Combustion synthesis and luminescence properties of NaY1−xEux(WO4)2 phosphors

The red phosphors NaY_1−xEu_x(WO₄)₂ with different concentrations of Eu³⁺ were synthesized via the combustion synthesis method. As a comparison, NaEu(WO₄)₂ was prepared by the solid-state reaction method. The phase composition and optical properties of as-synthesized samples were studied by X-ray powder diffraction and photoluminescence spectra. The results show that the red light emission intensity of the combustion synthesized samples under 394 nm excitation increases with increase in Eu³⁺ concentrations and calcination temperatures. Without Y ions doping, the emission spectra intensity of the NaEu(WO₄)₂ phosphor prepared by the combustion method fired at 900 °C is higher than that prepared by the solid-state reaction at 1100 °C. NaEu(WO₄)₂ phosphor synthesized by the combustion method at 1100 °C exhibits the strongest red emission under 394 nm excitation and appropriate CIE chromaticity coordinates (x=0.64, y=0.33) close to the NTSC standard value. Thus, its excellent luminescence properties make it a promising phosphor for near UV InGaN chip-based red-emitting LED application.     

Luminescent properties of green- or red-emitting Eu-doped Sr3Al2O6 for LED

Eu²⁺-doped Sr₃Al₂O₆ (Sr_3−xEu_xAl₂O₆) was synthesized by a solid-state reaction under either H₂ and N₂ atmosphere or CO atmosphere. When H₂ was used as the reducing agent, the phosphor exhibited green emission under near UV excitation, while CO was used as the reducing agent, the phosphor mainly showed red emission under blue light excitation. Both emissions belong to the d-f transition of Eu²⁺ ion. The relationship between the emission wavelengths and the occupation of Eu²⁺ at different crystallographic sites was studied. The preferential substitution of Eu²⁺ into different Sr²⁺ cites at different reaction periods and the substitution rates under different atmospheres were discussed. Finally, green-emitting and red-emitting LEDs were fabricated by coating the phosphor onto near UV- or blue-emitting InGaN chips.     

Synthesis and characterization of Sr3Al2O6：Eu2＋, Dy3＋ phosphors prepared by sol-gel-combustion processing

A type of red luminescent Sr3Al2O6:Eu2+, Dy3+ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3- by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3Al2O6:Eu2+, Dy3+. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250 C. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of (Sr0.94Eu0.03Dy0.03)3Al2O6 phosphors sintered at 1250 ℃ lasts for over 1000 s when the excited source is cut off.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

NIR to visible upconversion in Er/Yb co-doped CaYAl3O7 phosphor obtained by solution combustion process

Using the combustion synthesis, CaYAl₃O₇:Er³⁺ phosphor powders co-doped with Yb³⁺ have been prepared at low temperatures (550 °C) in a few minutes. Formation of the compound was confirmed by X-ray powder diffraction. Near-infrared to visible upconversion fluorescence emission in the Er³⁺ doped CaYAl₃O₇ phosphor powder has been observed. The effect of co-doping with triply ionized ytterbium in the CaYAl₃O₇:Er³⁺ phosphor has been studied and the process involved is discussed.     

White light-emitting diodes using blue and yellow-orange-emitting phosphors

A blue-emitting phosphor, BaMgAl₁₀O₁₇:Eu²⁺ (BAM) and a yellow-orange phosphor, Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ were prepared by the solid-state reaction. Excitation and emission spectra results showed that BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ can be efficiently excited by near-ultraviolet (n-UV)-visible light from 250 to 440 nm. The effects of the doped-Eu²⁺ concentration in BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ on the photoluminescence were investigated in detail. White light-emitting diodes (LED) was obtained by combining n-UV LED chip (GaN-based 380 nm emitting) with BaMgAl₁₀O₁₇:0.09Eu²⁺ and 0.1Ba²⁺-codoped Sr₃SiO₅: 0.2Eu²⁺ phosphors with the characteristic of color-rendering index of 86, CIE chromaticity coordinates (x,y) of (0.3216,0.3096), and color temperature T_c of 5700 K. As the current increases, the relative intensity simultaneously increases. The CIE chromaticity coordinates (x,y) of the white LED tends to decrease. The correlated color temperature T_c increases from 4100 to 7500 K and the color-rendering index R_a increases from 82 to 87 simultaneously.     

Spherical Zn2SiO4:Eu@SiO2 phosphor particles in core-shell structure: Synthesis and characterization

Spherical SiO₂ particles have been coated with Zn₂SiO₄:Eu³⁺ phosphor layers by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn₂SiO₄:Eu³⁺@SiO₂ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, and lifetime. The results demonstrate that the Zn₂SiO₄:Eu³⁺@SiO₂ particles, which have regular and uniform spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu³⁺ concentration, annealing temperature and charge compensators of Li⁺ ions on the PL emission intensities were investigated in detail.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Cathodoluminescence characteristics of particles and film of (Y, Zn)2O3:Eu phosphor prepared by spray pyrolysis

Eu-doped Y₂O₃ particles with spherical shape and fine size were prepared by spray pyrolysis. The cathodoluminescence of Y₂O₃:Eu³⁺ powder was optimized by substituting small amount of zinc atoms in place of yttrium sites. As a result, the optimized (Y, Zn)₂O₃:Eu³⁺ phosphor showed 60% improved cathodoluminescence compared with Y₂O₃:Eu³⁺ particles. The prepared (Y, Zn)₂O₃:Eu³⁺ phosphor had spherical shape and 0.726 μm in mean size. Using these particles, the thickness of the phosphor film was controlled by varying the phosphor loading. The brightness and luminous efficiency of phosphor films prepared were monitored with varying the accelerating voltage ranges from 4 to 14 kV. The dependency of the luminous efficiency on the accelerating voltage was very sensitive to the phosphor loading. As increasing the accelerating voltage from 4 to 14 kV, the brightness of phosphor films prepared was monotonically increased from 200 to 1085 cd/cm²_, but the saturation in the luminous efficiency appeared at 10 kV. The highest efficiency was achieved when the number of phosphor-particles layer was about 3. More details about the luminous efficiency and brightness were discussed with changing the phosphor loading.     

Highly water resistant surface coating by fluoride on long persistent Sr4Al14O25:Eu/Dy phosphor

A novel and efficient method of providing moisture resistance of inorganic particles such as divalent europium activated strontium aluminate phosphors (Sr₄Al₁₄O₂₅:Eu²⁺/Dy³⁺) was developed by firing the phosphor in the presence of appropriate amount of ammonium fluoride at a temperature of 600-700 °C. Scanning electron microscopy, X-ray diffraction, FT-IR, EDAX and Photoluminescence measurements were carried out to characterize the uncoated and coated samples. The pH measurements were carried out for the water resistivity measurements. The phosphor particles became coated with a moisture-impervious thin coating that did not suppress the luminescence of the phosphor and can withstand complete immersion in water for long periods of time, showing very high water resistivity.     

PL and CL degradation and characteristics of SrAl2O4: Eu,Dy phosphors

Strontium aluminate phosphors are ideal for luminescent infrastructure materials. Their brightness and persistent glow time are much higher than previously used sulphide phosphors. Strontium aluminates prepared by the sol–gel and combustion methods are compared with commercially available strontium aluminate. High luminescent efficient SrAl₂O₄:Eu²⁺,Dy³⁺ pulsed laser deposited (PLD) thin films were also produced using the commercially available powder. Photoluminescence (PL) degradation studies showed that the phosphor intensity decreased about 20% over a period of 2 weeks under ultraviolet (UV) irradiation. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) showed that cathodoluminescence (CL) degradation is due to the formation of SrO due to electron stimulated surface reactions. The light output mechanism of the phosphor is also discussed in more detail.     

Integrated chemical process for exothermic wave synthesis of high luminance YAG:Ce phosphors

In this paper, high-luminance yellow-emitting Y₃Al₅O₁₂:Ce³⁺ phosphor (YAG:Ce) microparticles were prepared in a solid flame using a 1.425Y₂O₃+2.5Al₂O₃+0.15CeO₂+k(KClO₃+urea)+mNH₄F precursor mixture (here k is the number of moles of the KClO₃+urea red-ox mixture, and m is the number of moles of NH₄F). The self-sustaining combustion process for the entire reaction sample was provided by the heat generated from the KClO₃+urea mixture. Parametric studies demonstrated that the maximum temperature in the combustion wave varied from 885 to 1200 °C for k=2.0-3.0 mole and m=0-1.5 mole. X-ray analysis results showed that the product obtained in the solid flame consisted of Y₃Al₅O₁₂:Ce³⁺ and KCl phases. Therefore, after dissolving potassium chloride in distillated water, pure-phase YAG:Ce phosphor powder was obtained. The as-prepared YAG:Ce phosphor particles had diameters of 10-25 μm and good dispersity and exhibited luminescence properties comparable to those of YAG:Ce phosphor powders prepared by conventional high-temperature processing.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

SiN掺杂提高BaMgAl10O17:Eu2+荧光粉光学性能的第一性原理研究

使用基于密度泛函理论的CASTEP软件计算了BAM:Eu²⁺(BaMgAl₁₀O₁₇:Eu²⁺)荧光粉在SiN掺杂前后的能带、态密度、吸收光谱和Mulliken布居．Eu²⁺处于BR位置光吸收更强;SiN掺杂使处于BR位置的Eu²⁺的数量上升,而处于mO位置的Eu²⁺的数量下降,抵消了SiN掺杂降低Eu的态密度对光谱的影响．所以适量掺杂的SiN提高了BAM:Eu²⁺荧光粉的吸收发射光谱强度．Si-N键和Eu-N键的Mulliken布居数分别高于Al-O键和Eu-O键, 说明Si-N键和Eu-N键的共价性分别强于Al-O键和Eu-O键．发光中心Eu²⁺局域结构共价性的增强降低了BAM:Eu²⁺镜面层的活性,这是SiN掺杂提高BAM:Eu²⁺+荧光粉光学稳定性的主要原因．     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

Luminescent properties of a new green emitting Eu doped CaZrSi2O7 phosphor for WLED applications

CaZrSi₂O₇ (CZS), a modification of the thortveitite family, was prepared as a polycrystalline powder material by the conventional solid-state reaction method. Structural, thermal and photoluminescence (PL) properties of the prepared material were investigated in order to evaluate its potentiality. XRD patterns confirm the monoclinic phase of CaZrSi₂O₇: Eu²⁺ phosphors.. Emissions arising from transitions between the 5d and 4f orbital gaps of Eu²⁺ are manifested in the broadband excitation and emission spectra with major peaks at 363 and 512 nm, respectively. The excitation wavelength matches well with that of the emission of the ultraviolet-light emitting diode (UV-LED). Concentration quenching occurs when the Eu²⁺ concentration is beyond 0.05 and the dipole-dipole interaction was the reason for the corresponding quenching mechanism. The temperature dependence of emission intensity of CZS: Eu²⁺ phosphor was investigated and it showed better thermal stability than the standard YAG: Ce³⁺ phosphor.     

Preparation and luminescent properties of cubic Eu:Y2O3 nanocrystals and comparison to bulk Eu:Y2O3

Y₂O₃:Eu³⁺ nanocrystals were prepared by combustion synthesis. The particle size estimated by X-ray powder diffraction (XRD) was about 10 nm. A blue-shift of the charge-transfer (CT) band in excitation spectra was observed in Y₂O₃:Eu³⁺ nanocrystals compared with bulk Y₂O₃:Eu³⁺. The electronic structure of Y₂O₃ is calculated by density functional method and exchange and correlation have been treated by the generalized gradient approximation (GGA) within the scheme due to Perdew-Burke-Ernzerhof (PBE). The calculated results show that the energy centroid of 5d orbital in nanocrystal has increasing trend compared with that in the bulk material. The bond length and bond covalency are calculated by chemical bond theory. The bond lengths of Y₂O₃:Eu³⁺ nanocrystal are shorter than those of the bulk counterpart and the bond covalency of Y₂O₃:Eu³⁺ nanocrystal also has an increasing trend. By combining centroid shift and crystal-field splitting, the blue-shift of the CT band is interpreted.     

节能灯用BaMgAl10O17:Eu2+,Mn2+荧光粉的劣化机理研究

对节能灯用BaMgAl₁₀O₁₇: Eu²⁺,Mn²⁺荧光粉的热劣化和紫外辐照劣化机理进行了对比研究. 发现热处理和紫外辐照处理均对BaMgAl₁₀O₁₇: Eu²⁺,Mn²⁺产生明显的发光劣化作用. 研究结果表明：热劣化主要涉及到Eu²⁺ 的氧化及其格位偏移, 而紫外辐照劣化与上述过程无关. 紫外辐照劣化主要源自高能紫外辐照使Eu²⁺ 处于更加不稳定的状态, 从而降低Eu²⁺ 的直接吸收和发射强度.     

Enhanced blue emission and EPR study of LaMgAl11O19:Eu phosphors

Europium doped LaMgAl₁₁O₁₉ phosphor was prepared by the combustion method. The as-prepared and post-treated (1350 °C 10 h 5% H₂+95% N₂) phosphors were investigated by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), scanning electron microscopy (SEM), photoluminescence (PL) and electron paramagnetic resonance (EPR) techniques. XRD patterns show that LaMgAl₁₁O₁₉:Eu phosphors have hexagonal structure. FT-IR spectrum exhibits absorption bands corresponding to the stretching vibration of AlO₄ and AlO₆. Morphological studies reveal that this phosphor has faceted plates of varying sizes and shapes. The as-prepared LaMgAl₁₁O₁₉:Eu phosphor consists of both Eu³⁺ and Eu²⁺ ions. The phosphor exhibits a bright blue emission at 450 nm (4f⁶5d→4f⁷ transition of Eu²⁺). On post-treating the phosphor we are able to enhance the blue emission efficiency by 330%. The process was detected from the evolution of excitation, emission and EPR spectra and the results are discussed.