Templated synthesis of silver nanoparticles in amphiphilic poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) comb copolymer

In this study, poly(vinylidene fluoride‐co‐chlorotrifluoroethylene)‐graft‐poly(oxyethylene methacrylate), P(VDF‐co‐CTFE)‐g‐POEM, an amphiphilic comb copolymer with hydrophobic P(VDF‐co‐CTFE) backbone and hydrophilic POEM side chains at 73:27 wt % was synthesized. The POEM side chains were grafted from the P(VDF‐co‐CTFE) mainchain backbone via atom transfer radical polymerization (ATRP) using direct initiation of the chlorine atoms in CTFE units. Synthesis of microphase‐separated P(VDF‐co‐CTFE)‐g‐POEM comb copolymer was successful, as confirmed by nuclear magnetic resonance (¹H NMR), FTIR spectroscopy, and transmission electron microscopy (TEM). Nanocomposite films were prepared using the comb copolymer as a template film and the in situ reduction of AgCF₃SO₃ precursor to silver nanoparticles under UV irradiation. Silver nanoparticles with 4–8 nm in average size were in situ created in the solid state template film, as revealed by TEM, UV–visible spectroscopy, and wide angle X‐ray scattering (WAXS). Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) presented the selective incorporation and the in situ growth of silver nanoparticles within the hydrophilic POEM domains of microphase‐separated comb copolymer film. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 702–709, 2008     

Synthesis and characterization of grafted/crosslinked proton conducting membranes based on amphiphilic PVDF copolymer

A novel graft copolymer consisting of a poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) backbone and poly(glycidyl methacrylate) side chains, that is, P(VDF‐co‐CTFE)‐g‐PGMA, was synthesized through atom transfer radical polymerization (ATRP) using CTFE units as a macroinitiator. Successful synthesis and microphase‐separated structure of the polymer were confirmed by ¹H NMR, FTIR spectroscopy, and TEM. As‐synthesized P(VDF‐co‐CTFE)‐g‐PGMA copolymer was sulfonated by sodium bisulfite, followed by thermal crosslinking with sulfosuccinic acid (SA) via the esterification to produce grafted/crosslinked polymer electrolyte membranes. The IEC values continuously increased with increasing SA content but water uptake increased with SA content up to 10 wt %, above which it decreased again as a result of competitive effect between crosslinking and hydrophilicity of membranes. At 20 wt % of SA content, the proton conductivity reached 0.057 and 0.11 S/cm at 20 and 80 °C, respectively. The grafted/crosslinked P(VDF‐co‐CTFE)‐g‐PGMA/SA membranes exhibited good mechanical properties (>400 MPa of Young's modulus) and high thermal stability (up to 300 °C), as determined by a universal testing machine (UTM) and TGA, respectively. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1110–1117, 2010     

Nanofiltration membranes based on poly(vinylidene fluoride‐co‐chlorotrifluoroethylene)‐graft‐poly(styrene sulfonic acid)

Graft copolymers comprising poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) backbone and poly(styrene sulfonic acid) side chains, i.e. P(VDF‐co‐CTFE)‐g‐PSSA were synthesized using atom transfer radical polymerization (ATRP) for composite nanofiltration (NF) membranes. Direct initiation of the secondary chlorinated site of CTFE units facilitates grafting of PSSA, as revealed by FT‐IR spectroscopy. The successful “grafting from” method and the microphase‐separated structure of the graft copolymer were confirmed by transmission electron microscopy (TEM). Wide angle X‐ray scattering (WAXS) also showed the decrease in the crystallinity of P(VDF‐co‐CTFE) upon graft copolymerization. Composite NF membranes were prepared from P(VDF‐co‐CTFE)‐g‐PSSA as a top layer coated onto P(VDF‐co‐CTFE) ultrafiltration support membrane. Both the rejections and the flux of composite membranes increased with increasing PSSA concentration due to the increase in SO₃H groups and membrane hydrophilicity, as supported by contact angle measurement. The rejections of NF membranes containing 47 wt% of PSSA were 83% for Na₂SO₄ and 28% for NaCl, and the solution flux were 18 and 32 L/m² hr, respectively, at 0.3 MPa pressure. Copyright © 2008 John Wiley & Sons, Ltd.     

P (VDF‐co‐CTFE)‐g‐P2VP amphiphilic graft copolymers: Synthesis,structure, and permeation properties

A series of amphiphilic graft copolymers of poly (vinylidene fluoride‐co‐chlorotrifluoroethylene)‐g‐poly(2‐vinyl pyridine), P (VDF‐co‐CTFE)‐g‐P2VP, with different degrees of P2VP grafting (from 26.3 to 45.6 wt%) was synthesized via one‐pot atom transfer radical polymerization (ATRP). The amphiphilic properties of P (VDF‐co‐CTFE)‐g‐P2VP graft copolymers allowed itself to self‐assemble into nanoscale structures. P (VDF‐co‐CTFE)‐g‐P2VP graft copolymers were introduced into neat P (VDF‐co‐CTFE) as additives to form blending membranes. When two different solvents, N‐methyl‐2‐pyrrolidone (NMP) and dimethylformamide (DMF), were used, specific organized crystalline structures were observed only in the NMP systems. P (VDF‐co‐CTFE)‐g‐P2VP played a pivotal role in controlling the morphology and pore structure of membranes. The water flux of the membranes increased from 57.2 to 310.1 L m^?2 h^?1 bar^?1 with an increase in the PVDF‐co‐CTFE‐g‐P2VP loading (from 0 to 30 wt%) due to increased porosity and hydrophilicity. The flux recovery ratio (FRR) increased from 67.03% to 87.18%, and the irreversible fouling (R_ir) decreased from 32.97% to 12.82%. Moreover, the pure gas permeance of the membranes with respect to N₂ was as high as 6.2 × 10⁴ GPU (1 GPU = 10^–6 cm³[STP]/[s cm² cmHg]), indicating their possible use as a porous polymer support for gas separation applications.     

Poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) Modification via Organocatalyzed Atom Transfer Radical Polymerization

To address the challenge of metal contamination, a “graft from” approach via organocatalyzed atom transfer radical polymerization (O‐ATRP) is developed to synthesize poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) (P(VDF‐co‐CTFE)) graft copolymers. N‐phenylphenothiazine is utilized as a model organic photoredox catalyst for catalyzing the (co)polymerization of methyl methacrylate (MMA), methacrylate (MA), and n‐butyl acrylate (BA). By employing this technique, high temporal control of polymerization and graft content are achieved. A series of P(VDF‐co‐CTFE)‐g‐PMMA, P(VDF‐co‐CTFE)‐g‐PMA, and P(VDF‐co‐CTFE)‐g‐PBA is prepared under mild conditions. The resultant graft copolymer can be used as macroinitiator to re‐initiate O‐ATRP to synthesize P(VDF‐co‐CTFE)‐g‐(PMMA‐b‐PMA), which might exhibit the potential application as novel dielectric material.     

Synthesis of unsaturation containing P(VDF‐co‐TrFE‐co‐CTFE) from P(VDF‐co‐CTFE) in one‐pot catalyzed with Cu(0)‐based single electron transfer living radical polymerization system

Poly(vinylidene fluoride‐co‐trifluoroethylene‐co‐chlorotrifluoroethylene) (P(VDF‐co‐TrFE‐co‐CTFE)) with internal double bond has been reported with high dielectric constant and energy density at room temperature, which is expected to serve as a promising dielectric film in high pulse discharge capacitors. An environmentally friendly one‐pot route, including the controllable hydrogenation via Cu(0) mediated single electron transfer radical chain transfer reaction (SET‐CTR) and dehydrochlorination catalyzed with N‐containing reagent, is successfully developed to synthesize P(VDF‐co‐TrFE‐co‐CTFE) containing unsaturation. The resultant polymer was carefully characterized with ¹H NMR, ¹⁹F NMR, and FTIR. The composition of the resultant copolymer is strongly influenced by reaction conditions, including the reaction temperature, catalyst concentration, the types of ligands and solvents. The kinetics data of the chain transfer and elimination reaction demonstrate their well‐controlled feature of the strategy. By shifting the equilibrium between the CTR and elimination reactions dominated by N‐compounds serving as ligands in SET‐CTR and catalyst in the dehydrochlorination of P(VDF‐co‐CTFE), P(VDF‐co‐TrFE‐co‐CTFE) with tunable TrFE and double‐bond content could be synthesized in this one‐pot route. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 3429–3440     

Composite polymer electrolyte membranes comprising P(VDF‐co‐CTFE)‐g‐PSSA graft copolymer and zeolite for fuel cell applications

Hybrid organic/inorganic composite polymer electrolyte membranes based on a poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) grafted membrane and varying concentrations of zeolite were investigated for application in proton exchange membrane fuel cells (PEMFC). A proton conducting comb copolymer consisting of poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) backbone and poly(styrene sulfonic acid) (PSSA) side chains, i.e. P(VDF‐co‐CTFE)‐g‐PSSA (graft copolymer) with 47 wt% of PSSA was synthesized using atom transfer radical polymerization (ATRP) and solution blended with zeolite. Upon incorporation of zeolite, the symmetric stretching band of both SO group (1169 cm^?1) and the ? OH group (3426 cm^?1) shifted to lower wavenumbers. The shift in these FT‐IR spectra suggests that the zeolite particles strongly interact with the sulfonic acid groups of PSSA chains. When the weight percent of zeolite 5A is above 7%, the proton conductivity at room temperature was reduced to 0.011 S/cm. The water uptake of the composite membranes decreased from 234 to 125% with an increase of the zeolite 5A weight percent to 10 wt%. The decrease in water uptake is likely a result of the decrease in the number of available water absorption sites because of the hydrogen bonding interactions between the zeolite particles and the graft copolymer matrix. This behavior is successfully investigated by scanning electron microscopy (SEM). The results of thermal gravimetric analysis (TGA) also showed that all the membranes were stable up to 300°C. Copyright © 2009 John Wiley & Sons, Ltd.     

Synthesis and characterization of poly(vinylidene fluoride‐co‐chlorotrifluoroethylene)‐grafted‐poly(acrylonitrile) via single electron transfer–living radical polymerization process

Preparation of functional fluoromaterials through chemical modification of traditional fluoropolymers has been recognized as an economic and convenient strategy to expand the application areas of fluoropolymers. Poly(vinylidene fluoride‐co‐chlorotrifluoroethylene)‐grafted‐polyacrylonitrile (P(VDF‐co‐CTFE)‐g‐PAN) has been successfully synthesized via single electron transfer–living radical polymerization (SET–LRP) process initiated with macroinitiator P(VDF‐co‐CTFE) in the presence of trace amount of Cu(0)/tris(2(dimethylamino)ethyl)amine (Me₆‐TREN) in dimethyl sulfoxide (DMSO) at ambient temperature. The typical side reactions happened on P(VDF‐co‐CTFE) induced by the nitrogen‐containing solvents and high reaction temperature in atom transfer radical polymerization process could be avoided in SET–LRP process by using the mild reaction conditions. Well‐controlled polymerization features were observed under varied reaction conditions including the different reaction temperature, catalyst concentration, as well as monomer amount in feed. An induction period of 0.5–1.0 h in the polymerization procedure was observed at low temperature, which may be attributed to the Cu₂O from the surface of the Cu(0) powder. When Cu(0) catalyst is activated, the introduction period is eliminated. The polymerization rates were decelerated by adding excessive Me₆‐TREN for the formation of more stable CuCl₂/(Me₆‐TREN)₂. The structure of P(VDF‐co‐CTFE)‐g‐PAN was demonstrated by FTIR, NMR, DSC, and TGA. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Composite of P(VDF‐CTFE) and aromatic polythiourea for capacitors with high‐capacity,high‐efficiency,and fast response

For next generation of miniaturized personal electronics and pulsed power systems for smart power grids, electric vehicles, and electromagnetic launchers, flexible capacitors from dielectric polymers with high‐capacity, high‐efficiency, and fast response are highly desirable. Dielectric polymer composite of P(VDF‐CTFE), that is poly(vinylidene fluoride‐chlorotrifluoroethylene) and a small amount of aromatic polythiourea (PTU) has been described. It combines the merits of both polymers, that is high dipole density and easy processability of P(VDF‐CTFE), as well as large dipole moment and high charge–discharge efficiency of PTU. Most impressively, PTU boosts the maximum breakdown strength of P(VDF‐CTFE), and thus extracts its maximum energy reserve capacity. PTU also contributes to the promoted charge–discharge efficiency, accelerated discharge, and reduced dielectric loss in P(VDF‐CTFE), which facilitate the composite for flexible capacitor applications. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2018 , 56, 193–199     

Cu(0)/2,6‐bis(imino)pyridines catalyzed single‐electron transfer‐living radical polymerization of methyl methacrylate initiated with poly(vinylidene fluoride‐co‐chlorotrifluoroethylene)

A series of 2,6‐bis(imino)pyridines, as common ligands for late transition metal catalyst in ethylene coordination polymerization, were successfully employed in single‐electron transfer‐living radical polymerization (SET‐LRP) of methyl methacrylate (MMA) by using poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) (P(VDF‐co‐CTFE)) as macroinitiator with low concentration of copper catalyst under relative mild‐reaction conditions. Well‐controlled polymerization features were observed under varied reaction conditions including reaction temperature, catalyst concentration, as well as monomer amount in feed. The typical side reactions including the chain‐transfer reaction and dehydrochlorination reaction happened on P(VDF‐co‐CTFE) in atom‐transfer radical polymerization process were avoided in current system. The relationship between the catalytic activity and the chemical structure of 2,6‐bis(imino)pyridine ligands was investigated by comparing both the electrochemical properties of Cu(II)/2,6‐bis(imino)pyridine and the kinetic results of SET‐LRP of MMA catalyzed with different ligands. The substitute groups onto N‐binding sites with proper steric bulk and electron donating are desirable for both high‐propagation reaction rate and C? Cl bonds activation capability on P(VDF‐co‐CTFE). The catalytic activity of Cu(0)/2,6‐bis(imino)pyridines is comparable with Cu(0)/2,2′‐bipyridine under the consistent reaction conditions. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 4378–4388     

Fluorinated copolymers and terpolymers based on vinylidene fluoride and bearing sulfonic acid side‐group

The radical co‐ and terpolymerization of perfluoro(4‐methyl‐3,6‐dioxaoct‐7‐ene) sulfonyl fluoride (PFSVE) with 1,1‐difluoroethylene (or vinylidene fluoride, VDF or VF₂), hexafluoropropene (HFP), chlorotrifluoroethylene (CTFE), and bromotrifluoroethylene (BrTFE) is presented. Although PFSVE could not homopolymerize under radical initiation, it could be copolymerized in solution under a radical initiator with VDF, while its copolymerizations with HFP or CTFE led to oligomers in low yields. The terpolymerizations of PFSVE with VDF and HFP, with VDF and CTFE, or with VDF and BrTFE also led to original fluorinated terpolymers bearing sulfonyl fluoride side‐groups. The conditions of co‐ and terpolymerization were optimized in terms of the nature and the amount of the radical initiators, of the nature of solvents (fluorinated or nonhalogenated), and of the initial amounts of fluorinated comonomers. The different mol % contents of comonomers in the co‐ and terpolymers were assessed by ¹⁹F NMR spectroscopy. A wide range of co‐ and terpolymers containing mol % of PFSVE functional monomer ranging from 10 to 70% was produced. The kinetics of copolymerization of VDF with PFSVE enabled to assess the reactivity ratios of both comonomers: r_VDF = 0.57 ± 0.15 and r_PFSVE = 0.07 ± 0.04 at 120 °C. The thermal and physicochemical properties were also studied. Moreover, the glass transition temperatures (T_gs) of poly(VDF‐co‐PFSVE) copolymers containing different amounts of VDF and PFSVE were determined and the theoretical T_g of poly(PFSVE) homopolymer was deduced. Then, the hydrolysis of the ? SO₂F into ? SO₃H function was investigated and enabled the synthesis of fluorinated copolymers bearing sulfonic acid functions. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1814–1834, 2007     

Proton conducting grafted/crosslinked membranes prepared from poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) copolymer

Poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) (P(VDF‐co‐CTFE)) backbone was grafted with crosslinkable chains of poly(hydroxyl ethyl acrylate) (PHEA) and proton conducting chains of poly(styrene sulfonic acid) (PSSA) to produce amphiphilic P(VDF‐co‐CTFE)‐g‐P(HEA‐co‐SSA) graft copolymer via atom transfer radical polymerization (ATRP). Successful synthesis and microphase‐separated structure of the copolymer were confirmed by ¹H NMR, FT‐IR spectroscopy, and TEM analysis. Furthermore, this graft copolymer was thermally crosslinked with sulfosuccinic acid (SA) to produce grafted/crosslinked membranes. Ion exchange capacity (IEC) increased continuously with increasing SA contents but the water uptake increased up to 6 wt% of SA concentration, above which it decreased monotonically. The membrane also exhibited a maximum proton conductivity of 0.062 S/cm at 6 wt% of SA concentration, resulting from competitive effect between the increase of ionic groups and the degree of crosslinking. XRD patterns also revealed that the crystalline structures of P(VDF‐co‐CTFE) disrupted upon graft polymerization and crosslinking. These membranes exhibited good thermal stability at least up to 250°C, as revealed by TGA. Copyright © 2009 John Wiley & Sons, Ltd.     

Hydrophobic/hydrophilic P(VDF‐TrFE)/PHEA polymer blend membranes

Polymer blend membranes have been obtained consisting of a hydrophilic and a hydrophobic polymers distributed in co‐continuous phases. In order to obtain stable membranes in aqueous environments, the hydrophilic phase is formed by a poly(hydrohyethyl acrylate), PHEA, network while the hydrophobic phase is formed by poly(vinylidene fluoride‐co‐trifluoroethylene) P(VDF‐TrFE). To obtain the composites, in a first stage, P(VDF‐TrFE) is blended with poly(ethylene oxyde) (PEO), the latter used as sacrificial porogen. P(VDF‐TrFE)/PEO blend membranes were prepared by solvent casting at 70°C followed by cooling to room temperature. Then PEO is removed from the membrane by immersion in water obtaining a P(VDF‐TrFE) porous membrane. After removing of the PEO polymer, a P(VDF‐TrFE) membrane results in which pores are collapsed. Nevertheless the pores reopen when a mixture of hydroxethyl acrylate (HEA) monomer, ethyleneglycol dimethacrylate (as crosslinker) and ethanol (as diluent) is absorbed in the membrane and subsequent polymerization yields hybrid hydrophilic/hydrophobic membranes with controlled porosity. The membranes are thus suitable for lithium‐ion battery separator membranes and/or biostable supports for cell culture in biomedical applications. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 672–679     

Fluorinated block copolymers containing poly(vinylidene fluoride) or poly(vinylidene fluoride‐co‐hexafluoropropylene) blocks from perfluoropolyethers: Synthesis and thermal properties

PFPE‐b‐PVDF and PFPE‐b‐poly(VDF‐co‐HFP) block copolymers [where PFPE, PVDF, VDF, and HFP represent perfluoropolyether, poly(vinylidene fluoride), vinylidene fluoride (or 1,1‐difluoroethylene), and hexafluoropropylene] were synthesized by radical (co)telomerizations of VDF (or VDF and HFP) with an iodine‐terminated perfluoropolyether (PFPE‐I). Di‐tert‐butyl peroxide (DTBP) was used and was shown to act as an efficient thermal initiator. The numbers of VDF and VDF/HFP base units in the block copolymers were assessed with ¹⁹F NMR spectroscopy. According to the initial [PFPE‐I]₀/[fluoroalkenes]₀ and [DTBP]₀/[fluoroalkenes]₀ molar ratios, fluorinated block copolymers of various molecular weights (1500–30,300) were obtained. The states and thermal properties of these fluorocopolymers were investigated. The compounds containing PVDF blocks with more than 30 VDF units were crystalline, whereas all those containing poly(VDF‐co‐HFP) blocks exhibited amorphous states, whatever the numbers were of the fluorinated base units. All the samples showed negative glass‐transition temperatures higher than that of the starting PFPE. Interestingly, these PFPE‐b‐PVDF and PFPE‐b‐poly(VDF‐co‐HFP) block copolymers exhibited good thermostability. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 160–171, 2003     

Polymer electrolyte membranes by in situ polymerization of poly(ethylene carbonate‐co‐ethylene oxide) macromonomers in blends with poly(vinylidene fluoride‐co‐hexafluoropropylene)

Salt‐containing membranes based on polymethacrylates having poly(ethylene carbonate‐co‐ethylene oxide) side chains, as well as their blends with poly(vinylidene fluoride‐co‐hexafluoropropylene) (PVDF‐HFP), have been studied. Self‐supportive ion conductive membranes were prepared by casting films of methacrylate functional poly(ethylene carbonate‐co‐ethylene oxide) macromonomers containing lithium bis(trifluorosulfonyl)imide (LiTFSI) salt, followed by irradiation with UV‐light to polymerize the methacrylate units in situ. Homogenous electrolyte membranes based on the polymerized macromonomers showed a conductivity of 6.3 × 10^?6 S cm^?1 at 20 °C. The preparation of polymer blends, by the addition of PVDF‐HFP to the electrolytes, was found to greatly improve the mechanical properties. However, the addition led to an increase of the glass transition temperature (T_g) of the ion conductive phase by ～5 °C. The conductivity of the blend membranes was thus lower in relation to the corresponding homogeneous polymer electrolytes, and 2.5 × 10^?6 S cm^?1 was recorded for a membrane containing 10 wt % PVDF‐HFP at 20 °C. Increasing the salt concentration in the blend membranes was found to increase the T_g of the ion conductive component and decrease the propensity for the crystallization of the PVDF‐HFP component. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 79–90, 2007     

Crosslinked P(VDF‐CTFE)/PS‐COOH nanocomposites for high‐energy‐density capacitor application

High‐capacity or high‐power‐density capacitors are being actively investigated for portable electronics, electric vehicles, and electric power systems. The dielectric nanocomposite with a small loading of carboxylic polystyrene (PS‐COOH) nanoparticles in poly(vinylidene fluoride‐chlorotrifluoroethylene) [P(VDF‐CTFE)] matrix, followed by chemical crosslinking has been described. Combination of these two methods significantly improved the capacity of electric energy storage at low electric field. Specially, the nanocomposite with 2 wt % nanoparticles and 15 wt % crosslinking agent achieved a dielectric constant of 17.2 and a discharged energy density of 17.5 J/cm³ (4.9 Wh/L) at an electric field as high as 324 MV/m, while corresponding values for pristine P(VDF‐CTFE) are 9.6 and 13.3 J/cm³ (3.7 Wh/L), respectively. Fundamental physics underlying the enhancement in the performance of the nanocomposites with respect to P(VDF‐CTFE) is illustrated by solid‐state ¹⁹F nuclear magnetic resonance of direct excitation or ¹⁹F{¹H} cross polarization. It revealed different dynamics behavior between crystalline/amorphous regions, and PS‐COOH nanoparticles favored the formation of polar γ‐form crystals. Small‐angle X‐ray scattering studies revealed the contribution of the interface to the extraordinary storage of electric energies in the nanocomposites. This approach provided a facile and straightforward way to design or understand PVDF‐based polymers for their practical applications in high‐energy‐density capacitors. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 1160–1169     

Tailoring poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) microstructure and physicochemical properties by exploring its binary phase diagram with dimethylformamide

Poly(vinylidene fluoride‐co‐chlorotrifluoroethylene) (PVDF‐CTFE) membranes were prepared by solvent casting from dimethylformamide (DMF). The preparation conditions involved a systematic variation of polymer/solvent ratio and solvent evaporation temperature. The microstructural variations of the PVDF‐CTFE membranes depend on the different regions of the PVDF‐CTFE/DMF phase diagram, explained by the Flory‐Huggins theory. The effect of the polymer/solvent ratio and solvent evaporation temperature on the morphology, degree of porosity, β phase content, degree of crystallinity, mechanical, dielectric, and piezoelectric properties of the PVDF‐CTFE polymer were evaluated. In this binary system, the porous microstructure is attributed to a spinodal decomposition of the liquid‐liquid phase separation. For a given polymer/solvent ratio, 20 wt % , and higher evaporation solvent temperature, the β phase content is around 82% and the piezoelectric coefficient, d₃₃, is ? 4 pC/N © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 761–773     

Amphiphilic polymer electrolytes consisting of PVC‐g‐POEM comb‐like copolymer and LiCF3SO3

An amphiphilic comb‐like copolymer consisting of a poly(vinyl chloride) (PVC) backbone and poly((oxyethylene)₉ methacrylate) (POEM) side chains, PVC‐graft‐POEM was synthesized via atom transfer radical polymerization. This comb copolymer was complexed with LiCF₃SO₃ to form a solid polymer electrolyte. FTIR and FT‐Raman spectroscopy indicate that lithium salts are dissolved in the ion conducting POEM domains of microphase‐separated graft copolymer up to 10 wt % of salt concentration. Microphase‐separated structure of the materials and the selective interaction of lithium ions with POEM domains were revealed by transmission electron microscopy, wide angle X‐ray scattering, and differential scanning calorimetry. The maximum ionic conductivity of 4.4 × 10^?5 S/cm at room temperature was achieved at 10 wt % of salt concentration, above which salts are present as less mobile species such as ion pairs and higher order ionic aggregates, as characterized by FT‐Raman spectroscopy. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1443–1451, 2009     

Enhanced electrostriction based on plasticized relaxor ferroelectric P(VDF‐TrFE‐CFE/CTFE) blends

The purpose of this work aims at enhancing the electrostrictive strain response and the mechanical energy density under moderate electric field, which is essential for actuator applications. For achieving this, plasticized effects as well as the influence of chlorofluoroethylene and chlorotrifluoroethylene defects on the electromechanical behavior of the copolymer matrix poly(vinylidene fluoride‐trifluoroethylene) (P(VDF‐TrFE)) are investigated. Experimental results showed that the plasticized terpolymer‐based CFE presented better electrical and mechanical performances than the CTFE one. Furthermore, such interesting properties exhibited superior advantages when CFE was combined with (DEHP) plasticizer, resulting in excellent electrostrictive strain response as well as mechanical energy density. Another aspect of this work reports on the influence of the composition, especially the CTFE content, on the electromechanical properties of the neat and plasticized P(VDF‐TrFE‐CTFE). This enables the determination of the desired terpolymer compositions for given applications, which are based on different criteria, such as crystallinity, elastic modulus, dielectric permittivity, and so forth. All the results demonstrated a possibility to realize high performance electroactive polymer actuators while achieving significant improved strain response and energy density under relatively low electric field. Such an investigation allows overcoming the current technological barrier of conventional electroactive polymers that suffer from the high applied electric field usually required to reach sufficient strain. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1368–1379     

Effect of biaxial orientation on dielectric and breakdown properties of poly(ethylene terephthalate)/poly(vinylidene fluoride‐co‐tetrafluoroethylene) multilayer films

Polymer films with enhanced dielectric and breakdown properties are essential for the production of high energy density polymer film capacitors. By capitalizing on the synergistic effects of forced assembly nanolayer coextrusion and biaxial orientation, polymer multilayer films using poly(ethylene terephthalate) (PET) and a poly(vinylidene fluoride‐co‐tetrafluoroethylene) [P(VDF‐TFE)] copolymer were produced. These films exhibited breakdown fields, under a divergent field using needle/plane electrodes, as high as 1000 kV mm^?1. The energy densities of these same materials, under a uniform electric field measured using plane/plane electrodes, were as high as 16 J cm^?3. The confined morphologies of both PET and P(VDF‐TFE) were correlated to the observed breakdown properties and damage zones. On‐edge P(VDF‐TFE) crystals induced from solid‐state biaxial stretching enhanced the effective P(VDF‐TFE) layer dielectric constant and therefore increased the dielectric contrast between the PET and P(VDF‐TFE) layers. This resulted in additional charge buildup at the layer interface producing larger tree diameters and branches and ultimately increasing the breakdown and energy storage properties. In addition to energy storage and breakdown properties, the hysteresis behavior of these materials was also evaluated. By varying the morphology of the P(VDF‐TFE) layer, the low‐field dielectric loss (or ion migration behavior) could be manipulated, which in turn also changed the observed hysteresis behavior. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 882–896