Acetate reduction synthesis of Sr2Si5N8:Eu phosphor and its luminescence properties

A novel synthesis method was developed for the efficient red phosphor, Eu²⁺-activated Sr₂Si₅N₈, by employing the strontium acetate as both the reducing agent and strontium source. The phase purity of final product was strongly dependent on the heating rate of the precursors. Sr₂Si₅N₈:Eu²⁺ (2 at%) phosphor presented a broadband excitation spectrum in the range 300–500 nm, matching well with the blue emission (400/460 nm) of current InGaN light-emitting diodes (LEDs). The red emission peaking at 619 nm gave the relatively high (about 155%) intensity compared with the Y₃Al₅O₁₂ (YAG) (P46-Y3) standard phosphor. In addition, the saturated chromatic coordinates (0.638, 0.359) allowed it a promising candidate as a red phosphor in white LEDs application for illumination or display.     

Luminescent properties of Eu-activated Sr3B2SiO8: A red-emitting phosphor for white light-emitting diodes

Single-phased Sr₃B₂SiO₈:Eu³⁺ phosphor was prepared by a solid-state method at 1020 °C. The luminescence spectra showed that Sr₃B₂SiO₈:Eu³⁺ phosphor can be effectively excited by near ultraviolet light (393 nm) and blue light (464 nm). When excited at 393 or 464 nm Sr₃B₂SiO₈:Eu³⁺ exhibited the main emission peaks at 611 and 620 nm, which resulted from the supersensitive ⁵D₀→⁷F₂ transition of Eu³⁺. The luminescence intensity of Sr₃B₂SiO₈:Eu³⁺ at 611 and 620 nm reached the maximum when the doping content of Eu³⁺ was 4.5 mol%. Its chromaticity coordinates (0.646, 0.354) were very close to the NTSC standard values (0.67, 0.33). Thus, Sr₃B₂SiO₈:Eu³⁺ is considered to be an efficient red-emitting phosphor for long-UV InGaN-based light-emitting diodes.     

Dy含量对红色长余辉发光材料Sr3Al2Ｏ6:Eu2＋,Dy3＋性能的影响

采用溶胶凝胶法制备了Sr₃Al₂Ｏ₆:Eu^2＋,Dy^3＋红色长余辉发光材料,利用X射线衍射仪对材料的物相进行了分析,结果表明,1200℃下制备的样品的物相为Sr₃Al₂Ｏ₆,少量的Eu和Dy掺杂没有影响样品的相组成.采用荧光分光光度计、照度计测定了样品的发光特性.结果表明Sr₃Al₂Ｏ关键词： 红色长余辉 3Al₂Ｏ₆')" href="#">Sr₃Al₂Ｏ₆ 溶胶凝胶法     

Effects of dopant concentrations on phosphorescence properties of Eu/Dy-doped Sr3MgSi2O8

Long afterglow Sr₃MgSi₂O₈: Eu, Dy phosphor with high brightness was prepared by sintering at high temperature and weak reductive atmosphere. The luminescent properties of this photoluminescent pigment were studied systematically by investigating concentration effects. The analytical results indicated that the main emission peaks appear at 482 nm. The excitation and emission spectra of this phosphor show that both of them are broadband. This is ascribed to the 4f⁷→4f⁶5d¹ transition of Eu²⁺ in the pigment matrix, which is in good agreement with the calculated value of 470 nm, and implies that luminescent centers Eu²⁺ occupy the deca-coordinated Sr²⁺ sites with the host of Sr₃MgSi₂O₈.     

Luminescence characteristics of Eu2+ activated Ca2SiO4 Sr2SiO4 and Ba2SiO4 phosphorsfor white LEDs

<正>This paper investigates the luminescence characteristics of Eu²⁺ activated Ca₂SiO₄,Sr₂SiO₄ and Ba₂SiO₄ phosphors. Two emission bands are assigned to the f-d transitions of Eu²⁺ ions doped into two different cation sites in host lattices,and show different emission colour variation caused by substituting M²⁺ cations for smaller cations.This behaviour is discussed in terms of two competing factors of the crystal field strength and covalence.These phosphors with maximum excitation of around 370 nm can be applied as a colour-tunable phosphor for light-emitting diodes（LEDs） based on ultraviolet chip/phosphor technology.     

Luminescent properties of green- or red-emitting Eu-doped Sr3Al2O6 for LED

Eu²⁺-doped Sr₃Al₂O₆ (Sr_3−xEu_xAl₂O₆) was synthesized by a solid-state reaction under either H₂ and N₂ atmosphere or CO atmosphere. When H₂ was used as the reducing agent, the phosphor exhibited green emission under near UV excitation, while CO was used as the reducing agent, the phosphor mainly showed red emission under blue light excitation. Both emissions belong to the d-f transition of Eu²⁺ ion. The relationship between the emission wavelengths and the occupation of Eu²⁺ at different crystallographic sites was studied. The preferential substitution of Eu²⁺ into different Sr²⁺ cites at different reaction periods and the substitution rates under different atmospheres were discussed. Finally, green-emitting and red-emitting LEDs were fabricated by coating the phosphor onto near UV- or blue-emitting InGaN chips.     

Novel green-emitting Na2CaPO4F:Eu phosphors for near-ultraviolet white light-emitting diodes

In this study, green-emitting Na₂CaPO₄F:Eu²⁺ phosphors were synthesized by solid-state reactions. The excitation spectra of the phosphors showed a broad hump between 250 and 450 nm; the spectra match well with the near-ultraviolet (NUV) emission spectra of light-emitting diodes (LEDs). The emission spectrum showed an intense broad emission band centered at 506 nm. White LEDs were fabricated by integrating a 390 nm NUV chip comprising blue-emitting BaMgAl₁₀O₁₇:Eu²⁺, green-emitting Na₂CaPO₄F:0.02 Eu²⁺, and red-emitting CaAlSiN₃:Eu²⁺ phosphors into a single package; the white LEDs exhibited white light with a correlated color temperature of 5540 K, a color-rendering index of 90.75, and color coordinates (0.332, 0.365) close to those of ideal white light.     

A white light emitting phosphor Sr1.5Ca0.5SiO4:Eu, Tb, Eu for LED-based near-UV chip: Preparation, characterization and luminescent mechanism

In this work, we report preparation, characterization and luminescent mechanism of a phosphor Sr_1.5Ca_0.5SiO₄:Eu³⁺,Tb³⁺,Eu²⁺ (SCS:ETE) for white-light emitting diode (W-LED)-based near-UV chip. Co-doped rare earth cations Eu³⁺, Tb³⁺ and Eu²⁺ as aggregated luminescent centers within the orthosilicate host in a controlled manner resulted in the white-light phosphors with tunable emission properties. Under the excitation of near-UV light (394 nm), the emission spectra of these phosphors exhibited three emission bands: one broad band in the blue area, a second band with sharp lines peaked in green (about 548 nm) and the third band in the orange-red region (588-720 nm). These bands originated from Eu²⁺ 5d→4f, Tb³⁺⁵D₄→⁷F_J and Eu³⁺⁵D₀→⁷F_J transitions, respectively, with comparable intensities, which in return resulted in white light emission. With anincrease of Tb³⁺ content, both broad Eu²⁺ emission and sharp Eu³⁺ emission increase. The former may be understood by the reduction mechanism due to the charge transfer process from Eu³⁺ to Tb³⁺, whereas the latter is attributed to the energy transfer process from Eu²⁺ to Tb³⁺. Tunable white-light emission resulted from the system of SCS:ETE as a result of the competition between these two processes when the Tb³⁺ concentration varies. It was found that the nominal composition Sr_1.5Ca_0.5SiO₄:1.0%Eu³⁺, 0.07%Tb³⁺ is the optimal composition for single-phased white-light phosphor. The CIE chromaticity calculation demonstrated its potential as white LED-based near-UV chip.     

白光LED用LiBaBO3:Eu2+材料发光特性研究

采用高温固相法制备了LiBaBO₃:Eu²⁺绿色发光材料.测量了Eu²⁺浓度为1mol%时样品的激发与发射光谱,其发射光谱为双峰宽谱,主峰分别为482和507nm,与理论计算值符合很好;监测482nm发射峰时,对应激发光谱的峰值为287和365nm,监测507nm发射峰时,对应的激发峰为365和405nm.研究了Eu²⁺浓度对材料发射光谱的影响,结果显示,随Eu²⁺浓度的增大,蓝、绿发射峰均发生了     

Luminescence characteristics of Eu3+ activated borate phosphor for white light emitting diode

In this paper, the Sr₃Y₂ (BO₃)₄:Eu³⁺ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613nm corresponding to the electric dipole ⁵D₀--⁷F₂ transition of Eu³⁺ under 365nm excitation, this is because Eu³⁺ substituted for Y³⁺ occupied the non-centrosymmetric position in the crystal structure of Sr₃Y₂ (BO₃)₄. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet (254nm, 365nm and 400nm) and blue (470nm) light. The effect of Eu³⁺ concentration on the red emission of Sr₃Y₂ (BO₃)₄:Eu³⁺ was measured, the result shows that the emission intensities increase with increasing Eu³⁺ concentration, then decrease. The Commission Internationale del'Eclairage chromaticity (x, y) of Sr₃Y₂(BO₃)₄:Eu³⁺ phosphor is (0.640,0.355) at 15 mol% Eu³⁺.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

An efficient blue-emitting phosphor LiCaPO4:Eu2+ for white LEDs

A new blue-emitting phosphor LiCaPO₄: Eu²⁺ was synthesized by solid state reaction at a relatively low temperature of 900 °C. It gives a single intense emission band centering at 470 nm, which corresponds to the 4f⁶5d¹→4f⁷ transition of Eu²⁺. The dependence of luminescence intensities on Eu²⁺ concentration was investigated. The phosphor, with a single excitation band extending from 250 to 400 nm, could be efficiently excited by near-ultraviolet light-emitting diodes and is believed to be a promising blue-emitting phosphor for white light-emitting diodes.     

Eu-activated Ba2Mg(BO3)2 yellow-emitting phosphors for near ultraviolet-based light-emitting diodes

A series of Eu²⁺-activated Ba₂Mg(BO₃)₂ yellow phosphors were prepared by a high temperature solid-state reaction. The phosphor emits intense yellow light under near ultraviolet excitation. Large Stokes shift can be attributed to the asymmetric nature of the Eu site and the lack of rigidity in the host. The concentration self-quenching mechanism of Ba₂Mg(BO₃)₂:Eu²⁺ is d-d interaction and the critical transfer distance is calculated to be about 12.29 Å. Prototype light-emitting diodes were fabricated by coating the Ba₂Mg(BO₃)₂:0.07Eu²⁺ phosphor onto ∼370 nm-emitting InGaN chips. The LEDs exhibit intense yellow-emitting under a forward bias of 20 mA. The results indicate that Eu²⁺-activated Ba₂Mg(BO₃)₂ is a candidate as a yellow component for fabrication of near-UV white light-emitting diodes.     

Energy transfer between activators at different crystallographic sites in Sr3SiO5:Eu

A yellow phosphor, Sr₃SiO₅:Eu²⁺, was synthesized by a high temperature solid-state method. Sr₃SiO₅:Eu²⁺ exhibits a single yellow emission under the blue radiation excitation. However, Sr₃SiO₅:Eu²⁺ shows a two-peak emission under the ultraviolet radiation excitation when Eu²⁺ doping content is less than 0.01 mol. Moreover, the blue emission disappears and the yellow emission reaches the peak value when Eu²⁺ doping content is 0.01 mol. Namely, the energy transfer takes place between the Eu²⁺ activators, which is located at two different crystallographic sites in the Sr₃SiO₅. And the energy transfer mechanism is the dipole-dipole interaction.     

The concentration quenching and crystallographic sites of Eu2+ in Ca2BO3Cl

A yellow phosphor, Ca2BO3CI：Eu2＋, is prepared by the high-temperature solid-state method. Under the condition of excitation sources ranging from ultraviolet to visible light, efficient yellow emission can be observed. The emission spectrum shows an asymmetrical single intensive band centred at 573 nm, which corresponds to the 4f65dl→4f7 transition of Eu2＋. Eu2＋ ions occupy two types of Ca2＋ sites in the Ca2BO3C1 lattice and form two corresponding emission centres, respectively, which lead to the asymmetrical emission of Eu2＋ in Ca2BO3C1. The emission intensity of Eu2＋ in Ca2BO3C1 is influenced by the Eu2＋ doping concentration. Concentration quenching is discovered, and its mechanism is verified to be a dipole-dipole interaction. The value of the critical transfer distance is calculated to be 2.166 nm, which is in good agreement with the 2.120 nm value derived from the experimental data.     

Synthesis and characterization of Sr3Al2O6：Eu2＋, Dy3＋ phosphors prepared by sol-gel-combustion processing

A type of red luminescent Sr3Al2O6:Eu2+, Dy3+ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3- by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3Al2O6:Eu2+, Dy3+. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250 C. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of (Sr0.94Eu0.03Dy0.03)3Al2O6 phosphors sintered at 1250 ℃ lasts for over 1000 s when the excited source is cut off.     

Preparation and luminescent properties of BaCa2Si3O9:Eu

A blue emitting phosphor of the triclinic BaCa₂Si₃O₉:Eu²⁺ was prepared by the combustion-assisted synthesis method and an efficient blue emission ranging from the ultraviolet to visible was observed. The luminescence and crystallinity were investigated using luminescence spectrometry and X-ray diffractometry (XRD), respectively. The emission spectrum shows a single intensive band centered at 445 nm, which corresponds to the 4f⁶5d¹→4f⁷ transition of Eu²⁺. The excitation spectrum is a broad extending from 260 to 450 nm, which matches the emission of ultraviolet light-emitting diodes (UV-LEDs). The critical quenching concentration of Eu²⁺ in BaCa₂Si₃O₉:Eu²⁺ phosphor is about 0.05 mol. The corresponding concentration quenching mechanism is verified to be a dipole-dipole interaction. The CIE of the optimized sample Ba_0.95Ca₂Si₃O₉:Eu_0.05²⁺ was (x, y)=(0.164, 0.111). The result indicates that BaCa₂Si₃O₉:Eu²⁺ can be potentially useful as a UV radiation-converting phosphor for white light-emitting diodes (LEDs).     

White light-emitting diodes using blue and yellow-orange-emitting phosphors

A blue-emitting phosphor, BaMgAl₁₀O₁₇:Eu²⁺ (BAM) and a yellow-orange phosphor, Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ were prepared by the solid-state reaction. Excitation and emission spectra results showed that BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ can be efficiently excited by near-ultraviolet (n-UV)-visible light from 250 to 440 nm. The effects of the doped-Eu²⁺ concentration in BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ on the photoluminescence were investigated in detail. White light-emitting diodes (LED) was obtained by combining n-UV LED chip (GaN-based 380 nm emitting) with BaMgAl₁₀O₁₇:0.09Eu²⁺ and 0.1Ba²⁺-codoped Sr₃SiO₅: 0.2Eu²⁺ phosphors with the characteristic of color-rendering index of 86, CIE chromaticity coordinates (x,y) of (0.3216,0.3096), and color temperature T_c of 5700 K. As the current increases, the relative intensity simultaneously increases. The CIE chromaticity coordinates (x,y) of the white LED tends to decrease. The correlated color temperature T_c increases from 4100 to 7500 K and the color-rendering index R_a increases from 82 to 87 simultaneously.     

Spherical Zn2SiO4:Eu@SiO2 phosphor particles in core-shell structure: Synthesis and characterization

Spherical SiO₂ particles have been coated with Zn₂SiO₄:Eu³⁺ phosphor layers by a Pechini sol-gel process. The microstructure and luminescent properties of the obtained Zn₂SiO₄:Eu³⁺@SiO₂ particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, and lifetime. The results demonstrate that the Zn₂SiO₄:Eu³⁺@SiO₂ particles, which have regular and uniform spherical morphology, emitted an intensive red light emission at 613 nm under excitation at 395 nm. Besides, the effects of the Eu³⁺ concentration, annealing temperature and charge compensators of Li⁺ ions on the PL emission intensities were investigated in detail.