复合光催化剂AgI/AgCl/h-BN的制备及光催化性能

以少层六方氮化硼纳米层状材料为载体,通过水溶性盐晶体模板法和离子交换法制备了h-BN稳定AgI/AgCl的三元复合体系。通过XRD、FT-IR、SEM、TEM等手段对样品的结构和形貌进行检测分析,利用UV-Vis DRS测试了样品的吸光性能。可见光光催化降解罗丹明B实验表明,光照24 min,AgI/AgCl/h-BN复合光催化材料对罗丹明B的降解率高达93%,远高于实验合成的大块AgCl、AgCl立方块、AgI/AgCl纳米腰果及文献报道的数值。并且三元材料循环利用4次后,对罗丹明B的降解率几乎保持不变。结合光电化学测试、活性物种捕获和电子自旋共振等实验结果,探讨了复合材料光催化活性和稳定性提高的机理。     

还原石墨烯氧化物/磷酸秘纳米复台物的台成及增强的光催化活性

以石墨烯氧化物和硝酸铋为前驱物、甘油为溶剂,200℃下反应1 h,采用溶剂热方法"一锅煮"合成还原石墨烯氧化物/磷酸铋复合纳米材料.利用扫描电镜、透射电镜、X射线衍射、X射线光电子能谱、表面增强拉曼光谱和紫外-可见光谱对所合成样品的形貌和结构进行表征.以罗丹明B作为降解模型分子,考察了复合纳米材料在紫外光照射下的光催化活性.实验结果表明,复合纳米材料的光催化活性优于磷酸铋.在2 h内,还原石墨烯氧化物/磷酸铋对罗丹明B降解率为87.5%;而同样条件下,磷酸铋对罗丹明B的降解率仅为45.7%.复合材料光催化活性的提高主要归因于石墨烯纳米片高效的电子受体和传输特性能有效促进电子-空穴对的分离,进而提高了复合材料的降解效率.     

静电纺丝制备g-C3N4/C纳米纤维及其可见光降解性能

采用g-C_3N_4纳米片与聚丙烯腈进行静电复合纺丝,再经预氧化和碳化制得g-C_3N_4/C纳米纤维。利用傅立叶变换红外光谱仪(FTIR)、X射线衍射仪(XRD)、拉曼光谱(Raman)和扫描电子显微镜(SEM)对样品结构和形貌进行表征,通过紫外-可见漫反射光谱(UV-Vis DRS)分析可见光响应性。研究表明,复合纳米纤维对罗丹明B表现出较好的可见光降解活性,源于无定形相/石墨相混合结构的碳基体能够降低g-C_3N_4的光生电子-空穴对复合的几率。复合纳米纤维膜在光催化降解搅拌条件下始终能保持完整,经过多次回收和光催化实验,对罗丹明B的光降解率依然较高,表现出较优异的循环利用稳定性。     

异质结型Er2O3/TiO2复合纳米纤维制备及光催化性能

采用静电纺丝技术与溶剂热法相结合,制备了异质结型Er2O3/TiO2复合纳米纤维光催化材料。利用X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、高分辨透射电镜(HRTEM)和紫外-可见吸收光谱(UV-Vis)等分析测试手段对材料进行表征,并以罗丹明B(RB)的脱色降解为模式反应,考察了材料的光催化性能。实验结果表明:Er2O3纳米粒子均匀地负载在TiO2纤维上,形成了异质型Er2O3/TiO2复合纳米纤维光催化材料,拓宽了光谱响应范围,有利于TiO2光生电子和空穴的分离,增强了体系的量子效率。与纯TiO2纳米纤维相比光催化活性明显提高,对RB的紫外光降解率达93.93%。     

Ag@AgI/Ni薄膜的制备及其模拟太阳光催化性能

采用电化学方法制备Ag@AgI/Ni表面等离子体薄膜催化剂,使用扫描电镜（SEM）,X射线衍射（XRD）和紫外-可见漫反射光谱（UV-Vis DRS）对薄膜的表面形貌、晶体结构、光谱特性以及能带结构进行分析表征,在模拟太阳光照射下,把罗丹明B作为模拟污染物对薄膜的光催化活性与稳定性进行评价,采用向反应体系中加入活性物种捕获剂的方法对薄膜光催化机理进行探究。结果表明：最佳工艺下制备的Ag@AgI/Ni薄膜表面是由附着少量Ag粒子的AgI纳米晶构成。薄膜具有显著的表面等离子共振作用、优异的光催化活性和突出的光催化稳定性。光催化反应60 min,薄膜对罗丹明B的降解率（81.1%）是AgI/Ni薄膜的1.35倍,是TiO₂（P25）/ITO薄膜的1.61倍。在薄膜光催化活性基本保持不变的前提下可循环使用5次。薄膜表面纳米Ag的等离子共振对光阴极反应的活化是光催化性能提高的重要原因。提出了薄膜光催化降解罗丹明B的反应机理。     

Ag@AgI/Ni薄膜的制备及其模拟太阳光催化性能

采用电化学方法制备Ag@AgI/Ni表面等离子体薄膜催化剂,使用扫描电镜(SEM),X射线衍射(XRD)和紫外-可见漫反射光谱(UV-Vis DRS)对薄膜的表面形貌、晶体结构、光谱特性以及能带结构进行分析表征,在模拟太阳光照射下,把罗丹明B作为模拟污染物对薄膜的光催化活性与稳定性进行评价,采用向反应体系中加入活性物种捕获剂的方法对薄膜光催化机理进行探究。结果表明:最佳工艺下制备的Ag@AgI/Ni薄膜表面是由附着少量Ag粒子的AgI纳米晶构成。薄膜具有显著的表面等离子共振作用、优异的光催化活性和突出的光催化稳定性。光催化反应60 min,薄膜对罗丹明B的降解率(81.1%)是AgI/Ni薄膜的1.35倍,是TiO_2(P25)/ITO薄膜的1.61倍。在薄膜光催化活性基本保持不变的前提下可循环使用5次。薄膜表面纳米Ag的等离子共振对光阴极反应的活化是光催化性能提高的重要原因。提出了薄膜光催化降解罗丹明B的反应机理。     

Ce掺杂Bi2MoO6/TiO2纳米纤维异质结的制备及可见光催化性能

以静电纺丝技术制备的TiO_2纳米纤维为基质,通过溶剂热法制备了异质结型稀土Ce掺杂Bi_2MoO_6/TiO_2复合纳米纤维。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)、透射电镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)以及荧光光谱(PL)等分析测试手段对样品的物相、形貌和光学性能等进行表征。以罗丹明B为模拟有机污染物,研究了样品的可见光催化性能。结果表明:在稀土掺杂样品中,Ce离子进入Bi_2MoO_6晶格,部分取代Bi3+,导致晶胞膨胀,晶格畸变,形成缺陷;与TiO_2复合形成异质结,有利于光生电荷的产生、转移和有效分离,从而提高TiO_2纳米纤维的光催化活性。可见光照射180 min,罗丹明B的降解率达到95.1%。经5次循环光催化降解活性基本不变,样品具有良好的光催化稳定性。     

异质结构AgCl/Bi2WO6微米球制备、表征及其光催化性能

首先利用水热法制备了由纳米片组装的粒径为1.5–2μm的Bi2WO6微球,然后在微球表面沉积了不同含量的AgCl (5 wt%,10wt%,20wt%,30wt%),制备了异质结构AgCl/Bi2WO6微球光催化剂.利用X射线粉末衍射、扫描电镜、透射电镜、红外光谱、紫外-可见漫反射吸收等手段对所制的光催化剂进行表征,并以紫外光和可见光分别为光源,罗丹明B为降解对象测试了其光催化活性,考察复合不同含量的AgCl对Bi2WO6光催化剂的性能影响.结果表明,沉积AgCl对Bi2WO6的晶体结构、表面性能和光吸收性能没有产生明显影响,但大幅度提高了Bi2WO6的紫外和可见光催化活性.当复合20wt%AgCl时, AgCl/Bi2WO6光催化活性最佳,紫外光下比纯Bi2WO6提高了2.2倍,可见光下提高了1倍.这主要是由于形成的AgCl/Bi2WO6异质结能有效抑制光生电子和空穴的复合,从而提了其光催化性能.     

可见光高催化活性GO/Ag3PO4/Ni复合薄膜的制备和性能

以磷酸铵和氧化石墨烯悬浊液的混合液为电解液,采用电化学共沉积法制备了Ag3PO4基GO/Ag3PO4/Ni复合薄膜。运用扫描电子显微镜(SEM)、能量色散谱(EDS)、X射线衍射(XRD)、拉曼光谱(Raman)和紫外可见漫反射光谱(UV-Vis DRS)等对其形貌、物相和光谱特性进行分析。最佳工艺制备的GO/Ag3PO4/Ni复合薄膜呈现出GO包覆在直径为100 nm左右的Ag3PO4纳米球外的表面形貌。GO片与Ag3PO4纳米球之间存在强电荷相互作用。与单独的Ag3PO4纳米球相比,GO片的附着导致带隙缩小,可见光区的吸收率增强。可见光下考察了复合薄膜降解罗丹明B的光催化活性和稳定性,并利用荧光光谱和捕获剂法对薄膜的光催化机理进行了探索。结果表明,GO片的加入不仅显著提高了Ag3PO4的光催化活性,而且提高了Ag3PO4的结构稳定性。光催化降解罗丹明B 60 min时,GO/Ag3PO4/Ni复合薄膜的降解率是Ag3PO4/Ni薄膜的1.32倍。在保持薄膜光催化活性基本不变的前提下可循环使用7次。GO优异的电荷传导性能,以及Ag3PO4纳米球与GO片之间的正协同效应是提高复合薄膜光催化性能的主要原因。     

Bi/TiO_2复合纳米纤维制备及可见光催化性能

以电纺TiO_2纳米纤维为基质,EDTA为鳌合剂和吸附剂,采用溶剂热法制备Bi/TiO_2复合纳米纤维光催化材料,利用X射线粉末衍射(XRD)、扫描电镜(SEM)、X射线能量色散谱(EDS)、透射电镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)和荧光光谱(PL)等分析测试手段对样品的物相、形貌和光学性能等进行表征,以罗丹明B(Rh B)为模拟有机污染物,考察了样品的光催化性能。结果表明:EDTA在复合纳米纤维的合成过程中起到关键作用,通过改变EDTA的用量可以有效控制纤维表面构筑单质Bi纳米球的大小和覆盖密度。所制备的复合纳米纤维具有良好的可见光催化活性和稳定性,当单质Bi的负载量为65%时光催化活性最强,可见光照射180 min,RhB的降解率达到96.40%,循环使用5次降解率仍保持在91%以上。     

AgI/h-MoO3异质结的构筑及其模拟燃油光催化氧化脱硫活性

利用沉积法获得了异质结AgI/h-MoO₃光催化剂,通过X射线衍射（XRD）、扫描电子显微镜（SEM）、光电子能谱（EDS）、X射线光电子能谱（XPS）、紫外-可见漫反射吸收光谱（UV-Vis-DRS）、光致发光（PL）、电化学阻抗（EIS）等方法对其物相组成、形貌、光吸收特性、光电化学性能等进行了表征。以噻吩的正辛烷溶液模拟催化裂化（FCC）汽油为探针考察了AgI/h-MoO₃光催化氧化脱硫活性,结果表明,AgI/h-MoO₃-18异质结在催化剂浓度为1.5 g·L^-1,可见光照射2 h后,光催化氧化脱硫活性达98%。利用XRD、XPS、UV-Vis-DRS揭示了AgI/h-MoO₃光照后生成少量的金属Ag,使其结构转变为Z型AgI/Ag/h-MoO₃,有利于光生电子（e^-）转移。利用活性物种捕获实验、循环实验研究了AgI/h-MoO₃光催化氧化脱硫机理及其稳定性,实验结果表明：AgI/h-MoO₃不仅具有较高的光催化氧化脱硫活性,而且还有良好的稳定性。     

AgI/h-MoO_3异质结的构筑及其模拟燃油光催化氧化脱硫活性

利用沉积法获得了异质结AgI/h-MoO_3光催化剂,通过X射线衍射(XRD)、扫描电子显微镜(SEM)、光电子能谱(EDS)、X射线光电子能谱(XPS)、紫外-可见漫反射吸收光谱(UV-Vis-DRS)、光致发光(PL)、电化学阻抗(EIS)等方法对其物相组成、形貌、光吸收特性、光电化学性能等进行了表征。以噻吩的正辛烷溶液模拟催化裂化(FCC)汽油为探针考察了AgI/h-MoO_3光催化氧化脱硫活性,结果表明,AgI/h-MoO_3-18异质结在催化剂浓度为1.5 g·L~(-1),可见光照射2 h后,光催化氧化脱硫活性达98%。利用XRD、XPS、UV-Vis-DRS揭示了AgI/h-MoO_3光照后生成少量的金属Ag,使其结构转变为Z型AgI/Ag/h-MoO_3,有利于光生电子(e~-)转移。利用活性物种捕获实验、循环实验研究了AgI/h-MoO_3光催化氧化脱硫机理及其稳定性,实验结果表明:AgI/h-MoO_3不仅具有较高的光催化氧化脱硫活性,而且还有良好的稳定性。     

Fabrication of AgI/MIL‐53(Fe) Composites with Enhanced Photocatalytic Activity for Rhodamine B Degradation under Visible Light Irradiation

AgI/MIL‐53(Fe) composites were fabricated through a simple solution method, and their photocatalytic activities on Rhodamine B (RhB) degradation were investigated. The results demonstrated that the introduction of AgI into the MIL‐53(Fe) was beneficial to the enhanced visible light response. Under visible light irradiation, almost 100 % RhB was bleached over AgI/MIL‐53(Fe) composites after 180 min. The promising photocatalytic performance was ascribed to three points: the existence of AgI helped to generate easily the electrons and holes in the composites; an intimate interfacial contact between MIL‐53 (Fe) and AgI offered the path for the charge carries transport; MIL‐53 (Fe) could fast transfer the excited electrons due to its inherent nature. Thus, these results were responsible for the effective inhibition of charge carrier recombination, resulting in an improved photocatalytic activity.     

Synthesis of V5+‐doped Ag/AgCl photocatalysts with enhanced visible light photocatalytic activity

V⁵⁺‐doped Ag/AgCl photocatalysts were prepared via the ion exchange method. The catalysts were characterized using X‐ray diffractometry, transmission electron microscopy, and energy‐dispersive X‐ray, X‐ray photoelectron, Fourier transform infrared and ultraviolet–visible spectroscopies. The V⁵⁺‐doped Ag/AgCl photocatalysts show much higher photocatalytic activities than Ag/AgCl under visible light irradiation for methyl orange (MO) decomposition. Especially, the 2.0 wt% V⁵⁺‐doped Ag/AgCl photocatalyst shows the highest photocatalytic activity and also high stability after five cycles. The MO degradation rate during each cycle is almost maintained at 97%. Electron spin resonance spectroscopy and radical trapping experiments reveal that holes play an important role in the photocatalytic process.     

Plasmonic Ag/AgCl‐modified bismuth subcarbonate with enhanced visible light photocatalytic activity

Plasmonic Ag/AgCl‐modified bismuth subcarbonate (Bi₂O₂CO₃) composites were prepared by a multistep process with hydrothermal, deposition, and photoreduction in the absence of organic capping agents. The properties of the obtained Ag/AgCl/Bi₂O₂CO₃ samples were characterized using X‐ray diffraction, field emission scanning electron microscopy and X‐ray photoelectron, UV–visible diffuse reflectance, and photoluminescence spectroscopies. The results reveal that Ag/AgCl nanoparticles are dispersed on the Bi₂O₂CO₃ surface to achieve plasmonic Ag/AgCl/Bi₂O₂CO₃. The Ag/AgCl/Bi₂O₂CO₃ nanocomposites show improved rhodamine B (RhB) adsorption capacity and photocatalytic activity compared with pure Bi₂O₂CO₃ and Ag/AgCl. In addition, the Ag/AgCl/Bi₂O₂CO₃ composite with 20 wt% Ag/AgCl exhibits the highest photocatalytic activity and remains stable for the photodegradation of RhB under visible light. The enhanced photocatalytic activity of Ag/AgCl/Bi₂O₂CO₃ may be attributed to the surface plasmon resonance effect of in situ generated Ag nanoparticles and synergistic effect of Ag/AgCl and Bi₂O₂CO₃, which increase the separation efficiency of photogenerated electron–hole pairs under visible light irradiation.     

薄膜表面等离子体光催化剂Ag@AgBr/CNT/Ni的制备和性能

用复合电沉积技术制备了Ag@AgBr/CNT/Ni表面等离子体薄膜催化剂,以扫描电镜（SEM）、X射线衍射（XRD）、拉曼光谱（Raman Spectra）、X射线光电子能谱（XPS）和紫外-可见漫反射光谱（UV-Vis DRS）对薄膜的表面形貌、晶体结构、化学组成和光谱特性进行了表征,在可见光照射下,用罗丹明B（RhB）作为模拟污染物对薄膜的光催化性质和稳定性进行测定,采用测定薄膜电化学阻抗谱（EIS）和向反应系统中加入活性物种捕获剂的方法对薄膜光催化机制进行探索。结果表明：最优工艺下制备的Ag@AgBr/CNT/Ni薄膜是由少量碳纳米管（CNT）和表面沉积纳米Ag粒子的AgBr晶体构成的复合薄膜。薄膜具有突出的表面等离子体共振效应、优异的光催化活性和良好的催化稳定性。光催化罗丹明B 20 min,Ag@AgBr/CNT/Ni薄膜的降解率是Ag@AgBr/Ni薄膜的1.32倍,是P25 TiO₂/ITO多孔薄膜的21.6倍。在保持光催化性能基本不变的前提下可循环使用5次。CNT的存在使薄膜电荷传导性能和光催化还原溶解氧的性能大幅增加,是所制薄膜相对于Ag@AgBr/Ni薄膜光催化性能提高的主要原因。提出了薄膜光催化罗丹明B的反应机理。     

Z-scheme TiO2/g-C3N4 composites prepared by hydrothermal assisted thermal polymerization with enhanced visible light photocatalytic activity

Melamine was added to the precursor of TiO₂, then TiO₂ prepared by hydrothermal, while melamine was modified. Subsequently, a series of Z-scheme TiO₂/g-C₃N₄ heterojunction composites were successfully synthesized by simple calcination. The morphology and structure of samples were characterized by XRD, FT-IR, UV–vis DRS, SEM, TEM, PL and BET. The photocatalytic activity of these samples has been investigated by degradation of Rhodamine B (RhB), and results indicated that photocatalytic activity of the as-prepared samples was greatly influenced by the content of titanium tetrabutoxide in precursors and the hydrothermal time. The degradation rate of TiO₂/g-C₃N₄-1 to RhB was the best, which was 5.05-fold of pure TiO₂ (19.61%) and 2.25-fold of bulk g-C₃N₄ (44.06%), respectively. The trapping experiment results showed that ^·O₂^? and h⁺ were main active species during degradation of RhB. The photocatalytic activity of the sample did not decrease significantly after 4 cycles. The unique Z-scheme heterojunction between TiO₂ and g-C₃N₄ improved photocatalytic activity of the samples under visible light.