Dy~(3+)和Tb~(3+)掺杂镓硼锗硅酸盐玻璃发光性能

采用高温熔融法分别制备了高含量Tb~(3+)单掺和Dy~(3+)/Tb~(3+)共掺的镓硼锗硅酸盐(GBSG)发光玻璃,并分析了其光谱性能。根据Dy~(3+)和Tb~(3+)掺杂的镓硼锗硅酸盐(GBSG)玻璃的激发和发射光谱、荧光寿命衰减曲线等特性,探讨了Dy~(3+)与Tb~(3+)之间的能量传递关系。结果表明:玻璃的发光强度和荧光寿命随着Tb~(3+)、Dy~(3+)含量的增加而减少。与相同摩尔浓度的单掺玻璃相比,共掺玻璃发光强度的衰减速率先减慢而后加快。Tb~(3+)、Dy~(3+)离子之间的能量传递方式为无辐射共振能量传递和~4F_(9/2)+~7F_6→~6H_(15/2)+~5D_4交叉弛豫效应。     

Na_2CaSiO_4:Sm~(3+),Eu~(3+)荧光粉的发光特性和能量传递

利用高温固相法合成Na_2CaSiO_4:Sm~(3+),Eu~(3+)系列荧光粉末,研究了Sm~(3+)和Eu~(3+)掺杂对Na_2CaSiO_4晶体结构的影响、材料发光特性以及存在的能量传递现象.X射线衍射结果表明Sm~(3+)和Eu~(3+)单掺及共掺样品均为单相的Na_2CaSiO_4结构,晶体结构没有改变.Na_2CaSiO_4:Sm~(3+)荧光样品在404 nm激发波长下呈现峰峰值为602 nm的橙红色荧光,来源于~4G_(5/2)→~6H_(7/2)跃迁.Na_2CaSiO_4:Eu~(3+)荧光样品在395 nm激发波长下发射出峰峰值为613 nm的红色荧光.对光谱和荧光寿命的测试和分析结果表明Sm~(3+)与Eu~(3+)之间存在能量传递,通过理论计算得到Sm~(3+)和Eu~(3+)之间的能量传递临界距离为1.36 nm,相互作用形式为电四极-电四极相互作用.随着Eu~(3+)掺杂浓度的增加,能量传递效率也逐渐提高至20.6%.     

Nb5+、Sm3+共掺杂YTaO4的长余辉发光性质

采用高温固相法合成了Nb~(5+)、Sm~(3+)共掺杂YTaO_4长余辉发光材料,通过X射线粉末衍射(XRD)、稳态荧光光谱、漫反射光谱和热释光曲线等多种表征手段研究了材料的结构、荧光和长余辉发光特性。XRD结果表明,共掺杂Nb~(5+)和Sm~(3+)没有引起YTaO_4晶体结构的改变。光谱分析表明,共掺Nb~(5+)不仅可大幅提高YTaO_4中Sm~(3+)的长余辉发光强度,而且可实现长余辉发光颜色的调控。对Sm~(3+)和Nb~(5+)共掺杂调控长余辉发光特性的机理也进行了分析。     

Dy~(3+),Sm~(3+)和Ce~(3+)离子在M_3La_2(BO_3)_4(M=Ca,Sr,Ba)中光谱性质的研究

本文报导了Dy~(3+),Sm~(3+)和Ce~(3+)离子在M_3La_2(BO_3)_4(M=Ca,Sr,Ba)基质中的激发与发射光谱;研究了Dy~(3+)离子黄蓝发射的相强度随基质化合物的组成和结构的不同而呈现的变化规律;讨论了Sm~(3+)离子电荷迁移激发带的能量与基质中近邻阳离子的关系并分析了Sm~(3+)和Eu~(3+)离子4f电子构型对电荷迁移带能量的影响。本文还给出了Dy~(3+),Sm~(3+)和Ce~(3+)离子发光的浓度淬灭值。     

单分散球形CaWO_4∶Re~(3+)(Sm~(3+),Eu~(3+))红色荧光粉的制备及其发光性能

目前使用的白光LEDs荧光粉,主要是适于蓝光GaN芯片激发的黄、绿、红色稀土荧光粉。黄、绿光荧光粉技术已经相对完善,而发光良好、性能稳定的红色荧光粉比较少。因此,需要开发新型的蓝光激发型红色荧光粉。相对于传统的高温固相法制备荧光粉体,本文利用水热法在较低温度160℃成功制备出了发光性能良好的单分散球形钨酸钙红色发光材料CaWO4∶Sm~(3+)和CaWO_4∶Eu~(3+)。通过X射线粉末衍射仪(XRD)、场发射扫描电镜(FE-SEM)、荧光光谱仪(PL)等表征手段,研究了所制备材料的晶体结构、表面形貌以及光学特性。讨论掺杂稀土离子浓度、反应时间等条件的改变对样品形貌以及发光性能的影响。结果显示,掺杂浓度不仅影响材料的形貌,还影响其发光强度。当Sm~(3+)和Eu~(3+)掺杂量分别为6%和4%时,CaWO_4∶Sm~(3+)和CaWO_4∶Eu~(3+)材料的发光性能最优。研究结果表明,Sm~(3+)和Eu~(3+)掺杂的CaWO_4材料可以作为荧光灯和蓝光芯片LED用荧光粉的备选材料。     

Dy~(3+)掺杂硼酸盐玻璃的制备、表征及发光特性

采用高温熔融-冷却法制备了一系列Dy~(3+)掺杂的B_2O_3-ZnO-Na_2O-Al_2O_3发光玻璃,通过红外光谱、紫外-可见-近红外光谱和荧光光谱等研究了其结构及发光特性。分析表明:制备的发光玻璃中出现基质组分的结构特征峰及Dy~(3+)的能级跃迁特征峰。在350 nm波长光激发下,样品的发光强度、黄蓝发射峰比、荧光寿命、色坐标及色温等均随Dy~(3+)浓度的变化发生明显的可调节变化。样品的荧光发射强度随Dy~(3+)浓度的增加呈现先增大后减小的变化,当Dy~(3+)掺杂摩尔分数为1.0%时,发光强度最大。此外,随着Dy~(3+)掺杂浓度的增大,发光玻璃的荧光寿命及发射光谱的色度坐标值、色温都呈现递减的趋势。这表明通过基质组分及掺杂元素的调节可以使得该硼酸盐体系发光玻璃获得高效可调节的光功能从而得到广泛应用。     

Er~(3+)和Eu~(3+)共注入GaN的光学特性和能量传递机制

采用离子注入法在GaN薄膜中实现了Er~(3+)和Eu~(3+)离子的共掺杂.以阴极荧光光谱仪为主要表征手段,研究样品的光学特性和能量传递机理.在300K温度下,Er~(3+)和Eu~(3+)共掺杂GaN薄膜能够实现绿光和红光的同时发射.随着Er~(3+)离子掺杂剂量的增加,Eu~(3+)离子相关发光峰的强度减弱,Er~(3+)离子对应的两个相关发光峰强度比值减小,表明Er~(3+)和Eu~(3+)离子之间发生了能量传递,能量传递的方向为Eu~(3+)→Er~(3+).变温阴极荧光光谱显示,Er~(3+)离子的2H11/2和4S3/2两个能态相关的跃迁峰相对强度比值随着温度升高而降低,主要是由两个能级之间的热耦合导致.改变Er~(3+)离子的掺杂剂量,能够调控GaN:Er~(3+)/Eu~(3+)样品的光学色度坐标和色温,表明此材料可用于发光器件.     

E u3+,D y3+共注入A lN薄膜结构和发光特性研究

采用离子注入方法在氢化物气相外延法生长的AlN薄膜中注入了不同剂量的Dy~(3+)和Eu~(3+),制备了Dy~(3+)单掺、Dy~(3+)和Eu~(3+)共掺的AlN样品.对于Dy~(3+)单掺杂AlN样品,X射线衍射和拉曼散射实验结果表明随着Dy注入剂量的增加,样品的压应力也增加,形成了比较明显的损伤层;但当注入剂量由5×1014at/cm~2增加至1×1015at/cm~2时,压应力增加不明显,接近于饱和.对于Dy~(3+)和Eu~(3+)共掺的AlN样品,阴极荧光实验表明,AlN中Eu~(3+)和Dy~(3+)之间可能存在能量传递,能量传递途径为在声子辅助下从Dy~(3+)的4F9/2→6H15/2至Eu~(3+)的7F0→5D2的共振能量传递.此外,计算发现改变Dy~(3+)和Eu~(3+)离子的注入剂量比能实现发光色度坐标和色温的有效调控.     

La2-x-yMgTiO6:xDy3+,yEu3+白色荧光粉的 荧光性能及能量传递

采用高温固相法合成了La_(2-x)MgTiO_6∶xDy~(3+)和La_(2-x-y)MgTiO_6∶xDy~(3+),yEu~(3+)系列荧光粉,通过X射线衍射对其相结构进行了表征,优化了荧光粉的组成,研究了Dy~(3+)和Eu~(3+)浓度对发光强度的影响,测试了荧光粉的荧光光谱和寿命,研究了Dy~(3+)和Eu~(3+)之间的能量传递机理和能量传递效率。结果表明:所有合成的掺杂荧光粉均为单相物质;La_(2-x)MgTiO_6∶xDy~(3+)最佳掺杂浓度为x=0.05;在350 nm近紫外光激发下,La_(2-x-y)MgTiO_6∶xDy~(3+),yEu~(3+)显示出Dy~(3+)的特征黄、蓝光发射和Eu~(3+)的特征红光发射;Dy~(3+)的荧光寿命呈双指数衰减,随着Eu~(3+)浓度的增大,Dy~(3+)的荧光寿命逐渐减小,证明了Dy~(3+)和Eu~(3+)离子之间存在着能量传递;能量传递效率随着Eu~(3+)掺杂浓度的增加而增加,La_(1.83)MgTiO_6∶0.05Dy~(3+),0.12Eu~(3+)荧光粉的能量传递效率为53.9%;改变调节Eu~(3+)的掺杂浓度可以得到从冷白色到暖白色的荧光粉,La_(1.83)MgTiO_6∶0.05Dy~(3+),0.12Eu~(3+)的色坐标为(0.337 3,0.354 4)。     

Tm~(3+)/Er~(3+)/Yb~(3+)掺杂的镓锗酸盐玻璃光谱性能及能量传递

采用熔融淬冷法制备得到透明的Tm~(3+)/Er~(3+)/Yb~(3+)掺杂镓锗钠玻璃。对比研究了808 nm和980 nm激发下Tm_2O_3含量对样品可见-红外光学光谱特性的影响。结合稀土离子能级结构,分析了Tm~(3+)、Er~(3+)和Yb~(3+)离子之间的能量传递机制。结果表明:在808 nm和980 nm的激发下,Tm~(3+)/Er~(3+)/Yb~(3+)掺杂样品中均观察到了473,655,521,544 nm的蓝、红和绿光。在808 nm激发下,随着Tm~(3+)浓度的增加,Tm~(3+):1 800 nm和Er~(3+):1 530 nm发射强度的比率I1.8/I1.53逐渐增大。由于在Tm~(3+)和Er~(3+)间的能量传递有效地改变了红光和绿光的发射强度,473,521,655 nm的发光强度呈现先升高再降低的趋势,在Tm_2O_3掺杂摩尔分数为0.3%时达到最大值。而在980 nm激发下,由于Yb~(3+)对Er~(3+)和Tm~(3+)的能量传递起主要作用,使得其上转换红光(655 nm)、绿光(521 nm和544 nm)和蓝光(473 nm)的发光强度高于808 nm激发下的上转换发光。     

Influence of Y3+, Bi3+ content on photoluminescence of YVO4:Dy3+ phosphor induced by ultraviolet excitation

YxVO4:0.01Dy3+ and Y0.99-xVO4:0.01Dy3+,xBi3+ phosphors were synthesized by chemical coprecipitation method.Their crystal structure,micromorphology and photoluminescence (PL) properties were investigated by X-ray diffraction (XRD),scan electron microscopy (SEM) and spectrofluorometer.YxVO4:0.01Dy3+ and Y0.99-xVO4:0.01Dy3+,xBi3+ phosphors have a broad excitation band from about 250 to 350 nm including a strongest peak at about 310 nm.Under its excitation,the emission spectra exhibits two sharp peaks,one of which centered at about 483 nm for 4 F9/2→6 H15/2 transition of Dy3+ and the other at about 574nm due to the 4F9/2→6H13/2 transition of Dy3+.For YxVO4:0.01Dy3+ (x=0.94,0.97,0.99,1.01,1.03)phosphor,with increasing value of x,the body color of phosphor changes from yellow to white and the strongest peak in the excitation spectra shifts a little to shorter wavelength.It is detrimental to luminous intensity when Y3+ content deviates stoichiometric ratio.For Y0.99-xVO4:0.01Dy3+,xBi3+ (x=0.01,0.05,0.1,0.15,0.2,0.25) phosphor,the samples have extraneous bismuth vanadium oxide phase except for the major tetragonal zircon structure when x≥0.20.With increasing value of x,the band edge in the excitation spectra shifts to longer wavelength,the excitation intensity and luminous intensity increase early and decrease late.When the value of x is 0.01,the intensities increase evidently.In addition,the influence of Y3+ or Bi3+ on the color temperature of emission and micromorphology of YVO4:Dy3+ is slight.     

Eu和Dy包覆纳米ZnO的发光特性的研究

通过共沉淀法制备了Eu和Dy包覆的纳米ZnO材料.X射线衍射被用来测量样品的结构和粒径.光致发光测量显示325 nm的紫外光能很好激发Eu3+的612 nnm的红光发射和Dy3+的484和575 nm发射,显示氧化锌基质与Eu3+和Dy3+之间实现了能量传递,并对能量传递的机制进行了讨论.在Eu和Dy共同包覆的样品中,通过能量传递可能在紫外激发下实现白光发射.     

Effects of Li~+ on photoluminescence of Sr_3SiO_5:Sm~(3+) red phosphor

The structure and photoluminescence (PL) properties of Sr3SiO5 : Sm3+ and Li+-doped Sr3SiO5 : Sm3+ red-emitting phosphors were investigated. Samples were prepared by the high-temperature solid-state method. PL spectra show that the concentration quenching occurs when the Sm3+ concentration is beyond 1.3 mol% in Sr3SiO5 : Sm3+ phosphor without doping Li+ ions. The concentration-quenching mechanism can be explained by the electric dipole-dipole interaction of Sm3+ ions. The incorporation of Li+ ions into Sr3SiO5 : Sm3+ phosphors, as a charge compensator, improves the PL properties. The lithium ions also suppress the concentration quenching in Sm3+ with concentration increased from 1.3 mol% to 1.7 mol%.     

燃烧法可控制备Eu~(3+)-Eu~(2+)共存Ca_(12)Al_(14)O_(32)F_2荧光粉及其荧光性能的研究

采用燃烧法合成Ca_(12-x)Al_(14)O_(32)F_2∶xEu荧光粉,对样品进行了X射线粉末衍射(XRD)、X射线光电子能谱(XPS)、扫描电镜(SEM)以及光致发光光谱等表征,探讨了燃烧温度、氟化铵、尿素、硼酸以及铕浓度等合成条件对荧光性能的影响。研究结果表明,利用燃烧法可以合成Eu~(3+)-Eu~(2+)共存、发光可调的荧光粉。通过改变合成条件,改变Eu~(2+)和Eu~(3+)的比例,荧光粉的发光颜色可表现为白光-橙红色-蓝白光-淡紫色-深蓝色-淡蓝色等变化。     

LiMBO3 : Dy3+材料的发光特性

采用固相法制备了LiM(M=Ca, Sr, Ba)BO₃ : Dy³⁺材料,并研究了材料的发光特性。LiM(M=Ca, Sr, Ba)BO₃ : Dy³⁺材料的发射光谱均呈多峰发射,对应于Ca,Sr,Ba,其主发射峰分别是Dy³⁺的⁴F_9/2→⁶H_15/2(484,486,486 nm),⁶H_13/2(577,578,578 nm)和⁶H_11/2(668,668,666 nm)跃迁。监测黄色发射峰时,所得激发光 谱峰值位置相同,主激发峰分别为331,368, 397,433,462,478 nm,对应Dy³⁺的⁶H_15/2→ ⁴D_7/2,⁶P_7/2,⁶M_21/2,⁴G_11/2,⁴I_15/2和⁶F_9/2跃迁。研究了敏化剂Ce³⁺及电荷补偿剂Li⁺、Na⁺和K⁺对LiM(M=Ca, Sr, Ba)BO₃ : Dy³⁺材料发光强度的影响。结果显示:加入敏化剂Ce³⁺提高了材料的发光强度,发光强度最大处对应的Ce³⁺浓度为3%;加入电荷补偿剂Li⁺、Na⁺和K⁺后,材料的发光强度也得到了明显提高,但发光强度最大处对应的Li⁺、Na⁺和K⁺浓度不同,依次为4%、4%和3%。     

掺Ce3+、Tb3+的M3Y2(BO3)4(M＝Ca,Sr)

采用固相反应的方法;经二次灼烧合成了掺Ce3+、Tb3+的Ca3Y2(BO3)4和Sr3Y2(BO3)4磷光体;分析了合成过程中铈的还原情况.用X-射线衍射分析确定了它们的结构均为正交晶系,空间群P21cn测定了Ce3+和Tb3+在两种基质中的光谱,得到Ce3+波长位移的某些规律,观察到Ce3+对Tb3+的敏化作用.     

Eu~(3+)掺杂的Na_2YMg_2(VO_4)_3荧光粉制备和发光特性

采用溶胶-凝胶法制备了Na2Y1-xMg2(VO4)3∶x Eu~(3+)(x=0.15~0.75)系列自激活荧光粉。用XRD、SEM、光致发光光谱和荧光衰减曲线分别对其结构、形貌和发光性能进行表征。XRD结果显示样品为纯石榴石结构,其中Eu~(3+)取代Y~(3+);SEM照片显示样品为粒径大小在0.3~1μm范围内不规则的光滑球状颗粒;光谱分析表明,Na2YMg2(VO4)3作为自激活发光基质可以被200~400 nm紫外光有效激发,发出源于VO_4~(3-)电荷迁移跃迁的波长范围为400~700 nm的宽谱带绿光。掺杂Eu~(3+)后,在340 nm紫外光激发下同时出现了VO_4~(3-)的电荷迁移带和Eu~(3+)的特征光谱。不同浓度Eu~(3+)掺杂的光谱和荧光衰减曲线表明,存在VO_4~(3-)和Eu~(3+)之间的能量传递。     

Bi3+掺杂对Sr2MgSi2O7∶Eu2+荧光粉的结构及发光性能的影响

采用溶胶-凝胶法在还原气氛下制备了Sr₂MgSi₂O₇∶Eu²⁺,xBi³⁺(x=0,0.02,0.04,0.06,0.08,0.1)荧光粉,并用XRD、TG-DTA及激发与发射谱仪对样品的结构及发光性能进行了表征。结果发现:单掺杂Bi³⁺的Sr₂MgSi₂O₇样品的发射光谱所用的材料的激发光谱为一主峰为286 nm的宽带谱,这是由于激发态时Bi³⁺的³P₁→¹S₀电子能级跃迁而造成的;单掺杂Eu²⁺的Sr₂MgSi₂O₇样品的发射光谱所用的材料的激发光谱为一主峰为358 nm的宽带谱,这是典型的Eu²⁺的4f⁶5d¹→4f⁷跃迁而引起的。当Bi³⁺离子掺杂到Sr₂MgSi₂O₇∶Eu²⁺样品的摩尔分数为0.04时,样品的发射强度是未掺杂Bi³⁺离子样品的1.9倍。     

Dy^3＋：ThO2的选择激发光谱和能级结构

本文首次用熔融法生长了Dy^3 :ThO2晶体,,详细研究了其光谱特性,通过12K下格位选择激发下的发射光谱测量,利用晶场理论,确定了Dy^3 在ThO2中的格位对称性为C3v。列表给出了Dy^3 :ThO2的晶场能级结构,测量和讨论了^4F9/2能级的寿命。