碳纳米管和天鹅绒阴极强流发射特性的对比研究

采用电泳沉积法、碳纳米管纸和化学气相沉积直接生长法制备了三种碳纳米管阴极. 从强流发射性能、阴极等离子体膨胀、阴极起动、发射均匀性、工作稳定性以及脉冲放气特性等多个方面, 对比研究了碳纳米管阴极和化纤天鹅绒阴极的强流发射特性, 研究表明碳纳米管阵列和碳纳米管纸阴极发射性能明显优于普通化纤天鹅绒, 碳纳米管阴极发射性能与碳纳米管取向无关, 管壁的缺陷发射对无序碳纳米管阴极强流发射具有重要贡献. 碳纳米管阴极的起动场强约为普通化纤天鹅绒的2/3, 电场上升率相同时碳纳米管阴极比化纤天鹅绒阴极起动时间短12–17 ns. 碳纳米管阴极发射均匀性优于化纤天鹅绒, 尤其是碳纳米管阵列, 整个阴极表面等离子体光斑致密且均匀. 在二极管本底气压为6×10^-3 Pa时, 碳纳米管纸阴极对应的二极管峰值气压不到0.3 Pa, 约为普通化纤天鹅绒阴极的1/5, 碳纳米管阵列阴极放气量在三种阴极中最少, 仅为0.042 Pa. 结果表明, 碳纳米管阴极在强流电子束源和相关高功率微波器件领域具有潜在的应用价值.     

Laser surface treatment of screen-printed carbon nanotube emitters for enhanced field emission

This paper investigates the surface treatment of screen-printed carbon nanotube (CNT) emitters using a 248 nm (KrF) excimer laser. The field emission characteristics of the CNT emitters are measured following irradiation using laser fluences ranging from 80 to 400 mJ/cm². The results show that the turn-on electric field, the current density, and the distribution of the emission sites are highly dependent on the value of the laser fluence and are optimized at a fluence of 150 mJ/cm². Two distinct laser fluence regimes are identified. In the low fluence regime, i.e. 80-150 mJ/cm², the surface treatment process is dominated by a photo ablation mechanism, which results in the gradual removal of the binding material from the cathode surface and leads to an improvement in the emission characteristics of the CNT cathodes with an increasing fluence. However, in the high fluence regime, i.e. 150-400 mJ/cm², the thermal ablation mechanism dominates; resulting in a removal of the CNTs from the cathode surface and a subsequent degradation in the emission characteristics.     

Influence of high-energy electron irradiation on field emission properties of multi-walled carbon nanotubes (MWCNTs) films

The effect of very high energy electron beam irradiation on the field emission characteristics of multi-walled carbon nanotubes (MWCNTs) has been investigated. The MWCNTs films deposited on silicon (Si) substrates were irradiated with 6 MeV electron beam at different fluence of 1×10¹⁵, 2×10¹⁵ and 3×10¹⁵ electrons/cm². The irradiated films were characterized using scanning electron microscope (SEM) and micro-Raman spectrometer. The SEM analysis clearly revealed a change in surface morphology of the films upon irradiation. The Raman spectra of the irradiated films show structural damage caused by the interaction of high-energy electrons. The field emission studies were carried out in a planar diode configuration at the base pressure of ∼1×10⁻⁸ mbar. The values of the threshold field, required to draw an emission current density of ∼1 μA/cm², are found to be ∼0.52, 1.9, 1.3 and 0.8 V/μm for untreated, irradiated with fluence of 1×10¹⁵, 2×10¹⁵ and 3×10¹⁵ electrons/cm². The irradiated films exhibit better emission current stability as compared to the untreated film. The improved field emission properties of the irradiated films have been attributed to the structural damage as revealed from the Raman studies.     

Enhanced field emission from LaB6 thin films with nanoprotrusions grown by pulsed laser deposition on Zr foil

Lanthanum hexaboride (LaB₆) films have been deposited on a zirconium foil by pulsed laser deposition method. The field emission studies of the LaB₆ deposited film have been performed in the planar diode configuration under ultra high vacuum conditions. The Fowler-Nordheim plots were found to be linear in accordance with the quantum mechanical tunneling phenomenon. A typical field emission current of 7.02 μA was drawn at an applied electric field of 2 V/μm. The field enhancement factor is calculated to be 8913 cm⁻¹, indicating that the field emission is from nanoscale protrusions present on the emitter surface. The atomic force microscope (AFM) investigation of the surface clearly shows the conical shaped nanoprotrusions of few hundred nanometers with asperities of 20-40 nm on its top. The emission current-time plot recorded at the pre-set value of emission current of 5 μA over a period of more than 3 h exhibits an initial increase and subsequent stabilization of the current. The results reveal that the LaB₆/Zr field emitter obtained by the pulsed laser deposition (PLD) is a promising cathode material for practical applications in field emission-based devices.     

The influence of H2 plasma treatment on the field emission of amorphous GaN film

The influence of H₂ plasma treatment on the field emission properties of amorphous GaN (a-GaN) films is studied. It is found that the treatment makes little change to the surface morphology. The current density of the treated film decreases from 400 to 30 μA/cm² at the applied field of about 30 V/μm. The treatment can reduce the defects in a-GaN films, and therefore the treatment results in the weakening of the tunneling emission of the a-GaN film at the high field region. The treatment also seems to change the conduction mechanism of the a-GaN film.     

Synthesis of Cu-ZnO and C-ZnO nanoneedle arrays on zinc foil by low temperature oxidation route: Effect of buffer layers on growth, optical and field emission properties

Different densities of ZnO nanoneedle films have been prepared by pre-coated zinc foils with thin layer of copper and carbon followed by thermal oxidation at 400 °C in air. The X-ray diffraction patterns show well defined peaks, which could be indexed to the wurtzite hexagonal phase of ZnO. The scanning electron microscope images clearly reveal formation of ZnO needles on the entire substrate surface. The X-ray photoelectron spectroscopy studies indicate that Cu and C ions are incorporated into the ZnO lattice. Photoluminescence studies evaluate different emission bands originated from different defect mechanism. From the field emission studies, the threshold field, required to draw emission current density of ∼100 μA/cm², is observed to be 2.25 V/μm and 1.57 V/μm for annealed zinc foil pre-coated with copper and carbon, respectively. The annealed film with copper layer exhibits good emission current stability at the pre-set value of ∼100 μA over a duration of 4 h. The results show that buffer layer is an important factor to control the growth rate, resulting in different density of ZnO needles, which leads to field emission properties. This method may have potential in fabrication of electron sources for high current density applications.     

Formation of aligned ZnO nanorods on self-grown ZnO template and its enhanced field emission characteristics

We report a novel method for producing aligned ZnO nanorods (ANR) on self-grown ZnO template in a single step process involving growth of ZnO by vapor transport, followed by quenching of growing ZnO flux in liquid nitrogen. In the present study Zn powder turns into ZnO sheet under oxygen flow at ∼900 °C and bottom surface of the sheet acts as template for the growth of ANR. It is revealed from XRD and EDAX analysis that the bottom of the sheet is Zn rich region and acts as self catalyst for the growth of ANR. The grown nanorods have length up to several tens of micrometers with diameters ranging from ∼100 to 150 nm. Microstructural analysis of ANR indicates the fractal like configuration. The field emission properties have been investigated for ANR with fractal geometry using the ANR on self-grown ZnO template as a cathode directly. The turn-on electric field required to draw current density of ∼1.0 μA/cm² has been found to be ∼0.98 V/μm. The field enhancement factor based on Fowler-Nordheim (F-N) plot was found to be ∼7815 for ANR. The fractal geometry of ANR has been shown to be advantageous for achieving improved field emission features. The present investigations of synthesis involving formation of ANR over self-grown ZnO template, together with fractal configuration of the as-synthesized ANR, are first of their type.     

12MeV直线感应加速器二极管优化设计研究

 本文用MAGIC程序对设计的多种12MV直线感应加速器的二极管结构进行模拟计算,得出了二极管阴极表面电场强度分布,并根据实验研究结果,得到了结构最佳设计的二极管模型;随后利用扫描电镜方法对不同天鹅绒的结构进行了分析与发射性能实验研究。最后得到优化后的二极管产生的电子束束流参数为发射束流I_e=8.50kA,传输束流I₈=3.0kA ,打靶束流I₀=2.30kA。     

Surface modification and submicron structure of carbon fibers through high current pulse

This paper investigated the behavior of carbon fibers subjected to a ∼20 kA, ∼5 μs high current pulse. It was found that the broken fibers and submicron particles were generated by electrical explosion process. After high current pulsed discharge, the fiber diameter increased significantly, from 5-7 μm to ∼13 μm. Also, the surface rupture of carbon fibers with valleys of hundreds of nanometers was observed. Most notably, the submicron particles appeared with two typical shapes (near-sphere and square). The high current pulsed discharge of carbon fibers can be divided into three stages, namely, heating stage, phase change stage, and explosion stage. Indeed, the electrical explosion process occurred in the last stage of ∼200 ns. The nature behind these results is closely related to the plasma development during the explosion process. The plasma expansion due to a large plasma thermal stress leads to the incomplete explosion. In the explosion stage, the current passing through the fibers exhibited a huge fluctuation, indicating plasma instabilities. Finally, the physical mechanisms, how to affect the surface morphology of carbon fibers, are presented.     

Emission properties of Ti-DLC films prepared by unbalanced magnetron sputtering

The field emission properties of Ti-DLC films in diode and coplanar device structures were studied. An emission current density of 1.14 A/cm² could be obtained at an applied field of 33 V/μm and the threshold field was 24 V/μm for the coplanar emission structure. The silicon substrate was found to limit the emission current in the diode structure because of its high resistivity.     

Characteristics of Co-filled carbon nanotubes

The Co-filled carbon nanotubes (CNTs) film was produced on silicon substrate by electron cyclotron resonance microwave plasma chemical vapor deposition (ECR-CVD). The effects of different plasma powers of 200, 300, 400 and 500 W, on the morphology, structure and electrical properties of the CNTs film, were studied. The results showed that the surface density of the vertical nanotubes decreased when the plasma power was higher than 200 W. When plasma power of 300 W was used, the ends of the metal-filled carbon nanotubes (MF-CNTs) became straighter and more uniform. The Co-filled CNTs grown at 300 and 400 W had a current discharge at the applied voltages of 30 and 40 V, respectively. In addition, the surface morphology and the structure of the CNTs film were examined using scanning electron microscopy (SEM) and high-resolution field emission gun transmission electron microscopy (TEM). Energy dispersive X-ray spectroscopy (EDXS) analyses were performed to identify the composition of the material inside the CNTs.     

High-field electron emission of carbon nanotubes grown on carbon fibers

Carbon nanotubes with uniform density were synthesized on carbon fiber substrate by the floating catalyst method. The morphology and microstructure were characterized by scanning electron microscopy and Raman spectroscopy. The results of field emission showed that the emission current density of carbon nanotubes/carbon fibers was 10 μA/cm² and 1 mA/cm² at the field of 1.25 and 2.25 V/μm, respectively, and the emission current density could be 10 and 81.2 mA/cm² with the field of 4.5 and 7 V/μm, respectively. Using uniform and sparse density distribution of carbon nanotubes on carbon fiber substrate, the tip predominance of carbon nanotubes can be exerted, and simultaneously the effect of screening between adjacent carbon nanotubes on field emission performance can also be effectively decreased. Therefore, the carbon nanotubes/carbon fibers composite should be a good candidate for a cold cathode material.     

Study of transients in the formation of heavy-current nanosecond electron beams

Results are presented from experimental and numerical studies of the spatial and temporal microstructure of a relativistic heavy-current electron beam of nanosecond duration. The beam is formed in a magnetically insulated coaxial diode with an edge-emitting cathode. Microcurrent oscillations and azimuthal nonuniformity of the beam are seen, the scale of the latter depending on the maximum cyclotron radius of the electrons. Two- and three-dimensional numerical calculations performed by the macroparticle method show that space-charge oscillations near the cathode produce these phenomena even in the case of a uniform emission surface. It is shown that the increase in the full current of the beam that occurs during the pulse in a weak magnetic field is connected with the gradual propagation of emission to the cylindrical outside surface of the cathode. A study is made of the effect of the discreteness of the emission surface on the impedance and current of the vacuum diode. The linear increase seen in current during the pulse with a small number of emission centers is attributed to an increase in their size as a result of expansion of the cathode plasma. Institute of Heavy-Current Electronics, Siberian Branch of the Russian Academy of Sciences. Translated from Izvestiya Vysshikh Uchebnykh Zavedenii, No. 12, pp. 31–48, December, 1996.     

Application of printed nanocrystalline diamond film for electron emission cathode

The low-cost and large area screen-printed nano-diamond film (NDF) for electronic emission was fabricated. The edges and corners of nanocrystalline diamond are natural field-emitters. The nano-diamond paste for screen-printing was fabricated of mixing nano-graphite and other inorganic or organic vehicles. Through enough disperse in isopropyl alcohol by ultrasonic nano-diamond paste was screen-printed on the substrates to form NDF. SEM images showed that the surface morphology of NDF was improved, and the nano-diamond emitters were exposed from NDF through the special thermal-sintering technique and post-treatment process. The field emission characteristics of NDF were measured under all conditions with 10⁻⁶ Pa pressure. The results indicated that the field emission stability and emission uniformity of NDF were improved through hydrogen plasma post-treatment process. The turn-on field decreased from 1.60 V/μm to 1.25 V/μm. The screen-printed NDF can be applied to the displays electronic emission cathode for low-cost outdoor in large area.     

Field emission behavior of cuboid zinc oxide nanorods on zinc-filled porous silicon

Single-crystalline zinc oxide (ZnO) nanorods with cuboid morphology have been prepared on the zinc-filled porous silicon substrate using a vapor phase transport method. Field-emission measurements showed that the turn-on field and threshold field of the cuboid ZnO nanorods film were about 3.2 and 8.2 V/μm respectively. From the emitter surface, a homogeneous emission image was observed with emission site density (ESD) of ∼10⁴ cm⁻². The better emission uniformity and the high ESD may be attributed to a large number of ZnO nanocrystallites as emitter on the surface of the nanorod end contributing to emission.     

Synthesis of amorphous carbon nanowalls by DC-PECVD on different substrates and study of its field emission properties

Amorphous carbon thin films with quasi vertical nanowall-like morphologies have been synthesized via direct current plasma enhanced chemical vapor deposition on both copper and silicon substrates with acetylene as a carbon precursor. The deposition temperature and pressure were maintained at 750 °C and 5 mbar respectively. The morphology of the as-prepared samples has been investigated with the help of a field emission scanning electron microscope and an atomic force microscope, both revealing nanowall-like morphologies with thicknesses of the walls ∼6-15 nm. The as-prepared carbon nanowalls showed good field electron emission with a turn-on field as low as 1.39 V/μm. The effect of inter-electrode distance on the field electron emission has also been studied in detail.     

Low-voltage pulse exciting electron emission from ferroelectric copolymer film cathode: Role of film thickness and emission stability

Ferroelectric copolymer thin films P(VDF-TrFE) are used as a ferroelectric cathode for investigation of their electron emission properties. This ferroelectric copolymer films with different thicknesses are deposited by spin-coating method, and then the annealing process is carried out to improve the crystallinities of as-deposited copolymer films. The measurement results of ferroelectric electron emission showed that the copolymer P(VDF-TrFE) films had a desired ferroelectric electron emission ability excited at low-voltage pulse, and its peak emission current can reach to be ∼1.3 μA when the pulse voltage is 280 V. In addition, the effect of film thickness on electron emission property and emission stability of copolymer thin film P(VDF-TrFE) are discussed.     

百纳秒脉冲下强流二极管的工作稳定性

以闪光二号加速器为研究平台,实验研究了前沿80 ns和34 ns脉冲电压下的二极管工作稳定性,通过对比实验结果和数值模拟结果,分析了脉冲前沿对二极管启动时间、阴极发射均匀性和阻抗重复性的影响,探讨了脉冲前沿对平面阴极二极管工作状态的影响机制。实验结果表明:脉冲前沿、二极管启动时间增加时,二极管的阻抗重复性降低;平面阴极易于在中心位置形成强区域发射,等离子体覆盖整个阴极发射面的时间随脉冲前沿增大而增加;屏蔽效应对阴极发射的影响随前沿增加而变大,进而导致阴极表面不均匀强点发射,等离子体运动速度增加,阴极有效发射面积减小,在等离子体运动速度和阴极有效发射面积共同作用下,二极管工作稳定性下降。     

Enhanced field emission characteristics of boron doped diamond films grown by microwave plasma assisted chemical vapor deposition

Boron doped diamond films were synthesized on silicon substrates by microwave plasma chemical vapor deposition (MPCVD) technique. The effect of B₂O₃ concentration varied from 1000 to 5000 ppm on the field emission characteristics was examined. The surface morphology and quality of films were characterized by scanning electron microscope (SEM) and Raman spectroscopy. The surface morphology obtained by SEM showed variation from facetted microcrystal covered with nanometric grains to cauliflower of nanocrystalline diamond (NCD) particles with increasing B₂O₃ concentration. The Raman spectra confirm the formation of NCD films. The field emission properties of NCD films were observed to improve upon increasing boron concentration. The values of the onset field and threshold field are observed to be as low as 0.36 and 0.08 V/μm, respectively. The field emission current stability investigated at the preset value of ∼1 μA is observed to be good, in each case. The enhanced field emission properties are attributed to the better electrical conductivity coupled with the nanometric features of the diamond films.     

强流四脉冲电子束源实验研究

 为了进行强流多电子束源研究，对现有2MeV LIA 注入器进行了四脉冲改造，二极管脉冲电压约500kV。实验研究了天鹅绒阴极在四脉冲条件下的发射能力、传导电流负载效应以及阴极等离子体运动对阴极电子发射和束能量的影响。利用空间电荷限制流模型推算出阴极等离子体膨胀速率在1 ~4cm/μs之间。