revealed nanoparticles remained monodisperse. The detection of sulfur and sodium signals was a convincing evidence that sodium 4-styrenesulfonate was grafted onto the surface of the magnetic silica in XPS analysis. Finally, super-paramagnetic properties of the composite particles, and the ease of modifying the surfaces may make the composites of important use in mild separation, enzyme immobilization, etc.     

Thermal oxide synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanorods and Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanowires

Fe₃O₄ nanorods and Fe₂O₃ nanowires have been synthesized through a simple thermal oxide reaction of Fe with C₂H₂O₄ solution at 200–600°C for 1 h in the air. The morphology and structure of Fe₃O₄ nanorods and Fe₂O₃ nanowires were detected with powder X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The influence of temperature on the morphology development was experimentally investigated. The results show that the polycrystals Fe₃O₄ nanorods with cubic structure and the average diameter of 0.5–0.8 μm grow after reaction at 200–500°C for 1 h in the air. When the temperature was 600°C, the samples completely became Fe₂O₃ nanowires with hexagonal structure. It was found that C₂H₂O₄ molecules had a significant effect on the formation of Fe₃O₄ nanorods. A possible mechanism was also proposed to account for the growth of these Fe₃O₄ nanorods. Supported by the Fund of Weinan Teacher’s University (Grant No. 08YKZ008), the National Natural Science Foundation of China (Grant No. 20573072) and the Doctoral Fund of Ministry of Education of China (Grant No. 20060718010)     

泡沫镍负载Fe2O3@Ni3S2纳米线网状结构电极的制备及其电催化析氧性能

通过两步水热法制备泡沫镍(NF)负载Fe_2O_3纳米粒子@Ni_3S_2纳米线网状结构电极(Fe_2O_3@Ni_3S_2/NF)。运用X射线衍射(XRD)、X射线光电子能谱(XPS)、透射电子显微镜(TEM)、N_2吸附-脱附测试等方法对电极材料的物相和微观结构特征等进行了表征。水热条件下原位表面化学刻蚀生成的Ni_3S_2纳米线与三维多孔NF基体间拥有强结合力和低界面电阻,Fe_2O_3粒子均匀分布在纳米线的表面。在1 mol·L~(-1)的KOH溶液中,运用线性扫描伏安测试(LSV)、计时电位法、电化学交流阻抗测试(EIS)等对电极的电催化析氧(OER)性能进行了测试。结果表明:在100 mA·cm~(-2)的超高电流密度下,Fe_2O_3@Ni_3S_2/NF电极的OER过电势仅为223 mV,比Ni_3S_2/NF材料的过电势降低了285 mV;经过10 h计时电位测试,性能保持率高达80%。     

Phase formation, crystal chemistry, and properties in the system Bi2O3-Fe2O3-Nb2O5

Subsolidus phase relations have been determined for the Bi₂O₃-Fe₂O₃-Nb₂O₅ system in air (900-1075 °C). Three new ternary phases were observed—Bi₃Fe_0.5Nb_1.5O₉ with an Aurivillius-type structure, and two phases with approximate stoichiometries Bi₁₇Fe₂Nb₃₁O₁₀₆ and Bi₁₇Fe₃Nb₃₀O₁₀₅ that appear to be structurally related to Bi₈Nb₁₈O₅₇. The fourth ternary phase found in this system is pyrochlore (A₂B₂O₆O′), which forms an extensive solid solution region at Bi-deficient stoichiometries (relative to Bi₂FeNbO₇) suggesting that ≈4-15% of the A-sites are occupied by Fe³⁺. X-ray powder diffraction data confirmed that all Bi-Fe-Nb-O pyrochlores form with positional displacements, as found for analogous pyrochlores with Zn, Mn, or Co instead of Fe. A structural refinement of the pyrochlore 0.4400:0.2700:0.2900 Bi₂O₃:Fe₂O₃:Nb₂O₅ using neutron powder diffraction data is reported with the A cations displaced (0.43 Å) to 96g sites and O′ displaced (0.29 Å) to 32e sites (Bi_1.721Fe_0.190(Fe_0.866Nb_1.134)O₇, Fd3¯m (#227), ). This displacive model is somewhat different from that reported for Bi_1.5Zn_0.92Nb_1.5O_6.92, which exhibits twice the concentration of small B-type cations on the A-sites as the Fe system. Bi-Fe-Nb-O pyrochlores exhibited overall paramagnetic behavior with large negative Curie-Weiss temperature intercepts, slight superparamagnetic effects, and depressed observed moments compared to high-spin, spin-only values. The single-phase pyrochlore with composition Bi_1.657Fe_1.092Nb_1.150O₇ exhibited low-temperature dielectric relaxation similar to that observed for Bi_1.5Zn_0.92Nb_1.5O_6.92; at 1 MHz and 200 K the relative permittivity was 125, and above 350 K conductive effects were observed.     

Crystal structure, stoichiometry, and dielectric relaxation in Bi3.32Nb7.09O22.7 and structurally related ternary phases

The crystal structure of the phase previously reported to occur at 4:9 Bi₂O₃:Nb₂O₅ has been determined using single-crystal X-ray and powder neutron diffraction (P6₃/mmc; a=7.4363(1) Å, c=19.7587(5) Å; Z=2). The structural study combined with phase equilibrium analyses indicate that the actual composition is Bi_3.32Nb_7.09O_22.7. This binary compound is the end-member of a family of four phases which form along a line between it and the pyrochlore phase field in the Bi₂O₃:Fe₂O₃:Nb₂O₅ system. The structures are derived from the parent pyrochlore end-member by chemical twinning, and can also be described as unit-cell intergrowths of the pyrochlore and hexagonal tungsten bronze (HTB) structures. The dielectric properties of the three chemically twinned pyrochlore phases, Bi_3.32Nb_7.09O_22.7, Bi_9.3Fe_1.1Nb_16.9O_57.8 and Bi_5.67FeNb₁₀O₃₅, were characterized. All exhibit low-temperature, broad dielectric relaxation similar to that of the Bi-Fe-Nb-O pyrochlore. At 1 MHz and ≈175 K the observed relative permittivites were 345, 240, and 205, respectively, compared to 125 for the Bi-Fe-Nb-O pyrochlore. The higher relative permittivities observed for the chemically twinned pyrochlore derivatives are ascribed to the presence of HTB blocks in their structures: The Bi atoms located in the HTB blocks feature highly asymmetric coordination environments compared to pyrochlore, and the magnitude of the relative permittivity increases with the proportion of Bi located within the HTB portions of the structures.     

Bi2Fe4O9/g-C3N4/UiO-66三元复合材料的协同光催化作用

通过水热法合成具有协同机制的三元复合材料Bi₂Fe₄O₉/g-C₃N₄/UiO-66,研究表明三元复合光催化剂的催化活性要高于二元材料和纯材料。这主要是由于Bi₂Fe₄O₉更易于和g-C₃N₄结合形成稳定的Z-scheme异质结结构,使三元复合材料增强了可见光响应能力,提高了电子-空穴分离能力,增强了空穴和电子的氧化还原能力。     

Bi2Fe4O9/g-C3N4/UiO-66三元复合材料的协同光催化作用

通过水热法合成具有协同机制的三元复合材料Bi₂Fe₄O₉/g-C₃N₄/UiO-66,研究表明三元复合光催化剂的催化活性要高于二元材料和纯材料。这主要是由于Bi₂Fe₄O₉更易于和g-C₃N₄结合形成稳定的Z-scheme异质结结构,使三元复合材料增强了可见光响应能力,提高了电子-空穴分离能力,增强了空穴和电子的氧化还原能力。     

Bi2Ti2O7/TiO2复合纤维：原位水热合成及光催化性能

采用静电纺丝技术制备的TiO2纤维作为模板和反应物,通过原位水热合成了具有异质结构的Bi2Ti2O7/TiO2复合纤维。利用X射线衍射(XRD)、扫描电镜(SEM)、能量散射光谱(EDS)、高分辨透射电镜(HRTEM)和紫外可见吸收光谱(UV-Vis)等分析测试手段对样品的结构和形貌进行表征。以罗丹明B为模拟有机污染物进行光催化降解实验。结果表明:花状Bi2Ti2O7纳米结构均匀地生长在TiO2纤维上,制备了Bi2Ti2O7与TiO2相复合的光催化材料,其光谱响应范围拓宽至可见光区,与纯TiO2纤维相比可见光催化活性显著提高,且易于分离、回收和循环使用。初步探讨了Bi2Ti2O7/TiO2异质结的生长机制和光催化活性提高机理。     

Template induced sol-gel synthesis of highly ordered LaNiO3 nanowires

The highly ordered LaNiO₃ nanowires of the rare-earth perovskite-type composite oxide were controlled synthesized within a porous anodic aluminum oxide (AAO) template by means of sol-gel method using nitrate as raw materials and citric acid as chelating agent. The results of scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed that the obtained LaNiO₃ nanowires had a uniform length and diameter, which were determined by the thickness and the pore diameter of the applied AAO template. The results of X-ray diffraction (XRD) and the selected-area electron diffraction (SAED) indicated that the LaNiO₃ nanowires were perovskite-type crystalline structures. Furthermore, X-ray photoelectron spectroscopy (XPS) and the energy dispersive X-ray (EDX) spectroscopy demonstrated that the stoichiometric LaNiO₃ was formed.     

MOF-808/Bi2MoO6复合材料的构筑及其光催化性能

采用简单的两步水热法制备出了锆基金属有机骨架和钼酸铋的复合材料MOF-808/Bi₂MoO₆。通过X射线粉末衍射、傅里叶红外光谱、扫描电子显微镜、透射电子显微镜、X射线光电子能谱、紫外可见漫反射光谱、N₂吸附-脱附测试和电化学测试对所制备材料的组成、微观结构、光学性质以及光生载流子的复合效率进行了分析。与纯Bi₂MoO₆和MOF-808相比,0.5%-MOF-808/Bi₂MoO₆复合材料展示出了较高的光催化活性,在可见光照射120 min时对抗生素环丙沙星(CIP)的降解率达89.7%。通过自由基捕获实验,证明了·O₂^-是主要活性物种,基于此我们提出了可能的光催化降解机理。     

MOF-808/Bi2MoO6复合材料的构筑及其光催化性能

采用简单的两步水热法制备出了锆基金属有机骨架和钼酸铋的复合材料MOF-808/Bi₂MoO₆。通过X射线粉末衍射、傅里叶红外光谱、扫描电子显微镜、透射电子显微镜、X射线光电子能谱、紫外可见漫反射光谱、N₂吸附-脱附测试和电化学测试对所制备材料的组成、微观结构、光学性质以及光生载流子的复合效率进行了分析。与纯Bi₂MoO₆和MOF-808相比,0.5%-MOF-808/Bi₂MoO₆复合材料展示出了较高的光催化活性,在可见光照射120 min时对抗生素环丙沙星(CIP)的降解率达89.7%。通过自由基捕获实验,证明了·O₂^-是主要活性物种,基于此我们提出了可能的光催化降解机理。     

g-C3N4/Bi2O2CO32D纳米片复合材料的制备及可见光催化性能研究

采用自组装和化学沉淀法分别制得两种可见光驱动复合材料石墨相氮化碳/碳酸氧铋(g-C_3N_4/Bi_2O_2CO_3).采用X射线衍射光谱(XRD),紫外可见光谱、扫描电镜(SEM)、N_2吸附、电化学阻抗谱(EIS)和X射线光电子能谱(XPS)等分析手段对制备的催化剂进行了表征.结果表明,制备方法对纳米复合材料的晶相、形态及光学性能没有影响,但是影响g-C_3N_4和Bi_2O_2CO_3之间的相互作用力,导致光生电子-空穴对的分离速率存在显著差异.以可见光驱动苯酚和罗丹明B的降解实验为探针反应检测催化剂的光催化性能.实验结果表明自组装法得到的异质结催化剂中相互作用力更强,催化效果最高.O_2-是罗丹明B降解反应的主要活性物种,染料的光敏化、Bi_2O_2CO_3与g-C_3N_4综合效应,导致光生载流子电荷分离效率更高.