Upconversion luminescence and mechanisms in Yb-sensitized Tm-doped oxyhalide tellurite glasses

Effect of Yb₂O₃ content on upconversion luminescence and mechanisms in Yb³⁺-sensitized Tm³⁺-doped oxyhalide tellurite glasses were investigated under 980 nm excitation. Intense blue and relatively weak red upconversion emission centered at 476 and 649 nm corresponding to the transitions ¹G₄→³H₆ and ¹G₄→³H₄ of Tm³⁺, respectively, are simultaneously observed at room temperature. The results show that upconversion blue and red emission intensities of Tm³⁺ first increase, reach its maximum at Yb₂O₃%=3 mol%, and then decrease with increasing Yb₂O₃ content. The effect of Yb₂O₃ content on upconversion intensity is discussed, and possible effect mechanisms are evaluated. The investigated results were conducing to increase upconversion luminescence efficiency of Tm³⁺.     

Multiphoton ultraviolet and visible upconversion luminescence of TmYb co-doped oxyfluoride glass

The ultraviolet upconversion luminescence of Tm³⁺ ions sensitized by Yb³⁺ ions in oxyfluoride glass when excited by a 975 nm diode laser was studied in this paper. One typical ultraviolet upconversion luminescence lines positioned at 362.3 nm was found. It can be attributed to the five-photon upconversion luminescence transition of ¹D₂ → ³H₆. Several visible upconversion luminescence lines at 451.1 nm, (477.9 nm, 462.5 nm), 648.7 nm, (680.5 nm, 699.5 nm) and (777.5 nm, 800.7 nm) were found also, which results from the fluorescence transitions of five-photon ¹D₂ → ³F₄, three-photon ¹G₄ → ³H₆, three-photon ¹G₄ → ³F₄, two-photon ³F₃ → ³H₆ and two-photon ³H₄ → ³H₆ of Tm³⁺ ion, respectively. The theoretical analysis suggests that the upconversion mechanism of the 362.3 nm ¹D₂ → ³H₆ upconversion luminescence is the cross energy transfer of {³H₄(Tm³⁺) → ³F₄(Tm³⁺), ¹G₄(Tm³⁺) → ¹D₂(Tm³⁺)} and {¹G₄(Tm³⁺) → ³F₄(Tm³⁺), ³H₄(Tm³⁺) → ¹D₂(Tm³⁺)} between Tm³⁺ ions. In addition, the upconversion luminescence of ¹G₄ and ³H₄ state results from the sequential energy transfer {²F_5/2(Yb³⁺) → ²F_7/2(Yb³⁺), ³H₄(Tm³⁺) → ¹G₄(Tm³⁺)} and {²F_5/2(Yb³⁺) → ²F_7/2(Yb³⁺), ³F₄(Tm³⁺) → ³F₂(Tm³⁺)} from Yb³⁺ ions to Tm³⁺ions, respectively.     

Broadband amplification and upconversion luminescence properties of Er/Yb co-doped fluorophosphate glass

Broadband and upconversion properties were studied in Er³⁺/Yb³⁺ co-doped fluorophosphate glasses. Large Ω₆ and S_ed/(S_ed+S_md) values and the flat gain profile over 1530-1585 nm indicate the good broadband properties of the glass system. And a premise of using Ω₆ as a parameter to estimate the broadband properties of the glasses is proposed for the first time to our knowledge. Results showed that fluorescence intensity, upconversion luminescence intensity, the intensity ratio of red/green light (656 nm/545 nm) are closely related to the Yb³⁺:Er³⁺ ratio and Er³⁺ concentration, and the corresponding calculated lifetime of ⁴F_9/2 and ⁴S_3/2 states for red and green upconversion samples proves this conclusion. The upconversion mechanism is also discussed.     

Comprehensive research about the cooperative up-conversion luminescence of the ytterbium-doped oxyfluoride vitroceramics

The cooperative up-conversion blue luminescence of Yb^{3+} ion-doped oxyfluoride vitroceramic material (Yb:FOV) and the influence of co-doped Ho^{3+} ion, when excited by a 960 nm diode-laser, are studied in this paper. A strong blue 479.1 nm up-conversion luminescence of the Yb:FOV material is discovered. It is found that the 479.1 nm luminescence results from the cooperative up-conversion of the coupled states of the Yb^{3+}－Yb^{3+} clusters formed by two adjacent Yb^{3+} ions. The measured cooperative up-conversion luminescence main peak 479.1 nm of this paper is different from the characteristic fluorescence main peak of the Tb^{3+} ion positioned at about 495－504 nm wave-range. Our result coincides with all the published correct papers, whose cooperative up-conversion luminescence main peaks of the direct Yb^{3+}－Yb^{3+} clusters are all positioned at about 476－480 nm wave-range. All of these indicate that the large cooperative up-conversion blue luminescence of the direct Yb^{3+}－Yb^{3+} clusters discovered in this paper is stable. It further proves that the cooperative up-conversion green luminescence may result from the Yb^{3+}-Tb^{3+} cooperative effect. In particular, the original work of this paper improves considerably on the traditional concept by the experimental facts that the blue 479.1 nm cooperative up-conversion luminescence strength of Yb(5):FOV is 230 times greater than that of fluoride glass Yb(3):ZBLAN. This is a great development to meet the practical requirements for blue up-conversion luminescence strength. This result indicates that the large cooperative up-conversion blue luminescence could be achieved excellently by using a suitable material, such as oxyfluoride vitroceramic, which provides a better chance to form better Yb^{3+}－Yb^{3+} clusters and has less relaxation to keep the more efficient up-conversion luminescence. It is also found that impurities seriously reduce the cooperative up-conversion luminescence intensity due to the cross-relaxation from the Yb^{3+}－Yb^{3+} clusters, which means that the cooperative up-conversion blue luminescence could be further improved by pure Yb^{3+} ion-doped materials that have as few impurities as possible to reduce the cross-relaxation. The large cooperative up-conversion blue luminescence of Yb(5):FOV also comes from its higher concentration (5 mol%) of activator Yb^{3+} ion which acts well because the cooperative up-conversion blue luminescence intensity varies linearly against the square of the concentration of Yb^{3+} ions in the range of 0.5－5 mol%. In summary, the great improvement of our work on cooperative up-conversion blue luminescence results from the comprehensive enhancement of the factors of better-coupled chance of the Yb^{3+}－Yb^{3+} clusters, less cross-relaxation, better concentration contribution of Yb^{3+} activator, non-saturation, and better up-conversion luminescence efficiency.     

Up and down conversion fluorescence studies on combustion synthesized Yb/Yb: MO-Al2O3 (M=Ca, Sr and Ba) phosphors

The ytterbium ions doped MO-Al₂O₃ (M=Ca, Sr and Ba) phosphors have been synthesized through combustion technique and their up and down conversion fluorescence properties have been studied and compared. The samples were calcinated at different temperatures and their FTIR and XRD spectra have shown a close relationship. With 976 nm excitation all these phosphors show cooperative upconversion emission at 488 nm from the pairs of two Yb³⁺ ions along with an unexpected broad upconversion band in the blue green region and has been assigned to arise from the defect centers. Contrary to this upconversion emission, calcium aluminate phosphor exhibits bright and very broad down-conversion fluorescence (FWHM≈160 nm) upon UV (266 nm) excitation due to Yb²⁺ ions. The inter-conversion between the 3+ and 2+ valence states of Yb ion has been observed on calcinations of samples in open atmosphere and has been correlated to the emission properties. The Yb²⁺ ions containing calcium aluminate phosphor has been found suitable for producing broad band light in the visible region (white light). Lifetime of the emitting states of Yb³⁺ and Yb²⁺ ions have also been measured and discussed.     

Energy transfer and upconversion luminescence in Tm/Yb co-doped lanthanum-zinc-lead-tellurite glasses

A series of Tm³⁺/Yb³⁺ co-doped lanthanum-zinc-lead-tellurite (TPZL) glasses pumped by a 980 nm laser diode (LD) were demonstrated to obtain a high efficiency of infrared-to-visible upconversion. Effects of PbO content on the thermal stability, structure and upconversion properties of Tm³⁺/Yb³⁺ co-doped TPZL glasses had been investigated. The efficient visible upconversion fluorescences corresponding to the ¹G₄→³H₆, ¹G₄→³F₄ and ³H₄→³H₆ transitions of Tm³⁺ were observed under 980 nm excitation. The upconversion intensities of blue, red and near infrared emissions in Tm³⁺/Yb³⁺ co-doped TPZL glasses were obviously enhanced with increasing PbO content. The dependence of upconversion intensities on excitation power and the possible upconversion mechanisms had been evaluated by a proper rate equation model. Population density in different levels and coefficients of the energy transfer rate C_Di (i=2, 4, 6) between Tm³⁺ and Yb³⁺ were estimated by fitting the simulated curves to the measured ones. The obtained three energy transfer coefficients C_D2, C_D4, and C_D6 were determined to be 5.7×10⁻¹⁷, 1.3×10⁻¹⁶ and 8.6×10⁻¹⁷ cm³/s, respectively.     

Spectral performance and intensive green upconversion luminescence in Er/Yb-codoped NaY(WO4)2 crystal

Using Czochralski (CZ) pulling method, an Er³⁺/Yb³⁺-codoped NaY(WO₄)₂ crystal was prepared. Absorption spectra, emission spectra and excitation spectra of this crystal were measured at room temperature. Some optical parameters, such as intensity parameters, spontaneous emission probabilities and lifetimes, were calculated from absorption spectra with Judd-Ofelt (J-O) theory. Upconversion luminescence excited by a 970 nm diode laser was studied. In this crystal, green upconversion luminescence is particularly intensive. Energy transfer mechanisms that play an important role in upconversion processes were analyzed. Two cross-relaxation processes: ⁴G_11/2 + ⁴I_9/2 → ²H_11/2 (or ⁴S_3/2) + ²H_11/2 (or ⁴S_3/2), and ⁴G_11/2 + ⁴I_15/2 → ²H_11/2 (or ⁴S_3/2) + ²I_13/2, which contribute to the intensive green luminescence under 378 nm excitation, were put forward. Background energy transfer ⁴G_11/2(Er³⁺) + ²F_7/2(Yb³⁺) → ⁴F_9/2(Er³⁺) + ²F_5/2(Yb³⁺) was also demonstrated.     

Upconversion luminescence of Tm/Yb-codoped oxyhalide tellurite glasses

Thermal stability, Raman spectra and blue upconversion luminescence properties of Tm³⁺/Yb³⁺-codoped halide modified tellurite glasses have been studied. The results showed that the mixed halide modified tellurite glass (TFCB) has the best thermal stability, the lowest phonon energies and the strongest upconversion emissions. The effect of halide on upconversion intensity is observed and discussed and possible upconversion mechanisms are evaluated. The intense blue upconversion luminescence of Tm³⁺ in TFCB glass may be a potentially useful material for developing upconversion optical devices.     

Spectroscopic investigations of Nd-, Er-, Er/Yb-, and Tm-ions doped SiO2-Al2O3-CaF2-GdF3 glasses

This paper reports on the absorption, visible and near-infrared luminescence properties of Nd³⁺, Er³⁺, Er³⁺/2Yb³⁺, and Tm³⁺ doped oxyfluoride aluminosilicate glasses. From the measured absorption spectra, Judd-Ofelt (J-O) intensity parameters (Ω₂, Ω₄ and Ω₆) have been calculated for all the studied ions. Decay lifetime curves were measured for the visible emissions of Er³⁺ (558 nm, green), and Tm³⁺ (650 and 795 nm), respectively. The near infrared emission spectrum of Nd³⁺ doped glass has shown full width at half maximum (FWHM) around 45 nm (for the ⁴F_3/2→⁴I_9/2 transition), 45 nm (for the ⁴F_3/2→⁴I_11/2 transition), and 60 nm (for the ⁴F_3/2→⁴I_13/2 transition), respectively, with 800 nm laser diode (LD) excitation. For Er³⁺, and Er³⁺/2Yb³⁺ co-doped glasses, the characteristic near infrared emission bands were spectrally centered at 1532 and 1544 nm, respectively, with 980 nm laser diode excitation, exhibiting full width at half maximum around 50 and 90 nm for the erbium ⁴I_13/2→⁴I_15/2 transition. The measured maximum decay times of ⁴I_13/2→⁴I_15/2 transition (at wavelength 1532 and 1544 nm) are about 5.280 and 5.719 ms for 1Er³⁺ and 1Er³⁺/2Yb³⁺ (mol%) co-doped glasses, respectively. The maximum stimulated emission cross sections for ⁴I_13/2→⁴I_15/2 transition of Er³⁺ and Er³⁺/Yb³⁺ are 10.81×10⁻²¹ and 5.723×10^-21 cm². These glasses with better thermal stability, bright visible emissions and broad near-infrared emissions should have potential applications in broadly tunable laser sources, interesting optical luminescent materials and broadband optical amplification at low-loss telecommunication windows.     

A new Yb-doped oxyorthosilicate laser crystal: Yb:Gd2SiO5

A new Yb-doped oxyorthosilicate laser crystal, Yb:Gd₂SiO₅ (Yb:GSO), has been grown by the Czochralski (Cz) method. The crystal structure was determined by means of X-ray diffraction analysis. Room temperature absorption and fluorescence spectra of Yb³⁺ ions in GSO crystal were measured. Then, spectroscopic parameters of Yb:GSO were calculated and compared with those of another Yb-doped oxyorthosilicate crystal Yb:YSO. Results indicated that Yb:GSO crystal seemed to be a very promising laser gain media in generating ultra-pulses and tunable solid state laser applications. As expected, the output power of 2.72 W at 1089 nm was achieved in Yb:GSO crystal with absorbed power of only 4.22 W at 976 nm, corresponding to the slope efficiency of 71.2% through the preliminary laser experiment.     

Three-photon upconversion luminescence phenomenon for the green levels in Er/Yb codoped cubic nanocrystalline yttria

In this paper, we observed that in Er³⁺/Yb³⁺ codoped nanocrystals (NC), with the decreasing particle size and the increasing Yb³⁺ concentration, the upconversion luminescence (UCL) of the red emissions of gradually increased, while the green emissions of gradually diminished under 980 nm diode laser excitation. In NC with lower Yb³⁺ concentration, both the red and green emissions result from a two-photon excitation. In NC with higher Yb³⁺ concentration, the red emissions result from a two-photon excitation, while the green emissions dominantly result from a three-photon excitation. A model was provided for explaining the above UCL phenomena.     

Intense White Luminescence from Combustion Synthesized Ca<Subscript>12</Subscript>Al<Subscript>14</Subscript>O<Subscript>33</Subscript>: Yb<Superscript>3+</Superscript>/Yb<Superscript>2+</Superscript> Single Phase Phosphor

The Ca₁₂Al₁₄O₃₃: Yb³⁺/Yb²⁺ single phase nano-phosphor has been synthesized through combustion route and its luminescence and lifetime studies have been carried out up to 20 K using 976 and 266 nm excitations. The samples heated in open atmosphere have shown the presence of Yb in Yb³⁺ and Yb²⁺ states. The 976 nm excitation results a cooperative upconversion emission at 486 nm due to the Yb³⁺ state and a broad band in the blue region and has been assigned to arise from the defect centers. The 266 nm excitation on the other hand results a broad emission band even from as-synthesized phosphor without doping of Yb, the width of which increases in presence of Yb due to the emission from Yb²⁺ ions formed in heated samples. The white emission covers almost whole visible region with bandwidth 190 nm. The ions in Yb²⁺ state has been found to increase with the increase in heating temperature up to 1,273 K. A back conversion of Yb²⁺ to Yb³⁺ has been observed for higher temperatures. Effect of boric and phosphoric acids as flux on the emission properties of Yb³⁺ and Yb²⁺ states have been examined and discussed. Quantum yield of emission has also been determined for different samples.     

Synthesis process and the luminescence properties of rare earth doped NaLa(WO4)2 nanoparticles

Rare earth doped NaLa(WO₄)₂ nanoparticles have been prepared by a simply hydrothermal synthesis procedure. The X-ray diffraction (XRD) pattern shows that the Eu³⁺-doped NaLa(WO₄)₂ nanoparticles with an average size of 10-30 nm can be obtained via hydrothermal treatment for different time at 180 °C. The luminescence intensity of Eu³⁺-doped NaLa(WO₄)₂ nanoparticles depended on the size of the nanoparticles. The bright upconversion luminescence of the 2 mol% Er³⁺ and 20 mol% Yb³⁺ codoped NaLa(WO₄)₂ nanoparticles under 980 nm excitation could also be observed. The Yb³⁺-Er³⁺ codoped NaLa(WO₄)₂ nanoparticles prepared by the hydrothermal treatment at 180 °C and then heated at 600 °C shows a 20 times stronger upconversion luminescence than those prepared by hydrothermal treatment at 180 °C or by hydrothermal treatment at 180 °C and then heated at 400 °C.     

Effect of Yb3+ concentration on photoluminescence properties of cubic Gd2O3 phosphor

Yb³⁺ doped phosphor of Gd₂O₃ (Gd₂O₃:Yb³⁺) have been prepared by solid state reaction method. The structure and the particle size have been determined by X-ray powder diffraction measurements. The average particle size of the phosphor is in between 35 and 50 nm. The particle size and structure of the phosphor was further confirmed by TEM analysis. The visible and NIR luminescence spectra were recorded under the 980 nm laser excitation. The visible upconversion luminescence of Yb³⁺ ion was due to cooperative luminescence and the presence of rare earth impurity ions. The cooperative upconversion and NIR luminescence spectra as a function of Yb³⁺ ion concentration were measured and the emission intensity variation with Yb³⁺ ion concentration was discussed. Yb³⁺ energy migration quenched the cooperative luminescence of Gd₂O₃:Yb³⁺ phosphor with doping level over 5%, while the NIR emission luminescence continuously increases with increasing Yb³⁺ ion concentration.     

Energy transfer and infrared-to-visible upconversion luminescence of Er/Yb-codoped halide modified tellurite glasses

We report on the energy transfer and frequency upconversion spectroscopic properties of Er³⁺-doped and Er³⁺/Yb³⁺-codoped TeO₂-ZnO-Na₂O-PbCl₂ halide modified tellurite glasses upon excitation with 808 and 978 nm laser diode. Three intense emissions centered at around 529, 546 and 657 nm, alongwith a very weak blue emission at 410 nm have clearly been observed for the Er³⁺/Yb³⁺-codoped halide modified tellurite glasses upon excitation at 978 nm and the involved mechanisms are explained. The quadratic dependence of fluorescence on excitation laser power confirms the fact that the two-photon contribute to the infrared to green-red upconversion emissions. And the blue upconversion at 410 nm involved a sequential three-photon absorption process.     

Synergistic upconversion effect in NaYF4:Yb,Tm nanorods under dual excitation of 980 nm and 808 nm

NaYF₄:Yb³⁺,Tm³⁺ nanorods are prepared with hydrothermal method. The upconversion luminescent properties are investigated under dual excitation of 980 nm and 808 nm. The blue emission is observed at about 475 nm under dual excitation. The intensity is 2.6 times higher than the total intensity of the two corresponding single wavelength excitations, showing a synergistic upconversion effect occurring there. The dual wavelength excitation not only effectively decreases non-radiative relaxation pumped by 980 nm but also reduces the rate of the back energy transfer from Tm³⁺ to Yb³⁺ pumped by 808 nm. The result provides a possible new way to further improve the upconversion efficiency of rare earth doped phosphor.     

Upconversion dynamics in Er-doped YAG

Green, blue, violet and ultraviolet upconversion luminescence is reported at room temperature in a YAG: 10.5%Er³⁺ crystal pumped by one-colour (647 nm) and two-colour (647+618 nm) laser excitation. The upconversion mechanism was studied by means of time-resolved luminescence spectroscopy and the energy flow pathways are described. Based on the results it appears that energy transfer upconversion is the dominant contribution to the upconverted luminescence upon 647 nm excitation, and excited state absorption is the dominating mechanism upon 647+618 nm excitation.     

Upconversion luminescence and kinetics in Er:YAlO3 under 652.2 nm excitation

Ultraviolet and visible upconversion properties of Er³⁺ in YAlO₃ were investigated following 652.2 nm excitation of the multiples ⁴F_9/2. The luminescence and excitation spectra were recorded. Ultraviolet (326-342 and 354-359 nm), violet (405-420 nm), blue (436-442 nm) and green (525-575 nm) upconversion and infrared downconversion luminescence were simultaneously observed. The intense green luminescence corresponds to the emissions from the thermal coupled ⁴S_3/2 and ²H_11/2 bands and ²G_9/2 level. Energy transfer upconversion processes were proposed to explain the upconversion phenomena. The luminescence kinetics was discussed in detail by the analyses of fluorescence decay curves.     

Cooperative energy transfer and frequency upconversion in Yb3+-Tb 3+ and Nd 3+-Yb 3+-Tb 3+ codoped GdAl3(BO3)4 phosphors

Polycrystalline GdAl₃(BO₃)₄ phosphors codoped with Yb³⁺/Tb³⁺ and/or Nd³⁺/Yb³⁺/Tb³⁺ have been synthesized by combustion method. Upon excitation with a 980 nm laser diode, an intense green upconversion luminescence has been observed in GdAl₃(BO₃)₄:Yb,Tb phosphor. The quadratic dependence of the luminescence on the pump-laser power indicating a cooperative energy transfer process. Meanwhile, it is noticed that upon excitation with 808 nm laser diode, intense luminescence has clearly been detected in GdAl₃(BO₃)₄:Nd,Yb,Tb phosphor. The luminescence intensity exhibits also a quadratic dependence on incident pump-laser power. However, no green-emission has been observed in GdAl₃(BO₃)₄ phosphors codoped with Yb³⁺/Tb³⁺ or Nd³⁺/Tb³⁺ respectively upon excited at 808 nm laser diode. A proposed upconversion mechanism involving energy transfer from Nd³⁺ to Yb³⁺, and then a cooperative energy transfer process from two excited Yb³⁺ to Tb³⁺ has been presented.     

掺Er3+氟氧化物玻璃陶瓷的直接上转换敏化发光

研究了ErYb共掺的氟氧化物玻璃陶瓷的直接上转换敏化发光现象,发现其上转换机理主要是 Er³⁺与Yb³⁺离子间的能量传递上转换而不是Er³⁺离子 的步进多光子吸收.研究发现由于稀土离子优先富集到Pb_xCd_1-xF2微晶中,形成数个稀土离子组成的耦合团,使其存在强烈的团簇效应,一方面导 致了上转换荧光非常强,另一方面也导致了上转换荧光随抽运激光功率的对数变化F-P曲线 存在逐 关键词： 直接上转换敏化 氟氧化物玻璃陶瓷 上转换合作辐射荧光