Morphology and electro-optical properties of reverse mode polymer dispersed liquid crystals

We have investigated the morphology and electro-optical properties of reverse mode polymer dispersed liquid crystals as a function of liquid crystal loading. Reverse mode shutters have been obtained by a polymerization-induced phase separation of mixtures, consisting of a liquid crystalline monomer and a non-reactive nematic liquid crystal, placed between rough conductive surfaces. Such surfaces are able to keep the photopolymerizable mixtures homeotropically aligned without the use of any aligning polymer substrate. OFF state transmittances are always larger than 80% and the switching fields decrease if the non-reactive liquid crystal percentage is increased. Both rise and decay times are always lower than 10 ms. The electro-optical properties have been related to the sample morphology and a simple mode is proposed.     

UV tuning of the electro-optical and morphology properties in polymer-dispersed liquid crystals

Polymer-dispersed liquid crystal (PDLC) films operating in reverse mode are transparent electro-optical devices, which can be turned into an opaque state by application of a suitable electric field. The effect was investigated of different UV powers, used during the polymerization process, on the electro-optical and morphology properties of PDLCs, working in reverse mode operation. Films were obtained by UV polymerization of mixtures of a low molecular weight nematic liquid crystal and a photopolymerizable liquid crystal monomer, homeotropically aligned by rough conductive surfaces. The electro-optical and morphology properties of samples were related to the polymerization conditions. Samples polymerized by lower UV powers exhibited “polymer ball” morphology and an electro-optical response due to the liquid crystal director reorientation, whereas samples obtained at higher UV powers showed a “Swiss cheese” morphology and an electro-optical response due to dynamic scattering. In addition, we observed by conductivity and IR measurements that UV exposure induces a degradation of the nematic liquid crystal.     

Morphology and electro-optical properties of reverse mode polymer dispersed liquid crystals

We have investigated the morphology and electro-optical properties of reverse mode polymer dispersed liquid crystals as a function of liquid crystal loading. Reverse mode shutters have been obtained by a polymerization-induced phase separation of mixtures, consisting of a liquid crystalline monomer and a non-reactive nematic liquid crystal, placed between rough conductive surfaces. Such surfaces are able to keep the photopolymerizable mixtures homeotropically aligned without the use of any aligning polymer substrate. OFF state transmittances are always larger than 80% and the switching fields decrease if the non-reactive liquid crystal percentage is increased. Both rise and decay times are always lower than 10 ms. The electro-optical properties have been related to the sample morphology and a simple mode is proposed.     

Liquid crystal orientation in elliptic droplets in nematic emulsions

Elliptic droplets of nematic liquid crystal dispersed in a fluid organic monomer were obtained by phase separation from an isotropic mixture consisting of an organic monomer and a nematic liquid crystal contained in a poly(ethylene terephthalate) cell with inner surfaces treated with rubbed polyimide. The elliptic shape is a consequence of the constraint upon droplet growth along the direction perpendicular to the cell surfaces owing to the small thickness. Then, the resulting droplets will have a contact area with the inner surfaces of the cell treated with polyimide, which will impart a planar orientation on the liquid crystal in the droplet. By means of an optical microscope, using a simple pin hole of 5 μ m, we have selected single droplets for a series of samples having different contact areas. By polarized infrared spectroscopy we have also studied the liquid crystal orientation in selected areas of the droplets. We then report the dependence of the order parameter of the liquid crystal on different contact areas with the alignment surface of the cell. The good degree of planar alignment of the liquid crystal in the elliptic droplets allows the use of such a technique for realizing electro-optical films operating in the reverse mode. We report the electro-optical transmission of reverse mode films with different sizes of elliptic droplet.     

Liquid crystal orientation in elliptic droplets in nematic emulsions

Elliptic droplets of nematic liquid crystal dispersed in a fluid organic monomer were obtained by phase separation from an isotropic mixture consisting of an organic monomer and a nematic liquid crystal contained in a poly(ethylene terephthalate) cell with inner surfaces treated with rubbed polyimide. The elliptic shape is a consequence of the constraint upon droplet growth along the direction perpendicular to the cell surfaces owing to the small thickness. Then, the resulting droplets will have a contact area with the inner surfaces of the cell treated with polyimide, which will impart a planar orientation on the liquid crystal in the droplet. By means of an optical microscope, using a simple pin hole of 5 μm, we have selected single droplets for a series of samples having different contact areas. By polarized infrared spectroscopy we have also studied the liquid crystal orientation in selected areas of the droplets. We then report the dependence of the order parameter of the liquid crystal on different contact areas with the alignment surface of the cell. The good degree of planar alignment of the liquid crystal in the elliptic droplets allows the use of such a technique for realizing electro-optical films operating in the reverse mode. We report the electro-optical transmission of reverse mode films with different sizes of elliptic droplet.     

Liquid Crystal Emulsions

We review recent findings about the behavior of emulsions made of droplets suspended in liquid crystalline materials. By contrast to classical emulsions, which are usually made of isotropic oils and water, liquid crystal emulsions exhibit a variety of structures result in the ordering of the continuous phase. The droplets induce the formation of topological defects and distortions that lead to strong and anisotropic elastic forces between the particles. These elastic forces govern the stability and the ordering of the particles. This is observed in aqueous emulsions as well as in non-aqueous emulsions obtained from phase separation phenomena. It is shown that phase separations in liquid crystals can lead to the formation of highly ordered arrays of uniformly sized droplets. More generally, ordered structures seen in liquid crystal emulsions are of interest as examples of topologicallv-controlled organizations; they are also of potential practical importance as a novel way to control both the stability and the structures of colloidal particles.     

Liquid Crystal-Polymer Composite Materials

Polymer dispersed liquid crystal (PDLC) films can be switched electrically from a light-scattering off-state to a highly transparent on-state. Thin films were prepared via a polymerization-induced phase separation process, using electron beam radiation. The liquid crystal (LC)/polymer materials were obtained from blends of an eutectic nematie mixture E7 and a polyester acrylate-based polymer precursor. The optical and electro-optical properties of the PDLC films obtained depend strongly on the LC concentration. The LC solubility limit in the polymer matrix and the fractional amount of LC contained in the droplets were determined by means of calorimetrie measurements.     

Propriétés optiques et thermophysiques de composites polyméres-cristaux liquides (PDLC)

Polymer dispersed liquid crystal (PDLC) films can be switched electrically from a light scattering off-state to a highly transparent on-state. Thin films were prepared via a polymerization-induced phase separation process using electron beam radiation. The liquid crystal (LC)/polymer materials were obtained from blends of a eutectic nematic mixture E7 and a polyester acrylate based polymer precursor. The optical and electrooptical properties of the obtained PDLC films strongly depend on the LC concentration. The LC solubility limit in the polymer matrix and the fractional amount of LC contained in the droplets were determined by calorimetric measurements.     

Calorimetric studies of poly (2-phenoxyethylacrylate)/5CB mixtures

The thermophysical properties of mixtures of poly (2-phenoxyethylacrylate) and 4-cyano-4'-pentyl-biphenyl, 5CB, are investigated using polarizing optical microscopy (POM) and differential scanning calorimetry (DSC). The polymer has a molar mass M w = 181 000 g mol -1 ; the low molecular mass liquid crystal exhibits a nematic to isotropic transition at 35.3°C and crystallizes below 23°C. The phase diagram exhibits miscibility gaps in certain regions of temperature and composition where coexisting nematic and isotropic phases are found. From a practical point of view when considering the electro-optical applications of these systems, it proves to be useful to know precisely the amount of small liquid crystal molecules dissolved in the polymer matrix and the concentration of polymer in the nematic phase. The former quantity has a mechanical impact due to a plasticizing effect, an optical impact since it changes the polymer refractive index, while the polymer in the nematic phase shifts the transition temperatures influencing the electro-optical response of the liquid crystal. The present work addresses these important aspects using POM and DSC.     

Orientational control of liquid crystal molecules via carbon nanotubes and dichroic dye in polymer dispersed liquid crystal

Polymer dispersed liquid crystals (PDLCs) using nematic liquid crystal and photo-curable polymer (NOA 65) were prepared by polymerisation-induced phase separation technique, in equal ratio (1:1) of polymer and liquid crystal (LC). We demonstrate that doping of small amount (0.125%, wt./wt.) of multiwall carbon nanotubes (CNTs) and orange azo dichroic dye in PDLC generously controlled the molecular orientation, dynamics of LC in droplet and size of droplets. The effects of multiwall CNTs and dye on PDLCs were studied in terms of transition temperature, droplet morphology, transmittance characteristic, contrast ratio and response time. The results exhibited that the values of the threshold electric fields were reduced from 8 V/µm (pure PDLC) to 1.18 and 1.72 V/µm, doped with multiwall CNTs and dye, respectively. The CNTs-doped PDLC shows faster switching response as compared with pure PDLC and dye-doped PDLC. However, dye-doped PDLC shows much higher contrast among all PDLC samples. Further, the results also illustrate that the birefringence value of LC in PDLCs was changed with doping of CNTs and dye.     

Photochemical phase transition versus photochemical phase separation

When a nematic liquid crystal is doped with a large amount of a liquid crystalline azobenzene compound (15 wt %), the photoisomerization of azobenzene under UV and visible light irradiation can give rise to reversible and interconvertible photochemical phase transition and photochemical phase separation. Both normal and reverse modes of photocontrolled switching of transmittance through crossed polarizers can be realized with the same mixture of liquid crystal/azobenzene dopant.     

The investigation of molecular affinity involved in poly(ethylene glycol)-based polymer-dispersed liquid crystal display

Acrylic polyethylene glycol(PEG)-based polymer-dispersed liquid crystal (PDLC) films have been fabricated to investigate the effect of intermolecular interactions on PDLC performance. For this purpose, the amphiphilic liquid crystal and polymers are selected as PDLC composite materials. The acrylic PEG contents are varied from 0 to 66.66 mol wt.% in order to understand the effects of different levels of additions on the microstructure and electro-optical properties of the PDLC films. For this intention, polarized optical microscopy and UV–vis spectroscopy are used. The extent of phase separation and anchoring energy are also examined using Fourier transform infrared (FTIR) spectroscopy and contact angle measurements in consequence of acrylic PEG addition. The contrast ratio, threshold voltage, as well as saturation voltage, tended to increase with the addition of acrylic PEG. The molecular affinity involved in the polymer matrix and LC molecules affected the phase separation which is responsible for the formation of domain size; this accordingly changed the electro-optical properties of PDLC film.     

Thermal behaviour of switchable nematic emulsions

We have investigated the electro-optical performance of switchable nematic emulsions as a function of temperature. The electro-optical properties of nematic emulsions are highly dependent on temperature because several parameters such as droplet size, number density, viscosity, surface free energy, elastic constant, refractive indices, dielectric anisotropy, and liquid crystal/monomer solubility are affected by temperature. In particular, both ON state transmittances and decay times show a decreasing behaviour with increasing temperature. On the contrary, the OFF state transmittances increase, and the rise times do not change in an appreciable way.     

Photopolymerisation kinetics and electro-optical properties in mixtures of dichroic dye-doped nematic liquid crystal and photocurable polymer

This work reports the effect of dye on the photopolymerisation and electro-optical properties of polymer dispersed liquid crystal (PDLC) composite films. Dichroic PDLC (DPDLC) films based on a photocurable polymer and nematic liquid crystal (LC) with an azo dichroic dye were prepared by photopolymerisation-induced phase separation method. Polarising optical microscopy has been used for monitoring the phase separation kinetics and two-phase morphology evolution in the DPDLC system. LC domains with radial structures during initial period of phase separation adopted a resultant morphology of bipolar configuration over the course of polymerisation. The phase separation and morphology of LC domains was found to be dependent on the amount of dye used. Moreover, the addition of small amount of dye reduced the switching voltage, and enhanced the contrast ratio with improved switching time in the PDLC films. It was shown that, under the application of an electric field, the molecular orientation and absorbance of dichroic dye can be controlled in DPDLC to induce non-linearity and colour contrast without the use of polarisers.     

Thermal behaviour of switchable nematic emulsions

We have investigated the electro-optical performance of switchable nematic emulsions as a function of temperature. The electro-optical properties of nematic emulsions are highly dependent on temperature because several parameters such as droplet size, number density, viscosity, surface free energy, elastic constant, refractive indices, dielectric anisotropy, and liquid crystal/monomer solubility are affected by temperature. In particular, both ON state transmittances and decay times show a decreasing behaviour with increasing temperature. On the contrary, the OFF state transmittances increase, and the rise times do not change in an appreciable way.     

Reverse-mode polymer dispersed liquid crystal films prepared by patterned polymer walls

This article proposes a methodology to prepare polymer dispersed liquid crystal (PDLC) films working in the reverse-mode operation, where the ion-doped nematic liquid crystals (NLCs) with negative dielectric anisotropy (Δε) were locked by polymer walls. On-state and off-state of films were controlled by an electric field. In the absence of an electric field, it appears to be transparent. In the field, the homogeneous alignment NLCs form dynamic scattering, giving rise to opaque. The effect of the cylindrical holes with different diameters of photo masks and liquid crystal Δε on the electro-optical properties and transmittance wavelength range of 400–3000 nm light of samples were investigated. It was found that it exhibited very good electro-optical characteristics, high contrast ratio and excellent infrared energy-efficient of films used as switchable windows.     

Dye-dependent studies on droplet pattern and electro-optic behaviour of polymer dispersed liquid crystal

In order to study the droplet pattern and electro-optic (EO) behaviour of polymer dispersed liquid crystal (PDLC) with the addition of dye, dichroic polymer dispersed liquid crystal (DPDLC) films were prepared using a nematic liquid crystal (NLC), photo-curable polymer (NOA 65) and anthraquinone blue dichroic dye (B2), in equal ratio (1:1) of polymer and liquid crystal (LC) by polymerisation induced phase separation (PIPS) technique. Dichroic dye was taken in different concentration (wt./wt. ratio) as 0.0625%, 0.125%, 0.25%, 0.5% and 1% of the LC mixture in DPDLC films. Initially, in an open circuit when there is no proviso for external electric field (0 V), LC droplets in polymer matrix exhibited bipolar pattern, though on closing the circuit with the increase of electric field pattern of droplets starts changing, LC molecules align along the direction of applied electric field and aligned completely relatively at higher field (30 V), which illustrate vertical radial pattern. Further, results show that the DPDLC film containing 0.0625% dye concentration with consistent average droplet size ~4.30 μm, exhibits the best transmission at lower operating voltage.     

Separation of Isomers on Nematic Liquid Crystal Stationary Phases in Gas Chromatography: A Review

Understanding the composition of complex hydrocarbon mixtures is important for environmental studies in diverse fields, but many prevalent compounds cannot be confidently identified using traditional gas chromatography (GC) techniques. Increasing requirements on analyses of isomeric compounds and the problems encountered in their separation demand a study of more efficient systems which exhibit a high selectivity. Kelker and Fresenius first used nematic liquid crystals as stereospecific stationary phases in GC. Nematic liquid crystal has shown this particular selectivity and sensitivity as stationary phases for the separation of isomers having similar volatilities. Because of their unique selectivity towards rigid solute isomers, liquid crystal stationary phases were considered at one time to be a very promising class of materials that give gas chromatographic separations very different from those that can be obtained with any other stationary phase. Since then, a great deal of attention has been paid to the separation properties of this relatively wide group of substances. Liquid crystal can be used to separate a variety of compounds including isomer mixtures which cannot be separated on conventional stationary phases. This paper aims to review all specific experimental results and presents a comparative analytical study of monomeric nematic liquid crystal stationary phases used in GC. A further contribution of this review is in the field of isomeric compounds separation.     

Electro-optic behaviour of a non-polar nematic liquid crystal and its mixtures

In this work we report preliminary results on the properties of a non-polar bicyclohexane nematic liquid crystal. Moreover, its binary mixtures both with a low viscosity phenylcyclohexane and with a normal polar nematic liquid have been investigated. The elastic, viscous and electro-optical properties of these compounds are presented. The non-polar compound, and its mixture with a low percentage of the well known liquid crystal MBBA, exhibit an electrohydrodynamic behaviour in which the conducting regime is absent, while the dielectric regime spreads to low frequencies. Additionally, at higher frequencies of the applied electric field, a regime whose thresholds are linear in frequency is observed. On the other hand, the mixture formed by 50 wt % of the non-polar compound with MBBA exhibits at low frequencies the usual behaviour, followed at higher frequencies by the linear regime.