LED用红色荧光粉NaGdTiO4∶Sm3+的合成与发光性能

采用高温固相法制备了白光LED用NaGd(1-x)TiO4∶xSm3+系列红色荧光粉,并对样品分别进行了X射线衍射分析和荧光光谱测试.结果表明,样品可以被紫外、近紫外和蓝光有效激发,在409 nm激发下,该荧光粉有三个主要发射峰,位于567 nm、607 nm和652 nm处,分别对应于Sm3+的4G/2→6H5/2、4G5/2→6H7/2、4G5/2→6H9/2的跃迁发射,其中607 nm处发射最强,呈现红色发光.当Sm3+的掺杂浓度为2.5mol;时,达到最佳的发光效果.因此,这种荧光粉是一种有应用潜力的白光LED红色荧光粉.     

橙红色荧光粉Ca10Li(PO4)7∶Sm3+的合成及其发光特性研究

采用固相法合成了Ca10Li(PO4)7∶xSm3+橙红色荧光粉,研究了材料的发光性质.结果表明,以404 nm近紫外光作为激发源时,Ca10Li(PO4)7∶xSm3+表现为多峰特征,主峰位于569 nm、606 nm、651 nm和713 nm,分别对应Sm3+的4G5/2→6H5/2、4G5/2→6H7/2,4 G5/2 →6H9/2 and 4 G5/2 →6H11/2跃迁发射,且606 nm发射峰最强,材料发射橙红光;监测606 nm发射峰,对应的激发光谱包含363 nm、376 nm、404 nm和478nm多个激发峰;改变Sm3+的掺杂量,发现Ca10 Li(PO4)7∶Sm3+的发射强度表现出先增大、后减小的变化趋势,x=0.05时发射强度最大,即存在浓度猝灭现象,造成浓度猝灭的机理为电多极相互作用,Ca10Li(PO4)7∶Sm3+的色坐标基本不变,位于橙红色区域.Ca10Li(PO4)7∶Sm3+具有较好的温度特性,激活能为0.188 eV.     

Er3+单掺与Er3+/Yb3+共掺NBT-CT无铅压电陶瓷的上转换发光性能研究

采用固相烧结法制备一系列Er³⁺单掺与Er³⁺/Yb³⁺共掺0.96Na_0.5Bi_0.5TiO₃-0.04CaTiO₃(NBT-CT∶xEr³⁺/yYb³⁺,x=0.002~0.015,y=0.010)无铅压电陶瓷。通过X射线衍射仪和荧光光谱仪分别对样品的物相结构和上转换发光特性进行表征和分析。结果表明,样品的主晶相为NBT晶相。在波长为980 nm的近红外光激发下,Er³⁺单掺与Er³⁺/Yb³⁺共掺NBT-CT陶瓷均呈现强的以绿光为主的Er³⁺特征上转换发光。在NBT-CT∶xEr³⁺中,当x=0.010时上转换发光性能最佳;Yb³⁺能够起到敏化作用,明显增强Er³⁺的上转换发光强度。     

白光LED用K2Ba(WO4)2∶Sm3+红色荧光粉的制备与表征

采用高温固相法合成了一种新型K2Ba(WO4)2∶xSm3+红色荧光粉.通过XRD、SEM和荧光分光光度计对样品的结构、形貌和发光性能进行了研究.结果表明:该荧光粉具有三方晶系结构,在402 nm处有较强的激发峰,与近紫外LED芯片相匹配.在402 nm激发下,出现了Sm3的4G5/2→6 HJ(J=5/2,7/2,9/2,11/2)的特征跃迁,最强峰位于602 nm处,对应于Sm3+的4G5/2→6H3/2跃迁.Sm3+的最佳掺杂量为x=0.02,且Sm3+之间的临界距离为2.776 nm,浓度猝灭的机理为电偶极-电偶极相互作用.     

Na2SrP2O7∶Sm3+橙色荧光粉的制备与发光性能的研究

利用稀土离子Sm3+作为激活剂,采用传统的高温固相法制备了Na2SrP2O7∶xSm3+(x=0.02mol;)橙色荧光粉.用扫描电镜、X射线衍射仪和荧光分光光度计对粉体的表面形貌、晶体结构和荧光光谱进行了表征.XRD分析和荧光光谱分析得出:最佳的烧结温度为700℃.该荧光粉能够被404 nm光高效激发,发射光谱在可见光区呈三峰发射,峰值位于564 nm、603 nm、647 nm,其最强发射峰位于603 nm处,对应于Sm3的4G5/2→6H7/2特征发射.设定发射波长为603 nm,得到荧光粉的激发光谱为一个主峰位于404 nm的宽带激发峰,表明该荧光粉可被紫外光和近紫外光有效地激发.研究了Sm3+掺杂浓度和助熔剂NH4Cl含量对Na2SrP2O7∶Sm3+橙色荧光粉荧光性能的影响,得出Sm3+的最佳掺杂量为2mol;.3wt;的助熔剂NH4Cl有利于荧光粉颗粒的分散,减小平均粒径,改善晶粒形貌,提高荧光粉的相对发光强度,还能降低制备所需的温度.     

CaGd2(MoO4)4:Sm3+,La3+荧光粉的 制备及发光性能研究

采用高温固相法合成了CaGd2-x(MoO4)4:xSm3+(x=0.1、0.3、0.5、0.7、0.9)橙红色荧光粉.研究了样品的X射线衍射谱(XRD)、激发光谱和发射光谱.从XRD图谱测试结果表明,在900℃下烧结6 h后得到的样品为纯CaMnO4晶相,样品CaGd2(MoO4)4:Sm3+的激发光谱由两部分组成:一部分(250～340)nm为属于O2--M6+O的电荷迁移带;另一部分(350～450)nm的系列线状峰是Sm3+的f-f跃迁特征激发峰.样品在405 nm(6H5/24F7/2)下激发得到的发射光谱,其主发射峰位于646 nm(6 G5/26 H7/2)处.当Sm3+掺杂浓度高于2;时,样品CaGd2-x(MoO4)4:xSm3+发生浓度猝灭现象,该现象是由于离子间的能量传递.在CaGd1.5(MoO4)4:0.5Sm3+样品中掺入一定浓度La3+,掺入La3+并没有改变CaGd2(MoO4)4:Sm3+光谱峰的形状和位置,当y=0.8时,荧光粉的发光强度最好.通过测量计算GIE在405 nm激发下的色坐标,显示色坐标均在橙红色区域移动,表明荧光粉的光色性较好.     

Synthesis and Luminescence Properties of Red Phosphor SrCeO3∶ Sm3 +

采用溶胶-凝胶法合成了SrCeO3∶Sm3+红色荧光粉,用XRD、SEM、FL分析表征了样品的结构、形貌及发光性能.研究了助熔剂H3BO3对其发光性能的影响.结果表明:样品为具有正交晶系结构的SrCeO3晶型,呈椭球型结构.荧光光谱测试结果表明:Sm3+掺杂的SrCeO3在紫外波段有两个吸收带,一是峰值位于320 nm左右的宽吸收带,归属于Ce4+→O2-的电荷迁移带,另一个为峰值位于408nm的锐线吸收带,对应于Sm3+的6H5/2→L13/2跃迁吸收;在波长408nm的激发下,样品发红光,发射主峰位于601nm,对应于Sm3+的4G/2 →6H7/2跃迁.样品的发光强度随着Sm3+和助熔剂H3BO3加入量的增加先增强,后减弱.当Sm3+的掺杂最为3mol％,H3 BO3加入量为0.5 mol％时,发光强度最大.     

近紫外激发的Na2ZnSiO4∶Sm3+橙红色荧光粉的合成及发光性能

采用溶胶-凝胶法制备了适合于近紫外激发的橙红色荧光粉Na2 ZnSiO4∶Sm3+,利用X射线衍射、扫描电镜、荧光光谱对样品的相结构、形貌及发光性能进行了表征.结果表明:制得的样品属于单斜晶系,粒径约为2 μm.样品的激发光谱在330 ～ 550 nm间呈多峰分布.在404 nm近紫外光激发下,发射光谱由峰值为566 nm,604 nm和650 nm的3个峰构成,发射主峰位于604 nm处,对应Sm3+的4 G5/2→6H7/2跃迁,呈橙红光发射.当Sm3+的掺量为3;时,其发光强度达到最大,随后减小,是由电偶极-电偶极相互作用引起的浓度猝灭.     

冷白光荧光粉ZnWO4∶Sm3+的制备及发光性质

采用水热法经过煅烧热处理成功制备了ZnWO4∶Sm3+白色荧光粉.通过X射线粉末衍射仪,扫描电子显微镜及荧光分光光度计对样品的物相结构、形貌粒度及发光性能进行了分析和表征.结果表明:在pH值为6和7下,所合成的ZnWO4∶Sm3+晶体结构与ZnWO4相似,为单斜晶系结构,样品颗粒为类球形,颗粒尺寸范围为100 ～ 220 nm.Sm3的摩尔掺杂量为0.5;时,发射峰强度达到最大值;继续增加Sm3+浓度,其发射峰强度反而减弱,出现了浓度猝灭效应.在254 nm波长激发下,ZnWO4∶Sm3+的色坐标集中在冷白光区.     

Bi2O3掺杂Sm0.5Sr0.5CoO3-δ的制备与光学性能研究

采用固相法制备(Sm1-xBix)05Sr05CoO3-δ (0≤x≤0.5),研究不同Bi3+掺杂浓度对材料的晶体结构、表面形貌与光学性能的影响.结果表明,当掺量0≤x(Bi3+)≤0.2,材料为单一纯相的钙钛矿结构;当掺量0.3≤x≤0.5,材料主相仍保持着钙钛矿结构,同时出现杂相CoO与Sr0.5CoBi0.5Ox.(Sm1-xBix)05Sr05CoO3-δ平均粒径随着Bi3+掺量的增加由1.98 μm增大为9.77 μm,晶粒形状由多边形状变为方块状;光学测试表明,随着Bi3+浓度的增加,材料的光学吸收率由0.73增大到0.87,发射率由0.34增大到0.80.     

溶胶-凝胶法制备Na0.5Bi0.5TiO3-K0.5Bi0.5TiO3体系无铅压电陶瓷的研究

采用溶胶-凝胶法制备(1-x)Na0.5Bi0.5 TiO3-xK0.5Bi0.5TiO3体系无铅压电陶瓷.XRD分析表明,用溶胶-凝胶法可以在650℃下合成具有钙钛矿结构的(1-x)Na0.5Bi0.5TiO3-xK0.5Bi0.5TiO3粉体,且在x=0.18～0.30之间存在三方-四方准同型相界(MPB).陶瓷的压电性能参数表明,该体系在MPB组成范围内具有最佳的压电性能:x=0.30时,压电常数d33达到最大值(d33=150 Pc·N-1),平面机电耦合系数kp与介电常数εH33T/ε0均在x=0.26时达到最大值,分别为36.7;和1107.     

Direct preparation of K0.5Na0.5NbO3 powders

K_0.5Na_0.5NbO₃ powders have been directly synthesized by an alternative solid–state method. Stoichimometric mixture of ammonium niobium oxalate and C₄H₄O₆KNa·4H₂O were calcined in temperature range from 500 to 800 °C for 3 h. The precursor and calcination products were characterized with respect to stoichiometry, purity, crystalline structure, particle size and powder morphology using X–ray diffraction (XRD), X‐ray fluorescence (XRF) spectrometer, scanning electron microscope (SEM), Fourier transform infrared (FTIR) spectra, thermogravimetric (TG) analysis, differential scanning calorimetry (DSC) and UV–Vis diffuse reflectance (UV–Vis) spectroscopy. XRD and XRF results reveal that stoichiometric K_0.5Na_0.5NbO₃ powders could be synthesized by the method. The particle size is about 68 nm for the precursor calcined at 500 °C according to XRD data, which is in good agreement with SEM data. The average band gap energy is estimated to be 3.18 eV by UV–vis diffuse reflectance spectra. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Bi(Zn0.5Ti0.5)O3对Bi0.5Na0.5TiO3基陶瓷相结构及弛豫性的影响

采用固相反应合成法制备了(1-x)(0.96Bi0.5Na0.5TiO3-0.04BaTiO3)-xBi(Zn0.5 Ti0.5)O3陶瓷(x≤0.10).通过X射线衍射,介电温度谱等对该体系陶瓷的相结构及弛豫特性进行了研究.结果发现,该陶瓷在Bi(Zn0.5Ti05)O3加入量低于0.05时呈现纯钙钛矿结构.此外,随着Bi(Zn0.5Ti0.5)O3加入量的增加,其相结构由三方-四方共存向赝立方结构转变;同时,陶瓷的弥散因子上升,偶极子取向冻结活化能下降,表明BZT的加入明显地增加了0.96Bi0.5Na0.5TiO3-0.04 BaTiO3陶瓷的弛豫性.     

(Na0.5Bi0.5)TiO3-(K0.5Bi0.5)TiO3无铅铁电单晶的生长、结构与介电特性

采用高温自助熔剂法制备了(Na0.5Bi0.5) TiO3-(K0.5Bi0.5) TiO3(简称:NBT-KBT)无铅铁电单晶,晶体尺寸为5mm×6 mm×1 mm.利用X射线衍射(XRD)手段研究了NBT-KBT单晶的相结构,结果表明晶体样品为钙钛矿四方相结构.Raman散射结果也表明了NBT-KBT单晶的拉曼振动模式具有四方相结构特征.利用扫描电镜(SEM)和透射电镜(TEM)研究了单晶的表面形貌和微结构特征.另外,单晶介电常数随温度以及频率的变化关系显示单晶具有弛豫铁电体特性.     

硅基外延SrRuO3/PbZr0.5Ti0.5O3/SrRuO3电容器的结构和性能研究

传统的方法很难直接在硅衬底上制备外延的氧化物铁电电容器,本实验采用生长在硅衬底上的外延SrTiO3为模板,直接生长了SrRuO3/PbZr0.5Ti0.5O3/SrRuO3电容器异质结,并对其结构及性能进行了研究.X射线衍射表明所制备的SrRuO3/PbZr0.5Ti0.5O3/SrRuO3异质结实现了在硅衬底上的外延生长.在5V测试电压下,铁电电容器的剩余极化强度和矫顽电压分别为19.6μC/cm2和0.8V.当极化翻转次数达到1010时,铁电电容器的极化强度没有明显的衰减,表明SrRuO3/PbZr0.5Ti0.5O3/SrRuO3电容器具有良好的抗疲劳性能.     

含NiTi阻挡层的硅基(La0.5Sr0.5)CoO3/Pb(Zr0.4Ti0.6)O3/(La0.5Sr0.5)CoO3铁电电容器异质结

应用磁控溅射法制备的非晶NiTi薄膜作阻挡层,在Si (100)衬底上构造了(La0.5Sr0.5)CoO3/ Pb(Zr0.4Ti0.6)O3/(La0.5Sr0.5)CoO3(LSCO/PZT/LSCO)铁电电容器异质结,研究了Pb(Zr0.4Ti0.6)O3铁电薄膜的结构和物理性能.实验发现LSCO/PZT/LSCO铁电电容器具有良好的电学性能,在417kV/cm的驱动场强下,PZT铁电电容器具有较低的矫顽场强(125kV/cm)和较高的剩余极化强度(19.0μC/cm2),良好电容-电压特性(C-V)和保持特性,铁电电容器经过1010次反转后,极化强度没有明显下降,表明了非晶NiTi薄膜可以用作高密度硅基铁电存储器的扩散阻挡层.     

Na0.5Bi0.5TiO3-K0.5Bi0.5TiO3-BaMnO3无铅压电陶瓷的结构与电性能

采用固相法制备了(0.8 -x)Na0.5 Bi0.5TiO3 -0.2K0.5Bi0.5TiO3-xBaMnO3(简称NBT-KBT-BM)无铅压电陶瓷,研究了不同BM含量(x=0,0.25％,0.50％,0.75％,1.00％,1.25％,物质的量分数)样品的物相组成、显微结构及电性能.结果表明:所制备的NBT-KBT-BM陶瓷样品均为单一的钙钛矿结构.与纯NBT-KBT陶瓷相比,掺BM陶瓷的烧结温度降低,相对密度ρr得到提高.随x的增加,材料的压电常数d33、平面机电耦合系数kp与机械品质因子Qm先增大后减小,而介电损耗tanδ以及退极化温度Td一直降低.BM的掺入降低了材料的矫顽场Ec,提高了剩余极化强度Pr,从而增强了铁电性.当x=0.75％时,陶瓷获得最佳性能:d33=167 pC/N,kp=0.269,Qm=133,εr=774,tanδ=2.93％.     

Crystal structure and magnetic properties of the LaCo0.5Fe0.5O3 perovskite

The magnetic and crystal structures of the LaCo_0.5Fe_0.5O₃ perovskite are investigated. It is established that the unit cell of this compound at room temperature is characterized by rhombohedral distortions. As the temperature decreases, the compound undergoes a structural phase transition from the rhombohedral phase to the orthorhombic phase in the temperature range 200–300 K. The LaCo_0.5Fe_0.5O₃ perovskite has an antiferromagnetic structure with the G _z spatial orientation of the antiferromagnetic vector. The magnetic properties of the LaCo_0.5Fe_0.5O₃ perovskite are interpreted within a model according to which the ground state of Co³⁺ ions is a low-spin state and the existence of the weak ferromagnetic component is associated with the exchange interactions between the Fe³⁺ ions.     

织构化K0.5Na0.5NbO3无铅压电陶瓷的性能研究

以分析纯Na2CO3、Bi2O3和Nb2O5为原料,以NaCl为熔盐,采用二次熔盐法和拓扑化学反应法合成各向异性片状NaNbO3粉体.以该片状NaNbO3粉体为模板品粒,以固相法合成的NaNbO3和KNbO3粉体为基料,采用流延工艺制备出较高取向度的织构化K0.5Na0.5NbO3(KNN)无铅压电陶瓷,系统研究了模板含量、烧结温度和保温时间等工艺参数对织构化KNN陶瓷显微结构和压电性能的影响规律.研究结果表明:随着模板含量的增加,陶瓷的取向度逐渐增加,当模板含量为15 wt;时,陶瓷的取向度可达0.69,当模板含量为10 wt;,1100 ℃下保温5 h烧结,可以获得具有一定织构度(f=0.58)的KNN陶瓷,并表现出优异的压电性能,d33=128 pC/ N.     

无铅高居里点BaTiO3-Bi0.5K0.5TiO3陶瓷的制备及其PTC性能的研究

采用固相反应法制备了(1-χ)BaTO3-χBi0.5K0.5TiO33(BT-BKT,χ=0,0.1和0.2),对陶瓷样品进行X射线衍射、扫描电镜、介电常数-温度及电阻率-温度测试分析,研究了掺杂BKT对该系统陶瓷相组成、显微结构和电性能的影响.结果表明:BaTi3,陶瓷的晶格参数c轴值随着BKT含量的增加基本不变,而a轴值有所减小.BT-BKT陶瓷的居里温度(Tc)随着BKT的加入向高温移动,当χ=0.1和0.2时,Tc分别提高至170℃和185℃左右;但室温电阻率随着BKT含量的增加明显增大.