Magnetocaloric effect in Gd6Co1.67Si3 compound with a second-order phase transition

The magnetic properties and the magnetic entropy change AS have been investigated for Gd6Co1.67Si3 compounds with a second-order phase transition. The saturation moment at 5 K and the Curie temperature TC are 38.1μB and 298 K, respectively. The AS originates from a reversible second-order magnetic transition around TC and its value reaches 5.2 J/kg.K for a magnetic field change from 0 to 5T. The refrigerant capacity （RC） of Gd6Co1.67Si3 are calculated by using the methods given in Refs.[12] and [21], respectively, for a field change of 0 5T and its values are 310 and 440 J/kg, which is larger than those of some magnetocaloric materials with a first-order phase transition.     

Giant magnetocaloric effect in the Gd5Ge2.025Si1.925In0.05 compound

The magnetocaloric properties of the Gd 5 Ge 2.025 Si 1.925 In 0.05 compound have been studied by x-ray diffraction,magnetic and heat capacity measurements.Powder x-ray diffraction measurement shows that the compound has a dominant phase of monoclinic Gd5Ge2Si2-type structure and a small quantity of Gd 5(Ge,Si) 3-type phase at room temperature.At about 270 K,this compound shows a first order phase transition.The isothermal magnetic entropy change(△SM) is calculated from the temperature and magnetic field dependences of the magnetization and the temperature dependence of MCE in terms of adiabatic temperature change(△Tad) is calculated from the isothermal magnetic entropy change and the temperature variation in zero-field heat-capacity data.The maximum S M is 13.6 J·kg-1·K-1 and maximum △Tad is 13 K for the magnetic field change of 0-5 T.The Debye temperature(θD) of this compound is 149 K and the value of DOS at the Fermi level is 1.6 states/eV·atom from the low temperature zero-field heat-capacity data.A considerable isothermal magnetic entropy change and adiabatic temperature change under a field change of 0-5 T jointly make the Gd5Ge2.025Si1.925 In 0.05 compound an attractive candidate for a magnetic refrigerant.     

Magnetic properties and magnetocaloric effects in Tb6Co1.67Si3 compound

Magnetic properties and magnetocaloric effects of Tb₆Co_1.67Si₃ have been investigated by magnetization measurement. This compound is of a hexagonal Ce$_{6}$Ni$_{2}$Si$_{3}$-type structure with a saturation magnetization of 187\,emu/g at 5\,K and a reversible second-order magnetic transition at Curie temperature $T_{\rm C} = 186$\,K. A magnetic entropy change $\Delta S = 7$\,J\,$\cdot$\,kg$^{-1}$\,$\cdot$\,K$^{-1}$ is observed for a magnetic field change from 0 to 5\,T. A large value of refrigerant capacity (RC) is found to be 330\,J/kg for fields ranging from 0 to 5\,T. The large RC, the reversible magnetization around $T_{\rm C}$ and the easy fabrication make the Tb₆Co_1.67Si₃ compound a suitable candidate for magnetic refrigerants in a corresponding temperature range.     

Effect of Fe-substitution on microstructure, hysteresis behaviour and magnetocaloric effect in Gd5Si2Ge2 Alloys

Effect of Fe-substitution on the phase formation, partitioning behaviour of Fe in the co-existing phases, magneto-structural transition, magnetic entropy change and associated hysteresis losses has been investigated in Gd₅Si₂Ge₂ alloy. The virgin alloy crystallizes in monoclinic Gd₅Si₂Ge₂-type phase, while Fe-substituted alloys form mixed monoclinic Gd₅Si₂Ge₂-type and orthorhombic Gd₅Si₄-type phases. Electron probe microanalysis reveals that Fe does not dissolve in the matrix, but influences the magneto-structural transitions. Magneto-structural characterization of the Fe-containing alloys reveals that the Fe-substitution suppresses the structural transition observed at 273 K in virgin alloy. A maximum magnetic entropy change, ΔS_M of 6.5 J/kg-K at 273 K was observed for a field change of 2 T in Gd₅Si₂Ge₂ alloy. The Fe-substituted alloys exhibit lower value of ΔS_M but with reduced hysteresis losses.     

Field and temperature induced colossal strain in Gd5(SixGe1−x)4

Gd₅(Si_xGe_1−x)₄, known for its giant magnetocaloric effect, also exhibits a colossal strain of the order of 10,000 ppm for a single crystal near its coupled first-order magnetic-structural phase transition, which occurs near room temperature for the compositions 0.41≤x≤0.575. Such colossal strain can be utilised for both magnetic sensor and actuator applications. In this study, various measurements have been carried out on strain as a function of magnetic field strength and as a function of temperature on single crystal Gd₅Si₂Ge₂ (x=0.5), and polycrystalline Gd₅Si_1.95Ge_2.05 (x=0.487) and Gd₅Si_2.09Ge_1.91 (x=0.52). Additionally a giant magnetostriction/thermally induced strain of the order of 1800 ppm in polycrystalline Gd₅Si_2.09Ge_1.91 was observed at its first order phase transition on varying temperature using a Peltier cell without the use of bulky equipment such as cryostat or superconducting magnet.     

Thermal stability,magnetic and magnetocaloric properties of Gd55Co35M10 (M = Si,Zr and Nb) melt-spun ribbons

The thermal stability, magnetic and magnetocaloric properties of Gd₅₅Co₃₅M₁₀ (M = Si, Zr and Nb) melts-pun ribbons were studied. The relatively high reduced glass transition temperature (T_x1/T_m > 0.60) and low melting point (T_m) resulted in excellent glass forming ability (GFA). The Curie temperatures (T_C) of melt-spun amorphous ribbons Gd₅₅Co₃₅M₁₀ for M = Si, Zr and Nb were 166, 148 and 173 K, respectively. For a magnetic field change of 2 T, the values of maximum magnetic entropy change (−ΔS_M)^max for Gd₅₅Co₃₅Si₁₀, Gd₅₅Co₃₅Zr₁₀ and Gd₅₅Co₃₅Nb₁₀ were found to be 2.86, 4.28 and 4.05 J kg⁻¹K⁻¹, while the refrigeration capacity (RC) values were 154, 274 and 174 J kg^–1, respectively. The RC_FWHM values of amorphous alloys Gd₅₅Co₃₅M₁₀ (M = Si, Zr and Nb) are comparable to or larger than that of LaFe_11.6Si_1.4 crystalline alloy. Large values of (−ΔS_M)^max and RC along with good thermal stability make Gd₅₅Co₃₅M₁₀ (M = Si, Zr and Nb) amorphous alloys be potential materials for magnetic cooling operating in a wide temperature range from 150 to 175 K, e.g., as part of a gas liquefaction process.     

Influence of hydrogenation on the electronic structure and the itinerant-electron metamagnetic transition in strong magnetocaloric compound La(Fe0.88Si0.12)13

The influence of interstitial hydrogen on the electronic structure and the itinerant-electron metamagnetic (IEM) transition in strong magnetocaloric compound La(Fe_0.88Si_0.12)₁₃H_1.6 has been investigated by Mössbauer spectroscopy. A slight change in the average hyperfine field at 4.2 K was observed after hydrogen absorption. In contrast, the thermally induced first-order transition related to the IEM transition for y=1.6 appears at the Curie temperature T_C=330 K, much higher than T_C=195 K for y=0.0. The increase of isomer shift δ_IS at 4.2 K indicates that the valence electron transfer from hydrogen to Fe is negligibly small, hence the change in the magnetic state is closely associated with a volume expansion after hydrogen absorption. No change in shape by hydrogenation for the Mössbauer spectra in the paramagnetic state has been observed except for a difference in only δ_IS, indicating the volume expansion by hydrogenation is isotropic. Accordingly, the significant increase of T_C by hydrogen absorption is attributed to the magnetovolume effect associated with characteristic feature in IEM compounds. A discontinuous change of ferromagnetic moment, ΔM, around T_C has been observed by Mössbauer spectra, as expected from the magnetization measurement. The value of ΔM is slightly decreased by increase of T_C after hydrogenation but its magnitude is almost the same due to the stabilization of ferromagnetic moment. As a result, strong magnetocaloric effect is maintained up to room temperature after hydrogenation.     

Magnetic field and temperature-induced first-order transition in Gd5(Si1.5Ge2.5): a study of the electrical resistance behavior

Magnetic field (0–4 T) and temperature dependencies (4.2–320 K) of the electrical resistance of Gd₅(Si_1.5Ge_2.5), which undergoes a reversible first-order ferromagnetic↔paramagnetic phase transition, have been measured. The electrical resistance of Gd₅(Si_1.5Ge_2.5) indicates that the magnetic phase transition can be induced by both temperature and magnetic field. The temperature dependence of the electrical resistance, R(T), for heating at low temperatures in the zero magnetic field has the usual metallic character, but at a critical temperature of T_cr=216 K the resistance shows a 20% negative discontinuity due to the transition from the low-temperature high-resistance state to the high-temperature low-resistance state. The R(T) dependence for cooling shows a similar but positive 25% discontinuity at 198 K. The isothermal magnetic field dependence of the electrical resistance from 212T224 K indicates the presence of temperature-dependent critical magnetic fields which can reversibly transform the paramagnetic phase into the ferromagnetic phase and vice versa. The critical magnetic fields diagram determined from the isothermal magnetic field dependencies of the electrical resistance of Gd₅(Si_1.5Ge_2.5) shows that the FM↔PM transition in zero magnetic field on cooling and heating occurs at 206 and 213 K, respectively. The full isothermal magnetic filed hysteresis for the FM↔PM transition is 2 T, and the isofield temperature gap between critical magnetic fields is 7 K.     

Magnetocaloric effect in high-energy ball-milled Gd5Si2Ge2 and Gd5Si2Ge2/Fe nanopowders

Evolution of structure and magnetocaloric properties in ball-milled Gd₅Si₂Ge₂ and Gd₅Si₂Ge₂/0.1 wt% Fe nanostructured powders were investigated. The high-energy ball-milled powders were composed of very fine grains (70–80 nm). Magnetization decreased with milling time due to decrease in the grain size and randomization of the magnetic moments at the surface. The magnetic entropy change (ΔS_M) was calculated from the isothermal magnetization curves and a maximum value of 0.45 J/kg K was obtained for 32 h milled Gd₅Si₂Ge₂ alloy powder for a magnetic field change of 2 T while it was still low in Fe-contained alloy powders. The thermo-magnetic measurements revealed that the milled powders display distribution of magnetic transitions, which is desirable for practical magnetic refrigerant to cover a wide temperature span.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Structure and magnetic entropy change of suck-cast Gd60Co26Al6Ge8 alloy

The Gd₆₀Co₂₆Al₆Ge₈ alloy has been prepared by the copper-mold suck-casting and its phase component has been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS). It is shown that this alloy consists of primary crystalline Gd₅Ge₃ phase and amorphous matrix. The glass transition temperature (T_g) and crystallization temperatures (T_x) occur at 292 and 320 °C, respectively. The maximal magnetic entropy change (ΔS_M) under 0-5 T field is about 7.6 J (kg⁻¹ K⁻¹) at 155 K and the refrigeration capacity (RC) is about 768 J kg⁻¹, which makes Gd₆₀Co₂₆Al₆Ge₈ bulk metallic glass matrix composite a promising candidate for magnetic refrigerant.     

Microstructural changes in Fe-doped Gd5Si2Ge2

Gd₅Si₂Ge₂-based alloys can exhibit a giant magnetocaloric effect (GMCE); this gives them the potential for use in cooling technologies. It has also been reported that a small addition of iron reduces the hysteresis losses in Gd₅Si₂Ge₂-based alloys, thus increasing the net refrigerating capacity. In this investigation, we have been the first to look at the effect on the microstructure and magnetic properties of Gd₅Si₂Ge₂ resulting from a wide range of substitutions of Si by Fe. The macrostructures of the arc-melted buttons revealed some very unusual surface morphologies, and the analytical results revealed a gradual substitution of the Gd₅(Si,Ge,Fe)₄-type phase by a Gd₅(Si,Ge,Fe)₃-type phase and the presence of three grain-boundary phases, two of which contain substantial amounts of iron. The magnetic measurements indicated that larger amounts of iron reduced the hysteresis losses, but at the same time reduced the Curie temperatures to below lower values that would make the material useful in practice.     

Dynamic magnetic susceptibility of compounds in Gd<Subscript>5</Subscript>Si<Subscript>2−x</Subscript>Ge<Subscript>2−x</Subscript>Sn<Subscript>2x</Subscript> (2x = 0 − 0.1) system

The dynamic magnetic susceptibility (χ_ac) of magnetically ordered Gd₅Si_2?xGe_2?xSn_2x compounds with the partial substitution for silicon and germanium atoms by isovalent tin atoms (2x = 0 ? 0.1) has been investigated experimentally. From the temperature dependence of χ_ac the Curie temperatures of these alloys are determined. It is established that tin-doped alloys have higher Curie temperatures as compared to Gd₅Si₂Ge₂ (ΔT _C ≈ 15 K).     

Unconventional magnetic and transport properties in Gd1−xLaxMn2Ge2 with two-dimensional arrangement of Mn atoms

In this paper, we present our recent experimental results of magnetic and transport properties of Gd_1−xLa_xMn₂Ge₂ intermetallic compounds with the ThCr₂Si₂-type layered structure. The results obtained indicate that, in GdMn₂Ge₂, a first-order transition from a collinear antiferromagnetic to a collinear ferrimagnetic state appears with decreasing temperature at T_t3, below the Néel temperature T_N. In Gd_1−xLa_xMn₂Ge₂ compounds with x=0.05 and 0.075, after ordering ferrimagnetically at T_t1, two kinds of first-order transitions from a canted ferrimagnetic to a non-collinear antiferromagnetic state and from a non-collinear antiferromagnetic to a reentrant canted ferrimagnetic state occur at T_t2 and T_t3. In Gd_0.925La_0.075Mn₂Ge₂, a field-induced metamagnetic transition from non-collinear antiferromagnetism to canted ferrimagnetism occurs at relatively low fields, accompanied by fractal like multi-step transitions, the so called “devil's stair-case”. Furthermore, a negative giant magnetoresistance (GMR) effect (Δρ/ρ15%) was observed at the field-induced metamagnetic transition. The mechanism of this negative GMR was clarified by comprehensive measurements of the resistivity on single crystals Gd_0.925La_0.075Mn₂Ge₂ and TbMn₂Ge₂. With further increasing x, only canted ferrimagnetism appears with a compensation temperature for 0.10<x<0.40, whereas no compensation behavior appears for x>0.50. The phase diagram obtained indicates that the overall magnetism is controlled by the Mn–Mn intralayer distance in the tetragonal c-plane, reflecting the two-dimensional arrangement of Mn atoms.     

Magnetic transition and large reversible magnetocaloric effect in EuCu1.75P2 compound

The magnetocaloric effect(MCE) in EuCu1.75P2 compound is studied by the magnetization and heat capacity measurements.Magnetization and modified Arrott plots indicate that the compound undergoes a second-order phase transition at TC ～ 51 K.A large reversible MCE is observed around TC.The values of maximum magnetic entropy change(-△SxMma) reach 5.6 J·kg-1·K-1 and 13.3 J·kg-1·K-1 for the field change of 2 T and 7 T,respectively,with no obvious hysteresis loss in the vicinity of Curie temperature.The corresponding maximum adiabatic temperature changes(△Tadmax) are evaluated to be 2.1 K and 5.0 K.The magnetic transition and the origin of large MCE in EuCu1.75P2 are also discussed.     

GREAT MAGNETIC ENTROPY CHANGE IN La(Fe, M)13 (M=Si, Al) WITH Co DOPING

Very large magnetic entropy change Δ S_M, which originates from a fully reversible second-order transition at Curie temperature T_C, has been discovered in compounds La(Fe, Si)₁₃, La(Fe, Al)₁₃ and those with Co doping. The maximum change ΔS_M\approx19 J·kg^-1·K^-1, achieved in LaFe_11.4Si_1.6 at 209K upon a 5T magnetic field change, exceeds that of Gd by more than a factor of 2. The T_C of the Co-doped compounds shifts to higher temperatures. ΔS_M still has a considerable large magnitude near room temperature. The phenomena of very large ΔS_M, convenience of adjustment of T_C, and also thesuperiority of low cost, strongly suggest that the compounds La(Fe, M)₁₃ (M=Si, Al) with Co doping are suitable candidates for magnetic refrigerants at high temperatures.     

Large magnetocaloric effect and magnetoresistance behavior in Gd4Co3

We report a large entropy change (ΔS) below 300 K, peaking near T _C = 220 K, due to isothermal change of magnetic field, for Gd₄Co₃, with a refrigeration capacity higher than that for, say, LaFe_11.4Si_1.6, ordering magnetically in the same temperature range. A noteworthy finding is that the isothermal magnetization is nonhysteretic — an important criterion for magnetic refrigeration without loss. ΔS behavior is also compared with that of magnetoresistance.     

Superparamagnetism and spin-glass like state for the MnFe2O4 nano-particles synthesized by the thermal decomposition method

MnFe₂O₄ nano-particles with an average size of about 7 nm were synthesized by the thermal decomposition method. Based on the magnetic hysteresis loops measured at different temperatures the temperature-dependent saturation magnetization (M_S) and coercivity (H_C) are determined. It is shown that above 20 K the temperature-dependence of the M_S and H_C indicates the magnetic behaviors in the single-domain nano-particles, while below 20 K, the change of the M_S and H_C indicates the freezing of the spin-glass like state on the surfaces. By measuring the magnetization–temperature (M–T) curves under the zero-field-cooling (ZFC) and field-cooling procedures at different applied fields, superparamagnetism behavior is also studied. Even though in the ZFC M–T curves peaks can be observed below 160 K, superparamagnetism does not appear until the temperature goes above 300 K, which is related with the strong inter-particle interaction.     

Reduction of hysteresis loss in LaFe11.7Si1.3Hx hydrides with significant magnetocaloric effects

Magnetic properties and magnetocaloric effects (MCEs) have been investigated in hydrogenated LaFe_11.7 Si_1.3H _x (x=0,1.37, and 2.07) compounds. It is found that the Curie temperature, T _C, can be tuned from 192 to 338 K by adjusting the hydrogen content from 0 to 2.07. It is attractive that both thermal and magnetic hysteresis are remarkably reduced because of the weakness of the itinerant-electron metamagnetic transition after hydrogenation. The maximal hysteresis loss at T _C decreases from 33.4 to 8.8 J/kg as x increases from 0 to 2.07. For the samples with x=0,1.37, and 2.07, the maximal values of the isothermal magnetic entropy change, ΔS _M, are 20.9, 15.1, and 15.83 J/kg K for the increasing field and 20.76 J/kg K, 14.53 J/kg K and 15.61 J/kg K for the decreasing field at T _C, with efficient refrigeration capacities of 439, 330, and 304 J/kg for a field change of 0–5 T, respectively. Large reversible MCE and small hysteresis with considerable refrigeration capacity indicate the potential of LaFe_11.7Si_1.3H _x hydride as a candidate magnetic refrigerant around room temperature.     

Magnetic phase transitions in Nd7Rh3 single crystal

Magnetic phase transitions in rare earth intermetallic compound Nd₇Rh₃ have been investigated using a single crystal. Measurement results of magnetization, magnetic susceptibility, specific heat, and electrical resistivity reveal that Nd₇Rh₃ has two magnetic phase transitions at T_N=34 K, T_t2=9.1 K and a change of the magnetic feature at T_t1=6.8 K in the absence of an external magnetic field. Antiferromagnetic orderings exist in all the three magnetic states; a large magnetic anisotropy between the c-axis and the c-plane is observed. In the magnetic phase below T_t2, an irreversible field-induced magnetic phase transition takes place in the c-plane; after removing external magnetic field, a coexistence state of ferro- and antiferromagnetic ordering or a ferrimagnetic state having a remanent magnetization M_R is stabilized. The M_R decays to a certain value for several hours after the first process; a magnetic field cooling effect was also observed in the c-plane below T_t2. In the antiferromagentic state above T_t2, the irreversibility disappears and an ordinary antiferromagnetic state takes place. As the origin of this phenomenon, a kind of martensitic structural transition that is observed in Gd₅Ge₄ can be considered.