Effects of sintering temperature on grain growth and the complex permeability of Co0.2Ni0.3Zn0.5Fe2O4 material prepared using mechanically alloyed nanoparticles

Nanoparticle-sized Co_0.2Ni_0.3Zn_0.5Fe₂O₄ was prepared using mechanical alloying and sintering. The starting raw materials were milled in air and subsequently sintered at various temperatures from 600 to 1300 °C. The effects of sintering temperature on physical, magnetic and electrical characteristics were studied. The complex permittivity and permeability were investigated in the frequency range 10 MHz to 1.0 GHz. The results show that single phase Co_0.2Ni_0.3Zn_0.5Fe₂O₄ could not be formed during milling alone and therefore requires sintering. The crystallization of the ferrite sample increases with increasing sintering temperature; which decrease the porosity and increase the density, crystallite size and the shrinkage of the material. The maximum magnetization value of 83.1 emu/g was obtained for a sample sintered at 1200 °C, while both the retentivity and the coercivity decrease with increasing the sintering temperature. The permeability values vary with both the sintering temperature and the frequency and the absolute value of the permeability decreased after the natural resonance frequency. The real part of the permittivity was constant within the measured frequency, while the loss tangent values decreased gradually with increasing frequency.     

Phase formation and change of magnetic properties in mechanical alloyed Ni0.5Co0.5Fe2O4 by annealing

The effects of milling time and annealing temperature on phase formation, microstructure and magnetic properties of nickel-cobalt ferrite synthesized from oxide precursors by mechanical alloying were studied. The study of milling time effects on phase formation of milled materials showed that if milling continues up to 55 h, single phase nano-sized nickel-cobalt ferrite is obtained. Also, magnetic properties of powders versus milling time and annealing at different temperatures extensively changed, so that annealing at 1200 °C increased the magnetization saturation of the as-milled powder from 15.1 to 53.6 emu/g. X-ray powder diffraction technique (XRD) with Cu-Ka radiation was employed for phase identification. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were also used to determine the morphology and size of the particles. The magnetic properties were measured by a vibration sample magnetometer (VSM).     

Magnetic, structural and micro-structural properties of mechanically alloyed nano-structured Fe48Co48V4 powder containing inter-metallic Co3V

The Fe₄₈Co₄₈V₄ alloy was synthesized in a planetary high-energy ball-mill under an argon atmosphere. The structure, microstructure and magnetic properties of the mechanically alloyed powders were investigated by X-ray diffraction, Scanning Electron Microscopy and a Vibration Sample Magnetometer, respectively. During the mechanical alloying of Fe₄₈Co₄₈V₄, inter-metallic Co₃V appears. The lattice parameter decreases up to 55 h of milling time with an oscillation and then increases from 55 to 125 h of milling time. The coercivity increases during the milling treatment from 49 to 58 Oe. The saturation magnetization has some fluctuations during the milling treatment and finally reaches ∼190 emu/g at 125 h.     

NbTi0.5Ni0.5O4 as anode compound material for SOFCs

NbTi_0.5Ni_0.5O₄ (NTNO) has been prepared using solid state synthesis and investigated as a potential anode material. The oxide form of NTNO has single phase rutile-type structure with tetragonal (P42/mnm) space group. The reduced form is a composite of nano-scaled particles of metallic Ni and Nb_1.33Ti_0.67O₄ phase. Reduced NTNO showed high electronic conductivity up to 280 S.cm^− 1 at 900 °C in reducing atmosphere, but suffers from low CTE equal to 3.78 10^− 6 K^− 1. Studies of NTNO as anode material were carried out in a three electrode - electrochemical half cell configuration under pure humidified H₂ at 900 °C using a 2 mm thick zirconia electrolyte and without any additional current collector material. The results show a reasonable series resistance (R_s) equal to 2.7 Ωcm² (about 50% higher than for metallic gold layers) indicating a good current collection performance for a 10 μm layer of material. The polarization resistance (R_p) was equal to 33 Ωcm² and is attributed to a poor density of three phase boundaries (TPB) and shortage of oxide ion conduction in the anode layer. The results show the potential of NTNO as an anode material, especially after optimization of the microstructure towards the increase of TPB length.     

Sintering temperature dependence of room temperature magnetic and dielectric properties of Co0.5Zn0.5Fe2O4 prepared using mechanically alloyed nanoparticles

Co_0.5Zn_0.5Fe₂O₄ nanoparticles were prepared using mechanical alloying (MA) and sintering. The crystallite size, coercivity, retentivity and saturation magnetization were also measured. The frequency dependence of dielectric and the magnetic parameters, namely, real permittivity ε′, loss tanget tan δ, real permeability μ′ and loss factor μ″ were measured at room temperature for samples sintered from 600 to 1000 °C, in the frequency range 10 MHz to 1.0 GHz. The results show that the crystallite size of the resulting products ranges between 16 and 67 nm for as-milled sample and the sample sintered at 1000 °C, respectively. The sample sintered at 1000 °C, measured at room temperature exhibited a saturation magnetization of 37 emu g⁻¹. The values of permittivity remain constant within the measured frequency, but vary with sintering temperature. The permeability values, on the other hand however vary with both the sintering temperature and the frequency, thus, the absolute value of the permeability decreased after the natural resonance frequency.     

Local composition and carrier concentration in Pb0.7Ge0.3Te and Pb0.5Ge0.5Te alloys from Te NMR and microscopy

Pb_0.7Ge_0.3Te and Pb_0.5Ge_0.5Te alloys, (i) quenched from 923 K or (ii) quenched and annealed at 573 K for 2 h, have been studied by ¹²⁵Te NMR, X-ray diffraction, electron and optical microscopy, as well as energy dispersive spectroscopy. Depending on the composition and thermal treatment history, ¹²⁵Te NMR spectra exhibit different resonance frequencies and spin-lattice relaxation times, which can be assigned to different phases in the alloy. Quenched and annealed Pb_0.7Ge_0.3Te alloys can be considered as solid solutions but are shown by NMR to have components with various carrier concentrations. Quenched and annealed Pb_0.5Ge_0.5Te alloys contain GeTe- and PbTe-based phases with different compositions and charge carrier concentrations. Based on the analysis of non-exponential ¹²⁵Te NMR spin-lattice relaxation, the fractions and carrier concentrations of the various phases have been estimated. Our data show that alloying of PbTe with Ge results in the formation of chemically and electronically inhomogeneous systems. ¹²⁵Te NMR can be used as an efficient probe to detect the local composition in equilibrium as well as non-equilibrium states, and to determine the local carrier concentrations in complex multiphase tellurides.     

Dependence of magnetic properties and microstructure of mechanically alloyed Ni0.5Zn0.5Fe2O4 on soaking time

Possible soaking-time effects on the magnetic and microstructural properties of polycrystalline samples of Ni_0.5Zn_0.5Fe₂O₄ have been studied. Nanosize powder produced by mechanical alloying was sintered at 800 °C with various soaking times. All samples showed the signature peak of Ni_0.5Zn_0.5Fe₂O₄ even with one hour of soaking time. The size distributions show a slow growth of microstructural evolution related to density, porosity and also to the magnetic hysteresis loops. Within these distributions it is observed that the formation of multi-domains is not possible and probably there are the regions of superparamagnetic and single-domain grains. From the permeability studies, it is believed that the rise of the magnetic moment on the B sites give rise to the total saturation magnetization with increase of soaking time. The hysteresis loop of one-hour soaking time showed paramagnetic behavior dominating while longer soaking times showed ferromagnetic behavior starting to dominate. The coercivity was observed to increase with soaking time, signaling the increase of the anisotropy fields which was attributed to the shape anisotropy and also to the magnetocrystalline anisotropy. By correlating the morphology, phase analysis, permeability and hysteresis loops results, it is believed that there was an increase in number of crystalline-growth regions which together formed a total mass of mixed superparamagnetic and ferromagnetic grains with the latter starting to dominate the samples.     

X-ray diffraction,microstructure, Mössbauer and magnetization studies of nanostructured Fe50Ni50 alloy prepared by mechanical alloying

Nanocrystalline Fe₅₀Ni₅₀ alloy samples were prepared by the mechanical alloying process using planetary high-energy ball mill. The alloy formation and different physical properties were investigated as a function of milling time, t, (in the 0–50 h range) by means of the X-ray diffraction (XRD) technique, scanning electron microscopy (SEM), energy dispersive X-ray (EDAX), Mössbauer spectroscopy and the vibrating sample magnetometer (VSM). The complete formation of γ-FeNi is observed after 24 h milling. When milling time increases from 0 to 50 h, the lattice parameter increases towards the Fe₅₀Ni₅₀ bulk value, the grain size decreases from 67 to 13 nm, while the strain increases from 0.09% to 0.41%. Grain morphologies at different formation stages were observed by SEM. Saturation magnetization and coercive fields derived from the hysteresis curves are discussed as a function of milling time.     

Study of magnetic phases in mechanically alloyed Fe50Zn50 powder

The mechanosynthesis of Fe₅₀Zn₅₀ alloy resulted in the formation of the bcc Fe(Zn) solid solution after 20 h of milling. Structural transformations induced by mechanical alloying and heating, and magnetic properties of the powders were studied by Mössbauer spectroscopy, X-ray diffraction, Faraday balance and vibrating sample magnetometry techniques. All alloys studied exhibit strong magnetic ordering with Curie temperatures close to 900 K. Room temperature Mössbauer measurements revealed distinguished magnetic environments in the samples. The decrease of coercivity with prolonged milling time was attributed to the reduction or averaging of local magnetic anisotropies.     

Structure and magnetic properties of nanocrystalline Fe75Si25 powders prepared by mechanical alloying

Nanocrystalline Fe₇₅Si₂₅ powders were prepared by mechanical alloying in a planetary ball mill. The evolution of the microstructure and magnetic properties during the milling process were studied by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer measurements. The evolution of non-equilibrium solid solution Fe (Si) during milling was accompanied by refinement of crystallite size down to 10 nm and the introduction of high density of dislocations of the order of 10¹⁷ m⁻². During the milling process, Fe sites get substituted by Si. This structural change and the resulting disorder are reflected in the lattice parameters and average magnetic moment of the powders milled for various time periods. A progressive increase of coercivity was also observed with increasing milling time. The increase of coercivity could be attributed to the introduction of dislocations and reduction of powder particle size as a function of milling time.     

Evolution of structure, microstructure and hyperfine properties of nanocrystalline Fe50Co50 powders prepared by mechanical alloying

Nanostructured Fe₅₀Co₅₀ powders were prepared by mechanical alloying of Fe and Co elements in a vario-planetary high-energy ball mill. The structural properties, morphology changes and local iron environment variations were investigated as a function of milling time (in the 0-200 h range) by means of X-ray diffraction, scanning electron microscopy (SEM), energy dispersive X-ray analysis and ⁵⁷Fe Mössbauer spectroscopy. The complete formation of bcc Fe₅₀Co₅₀ solid solution is observed after 100 h milling. As the milling time increases from 0 to 200 h, the lattice parameter decreases from 0.28655 nm for pure Fe to 0.28523 nm, the grain size decreases from 150 to 14 nm, while the meal level of strain increases from 0.0069% to 1.36%. The powder particle morphology at different stages of formation was observed by SEM. The parameters derived from the Mössbauer spectra confirm the beginning of the formation of Fe₅₀Co₅₀ phase at 43 h of milling. After 200 h of milling the average hyperfine magnetic field of 35 T suggests that a disordered bcc Fe-Co solid solution is formed.     

Influence of epitaxial growth on phase competition in Pr0.5Sr0.5MnO3 films

A series of Pr_0.5Sr_0.5MnO₃ (PSMO) films with various thickness were epitaxially grown on substrates of (0 0 1)-oriented (LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (LSAT), LaAlO₃ (LAO) and SrTiO₃ (STO), and (0 1 1)-oriented STO using pulse laser deposition. Influence of epitaxial growth on phase competition was investigated. A ferromagnetic metal to antiferromagnetic insulator (FMM-AFI) transition upon cooling is present in both largely compressed situations deposited on LAO (0 0 1) and tensile cases deposited on STO (0 0 1) but absent in little strained films grown on LSAT (0 0 1), indicating that the antiferromagnetic insulating state is favored by strains. On the other hand, the 400 nm films deposited on (0 1 1)-oriented STO as well as LAO substrates show FMM-AFI transition. These results reveal that both the orientation of epitaxial growth and substrate-induced strain affect the FMM-AFI transition.     

Growth of superconducting FeSe0.5Te0.5 thin films by pulsed-laser deposition

FeSe_0.5Te_0.5 thin films with PbO-type structure are successfully grown on MgO(1 0 0) and LaSrAlO₄(0 0 1) substrates from FeSe_0.5Te_0.5 or FeSe_0.5Te_0.75 polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness ∼ 55 nm) shows superconductivity at 10.6 K (onset) and 9.2 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO₄ substrate (film thickness ∼ 250 nm) exhibits superconductivity at 5.4 K (onset) and 2.7 K (zero resistivity). This suggests the strong influence of substrate materials and/or the c-axis length to superconducting properties of FeSe_0.5Te_0.5 thin films.     

Influence of milling time on the structural, microstructural and magnetic properties of mechanically alloyed Ni58Fe12Zr10Hf10B10 nanostructured/amorphous powders

This paper investigates structural, microstructural and magnetic properties of amorphous/nanocrystalline Ni₅₈Fe₁₂Zr₁₀Hf₁₀B₁₀ powders prepared by high energy milling. Ball milling of Ni, Fe, Zr, Hf and B leads to alloying of the element powders at 120 h. The results show that at 190 h the amorphous content is at the highest level and the grain size is about 2 nm. The magnetic measurements reveal that the coercivity and the saturation magnetization reach about 20 Oe and 30 emu/g at 190 h and become approximately 5 Oe and 40 emu/g after a suitable heat treatment, respectively.     

Molten salt synthesis of Li1 + x (Ni0.5Mn0.5)1 − xO2 as cathode material for Li-ion batteries

Li_1 + x(Ni_0.5Mn_0.5)_1 − xO₂ cathode material for Li-ion batteries has been prepared by a molten salt method using Li₂CO₃ salt. The influences of synthetic temperature and time have been intensively investigated. It is easy to obtain materials with a hexagonal α-NaFeO₂ structure except broad peaks between 20° and 25°. Nickel in Li_1 + x(Ni_0.5Mn_0.5)_1 − xO₂ is oxidized to a trivalent state while manganese maintained a tetravalent state. It is found that the discharge capacities of all samples increase with cycling. The sample prepared at 850 °C for 5 h has a discharge capacity of 130 mAh g^− 1 between 2.5 and 4.5 V versus V_Li+/Li at a specific current of 0.13 mA cm^− 2 after 50 cycles at 25 °C.     

Simultaneous variations of microstructure and magnetic properties of Ni58Fe12Zr20B10 nanostructure/amorphous alloy prepared by mechanical alloying

This study aims to evaluate magnetic and micro-structural properties of amorphous/nanocrystalline mechanically alloyed Ni₅₈Fe₁₂Zr₂₀B₁₀ powders with ball-milling time up to 190 h. Structural, micro-structural and thermal evaluations of the milled powders were carried out by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and differential scanning calorimetry (DSC) methods. Magnetic properties were also measured by a vibrating sample magnetometer (VSM) instrument. Results showed that the amorphous phase reached maximum value of 95% and the crystallite size was about 3 nm at the end of the milling. Magnetization saturation (M_s) decreased slightly and coercivity (H_c) reached to the highest value at 72 h of the milling time. At the 190 h of milling, the coercivity and saturation magnetization reached 18 Oe and 20 emu/g, respectively. While, after an appropriate amount of heat treatment, these two variables became approximately 2 Oe and 32 emu/g.     

Research on charge-ordering state in La0.5Sr0.5MnO2.88 and La0.5Sr0.5Mn0.5Ti0.5O3 systems

The structural, magnetic and transport properties of La_0.5Sr_0.5MnO_2.88 and La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ samples have been investigated systematically. Indeed, this series has been considered to understand the influence of physical parameters such as oxygen deficiency and titanium doping effect in undoped La_0.5Sr_0.5MnO₃ sample. Ceramic material based on La_0.5Sr_0.5MnO_2.88 exhibits interesting behaviours of charge-ordering (CO), ferromagnetic (FM) states and a good conductivity down to the lowest temperatures. The substitution of Ti for Mn destroyed drastically the CO, damaged the motion of itinerant e_g electrons and changed the local parameters of perovskite cell. A change of the structure from tetragonal to rhombohedral symmetry is observed causing a weakening of double-exchange interaction. The experiment results show that the suppression of the CO is sensitive to the variety of Mn³⁺/Mn⁴⁺ ratio. In a field of 8 T at 10 K, FM and CO phase can be evaluated to be ∼20:80 according to the μ_exp/μ_cal ratio for La_0.5Sr_0.5MnO_2.88, whereas the CO state is suppressed for La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ sample, FM and anti-ferromagnetic (AFM) phase are coexisted and evaluated to be ∼54:46, respectively.     

Hydrothermal synthesis and Magnetocaloric effect of La0.5Ca0.3Sr0.2MnO3

The hydrothermal synthesis and magnetic entropy change for the perovskite manganite La_0.5Ca_0.3Sr_0.2MnO₃ have been studied. The La_0.5Ca_0.3Sr_0.2MnO₃ can be produced as phase-pure, crystalline powders in one step from solutions of metal salts in aqueous potassium hydroxide solution at a temperature of 513 K in 72 h. Scanning electron microscopy shows that the materials are made up of cuboid-shaped particles in typical dimension of 4.0×2.5×1.6 μm. Heat treatment can improve the magnetocaloric effect for the hydrothermal sample. The maximum magnetic entropy change ΔS_M for the as-prepared sample is 0.88 J kg⁻¹ K⁻¹ at 315 K for a magnetic field change of 2.0 T. It increases to 1.52 J kg⁻¹ K⁻¹, near its Curie temperature (317 K) by annealing the sample at 1473 K for 6 h. The hydrothermal synthesis method is a feasible route to prepare high-quality perovskite material for magnetic refrigeration application.     

Electrical properties of SrBi2(Nb0.5Ta0.5)2O9 ceramics

Aurivillius SrBi₂(Nb_0.5Ta_0.5)₂O₉ (SBNT 50/50) ceramics were prepared using the conventional solid-state reaction method. Scanning electron microscopy was applied to investigate the grain structure. The XRD studies revealed an orthorhombic structure in the SBNT 50/50 with lattice parameters a=5.522 Å, b=5.511 Å and c=25.114 Å. The dielectric properties were determined by impedance spectroscopy measurements. A strong low frequency dielectric dispersion was found to exist in this material. Its occurrence was ascribed to the presence of ionized space charge carriers such as oxygen vacancies. The dielectric relaxation was defined on the basis of an equivalent circuit. The temperature dependence of various electrical properties was determined and discussed. The thermal activation energy for the grain electric conductivity was lower in the high temperature region (T>303.6 °C, E_a−ht=0.47 eV) and higher in the low temperature region (T<303.6 °C, E_a−lt=1.18 eV).     

Annealing effects on structural, optical and electrical properties of e-beam evaporated CuIn0.5Ga0.5Te2 thin films

CuIn_0.5Ga_0.5Te₂ (CIGT) thin films have been prepared by e-beam evaporation from a single crystal powder synthesized by direct reaction of constituent elements in a stoichiometric proportion. Post-depositional annealing has been carried out at 300 and 350 °C. The compositions of the films were determined by energy dispersive X-ray analysis (EDXA) and it was found that there was a remarkable fluctuation in atomic percentage of the constituent elements following to the post-depositional annealing. X-ray diffraction analysis (XRD) has shown that as-grown films were amorphous in nature and turned into polycrystalline structure following to the annealing at 300 °C. The main peaks of CuIn_0.5Ga_0.5Te₂ and some minor peaks belonged to a binary phase Cu₂Te appeared after annealing at 300 °C, whereas for the films annealed at 350 °C single phase of the CuIn_0.5Ga_0.5Te₂ chalcopyrite structure was observed with the preferred orientation along the (1 1 2) plane. The effect of annealing on and near surface regions has been studied using X-ray photoelectron spectroscopy (XPS). The results indicated that there was a considerable variation in surface composition following to the annealing process. The transmission and reflection measurements have been carried out in the wavelength range of 200-1100 nm. The absorption coefficients of the films were found to be in the order of 10⁴ cm⁻¹ and optical band gaps were determined as 1.39, 1.43 and 1.47 eV for as-grown and films annealed at 300 and 350 °C, respectively. The temperature dependent conductivity and photoconductivity measurements have been performed in the temperature range of −73 to 157 °C and the room temperature resistivities were found to be around 3.4 × 10⁷ and 9.6 × 10⁶ (Ω cm) for the as-grown and annealed films at 350 °C, respectively.