Microwave syntheses of poly(ε‐caprolactam‐co‐ε‐caprolactone)

Microwave irradiation was applied to synthesize poly(ε‐caprolactam‐co‐ε‐caprolactone) directly from the anionic catalyzed ring opening of two cyclic monomers, ε‐caprolactam and ε‐caprolactone using a variable frequency microwave furnace, programmed to a set temperature and controlled by a pulsed power on–off system. Dielectric properties of ε‐caprolactam, ε‐caprolactone, and their mixture were measured in the microwave range from 0.4 to 3 GHz, showing that both ε‐caprolactam and ε‐caprolactone exhibited effective absorption of microwave energy to induce a fast chemical reaction. The microwave induced anionic copolymerization of ε‐caprolactam and ε‐caprolactone generated copoly(amide‐ester)s in yields as high as 70%. Conventional thermal and microwave copolymerization studies were also conducted for comparison with the microwave results. These studies demonstrated that an effective and efficient microwave method to copolymerize ε‐caprolactam with ε‐caprolactone in higher yield, higher amide content, and higher T_g 's, relative to the thermal process, has been developed. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1379–1390, 2000     

Microwave‐assisted ring‐opening polymerization of ϵ‐caprolactone

Ring‐opening polymerization of ?‐caprolactone was carried out smoothly and effectively with constant microwave powers of 170, 340, 510, and 680 W, respectively, with a microwave oven at a frequency of 2.45 GHz. The temperature of the polymerization ranged from 80 to 210 °C. Poly(?‐caprolactone) (PCL) with a weight‐average molar mass (M_w) of 124,000 g/mol and yield of 90% was obtained at 680 W for 30 min using 0.1% (mol/mol) stannous octanoate as a catalyst. When the polymerization was catalyzed by 1% (w/w) zinc powder, the M_w of PCL was 92,300 g/mol after the reaction mixture was irradiated at 680 W for 270 min. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1749–1755, 2002     

Synthesis and structural analysis of functionalized poly (ϵ‐caprolactone)‐based three‐arm star polymers

Hydroxyl‐functionalized three‐arm poly(?‐caprolactone)s (PGCL‐OHs) were synthesized by the ring‐opening polymerization of ?‐caprolactone in the presence of glycerol (as the core) and stannous octoate. The effect of the feed ratio of ?‐caprolactone to glycerol on the ring‐opening polymerization was studied. These three‐arm PGCL‐OHs were then converted into double‐bond‐functionalized three‐arm poly(?‐caprolactone)s (PGCL‐Mas) by the reaction of PGCL‐OH with maleic anhydride in the melt at 130 °C. The quantitative conversion of hydroxyl functionality was achieved at a low molecular weight. The resulting PGCL‐OH and PGCL‐Ma were characterized with gel permeation chromatography, Fourier transform infrared, ¹H NMR, ¹³C NMR, and differential scanning calorimetry. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1127–1141, 2002     

Synthesis and characterization of well‐defined poly(2‐hydroxyethyl methacrylate‐co‐styrene)‐graft‐poly(ε‐caprolactone) by sequential controlled polymerization

A new graft copolymer, poly(2‐hydroxyethyl methacrylate‐co‐styrene) ‐graft‐poly(?‐caprolactone), was prepared by combination of reversible addition‐fragmentation chain transfer polymerization (RAFT) with coordination‐insertion ring‐opening polymerization (ROP). The copolymerization of styrene (St) and 2‐hydroxyethyl methacrylate (HEMA) was carried out at 60 °C in the presence of 2‐phenylprop‐2‐yl dithiobenzoate (PPDTB) using AIBN as initiator. The molecular weight of poly (2‐hydroxyethyl methacrylate‐co‐styrene) [poly(HEMA‐co‐St)] increased with the monomer conversion, and the molecular weight distribution was in the range of 1.09 ～ 1.39. The ring‐opening polymerization (ROP) of ?‐caprolactone was then initiated by the hydroxyl groups of the poly(HEMA‐co‐St) precursors in the presence of stannous octoate (Sn(Oct)₂). GPC and ¹H‐NMR data demonstrated the polymerization courses are under control, and nearly all hydroxyl groups took part in the initiation. The efficiency of grafting was very high. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5523–5529, 2004     

Biodegradable brushlike graft polymers. I. Polymerization of ϵ‐caprolactone onto water‐soluble hydroxypropyl cellulose as the backbone by the protection of the trimethylsilyl group

After the protection of partial hydroxyl groups with trimethylsilyl (TMS) groups, hydroxypropyl cellulose becomes soluble in organic solvents, and the number of hydroxyl groups as initiating groups can be controlled. As a result, a new brushlike graft poly(?‐caprolactone) can be prepared with hydroxypropyl cellulose as the backbone polymer by homogeneous ring‐opening graft polymerization and deprotection. The protection and deprotection of the TMS group during the entire procedure were carefully monitored with Fourier transform infrared (FTIR) and NMR, and the final graft copolymers were characterized with FTIR, ¹H NMR, ¹³C NMR, gel permeation chromatography, and differential scanning calorimetry. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 273–280, 2003     

Microwave‐improved polymerization of ϵ‐caprolactone initiated by carboxylic acids

The ring‐opening polymerization of ε‐caprolactone (ε‐CL), initiated by carboxylic acids such as benzoic acid and chlorinated acetic acids under microwave irradiation, was investigated; with this method, no metal catalyst was necessary. The product was characterized as poly(ε‐caprolactone) (PCL) by ¹H NMR spectroscopy, Fourier transform infrared spectroscopy, ultraviolet spectroscopy, and gel permeation chromatography. The polymerization was significantly improved under microwave irradiation. The weight‐average molecular weight (M_w) of PCL reached 44,800 g/mol, with a polydispersity index [weight‐average molecular weight/number‐average molecular weight (M_w/M_n)] of 1.6, when a mixture of ε‐CL and benzoic acid (25/1 molar ratio) was irradiated at 680 W for 240 min, whereas PCL with M_w = 12,100 and M_w/M_n = 4.2 was obtained from the same mixture by a conventional heating method at 210 °C for 240 min. A degradation of the resultant PCL was observed during microwave polymerization with chlorinated acetic acids as initiators, and this induced a decrease in M_w of PCL. However, the degradation was hindered by benzoic acid at low concentrations. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 13–21, 2003     

Synthesis and characterization of poly(β‐hydroxybutyrate) and poly(ϵ‐caprolactone) copolyester by transesterification

To synthesize the copolyester of poly(β‐hydroxybutyrate) (PHB) and poly(?‐caprolactone) (PCL), the transesterification of PHB and PCL was carried out in the liquid phase with stannous octoate as the catalyzer. The effects of reaction conditions on the transesterification, including catalyzer concentration, reaction temperature, and reaction time, were investigated. The results showed that both rising reaction temperature and increasing reaction time were advantageous to the transesterification. The sequence distribution, thermal behavior, and thermal stability of the copolyesters were investigated by ¹³C NMR, Fourier transform infrared spectroscopy, differential scanning calorimetry, wide‐angle X‐ray diffraction, optical microscopy, and thermogravimetric analysis. The transesterification of PHB and PCL was confirmed to produce the block copolymers. With an increasing PCL content in the copolyesters, the thermal behavior of the copolyesters changed evidently. However, the introduction of PCL segments into PHB chains did not affect its crystalline structure. Moreover, thermal stability of the copolyesters was little improved in air as compared with that of pure PHB. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1893–1903, 2002     

Microwave assisted hydroxyalkylamidation of poly(ethylene‐co‐acrylic acid) and formation of grafted poly(ϵ‐caprolactone) side chains

The microwave assisted amidation of poly(ethylene‐co‐acrylic acid) (PEAA) with 2‐(2‐aminoethoxy)ethanol was performed to yield a hydroxy functionalized poly(ethylene) based copolymer (PEAAOH) in a single step. PEAAOH was used as a polyinitiator for the ring‐opening polymerization of ε‐caprolactone. The obtained graft copolymers were studied via ¹H NMR spectroscopy, gel permeation chromatography, differential scanning calorimetry, polarized optical microscopy, and scanning electron microscopy. Microscopy methods show a crystallization behavior of banded spherulites. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3659–3667, 2007     

A convenient synthesis of α,α′‐ homo‐ and α,α′‐hetero‐bifunctionalized poly(ε‐caprolactone)s by ring opening polymerization: The potentially valuable precursors for miktoarm star copolymers

Two new ring opening polymerization (ROP) initiators, namely, (3‐allyl‐2‐(allyloxy)phenyl)methanol and (3‐allyl‐2‐(prop‐2‐yn‐1‐yloxy)phenyl)methanol each containing two reactive functionalities viz. allyl, allyloxy and allyl, propargyloxy, respectively, were synthesized from 3‐allylsalicyaldehyde as a starting material. Well defined α‐allyl, α′‐allyloxy and α‐allyl, α′‐propargyloxy bifunctionalized poly(ε‐caprolactone)s with molecular weights in the range 4200–9500 and 3600–10,900 g/mol and molecular weight distributions in the range 1.16–1.18 and 1.15–1.16, respectively, were synthesized by ROP of ε‐caprolactone employing these initiators. The presence of α‐allyl, α′‐allyloxy and α‐allyl, α′‐propargyloxy functionalities on poly(ε‐caprolactone)s was confirmed by FT‐IR, ¹H, ¹³C NMR spectroscopy, and MALDI‐TOF analysis. The kinetic study of ROP of ε‐caprolactone with both the initiators revealed the pseudo first order kinetics with respect to ε‐caprolactone consumption and controlled behavior of polymerization reactions. The usefulness of α‐allyl, α′‐allyloxy functionalities on poly(ε‐caprolactone) was demonstrated by performing the thiol‐ene reaction with poly(ethylene glycol) thiol to obtain (mPEG)₂‐PCL miktoarm star copolymer. α‐Allyl, α′‐propargyloxy functionalities on poly(ε‐caprolactone) were utilized in orthogonal reactions i.e copper catalyzed alkyne‐azide click (CuAAC) with azido functionalized poly(N‐isopropylacrylamide) followed by thiol‐ene reaction with poly(ethylene glycol) thiol to synthesize PCL‐PNIPAAm‐mPEG miktoarm star terpolymer. The preliminary characterization of A₂B and ABC miktoarm star copolymers was carried out by ¹H NMR spectroscopy and gel permeation chromatography (GPC). © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 844–860     

Synthesis of four‐armed poly(ε‐caprolactone)‐block‐poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four‐armed poly(?‐caprolactone)‐block‐poly(ethylene oxide) (PCL‐b‐PEO) copolymers were synthesized by ring‐opening polymerization of ethylene oxide in the presence of four‐armed poly(?‐caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt₂) as a catalyst. The chemical structure of PCL‐b‐PEO copolymer was confirmed by ¹H NMR and ¹³C NMR. The hydroxyl end groups of the four‐armed PCL were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four‐armed architecture of the copolymer. Physicochemical properties of the four‐armed block copolymers differed from their starting four‐armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four‐armed block copolymer increased with PEO length and PEO content. The micelle formation of the four‐armed block copolymer was examined by a fluorescent probe technique, and the existence of the critical micelle concentration (cmc) confirmed the amphiphilic nature of the resulting copolymer. The cmc value increased with increasing PEO length. The absolute cmc values were higher than those for linear amphiphilic block copolymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 950–959, 2004     

Preparation of novel poly(ethylene oxide‐co‐glycidol)‐graft‐poly(ε‐caprolactone) copolymers and inclusion complexation of the grafted chains with α‐cyclodextrin

A well‐defined comblike copolymer of poly(ethylene oxide‐co‐glycidol) [(poly(EO‐co‐Gly)] as the main chain and poly(ε‐caprolactone) (PCL) as the side chain was successfully prepared by the combination of anionic polymerization and ring‐opening polymerization. The glycidol was protected by ethyl vinyl ether to form 2,3‐epoxypropyl‐1‐ethoxyethyl ether (EPEE) first, and then ethylene oxide was copolymerized with EPEE by an anionic mechanism. The EPEE segments of the copolymer were deprotected by formic acid, and the glycidol segments of the copolymers were recovered after saponification. Poly(EO‐co‐Gly) with multihydroxyls was used further to initiate the ring‐opening polymerization of ε‐caprolactone in the presence of stannous octoate. When the grafted copolymer was mixed with α‐cyclodextrin, crystalline inclusion complexes (ICs) were formed, and the intermediate and final products, poly(ethylene oxide‐co‐glycidol)‐graft‐poly(ε‐caprolactone) and ICs, were characterized with gel permeation chromatography, NMR, differential scanning calorimetry, X‐ray diffraction, and thermogravimetric analysis in detail. The obtained ICs had a channel‐type crystalline structure, and the ratio of ε‐caprolactone units to α‐cyclodextrin for the ICs was higher than 1:1. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3684–3691, 2006     

Ring‐opening polymerization of ϵ‐caprolactone by iodine charge‐transfer complex

The ring‐opening polymerization of ?‐caprolactone (?‐CL) catalyzed by iodine (I₂) was studied. The formation of a charge‐transfer complex (CTC) among triiodide, I, and ?‐CL was confirmed with ultraviolet–visible spectroscopy. The monomer ?‐CL was polymerized in bulk using I₂ as a catalyst to form the polyester having apparent weight‐average molecular weights of 35,900 and 45,500 at polymerization temperatures of 25 and 70 °C, respectively. The reactivity of both, ?‐CL monomer and ?‐CL:I₂ CTC, was interpreted by means of the potential energy surfaces determined by semiempirical computations (MNDO‐d). The results suggest that the formation of the ?‐CL:I₂ CTC leads to the ring opening of the ?‐CL structure with the lactone protonation and the formation of a highly polarized polymerization precursor (?‐CL)⁺. The band gaps approximated from an extrapolation of the oligomeric polycaprolactone (PCL) structures were computed. With semiempirical quantum chemical calculations, geometries and charge distributions of the protonated polymerization precursor (?‐CL)⁺ were obtained. The calculated band gap (highest occupied molecular orbit/lowest unoccupied molecular orbit differences) agrees with the experiment. The analysis of the oligomeric PCL isosurfaces indicate the existence of a weakly lone pair character of the C?O and C? O bonds suggesting a ?‐CL ring‐opening specificity. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 714–722, 2002     

Poly(ϵ‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(ϵ‐caprolactone) triblock copolymers: Synthesis and self‐assembly in aqueous solutions

Nontoxic and biodegradable poly(?‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(?‐caprolactone) triblock copolymers were synthesized by the solution polymerization of ?‐caprolactone in the presence of poly(ethylene glycol). The chemical structure of the resulting triblock copolymer was characterized with ¹H NMR and gel permeation chromatography. In aqueous solutions of the triblock copolymers, the micellization and sol–gel‐transition behaviors were investigated. The experimental results showed that the unimer‐to‐micelle transition did occur. In a sol–gel‐transition phase diagram obtained by the vial‐tilting method, the boundary curve shifted to the left, and the gel regions expanded with the increasing molecular weight of the poly(?‐caprolactone) block. In addition, the hydrodynamic diameters of the micelles were almost independent of the investigated temperature (25–55 °C). The atomic force microscopy results showed that spherical micelles formed at the copolymer concentration of 2.5 × 10^?4 g/mL, whereas necklace‐like and worm‐like shapes were adopted when the concentration was 0.25 g/mL, which was high enough to form a gel. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 605–613, 2007     

Ring‐opening copolymerization of ethylene carbonate and ε‐caprolactone catalyzed by neodymium tris(2,6‐di‐tert‐butyl‐4‐methylphenolate): Synthesis,characterization, and dynamic mechanic analysis

The ring‐opening copolymerization of ethylene carbonate (EC) with ε‐caprolactone (CL) was carried out using neodymium tris(2,6‐di‐tert‐butyl‐4‐methylphenolate) as a single‐component catalyst. Copolymers containing up to 22.0% EC contents with high molecular weights (up to 23.97 × 10⁴) and moderate molecular weight distributions (between 1.66 and 2.03) were synthesized at room temperature. Compared with homopoly(ε‐caprolactone), the copolymers with EC units exhibited increased glass transition temperatures (?35.6 °C), reduced melting temperatures (44.5 °C), and greatly enhanced elongation percentage at break (2383%) based on dynamic mechanic analysis. The crystallinities of the copolymers decreased with the increasing EC molar percentage in the products. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4050–4055, 2008     

Molecular composites composed of castor oil‐modified poly(ε‐caprolactone) and self‐assembled hydroxystearic acid fibers

After (R)‐12‐hydroxystearic acid (HSA) was mixed at 100 °C with the castor oil‐modified poly(ε‐caprolactone) (CO‐PCL) prepared by the ring‐opening polymerization of ε‐caprolactone in the presence of castor oil, the mixture was gradually cooled to room temperature to give a solidified CO‐PCL/HSA composite. The CO‐PCL/HSA sample showed an exothermic peak at around 67–71 °C which was lower than the melting point of HSA (76.8 °C), indicating the formation of mesogenic HSA aggregates. The rheological measurement of the CO‐PCL/HSA revealed the formation of HSA organogel at around 67–55 °C during the cooling process from the melt. Furthermore, the polarized and normal optical microscopic analyses of CO‐PCL/HSA on the cooling stage revealed that anisotropic fibrous materials are formed at around 60 °C and then the fibrous network propagated over the matrix polymer. The flexural modulus and storage modulus of the CO‐PCL/HSA composite increased with increasing HSA content. The CO‐PCL/HSA composite annealed at 60 °C for 2 h on the cooling process had a higher flexural and storage modulus than the sample without annealing. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1281–1289, 2010     

Cyclic poly(ε‐caprolactone) synthesized by combination of ring‐opening polymerization with ring‐closing metathesis,ring closing enyne metathesis,or “click” reaction

This article described the synthesis of cyclic poly(ε‐caprolactone) (PCL) via ring‐closing metathesis (RCM), ring closing enyne metathesis (RCEM), and “click” reaction of different difunctional linear PCL. Linear PCL precursors were prepared by ring‐opening polymerization (ROP) of ε‐caprolactone in bulk using 10‐undecen‐1‐ol or propargyl alcohol as the initiator, followed by reacting with corresponding acyl chloride containing vinyl or azido end group. The subsequent end‐to‐end intramolecular coupling reactions were performed under high dilution conditions. The successful transformation of linear PCL precursor to cyclic PCL was confirmed by Gel permeation chromatography, ¹H NMR, and Fourier transform infrared measurements. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3022–3033, 2009     

Anionic lanthanide phenoxide complexes as novel single‐component initiators for the polymerization of ε‐caprolactone and trimethylene carbonate

The anionic lanthanide‐sodium‐2,6‐di‐tert‐butyl‐phenoxide complexes [Ln(OAr)₄][Na(DME)₃]·DME (Ln = Nd 1 (neodymium), Sm 2 (samarium), or Gd 3 (gadolium); DME = dimethoxyethane) were synthesized by the reaction of anhydrous LnCl₃ with 4 equiv of sodium‐2,6‐di‐tert‐butyl‐phenoxide NaOAr in high yields and structurally characterized. These complexes showed high catalytic activity in the ring‐opening polymerizations of ?‐caprolactone (?‐CL) and trimethylene carbonate (TMC). The catalytic activity profoundly depended on the lanthanide metals. The active order of Gd < Sm < Nd for the polymerization of ?‐CL and TMC was observed. The polymers obtained with these initiators all showed a unimodal molecular weight distribution, indicating that the [Ln(OAr)₄][Na(DME)₃]·DME anionic complexes could be used as single‐component initiators. The anionic complex was more efficient than the corresponding neutral complex, Ln(OAr)₃(THF)₂. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1210–1218, 2007     

Nonisothermal crystallization kinetics of poly(ε‐caprolactone) blocks in double crystalline triblock copolymers containing poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) and poly(ε‐caprolactone) units

The poly(3‐hydroxbutyrate‐co‐3‐hydroxyvalerate)/poly(ε‐caprolactone) block copolymers (PHCLs) with three different weight ratios of PCL blocks (38%, named PHCL‐38; 53%, named PHCL‐53; and 60%, named PHCL‐60) were synthesized by using PHBV with two hydroxyl end groups to initiate ring‐opening polymerization of ε‐caprolactone. During DSC cooling process, melt crystallization of PHCL‐53 at relatively high cooling rates (9, 12, and 15 °C min^?1) and PHCL‐60 at all the selected cooling rates corresponded to PCL blocks so that PHCL‐53 and PHCL‐60 were used to study the nonisothermal crystallization behaviors of PCL blocks. The kinetics of PCL blocks in PHCL‐53 and PHCL‐60 under nonisothermal crystallization conditions were analyzed by Mo equation. Mo equation was successful in describing the nonisothermal crystallization kinetics of PCL blocks in PHCLs. Crystallization activation energy were estimated using Kissinger's method. The results of kinetic parameters showed that both blocks crystallized more difficultly than corresponding homopolymers. With the increase of PCL content, the crystallization rate of PCL block increased gradually. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Core–shell‐type multiarm star polyethylenimine‐block‐poly(ε‐caprolactone): Synthesis and guest encapsulation potential

Novel multiarm star copolymers with poly(?‐caprolactone) (PCL) as the arms and hyperbranched polyethylenimine (HPEI) as the core have been successfully prepared by the tin(II) 2‐ethylhexanoate catalyzed ring‐opening polymerization of ?‐caprolactone (CL) with HPEI used directly as a macroinitiator. Not only primary but also secondary amine groups of HPEI participate in initiating the ring‐opening polymerization of CL with almost 100% initiation efficiency. The average degree of polymerization of the PCL arms can be controlled by the feed ratio of the monomers to the initiating sites. Because of the polarity difference of the PCL arms and HPEI core, the obtained multiarm star polymers display an inverted micellar structure with potential extraction and encapsulation of water‐soluble guests. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4165–4173, 2006     

Ring‐opening polymerization of ϵ‐caprolactone initiated with different ruthenium derivatives: Kinetics and mechanism studies

End‐functionalized polyesters have been synthesized by ring‐opening polymerization (ROP) of ?‐caprolactone (CL) initiated with five different ruthenium derivatives in the presence of a series of alcohols as transfer agents. Mechanistic studies were performed for ROP of CL with RuCl₂(PPh₃)₃ ( I ), TpRuCl(PPh₃)₂ ( II ), and TpRuCl(PHPh₂)(PPh₃) ( III ) as catalysts in the presence or absence of benzyl alcohol (BzOH). Obtained molecular weights are proportional to CL/BzOH ratio, but there is not a direct relationship with CL/ruthenium complex ratios. ¹H and ¹³C NMR spectroscopy revealed the existence of benzyl ester end‐groups. Catalysis involves (a) dissociation of ruthenium complexes, (b) coordination of the lactone CL, (c) coordination of the BzOH with the formation of a metal alkoxide, (d) transfer from the alkoxyl ligand to the coordinated lactone, and (e) ring‐opening of CL by oxygen‐acyl bond cleavage. The proposed mechanism is supported by ¹H, ¹³C, and ³¹P NMR, gel permeation chromatography (GPC), and MALDI‐TOF analysis of the polymers. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6926–6942, 2006