Near room temperature magnetocaloric properties of melt-spun Gd100−xBx (x=0, 5, 10, 15, and 20 at%) alloys

The magnetocaloric properties of melt-spun Gd-B alloys were examined with the aim to explore their potential application as magnetic refrigerants near room temperature. A series of Gd_100−xB_x (x=0, 5, 10, 15, and 20 at%) alloys were prepared by melt spinning. With the decrease in Gd/B ratio, Curie temperature (T_C) remains constant at ∼293 K, and saturation magnetization, at 275 K, decreases from ∼100 to ∼78 emu/g. Negligible magnetic hysteresis was observed in these alloys. The peak value of magnetic entropy change, (−ΔS_M)_max, decreased from ∼9.9 J/kg K (0-5 T) and ∼5.5 J/kg K (0-2 T) for melt-spun Gd to ∼7.7 J/kg K (0-5 T) and ∼4.0 J/kg K (0-2 T), respectively for melt-spun Gd₈₅B₁₅ and Gd₈₀B₂₀ alloys. Similarly, the refrigeration capacity (q) decreased monotonously from ∼430 J/kg (0-5 T) for melt-spun Gd to ∼330 J/kg (0-5 T) for melt-spun Gd₈₀B₂₀ alloy. The near room temperature magnetocaloric properties of melt-spun Gd_100−xB_x (0≤x≤20) alloys were found to be comparable to few first-order transition based magnetic refrigerants.     

Magnetocaloric properties of (La0.67−xGdx)Sr0.33MnO3 polycrystalline nanoparticles

In this paper, magnetic property and magnetocaloric effect (MCE) in nanoparticles perovskite manganites of the type (La_0.67−xGd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) synthesized by using an amorphous molecular alloy as precursor have been reported. From the magnetic measurements as function of temperature and magnetic applied field, we have discovered that the Curie temperature (T_C) of the prepared samples is found to be strongly dependent on Gd content. The Curie temperature of samples is 358.4, 343.2, and 285.9 K for x=0.1, 0.15, and 0.2, respectively. A large magnetocaloric effect close to T_C has been observed with a maximum of magnetoentropy change in all the samples, ∣ΔS_M∣_max of 1.96 and 4.90 J/kg K at 2 and 5 T, respectively, for a substitution rate of 0.15. In addition, the maximum magnetic entropy change observed for samples with different concentration of Gd, exhibits a linear dependence with the applied high magnetic field. These results suggest that (La_0.67−x Gd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) compounds could be a suitable candidate as working substance in magnetic refrigeration near room temperature.     

Room temperature magnetic entropy change and magnetoresistance in La0.70(Ca0.30−xSrx)MnO3:Ag 10% (x=0.0−0.10)

The magnetic and magnetocaloric properties of polycrystalline La_0.70(Ca_0.30−xSr_x)MnO₃:Ag 10% manganite have been investigated. All compositions are crystallized in single phase orthorhombic Pbnm space group. Both, the insulator–metal transition temperature (T^IM) and Curie temperature (T_c) are observed at 298 K for x=0.10 composition. Though both T^IM and T_c are nearly unchanged with Ag addition, the MR is increased. The MR at 300 K is found to be as large as 31% with magnetic field change of 1 T, whereas it reaches up to 49% at magnetic field of 3 T for the La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample. The maximum entropy change (ΔS_Mmax) at near its T_c (300.5 K) is 7.6 J kg⁻¹ K⁻¹ upon the magnetic field change of 5 T. The La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample having good MR (31%^1 T, 49%^3 T) and reasonable change in magnetic entropy (7.6 J kg⁻¹.K⁻¹, 5 T) at 300 K can be a potential magnetic refrigerant material at ambient temperatures.     

Structural,magnetic and magnetocaloric properties of AMn1−xGaxO3 compounds with 0≤x≤0.2

Structural, magnetic and magnetocaloric properties of manganites series with the AMn_1−xGa_xO₃ (A=La_0.75Ca_0.08Sr_0.17 and x=0, 0.05, 0.1 and 0.2) composition have been investigated to shed light on Ga-doping influence. Solid-state reaction method was used for preparation. From XRD study, all samples are found single phase and crystallize in the orthorhombic structure with the Pnma space group. The variation of the magnetization M vs. temperature T, under an applied magnetic field of 0.05 T, reveals a ferromagnetic–paramagnetic transition for all samples. The experimental results indicate that T_C decreases from 336 to 135 K with increasing Ga substitution. Magnetocaloric effect (MCE) was estimated, in terms of isothermal magnetic entropy change (−ΔS_M), using the M(T, μ₀H) data and employing the thermodynamic Maxwell equation. The maximum entropy change and Relative Cooling Power (RCP) show non-monotonic behaviors with increasing the concentration of Gallium. In fact, the maximum value of ΔS_Mmaxof AMn_1−xGa_xO₃ for x=0.00 and 0.2 samples is found to be, respectively, 2.87 and 1.17 J/kg/K under an applied magnetic field change of 2 T. For the same applied magnetic field (μ₀H=2 T), the RCP values are found to vary between 97.58 and 89 J/kg.     

Magnetic properties of RNi5−xCux intermetallics

The magnetic properties have been studied for the series of RNi_5−xCu_x intermetallics with R=Y, La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm, Lu; x  ?2.5. Compositional dependences of magnetic susceptibility for the Pauli paramagnets (R=Y, La, Ce, Lu) and the Curie temperature for ferromagnets (R=Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm) have maximum at x=0.2–0.4$x=0.2–0.4$ and 1, respectively. The substitution of Cu for Ni is accompanied by decreasing spontaneous magnetic moment and increasing coercive force of all ferromagnetic RNi_5−xCu_x but GdNi_5−xCu_x. These results are explained in the frame of band magnetism, random local crystal field, and domain wall pinning theories.     

Kondo behaviour of the solid solution (Ce1−xLax)PtGa

The solid solution (Ce_1−xLa_x)PtGa has been studied through X-ray diffraction, magnetization (σ(B)), magnetic susceptibility (χ(T)), electrical resistivity (ρ(T)), magnetoresistivity (MR) and heat capacity (C_P(T)) measurements. The Néel temperature (T_N=3.3 K) for CePtGa is lowered upon La substitution as observed from χ(T) and ρ(T) measurements. The Kondo temperature T_K as calculated from MR measurements is comparable to T_N and also decreases with La substitution. The volume dependence of T_K is in accordance with the compressible Kondo lattice model and a Doniach diagram of the results is presented. C_P(T) measurements are presented for CePtGa, Ce_0.2La_0.8PtGa and LaPtGa and the results are discussed in terms of the electronic and magnetic properties. Other features of interest are anomalies in ρ(T) and C_P(T) due to crystalline electric field effects and metamagnetism as observed in σ(B) studies for samples with 0≤x≤ 0.3.     

Effects of Nb substitution for Zr on the phases,microstructure and magnetic properties of Co80Zr18−xNbxB2 melt-spun ribbons

The phases, microstructure, and magnetic properties of Co₈₀Zr_18−xNb_xB₂ (x=1, 2, 3, and 4) melt-spun ribbons were investigated. The small substitution of Nb for Zr in the Co–Zr–B melt-spun ribbons resulted in the improvement of magnetic properties, especially the coercivity. The main effect of added Nb on the coercovity of Co–Zr–Nb–B melt-spun ribbons, originated from modification of the grain size of Co₁₁Zr₂ phase. The coercivity of the Co–Zr–Nb–B melt-spun ribbons depends on the annealing temperature. The optimal magnetic properties of H_c=5.1 kOe, and (BH)_max=3.4 MGOe were obtained in the Co₈₀Zr₁₅Nb₃B₂ melt-spun ribbons annealed at 600 °C for 3 min.     

Influence of Ce doping on electrical and thermal properties of La0.7−xCexCa0.3MnO3 (0.0≤x≤0.7) manganites

The effect of Ce-doping on structural, magnetic, electrical and thermal transport properties in hole-doped manganites La_0.7−xCe_xCa_0.3MnO₃ (0.0≤x≤0.7) is investigated. The structure of the compounds was found to be crystallized into orthorhombically distorted perovskite structure. dc Susceptibility versus temperature curves reveal various magnetic transitions. For x≤0.3, ferromagnetic regions (FM) were identified and the magnetic transition temperature (T_C) was found to be decreasing systematically with increasing Ce concentration. The electrical resistivity ρ(T) separates the well-define metal-semiconducting transition (T_MS) for low Ce doping concentrations (0.0≤x≤0.3) consistent with magnetic transitions. For the samples with 0.4≤x≤0.7, ρ(T) curves display a semiconducting behavior in both the high temperature paramagnetic (PM) phase and low temperature FM or antiferromagnetic phase. The electron–phonon and electron–electron scattering processes govern the low temperature metallic behavior, whereas small polaron hopping model is found to be operative in PM phases for all samples. These results were broadly corroborated by thermal transport measurements for metallic samples (x≤0.3) in entire temperature range we investigated. The complicated temperature dependence of Seebeck coefficient (S) is an indication of electron–magnon scattering in the low temperature magnetically ordered regime. Specific heat measurements depict a broadened hump in the vicinity of T_C, indicating the existence of magnetic ordering and magnetic inhomogeneity in the samples. The observation of a significant difference between ρ(T) and S(T) activation energies and a positive slope in thermal conductivity κ(T) implying that the conduction of charge carriers were dominated by small polaron in PM state of these manganites.     

Anisotropy and FOMP in Tb3 (Fe28−xCox) V1.0 (x=0, 3 and 6) compounds

In this work, the structural and magnetic properties of Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) compounds have been investigated. The structural characterization of compounds by X-ray powder diffraction is an evidence for a monoclinic Nd₃(Fe, Ti)₂₉-type structure (A2/m space group). The refined lattice parameters a and b (but not c) and the unit cell volume V, obtained from the XRD data by the Rietveld method, are found to decrease with increasing Co concentration. The unit cell parameters behavior has been attributed to the smaller Co atoms and a preferential substitution of Fe by Co. The anisotropy field (H_a) as well as critical field (H_cr) was measured using the singular point detection (SPD) technique from 5 to 300 K in a pulsed magnetic field of up to 30 T. At T=5 K, a FOMP of type 2 was observed for all samples and persists at all temperatures up to 300 K. For sample x=0, H_cr=10.6 and 2.0 T at 5 and 300 K, respectively, is equal to that reported earlier. The occurrence of canting angles between the magnetic sublattices during the magnetization process instead of high-order anisotropy contributions (at room temperature are usually negligible) has been considered to explain the survival of the FOMP at room temperature. The anisotropy and critical fields behave differently for samples with x=0, 3 compared with x=6. The observed behavior has been related to the fact that the Co substitution for Fe takes place with a preferential entrance in the inequivalent crystallographic sites of the 3:29 structure. The contribution of the Tb-sublattice in the Tb₃(Fe, V)₂₉ compound with uniaxial anisotropy has been scaled from the anisotropy field measured on a Y₃(Fe, V)₂₉ single crystal with easy plane anisotropy.     

Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

Behavior of the irreversibility line in the new superconductor La1.5+xBa1.5+x−yCayCu3Oz

The irreversibility properties of high-T_c superconductors are of major importance for technological applications. For example, a high irreversibility magnetic field is a more desirable quality for a superconductor [1]. The irreversibility line in the H–T plane is constituted by experimental points, which divides the irreversible and reversible behavior of the magnetization. The irreversibility lines for series of La_1.5+xBa_1.5+x−yCa_yCu₃O_z polycrystalline samples with different doping were investigated. The samples were synthesized using the usual solid estate reaction method. Rietveld-type refinement of x-ray diffraction patterns permitted to determine the crystallization of material in a tetragonal structure. Curves of magnetization ZFC–FC for the system La_1.5+xBa_1.5+x−yCa_yCu₃O_z, were measured in magnetic fields of the 10–20,000 Oe, and allowed to obtain the values for the irreversibility and critical temperatures. The data of irreversibility temperature allowed demarcating the irreversibility line, T_irr(H). Two main lines are used for the interpretation of the irreversibility line: one of those which suppose that the vortexes are activated thermally and the other proposes that associated to T_irr a phase transition occurs. The irreversibility line is described by a power law. The obtained results allow concluding that in the system La_1.5+xBa_1.5+x−yCa_yCu₃O_z a characteristic bend of the Almeida–Thouless (AT) tendency is dominant for low fields and a bend Gabay–Toulouse (GT) behavior for high magnetic fields. This feature of the irreversibility line has been reported as a characteristic of granular superconductors and it corroborates the topological effects of vortexes mentioned by several authors 1 and 2.     

High field magnetization of Pr1-xGdxNi single crystals

Magnetization measurements were carried out on Pr_1−xGd_xNi single crystals for x=0.1, 0.2, 0.3 and 0.4 using pulsed magnetic fields up to 55 T and at 4.2 K. For the data observed along the c-axis there are clear indications of transitions, of the combined system of Pr and Gd moments, from a ferrimagnetic to a ferromagnetic state. The observed saturation magnetizations at 55 T and intermediate magnetizations at 1 T were well modeled assuming ferro- and ferri-magnetic structures, respectively.     

A study on magnetoelastic properties of Tb3 (Fe28−xCox) V1.0 (x=0, 3, 6) compounds

In this work, The magnetoelastic properties of polycrystalline samples of Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) intermetallic compounds are investigated by means of linear thermal expansion and magnetostriction measurements in the temperature range of 77–515 K under applied magnetic fields up to 1.5 T. The linear thermal expansion increases with the Co content. The well-defined anomalies observed in the linear thermal expansion coefficients for Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) compounds are associated with the magnetic ordering temperature for x=0 and spin reorientation temperatures for x=3, 6. Below transition temperatures, the value of the longitudinal magnetostriction (λ_Pa) at 1.6 T increases with Co content.     

Magnetotransport properties and magnetocaloric effect in La0.67Ca0.33Mn1−xTMxO3 (TM=Cu,Zn) perovskite manganites

The magnetic and transport properties of the perovskites La_0.67Ca_0.33Mn_1-xTM_xO₃ were found to be sufficiently changed with the substitution of Mn-sites by other 3d transition-metal cations (TM=Cu,Zn; x=0.15). The values of T_C, T_M−I, and T_CMR were surveyed when Mn was replaced by Cu and Zn. The magnetic field induced resistivity and magnetic entropy change of these samples showed abrupt changes near T_C (194.2 and 201.5 K for Cu and Zn-doped case respectively) and attained the highest values among the doped cases (up to 20% Cu). The maximum values (obtained at H=4 kOe) of magnetoresistance ratio (CMR) were 27.8%, and 24.5% and of magnetic entropy change (−ΔS_M) were 3.9 and 3.2 J/kg K for Cu and Zn-doped, respectively.     

The magnetic entropy changes in Gd1−xBx alloys

A series of Gd_(1−x)B_x alloys have been prepared by arc melting method. After introducing small quantity of B atom in Gd, the Curie temperature of these alloys increase while the magnetic entropy changes are almost same as that of Gd. The refrigerant capacities of these alloys are also greater than that of Gd. These results suggest that Gd_(1−x)B_x alloys may be utilized as refrigerant in household magnetic refrigeration.     

Magnetocaloric effect in high Ni content Ni52Mn48−xInx alloys under low field change

Ni-rich Heusler alloys Ni₅₂Mn_48−xIn_x (x=15.5, 16 and 16.5) were prepared by the arc melting method. X-ray diffraction analysis revealed that the martensite has orthorhombic structure (S.G. Pmm2) at room temperature. The only alloy with x=15.5 has structural transmission from martensite to austenite without any magnetic transmission. The temperature dependence and the field dependence of the magnetization measurement indicated that the magnetization increased with the decreasing of the concerntration of Mn. The lesser the Mn atoms located in the In atom sites, the weaker the total AFM interaction in the system. Giant entropy changes ΔS_M(T, H) were found in Ni₅₂Mn_48−xIn_x alloys with the maximum ΔS_M value of 22.3 J kg K for the sample with x=16.5 at 270 K under the magnetic field change of 1.5 T.     

Magnetocaloric effects in (Gd1−xTbx)Co2

The structures and magnetocaloric effects of (Gd_1−xTb_x)Co₂ (x=0, 0.25, 0.4, 0.5, 0.6, 0.7, 0.8, and 1) pseudobinary compounds were investigated by X-ray powder diffraction and magnetic properties measurement. The results show that the T_c of the alloy is near room temperature when X=0.6. The magnetic entropy changes of the compounds increase from 1.7 to 3.6 J/kg K with increasing the content of Tb under an applied field up to 2 T. All the compounds exhibit second order magnetic change. As a result, the values of their ΔS_M are lower than that of some large magnetocaloric effect materials.     

Structural and electrical transport properties of ZnxFe3−xO4 thin film deposited on Si (1 1 1) by pulsed-laser deposition

Polycrystalline thin films of Fe_3−xZn_xO₄ (x = 0.0, 0.01 and 0.02) were prepared by pulsed-laser deposition technique on Si (1 1 1) substrate. X-ray diffraction studies of parent as well as Zn doped magnetite show the spinel cubic structure of film with (1 1 1) orientation. The order–disorder transition temperature for Fe₃O₄ thin film with thickness of 150 nm are at 123 K (Si). Zn doping leads to enhancement of resistivity by Zn²⁺ substitution originates from a decrease of the carrier concentration, which do not show the Verwey transition. The Raman spectra for parent Fe₃O₄ on Si (1 1 1) substrate shows all Raman active modes for thin films at energies of T_2g¹, T_2g³, T_2g², and A_1g at 193, 304, 531 and 668 cm⁻¹. It is noticed that the frequency positions of the strongest A_1g mode are at 668.3 cm⁻¹, for all parent Fe₃O₄ thin film shifted at lower wave number as 663.7 for Fe_2.98Zn_0.02O₄ thin film on Si (1 1 1) substrate. The integral intensity at 668 cm⁻¹ increased significantly with decreasing doping concentration and highest for the parent sample, which is due to residual stress stored in the surface.     

Magnetic phase diagram of GdAg1−xZnx

The magnetic phase diagram of GdAg_1?xZn_x, an intermetallic solid solution of an antiferromagnet (GdAg: T_N = 136 K) and a ferromagnet (GdZn: T_C = 269 K), has been elaborated from magnetization measurements. The antiferromagnetic phase boundary T_N(x) first passes a broad maximum meeting the ferromagnetic phase boundary T_C(x) at x₁ = 0.575 and T₁ = 72 K, where four phases coexist. On approaching (x₁, T₁) along T_N(x) the magnetization phenomena vanish. At x₁ the phase transition still has ferromagnetic appearance but proceeds into a state without spontaneous magnetic moment. Two different ferromagnetic phases (F₁, F₂) and one ferrimagnetic phase (F₃) occur in the composition intervals 0.69 < x₁ <1, and 0.61 <x₂ < 0.69 and 0.51 < x₃ < 0.61. All phase transitions seem to be of second order except th e F₁?F₂ one at x = 0.69 which is of first order. This phase line meets the paramagnetic to ferromagnetic phase boundary T_C(x) in a multicritical point with the coordinates x_m = 0.69, T_m = 123 K.Six further mixed magnetic phases, M_{1, 2, ..., 6}, are observed between x = 0.33 and 0.6 below the antiferromagnetic branch and exhibit irreversible thermodynamic properties, such as hysteresis, below about 40 K.Assuming local magnetic interactions only between nearest and next-nearest Gd neighbours, the T_N(x) and T_C(x) phase boundaries can be described fairly well by a simple model calculation using different exchange parameters for a few relevant distributions of Ag and Zn atoms.     

Magnetic/structural diagram, chemical composition-dependent magnetocaloric effect in self-doped antipervoskite compounds Sn1−xCMn3+x (0≤x≤0.40)

The effects of Mn substitutions on the crystal structure, magnetic properties, and magnetocaloric effect (MCE) of antiperovskite Sn_1−xCMn_3+x (0≤x≤0.40) have been investigated detailedly. Both the Curie temperature (T_C) and the magnetizations at 40 kOe decrease with increasing x firstly for x≤0.10, and then increase with increasing x further. The type of magnetic transition changes from first-order to second-order around x=0.10 with increasing x. Chemical composition-dependent MCE is also studied around T_C. With increasing x, the maximal magnetic entropy changes decrease and the magnetic phase transitions broaden. Accordingly, the relative cooling power (RCP) increases with increasing x, reaching the largest values of ∼0.56 J/cm³ (∼75 J/kg) and ∼1.66 J/cm³ (∼221 J/kg) with the magnetic changes of 20 kOe and 48 kOe, respectively. Considering the large RCP, inexpensive, and innoxious raw materials, these serial samples Sn_1−xCMn_3+x are suggested to be potential room-temperature magnetic refrigerant materials.