Studies on thin films of TiO2 for resistance-based sensing of ethanol vapor at room temperature

We investigate the gas sensing properties of TiO₂ thin films prepared by spin coating. The presence of anatase and rutile phases in the sample was confirmed by powder X-Ray diffraction study. The thin film was characterized by FE-SEM and EDAX. The TiO₂ thin films were found to have good sensitivity towards ethanol compared to other gases. The sensing studies revealed the ethanol sensing properties of the thin film at room temperature even at lower concentrations. The response and selectivity of the film were also discussed in detail.     

The hybrid photocatalyst of TiO2–SiO2 thin film prepared from rice husk silica

The TiO₂–SiO₂ thin film was prepared by self-assembly method by mixing SiO₂ precursor with titanium precursor solution and aged to obtain a co-precipitation of silica and titanium crystals. Dip coating method was applied for thin film preparation on glass slide. The X-ray diffraction (XRD) of the self-assembly thin film had no characteristic property of SiO₂ and even anatase TiO₂ but indicated new crystal structure which was determined from the Fourier Transform Infrared Spectrophotometer (FTIR) as a hybridized Ti–O–Si bonding. The surface area and surface volume of the self-assembly sample were increased when SiO₂ was incorporated into the film. The self-assembly TiO₂–SiO₂ thin film exhibited the enhanced photocatalytic decolorization of methylene blue (MB) dye. The advantages of SiO₂ are; (1) to increase the adsorbability of the film and (2) to provide the hydroxyl radical to promote the photocatalytic reaction. The self-assembly thin film with the optimum molar ratio (SiO₂:TiO₂) as 20:80 gave the best performance for photocatalytic decolorization of MB dye with the overall efficiency of 81%.     

The fabrication of polymer-based evanescent optical waveguide for biosensing

A polymer waveguide was fabricated to amplify the evanescent optical field for biosensing. The structure of waveguide was designed to propagate a normal single mode at the input and output regions for low loss beam coupling and propagation. A sensing region was formed in the middle of the waveguide to activate the evanescent mode and to induce high birefringence by depositing a thin dielectric film with a high refractive index on a single mode waveguide. A polymer waveguide with the dimensions of 7 μm-width and 2.5 μm-thickness was fabricated by photolithography and dry-etching. The active region of the TiO₂ thin film was fabricated with the dimensions of 20 mm-length, 20 nm-thickness and 2 mm-tapered tail. A polarimetric interference technique was used to evaluate the evanescent waveguide biosensor, and biomaterial such as glycerol was tested. The sensitivity of the sensor increased with increasing TiO₂ film thickness. For the fabricated waveguide with a 20 nm-thick TiO₂ film, the measured index change to the lead phase variation of 2π was 1.8 × 10⁻⁴.     

Microstructure and electrical properties of Ba0.5Sr0.5TiO3 thin films prepared on copper foils with La2O3 buffer layers

Ba_0.5Sr_0.5TiO₃ (BST) thin films were deposited on copper foils via sol-gel method with La₂O₃ as a buffer layer. The films were processed in almost inert atmosphere so that the substrate oxidation was avoided while allowing the perovskite film phase to crystallize. The existence of a La₂O₃ buffer layer between the BST thin film and Cu foil improved the dielectric constant and reduced the leakage current density of the BST thin film. Meanwhile, the BST thin film exhibited ferroelectric character at room temperature, which was contrast to the para-electric behavior of the film without the buffer layer. Effects of La₂O₃ buffer layer on the crystallizability and microstructure of BST thin films were also investigated.     

Response improvement for In2O3-TiO2 thick film gas sensors

In₂O₃ is introduced into TiO₂ by sol-gel method to improve the response/recovery rate and expand the operating temperature, when the In₂O₃-TiO₂ mixed system is exposed to H₂/O₂. The sensor is fabricated by thick film technology. Influence of In₂O₃ on the film phase composition, microstructure and sensing characteristics is discussed. Dynamic response properties show that the operating temperature of the mixed system is at 500-800 °C, which is about 600-800 °C for pure TiO₂. Response time of the sensor is about 200-260 ms (millisecond) while recovery time is in a narrow range of 60-280 ms at 600-800 °C. The promoting mechanism is suggested to arise from the introduction of In₂O₃ and grain size effect of the sensing film. Then In₂O₃-TiO₂ thick films are surface-modified by Pt using chloroplatinic acid. The promoting effect of Pt dispersed on the mixed system is also investigated.     

Enhanced photocatalytic activity of TiO2 nano-structured thin film with a silver hierarchical configuration

TiO₂ sol-gels with various Ag/TiO₂ molar ratios from 0 to 0.9% were used to fabricate silver-modified nano-structured TiO₂ thin films using a layer-by-layer dip-coating (LLDC) technique. This technique allows obtaining TiO₂ nano-structured thin films with a silver hierarchical configuration. The coating of pure TiO₂ sol-gel and Ag-modified sol-gel was marked as T and A, respectively. According to the coating order and the nature of the TiO₂ sol-gel, four types of the TiO₂ thin films were constructed, and marked as AT (bottom layer was Ag modified, surface layer was pure TiO₂), TA (bottom layer was pure TiO₂, surface layer was Ag modified), TT (pure TiO₂ thin film) and AA (TiO₂ thin film was uniformly Ag modified). These thin films were characterized by means of linear sweep voltammetry (LSV), X-ray diffraction (XRD), scanning electron microscopy (SEM), electrochemical impedance spectroscopy and transient photocurrent (I_ph). LSV confirmed the existence of Ag⁰ state in the TiO₂ thin film. SEM and XRD experiments indicated that the sizes of the TiO₂ nanoparticles of the resulting films were in the order of TT > AT > TA > AA, suggesting the gradient Ag distribution in the films. The SEM and XRD results also confirmed that Ag had an inhibition effect on the size growth of anatase nanoparticles. Photocatalytic activities of the resulting thin films were also evaluated in the photocatalytic degradation process of methyl orange. The preliminary results demonstrated the sequence of the photocatalytic activity of the resulting films was AT > TA > AA > TT. This suggested that the silver hierarchical configuration can be used to improve the photocatalytic activity of TiO₂ thin film.     

Optical and hydrophilic properties of Cr doped TiO2-SiO2 nanostructure thin film

Cr doped TiO₂-SiO₂ nanostructure thin film on glass substrates was prepared by a sol-gel dip coating process. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) were used to characterize the structural and chemical properties of the films. A UV-vis spectrophotometer was used to measure the transmittance spectra of the thin film. The hydrophilicity of the thin film during irradiation and storage in a dark place was measured by a contact angle analyzer. The results indicated that Cr doping has a significant effect on the transmittance and super-hydrophilicity of TiO₂-SiO₂ thin film.     

A nano-porous TiO2 thin film coating method for dye sensitized solar cells (DSSCs) using electrostatic spraying with dye solution

The dye coloring process on a nano-porous TiO₂ thin film for DSSCs was studied using an electrostatic spraying (ESS) method. In this study, dye coating experiments were performed using homemade ESS equipment. The coating patterns on the TiO₂ thin film are changed by adjusting the applied voltages of the ESS system. The geometry of the coating patterns is observed by a charge-coupled device (CCD) camera. The TiO₂ thin film is fabricated by controlling the electric field which allows a uniform color distribution to be obtained with a high dyeing capacity. The colored TiO₂ thin films are compared with those obtained using a conventional immersed dye solution by means of an UV–vis spectrometer. The performance of this novel coloring process was confirmed by measuring I–V curve characteristics.     

The dispersion study of TiO2 nanoparticles surface modified through plasma polymerization

In this study, the surface of TiO₂ nanoparticles was modified through plasma polymerization, which is a dry coating method at room temperature. The surface morphology of TiO₂ nanoparticles was characterized by high-resolution transmission electron microscope (HRTEM). The dispersion behavior of TiO₂ nanoparticles in water and ethyl glycol was investigated by laser size distribution and ultraviolet–visible absorption spectrum. TiO₂ nanoparticles were coated with a thin film through plasma polymerization, which prevents the agglomeration and improves the dispersion behavior of TiO₂ nanoparticles.     

Grain Size Effects in Sensor Response of Nanostructured SnO2- and In2O3-Based Conductometric Thin Film Gas Sensor

Based on the experimental results, obtained by studying both structural and gas-sensing properties of the SnO₂ and In₂O₃ films deposited by the spray pyrolysis method, we analyzed the influence of crystallite size on the parameters of the SnO₂- and In₂O₃-based thin film solid-state gas sensors. For comparison, the behavior of ceramic-type gas sensors was considered as well. In particular, we examined the correlation between the grain size and parameters of conductometric-type gas sensors such as the magnitude of sensor signal, the rate of sensor response, thermal stability, and the sensitivity of sensor signal to air humidity. Findings confirmed that that grain size is one of the most important parameters of metal oxides, controlling almost all operating characteristics of the solid state gas sensors fabricated using both the ceramic and thin film technologies. However, it was shown that there is no single universal requirement for the grain size, because changes in grain size could either improve, or worsen of operating characteristics of gas sensors. Therefore, the choice of optimal grain size should be based on the detailed consideration of all possible consequences of their influence on the parameters of sensors designed.     

Photosensitization of nanocrystalline TiO2 film electrode with cadmium sulphoselenide

Nanocrystalline titanium dioxide (TiO₂) thin films composed of densely packed nanometer-sized grains have been successfully deposited onto an indium-doped-tin oxide (ITO) substrate. Then cadmium sulphoselenide (CdSSe) thin film was deposited onto pre-deposited TiO₂ to form a TiO₂/CdSSe film, at low temperature using a simple and inexpensive chemical method. The X-ray diffraction, selected area electron diffraction, scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and water contact angle techniques were used for film characterization. Purely rutile phase of TiO₂ with super-hydrophilic and densely packed nanometer-sized spherical grains of approximate diameter 30-40 (±2) nm was observed. The increase in optical absorption was observed after CdSSe film deposition. Nest like surface morphology of CdSSe on TiO₂ surface results in air trapping in the crevices which prevents water from adhering to the film with increase in water contact angle. Photosensitization of TiO₂ with CdSSe was confirmed with light illumination intensity of 80 mW/cm².     

Preparation and photoelectrochemical performance of Ag/graphene/TiO2 composite film

By dipping-lifting in sol-gel solution and reducing process, the graphene/TiO₂ composite film on the glass plate was first prepared. Then, the Ag/graphene/TiO₂ composite film was fabricated by interface reaction with AgNO₃ and N₂H₄·H₂O on the surface of graphene/TiO₂ composite film. The characterization results show that the uniform porous TiO₂ film is made up of the anatase crystal, and the Ag/graphene/TiO₂ composite film is constructed by doping or depositing graphene sheets and Ag nanoparticles on the surface of TiO₂ film. The photoelectrochemical measurement results indicate that the Ag/graphene/TiO₂ composite film has an excellent photoelectrochemical conversion property.     

Enhancing the crystallinity and surface roughness of sputtered TiO2 thin film by ZnO underlayer

TiO₂ and TiO₂/ZnO double layer films were sputtered on glass substrates. It was found that a thin ZnO underlayer is helpful for tailoring the microstructure and surface morphology of the TiO₂ film. By applying a 70-nm-thick ZnO underlayer, a TiO₂ thin film of 100 nm in thickness with well crystallized anatase phase and rough surface was successfully fabricated without heating the substrate. Relatively high photo-catalytic activity and good hydrophilic properties were observed in such TiO₂/ZnO double layer films.     

Effects of γ rays irradiation on structure and property of TiO2 thin films

TiO₂ thin films were deposited on a glass substrate by the radio frequency magnetron sputtering method, and annealed for 2 h at temperatures of 550°C. Then, ⁶⁰Co γ rays with different doses were used to irradiate the resulting TiO₂ thin films. The surface features of films before and after irradiation were observed by scanning electron microscope (SEM). Simultaneously, the crystal structure and optical properties of films before and after irradiation were studied by X-ray diffraction (XRD), UV–VIS transmission spectrum and Photoluminescence (PL) spectrum, respectively. The SEM analysis shows that the film is smooth with tiny particles on the film surface, and non-crystallization trend was clear after irradiated with γ rays. The XRD results indicated that the structure of the film at the room temperature mainly exists in the form of amorphous and mixed crystal at a sputtering power of 200 W, and non-crystallinity was more obvious after irradiation. Obvious difference can be found for the transmissibility of the irradiated and pre irradiation TiO₂ films by the UV-VIS spectra. The color becomes light yellow, and the new absorption edge also appeared at about 430 nm. PL spectra and photocatalysis experiments indicate that the photocatalysis degradation rate of the TiO₂ films on methylthionine chloride solution irradiated with the maximum dose can be increased to 90%.     

TiO2 Nanoparticles Produced by Electric-Discharge-Nanofluid-Process as Photoelectrode of DSSC

利用自制TiO₂纳米粒子研究敏化染敏太阳能电池. 使用自制的旋转涂布加热平台装置将产出的TiO₂粒子均匀的涂布在ITO导电玻璃上形成薄膜,浸泡于N-719 染料中12小时以上作为DSSCs的光电极 元件,最后完成染料敏化太阳能电池的系统组装并进行光电转换效率测量. 实验结果表明,放电过程产出的TiO₂纳米粒子具有锐钛矿晶相,粒径尺寸可控制在20～70 nm,粒子表面电位约为-30 mV,是稳定的纳米悬浮夜. 添加0.5 mL 的Triton X-100在导电玻璃表面上,利用的旋转涂布加热到22 oC可以制得厚度均匀缜密的薄膜结构,不但粒子不受到热处理效应与介面活性剂的影响而发生晶相改变,并且薄膜也有良好的染料吸附效果. 较厚二氧化钛薄膜的光电极会提升敏化染敏太阳能电池的效率. 实验结果得知,以15 μm的二氧化钛薄膜组装DSSCs测得最高效率2.15%,但是当薄膜厚度超过15 μm 则会导致开路电压与充填因子逐渐下降,光电转换效率变差.     

Transparent nano composite PVA–TiO2 and PMMA–TiO2 thin films: Optical and dielectric properties

Transparent nano composite PVA–TiO₂ and PMMA–TiO₂ thin films were prepared by an easy and cost effective dip coating method. Al/PVA–TiO₂/Al and Al/PMMA–TiO₂/Al sandwich structures were prepared to study the dielectric behavior. The presence of metal–oxide (Ti–O) bond in the prepared films was confirmed by Fourier transform infrared spectroscopy. X-ray diffraction pattern indicated that the prepared films were predominantly amorphous in nature. Scanning electron micrographs showed cluster of TiO₂ nanoparticles distributed over the film surface and also there were no cracks and pin holes on the surface. The transmittance of the films was above 80% in the visible region and the optical band gap was estimated to be about 3.77 eV and 3.78 eV respectively for PVA–TiO₂ and PMMA–TiO₂ films by using Tauc's plot. The determined refractive index (n) values were between 1.6 and 2.3. High value of dielectric constant (?′ = 24.6 and ?′ = 26.8) was obtained for the prepared composite films. The conduction in the composite films was found to be due to electrons. The observed amorphous structure, good optical properties and dielectric behavior of the prepared nano composite thin films indicated that these films could be used in opto-electronic devices and in thin film transistors.     

Sputter deposition of high transparent TiO2−xNx/TiO2/ZnO layers on glass for development of photocatalytic self-cleaning application

In this study, TiO_2−xN_x/TiO₂ double layers thin film was deposited on ZnO (80 nm thickness)/soda-lime glass substrate by a dc reactive magnetron sputtering. The TiO₂ film was deposited under different total gas pressures of 1 Pa, 2 Pa, and 4 Pa with constant oxygen flow rate of 0.8 sccm. Then, the deposition was continued with various nitrogen flow rates of 0.4, 0.8, and 1.2 sccm in constant total gas pressure of 4 Pa. Post annealing was performed on as-deposited films at various annealing temperatures of 400, 500, and 600 °C in air atmosphere to achieve films crystallinity. The structure and morphology of deposited films were evaluated by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and atomic force microscopy (AFM). The chemical composition of top layer doped by nitrogen was evaluated by X-ray photoelectron spectroscopy (XPS). Photocatalytic activity of samples was measured by degradation of Methylene Blue (MB) dye. The optical transmittance of the multilayer film was also measured using ultraviolet-visible light (UV-vis) spectrophotometer. The results showed that by nitrogen doping of a fraction (∼1/5) of TiO₂ film thickness, the optical transmittance of TiO_2−xN_x/TiO₂ film was compared with TiO₂ thin film. Deposited films showed also good photocatalytic and hydrophilicity activity at visible light.     

The photocatalytic application and regeneration of anatase thin films with embedded commercial TiO2 particles deposited on glass microrods

Anatase thin films (<200 nm in thickness) embedding Degussa P25 TiO₂ were prepared by sol-gel method. TiO₂-anatase thin films were deposited on a fiberglass substrate and then ground to obtain glass microrods containing the composite films. The film structure was characterized using Raman spectroscopy, atomic absorption and UV-vis spectrophotometry, and atomic force microscopy. The photocatalytic activity of the composite films, calcined at 450 °C, and the regeneration of the activity under the same experimental conditions, were assessed using gas chromatography to study the photodegradation of phenol, an industrial pollutant, in water under 365 nm irradiation. The film with 15.0 wt.% of P25 TiO₂ was found to be more photoactive (54 ppm of degraded phenol at 6 h of illumination) than the other ones.     

稀土钇、镧掺杂TiO2薄膜的拉曼谱分析

采用溶胶-凝胶法在石英玻璃衬底上用旋涂法制备了未掺杂、掺杂钇和掺杂镧的TiO₂薄膜样品,对样品在700—1100 ℃范围内进行退火处理,并对样品的拉曼光谱进行了分析.分析表明:随着退火温度的升高,未掺杂TiO₂薄膜发生了从锐钛矿相经混相最终向金红石相的转换,掺杂钇和掺杂镧对TiO₂薄膜的晶相转换起阻碍作用,掺杂镧的阻碍作用更强;稀土掺杂能使TiO₂薄膜晶粒细化,并使晶粒内部应力增大从而阻碍晶格振动,掺杂镧比掺杂钇的效果 关键词： 2薄膜')" href="#">TiO₂薄膜 稀土掺杂 拉曼光谱 溶胶-凝胶     

Annealing effects on microstructural and optical properties of Nanostructured-TiO2 thin films prepared by sol-gel technique

In this paper we report on the effect of annealing on the microsctructural and optoelectronic properties of titanium dioxide (TiO₂) thin films prepared using sol-gel method onto silicon (Si) (100) and quartz substrates. The annealing temperatures range from 200 to 1000 °C. The Microstructural properties of annealed thin films were investigated by Thermal gravimetric analyses (TGA), X-ray diffraction (XRD) and Raman Spectroscopy. The surface morphology of the film was examined using Atomic Force Microscopy (AFM) method. The optical properties of TiO₂ thin films were characterized using UV-VIS and Spectroscopic ellipsometry. The results have shown that the TiO₂ thin films persist in the anatase phase even after annealing at 800 °C. The phase transformation from anatase to rutile occurred only when the films were annealed at 1000 °C. AFM studies revealed nanocrystalline structure where their shape and density depend strongly on the annealing temperatures. The elaborated nanostructured-TiO₂ thin films present a high transparency in the visible range. Spectroscopic ellipsometry (SE) study was used to determine the effect of annealing temperature on the thickness and on the optical constant of TiO₂ thin films. Spectroscopic ellipsometry and UV-VIS shows that the band gap of TiO₂ thin films was found to decrease when the annealing temperature increases. The Anatase phase was find to show higher photocatalytic activity than the rutile one.