Quasi-one-dimensional structures on the Si(1 1 1) surface induced by Ba adsorption

Ba-induced quasi-one-dimensional reconstructions of the Si(1 1 1) surface have been investigated by low energy electron diffraction (LEED) and scanning tunneling microscopy (STM). While the 3 × ‘2’ surface shows double-periodicity along the stripes in STM images consistent with half-order streaks observed in LEED patterns, no sign of the double-periodicity along the chain direction was detected for the 5 × 1 surface. The 5× stripes in STM images show internal structures with multiple rows. The two rows comprising the boundaries of a 5× stripe in the filled-state STM image are found to have 3a × √3/2 spacing across the stripe. The observation of the successive 3× and 2× spacings between the boundary rows supports a structural model proposed for the Ba-induced 5 × 1 Si reconstruction composed of honeycomb chains and Seiwatz chains. The highest coverage 2 × 8 surface does not reveal a quasi-1D row structure in STM images.     

Effect of Pb adatom flux rate on adlayer coverage for Stranski-Krastanov growth mode on Si(1 1 1)7 × 7 surface

Lead (Pb) has been a prototypical system to study diffusion and reconstruction of silicon surfaces. However, there is a discrepancy in literature regarding the critical coverage at which island formation takes place in the Stranski-Krastanov (S-K) mode. We address this issue by studying the initial stages of evolution of the Pb/Si(1 1 1)7 × 7 system by careful experiments in ultra-high vacuum with in situ characterization by auger electron spectroscopy, electron energy loss spectroscopy and low-energy electron diffraction. We have adsorbed Pb onto clean Si(1 1 1 )7 × 7 surface with sub-monolayer control at different flux rates of 0.05 ML/min, 0.14 ML/min and 0.22 ML/min, at room temperature. The results clearly show that the coverage of the Pb adlayer before the onset of 3D Pb islands in the S-K mode depends on the flux rates. LEED results show the persistence of the (7 × 7) substrate reconstruction until the onset of the island formation, while EELS results do not show any intermixing at the interface. This suggests that the flux rates influence the kinetics of growth and the passivation of dangling bonds to result in the observed rate-dependent adlayer coverages.     

Reconstruction and de-reconstruction of the Ir(1 0 0) surface and ultrathin Fe/Ir(1 0 0) films

The structure, energetics and magnetic properties of the quasihexagonal reconstruction of the Ir(1 0 0) surface and nanostructures formed by Fe atoms on this surface have been investigated using first-principles density functional theory with generalized gradient corrections. We find the reconstructed (1 × 5) surface to be 0.10 eV/(1 × 1) area lower in energy than the unreconstructed surface and we demonstrate that first-principles calculations can achieve quantitative agreement with experiment even for such long-period and deep-going reconstructions. For Fe coverage of 0.4 monolayers (ML) we have studied the stripe-like structure with biatomic Fe rows placed in the troughs of the (1 × 5)-reconstructed surface. Results of nonmagnetic calculations agree well with the structure inferred from STM data. Higher Fe coverages lead to a de-reconstruction of the Ir substrate. At 0.8 ML coverage a surface compound with composition Fe₄Ir is formed, which shows an appreciable buckling. In this case, a ferromagnetic calculation leads to good agreement with the low-temperature LEED data. We predict that the (1 × 5) periodicity of the mixed interface layer will persist also in thicker films with a pure Fe surface. Films with 1-4 ML Fe are predicted to be tetragonally distorted and ferromagnetic, with an axial ratio corresponding well to an elastic distortion of the Fe lattice.     

K-induced surface structural change of Si(1 1 1)-7 × 7 probed by second-harmonic generation

The growth of thin K films on Si(1 1 1)-7 × 7 has been investigated by selecting the input and output polarizations of second-harmonic generation (SHG) at room temperature (RT) and at an elevated temperature of 350 °C. The SH intensity at 350 °C showed a monotonic increase with K coverages up to a saturated level, where low energy electron diffraction (LEED) showed a 3 × 1 reconstructed structure. The additional deposition onto the K-saturated surface at 350 °C showed only a marginal change in the SH intensity. These variations are different from the multi-component variations up to 1 ML and orders of magnitude increase due to excitation of plasmons in the multilayers at RT. The variations of SHG during desorption of K at 350 °C showed a two-step decay with a marked shoulder which most likely corresponds to the saturation K coverage of the Si(1 1 1)-3 × 1-K surface. The dominant tensor elements contributing to SHG are also identified for each surface.     

Oxidation of Pt(1 0 0)-hex-R0.7° by gas-phase oxygen atoms

We utilized temperature programmed desorption (TPD), X-ray photoelectron spectroscopy (XPS), electron energy loss spectroscopy (ELS), and low energy electron diffraction (LEED) to investigate the oxidation of Pt(1 0 0)-hex-R0.7° at 450 K. Using an oxygen atom beam, we generated atomic oxygen coverages as high as 3.6 ML (monolayers) on Pt(1 0 0) in ultrahigh vacuum (UHV), almost 6 times the maximum coverage obtainable by dissociatively adsorbing O₂. The results show that oxidation occurs through the development of several chemisorbed phases prior to oxide growth above about 1 ML. A weakly bound oxygen state that populates as the coverage increases from approximately 0.50 ML to 1 ML appears to serve as a necessary precursor to Pt oxide growth. We find that increasing the coverage above about 1 ML causes Pt oxide particle growth and significant surface disordering. Decomposition of the Pt oxide particles produces explosive O₂ desorption characterized by a shift of the primary TPD feature to higher temperatures and a dramatic increase in the maximum desorption rate with increasing coverage. Based on thermodynamic considerations, we show that the thermal stability of the surface Pt oxide on Pt single crystal surfaces significantly exceeds that of bulk PtO₂. Furthermore, we attribute the high stability and the acceleratory decomposition rates of the surface oxide to large kinetic barriers that must be overcome during oxide formation and decomposition. Lastly, we present evidence that structurally similar oxides develop on both Pt(1 1 1) and Pt(1 0 0), therefore concluding that the properties of the surface Pt oxide are largely insensitive to the initial structure of the Pt single crystal surface.     

Growth of Ce on Rh(1 1 1)

We have studied the growth of cerium films on Rh(1 1 1) using STM (scanning tunneling microscopy), LEED (low energy electron diffraction), XPS (X-ray photoelectron spectroscopy) and AES (Auger electron spectroscopy). Measurements of the Ce films after room temperature deposition showed that Ce is initially forming nanoclusters in the low coverage regime. These clusters consist of 12 Ce atoms and have the shape of pinwheels. At a coverage of 0.25 ML (monolayer, ML) an adatom layer with a (2 × 2) superstructure is observed. Above 0.4 ML, Rh is diffusing through pinholes into the film, forming an unstructured mixed layer. Annealing at 250 °C leads to the formation of ordered Ce-Rh compounds based on the bulk compound CeRh₃. At a coverage of 0.1 ML, small ordered (2 × 2) surface alloy domains are observed. The exchanged Rh atoms form additional alloy islands situated on the pure Rh(1 1 1) surface, showing the same (2 × 2) superstructure as the surface alloy. At a coverage of 0.25 ML, the surface is completely covered by the surface alloy and alloy islands. The (2 × 2) structure is equivalent to a (1 1 1)-plane of CeRh₃, contracted by 6%. Annealing a 1 ML thick Ce layer leads to a flat surface consisting of different rotational domains of CeRh₃(1 0 0). The Rh needed for alloy formation comes from 50 Å deep pits in the substrate. Finally we show that LEIS (low energy ion scattering) is not suitable for the characterization of Ce and CeRh films due to strong effects of neutralization.     

Growth and structure of vanadium oxide on anatase (1 0 1) terraces

The interaction of vanadium oxide with epitaxial anatase films exposing (1 0 1) terraces was characterized. The TiO₂ films were grown on vicinal LaAlO₃ (1 1 0) substrates by oxygen plasma-assisted molecular beam epitaxy (OPA-MBE); reflection high energy and low energy electron diffraction (RHEED and LEED) indicated that the films exposed (1 0 1) terraces of the anatase TiO₂ polymorph. When a vanadium oxide monolayer was deposited onto the anatase surface by OPA-MBE at 725 K, only (1 × 1) RHEED and LEED patterns were observed. The V X-ray photoelectron spectroscopy (XPS) peak intensities indicated that the monolayer wetted the anatase surface and so the diffraction patterns were attributed to an epitaxial vanadia layer. Analysis of the vanadium oxide monolayer by X-ray and ultraviolet photoelectron spectroscopies revealed that the V was predominantly 5+. When the vanadia coverage was increased at 725 K, Auger electron spectra showed only very slow attenuation of the anatase Ti peaks while spots began to develop in RHEED patterns recorded along the LaAlO₃ direction; both indicative of 3-D cluster formation. In the orthogonal direction, the RHEED patterns showed unusual diagonal streaks. Meanwhile, the (1 × 1) LEED pattern persisted even after 30 nm of vanadia was deposited. This was attributed to gaps between the 3-D clusters exposing the epitaxial monolayer. Core level XPS spectra of the 3-D clusters revealed a broad V 2p_3/2 peak that was centered at the position expected for V⁴⁺ but could be deconvoluted into three peaks corresponding to V³⁺, V⁴⁺, and V⁵⁺. It is shown that crystallographic shear that accommodates such variations in the oxygen content of V oxides can lead to the diagonal streaks in RHEED patterns recorded along the LaAlO₃ [0 0 1] direction even as the pattern in the orthogonal direction shows sharp transmission spots. The results show that vanadia growth on anatase (1 0 1) proceeds through the Stranski-Krastanov mode with a strong vanadia-titania interaction stabilizing a dispersed vanadia monolayer. The results are compared with previous data for vanadia growth on anatase (0 0 1) where smooth, epitaxial VO₂ films grow ad infinitum.     

Photoemission study of the (2 × 2) structure formed by H2O adsorption on the Zr(0 0 0 1) surface

We have studied adsorption of water on the Zr(0 0 0 1) surface at sub-monolayer coverage by means of LEED and photoemission spectroscopy. An ordered (2 × 2) structure is formed after adsorption of 0.6-1.4 Langmuirs at 473 K. The sharpest LEED pattern was observed at an exposure of 1.2 L implying a coverage of 0.5 ML of oxygen. The same exposure at 293 K gives only a weak and diffuse (2 × 2) pattern. In addition, the sharp (2 × 2) pattern obtained at 473 K can be reversibly weakened by cooling to 293 K and subsequently sharpened by heating. For the sharp (2 × 2) structure, valence band spectra indicated dissociation of water and showed a peak composed mainly of O 2p derived states with two components at 6.0 eV and 6.6 eV binding energy. On cooling to 293 K, the O 2p peak became narrower and a new state appeared at 7.9 eV. Two components of the O 1s core level were resolved for the (2 × 2) structure, assigned to oxide and hydroxyl groups. The hydrogen on the surface of Zr(0 0 0 1) resulting from the dissociation of water and from bulk segregation strongly influenced the formation of the (2 × 2) structure of oxygen, and caused a temperature instability of the structure.     

Epitaxial growth of Bi thin films on Ge(1 1 1)

We investigated Bi thin film growth on Ge(1 1 1) by using low-energy electron diffraction (LEED) and scanning tunneling microscopy (STM). In the submonolayer regime, adsorbed Bi atoms form patches of the (2×1) structure. However, the structure does not grow to a long-range order. Following the formation of a (1×1) monolayer (ML) film, two-dimensional (1 1 0)-orientated Bi islands grow. The film orientation changes from (1 1 0) to (1 1 1) at 6-10 ML. The (1 1 0)-oriented Bi film shows a six-domain LEED pattern with missing spots, associated with a glide-line symmetry. The hexagonal (1 1 1) film at 14 ML has a lattice constant 2% smaller than bulk Bi(1 1 1).     

Ultrathin nickel oxide films grown on Ag(0 0 1): a study by XPS, LEIS and LEED intensity analysis

The structure of a nickel oxide film 2 ML thick has been investigated by LEED intensity analysis. The NiO film was prepared by evaporating Ni in presence of O₂ at a pressure in the 10⁻⁶ mbar range. The growth of the oxide film was followed by XPS, LEIS and LEED. In the early stages of deposition, the film shows a (2 × 1) superstructure in LEED. After deposition of 2 ML of NiO, a sharp (1 × 1) LEED pattern is observed. The intensity versus electron energy curves of the LEED spots were measured for this NiO(1 × 1) film and analysed by means of the tensor LEED method. A good level of agreement of the experimental LEED intensities with those calculated for a pseudomorphic NiO(0 0 1) film was obtained. We found that oxygen atoms at the oxide-substrate interface are on-top silver atoms. The interlayer distance in the oxide does not differ significantly from that in bulk NiO(0 0 1), within the accuracy of the analysis. An outward displacement (0.05 ± 0.05 Å) of oxygen atoms with respect to nickel atoms was found at the oxide film surface. The interlayer distance at the silver-nickel oxide interface is 2.43 ± 0.05 Å.     

(2 × 1)-Na surface reconstruction induced by NaCl dissociation on Ag(1 1 0) during LEED analysis

This study first reports the initial growth stages of sodium chloride (NaCl) on Ag(1 1 0) at room temperature. NaCl grows in bi-layer mode along its [1 0 0] axis and gives rise to (4 × 1) and (1 × 2) reconstructed domains for coverages lower than two monolayers (ML), a minimal thickness inducing a bi-dimensional closed film. In addition, a 10 ML NaCl film has been examined by low energy electron diffraction (LEED). LEED analysis leads to the dissociation of the NaCl deposit in a few minutes. The NaCl dissociation implies Cl desorption from the surface and Na remaining on it. The residual Na is arranged in the form of a (2 × 1) surface reconstruction and is found to be strongly bounded to the Ag substrate. These findings have been established by using the X-ray photoelectron spectroscopy technique.     

Alloy formation of Co/Ni/Pt(1 1 1)

The initial growth and alloy formation of ultrathin Co films deposited on 1 ML Ni/Pt(1 1 1) were investigated by Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and ultraviolet photoelectron spectroscopy (UPS). A sequence of samples of d_Co Co/1 ML Ni/Pt(1 1 1) (d_Co = 1, 2, and 3 ML) were prepared at room temperature, and then heated up to investigate the diffusion process. The Co and Ni atoms intermix at lower annealing temperature, and Co-Ni intermixing layer diffuses into the Pt substrate to form Ni-Co-Pt alloys at higher annealing temperature. The diffusion temperatures are Co coverage dependent. The evolution of UPS with annealing temperatures also shows the formation of surface alloys. Some interesting LEED patterns of 1 ML Co/1 ML Ni/Pt(1 1 1) show the formation of ordered alloys at different annealing temperature ranges. Further studies in the Curie temperature and concentration analysis, show that the ordered alloys corresponding to different LEED patterns are Ni_xCo_1−xPt and Ni_xCo_1−xPt₃. The relationship between the interface structure and magnetic properties was investigated.     

Growth and alloy formation of ultrathin Ni films on Co/Pt(1 1 1)

Low-energy electron diffraction (LEED) and Auger electron spectroscopy (AES) were used to study the growth and the structural evolution of Ni/Co/Pt(1 1 1) following high-temperature annealing. From the oscillation of the specular beam of the LEED and Auger uptake curve, we concluded that the growth mode of thin Ni films on 1 ML Co/Pt(1 1 1) is at least 2 ML layer-by-layer growth before three-dimensional island growth begins. The alloy formation of Ni/1 ML Co/Pt(1 1 1) was analyzed by AES. The temperature for the intermixing of Ni and Co layers in the upper interface without diffusing into the bulk of Pt is independent of the thickness of Ni when a Co buffer is one atomic monolayer. After the temperature was increased, formations of Ni-Co-Pt alloy, Ni-Pt alloy and Co-Pt alloy were observed. The temperature required for the Ni-Co intermixing layer to diffuse into Pt bulk increases with the thickness of Ni. The interlayer distance as a function of annealing temperature for 1 ML Ni/1 ML Co/Pt(1 1 1) was calculated from the I-V LEED. The evolution of LEED patterns was also observed at different annealing temperatures.     

The epitaxial growth of Pd electrodeposition on Au(1 0 0) studied by LEED and RHEED

The epitaxial growth of Pd adlayers electrochemically deposited onto Au(1 0 0) has been studied by LEED, RHEED and AES. For the first 6 ML, the Pd deposits grow pseudomorphically on Au(1 0 0) with a lateral expansion of 4.5% with respect to bulk Pd. The strain in the expanded commensurate (1 × 1) Pd layers on Au(1 0 0) begins to be relieved at the Pd coverage between 6 and 9 ML range by formation of a compressed Pd film with respect to Au(1 0 0) surface and the compression increases continuously with thickness. At ca. 20 ML Pd the lattice constant of the film approaches to the bulk Pd and three-dimensional Pd islands develop since around 30 ML coverage. No superstructure due to the Pd-Au surface alloy can be found for coverages from monolayer up to 30 ML Pd on Au(1 0 0). A c(2 × 2) phase has been observed on the Pd-deposited Au(1 0 0) electrodes, which is ascribed to an ordered Cl adlayers adsorbed on Pd adlayers rather than a Pd-Au surface alloy.     

Study of the early stages of Cr/6H-SiC(0 0 0 1) interface formation

The early stages of the Cr/6H-SiC(0 0 0 1) interface formation at room temperature were investigated using XPS, LEED and work function (WF) measurements. Upon stepwise Cr evaporation in UHV up to a thickness of 5-10 monolayers (ML) at RT, the binding energy of the XPS Cr 2p_3/2 core level peak shifted from 576.1 eV, at submonolayer coverage, to 574.7 eV (corresponding to metallic Cr) for the final Cr deposit, while the binding energies of the substrate XPS core level peaks remained stable. The WF exhibited a steep decrease of about 0.5 eV from the initial SiC substrate value, upon submonolayer coverage, but then increased gradually to saturation at a value of about 4.8 eV (polycrystalline Cr film with some chemisorbed oxygen). The growth of the ultrathin film was via 3D-cluster formation. The height of the Schottky barrier for the Cr/6H-SiC(0 0 0 1) contact was found by XPS to be 0.5 ± 0.1 eV. The results, generally, indicate the absence of any extended interfacial silicide-like interaction at RT.     

Adsorption of gas-phase oxygen atoms on Pt(1 0 0)-hex-R0.7°: Evidence of a metastable chemisorbed phase

We utilized temperature programmed desorption (TPD) and low energy electron diffraction (LEED) to study the chemisorption of gas-phase oxygen atoms on Pt(1 0 0)-hex-R0.7° at 450 K and 573 K, and find that the types and relative populations of oxygen phases that develop are highly dependent on the surface temperature during adsorption. At both temperatures, oxygen atoms initially adsorb on defects associated with the surface reconstruction. Increasing the coverage to about 0.32 ML (monolayers) at 573 K causes deconstruction and population of a phase with apparent (3 × 1) symmetry that desorbs in a single feature centered at about 672 K. Saturating at 0.63 ML leads to the formation of an additional “complex” ordered phase that desorbs in a sharp feature exhibiting autocatalytic behavior as it shifts from approximately 631 K to 642 K. Uptake at 450 K also initiates deconstruction, but in this case two desorption maxima at about 652 K and 672 K grow simultaneously with increasing coverage to about 0.32 ML. The feature at 672 K is associated with the disordered (3 × 1) phase, while the feature at 652 K has not been previously reported. We attribute this new feature to desorption from disordered arrangements of high oxygen concentrations on (1 × 1) surface regions. As the coverage increases to about 0.51 ML, small amounts of the complex phase grow, while this “high-concentration” (1 × 1) and the (3 × 1) phases continue to develop. We conclude that the complex phase is energetically preferred over the high-concentration (1 × 1) phase, but kinetic barriers hinder its formation at 450 K, causing oxygen to become trapped in the high-concentration (1 × 1) phase. Therefore, the high-concentration (1 × 1) phase is metastable relative to the complex phase. Lastly, above about 0.51 ML, further adsorption at 450 K promotes the growth of Pt oxide islands as detailed in a future investigation.     

Structure and composition of chemically prepared and vacuum annealed InSb(0 0 1) surfaces

The InSb(0 0 1) surfaces chemically treated in HCl-isopropanol solution and annealed in vacuum were studied by means of X-ray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED) and electron energy-loss spectroscopy (EELS). The HCl-isopropanol treatment removes indium and antimony oxides and leaves on the surface about 3 ML of physisorbed overlayer, containing indium chlorides and small amounts of antimony, which can be thermally desorbed at 230 °C. The residual carbon contaminations were around 0.2-0.4 ML and consisted of the hydrocarbon molecules. These hydrocarbon contaminations were removed from the surface together with the indium chlorides and antimony overlayer. With increased annealing temperature, a sequence of reconstructions were identified by LEED: (1 × 1), (1 × 3), (4 × 3), and (4 × 1)/c(8 × 2), in the order of decreasing Sb/In ratio. The structural properties of chemically prepared InSb(0 0 1) surface were found to be similar to those obtained by decapping of Sb-capped epitaxial layers.     

Structure and electronic properties of gold adsorbed on Ti(0 0 0 1)

The Au/Ti(0 0 0 1) adsorption system was studied by low energy electron diffraction (LEED) and photoemission spectroscopy with synchrotron radiation after step-wise Au evaporation onto the Ti(0 0 0 1) surface. For adsorption of Au at 300 K, no additional superstructures were observed and the (1 × 1) pattern of the clean surface simply became diffuse. Annealing of gold layers more than 1 ML thick resulted in the formation of an ordered Au-Ti surface alloy. Depending on the temperature and annealing time, three surface reconstructions were observed by LEED: (√3 × √3) R30°, (2 × 2) and a one-dimensional incommensurate (√3 × √3) rectangular pattern. The Au 4f core level and valence band photoemission spectra provided evidence of a strong chemical interaction between gold and titanium. The data indicated formation of an intermetallic interface and associated valence orbital hybridization, together with diffusion of gold into the bulk. Au core-level shifts were found to be dependent on the surface alloy stoichiometry.     

Formation of oxygen-induced Si(1 1 3)-3 × 2 facets on the Si(5 5 12) surface

We report the formation of Si(1 1 3)-3 × 2 facets upon exposing oxygens on the Si(5 5 12) surface at an elevated temperature. These facets are found to form only for a limited range of oxygen exposure and exhibit a well-defined 3 × 2 LEED pattern. We also find the surface electronic state unique only to the facets in the valence band. The spectral feature of these electronic states and the behavior of a (1/3 1/2) LEED spot upon oxygen contents in the facets indicate that the formation is a heterogeneous mixture of the clean Si(1 1 3) facets free of oxygens and other facets containing oxygen atoms.