Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Characterization of the VUV excitation spectrum of BaZr(BO3)2:Eu

The excitation spectra of M (M=Si⁴⁺, Ti⁴⁺) and Eu³⁺ co-doped BaZr(BO₃)₂, BaZrO₃:Eu and La₂Zr₂O₇:Eu in the vacuum ultraviolet (VUV) regions of 110-300 nm are investigated and the host-lattice absorption are characterized. The result indicated that BaZr(BO₃)₂:Eu³⁺ phosphor has a strong absorption under the VUV excitation, and in the host-lattice excitation, the strong band at 130-160 nm could be due to the BO₃ atomic groups; the band at 160-180 nm is related to the excitation of Ba-O; 180-200 nm corresponds to the charge transfer (CT) transition of Zr-O. The band at 200-235 nm due to the CT band of Eu³⁺-O²⁻ and a bond valence study explained the observed weak CT band of Eu³⁺-O²⁻ in the excitation spectra of BaZr(BO₃)₂:Eu³⁺. The emission results show that Si⁴⁺ can sensitize luminescence in the host of BaZr(BO₃)₂:Eu but Ti⁴⁺ has no improvement effect on luminescence.     

KBaPO4:Ln (Ln=Eu, Tb, Sm) phosphors for UV excitable white light-emitting diodes

This letter reports the novel three emission bands based on phosphate host matrix, KBaPO₄ doped with Eu²⁺, Tb³⁺, and Sm³⁺ for white light-emitting diodes (LEDs). The phosphors were synthesized by solid-state reaction and thermal stability was elucidated by measuring photoluminescence at higher temperatures. Eu²⁺-doped KBaPO₄ phosphor emits blue luminescence with a peak wavelength at 420 nm under maximum near-ultraviolet excitation of 360 nm. Tb³⁺-doped KBaPO₄ phosphor emits green luminescence with a peak wavelength at 540 nm under maximum near-ultraviolet excitation of 370 nm. Sm³⁺-doped KBaPO₄ phosphor emits orange-red luminescence with a peak wavelength at 594 nm under maximum near-ultraviolet excitation of 400 nm. The thermal stabilities of KBaPO₄:Ln (Ln=Eu²⁺, Tb³⁺, Sm³⁺), in comparison to commercially available YAG:Ce³⁺ phosphor were found to be higher in a wide temperature range of 25-300 °C.     

Synthesis and luminescence properties of Eu, Ce and Tb-activated Sr3La2(BO3)4 under UV excitation

The spectroscopic properties in UV-excitable range for the phosphors of Sr₃La₂(BO₃)₄:RE³⁺ (RE³⁺=Eu³⁺, Ce³⁺, Tb³⁺) were investigated. The phosphors were synthesized by conventional solid-state reactions. The photoluminescence (PL) spectra and commission international de I'Eclairage (CIE) coordinates of Sr₃La₂(BO₃)₄:RE³⁺ were investigated. The f-d transitions of Eu³⁺, Ce³⁺ and Tb³⁺ in the host lattices are assumed and corroborated. The PL and PL excitation (PLE) spectra indicate that the main emission wavelength of Sr₃La₂(BO₃)₄:Eu³⁺ is 611 nm, and Sr₃La₂(BO₃)₄:Ce³⁺ shows dominating emission peak at 425 nm, while Sr₃La₂(BO₃)₄:Tb³⁺ displays green emission at 487, 542, 582 and 620 nm. These phosphors were prepared by simple solid-state reaction at 1000 °C. There are lower reactive temperature and more convenient than commercial phosphors. The Sr₃La₂(BO₃)₄:Tb³⁺ applied to cold cathode fluorescent lamp was found to emit green light and have a major peak wavelength at around 542 nm. These phosphors may provide a new kind of luminescent materials under ultraviolet excitation.     

Synthesis and luminescence properties of europium doped YBa3B9O18

Europium (Eu³⁺) doped YBa₃B₉O₁₈ were synthesized by conventional solid state solidification methods. (Y_1−xEu_x)Ba₃B₉O₁₈ formed solid solutions in the range of x=0–1.0. The luminescence property measurements upon excitation in ultraviolet–visible range show well-known Eu³⁺ excitation and emission. The charge transfer excitation band of Eu³⁺ dominates the excitation spectra. The emission spectrum of Eu³⁺ ions consists mainly of several groups of lines in the 550–720 nm region, due to the transitions from the ⁵D₀ level to the levels ⁷F_J (J=0, 1, 2, 3, 4) of Eu³⁺ ions. The dependence of luminescence intensity on Eu³⁺ concentration shows no concentration quenching for fully concentrated EuBa₃B₉O₁₈. Eu³⁺ doped YBa₃B₉O₁₈ are promising phosphors for applications in displays and optical devices.     

Photoluminescence of Eu-doped CaMgSi2xO6+2x (1.00?x?1.20) phosphors in UV-VUV region

Alkaline-earth silicate phosphors CaMgSi_2xO_6+2x:Eu²⁺ (1.00?x?1.20) were prepared by traditional solid-state reaction. The phosphors showed an intense blue emission centered around 453 nm, with both 254 and 147 nm excitations. The host absorption below 200 nm in the excitation spectra consisted of two bands around 160 and 190 nm. The band around 160 nm was ascertained to be associated with the SiO₄-tetrahedra and MgO₆-polyhedra, and that around 190 nm was due to the CaO₈-polyhedra or some impurities. The incorporation of excess Si of less than 15% would not lead to formation of impurities and the results indicated that an appropriate Si excess could improve the Photoluminescence (PL) intensity in both ultraviolet (UV) and vacuum ultraviolet (VUV) regions     

Novel green-emitting Na2CaPO4F:Eu phosphors for near-ultraviolet white light-emitting diodes

In this study, green-emitting Na₂CaPO₄F:Eu²⁺ phosphors were synthesized by solid-state reactions. The excitation spectra of the phosphors showed a broad hump between 250 and 450 nm; the spectra match well with the near-ultraviolet (NUV) emission spectra of light-emitting diodes (LEDs). The emission spectrum showed an intense broad emission band centered at 506 nm. White LEDs were fabricated by integrating a 390 nm NUV chip comprising blue-emitting BaMgAl₁₀O₁₇:Eu²⁺, green-emitting Na₂CaPO₄F:0.02 Eu²⁺, and red-emitting CaAlSiN₃:Eu²⁺ phosphors into a single package; the white LEDs exhibited white light with a correlated color temperature of 5540 K, a color-rendering index of 90.75, and color coordinates (0.332, 0.365) close to those of ideal white light.     

Luminescent properties of (Y,Gd)BO3:Bi,RE (RE=Eu, Tb) phosphor under VUV/UV excitation

Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors were prepared and their luminescent properties under vacuum ultraviolet (VUV)/UV excitation were investigated. Strong red emission for (Y,Gd)BO₃:Bi³⁺,Eu³⁺ and strong green emission for (Y,Gd)BO₃:Bi³⁺,Tb³⁺ are observed under VUV excitation from 147 to 200 nm with a much broader excitation region than that of single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃ phosphor. Strong emissions are also observed under UV excitation around 265 nm where as nearly no luminescence is observed for single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃. The luminescence enhancement of Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors is due to energy transfer from Bi³⁺ ion to Eu³⁺ or Tb³⁺ ion not only in the VUV region but also in the UV region. Besides, host sensitization competition between Bi³⁺ and Eu³⁺ or Tb³⁺ is also observed. The investigated phosphors may be preferable for devices with a VUV light 147-200 nm as an excitation source such as PDP or mercury-free fluorescent lamp.     

Excitation energy dependent chromaticity of BaZr(BO3)2:Eu

The luminescence properties of BaZr(BO₃)₂:5% Eu were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) excitation and different luminescence behaviors were observed by different excitation energies. After the analyses of the luminescence spectra, the result indicates that Eu³⁺ occupying non-centrosymmetric sites Ba²⁺ can be excited preferentially under 254 nm excitation, while Eu³⁺ occupying centrosymmetric sites Zr⁴⁺ can be excited preferentially under 147 nm excitation.     

Synthesis of Y2Si2O7:Eu nanocrystal and its optical properties

Nanocrystalline Y₂Si₂O₇:Eu phosphor with an average size about 60 nm is easily prepared using silica aerogel as raw material under ultrasonic irradiation and annealing temperature at 300-600 °C and this nanocrystalline decomposes into Y₂O₃:Eu and silica by heat treatment at 700-900 °C. The excitation broad band centered at 283 and 254 nm results from Eu³⁺ substituting for Y³⁺ in Y₂Si₂O₇ and Y₂O₃/SiO₂, respectively. Compared with Y₂O₃:Eu/SiO₂ crystalline, the PL excitation and emission peaks of Y₂Si₂O₇:Eu nanocrystalline red-shift and lead to the enhance of its luminescence intensity due to the different chemical surroundings of Eu³⁺ in above nanocrystallines. The decrease of PL intensity may be ascribed to quenching effect resulting from more defects in Y₂O₃:Eu/SiO₂ crystalline.     

Intense blue-emitting Ca5Al8O14: Eu phosphor for mercury free lamp

The calcium aluminates doped with Eu ions, Ca₅Al₈O₁₄: Eu, phosphors are prepared by the combustion method. The formation of crystalline aluminates was confirmed by X-ray diffraction pattern. The prepared phosphors were characterized by SEM, TGA, DTA, particle size analyzer and Photoluminescence (PL) techniques. From the UV-excited luminescence spectra it was found that the Eu ions acts as a luminescent centre with luminescence at the blue (λ _max = 470 nm) region due to 4f ⁶5d ¹ → 4f ⁷ transition. The excitation spectra show the broad band at 355 nm wavelength (λ _em = 470 nm). The excitation 355 nm is a mercury free excitation and therefore Ca₅Al₈O₁₄: Eu may be useful for the solid state lighting phosphor in lamp industry.      

Photophysical properties of highly efficient red-emitting CaTiO3:Eu phosphors under near ultra-violet excitation

The photophysical properties of europium-doped calcium titanate for near ultra-violet excitation were studied in order to investigate whether it is applicable to white light-emitting diodes. CaTiO₃:Eu³⁺ phosphors were synthesized by using the solid-state reaction method. The structures and basic properties of the phosphors were characterized by using X-ray diffractometer, scanning electron microscope, UV-visible spectrophotometer, and X-ray photoelectron spectrometer. The photophysical properties were examined by taking excitation and emission spectra. A strong red luminescence corresponding to ⁵D₀ → ⁷F₂ transition of Eu³⁺ under near ultra-violet excitation was observed. It was found that CaTiO₃:Eu³⁺ was a red-emitting phosphor and had higher efficiency for operation under near ultra-violet excitation.     

Dy含量对红色长余辉发光材料Sr3Al2Ｏ6:Eu2＋,Dy3＋性能的影响

采用溶胶凝胶法制备了Sr₃Al₂Ｏ₆:Eu^2＋,Dy^3＋红色长余辉发光材料,利用X射线衍射仪对材料的物相进行了分析,结果表明,1200℃下制备的样品的物相为Sr₃Al₂Ｏ₆,少量的Eu和Dy掺杂没有影响样品的相组成.采用荧光分光光度计、照度计测定了样品的发光特性.结果表明Sr₃Al₂Ｏ关键词： 红色长余辉 3Al₂Ｏ₆')" href="#">Sr₃Al₂Ｏ₆ 溶胶凝胶法     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Highly luminescent red light phosphor CaTiO3:Eu under near-ultraviolet excitation

The Eu-doped CaTiO₃ particles with a good crystallinity were prepared via sol-gel method. The phosphors showed a strong red emission corresponding to ⁵D₀→⁷F₂ (618 nm) of Eu³⁺ under the near-ultraviolet excitation (400 nm). X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), photoluminescent (PL) analysis and Brunauer-Emmett-Teller (BET) specific surface area measurement were utilized to characterize the CaTiO₃:Eu³⁺ particles. The concentration quenching and thermal quenching of the samples were discussed as well. The optimal concentration and the calcination temperature were 16 mol% of Eu³⁺ and 1400 °C for these phosphors, and the possible reason was discussed as well. CaTiO₃:Eu³⁺ is a promising red phosphor under near-ultraviolet excitation for various applications.     

Photoluminescence spectra of thenardite Na2SO4 activated with rare-earth ions, Ce, Sm, Tb, Dy and Tm

Five Na₂SO₄:RE³⁺ phosphors activated with rare-earth (RE) ions (RE³⁺=Ce³⁺, Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) were synthesized by heating natural thenardite Na₂SO₄ from Ai-Ding Salt Lake, Xinjiang, China with small amounts of rare-earth fluorides, CeF₃, SmF₃, TbF₃, DyF₃ and TmF₃, at 920 °C in air. The photoluminescence (PL) and optical excitation spectra of the obtained phosphors were measured at 300 and 10 K. In the PL spectrum of Na₂SO₄:Ce³⁺ at 300 K, two overlapping bands with peaks at 335 and 356 nm due to Ce³⁺ were first observed. Narrow bands observed in PL and excitation spectra of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors were well identified with the electronic transitions within the 4fⁿ (n=5, 8, 9 and 12) configurations of RE³⁺. The existence of excitation bands with high luminescence efficiency at wavelengths shorter than 230 nm is characteristic of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors. The obtained results suggest that these phosphors are unfavorable as the phosphor for usual fluorescence tubes, i.e., mercury discharge tubes, but may be favorable as the phosphor for UV-LED fluorescent tubes and as cathodoluminescence, X-ray luminescence and thermoluminescence phosphors.     

Photoluminescence properties of Sr(Y, Gd)2O4:Euunder VUV excitation

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) properties of Sr(Y, Gd)₂O₄ doped with Eu³⁺ were studied. The excitation spectra of SrY_1.9Eu_0.1O₄ and SrY_1.0Gd_0.9Eu_0.1O₄ had absorption in the VUV region with the absorption band edge at 149 nm, while the absorption of SrGd_1.9Eu_0.1O₄ in the VUV region was weak, which could be due to the narrow host band gap and no efficient energy transfer occurred in the VUV region. The PL spectra of all samples exhibited the characteristic emission of Eu³⁺ with the red ⁵D₀-⁷F₂ transition (611 nm) being the most prominent group.     

Preparation and photoluminescence properties of the Sr1.56Ba0.4SiO4:0.04Eu2+ phosphor

The Sr_1.56Ba_0.4SiO₄:0.04Eu²⁺ phosphors were prepared via a combustion reaction and following the calcination method at low temperature. The influences of the amount of the uncommonly used SrCl₂ flux, different calcination temperatures and time on the structure and the photoluminescence (PL) properties of the phosphors were investigated. Under the excitation of 450 nm blue light, the phosphor shows the intense broad emission band from 490 nm to 650 nm, and the emission peak is centered at 553 nm. The luminescence intensity of Sr_1.56Ba_0.4SiO₄:0.04Eu²⁺ was very sensitive to the crystallinity and morphology characteristics of the phosphor. The phosphor calcined at 950 °C for 3 h in 20%H₂/80%Ar atmosphere exhibits improved PL properties due to its high crystallinity and excellent morphology characteristics. The use of the SrCl₂ flux provides a novel way to improve the crystallinity of the silicates phosphors at low preparation temperature.     

Luminescent properties of a new green emitting Eu doped CaZrSi2O7 phosphor for WLED applications

CaZrSi₂O₇ (CZS), a modification of the thortveitite family, was prepared as a polycrystalline powder material by the conventional solid-state reaction method. Structural, thermal and photoluminescence (PL) properties of the prepared material were investigated in order to evaluate its potentiality. XRD patterns confirm the monoclinic phase of CaZrSi₂O₇: Eu²⁺ phosphors.. Emissions arising from transitions between the 5d and 4f orbital gaps of Eu²⁺ are manifested in the broadband excitation and emission spectra with major peaks at 363 and 512 nm, respectively. The excitation wavelength matches well with that of the emission of the ultraviolet-light emitting diode (UV-LED). Concentration quenching occurs when the Eu²⁺ concentration is beyond 0.05 and the dipole-dipole interaction was the reason for the corresponding quenching mechanism. The temperature dependence of emission intensity of CZS: Eu²⁺ phosphor was investigated and it showed better thermal stability than the standard YAG: Ce³⁺ phosphor.     

Luminescent properties of YVO4:Eu/SiO2 core–shell composite particles

We report an efficient process for preparing monodisperse SiO₂@Y_0.95Eu_0.05VO₄ core–shell phosphors using a simple citrate sol–gel method and without the use of surface-coupling silane agents or large stabilizers. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), and photoluminescence (PL) spectra were used to characterize the resulting SiO₂@Y_0.95Eu_0.05VO₄ core–shell phosphors. The XRD results demonstrate that the Y_0.95Eu_0.05VO₄ particles crystallization on the surface of SiO₂ annealing at 800 °C is perfectly and the crystallinity increases with raising the annealing temperature. The obtained core–shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 500 nm and an average thickness of ~50 nm), are not agglomerated, and have a smooth surface. The thickness of the YVO₄:Eu³⁺ shells on the SiO₂ cores could be easily tailored by changing the mass ratio of shell to core (W = [YVO₄]/[SiO₂]) (~50 nm for W = 30%). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀ − ⁷F₂ red emission at 618 nm) under the excitation of 320 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the values of W.