Synthesis and luminescent properties of nanoparticles GdCaAl3O7:RE (RE=Eu, Tb) via the sol-gel method

By using metal nitrates as starting materials and citric acid as complexing agent, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ powder phosphors were prepared by a citrate-gel method. Thermal analysis (TG-DTG), X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM), photoluminescence excitation and emission, as well as kinetic decays were employed to characterize the resulting samples. The results of the XRD indicated the precursor samples began to crystallize at 800 °C and the crystallinity increased with elevation the annealing temperature. TEM images showed that the phosphor particles were basically of spherical shape, with good dispersion about a particle size of around 40-70 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺, and at around 543 nm corresponding to the ⁵D₄-⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺ (or Tb³⁺) concentration and annealing temperature were also studied in detail.     

Investigation of crystallographic sites of Eu in La2BaZnO5 by site-selective laser-excitation spectroscopy

La₂BaZnO₅:Eu³⁺ (0.05 mol%) was prepared by a solid-state reaction at high temperature. X-ray powder diffraction analysis confirmed the formation of single phase La₂BaZnO₅. Luminescence properties of La₂BaZnO₅:Eu³⁺ are investigated by site-selective laser-excitation and emission spectroscopy at 18 K. Two different crystallographic sites for Eu³⁺ corresponding to the La³⁺ and Ba²⁺ sites are identified from the ⁷F₀→⁵D₀ excitation spectra obtained by monitoring the ⁵D₀→⁷F_J (J=1, 2, …, 6) emissions. It is found that Eu³⁺ substituted for the Ba²⁺ ion experiences stronger crystal-field strength than Eu³⁺ substituted for the La³⁺ ion. Energy transfer between the two crystallographic Eu³⁺ centers is investigated by luminescence decay curves at 18 K.     

Optical and fluorescence spectroscopy of Eu2O3-doped P2O5-K2O-KF-MO-Al2O3 (M = Mg, Sr and Ba) glasses

Fluorophosphate glasses of composition, P₂O₅ + K₂O + KF + MO + Al₂O₃ + xEu₂O₃ (M = Mg, Sr and Ba; x = 0.01, 0.05, 0.1, 1.0, 2.0, 4.0 and 6.0 mol%) were prepared and characterized their optical properties. Crystal-field (CF) analysis revealed a relatively weak CF strength around Eu³⁺ ions in the Ba based fluorophosphate glasses. The Judd-Ofelt parameters have been estimated from the oscillator strengths of ⁷F₀ → ⁵D₂, ⁷F₀ → ⁵D₄ and ⁷F₀ → ⁵L₆ absorption transitions of Eu³⁺ ions and were used to evaluate the radiative properties of the ⁵D₀ → ⁷F_J (J = 0-4) transitions. Considerable variation has been observed in the relative intensity ratio of ⁵D₀ → ⁷F₂ to ⁵D₀ → ⁷F₁ transitions of Eu³⁺ ions due to change in the alkaline earth metal ions. The decay of the ⁵D₀ level shows single exponential and less sensitive to Eu³⁺ ions concentration as well as MgO/SrO/BaO modifiers.     

Photoluminescence characteristics of ZnO doped with Eu powders

In this work, we have investigated the photoluminescence spectra of europium-doped zinc oxide crystallites prepared by a vibrating milled solid-state reaction method. X-ray diffraction, scanning electron microscopy, luminescence spectra and time-resolved spectra analysis were used to characterize the synthetic ZnO:Eu³⁺ powders. XRD results of the powders showed a typical wurtzite hexagonal crystal structure. A second phase occurred at 5 mol% Eu₂O₃-doped ZnO. The ⁵D₀-⁷F₁ (590 nm) and ⁵D₀-⁷F₂ (609 nm) emission characteristics of Eu³⁺ appeared after quenching with more than 1.5 mol% Eu₂O₃ doping. The Commission Internationale d’Eclairage (CIE) chromaticity coordinates of a ZnO:Eu³⁺ host excited at λ_ex=467 nm revealed a red-shift phenomenon with increase in Eu³⁺ ion doping. The lifetime of the Eu³⁺ ion decreased as the doping concentration was increased from 1.5 to 10 mol%, and the time-resolved ⁵D₀→⁷F₂ transition presents a single-exponential decay behavior.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Rapid synthesis and luminescence of the Eu, Er codoped ZnO quantum-dot chain via chemical precipitation method

ZnO quantum-dot chains codoped with Eu³⁺ and Er³⁺ were synthesized by the chemical precipitation method and the codoping effects on the structures, morphologies and optical properties of the powders were briefly investigated. The X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) results indicated the Eu³⁺ and Er³⁺ were incorporated into the crystal lattice of ZnO host. Transmission electron microscope (TEM) measurements showed the sizes of the ZnO quantum dots decreased with the increase of Eu³⁺ and Er³⁺ doping concentration, and the quantum-dot chains were formed by codoping with Eu³⁺ and Er³⁺. The green emissions in the photoluminescence spectra were attributed to 4f-4f of Er³⁺ inner shell ²H_11/2 → ⁴I_15/2 and ⁴S_3/2 → ⁴I_15/2 transitions, and the characteristic red emissions of Eu³⁺ ions were attributed to the ⁵D₀ → ⁷F₁ and ⁵D₀ → ⁷F₂ transitions, respectively. Moreover, the red emission of the Eu³⁺ ions gradually decreased with the Er³⁺ ions doping concentration increased, which may be due to the different energy storage centers in the powders.     

Thermal loading induced near-infrared broadband upconversion emission of Sm-doped β-NaYbF4 nano-phosphors

A non-closed hydrothermal synthetic processing is improved to synthesize Sm³⁺ doped β-NaYbF₄ nano-phosphors at 98 °C without any high-temperature and high-pressure treatments as a final step. Novel green, red, and near-infrared broadband (799-873 nm) upconversion emissions of Sm³⁺-doped β-NaYbF₄ nano-phosphors under 980 nm excitation are observed. These UC emissions can be assigned to the Sm³⁺ transitions of ⁴G_J, ⁴F_3/2 and ⁶F_11/2→⁶H_J. The half-width of 873 nm emission band is broadened nearly two-fold through the annealing treatment for nano-phosphors. The upconversion process in Yb³⁺-Sm³⁺ system is discussed based on energy transfer mechanisms.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Eu photoluminescence enhancement due to thermal energy transfer in Eu2O3-doped SiO2-B2O3-PbO2 glasses system

In this work, Eu³⁺-doped lead borosilicate glasses (SiO₂-B₂O₃-PbO₂) synthesized by fusion method had their optical properties investigated as a function of temperature. Atomic Force Microscopy images obtained for a glass matrix annealed at 350 and 500 °C show a precipitated crystalline phase with sizes 11 and 21 nm, respectively. Besides, as the temperature increases from 350 to 300 K a strong Eu³⁺ photoluminescence (PL) enhancement takes place. This anomalous feature is attributed to the thermally activated carrier transfer process from nanocrystals and charged intrinsic defects states to Eu³⁺ energy levels. In addition, the PL peaks in this temperature range were assigned to the Eu³⁺ transitions ⁵D₀→⁷F₂, at 612 nm, ⁵D₀→⁷F₁, at 595 nm, and ⁵D₀→⁷F₀, at 585 nm. It was also observed that the ⁵D₀→⁷F₃ and ⁵D₀→⁷F₄ PL bands at 655 and 700 nm, respectively, show a continuous decrease in intensity as the temperature increases.     

Photoluminescence properties of Eu-doped ZnO films grown by sputtering-assisted metalorganic chemical vapor deposition

Photoluminescence (PL) properties of Eu-doped ZnO (ZnO:Eu) grown by a sputtering-assisted metalorganic chemical vapor deposition technique were investigated. In PL measurements at 300 K, the samples annealed at 600 °C for 30 min showed clear red-emission lines due to the intra-4f shell transition of ⁵D₀→⁷F_J (J=0–4) in Eu³⁺. In photoluminescence excitation (PLE) spectra, the PL was observed under the high-energy excitation above the band-gap energy of ZnO (indirect excitation) and the low-energy excitation resonant to the energy levels of ⁷F₀–⁵D₃ and ⁷F₀–⁵D₂ transitions in Eu³⁺ (direct excitation). The PL lifetime under the indirect excitation was shorter than that under the direct excitations. These PL properties revealed that the energy transfer from ZnO host to Eu³⁺ was accompanied under indirect excitation.     

Dependence of photoluminescent properties of cubic Y2O3:Tb nanocrystals on particle size and temperature

Temperature-dependent spectral properties in the cubic Y₂O₃:Tb³⁺ nanocrystals (NCs, 10-70 nm) under 488 nm excitation were studied and compared to that in the bulk. In NCs, emission lines assigned to the ⁵D₄-⁷F_J (J=1-6) transitions of Tb³⁺ ions and a broad band originated from oxygen defects were observed. As a function of temperature, two intensity maximums of the ⁵D₄-Σ⁷F_J transitions appeared in the NCs, at ∼250 and ∼500 K, while in the bulk only one maximum appeared at ∼250 K. The relative intensity of the maximum at ∼500 K to that at ∼250 K increased with decreasing particle size. The intensity maximum of the band emissions that came from the oxygen defects appeared in the range of 500-600 K. The appearance of intensity maximum as a function of temperature was attributed to the rivalry between thermal quenching process and phonon-assisted excitation. The appearance of two maxima in the NCs was attributed to the luminescence contributed by different Tb³⁺ centers, the internal and the surface. The emission for the surface Eu³⁺ centers has higher quenching temperature in contrast to that for the internal centers.     

A potential reddish orange emitting phosphor Ca2BO3Cl:Eu for white light-emitting diodes

A series of phosphors Ca₂BO₃Cl:Eu³⁺ were synthesized by using a high-temperature solid-state reaction technique, and their UV–vis luminescence properties were investigated. The f–f transitions of Eu³⁺ in the host lattice were assigned and discussed. The excitation and emission spectra indicate that this phosphor can be effectively excited by ultraviolet (394 nm), and exhibit reddish orange emission corresponding to the ⁵D₀→⁷F_J (J=0, 1, 2) transitions of Eu³⁺. The influence of the doping concentration and charge compensators on the relative emission intensity of Eu³⁺ was investigated, and the optimum doping concentration is 0.04. The critical distance R_c was estimated to be 17.1 Å in terms of the concentration quenching data. The present study suggests that Ca₂BO₃Cl:Eu³⁺ can be a potential candidate as an UV-convertible phosphor for white light-emitting diodes (LEDs).     

Glass composition dependence of Eu ion red fluorescence

Eu³⁺ ion-doped B₂O₃-, SiO₂-, and P₂O₅-based glasses were prepared by the melt-quenching method, and their absorption, fluorescence, and excitation spectra were recorded and assigned. The glass composition dependence of the fluorescence was investigated to obtain the high brightness of the red fluorescence due to the ⁵D₀→⁷F₂ transition of the Eu³⁺ ion. The integrated intensity of the red fluorescence was the strongest at the Eu₂O₃ concentration of 3.5 mol% because the cross-relaxation (CR) processes, (⁵L₆→⁵D_J^′)→(⁷F_J^*←⁷F_J^#) and (⁵D_J→⁵D_J^′)→(⁷F_J^*←⁷F_J^#) (3≧J>J′≧0, 6≧J^*>J^#≧0) between the Eu³⁺ ions were promoted, but the CR processes, (⁵D₀→⁷F_J^′)→∑_m(⁷F_J^*←⁷F_J^″)_m (6≧J′≧0, 6≧J^*>J^″≧0), between the excited Eu³⁺ ion at the ⁵D₀ level and m ions of Eu³⁺ in the ⁷F_J^″ levels were depressed. The former CR processes, (⁵L₆→⁵D_J^′)→(⁷F_J^*←⁷F_J^#) and (⁵D_J→⁵D_J^′)→(⁷F_J^*←⁷F_J^#) were enhanced in the host glasses consisted of the cations with small ionic radius. In this study, a 70B₂O₃-30CaO-3.5Eu₂O₃ glass showed the strongest red fluorescence.     

PL and EL characterizations of ZnO:Eu, Li films derived by sol-gel process

ZnO:Eu³⁺, Li⁺ films prepared by the dip-coating method were characterized by photoluminescence (PL) and electroluminescence (EL). When the ZnO:Eu³⁺, Li⁺ films were excited using UV light with energy corresponding to the band-to-band excitation of the host matrix, the PL spectra showed emissions from both ZnO and Eu³⁺ ions, while their EL spectra showed emissions only from Eu³⁺ ions, and no emission from ZnO could be detected. It is found that the EL emission intensity B is dependent on the applied voltage, B=B_o exp(−bV^−1/2). With increasing frequency, the EL intensity dramatically increases at lower frequencies (<1000 Hz), and then increases gradually at higher frequencies (>1000 Hz).     

Synthesis, microstructure and photoluminescence of Eu/Tb activated Y2SiO5 nanophosphors by new silicate sources

Y_2−xTb_xSiO₅ and Y_2−xEu_xSiO₅ nanophosphors with seven different kinds of silicate sources were synthesized by sol-gel method. The structures have been investigated to be composed of nanometer-size grains of 30-60 nm through X-ray diffraction (XRD) and scanning electron microscopy (SEM) was used to compare the different morphology of patterns from seven different silicon sources. The photoluminescence of Y_2−xTb_xSiO₅ was investigated as a function of silicate sources and the results revealed that these nanometer materials showed the characteristic emission ⁵D₄ → ⁷F_J (J = 6, 5, 4, 3) of Tb ions. The characteristic emission ⁵D₀ → ⁷F_J (J = 1, 2, 4) of Eu ions was also found in the materials of Y_2−xEu_xSiO₅.     

Synthesis and luminescent properties of oleic acid (OA)-modified CaF2: Eu nanocrystals

The OA-modified CaF₂: Eu nanocrystals that can be well dispersed in chloroform to form a clear solution were synthesized and characterized. The nanocrystals have a roughly spherical shape with particle diameter of about 10 nm. Possible mechanism was proposed to explain the growth process. Upon the excitation at 395 nm, the room-temperature emission spectrum of the nanocrystals in chloroform presents the characteristic transitions ⁵D₀→⁷F_J of Eu³⁺ ions, with ⁵D₀→⁷F₂ (610 nm) transition as the most prominent group. The luminescence decay of Eu³⁺ ions in CaF₂ nanocrystals was also investigated and two luminescence lifetimes of 737 μs (11.2%) and 2.08 ms (88.8%) were obtained.     

Spectra, energy levels, and symmetry assignments for Stark components of Eu(4f) in gadolinium gallium garnet (Gd3Ga5O12)

Absorption and fluorescence spectra observed between 450 and 750 nm at 85 K and room temperature (300 K) are reported for Eu³⁺(4f⁶) in single-crystal Czochralski-grown garnet, Gd₃Ga₅O₁₂ (GGG). The spectra represent transitions between the ^2S+1L_J multiplets of the 4f⁶ electronic configuration of Eu³⁺ split by the crystal field of the garnet. In absorption, Eu³⁺ transitions are observed from the ground state, ⁷F₀, and the first excited multiplet, ⁷F₁, to multiplet manifolds ⁵D₀, ⁵D₁, and ⁵D₂. The Stark splitting of the ⁷F_J multiplets (J=0-6) was determined by analyzing the fluorescence transitions from ⁵D₀, ⁵D₁, and ⁵D₂ to ⁷F_J. The Eu³⁺ ions replace Gd³⁺ ions in sites of D₂ symmetry in the lattice during crystal growth. Associated with each multiplet manifold are 2J+1 non-degenerate Stark levels characterized by one of four possible irreducible representations (irreps) assigned by an algorithm based on the selection rules for electric-dipole (ED) and magnetic-dipole (MD) transitions between Stark levels in D₂ symmetry. The quasi-doublet in ⁵D₁ was characterized by an analysis of the magneto-optical spectra obtained from the transitions observed between ⁵D₁ and ⁷F₁. A parameterized Hamiltonian defined to operate within the entire 4f⁶ electronic configuration of Eu³⁺ was used to model the experimental Stark levels and their irreps. The crystal-field parameters were determined through use of a Monte-Carlo method in which nine independent crystal-field parameters, were given random starting values and optimized using standard least-squares fitting between calculated and experimental levels. The final fitting standard deviation between 57 calculated-to-experimental Stark levels is 5.9 cm⁻¹. The choice of coordinate system, in which the nine are real and the crystal-field z-axis is parallel to the [0 0 1] crystal axis and perpendicular to the xy plane, is identical to the choice we used previously in analyzing the spectra of Er³⁺ and Ho³⁺ garnets.     

Optical absorption and photoluminescence studies of Eu-doped phosphate and fluorophosphate glasses

Phosphate (P₂O₅+K₂O+BaO+Al₂O₃+Eu₂O₃) and fluorophosphate (P₂O₅+K₂O+BaO+BaF₂+Al₂O₃+Eu₂O₃) glasses with different Eu³⁺ ion concentrations have been prepared and characterized through optical absorption, photoluminescence and decay times. An intense red luminescence is observed from the ⁵D₀ emitting level of Eu³⁺ ions in these glasses. The relative luminescence intensity ratio of ⁵D₀→⁷F₂→⁵D₀→⁷F₁ transitions has been evaluated to estimate the local site symmetry around the Eu³⁺ ions. The emission spectra of these glasses show a complete removal of degeneracy for the ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transitions. Second and fourth rank crystal-field (CF) parameters have been calculated together with the CF strength parameter by assuming the C_2v symmetry for the Eu³⁺ ions in both the phosphate and fluorophosphate glasses. Judd-Ofelt parameters have been evaluated from the luminescence intensity ratios of ⁵D₀→⁷F_J (J=2, 4 and 6) to ⁵D₀→⁷F₁ transitions. These parameters have been used to derive radiative properties such as transition probabilities, branching ratios, radiative lifetimes and peak stimulated emission cross-sections for the ⁵D₀→⁷F_J transitions. Decay curves of the ⁵D₀ level of Eu³⁺ ions in these two Eu³⁺:glass systems have been measured by monitoring the ⁵D₀→⁷F₂ transition (611 nm) at room temperature. The experimental lifetime of the ⁵D₀ level in the title glasses is found to be higher than Eu³⁺-doped niobium phosphate glasses. The analysis indicates that the lifetime of the ⁵D₀ level is found to be less sensitive to the Eu³⁺ ion concentration and addition of BaF₂ has no significant effect on the optical properties of Eu³⁺-doped phosphate glasses.     

Upconversion luminescence in Yb/Tb-codoped monodisperse NaYF4 nanocrystals

Upconversion (UC) luminescence in monodisperse NaYF₄:Yb³⁺/Tb³⁺ nanocrystals was observed under diode laser excitation of 970 nm, which were synthesized by a hydrothermal method. UC emissions at 380, 413, 436 nm and at 488, 542, 584, 620 nm arise from transitions ⁵D₃(⁵G₆) → ⁷F_J(J = 6, 5, 4) and ⁵D₄ → ⁷F_J(J = 6, 5, 4, 3) of Tb³⁺ ions, respectively. UC mechanisms are proposed based on spectral, kinetic, decay time measurements, and pump power dependence analyses. Blue, green and red emissions originate from the same long-lived (milliseconds) upper ⁵D₄ state, which promises the potential applications of these monodisperse Yb³⁺/Tb³⁺-codoped NaYF₄ nanocrystals in the field of photonics, lasers and biomedicine.     

Improved color purity in nano-size Eu-doped YBO3 red phosphor

Nano-size YBO₃:Eu³⁺ phosphor has been synthesized by the co-precipitation method. X-ray diffraction (XRD) pattern confirmed the formation of hexagonal vaterite-type structures of YBO₃:Eu³⁺ nanoparticles. The transmission electron microscopy (TEM) study revealed the formation of spherical YBO₃:Eu³⁺ nanoparticles with size 20-40 nm. The photoluminescence spectra revealed that the ratio of the red emission (⁵D₀-⁷F₂) to the orange emission (⁵D₀-⁷F₁) was much higher in the synthesized nano-size YBO₃:Eu³⁺ phosphor. The improved relative intensity, i.e., higher R/O value of emission peaks, is due to a lower symmetry of crystal field around Eu³⁺ ions.