Electrical transport and superconductivity in the Al2O3-Bi2Sr1.8Ca1.2Cu2Oy and MgO-Bi2Sr1.8Ca1.2Cu2Oy composites

We have measured the resistivities of Al₂O₃-Bi₂Sr_1.8Ca_1.2Cu₂O_y and MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y composites with the nominal Bi₂Sr_1.8Ca_1.2Cu₂O_y volume fraction, ₂₂₁₂, ranging from 0.15 to 1.00. For the Al₂O₃-Bi₂Sr_1.8Ca_1.2Cu ₂O_y composites, we find for the samples with ₂₂₁₂≥0.6 that the superconducting transition temperature, T_c, is not disturbed by the addition of Al₂O₃. For ₂₂₁₂<0.3, no zero-resistivity state is observed. For the MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y composites, T_c is barely disturbed for the samples with ρ₂₂₁₂≥0.7. No superconducting state is observed for the samples with ρ₂₂₁₂<0.35. The variation of (300 K) with ρ₂₂₁₂ indicates a three-dimensional percolating Bi-Sr-Ca-Cu-O matrix occurring at ρ₂₂₁₂≈0.19 and ≈0.15 in Al₂O₃-Bi₂Sr_1.8Ca_1.2 Cu₂O_y and MgO-Bi₂Sr_1.8Ca_1.2Cu₂O_y, respectively. Both resistivity and magnetization measurements suggest that the reactions of Bi₂Sr_1.8Ca_1.2Cu₂O_y with MgO are weaker than with Al₂O₃.     

Zone melting of suspension spun Bi2Sr2Ca1Cu2Ox filament

Zone melting was used to enhance the J_c of suspension spun Bi₂Sr₂Ca₁Cu₂O_x filaments. By controlling the directional solidification of the molten zone, highly orientated textures were produced and a transport critical current density of more than 2 × 10⁴ A/cm² at 77 K, 0 T was achieved.     

Temperature dependence of the critical current in YBa2Cu3O7−δ and Bi2Sr2Ca1Cu2O8 Josephson junctions

We have studied the stationary Josephson effect on YBa₂Cu₃O_7−δ (T_c=90 K) and Bi₂Sr₂Ca₁Cu₂ O₈ (T_c=80 K and 87 K for two samples of different origin) ceramic based junctions. The temperature dependence of the critical current near T_c has been found as I_c≈(T_c-T) for the Y-Ba-Cu-O samples indicating that they should be classified as S-N-I-N-S type junctions. The I-V curves of the Bi-Sr-Ca-Cu samples show the typical behaviour of S-I-S structures. Using Ambegaokar-Baratoff's theory for Bi₂Sr₂Ca₁Cu₂O₈, the temperature dependence of the superconducting state gap Δ(T) was calculated and it was evaluated that 1.452Δ(0)/k_BT_c3.5.     

The nuclear contribution to the specific heat of single crystals of YBa2Cu3O7 and Bi2Sr2CaCu2O8

Specific heat data below 1 K of Bi₂Sr₂CaCu₂O₈ and YBa₂Cu₃O₇ are analyzed. For YBa₂Cu₃O₇ the nuclear specific heat, C_N, amounts to 38T⁻² μJ/mol K. C_N for Bi₂Sr₂CaCu₂O₈ exceeds that of YBa₂Cu₃O₇ by a factor of 15. The nuclear quadrupolar specific heat contribution alone is insufficient to explain the data for YBa₂Cu₃O₇, while lack of NQR data does not allow such a comparison in Bi₂Sr₂CaCu₂O₈ to be made. The contribution to C_N from nuclear spins coupled via the contact hyperfine interaction with correlated magnetic spins (in the CuO₂ plane) is derived as a function of the correlation length. This contribution can be treated independently from the quadrupolar term. We show that the excess specific heat in YBa₂Cu₃O₇ likely originates in a few percentage of an impurity (oxygen deficient) phase with a strong hyperfine field on the Cu nuclei.     

Laser ablated bismuth cuprate thin films preparation and effect of oxygen nonstoichiometry upon superconductivity

Thin films of Bi₂Sr₂CaCu₂O₈ and (Bi, Pb)₂Sr₂Ca₂Cu₃O₁₀ have been prepared on monocrystalline (100) MgO substrates, using a laser ablation method with post annealing treatment. The influence of substrate temperature and oxygen pressure during deposition were investigated. SEM observations, EDS analysis, electric and magnetic measurements have been used to characterize the films. Superconducting “2212” films, with T_c(R = 0) at 80–83 K and J_c (50 K) up to 5 × 10⁵ A/cm², have been currently achieved, while Pb-doped “2223” films exhibit T_c as high as 110 K with J_c = 5 × 10⁴ A/cm² at 77 K. The effect of annealing at low temperature (350°C) in an argon flow has been studied for the 2212 phase, it shows the influence of the oxygen non-stoichiometry, i.e. of the hole carrier density upon T_c's which can be measured up to 89 K (zero resistance).     

The flux jumps in high TcBi1.7Pb0.3Sr2Ca2Cu3Oy bulk superconductor

There was giant flux jumps in high Tc Bi_1.7Pb_0.3Sr₂Ca₂Cu₃O_y bulk superconductor. The relaxation time, τ, decreased with both the increase of magnetic field and the rise of temperature. The maximum τ was about 40 min.. The average-dM/dt increased with both the increase of magnetic field and the rise of temperature. The minimum average-dM/dt was about 4.1×10⁻²G/min.. The flux jump weakened with time. It was dependent on the decrease of gradient of magnetic flux density dn/dx in the sample.     

Angle-resolved photoemission study of nonsuperconductive Bi2Sr2Ca0.4Y0.6Cu2O8

A comparative angle-resolved photoemission measurement has been performed on nonsuperconductive Bi₂Sr₂Ca_0.4Y_0.6Cu₂O₈ and superconductive Bi₂Sr₂CaCu₂O₈ to study the nature and origin of the electronic states near the Fermi level. It was found that hole-doping does not cause a rigid shift of the density of states relative to the Fermi level, but creates new electronic states in the vicinity of the Fermi level.     

Oxygen nonstoichiometry effect on structural modulation in Bi-2212 cuprate superconductors

The X-ray diffraction patterns for Bi₂Sr₂Ca_1−xY_xCu₂O_8+y sintered in air or Ar indicated that the reduction in the number of excess oxygen ions induced a structural change from orthorhombic to pseudotetragonal. When the oxygen contents decreased with the reducing treatment, the period of modulation in Bi₂Sr₂Ca_1−xY_xCu₂O_8+y increased. This result supported the model of excess oxygen ions in the Bi---O sheet. However, it was difficult to understand the change of modulation period with increasing Y contents using the model of excess oxygen ions in the Bi---O layers. Also, it is included that the Y substitution for Ca and La substitution for Sr in the Bi₂Sr₂CaCu₂O_8+y system result in parallel effects for the modulation structure.     

Effective activation energy Ue(T,J,H) in textured Bi1.84Pb0.4Sr2Ca2Cu3Oy silver-clamped thick films

We have measured the resistivity of textured Bi_1.84Pb_0.4Sr₂Ca₂Cu₃O_y silver-clamped thick films as a function of temperature, current density ranging from 10 to 1×10³ A/cm² and magnetic field up to 0.3 T. We find that the effective activation energy U_e follows U_e(T,J,H)=U₀(1−T/T_p)^mln(J_c0/J)H⁻ with m=1.75 for Hab-plane and 2.5 for Hc-axis and =0.76 for Hab and 0.97 for Hc, for the current density regime above 100 A/cm², where T_p is a function of applied magnetic field and current density. This result suggests the effective activation energy U_e be correlated with the temperature, current density and magnetic field. The possible dissipative mechanisms responsible for the temperature, current density and magnetic field dependence of the effective activation energy are discussed.     

Ionic conductivity of crystalline and glassy Mg4.5Na7(P2O7)4

In our work single crystals of Mg_4.5Na₇(P₂O₇)₄ were prepared, pulverized, pressed into pellets and sintered in order to measure the electrical conductivity of polycrystalline specimens. The conductivity was also measured on glassy specimens obtained by the melting of previously prepared crystals. The electrical conductivities at 25°C with values of the order of 10⁻¹⁶ Ω⁻¹ cm⁻¹ for polycrystalline samples and a value of the order of 10⁻¹⁴ Ω⁻¹ cm⁻¹ for glass, show that the glassy phase of Mg_4.5Na₇(P₂ because of its greater molar volume and loosely packed structure, is a better matrix for ionic motion.     

Impurity-state-like nature of Fermi-liquid states in Bi2Sr2CaCu2O8 observed by photoemission and x-ray absorption

Photoemission and X-ray absorption spectroscopy have been performed on Bi₂Sr₂Ca_1−xY_xCu₂O₈ in which the hole concentration is controlled by the ratio between Ca and Y atoms. It was found that the density of electronic states at the Fermi level gradually increases as the hole concentration with almost no rigid shift of the electronic structure with respect to the Fermi level. This suggests that the electronic states at the Fermi level (Fermi-liquid states) would not be simple one-electron states but be a kind of impurity states produced through the strong hybridization between doped O2p hole orbitals and empty Cu3d orbitals.     

Fabrication and growth rate estimation of PrBa2Cu3O7−δ single crystal by the modified top seeded crystal pulling method

Recently, we succeeded in fabricating single crystals of PrBa₂Cu₃O_7−δ by a modified top seeded crystal pulling method called the SRL-CP (Solute Rich Liquid-Crystal Pulling) method. Y₂O₃ and MgO polycrystalline crucibles and a MgO single crystal crucible were used to grow the single crystals. The crystal growth temperature was set in the range of 968°C to 972°C. The grown crystals were identified as PrBa₂Cu₃O_7−δ by X-ray diffraction. In the case of using Y₂O₃ crucibles the composition of the grown crystals was Y_xPr_1−xBa₂Cu₃O_7−δ (0.48 < x < 0.57) and in the case of using MgO crucibles a relatively small amount of Mg contamination to the grown crystals occurred at a typical concentration of approximately 1 at.% of the sum of cations. According to the crystal growth model of the SRL-CP method [1–5], a maximum growth rate of 1.7 × 10⁻⁵ cm/s was calculated with the aid of the phase diagram studies we reported earlier [6]. This value is reasonably in agreement with the experimental results.     

Determination of different oxygen transport mechanisms and measurement of the oxygen ion conductivity of Y1Ba2Cu3O7−x

By undertaking AC electrochemical impedance experiments on yttria stabilised zirconia electrolytes with polished Y₁Ba₂Cu₃O_7−x electrodes, the activation energy for oxygen ion transport within the bulk of Y₁Ba₂Cu₃O_7−x, in air, over the temperature range 823 K–1043 K, was determined to be 1.50 ± 0.05 eV. At 1000 K the oxygen ionic conductivity was calculated to be around one order of magnitude lower than that in yttria stabilised zirconia. Typical calculated values were σ=5×10⁻⁵ (ω cm)⁻¹ and 6×10⁻³ (ω cm)⁻¹ at the respective temperatures 823 K and 1043 K. By employing a similar cell but with Y₁Ba₂Cu₃O_7−x paste electrodes, oxygen transfer between the Y₁Ba₂Cu₃O_7−x and the electrolyte was found to occur via a surface diffusional processes. Over the temperature range 873 K–1098 K, in air, the activation energy for in-diffusion at the surface was found to be 1.4±0.1 eV and that for out-diffusion at the surface to be 1.76±0.05 eV.     

Synthesis and investigation of the complex copper oxides Bi2Sr2R2−xCexCu2O10+δ (R=rare earth)

Bi-2222 phases were prepared by solid state reactions and were studied using X-ray diffraction, chemical and EDS-analysis. Compounds with composition Bi₂Sr₂R_1.33Ce_0.67Cu₂O_10+δ were obtained for R=Pr, Nd, Sm-Er. The phases Bi₂Sr₂Cu₂O_10+δ with similar structure but without Ce were prepared for R = Pr, Sm-Dy. For Bi₂Sr₂Eu_2−xCe_xCu₂O_10+δ the solubility limit was determined and the effect of treatment under different oxygen pressures was investigated. Weak diamagnetic signals (<3%) were detected for some of these samples.     

Influence of Nd substitution on the superconducting properties of ceramics in the 2212 system Bi2−wPbwSr2−xCa1−yNdx+yCu2O8+z

In the system Bi_2−wPb_wSr_2−xCa_1−yNd_x+yCu₂O_8+z different fractions of Nd are substituted on either Sr of Ca sites in order to introduce intrinsic insulating pinning centres. It is shown that a Nd concentration around x or y = 0.2 is likewise favourable with an average Nd---Nd distance in the range of the coherence length in the a, b-plane. However, clear evidence of flux pinning is only present for charge compensation with Pb²⁺. A simultaneous substitution of the Bi-based 2212 superconductor with moderate amounts of Nd³⁺ and Pb²⁺ improves the superconducting properties by strengthening the flux pinning forces.     

Effect of Hg addition on synthesis of Bi-based superconductors

We have investigated the effect of Hg addition on the superconducting properties of BiSrCaCuO system. Polycrystalline samples with nominal composition Bi₂Sr_2−xHg_xCa₁Cu₂O_y and Bi₂Sr_2−xHg_xCa₂Cu₃O_y (x=0.3) were synthesized and used to investigate the phase evolution by XRD, superconducting behaviour by R–T measurement and the structural grain boundary effects by SEM. From these measurements, it has been noticed that the phases obtained with both types of compositions are the same as Bi2212 but the T_c values are different. With additional annealing, T_{c zero} values were raised from 60 to 72 K in Bi₂Sr_2−xHg_xCa₁Cu₂O_y and 64 to 92 K in Bi₂Sr_2−xHg_xCa₂Cu₃O_y. Also, an improved grain boundary linkage has been observed by SEM for the 92 K sample.     

Intergrain and intragrain superconductivity in Sn- and Sb-doped Bi1.7Pb0.3Sr2Cu3Oy

Measurements of the resistivity and current dependent resistivity for small current densities ranging from 0.03 A/cm² to 3.0 A/cm² were performed with two Sn-doped and two Sb-doped polycrystalline Bi_1.7Pb_0.3Sr₂Ca₂Cu₃O_y samples in magnetic fields up to 1.7 T. Features in the temperature derivative of the resistivity curves were associated with the presence of a superconducting transition between superconducting grains, coupled by weak links with a distribution of critical currents and critical temperatures, and the superconducting transition within grains. The transition between grains was more strongly suppressed in temperature with the application of a magnetic field in samples with weaker coupling between grains. The presence of a transition in a magnetic field due to weak links between grains was verified at 77 K by the observation of a current dependent resistivity in a magnetic field.     

Microwave absorption and paracoherence excess conductivity studies in high-Tc superconductors

Single phase polycrystalline samples of La_1.8Sr_0.2CuO₄, YBa₂Cu₃O_7−δ and Bi_1.6Pb_0.4Sr₂Ca₂Cu₃O_y high-T_c superconductors have been studied using XRD, SEM, EDAX, (T), χ_AC and EPR techniques. Detailed investigations on low-field-dependent microwave absorption have been carried out in order to investigate the effects of field exposure, field cooling, zero field cooling and amplitude of field variation on the samples. The results have been discussed on the basis of granular model via Josephson junctions of high-T_c superconductors. Over and above, paracoherence excess conductivity analysis has been carried out in all the three samples. The critical exponent (γ) estimated for all the three samples in close vicinity to their respective transition temperatures has an excellent agreement with the theoretically predicted value for 3-dimensional XY-ferromagnet (γ = 1.33 for D = 3, N = 2).     

Tunneling studies on single crystals of superconducting Bi2Ca1−xYxSr2Cu2O8+δ

Tunneling studies have been carried out on single crystals of Bi₂Ca_1−xSr_xCu₂O_8+δ over a wide range of compositions wherein the hole concentration varies by a factor of 2.5. The 2Δ value varies between 25 meV and 75 meV over the composition range studied, but scales with 2Δ/k_BT_c≈9.5 throughout.     

Evidence for pinning by (Sr,Ca)2CuOy particles in partial-melting processed bulk Bi2Sr2CaCu2O8+δ ceramics

Flux distributions of partial-melting processed Bi₂Sr₂CaCu₂O_8+δ ceramics are obtained using magneto-optic imaging. In remanent states (μ₀H_a=0 T), large amounts of trapped flux are observed along (Sr,Ca)₂CuO_y particles embedded in the Bi₂Sr₂CaCu₂O_8+δ matrix. Despite the relatively large size of these particles (up to 30 μm), the pinning effect is similar to that of Y₂BaCuO₅ particles in melt-processed YBa₂Cu₃O_7−δ. Furthermore, we discuss how the pinning capability of non-superconducting particles of different sizes and densities will show up in magneto-optic images.