Room temperature magnetic entropy change and magnetoresistance in La0.70(Ca0.30−xSrx)MnO3:Ag 10% (x=0.0−0.10)

The magnetic and magnetocaloric properties of polycrystalline La_0.70(Ca_0.30−xSr_x)MnO₃:Ag 10% manganite have been investigated. All compositions are crystallized in single phase orthorhombic Pbnm space group. Both, the insulator–metal transition temperature (T^IM) and Curie temperature (T_c) are observed at 298 K for x=0.10 composition. Though both T^IM and T_c are nearly unchanged with Ag addition, the MR is increased. The MR at 300 K is found to be as large as 31% with magnetic field change of 1 T, whereas it reaches up to 49% at magnetic field of 3 T for the La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample. The maximum entropy change (ΔS_Mmax) at near its T_c (300.5 K) is 7.6 J kg⁻¹ K⁻¹ upon the magnetic field change of 5 T. The La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample having good MR (31%^1 T, 49%^3 T) and reasonable change in magnetic entropy (7.6 J kg⁻¹.K⁻¹, 5 T) at 300 K can be a potential magnetic refrigerant material at ambient temperatures.