采用共沉淀法制备了CuGa₂O₄纳米材料,并利用水热法制备了一系列WS₂/CuGa₂O₄复合材料。结合X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)等对制备的材料进行了物相组成、表面形貌以及元素价态的分析。研究了WS₂的复合量对CuGa₂O₄材料检测乙醇气体敏感性能的影响。实验结果表明,当WS₂与CuGa₂O₄质量比为1%时,该复合材料制备的传感器在室温下对100μL·L^-1乙醇气体表现出345.3的灵敏度,响应时间和恢复时间分别为184和69 s,且最低检测限为0.1μL·L^-1。     

Lu(La)2O3微米晶中提高Bi3+离子下转换蓝光发光性能的研究

采用尿素沉淀法制备一系列Bi³⁺/La³⁺共掺Lu₂O₃和Bi³⁺/Lu³⁺共掺La₂O₃微米晶。在掺杂Bi³⁺离子的Lu₂O₃微米晶中,C₂位点的Bi³⁺离子可以将吸收的能量转移给S₆位点的Bi³⁺离子。同时,在Lu₂O₃:1%Bi³⁺,0～5%(摩尔分数,下同)La³⁺微米晶中,372和337 nm(C₂和S₆位点的Bi³⁺离子)紫外光的激发下,Bi³⁺离子的发射峰强度随着La³⁺离子掺杂浓度的增加而增加,掺杂5%La³⁺时与不掺杂La     

ZrO2包覆高镍LiNi0.8Co0.1Mn0.1O2正极材料提高其循环稳定性的作用机理

高镍三元材料作为一种锂离子电池正极材料,因其较高的放电比容量而得到科学界和工业界的广泛关注。研究表明,高镍三元材料的比容量与材料中的Ni含量呈正相关,但Ni含量的增加也会加剧循环过程中的界面副反应,材料表面释氧以及结构转变等问题。本文采用ZrO₂包覆LiNi_0.8Co_0.1Mn_0.1O₂材料,利用X射线衍射证明,在高温处理下ZrO₂包覆物中的Zr⁴⁺会掺杂进LiNi_0.8Co_0.1Mn_0.1O₂材料表面晶格中,使得X射线衍射谱中的(003)衍射峰左移。电化学测试证明在4.3和4.5 V的截止电压下,改性最优的材料在1C循环100周后容量保持率分别从84.89%和75.60%提高到97.61%和81.37%,同时发现循环稳定性的提升主要来自材料表面的Zr⁴⁺掺杂。X射线光电子能谱证明Zr⁴⁺表层掺杂后材料的Ni化合价由Ni3+向Ni²⁺转变,透射电子显微镜观察到Zr⁴⁺的表层掺杂使得材料表面的层状结构发生重构,从而稳定了材料体相结构,提高了材料整体的循环稳定性。     

ZIF-67衍生的花状Ga掺杂Co3O4用于增强三乙胺传感性能

基于Ga³⁺对Co-MOF(ZIF-67)进行掺杂的策略，衍生制备了具有花状结构的Ga掺杂Co₃O₄气敏材料，并应用于三乙胺(TEA)选择性气敏传感。采用X-射线衍射仪表征了气敏材料的晶体构型，结果表明，Ga离子成功地掺杂到Co₃O₄晶格中。采用扫描电镜以及透射电镜对气敏材料的微观形貌进行表征，结果表明，含有1%Ga掺杂比例的Co₃O₄具有更为疏松多孔的花状结构。采用X-射线光电子能谱以及氮气吸脱附测试对材料的氧空位含量以及比表面积进行表征，结果表明，含有1%Ga掺杂比例的Co₃O₄具有丰富的氧空位含量以及较大的比表面积。最后，采用CGS-8气敏测试分析系统对含有不同Ga掺杂比例的Co₃O₄气敏材料进行三乙胺选择性气敏测试，结果表明，Ga掺杂比例为1%的Co₃O₄气敏传感器显示出最优的TEA气敏响应特性，...     

CoFe2O4/CuO活化过氧乙酸高效降解磺胺甲恶唑(英文)

利用化学沉淀法和溶胶凝胶法,通过两步法成功制备出含有尖晶石钴铁氧体和氧化铜的复合催化剂CoFe₂O₄/CuO,通过扫描电子显微镜(SEM)、X射线光电子能谱(XPS)和X射线衍射(XRD)对制备出的CoFe₂O₄/CuO进行表征,探究不同高级氧化体系对磺胺甲恶唑(SMX)去除能力,考察过氧乙酸(PAA)浓度、催化剂投加量、水体中常见干扰物质(Cl^-,HCO-3,SO₄^2-,HA)和不同自由基捕获剂对SMX去除的影响。分析结果表明CoFe₂O₄/CuO同时具有CoFe₂O₄与CuO的特征,对比单独CoFe₂O₄与CuO,CoFe₂O₄/CuO对PAA展现出极高的活化性能,在最佳反应条件下(催化剂投加量=20mg·L^-1,c(PAA)=200μ...     

固体酸S2O82-/Nb2O5/La3+的制备、表征及催化合成乙酸正丁酯

以Nb₂O₅为载体,浸渍法研制固体酸（S₂O₈^2-/Nb₂O₅/La⁺）催化剂,经SEM、XRD和EDS表征,考察了固体酸的焙烧温度、陈化时间及S₂O₈^2-浓度等因素对该催化剂催化活性的影响。结果表明：在(NH₄)₂S₂O₈浓度为1 mol/L、浸渍时间18 h、w(La³⁺)=3%（基于Nb₂O₅的质量）、焙烧温度为500 ℃时,制备出最高催化效果的催化剂。接着考察了其催化合成乙酸正丁酯的催化活性,通过正交实验确定了反应的最佳条件：n(正丁醇)/n(冰醋酸）=2.0/1.0、催化剂用量w（S₂O₈^2-/Nb₂O₅/La³⁺）=2.9%（基于反应物质量）、反应温度为125 ℃,反应时间为3.0 h,酯化率为95.70%。催化剂循环利用3次后仍有90.1%的酯化率。      

LaNi1-xFexO3钙钛矿型氧化物的制备与光催化降解性能

通过溶胶-凝胶法制备系列LaNi_1-xFe_xO₃（x=0.05, 0.1, 0.2, 0.4, 0.6和0.8）钙钛矿型氧化物光催化材料,采用X射线衍射进行结构表征,以甲基橙的降解率作为催化剂活性的评价指标,探究了实验条件对光催化活性的影响。结果表明,少量掺杂Fe³⁺可提高LaNiO₃的光催化活性,在所有样品中LaNi_0.95Fe_0.05O₃的光催化活性最高;当催化剂用量为1.0 g﹒L^-1时,对浓度为10 mg﹒L^-1的甲基橙溶液的光催化效果最佳,可见光照射120 min的降解率高达98.9%,5次重复使用后的降解率仍可达84.6%,具有稳定高效的重复利用性。      

基于H2O2-丁基玫瑰红B-Fe2+体系的荧光猝灭法测定血清过氧化氢酶的活性

利用H₂O₂-Fe²⁺可以快速使丁基玫瑰红B(BRMB)发生荧光猝灭,而过氧化氢酶(CAT)对该猝灭有抑制效应,提出了基于H₂O₂-BRMB-Fe²⁺体系的荧光猝灭法测定血清CAT活性的方法。取血清样品10μL,加入1 mmol·L^-1 H₂O₂底液0.50 mL,于30℃恒温反应15 min,再依次加入0.02 mmol·L^-1 BRMB溶液0.70 mL、0.1 mol·L^-1冰乙酸-乙酸钠缓冲液(pH 4.2)1.00 mL和0.01 mol·L^-1 Fe²⁺溶液0.08 mL,于室温反应20 min后用水定容至10 mL,测定体系在590 nm发射波长处的荧光强度F;以煮死酶液为对照,按照同样的方法测定其在590 nm发射波长处的荧光强度F₀。结果表明：CAT活性在0.005...     

锌掺杂OV-β-Bi2O3可见光催化活性的提高:能带结构的调节和电荷分离的促进

采用溶胶-凝胶-原位碳热还原处理的方法,制备了一种含有氧空位(OV)的新型Zn掺杂β-Bi₂O₃纳米材料(OV-Zn∶Bi₂O₃),氧空位的浓度可以通过改变Zn²⁺的掺杂量进行调节。作为参照,只有氧空位没有Zn²⁺的新型β-Bi₂O₃(OV-β-Bi₂O₃)也通过类似的方法制得。通过紫外可见漫反射光谱、X射线光电子能谱、电子顺磁共振、光致发光光谱和光电化学测试,系统研究了氧空位和Zn²⁺掺杂对OV-Zn∶Bi₂O₃降解亚甲基蓝(MB)和2,4,6-三氯苯酚(2,4,6-TCP)可见光催化活性的综合影响。结果表明,氧空位的引入不仅可以使光吸收向长波方向拓展,而且可以促进光生载流子的分离。因此,与传统的β-Bi₂O₃相比,OV-β-Bi₂O₃对亚甲基蓝(MB)和2,4,6-三氯苯酚(2,4,6-TCP)的降解活性显著增强。对于OV-Zn∶Bi₂O₃催化剂,Zn²⁺掺杂可使光催化剂的价带边缘向下移动,增强了光激发空穴的氧化能力,并且适量的锌掺杂也能提高光生载流子的分离效率。因此,OV-Zn∶Bi₂O₃的可见光活性优于OV-β-Bi₂O₃,而且当Zn与Bi物质的量之比为0.3时,OV-Zn∶Bi₂O₃-0.3对MB和2,4,6-TCP的降解活性最高。     

PO43-掺杂和AlF3包覆协同增强Li1.2Ni0.13Co0.13Mn0.54O2正极材料电化学性能

本研究采用PO₄^3-掺杂和AlF₃包覆的协同改性策略制备了P-LNCM@AlF₃正极材料(P=PO₄^3-,LNCM=Li_1.2Ni_0.13Co_0.13Mn_0.54O₂),提高了LNCM的结构稳定性以及抑制了界面副反应。其中,大四面体的PO₄^3-聚阴离子掺杂在晶格中抑制了过渡金属离子的迁移,降低体积变化,从而稳定了晶体结构,而且PO₄^3-掺杂能够扩大锂层间距,促进Li⁺的扩散,从而提升材料的倍率性能。此外,AlF₃包覆层能抑制材料与电解液的副反应从而提升界面稳定性。基于以上优势,P-LNCM@AlF₃正极表现出了优异的电化学性能。在1C电流密度下表现出了179.2 mAh·g^-1     

Ca2+-Mg2+-Zn2+体系在水溶性聚磷酸铵溶液中螯合规律的研究

近年来,水溶性聚磷酸铵在液体肥料和复合肥料的领域受到了广泛的关注,并在发达国家中得到了大面积的推广及应用。在pH值为5.5~8.0、温度为278.15 K~323.15 K的条件下,本文采用滴定法研究Ca_²⁺-Mg_²⁺-Zn_²⁺体系在聚磷酸铵溶液中的螯合规律。实验结果表明：相同质量分数的聚磷酸铵溶液对金属离子的螯合量会随着体系中Ca_²⁺、Mg_²⁺、Zn_²⁺的摩尔浓度的变化而变化;随着温度的升高而逐渐降低;随着pH的增加而逐渐增加;随着聚合度的升高而逐渐增加。采用傅里叶红外光谱对聚磷酸铵和A₁B₃C₃体系的螯合物进行表征。     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

氨基酸-BrO-3-Mn2+-H2SO4-丙酮体系的振荡反应

This paper, Using potentiometric method, first reports the oscillating behavior of five amino acids (L-methionine, L-cystine, L-tryptophan, L-serine, L-tyrosine) in a new oscillating system of amino acid-BrO_3~--Mn~(2+)-H_2SO_4-acetone. The effect of many factors on oscillation have been investigated. According to Arrhenius equation, the apparent activation energy of the oscillatary induction period and oscillation period of five oscillating systems are obtained within temperature range of 20～37 ℃.     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

复合催化剂上CO2加氢合成C2烃类

介绍了由CO₂+H₂合成C2⁺烃的几种复合催化剂体系的研究进展，比较和评价了复合催化剂体系的活性和选择性及对C2⁺烃类生成的影响。着重于复合催化剂体系对C4⁺烃的生成及产物分布的影响并简述反应机理。     

PO43-掺杂Bi2O2CO3/Bi0的制备及其可见光催化性能

构建氧空位以及附着金属单质Bi(Bi⁰)是增强半导体材料光吸收性能、促进半导体光生载流子分离的有效方法。通过简单的共沉淀法及氢气热还原成功制备了PO₄^3-掺杂Bi₂O₂CO₃附着Bi⁰(Bi-P-BOC)的可见光催化剂,并对其在可见光下催化降解氧氟沙星(OFX)的性能及机理进行了研究。材料表征结果表明BOC随着PO₄^3-的均匀掺杂,可见光吸收能力增强,表面缺陷增多,比表面积增大。而随着氢气热还原,BOC表面形成 Bi⁰的同时也原位构建了大量的氧空位。可见光催化性能测试表明,Bi-P-BOC可以在180 min内降解约85%的OFX,降解速率为0.013 0 min^-1,是BOC降解速率的8倍。Bi-P-BOC光催化降解机理表明其具有更好的可见光吸收能力,Bi⁰以及氧空位的存在促进了光生载流子的分离,h+是其光催化降解过程中的主要的活性氧物种(ROS),此外,¹O₂和·O₂^-也对降解有一定贡献。     

PO43-掺杂Bi2O2CO3/Bi0的制备及其可见光催化性能

构建氧空位以及附着金属单质Bi(Bi⁰)是增强半导体材料光吸收性能、促进半导体光生载流子分离的有效方法。通过简单的共沉淀法及氢气热还原成功制备了PO₄^3-掺杂Bi₂O₂CO₃附着Bi⁰(Bi-P-BOC)的可见光催化剂,并对其在可见光下催化降解氧氟沙星(OFX)的性能及机理进行了研究。材料表征结果表明BOC随着PO₄^3-的均匀掺杂,可见光吸收能力增强,表面缺陷增多,比表面积增大。而随着氢气热还原,BOC表面形成Bi⁰的同时也原位构建了大量的氧空位。可见光催化性能测试表明,Bi-P-BOC可以在180 min内降解约85%的OFX,降解速率为0.013 0 min^-1,是BOC降解速率的8倍。Bi-P-BOC光催化降解机理表明其具有更好的可见光吸收能力,Bi⁰以及氧空位的存在促进了光生载流子的分离,h⁺是其...     

Ho3+/Yb3+共掺ZnO-Al2O3-GeO2-SiO2玻璃陶瓷的制备和上转换发光性质

综合ZnO-Al₂O₃-SiO₂系和锗酸盐玻璃陶瓷的优点,采用熔融-晶化法首次制备了Ho³⁺/Yb³⁺共掺以ZnAl₂O₄为主晶相的ZnO-Al₂O₃-GeO₂-SiO₂系玻璃陶瓷。因[GeO₄]四面体和[SiO₄]四面体都是玻璃网络形成体,讨论了GeO₂取代SiO₂对玻璃陶瓷样品硬度及发光性能的影响,最终确定GeO₂的取代量为10.55%（w/w）时,玻璃陶瓷综合性能最佳。在980 nm泵浦光的激发下,发现强的绿色（546 nm）和弱的红色（650 nm）上转换发光,并研究了不同Ho³⁺/Yb³⁺掺杂比对样品上转换发光的影响,最终结果表明当Ho³⁺/Yb³⁺掺杂比为1：11（n/n）时样品荧光强度最强,在绿色上转换发光材料方面具有潜在的应用。     

IR and Raman spectra of two layered aluminium phosphates Co(en)3Al3P4O16 · 3H2O and [NH4]3[Co(NH3)6]3[Al2(PO4)4]2 · 2H2O

The FT IR and FT Raman spectra of Co(en)₃Al₃P₄O₁₆ · 3H₂O (compound I) and [NH₄]₃[Co(NH₃)₆]₃[Al₂(PO₄)₄]₂ · 2H₂O (compound II) are recorded and analysed based on the vibrations of Co(en)₃³⁺, Co(NH₃)₆³⁺, NH₄⁺, Al---O---P, PO₃, PO₂ and H₂O. The observed splitting of bands indicate that the site symmetry and correlation field effects are appreciable in both the compounds. In compound I, the overtone of CH₂ deformation Fermi resonates with its symmetric stretching vibration. The NH₄ ion in compound II is not free to rotate in the crystalline lattice. Hydrogen bonding of different groups is also discussed.     

稀土掺杂Lu3Al5O12荧光粉的发光特性及能量传递

采用高温固相法制备了Ce、Sm共掺Lu₃Al₅O₁₂荧光粉。通过X射线衍射分析、荧光光谱分析研究了样品的结构、发光特性,并通过理论计算研究了能量传递效率、能量传递的临界距离以及能量传递方式。X射线衍射分析表明所制备的荧光粉具有单一的石榴石结构;荧光光谱分析表明,在464 nm蓝光激发下,Sm³⁺的引入可增加Lu₃Al₅O₁₂：Ce,Sm发射光谱中红光成分,并且随着Sm³⁺浓度的增加,Ce³⁺发光强度逐渐减弱。计算出Ce³⁺、Sm³⁺之间的能量传递效率高达77.42%,确定了Ce³⁺、Sm³⁺之间的能量传递机制为偶极-偶极相互作用。