Preparation of temperature‐responsive polymer gels physically immobilizing core‐shell type bioconjugates

Poly(N‐isopropylacrylamide) (PNIPAAm) gels are temperature‐responsive polymer gels; and were prepared by redox polymerization of N‐isopropylacrylamide in the presence of N,N′‐methylenebisacrylamide as a crosslinking reagent and core‐shell type bioconjugates, which were core‐crosslinked polyion complex micelles formed from the mixture of bovine pancreas trypsin and poly(ethylene glycol)‐block‐poly(α,β‐aspartic acid). The phase transition temperature of PNIPAAm gels was no change with physically immobilization of bioconjugates. Also, the enzymatic activity of bioconjugates was essentially maintained even in PNIPAAm gels, although enzymatic reaction rate was apparently controlled by temperature, i.e., by the degree of swelling of PNIPAAm gels. Further, the control of enzymatic reaction synchronizing the phase transition of PNIPAAm gels immobilized bioconjugates. PNIPAAm gels could immobilize core‐shell type bioconjugates, and were successfully prepared without interfering with the properties of temperature‐responsive polymer gels and the bionanoreactor. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5942–5948, 2007     

Multi‐responsive methylcellulose/Fe‐alginate‐g‐PVA/PVA/Fe3O4 microgels for immobilizing enzyme

To take advantage of the respective character of methylcellulose (MC), poly(vinyl alcohol) (PVA), and alginate, novel physically cross‐linked methylcellulose/Fe‐alginate‐g‐PVA/PVA (MC/Fe‐Alg‐g‐PVA/PVA) microgels were prepared by emulsification/thermal gelation/freezing–thawing/ionic cross‐linking technique. Subsequently, some ferrous ions bound in the microgels were transformed into magnetite via in situ self oxidation. A model enzyme α‐amylase was immobilized into microgels by direct adsorption. The release behavior of α‐amylase indicated that the obtained complex microgels were magnetic‐, temperature‐, and pH‐ triple sensitive. Copyright © 2010 John Wiley & Sons, Ltd.     

Interfacial layers of stimuli-responsive poly-(N-isopropylacrylamide-co-methacrylicacid) (PNIPAM-co-MAA) microgels characterized by interfacial rheology and compression isotherms

Stimuli-sensitive emulsions stabilized by microgel particles consisting of poly-(N-isopropylacrylamide-co-methacrylicacid) (PNIPAM-co-MAA) and being responsive to both pH and temperature have been investigated with respect to the visco-elastic properties of the interfacial layer. Properties of the interfacial layer were probed by means of shear and dilatational rheology as well as by compression isotherms and are related to the microgel packing at the interface as visualized by cryogenic scanning electron microscopy. The corresponding pH dependent emulsion stability is strongly correlated with the visco-elastic properties of the microgel covered oil-water interface. At high pH when the microgels are charged, a structure of partially interconnected microgels is found that provides elastic, soft gel-like interfaces. At low pH, however, the uncharged microgels are densely packed and the interface is rather brittle. Obviously, these pH dependent visco-elastic properties of the microgel layer at the oil-water interface play a determining role in the stability of emulsion droplets and allow us to prepare very stable emulsions when the microgels are charged and to break the emulsion by changing the pH.     

Nanoscopic Visualization of Cross‐Linking Density in Polymer Networks with Diarylethene Photoswitches

The in situ nanoscopic imaging of soft matter polymer structures is of importance to gain knowledge of the relationship between structure, properties, and functionality on the nanoscopic scale. Cross‐linking of polymer chains effects the viscoelastic properties of gels. The correlation of mechanical properties with the distribution and amount of cross‐linkers is relevant for applications and for a detailed understanding of polymers on the molecular scale. We introduce a super‐resolution fluorescence‐microscopy‐based method for visualizing and quantifying cross‐linker points in polymer systems. A novel diarylethene‐based photoswitch with a highly fluorescent closed and a non‐fluorescent open form is used as a photoswitchable cross‐linker in a polymer network. As an example for its capability to nanoscopically visualize cross‐linking, we investigate pNIPAM microgels as a system known with variations in internal cross‐linking density.     

Metal‐conducting polymer interface studied by Kelvin probe microscopy: Au and Al on poly(3‐octyl‐thiophene)

In this work, we report a Kelvin probe microscopy investigation on the structural and electronic properties of gold and aluminum thin films evaporated on poly(3‐octyl‐thiophene) films. Our experimental setup allows us to perform scanning force microscopy (SFM) studies of the same area even if the sample is taken out of the SFM system for different processes (Au and Al evaporation). This allows a detailed study of the effect of adsorbed metal particles on the morphology and electrical properties of polymer thin films at the nanoscale. We found different behavior for both metals in morphology and electrical properties at the interface. These results can contribute to explain what happens at the metal–polymer interface of the devices when the metal contacts are grown. Thereby the observed nanoscale structural changes can be correlated with the overall performance of the fabricated devices. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 1083–1093     

Structure and properties of cellulose/poly(N‐isopropylacrylamide) hydrogels prepared by IPN strategy

Interpenetrating polymer network (IPN) strategy was developed to fabricate novel hydrogels composed of cellulose and poly(N‐isopropylacrylamide) (PNIPAAm) with high mechanical strength and adjustable thermosensitivity. Cellulose hydrogels were prepared by chemically cross‐linking cellulose in NaOH/urea aqueous solution, which were employed as the first network. The second network was subsequently obtained by in situ polymerization/cross‐linking of N‐isopropylacrylamide in the cellulose hydrogels. The results from FTIR and solid ¹³C NMR indicated that the two networks co‐existed in the IPN hydrogels, which exhibited uniform porous structure, as a result of good compatibility. The mechanical and swelling properties of IPN hydrogels were strongly dependent on the weight ratio of two networks. Their temperature‐sensitive behaviors and deswelling kinetics were also discussed. This work created double network hydrogels, which combined the advantages of natural polymer and synthesized PNIPAAm collectively in one system, leading to the controllable temperature response and improvement in the physical properties. Copyright © 2009 John Wiley & Sons, Ltd.     

Polypyrrole/poly(N‐isopropylacrylamide‐co‐acrylic acid) thermosensitive and electrically conductive composite microgels

The electrically conductive polypyrrole/dodecylbenzene sulfonic acid/poly(N‐isopropylacrylamide‐co‐acrylic acid) (PPy/DBSA/poly(NIPAAm‐co‐AA)) composite microgels were synthesized by a chemical oxidation of pyrrole in the presence of DBSA as the primary dopant, and poly(NIPAAm‐co‐AA) microgels as the polymeric codopant and template, in which APS was used as the oxidant. It was proposed to prepare “intelligent” polymer microgel particles containing both thermosensitive and electrically conducting properties. The polymerization of pyrrole took place directly inside the microgel networks, leading to formation of composite microgels and the morphology was observed by transmission electron microscope. PPy particles interacted strongly with microgels, as the acid groups of microgels acted as the polymeric codopant. The composite microgels thus formed showed electrically conducting behavior dependent on humidity and temperature. At temperatures lower than lower critical solution temperature, the conductivity decreased with increasing the humidity and a small hysteresis phenomenon was observed. The hysteresis became indistinct when temperature was near volume phase transition temperature. However, after the treatment of high temperature and high humidity, the conductivity increased surprisingly due to the structure reorganization inside the composite microgels. The distinctive functionality of the PPy composite microgels was expected to be utilized in many attractive applications. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1648–1659, 2006     

Synthesis and characterization of stimuli‐responsive porous/hollow nanoparticles by self‐assembly of chitosan‐based graft copolymers and application in drug release

In this research, stimuli‐responsive porous/hollow nanoparticles were prepared by the self‐assembly method. First, chitosan‐graft‐poly(N‐isopropylacrylamide) (CS‐g‐PNIPAAm) copolymers were synthesized through polymerization of N‐isopropylacrylamide (NIPAAm) monomer in the presence of chitosan (CS) solution using ceric ammounium nitrate as the initiator. Then, the CS‐g‐PNIPAAm copolymers were dissolved in the acetic acid aqueous solution and heated to 40 °C to induce their self‐assembly. After CS‐g‐PNIPAAm assembled to form micelles, a cross‐linking agent was used to reinforce the structure to form nanoparticles. The molecular weight of grafted PNIPAAm on CS chains was changed to investigate its effect on the structure, morphology, thermo‐, and pH‐responsive properties of the nanoparticles. TEM images showed that a porous or hollow structure in the interior of nanoparticles was developed, depending on the medium temperature. The synthesized nanoparticles carried positive charges on the surface and exhibited stimuli‐responsive properties, and their mean diameter thus could be manipulated by changing the pH value and temperature of the environment. The nanoparticles showed a continuous release of the encapsulated doxycycline hyclate up to 10 days during an in vitro release experiment. These porous/hollow particles with environmentally sensitive properties are expected to be used in hydrophilic drug delivery system. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2377–2387, 2010     

A Way to Prepare Core‐Shell Biocompatible Polymeric Nano‐Particles from Gelatin and Acrylic Acid

Narrowly distributed core‐shell nano‐particles at relatively high concentration (30 mg/mL) were prepared via in situ polymerization of acrylic acid in an aqueous solution of biocompatible gelatin. These polymeric nano‐particles, in aqueous solution, had cores mainly comprised of an insoluble inter‐polymer complex of poly(acrylic acid, PAA) and gelatin and shells comprised of soluble gelatin (denoted as gelatin/PAA nano‐particles). Dynamic light scattering and electrophoretic light scattering techniques were used to trace the in situ polymerization process. The structure of the gelatin/PAA nano‐particle was further locked‐in via shell crosslinking; i.e., the reaction between glutaraldehyde and gelatin. Scanning force microscopy (SFM) was used to observe the morphologies of the particles before and after cross‐linking. Furthermore, the pH responsive behaviors of the gelatin/PAA nano‐particles before and after shell crosslinking were studied.     

A Novel Route to the Preparation of Poly(N‐isopropylacrylamide) Microgels by Using Inorganic Clay as a Cross‐Linker

Adopting inorganic clay (hectorite) and MBA as physical and chemical cross‐linking agents, respectively, PNIPAM microgels were synthesized by SFEP. The chemical structure and morphology of the microgels were confirmed by FTIR, WXRD, and SEM. The temperature‐sensitivity of the microgels was investigated by DLS and UV spectrophotometers. The results inferred that clay platelets dispersed in an aqueous medium were fully exfoliated and could act as a kind of multifunctional cross‐linking agent and significantly reduced the hydrodynamic diameters of the microgels. In fact, the hydrodynamic diameters of the PNIPAM microgels with clay as cross‐linker ranged from 154 to 322 nm which was much smaller than that using MBA as chemical cross‐linker, the later was in the range of 284–808 nm on heating from 5 to 50 °C.

     

Preparation and properties of novel fluorosilicone thermoplastic vulcanizate with cross‐linking–controlled core‐shell structure

A new fluorosilicone thermoplastic vulcanizate (TPV) composed of poly(vinylidene fluoride) (PVDF), silicone rubber (SR), and fluororubber (FKM) was successfully prepared through dynamic vulcanization. The morphological structure of the TPVs had core‐shell elastomer particles dispersed in a continuous PVDF matrix. Furthermore, the cross‐linking of core‐shell structure was controlled by adopting different curing agent. The effect of cross‐linking–controlled core‐shell structure on the morphology, crystallization behavior, stress relaxation test, solvent‐resistant properties of the obtained TPVs were investigated. It was found that the shell cross‐link had a significant influence on the crystallinity of the PVDF phase. The core‐shell bicross‐linked TPV was found to provide the lowest rate of relaxation. An obvious stress softening phenomenon was observed in the uniaxial loading‐unloading cycles in tension. The bicross‐linked TPV had good solvent resistant properties. The tensile strength of the bicross‐linked TPV was still 12 MPa even after immersed in butyl acetate for 48 hours.     

Fine tuning of SAP properties via epoxy‐silane surface modification

Using 3‐[(2,3‐epoxypropoxy)‐propyl]‐trimethoxysilane as a surface modifier, superabsorbent polymers with improved gel strength in their swollen state and saline absorbency under load are synthesized. The products are characterized using attenuated total reflectance–Fourier transform infrared spectroscopy (ATR–FTIR), rheometry, scanning electron microscopy–energy dispersive X‐ray analysis, contact angle, thermogravimetric analysis, water absorbency and gel content. The temperature and the duration effect of the surface‐treatment process on residual monomer content are also investigated by high performance liquid chromatography. The gel strength (as shown by storage modulus) and absorbency under load are improved up to 3500–4000 Pa, and 30–40 g/g, respectively. It is suggested that the surface of the superabsorbent polymer particles has been modified by two mechanisms: i.e. interpenetrating polymer network and cross‐linking. Moreover, the surface modification has enhanced thermo‐stability and prohibited undesirable gel blockage. Depending on the post‐treatment method used, the wetting behavior of particles is also altered. Copyright © 2017 John Wiley & Sons, Ltd.     

Facile preparation of monodisperse hollow cross‐linked chitosan microspheres

We have successfully prepared biocompatible and biodegradable hollow microspheres using carboxyl‐functionalized polystyrene particles as core template and the chitosan cross‐linked with glutaraldehyde as the shell. The monodisperse carboxyl‐functionalized polystyrene particles were made by emulsifier‐free emulsion polymerization. The structure, morphology, and constitution of the carboxyl‐functionalized polystyrene particles were characterized by FTIR, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X‐ray photoelectron spectroscopy (XPS). The structure, morphology, and formation process of the hollow cross‐linked chitosan microspheres were characterized by FTIR, SEM, and TEM. The results revealed that the latex particles were removed by exposed to solvent and the microspheres exhibited the hollow structure. This work confirmed that the hollow microspheres were accomplished by fabricating on the basis of chemical cross‐linking on the surface of the carboxyl‐functionalized polystyrene particles and then removing off the cores of particles. Moreover, with the increase of carboxyl‐functionalization degree at the surface of latexes and the increase of cross‐linking period, the thicker and firmer monodisperse hollow microspheres were obtained. In addition, a water‐soluble drug, salicylic acid, encapsulated in the microcapsules slowly released at pH 1.2. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 228–237, 2008     

N‐vinylcaprolactam‐based microgels: Synthesis and characterization

Poly(N‐vinylcaprolactam) (PVCL) is well known for its thermoresponsive behavior in aqueous solutions. PVCL combines useful and important properties; it is biocompatible polymer with the phase transition in the region of physiological temperature (32–38 °C). This combination of properties allows consideration of PVCL as a material for design biomedical devices and use in drug delivery systems. In this work, PVCL based temperature‐sensitive crosslinked particles (microgels) were synthesized in a batch reactor to analyze the effect of the crosslinker, initiator, surfactant, temperature, and VCL concentration on polymerization process and final microgels characteristics. The mean particle diameters at different temperatures and the volume phase‐transition temperature of the final product were analyzed. To obtain information about the inner structure of microgel particles, semicontinuous polymerizations were carried out and the evolution of the hydrodynamic average particle diameters at different temperatures of the microgel synthesized was investigated. In the case of microgel particles obtained in a batch reactor the size and the swelling‐de‐swelling behavior as a function of the temperature of the medium can be tuned by modulating the reaction variables. When the microgel particles were synthesized in a semibatch reactor different swelling‐de‐swelling behaviors were observed depending on particles inner structure. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2510–2524, 2008     

Control of thermal cross‐linking reactions and the degree of crystallinity of syndiotactic 1,2‐polybutadiene

Thermal stability, crystallization, morphological development, subsequently melting, and crystallinity control of a syndiotactic 1,2‐polybutadiene sample were carefully carried out by thermogravimetry (TGA), polarized optical microscopy (POM), differential scanning calorimetry (DSC), temperature‐modulated differential scanning calorimetry (TMDSC), and wide‐angle X‐ray diffraction (WAXD), respectively. The experiments indicate that thermal cross‐linking reaction rates under nitrogen protection and in air are different for this polymer at temperature above 155 °C. Under nitrogen protection, the thermal cross‐linking reaction rate is delayed and the mechanism of melt crystallization obtained from the DSC results is in good accordance with that from POM observation. TMDSC results indicate that melting–recrystallization–melting model is more proper to explain the double melting events of this sample. At the same time, the evolution of the degree of crystallinity as the function of the time was investigated by WAXD profiles for the samples firstly crystallized at 145 °C for 1 h and then kept at 163 °C mediated between the temperatures of the double peaks. It shows that as prolonging the annealing time at 163 °C thermal cross‐linking reactions possibly occur, leading to gradual reduction of the apparent crystallite sizes, evaluated by Scherrer equation and the degree of crystallinity. The changing sequence of the relative intensity of the stronger four diffraction peaks with time due to thermal cross‐linking reactions is (111)/(201) > (210) > (010) > (200)/(110). © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2885–2897, 2005     

Catalytic reduction of 4‐nitrophenol using silver nanoparticles‐engineered poly(N‐isopropylacrylamide‐co‐acrylamide) hybrid microgels

Nearly monodisperse poly(N ‐isopropylacrylamide‐co ‐acrylamide) [P(NIPAM‐co‐AAm)] microgels were synthesized using precipitation polymerization in aqueous medium. These microgels were used as microreactors to fabricate silver nanoparticles by chemical reduction of silver ions inside the polymer network. The pure and hybrid microgels were characterized using Fourier transform infrared and UV–visible spectroscopies, dynamic light scattering, X‐ray diffraction, thermogravimetric analysis, differential scanning calorimetry and transmission electron microscopy. Results revealed that spherical silver nanoparticles having diameter of 10–20 nm were successfully fabricated in the poly(N ‐isopropylacrylamide‐co ‐acrylamide) microgels with hydrodynamic diameter of 250 ± 50 nm. The uniformly loaded silver nanoparticles were found to be stable for long time due to donor–acceptor interaction between amide groups of polymer network and silver nanoparticles. Catalytic activity of the hybrid system was tested by choosing the catalytic reduction of 4‐nitrophenol as a model reaction under various conditions of catalyst dose and concentration of NaBH₄ at room temperature in aqueous medium to explore the catalytic process. The progress of the reaction was monitored using UV–visible spectrophotometry. The pseudo first‐order kinetic model was employed to evaluate the apparent rate constant of the reaction. It was found that the apparent rate constant increased with increasing catalyst dose due to an increase of surface area as a result of an increase in the number of nanoparticles.     

Novel synthesis of nano‐calcium carbonate (CaCO3)/polystyrene (PS) core–shell nanoparticles by atomized microemulsion technique and its effect on properties of polypropylene (PP) composites

Calcium carbonate (CaCO₃)/polystyrene (PS) nanoparticles (<100 nm) with core–shell structure were synthesized by atomized microemulsion technique. The polymer chains were anchored onto the surface of nano‐CaCO₃ through triethoxyvinyl silane (TEVS) as a coupling agent. Ammonium persulfate (APS), sodium dodecyl sulfate (SDS) and n‐pentanol were used as initiator, surfactant, and cosurfactant, respectively. Polymerization mechanism of core–shell latex particles was discussed. Encapsulation of nano‐CaCO₃ by PS was confirmed by using transmission electron microscope (TEM). Grafting percentage of core–shell particles was investigated by Thermogravimetric Analyzer (TGA). Nano‐CaCO₃/PS core–shell particles were characterized by Fourier transform infrared (FTIR) spectrophotometer and differential scanning calorimeter (DSC). The results of FTIR revealed existence of a strong interaction at the interface of nano‐CaCO₃ particle and PS, which implies that the polymer chains were successfully grafted onto the surface of nano‐CaCO₃ particle through the link of the coupling agent. In addition, TGA and DSC results indicated an enhancement of thermal stability of core–shell materials compared with the pure nano‐PS. Nano‐CaCO₃/PS particles were blended with polypropylene (PP) matrix on Brabender Plastograph by melt process with different wt% of loading (i.e. 0.1–1 wt%). The interfacial adhesion between nano‐CaCO₃ particles and PP matrix was significantly improved when the nano‐CaCO3 particles were grafted with PS, which led to increased thermal, rheological, and mechanical properties of (nano‐CaCO₃/PS)/PP composites. Scanning electron microscope (SEM) and atomic force microscope (AFM) images showed a perfect dispersion of the nano‐CaCO₃ particles in PP matrix. Copyright © 2011 John Wiley & Sons, Ltd.     

Ultrafine hydrogel fibers with dual temperature‐ and pH‐responsive swelling behaviors

Ultrafine hydrogel fibers that were responsive to both temperature and pH signals were prepared through the electrospinning of poly(N‐isopropylacrylamide) (PNIPAAm) and poly(acrylic acid) mixtures in dimethylformamide. Both the diameters (700 nm to 1.2 μm) and packing of the fibers could be controlled through changes in the polymer compositions and PNIPAAm molecular weights. These fibers were rendered water‐insoluble by the addition of either Na₂HPO₄ or poly(vinyl alcohol) (PVA) to the solution, followed by the heat curing of the fibers. The fibers crosslinked with Na₂HPO₄ swelled to 30–120 times in water; this was significantly higher than the swelling of those crosslinked with PVA. The PVA‐crosslinked hydrogel fibers, however, exhibited faster swelling kinetics; that is, they reached equilibrium swelling in less than 5 min at 25 °C. They were also more stable after 1 week of water exposure; that is, they lost less mass and retained their fibrous form better. All the hydrogel fibers showed a drastic increase in the swelling between pH 4 and 5. The PVA‐crosslinked hydrogel fibers exhibited distinct temperature‐responsive phase‐transition behavior of PNIPAAm, whereas the Na₂HPO₄‐crosslinked hydrogel fibers showed altered two‐stage phase transitions that reflected side‐chain modification of PNIPAAm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 6331–6339, 2004     

Polystyrene‐Core–Silica‐Shell Hybrid Particles Containing Gold and Magnetic Nanoparticles

Polystyrene‐core–silica‐shell hybrid particles were synthesized by combining the self‐assembly of nanoparticles and the polymer with a silica coating strategy. The core–shell hybrid particles are composed of gold‐nanoparticle‐decorated polystyrene (PS‐AuNP) colloids as the core and silica particles as the shell. PS‐AuNP colloids were generated by the self‐assembly of the PS‐grafted AuNPs. The silica coating improved the thermal stability and dispersibility of the AuNPs. By removing the “free” PS of the core, hollow particles with a hydrophobic cage having a AuNP corona and an inert silica shell were obtained. Also, Fe₃O₄ nanoparticles were encapsulated in the core, which resulted in magnetic core–shell hybrid particles by the same strategy. These particles have potential applications in biomolecular separation and high‐temperature catalysis and as nanoreactors.     

Synthesis and characterization of poly(styrene‐maleic anhydride)‐montmorillonite nanocomposite

Poly(styrene‐maleic anhydride)‐montmorillonite nanocomposites were prepared by intercalation of layered montmorillonite with the polymer ions. Synthetic approaches including polymerization and phosphonium salt formation have been used for polymer intercalation and dispersion of the host layers in the polymer matrix. The ratio of the mineral in the composites ranged 30–50%. Wide‐angle X‐ray diffraction (WAXD) disclosed that the d₍₀₀₁₎ spacing between the internal lamellar surface were only expanding to about 13 and 15 Å according to the type of phosphonium salt suggesting packing of polymer molecules between the layers. Examination of these materials by scanning and transmission electron microscopy showed spherical nano size particles of average diameter, 350 nm. Copyright © 2002 John Wiley & Sons, Ltd.