We propose a theory of thin film photovoltaics in which one of the polycrystalline films is made of a pyroelectric material grains such as CdS. That film is shown to generate strong polarization improving the device open circuit voltage. Implications and supporting facts for the major photovoltaic types based on CdTe and CuIn(Ga)Se2 absorber layers are discussed.
High‐speed solution shearing, in which a drop of dissolved material is spread by a coating knife onto the substrate, has emerged as a versatile, yet simple coating technique to prepare high‐mobility organic thin film transistors. Solution shearing and subsequent drying and crystallization of a thin film of conjugated molecules is probed in situ using microbeam grazing incidence wide‐angle X‐ray scattering (μGIWAXS). We demonstrate the advantages of this approach to study solution based crystal nucleation and growth, and identify casting parameter combinations to cast highly ordered and laterally aligned molecular thin films.
The crystallization process of mechanically alloyed Fe75Zr25 metallic glasses is investigated by means of both thermo‐magnetization and in situ neutron powder thermo‐diffraction experiments in the temperature range 300–1073 K. It was found that the crystallization takes place in a two‐step process, involving firstly the appearance of metastable Fe and Fe2Zr crystalline phases between 880 K and 980 K, and a subsequent polymorphic transformation into Fe3Zr above 980 K. These findings explain the anomalous magnetization vs. temperature behaviour on heating–cooling cycles.
The metastability of the bixbyite‐ and corundum‐type In2O3 polymorphs up to 33 GPa (at room temperature) is shown. While compressed (in diamond anvil cells) and laser‐heated, both polymorphs undergo a phase transition to the Rh2O3‐II‐type structure (space group Pbcn, No. 60). The direct transition from bixbyite to Rh2O3‐II structure has not yet been observed for any other oxide.
This Letter reports on the assembly on the tip of an optical fibre of a metamaterial film fabricated by a self‐assembly bottom‐up method, composed of silver nanowires embedded in an alumina matrix. By illuminating the film through the fibre in a reflection configuration, we observe experimentally the optical response of the metamaterial in agreement with theoretical predictions and interpreted as the excitation of surface plasmon‐polaritons in the cylindrical surface of the nanowires. These results pave the way for low‐cost optical fibre devices that incorporate metamaterial films.
We report a very simple and novel approach to produce anodic TiO2 nanotube arrays with highly defined and ordered tube openings. It is based on carrying out anodization through a slowly soluble photoresist coating. This eliminates the formation of undesired initiation layers on the tube tops and protects them to a certain extent from etching by the electrolyte.
Epitaxial TiC/SiC multilayers were grown by magnetron sputtering at a substrate temperature of 550 °C, where SiC is normally amorphous. The epitaxial TiC template induced growth of cubic SiC up to a thickness of ～2 nm. Thicker SiC layers result in a direct transition to growth of the metastable amorphous SiC followed by renucleation of nanocrystalline TiC layers.
Polymer nanocomposites containing different concentrations of Au nanoparticles have been investigated by small angle X‐ray scattering and electronic absorption spectroscopy. The variation in the surface plasmon resonance (SPR) band of Au nanoparticles with concentration is described by a scaling law. The variation in the plasmon band of ReO3 nanoparticles embedded in polymers also follows a similar scaling law.
Bulk polycrystalline La0.8Li0.2MnO3 is found to switch between a low‐resistance state and a high‐resistance state on thermal cycling. The low‐temperature, high‐resistance state exhibits strong electroresistance whereas the high‐temperature, low‐resistance state does not. The change in resistance between the two distinct states is of two orders of magnitude. It is proposed that the observed metastability may serve as the basis for resistive thermal‐switching devices.
Graphene, the two‐dimensional form of carbon presents outstanding electronic and transport properties. This gives hope for the development of applications in nanoelectronics. However, for industrial purpose, graphene has to be supported by a substrate. We focus here on the graphene‐on‐SiC system to discuss how the SiC substrate interacts with the graphene layer and to show the effect of the interface on graphene atomic and electronic structures.
Monte‐Carlo simulations predict that a local correlated disorder is responsible for many of the novel transport and magnetic properties of colossal magnetoresistance (CMR) materials such as manganites. One important prediction of these models is that the resistivity at the metal–insulator transition (MIT) in manganites depends strongly on the correlated quenched disorder. However, experimental confirmation has been challenging since it is difficult to control the amount of disorder in these compounds. We carried out experiments on Sm0.55Sr0.45MnO3, a prototypical CMR manganite with a sharp MIT, whereby the oxygen‐related disorder is systematically enhanced by low temperature thermal activation. We observe dramatic changes in the temperature dependence of resistivity at the MIT as the amount of quenched disorder is increased, occurring in a manner that is in agreement with theoretical predictions.
We report on wet etching of photomodified regions in crystalline sapphire using KOH solution. Tightly focused femtosecond laser pulses (150 fs at 800 nm wavelength) were used to create void structures enclosed in an amorphised sapphire shell inside the bulk of a crystalline host. The diameter of the amorphous regions can be controlled by pulse energy and was typically 0.5–1.5 µm. The etching rate depends on the distance between adjacent irradiation spots, pulse energy, concentration of etchant and ultrasonic agitation.
A high‐stability Eu complex has been achieved by coating with a silica glass via a low temperature sol–gel process using deuterated methanol. A three‐dimensional glass network protects the Eu complex from free oxygen and/or water to change the ligand structure. In addition, the chemical bond of the deuterated Eu complex is more stable than that of the conventional Eu complex. Therefore, we achieved a high‐thermal‐stability Eu complex encapsulated by a sol–gel derived silica glass using deuterated methanol instead of ethanol.
We have shown that nitrophenyl groups may be added to the surface of few‐layer epitaxial graphene (EG) by the formation of covalent carbon–carbon bonds thereby changing the electronic structure and transport properties of EG from near‐metallic to semiconducting. In the present Letter we discuss the opportunities afforded by such chemical processes to engineer device functionality in graphene by modification of the electronic properties without physical patterning.
A passive micro‐displacement sensor (for ～μm displacement) was fabricated based on a magnetoelectric laminate, in which the displacement change can result in a change of the magnetic flux around the magnetoelectric sensor. The displacement measurement was realized by measuring the magnetoelectric output voltage. The displacement detecting coefficient was ～2.5 mV/μm at a frequency of ～1 kHz. This passive displacement sensor possesses the advantages of low cost, high resolution, low energy consumption and good linearity and has potential for application in future displacement detectors.
Bi2Te3 doped p‐type Pb0.13Ge0.87Te samples were prepared by hot pressing. We report on very high power factor values of ～30 μW/cm K2 at 500 °C, as were determined from Seebeck coefficient and electrical resistivity measurements. From dilatometric characterization, the phase transition from the low temperature rhombohedral to the high temperature cubic NaCl structures, takes place at 373 °C. This transition is accompanied by a continuous and gradual change of the lattice parameters, as was observed by hot stage XRD, suggesting a good mechanical durability upon thermal cycling and operating in large thermal gradients.
A facile metal catalyst free route to synthesize boron doped (0.6%–1.0%) carbon nanotubes via ceramic nanowires in which the formation of the nanowires (probably serving as templates), the carbon nanotubes and their doping all occur unanimously in the reaction, is presented.
An original approach is proposed to study the magnetic phase separation phenomenon. It is based on the registration of the noise‐like FMR Fine Structure (FMR FS) caused by the magnetic interparticle dipole–dipole interaction between spatially separated ferromagnetic regions. Data obtained for a La0.7Pb0.3MnO3 single crystal point to the existence of spatially separated ferromagnetic regions. It is shown that FMR FS of the La0.7Pb0.3MnO3 single crystal is temperature reversible and disappears at the maximum of magnetoresistance.
Optically transparent and high‐quality hybrid ZnO nanoparticle and anthracene embedded polyphenylsiloxane (PPS) glass films were spin‐coated on quartz substrates. A strong Förster resonant energy transfer (FRET) process was indicated by the observation of quenching of the ZnO emission and an enhancement of the anthracene emission at room temperature. The efficiency of this energy transfer between ZnO and the S1 vibronic states of the anthracene molecules can be optimized to exceed 90%.