Dual behaviors of magnetic CoxFe1−x (0≤x≤1) nanowires embedded in nanoporous with different diameters

Co_xFe_1−x nanowire arrays with various diameters and different composition were fabricated by ac electrodeposition using porous alumina template. Coercivity along the easy axis reaches to a maximum at 2330 Oe, for Co_xFe_1−x nanowires containing about 40 at% Co. The crystalline structure of the nanowires was concentration-independent and shows a bcc structure. The critical diameter for transition from coherent rotation to curling mode is 35 nm for CoFe containing less than 40 at% Co while it is 30 nm for those with more than 40 at% Co. Optimizing the magnetic properties of CoFe with different Co content was seen to be dependent on the diameter of nanowires. For 25 nm diameter, the optimum was shown below 50 at% Co while it was seen above 50 at% for nanowires with 50 nm diameter. The angular dependence of the coercivity with nanowires diameter were also studied.     

Fabrication and characterization of electrodeposited Co1−xCrx nanowires

Co_1−xCr_x   alloy nanowires with 0.01<x<0.93$0.01<x<0.93$ were fabricated by electrodeposition in a porous alumina membrane from an electrolyte containing Co and Cr ions. The composition, structure and magnetic properties of the nanowires have been characterized. Cobalt-rich nanowires were electrodeposited at a potential of −1.0 V relative to Ag/AgCl and chromium-rich nanowires were deposited beyond −3.5 V. The optimized processing conditions include hydrogen annealing to give hysteresis loops for the Co₈₀Cr₂₀ nanowires with coercivity of up to 200 mT and squareness of up to 0.95. Magnetization of the Co₈₀Cr₂₀ nanowire is 77 A m² kg⁻¹ and the energy product of the arrays is 35 kJ m⁻³.     

Electrical conduction and magnetoelectric effect of (x) BaTiO3 + (1−x) Ni0.92Co0.03Cu0.05Fe2O4 composites in ferroelectric rich region

Particulate composites with composition (x)BaTiO₃+(1−x)Ni_0.92Co_0.03Cu_0.05Fe₂O₄ in which x varies as 1, 0.85, 0.70, 0.55 and 0 (in mol%) were prepared by the conventional double sintering ceramic technique. The presence of two phases viz. ferromagnetic (Ni_0.92Co_0.03Cu_0.05Fe₂O₄) and ferroelectric (BaTiO₃) was confirmed by X-ray diffraction analysis. The dc resistivity and thermo-emf measurements were carried out with variation of temperature. The ac conductivity (σ_ac) measurements investigated in the frequency range 100 Hz to 1 MHz conclude that the conduction in these composites is due to small polarons. The variation of dielectric constant and loss tangent with frequency (20 Hz to 1 MHz) was studied. The static magnetoelectric conversion factor, i.e. dc (dE/dH)_H was measured as a function of intensity of applied magnetic field. The changes were observed in electrical properties as well as in magnetoelectric voltage coefficient as the molar ratio of the constituent phases was varied. A maximum value of magnetoelectric conversion factor of 536.06 μV/cm Oe was observed for the composite with 70% BaTiO₃+30% Ni_0.92Co_0.03Cu_0.05Fe₂O₄ at a dc magnetic field of 2.3 K Oe. The maximum magnetoelectric conversion output has been explained in terms of ferrite-ferroelectric content, applied static magnetic field and resistivity.     

Effects of annealing temperature on structure and magnetic properties of amorphous Fe61Co27P12 nanowire arrays

Arrays of Fe₆₁Co₂₇P₁₂ nanowire with an aspect ratio about 70 were prepared in anodic aluminum oxide templates by electrodeposition. The influences of annealing temperature on structure and magnetic properties of Fe₆₁Co₂₇P₁₂ nanowires were studied. When the specimens were annealed below 400 °C, there are no obvious changes in structure except relaxation. With the annealing temperature increasing from 400 to 600 °C, the Fe-Co phase is detected by X-ray diffraction and Mössbauer spectra. The crystalline fraction and hyperfine field can be derived from Mössbauer spectra. The room temperature magnetic hysteresis loops show that the coercivity and squareness of the nanowire arrays in parallel to the wire axis increase with the increasing of annealing temperature, which mainly attributes to the strengthening of anisotropy.     

Magnetic domain structure in Fe78.8−xCoxCu0.6Nb2.6Si9B9 nanocrystalline alloys studied by Lorentz microscopy

The magnetic domain structures of Fe_78.8−xCo_xCu_0.6Nb_2.6Si₉B₉ (x=0, 20, 40, 60) alloys are investigated by Lorentz microscopy coupled with the focused ion beam method. The specimen prepared using the FIB method is found to have a considerably more uniform thickness compared to that prepared using the ion-milling method. In Fe_38.8Co₄₀Cu_0.6Nb_2.6Si₉B₉ and Fe_18.8Co₆₀Cu_0.6Nb_2.6Si₉B₉ alloys, 180° domain walls extending in the direction of the induced magnetic anisotropy are observed. Analysis with Lorentz microscopy reveals that the width of the magnetic domains decreases with an increase in the cobalt content or the induced magnetic anisotropy K_u, that is, the domain width d is proportional to the induced magnetic anisotropy (K_u)^−1/4. On the other hand, in the in situ Lorentz microscopy observation as a function of temperature, magnetic ripple structures are found to appear in a localized area due to the fluctuation of magnetization vectors from 423 K. It is observed that the induced magnetic anisotropy caused by the applied magnetic field at 803 K is not suppressed by the magnetic ripple structures observed at 423–443 K.     

Magnetoelectric characterization of xNi0.75Co0.25Fe2O4-(1−x)BiFeO3 nanocomposites

Magnetoelectric (ME) nanocomposites containing Ni_0.75Co_0.25Fe₂O₄-BiFeO₃ phases were prepared by citrate sol-gel process. X-ray diffraction (XRD) analysis showed phase formation of xNi_0.75Co_0.25Fe₂O₄-(1−x)BiFeO₃ (x=0.1, 0.2, 0.3 and 0.4) composites on heating at 700 °C. Transmission electron microscopy revealed the formation of powders of nano order size and the crystal size was found to vary from 30 to 85 nm. Dispersion in dielectric constant (ε) and dielectric loss (tan δ) in the low-frequency range have been observed. It is seen that nanocomposites exhibit strong magnetic properties and a large ME effect. On increasing Ni_0.75Co_0.25Fe₂O₄ contents in the nanocomposites, the saturation magnetization (M_S) and coercivity (H_C) increased after annealing at 700 °C. The large ME output in the nanocomposites exhibits strong dependence on magnetic bias and magnetic field frequency. The large value of ME output can be attributed to small grain size of ferrite phase of nanocomposite being prepared by citrate precursor process.     

The size and space arrangement roles on coercivity of electrodeposited Co1−xCux nanowires

Magnetization curves with various magnetic field orientations and nanowire diameters were measured at room temperature. The measured coercivity as a function of angle (θ) between the field and wire axis reveals that the coercivity decreases with increasing value of θ for various nanowires. Theoretically, based on Monte Carlo simulation we investigated the magnetization reversal modes of the Co_1−xCu_x nanowires and obtained also the θ dependence of the coercivity. Comparing the simulated with the experimental results, we find that the magnetocrystalline anisotropy plays an important role on the magnetic properties of Co_1−xCu_x nanowires, and the magnetization reversal process in the Co_1−xCu_x nanowires could not be understood by the classical uniform rotation mode in the chain-of-sphere model.     

Structural,microstructural and magnetic properties of nanocomposite isotropic Sm(CobalFe0.1MyZr0.04B0.04)7.5 ribbons with M=Ni,Cu and y=0.09 and 0.12

In boron-substituted melt-spun Sm(Co,Fe,Cu,Zr)_7.5-type alloys a nanocomposite microstructure and high coercivities in both as-spun and short-time annealed ribbons can be obtained. In the present study three different compositions, namely Sm(Co_0.73Fe_0.1Cu_0.09Zr_0.04B_0.04)_7.5, Sm(Co_0.70Fe_0.1Cu_0.12Zr_0.04B_0.04)_7.5 and Sm(Co_0.70Fe_0.1Ni_0.12Zr_0.04B_0.04)_7.5 have been examined in order to investigate the influence of composition on the magnetic properties and the microstructure. Melt-spun ribbons have been obtained and annealing has been followed under argon atmosphere for 30–75 min at 600–870 °C. For the as-spun ribbons the TbCu₇-type of structure and fcc-Co as a secondary phase have been identified in the X-ray diffraction patterns. For the annealed ribbons above 700 °C the 1:7 phase transforms into 2:17 and 1:5 phases. The TEM studies have shown a homogeneous nanocrystalline microstructure with average grain size of 30–80 nm. Coercivity values of 15–27 kOe have been obtained from hysteresis loops traced in non-saturating fields. The coercivity decreases with temperature, but it is sufficiently large to maintain values higher than 5 kOe at 380 °C.     

Fabrication and magnetic properties of Fe3O4 nanowire arrays in different diameters

Fe₃O₄ nanowire arrays with different diameters of D=50, 100, 150 and 200 nm were prepared in anodic aluminum oxide (AAO) templates by an electrodeposition method followed by heat-treating processes. A vibrating sample magnetometer (VSM) and a Quantum Design SQUID MPMS magnetometer were used to investigate the magnetic properties. At room temperature the nanowire arrays change from superparamagnetism to ferromagnetism as the diameter increases from 50 to 200 nm. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurements show that the blocking temperature T_B increases with the diameter of nanowire. The ZFC curves of D=50 nm nanowire arrays under different applied fields (H) were measured and a power relationship between T_B and H were found. The temperature dependence of coercivity below T_B was also investigated. Mössbauer spectra and micromagnetic simulation were used to study the micro-magnetic structure of nanowire arrays and the static distribution of magnetic moments of D=200 nm nanowire arrays was investigated. The unique magnetic behaviors were interpreted by the competition of the demagnetization energy of quasi-one-dimensional nanostructures and the magnetocrystalline anisotropy energy of particles in nanowires.     

The synthesis and the magnetic properties of Gd-doped FexCo1−x/CoyFe3−yO4 micro-octahedrons composites

Gd³⁺-substituted micro-octahedron composites (Fe_xCo_1−x/Co_yGd_zFe_3−y−zO₄) in which the Fe-Co alloy has either a bcc or fcc structure and the oxide is a spinel phase were fabricated by the hydrothermal method. The X-ray diffraction (XRD) patterns indicate that the as-synthesized Gd³⁺-substituted micro-octahedron composites are well crystallized. Scanning electron microscopy (SEM) images show that the final product consists of larger numbers of micro-octahedrons with the size ranging from 1.3 to 5 μm, and the size of products are increased with increasing the concentration of KOH. The effect of the Co²⁺/Fe²⁺ ratio (0?Co²⁺/Fe²⁺?1) and substitution Fe³⁺ ions by Gd³⁺ ions on structure, magnetic properties of the micro-octahedrons composites were investigated, and a possible growth mechanism is suggested to explain the formation of micro-octahedrons composites. The magnetic properties of the structure show the maximal saturation magnetization (107 emu/g) and the maximal coercivity (1192 Oe) detected by a vibrating sample magnetometer.     

Fabrication and magnetic properties of CoxPd1−x composite nanowire

A series of Co_xPd_1−x   (x=0.37–0.85$x=0.37–0.85$) nanowire arrays have been successfully deposited in a single Co²⁺/ Pd²⁺=20:1 solution by applying the various depositing potentials. We found that the nanowires are the composites of CoPd alloy with some Co and Pd clusters, but the overall structure of the composite wires followed the binary phase relation of Pd–Co. The existence of Pd content makes the nanowires structured in FCC phase, except for Co_0.85Pd_0.15 sample in which some HCP Co phase coexists with the dominating FCC phase. Between Co-rich and Pd-rich nanowires, we found that the optimized composition for Co_xPd_1−x nanowire is around Co_0.73Pd_0.27 in which the coercivity (H_c) and squareness (M_r/M_s) have their maximum values consistently.     

Structure,magnetic properties and magnetostriction of laves compounds Nd1−xPrx(Fe0.35Co0.55B0.1)2

The C15 Laves phases with composition Nd_1−xPr_x(Fe_0.35Co_0.55B_0.1)₂ (0?x?1) have been synthesized by arc melting and subsequent annealing. The Curie temperature T_c and the saturation magnetizations M_s at 5 and 295 K decrease with increasing Pr content. The linear anisotropic magnetostriction λ_a=λ_∥−λ_⊥ at room temperature for Nd_1−xPr_x(Fe_0.35Co_0.55B_0.1)₂ alloys with 0?x?0.4 initially reaches a negative minimum, then increases and changes its sign with increasing magnetic field H, and the λ_a for the alloys with x?0.6 is positive and increases as magnetic field H increases.     

Effect of quenching wheel speed on the structure, magnetic properties and magnetoimpedance effect in Co64Fe4Ni2B19−xSi8Cr3Alx (x=0, 1 and 2) melt-spun ribbons

Melt-spun ribbons of Co₆₄Fe₄Ni₂B_19−xSi₈Cr₃Al_x (x=0, 1 and 2) alloy at wheel speed of 25 m/s and Co₆₄Fe₄Ni₂B_19−xSi₈Cr₃Al₁ alloy at different wheel speeds (25, 30, 35 and 40 m/s) have been prepared and investigated for structural and magnetic properties and magnetoimpedance effect. Based on the results obtained, it was shown that replacement of B by Al can improve the magnetoimpedance ratio (MIR) and the highest value of MIR (191%) was observed for the sample with X_Al=1 at wheel speed of 25 m/s. Further, it was seen that the higher quenching wheel speed gives rise to a higher coercivity and lower magnetic permeability/MIR value.     

High Bs nanocrystalline Fe84−x−yCuxNbySi4B12 alloys (x=0.0-1.4, y=0.0-2.5)

In this study, Cu and Nb content dependences of magnetic properties for annealed Fe_84−x−yCu_xNb_ySi₄B₁₂ alloy ribbons fabricated by melt spinning were investigated. In Fe_83−xCu_xNb₁Si₄B₁₂ alloy systems, the coercivity H_c markedly decreases with increasing x and exhibits a minimum at around x=1.0-1.2, while the saturation magnetic flux density B_s shows a slight variation. In Fe_83−yCu₁Nb_ySi₄B₁₂ alloy systems, H_c markedly decreases at around y=0.5, while B_s shows a monotonic decrease. Fe₈₂Cu₁Nb₁Si₄B₁₂ nanocrystalline alloy ribbons exhibit a high B_s of 1.78 T and a low H_c of 3.2 A/m. The core losses of the present alloys at 1.0 T at 400 Hz, P_10/400, and at 1.0 T at 1 kHz, P_10/1k, are 1.3 and 4.4 W/kg, respectively.     

Magnetic properties of the Ce2Fe17−xMnx helical magnets up to high magnetic fields

Magnetic properties of the Ce₂Fe_17−xMn_x, x=0–2, alloys in magnetic fields up to 40 T are reported. The compounds with x=0.5–1 are helical antiferromagnets and those with 1<x?2 are helical ferromagnets or helical antiferromagnets at low and high T, respectively. Mn ions in the system carry average magnetic moment of 3.0±0.2 μ_B that couple antiparallelly to the Fe moments. Easy-plane magnetic anisotropy in the Ce₂Fe_17−xMn_x compounds weakens upon substitution of Mn for Fe. The absolute value of the first anisotropy constant in the Ce₂Fe_17−xMn_x helical ferromagnets decreases slower with increasing temperature than that calculated from the third power of the spontaneous magnetization. Noticeable magnetic hysteresis in the Ce₂Fe_17−xMn_x, x=0.5–2, helical magnets over the whole range of magnetic fields reflects mainly irreversible deformation of the helical magnetic structure during the magnetization of the compounds. A contribution from short-range order (SRO) magnetic clusters to the magnetic hysteresis of the helical magnets has been also estimated.     

Synthesis and investigation of magnetic properties of substituted ferrite nanoparticles of spinel system Mn1−xZnx[Fe2−yLy]O4

Superparamagnetic nanoparticles of the spinel ferrite four-element system Mn_1−xZn_x[Fe_2−yL_y]O₄ (where L:Gd³⁺, La³⁺, Ce³⁺, Eu³⁺, Dy³⁺, Er³⁺,Yb³⁺) were synthesized by the co-precipitation method. The magnetic moments of the 10 nm diameter nanoparticles were comparable to the ones of Fe₃O₄ nanoparticles. A comparatively low T_C (∼52–72 °C) was observed for some of the compositions. The heating mechanism of the superparamagnetic particles in the AC magnetic field at radiofrequency range is discussed and especially the absence of the hysteresis loop in the M–H curve at room temperature. One possible explanation—spontaneous particle agglomeration—was experimentally verified.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

Synthesis and characterization of Ni1−xCoxFe2O4 nanoparticles

Ni_1−xCo_xFe₂O₄ (x=0.6, 0.8 and 0.9) nanoparticles have been synthesized with various crystallite sizes depending on the thermal treatments and composition (cobalt content) using the sol-gel combustion method. The size of nanoparticles has been controlled by thermal treatment. On the other hand, the magnetic property of the ferrite has been controlled by changing the heat treatment. Morphology and particle sizes of Ni_1−xCo_xFe₂O₄ have been studied using atomic force microscopy (AFM) and transmission electron microscopy (TEM). The presence of functional group has been identified by Fourier Transform Infrared (FTIR) spectra. From TGA-DTA studies, the weight gains of Ni_1−xCo_xFe₂O₄ nanoparticles have been observed and it might be due to capping organic molecules with oxygen at temperatures above 200 °C. Magnetic properties of Ni_1−xCo_xFe₂O₄ particles have been analysed using VSM and it is found that saturation magnetization (M_s) has increased with particle size and has coercivity (H_c) increased initially and then decreased. The M_s and H_c values decreased with the increase of content of cobalt in Ni_1−xCo_xFe₂O₄.     

Magnetic properties of the novel nanocomposite (Zn0.15Ni0.85Fe2O4)0.15/(SiO2)0.85 at room temperature

The value of the effective magnetic anisotropy constant of the ferrimagnetic nanoparticles Zn_0.15Ni_0.85Fe₂O₄ embedded in a SiO₂ silica matrix, determined through ferromagnetic resonance (FMR), is much higher than the magnetocrystalline anisotropy constant. The higher value of the anisotropy constant is due to the existence of surface anisotropy. However, even if the magnetic anisotropy is high, the ferrimagnetic nanoparticles with a 15% concentration, which are isolated in a SiO₂ matrix, display a superparamagnetic (SPM) behavior at room temperature and at a frequency of the magnetization field equal to 50 Hz. The FMR spectrum of the novel nanocomposite (Zn_0.15Ni_0.85Fe₂O₄)_0.15/(SiO₂)_0.85, recorded at room temperature and a frequency of 9.060 GHz, is observed at a resonance field (B_0r) of 0.2285 T, which is substantially lower than the field corresponding to free electron resonance (ESR) (0.3236 T). Apart from the line corresponding to the resonance of the nanoparticle system, the spectrum also contains an additional weaker line, identified for a resonance field of ∼0.12 T, which is appreciably lower than B_0r. This line was attributed to magnetic ions complex that is in a disordered structure in the layer that has an average thickness of 1.4 nm, this layer being situated on the surface of the Zn_0.15Ni_0.85Fe₂O₄ nanoparticles that have a mean magnetic diameter of 8.9 nm.     

Giant magnetoimpedance in amorphous (Co0.93Fe0.7)63Ni10Si11B16 glass-coated microwire

Giant magnetoimpedance (GMI) effect has been measured in a glass-coated amorphous (Co_0.93Fe_0.7)₆₃Ni₁₀Si₁₁B₁₆ microwire as a function of DC magnetic field and up to the frequency of 11 MHz. The sample shows single peak GMI characteristics within the whole range of frequency. The domain structure of the above sample has been changed by applying tensile stresses up to 603 MPa and current annealing with a DC current of 50 mA for various time durations, and the corresponding effect on GMI has been studied in detail. A maximum change of 8.85% in MI of the as-quenched sample has been observed around a frequency of 5.05 MHz. Application of an external tensile stress reduces the GMI value by increasing the inner core domain, whereas heat treatment of the sample enhances the same. The square-shaped magnetic hysteresis loop of the as-quenched sample helps us understanding the MI results.