Magnetic pair making and breaking effect of Ru in La0.7Sr0.3Mn0.9Ru0.1O3 and La0.5Sr0.5Co0.9Ru0.1O3

The substitutional effect of Ru on the magnetic and transport properties of double exchange ferromagnets, La_0.7Sr_0.3MnO₃ and La_0.5Sr_0.5CoO₃ has been investigated. It is found that substitution of 10% Ru at the Mn site of La_0.7Sr_0.3MnO₃ decreases the Curie temperature by 20 K than that of the parent compound. However, a large decrease in the Curie temperature, ΔT_c80 K and the system undergoes a transition from metallic state to insulating state is observed when 10% Ru is doped in La_0.5Sr_0.5CoO₃. The marginal effect of Ru in the Mn–O–Mn sublattice in comparison to the Co–O–Co sublattice could be due to the magnetic exchange interaction between Mn and Ru by virtue of the fact that Ru exhibits variable valence states, Ru⁺⁴/Ru⁺⁵. The e_g and t_2g parentage of Ru⁺⁵ is similar to Mn⁺⁴ and therefore, Ru⁺⁵ ion appears to participate in the double exchange mediated ferromagnetic (FM) interaction. On the other hand, Ruthenium (IV) ion disrupts an intermediate spin state of cobalt (Co⁺³: t_2g⁵e_g¹), forcing a double exchange FM state to anti-FM state.     

Structure, magnetic and transport properties of La1−xBixMnO3

We have investigated the structural, magnetic and transport properties of La_1−xBi_xMnO₃ samples. As the Bi content increases, a structural transition from rhombohedral to pseudocubic and a magnetic phase transition from ferromagnetic ordering to cluster glass are identified. Metal–insulator (MI) transitions and large magnetoresistance (MR) effects are observed at low Bi doping levels, while insulating behavior of resistivity is found in the whole measured temperature range at high-doping levels. Two distinct ferromagnetic insulating (FI) states are found at low temperatures in this system. One can be suppressed and the other can be enhanced by applying magnetic fields. Possible reasons for the observed structural, magnetic phase transitions and changes of resistivity behavior with Bi doping are discussed.     

High hydrostatic pressure effect on magnetic state of anion-deficient La0.70Sr0.30MnOx perovskite manganites

The magnetic state of La_0.70Sr_0.30MnO_x (x=2.85, 2.80) anion-deficient manganites is studied experimentally under hydrostatic pressure up to 5.2 GPa. These materials possessing the properties of a spin-glass state. The La_0.70Sr_0.30MnO_2.85 exhibits a coexistence of the rhombohedral (R3¯c) and tetragonal (I4/mcm) crystal structures and below T_f 50 K the spin-glass state is formed. The La_0.70Sr_0.30MnO_2.80 exhibits the tetragonal (I4/mcm) crystal structure. For this compound a phase-separated magnetic state below T_f is formed, involving coexistence of C-type antiferromagnetic (AFM) clusters within spin-glass matrix. In both compounds the crystal structure and magnetic states remain stable upon compression. Under the hydrostatic pressure up to 1 GPa, the La_0.70Sr_0.30MnO_2.85 is a spin glass with a smeared phase transition to the paramagnetic state. The freezing temperature T_f of the magnetic moments of the ferromagnetic clusters increases at a rate of 4.30 K/GPa and the magnetic ordering temperature T_MO increases at a rate of 12.90 K/GPa. The enhancement of the ferromagnetic properties of La_0.70Sr_0.30MnO_2.85 anion-deficient manganite under hydrostatic pressure is explained by the redistribution of oxygen vacancies and a decrease in the unit cell parameters.     

Fitting of transport measurements in polycrystalline La2/3Ca1/3MnO3

Using a previous qualitative explanation to describe the transport properties of polycrystalline La_2/3Ca_1/3MnO₃ thick films, we achieved a good fit of the temperature dependence of the resistance R(T). Depending on the sample, we have observed different metal–insulator (MI) transitions while the magnetic behavior is always similar. Small regions of depleted T_c adjacent to the grain boundary could have an important resistance contribution without affecting the magnetic properties in an appreciable manner. In this work, we achieve a quantitative explanation for the different transport behaviors that we have observed experimentally.     

The effects of Cu doping on the magnetoresistive behavior of perovskites La0.7Ca0.3MnO3

The electronic and magnetic properties of Cu-doped perovskite La_0.7Ca_0.3Mn_1−xCu_xO₃ obtained by doping Cu on its Mn sites have been studied. The perovskite structure was found to remain intact up to the highest doping level of x=0.20. At low Cu concentration (x=0.05) the temperature-dependence of resistivity of the material exhibited up to two peaks corresponding to the magnetic transitions from the PM to the FM phase, and from the FM to the AFM phase. In general, the doping level was found to suppress the ferromagnetic ordering of the material, increase its resistivity, and produce large values of magnetoresistance near the resistivity peak. These results were explained as due to the formation of the antiferromagnetic phase.     

Direct measurement of the magnetocaloric effect in La0.67Ca0.33MnO3

Polycrystalline perovskite La_0.67Ca_0.33MnO₃ was synthesized by a sol–gel method. Its adiabatic temperature change ΔT_ad induced by a magnetic field change was measured directly. At 268 K, near its Curie temperature T_C, ΔT_ad of La_0.67Ca_0.33MnO₃ induced by a magnetic field change of 2.02 T reaches 2.4 K. The latent heat Q and magnetic entropy change −ΔS_M induced by a magnetic field change were calculated from the temperature dependence of ΔT_ad and zero-field heat capacity C_p. The maximum values of Q and −ΔS_M in La_0.67Ca_0.33MnO₃ induced by a magnetic field change of 2.02 T are 1.85 J g⁻¹ and 6.9 J kg⁻¹ K⁻¹, respectively. The former is larger than the phase transition latent heat of heating or cooling, which is about 1.70 J g⁻¹.     

Temperature dependence of ESR anisotropy in La7/8Sr1/8MnO3

We report X-ray diffraction, DC-susceptibility, electron spin resonance (ESR), and dilatometry measurements carried out on an La_7/8Sr_1/8MnO₃ single crystal. Thermal expansion was measured along different crystallographic axes using a three-terminal dilatometer. The sharp anomalies observed in the temperature dependence of Δl/l allowed us to locate the Jahn–Teller transition at T_JT=285(1) K. ESR experiments were carried out in the paramagnetic regime from 220 to 570 K, at 9.4 GHz. We measured the ESR line width ΔH_pp(T) with the magnetic field parallel to the crystallographic directions [1 0 0] and [0 0 1], referred to the orthorhombic (Pbnm) axes. We correlate the temperature dependence of ΔH_pp with the structural changes of the lattice.     

Double peak behavior of resistivity curves in Cd doped LaMnO3 perovskite systems

The effect of Cd doping on transport, magnetotransport, and magnetic properties has been investigated in the perovskite La_1−xCd_xMnO₃ (0x0.5) systems. The ρ(T) curves exhibit a sharp metal insulator transition (T_p1), which is close to paramagnetic to ferromagnetic transition (T_c) obtained from M−T curves for all samples. In addition, ρ(T) curves for Cd doped samples exhibit another broad transition (T_P2) below T_p1. This transition becomes more prominent and the transition temperature (T_p2) shifts to lower temperature with increasing Cd content. Such double peak behavior in the ρ(T) curve is attributed to the phase separation between the ferromagnetic metallic phases and the ferromagnetic insulating phases induced by the electronic inhomogeneity in the samples.     

Magnetic properties of Mn-substituted GdCoxMn1−xO3 and LaCoxMn1−xO3

Partial substitution of manganese by cobalt in rare-earth perovskites REMnO₃ leads to unusual magnetic phenomena because of the simultaneous presence of Mn³⁺, Mn⁴⁺, Co²⁺ and Co³⁺ species. The magnetic nature of the RE cation plays a fundamental role in the magnetic properties. We present herein two specific families: for RE=La the magnetic behavior of the |Co+Mn| network is observed, while for Gd its strong magnetic moment interacts with the transition metals, leading to a spin reversal state. Magnetic interactions are maximized at x=0.50, as if two regimes exist: for x<0.5 Co substitutes Mn in the REMnO₃ manganite, and for x>0.5 Mn substitutes Co in the RECoO₃ cobaltite.     

Crystal structure, superconductivity and magnetic properties of the superconducting ferromagnets Gd1.4−xDyxCe0.6Sr2RuCu2O10 (x=0–0.6)

The structural, electrical and magnetic properties of the superconducting ferromagnets, Gd_1.4−xDy_xCe_0.6Sr₂RuCu₂O₁₀ (x=0–0.6) are systematically investigated as a function of Dy doping and temperature. These compounds are characterized by high temperature superconductivity (T_c ranging from 20 to 40 K depending upon the Dy content) co-existing with weak ferromagnetism with two magnetic transitions (T_M2 ranging from 95 to 106 K and T_M1 around 120 K). Doping with Dy gives no significant structural changes except for a minor change in the c/a ratio. However the superconducting transition temperature is significantly suppressed and magnetic ordering temperature enhanced on Dy doping. These effects are described and discussed.     

钙钛矿型锰氧化物(La$lt;sub$gt;0.8$lt;/sub$gt;Eu$lt;sub$gt;0.2$lt;/sub$gt;)$lt;sub$gt;4/3$lt;/sub$gt;Sr$lt;sub$gt;5/3$lt;/sub$gt;Mn$lt;sub$gt;2$lt;/sub$gt;O$lt;sub$gt;7$lt;/sub$gt;的磁性和电性研究

采用传统固相反应法制备钙钛矿型锰氧化物 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇多晶样品, X-射线衍射分析表明, 样品(La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇结构呈现良好的单相. 通过磁化强度随温度的变化曲线(M-T)、不同温度下磁化强度随磁场的变化曲线(M-H)和电子自旋共振谱发现: 在300 K以下, 随着温度的降低, 样品先后经历了二维短程铁磁有序转变 (T_C^2D ≈ 282 K)、三维长程铁磁有序转变(T_C^3D ≈ 259 K)、奈尔转变(T_N ≈ 208K)和电荷有序转变(T_CO ≈ 35 K); 样品 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇在T_N以下, 主要处于反铁磁态; 在T_C^3D达到370 K时, 样品处于铁磁-顺磁共存态, 在370 K以上时样品进入顺磁态. 此外, 分析电阻率随温度的变化曲线(ρ-T)得到: 样品在金属-绝缘转变温度(T_P ≈ 80 K)附近出现最大磁电阻值, 其位置远离T_C^3D, 表现出非本征磁电阻现象, 其磁电阻值约为61%. 在T_CO以下, 电阻率出现明显增长, 这是由于温度下降使原本在高温部分巡游的e_g电子开始自发局域化增强所致. 通过对 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇的ρ-T 曲线拟合, 发现样品在高温部分的导电方式基本遵循小极化子的导电方式. 关键词： 磁性 电性 金属-绝缘转变温度 电子自旋共振     

Strain effects in epitaxially grown La0.7Sr0.3MnO3 thin films

We report here on an X-ray absorption study of La_0.7Sr_0.3MnO₃ films epitaxially grown on SrTiO₃ substrate. The local organization around Mn in oriented films with 600 Å in thickness was investigated by polarized Extended X-ray Absorption Fine Structure. The angle between electric field vector and film surface was set equal to 5° and 70° to investigate almost independently the contribution of the manganese neighbors situated in and out of the film plane. The first neighboring shell oxygen is found to be the same in both geometries, but small changes in the next neighboring contribution are observed. These changes are associated with variation in the Mn–Mn bond length. A small in-plane elongation (3%) is observed in the constrained films with respect to the unconstrained case.     

Tuning the multiferroic properties of Pb(Fe1/2Nb1/2)O3 by cationic substitution

A series of substituted lead iron niobate compounds with the general formula Pb²⁺_(1−x)A^Z_x(Fe_{{(1−(2−Z)x)/2}}Nb_{{(1+(2−Z)x)/2}})O₃ (0<x<0.6 and A=La³⁺, K⁺ or Sr²⁺) were prepared by a modified solid-state synthesis. The relative concentrations of Fe³⁺ and Nb⁵⁺ were adjusted to compensate the charge imbalance due to the aliovalent substitution. The dielectric constant and magnetic susceptibilities were studied as a function of temperature. The temperature of the dielectric maximum, T_M, of the substituted compounds decreased linearly with increasing concentration of the substituent ions. The magnetic measurements showed an antiferromagnetic transition at temperatures T_N1 due to the superexchange interactions mediated by Fe–O–Fe and an additional antiferromagnetic-type transition at T_N2. T_N1 linearly increased with the increasing concentration of Fe³⁺ ion at the B-site of ABO₃-type substituted compounds. T_M is shown to be directly dependent on the concentration of the ferroactive Nb⁵⁺ ions at the B-site and Pb²⁺ ions at the A-site.     

Effects of crystallographic ordering on the magnetic behaviour of (AgIn)1-zMn2zTe2 and (CuIn)1-zMn2zTe2 alloys

Measurements of magnetic susceptibility in the temperature range 4.2–300 K were made on polycrystalline samples of the (AgIn)_{1 - z}Mn_2zTe₂ and (CuIn)_{1 - z}Mn_2zTe₂ alloys, and the data used to give values of spin-glass transition te mperature T_g and Curie-Weiss paramagnetic temperature θ. For any sample for which the X-ray powder photograph indicated an apparently single phase condition, either zinc-blende or chalcopyrite, the susceptibility data could show up to three separate T_g values. These different magnetic conditions are attributed to crystallographic ordering of the Mn ions on the chalcopyrite and zinc-blende lattices, the three observed T_g values corresponding to disordered zinc-blende, ordered zinc-blende and ordered chalcopyrite. The value of θ obtained from the 1/χ vs. T plot is shown to be a weighted mean of the separate values of θ for the phases present. The relative sizes of the T_g peaks and the values of θ for any given sample gives an indication of the amount of each phase present. These amounts were varied by using different methods of heat treatment and it was shown that the magnetic behaviour was consistent with the T(z) phase diagram for the two alloy systems.     

Disruption of antiferromagnetic order in Zn-doped La2CuO4

The magnetic phase diagram of La₂(Cu_1−xZn_x)O₄ has been determined from zero-field muon-spin-rotation (ZF-μSR) data taken at LAMPF for 0 ≤ x ≤ 0.10. Antiferromagnetic onset temperatures follow T_N(x) from susceptibility measurements on the same samples. However, the order becomes long range, as evidenced by a well-defined internal magnetic field, only at temperatures well below T_N. Extrapolation of our results yields T_N → 0 K at x = 0.11 for a single (Cu_1−xZn_x)O₂ plane, and comparison with YBa₂(Cu_1−xZn_x)₃O₆ implies identical disruption of magnetism by Zn doping in the single- and double-plane systems.     

钙钛矿锰氧化物(La1-xGdx)4/3Sr5/3Mn2O7 (x=0, 0.025) 磁性和输运性质研究

采用传统的高温固相烧结法制备了双层钙钛矿锰氧化物(La_1-xGd_x)_4/3Sr_5/3Mn₂ O₇ (x=0, 0.025)多晶样品. 通过X射线衍射仪研究发现样品为Sr₃Ti₂O₇型四方结构, 空间群为I4/mmm; 磁性测量表明, Gd³⁺掺杂后的样品(La_0.975Gd_0.025)_4/3Sr_5/3Mn₂O₇的三维磁有序转变温度(T_C1^3D)、磁化强度(M)均降低, 这是由于Gd³⁺的掺杂引起晶格的畸变, 从而使得晶格常数发生改变, 减弱了铁磁耦合而导致的; 通过电子自旋共振谱测量发现, 在T_C^3D<T<300 K温度范围内, 两样品在顺磁的基体上均有短程的铁磁团簇存在, 出现了相分离现象. 电性测量表明: 两样品分别在T_C1^3D (La_4/3Sr_5/3Mn₂O₇ 样品的三维磁有序转变温度, T_C0^3D)<T<300 K温度范围内均以三维变程跳跃的方式导电, 分析得出Gd³⁺的掺杂使得载流子局域长度的减小. 这表明载流子需要吸收更多的能量才能克服晶格的束缚进行跳跃, 因此(La_0.975Gd_0.025)_4/3Sr_5/3Mn₂ O₇ 样品的电阻较高.     

Magnetic order in M2Mo3O8 single crystals (M = Mn, Fe, Co, Ni)

Magnetic measurements on hexagonal single crystals of M₂Mo₃O₈ (M = Mn, Fe, Co and Ni) are reported. The Mn compound orders ferrimagnetically at T_c = 41.5 K; the Fe and Co compounds antiferrimagnetically at T_N = 59.5 K and 40.8 K, respectively. No magnetic ordering was found in the Ni compound down to 2 K. All the compounds showed strong magnetic anisotropy when ordered, the results indicating that the magnetic spins' preferred orientation is along the hexagonal axis. Mn₂Mo₃O₈ shows a temperature dependence of the spontaneous magnetization in the ferrimagnetic regime which is rarely observed: as T → 0, M_s → 0.     

A new interpretation of the CO state in half-doped manganites: new results from neutron diffraction and synchrotron radiation experiments

In the R_1−xD_xMnO₃ (x0.5) manganites, the structural phase transition at T_CO is commonly interpreted as a concomitant charge and orbital ordering (CO/OO) process driven by a co-operative Jahn–Teller effect and Coulomb repulsion forces. The low-temperature phase is supposed to contain well-separated and ordered Mn³⁺ and Mn⁴⁺ ionic species in an NaCl-like pattern. Structure refinement, from a neutron diffraction experiment below T_CO on a Pr_0.6Ca_0.4MnO₃ single crystal, gives us a model for the displacement of atoms with respect to the high-temperature phase that invalidates the standard model based in the CO/OO picture. Our result is a non-centrosymmetric crystal structure with two non-equivalent MnO₆ octahedra, both being slightly elongated but displaying very similar average Mn–O distances (1.96 and 1.95 Å, respectively) and having off-centered Mn atoms. We argue that this is a proof of the absence of charge ordering in half-doped manganites in the sense of formation of separated Mn³⁺ and Mn⁴⁺ ionic species. A new qualitative interpretation of the CE-type spin ordering (SO) is proposed. The so-called CO transition is, in fact, a structural transition induced by the change in the mean free path of electrons that continue to be thermally activated below T_CO by forming ferromagnetic Mn–Mn pairs stabilized by a local double-exchange process. The CE SO pattern results from the ordering of these pairs formed at T_CO. High-resolution synchrotron powder diffraction shows a complex anisotropic/asymmetric strains appearing at the transition that can be phenomenologically fitted by additional phases. Complementary electron diffraction and microscopy have shown no trace of macroscopic phase separation.     

Structural study and magnetoresistance effect of epitaxial La0.67Sr0.33MnO3–δ and Pr0.7Ca0.3MnO3−δ multilayer films

La_0.67Sr_0.33MnO_3−δ (LSMO) and Pr_0.7Ca_0.3MnO_3−δ (PCMO) multilayer epitaxial films, which were fabricated with different LSMO and PCMO layer thickness on LaAlO₃ single crystal substrates of (0 0 1) orientation by a direct current magnetron sputtering technique, were studied further, after the structure, magnetoresistance effect and magnetic properties of LSMO/PCMO/LSMO (LPL) trilayer epitaxial films were systemically studied. The superlattice structures of multilayer films were observed according to the diffraction peaks of X-ray diffraction patterns at small angles. The metal–insulator transition temperature (T_P) and peak resistivity (ρ_max) obviously changed when we altered the thickness of PCMO middle layer and the intra-field related with the thickness of those layers and their interaction. Considering the effect of the distribution of electrical field and current, and the interaction among the layers of LSMO and PCMO, an effective fact n* was introduced to replace n (the number of layer). All the calculated values of ρ (the resistivity of multilayer films) accorded with the experimental values.     

The order of magnetic phase transition in La(Fe1−xCox)11.4Si1.6 compounds

Magnetic transitions in La(Fe_1−xCo_x)_11.4Si_1.6 compounds with x=0–0.08, have been studied by DC magnetic measurements and Mössbauer spectroscopy. The temperature dependence of the Landau coefficients has been derived by fitting the magnetization, M(μ₀H), using the Landau expansion of the magnetic free energy. For x0.02 there is a strongly first-order magnetic phase transition between ferromagnetic and paramagnetic (F–P) states in zero external field and a metamagnetic transition from paramagnetic to ferromagnetic (P–F) above T_c. Increasing the cobalt content drives the F–P transition towards second order and eliminates the metamagnetic transition.