Structural and magnetic ordering in the VxNb1+yS2 system

The influence of composition on the structural ordering and magnetism in the V_xNb_1+yS₂ system has been investigated by X-ray diffraction and magnetic measurements. Stoichiometric V_1/3NbS₂ did not exhibit the structural ordering of vanadium between the NbS₂ layers. In the ordered structure, the vanadium composition deviated from the ideal value of to both higher and lower values, while the niobium composition was in the range of 0.05?y?0.18. Excess niobium, y>0, is thought to play an essential role in the structural ordering in this system. For samples with excess niobium and ordered structures, a magnetic transition was observed at 20-50 K, depending on the composition. The spontaneous magnetization of 3-5×10⁻³ μ_B/V atom is thought to be intrinsic to this system. The magnetization curves consisted of a constant and a proportional parts of the magnetic field, which correspond to the spontaneous magnetization and high-field susceptibility, respectively. The magnetization curves and the temperature dependencies of the high-field susceptibility were quite similar to those of the canted antiferromagnetic NiS₂. A correlation between the structural and magnetic ordering is suggested.     

Superconductivity and calorimetric studies of Pr1.85Ce0.15CuO4+δ under different annealing conditions

Polycrystalline samples of electron-doped Pr_1.85Ce_0.15CuO_4+δ have been prepared under different annealing conditions and investigated by means of X-ray-diffraction, oxygen content analysis, electrical resistivity, magnetic susceptibility and low temperature specific heat measurements. X-ray-diffraction patterns show that samples contain a single T′ phase. The superconducting transition temperatures T_cm taken with the onset of diamagnetism in magnetic-susceptibility measurements are 20 and 19.5 K for sample annealed in flowing Ar gas and in vacuum (∼10⁻³ torr), respectively. The data of the samples, which are annealed in flowing Ar gas, show clear evidence for an αT² term at zero magnetic field in superconducting electronic specific heat, and are consistent with d-wave superconductivity. However, this behavior is not observed in the other sample, which is annealed in vacuum. These results indicate that different heat treatments affect the oxygen content, homogeneity, superconducting transition temperature T_c, superconducting volume fraction, and the superconducting pairing symmetry of Pr_1.85Ce_0.15CuO_4+δ.     

Selected properties of EuCo2(Si1−xGex)2 alloys

EuCo₂(Si_1−xGe_x)₂, x=0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1 samples were synthesised by induction melting followed by annealing at 900 °C and rapid quenching. X-ray powder diffraction and Auger electron spectroscopy studies revealed that solid solutions are formed only for x?0.2 and x?0.7. Magnetic susceptibility investigations for the solid solutions revealed a dominant divalent europium valence state in the germanium-rich samples and a dominant trivalent europium component in the silicon-rich samples. In the germanium-rich samples, a long-range antiferromagnetic ordering was observed. In all samples studied, additional magnetic transitions at various temperatures were detected, which could be attributed to small clusters containing different europium chemical surrounding from that in the predominant phase.     

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetism in Fe- and Ni-co-doped In₂O₃ samples (In_0.9Fe_0.1−xNi_x)₂O₃ (0?x?0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at room-temperature. The highest saturation magnetization (0.453 μ_B/Fe+Ni ions) moment is reached in the sample with x=0.04. The highest solubility of Fe and Ni ions in the In₂O₃ lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10 at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases.     

Dielectric properties of valence compensated Ca1−xBixTi1−xCrxO3 perovskite prepared using the sol-gel process

Ca_1−xBi_xNb_1−xCr_xO₃ (x=0.01-0.5) ceramic powders were synthesized using the sol-gel process. The single-phase solids can be presented at x=0.01 and 0.03. The coexistence of orthorhombic perovskite and the secondary phase of BiCrO₃ was verified, as presented for x=0.05-0.5. Grains with a micro-cube topography were obtained for x=0.3-0.5. The average grain size is about 0.4 and 1.1 μm for x=0.3 and 0.5, respectively. The highest dielectric constant peak was measured at around 55 °C for x=0.5 and at 75 °C for x=0.3. The high dielectric constant was caused by the formation of barrier layers at the interface of the bi-phase mixed ceramics. Space charge polarization contributed to the observed behavior.     

Coexistence of superconductivity and magnetism in the La0.87−xLnxSr0.13FeAsO (Ln=Sm, Gd, Dy) system

The interplay between the superconducting phase and spin density wave order phase was studied. We report the magnetic and superconducting properties of the hole-doped FeAs-based superconducting compound La_0.87−xLn_xSr_0.13FeAsO (Ln=Sm, Gd, Dy; 0≤x≤0.06). Both resistivity and magnetic susceptibility measurements show that the superconducting transition temperature decreases with increase in composition of magnetic ions. The hysteresis loop of the La_0.87−xLn_xSr_0.13FeAsO sample shows a superconducting hysteresis in addition to a paramagnetic background. The experiment demonstrates that the magnetism and superconductivity coexist in hole-doped FeAs-based superconducting compounds. Among these three magnetic rare-earth elements, the influence of Dy³⁺ doping on superconductivity is more evident than that of Gd³⁺ doping, while the influence of Sm³⁺ doping is the weakest. The trend is consistent with the variation of the lattice parameter along c-axis.     

Spin-glass-like behavior in ZnxCryAlzSe4

The magnetic and electrical properties of the Al-doped polycrystalline spinels Zn_xCr_yAl_zSe₄ (0.13≤z≤0.55) with the antiferromagnetic (AFM) order and semiconducting behavior were investigated. A complex antiferromagnetic structure below a Néel temperature T_N≈23 K for the samples with z up to 0.4 contrasting with the strong ferromagnetic (FM) interactions evidenced by a large positive Curie-Weiss temperature θ_CW decreasing from 62.2 K for z=0.13 to 37.5 K for z=0.55 was observed. Detailed investigations revealed a divergence between the zero-field-cooling (ZFC) and field-cooling (FC) susceptibilities at temperature less than T_N suggesting bond frustration due to competing ferromagnetic and antiferromagnetic exchange interactions in the compositional range 0.13≤z≤0.4. Meanwhile, for z=0.55 a spin-glass-like behavior of cluster type with randomly oriented magnetic moments is observed as the ZFC-FC splitting goes up to the freezing temperature T_f=11.5 K and the critical fields connected both with a transformation of the antiferromagnetic spin spiral via conical magnetic structure into ferromagnetic phase disappear.     

Magnetic phase diagram of double-layered La2−2xCa1+2xMn2O7 manganite

Double-layered manganite La_2−2xCa_1+2xMn₂O₇ have been synthesized for compositions ‘x’=0.0, 0.1, 0.2, 0.3, 0.4 and 0.5 by solid state reaction method. From X-ray diffraction study, their crystal structures were found to be tetragonal perovskite with lattice parameters decreasing with increasing ‘x’. The decreasing lattice parameters affect the balance between in-plane, intra-bilayer and inter-bilayer exchange interactions, which is reflected on magnetotransport properties. The metal-to-insulator transition temperature is found to vary with composition and peaked around ‘x’=0.3. From ac-susceptibility study, 2D-ferromagnetic ordering was observed at higher temperatures for all compositions whereas 3D-ferromagnetic ordering was observed at quite low temperatures. In low-temperature region, decreasing susceptibility shows antiferromagnetic state for all compositions. On the basis of electrical and magnetic properties, a magnetic phase diagram is given.     

Magnetic properties of compounds in the system CaBaCo4−x−yZnxAlyO7 (x=0,1,2, y=0,1)

The magnetic properties of four compounds in the series CaBaCo_4−x−yZn_xAl_yO₇ (x=0,1,2, y=0,1) were investigated. Using AC-susceptibility and DC-magnetometry, magnetic transitions (T_fs) were found for all four compositions in the range 50-3 K. The data from the AC measurements proved to be frequency dependent: T_f increases with higher frequencies. An energy-loss in the magnetic coupling, indicated as contributions in the imaginary part of the magnetic susceptibility (χ″), was seen for every compound and its maximum appeared just below the maximum χ′. Modelling the data with Arrhenius-, Vogel-Fulcher-, and the power-law made it possible to relate the four compounds to spin-glass materials. The Casimir-du Pré relation was used to extract average relaxation times at T_f. The DC magnetisations clearly show differences between field-cooled and zero-field-cooled measurements. None of the compounds exhibit any metamagnetic properties up to 8 T. A new method is presented to calculate the saturation fields using DC data. Relaxation measurements on three compounds indicate that the systems relax very fast, in contrast to spin-glasses. Aging does not affect the fast relaxations. The compounds are interpreted as disordered anti-ferromagnets with spin-glass features.     

Effect of holmium substitution for the improvement of multiferroic properties of BiFeO3

This paper reports on multiferroic properties of Ho substituted BiFeO₃ (Bi_1−xHo_xFeO₃) ceramics. It is observed that for x=0.15, a prominent ferroelectric loop is seen at 300 K even if the system remains in rhombohedral (R3c) phase without appearance of any observable impurity phases. A well shaped M-H loop is observed at 10 K for x=0.15. However it showed ferromagnetism, confirming the contribution of Ho³⁺ towards enhancement of ferromagnetic properties of BiFeO₃ at 300 K. Suppression of impurity phases of pure BiFeO₃ bulk ceramic favors the reduction of mobile oxygen vacancies and reduces leakage current, due to which ferroelectric properties of BiFeO₃ is enhanced. We argue that Ho substitution at Bi site is likely to suppress the spiral spin modulation and at the same time increase the canting angle, which favors enhanced multiferroic properties. XRD, SEM, magnetization, polarization and chemical bonding analysis measurements were carried out to explain the multiferroic behavior.     

Synthesis and physical properties of alkaline earth metal graphite compounds

We report synthesis and search for superconductivity of Ba, Sr, Ca and Mg-GIC. We adopted conventional vapor phase reaction in order to prepare high quality GICs. No superconducting transition was found for Ba and Mg-GIC. As for Sr, Sr-GIC showed a sharp superconducting transition at T_c=1.65 K. Sr graphite compound SrC_x prepared from powder graphite by thermal treatment at higher temperature showed ferromagnetic character.     

Suppression of Tc by Zn impurity in the electron-type LaFe0.925−y Co0.075ZnyAsO system

The effect of non-magnetic Zn impurity on superconductivity in electron-type pnictide superconductor LaFe_0.925−yCo_0.075Zn_yAsO is studied systematically. The optimally doped LaFe_0.925Co_0.075AsO without Zn impurity exhibits superconductivity at T_c^mid of 13.2 K, where T_c^mid is defiend as the mid-point in the resistive transition. In the presence of Zn impurity, the superconducting transition temperature, T_c^mid, is severely suppressed. The result is consistent with the theoretic prediction on the effect of non-magnetic impurity in the scenario of s_± pairing, but it is in sharp contrast to the previous report on the effect of Zn impurity in the F-doped systems. The possible interpretation of the different effects of Zn impurity on superconductivity in different systems is discussed.     

Structural and magnetic properties of ferromagnetic In1−xMnxAs1−yPy layers

The structural and magnetic properties of epitaxial In_1−xMn_xAs_1−yP_y quaternary layers with Mn content ranging from 0.01 to 0.04 and phosphorous content ranging from 0.11 to 0.21 were studied. X-ray diffraction indicated that the films were two phase consisting of an InMnAsP solid solution and hexagonal MnAs nanoprecipitates. Addition of phosphorus promoted precipitate formation. Films were ferromagnetic showing hysteretic behavior in the field dependence of magnetization at 5 and 298 K. From field-cooled magnetization measurements ferromagnetic transitions were observed at 280 and 325 K. The zero field-cooled magnetization versus temperature measurements showed irreversibility for T<300 K that was attributed to the presence of MnAs nanoprecipitates. The calculated coercivity using the Neel model was 1380 G compared to the experimental value of 380 G at 5 K. The difference was attributed to a strong inter-cluster exchange that stabilizes the ferromagnetic state.     

Superconducting properties of SmFeAsO1−x prepared under high-pressure condition

Synthetic conditions such as stoichiometries, temperature and pressure are optimized to achieve a high quality oxygen deficient SmFeAsO_0.6 superconductor. Both electric and magnetic measurements show a sharp superconducting transition at about 55 K. Several important physical parameters are deduced. The apparent superconducting gap observed in heat capacity with 2Δ_o/k_BT_c of 4.57 larger than that of previous fluorine replaced samples indicate that this superconductivity will not strongly conflict with the phonon-mediated BCS mechanism. The mean free length ?=18.8 nm and the coherent length ξ=2.3-3.3 nm show that the superconductivity is in the clean limit.     

Magnetic behavior of MnAs precipitates in Ga1−xMnxAs diluted magnetic semiconductor

Ferromagnetic Ga_1−xMn_xAs layers (where x≈4.7–5.5%) were grown on (1 0 0) GaAs substrates by molecular beam epitaxy. These p-type (Ga,Mn)As films were revealed to have a ferromagnetic structure and ferromagnetism is observed up to a Curie temperature of 318 K, which is ascribed to the presence of MnAs secondary magnetic phases within the film. It is highly likely that the phase segregation occurs due to the high Mn cell temperature around 890–920 °C, as it is well established that GaMnAs is unstable at such a high temperature. The MnAs precipitate in the samples with x≈4.7–5.5% has a Curie temperature T_c≈318 K, which was characterized from field-cooled and zero-field-cooled magnetization curves.     

Effects of Zn on the grain boundary properties of La2−xSrxCu1−yZnyO4 superconductors

The properties of the grain boundaries (GBs) are of significant importance in high-T_c cuprates. Most large scale applications of cuprate superconductors involve usage of sintered compounds. The critical current density and the ability to trap high magnetic flux inside the sample depend largely on the quality of the GBs. Zn has the ability to pin vortices but it also degrades superconductivity. In this study we have investigated the effect of Zn impurity on the intergrain coupling properties in high-quality La_2−xSr_xCu_1−yZn_yO₄ sintered samples with different hole concentrations, p (≡x), over a wide range of Zn contents (y) using field-dependent AC susceptibility (ACS) measurements. The ACS results enabled us to determine the superconducting transition temperature T_c, and the temperature T_gcp, at which the randomly oriented superconducting grains become coupled as a function of hole and disorder contents. We have analyzed the behavior of the GBs from the systematic evolution of the values of T_gcp(p, y), T_c(p, y), and from the contribution to the field-dependent ACS signal coming from the intergrain shielding current. Zn suppresses both T_c and T_gcp in a similar fashion. The hole content and the carrier localization due to Zn substitution seem to have significant effect on the coupling properties of the GBs. We have discussed the possible implications of these findings in detail in this article.     

Low field AC susceptibility study of intergranular critical current density in Mg-substituted CuBa2Ca3Cu4O12−y high temperature superconductors

Measurements of the a.c.susceptibility (χ=χ′+iχ″) have been made on the Mg substituted high T_C superconducting system, CuBa₂(Mg_xCa_1−x)₃Cu₄O_12−y (Cu-1234) with x=0, 0.10 & 0.20, at different values of the a.c.field amplitude. Estimates of the intergranular critical current density(J_C) made from the field dependent χ″-T curves show an improvement in the Mg-substituted Cu-1234 system. Results have been analysed in the light of the crystal structure and the superconducting anisotropy factor (γ=ξ_ab/ξ_c) of the Cu-1234 system. Lower superconducting anisotropy emanating from Mg substitution has been found to be significant, resulting in better superconducting properties.     

High sensitivity of magnetism of the “114” ferrimagnet CaBaCo4O7 to stoichiometry deviation

The effect of oxygen/cobalt off-stoichiometry upon magnetism in CaBaCo₄O₇ has been investigated. It is shown that the oxides CaBaCo₄O_7+δ and CaBaCo_4−xO_7−δ (0≤x≤0.20) synthesized below 1100 °C in air exhibit phase separation, where ferrimagnetic regions with T_C~56 K to 64 K coexist with regions of magnetic clusters. The latter are detected from ac-susceptibility measurements, which show various frequency dependent peaks at ~14–20 K, 37 K, and 45 K, depending on the stoichiometry. The origin of this phenomenon is attributed to the great sensitivity of the material to oxidation as the synthesis of temperature is lowered, leading to the introduction of additional Co³⁺ cations, with respect to the ideal formula CaBaCo₂²⁺Co₂³⁺O_7. This excess Co³⁺ tends to destroy the ferromagnetic zig-zag chains of the ferrimagnetic structure and creates various cobalt spin clusters, leading to the inherent phase separation in the samples.     

The influence of out-of-plane disorder on the formation of pseudogap and Fermi arc in Bi2Sr2−xRxCuOy (R=La and Eu)

We found that the length of the Fermi arc decreases with increasing out-of-plane disorder by performing angle resolved photoemission spectroscopy (ARPES) measurements in the superconducting state of optimally doped R=La and Eu samples of Bi₂Sr_2−xR_xCuO_y. Since out-of-plane disorder stabilizes the antinodal pseudogap as was shown in our previous study of the normal state, the present results indicate that this antinodal pseudogap persists into the superconducting state and decreases the Fermi arc length. We think that the shrinkage of the Fermi arc reduces the superfluid density, which explains the large suppression of the superconducting transition temperature when out-of-plane disorder is increased.     

High-resolution photoemission study of FeSr2YCu2O7+δ

We have performed high-resolution photoemission spectroscopy (PES) on FeSr₂YCu₂O_7+δ, of which superconductivity of T_c=49 K was recently reported. We clearly observed opening of a d-wave-like superconducting gap and estimated the maximum gap value (Δ_max) to be 10 meV at 15 K. This gap value gives 2Δ_max/k_BT_c∼5, suggesting a strong-coupling nature of superconductivity in FeSr₂YCu₂O_7+δ. Comparative PES study with superconducting and insulating samples shows that the valence band is rigidly shifted as a function of doping without evolution of additional states within the insulating gap.