Combined EELS, LEED and SR-XPS study of ultra-thin crystalline layers of indium nitride on InP(1 0 0)—Effect of annealing at 450 °C

In this study, InP(1 0 0) surfaces were bombarded by argon ions in ultra high vacuum. Indium metallic droplets were created in well controlled quantities and played the role of precursors for the nitridation process. A glow discharge cell was used to produce a continuous plasma with a majority of N atomic species. X-ray photoelectron spectroscopy (XPS) studies indicated that the nitrogen combined with indium surface atoms to create InN thin films (two monolayers) on an In rich-InP(1 0 0) surface. This process occurred at low temperature: 250 °C. Synchrotron radiation photoemission (SR-XPS) studies of the valence band spectra, LEED and EELS measurements show an evolution of surface species and the effect of a 450 °C annealing of the InN/InP structures. The results reveal that annealing allows the crystallization of the thin InN layers, while the LEED pattern shows a (4 × 1) reconstruction. As a consequence, InN related structures in EELS and valence bands spectra are different before and after the annealing. According to SR-XPS measurements, the Fermi level is found to be pinned at 1.6 eV above the valence band maximum (VBM).     

Hydrogen adsorption on GaAs(0 0 1)-c(4 × 4)

Exposure of the As-terminated GaAs(0 0 1)-c(4 × 4) reconstructed surface to atomic hydrogen (H) at different substrate temperatures (50-480 °C) has been studied by reflection high-energy electron diffraction (RHEED) and scanning tunnelling microscopy (STM). Hydrogen exposure at low temperatures (∼50 °C) produces a disordered (1 × 1) surface covered with AsH_x clusters. At higher temperatures (150-400 °C) exposure to hydrogen leads to the formation of mixed c(2 × 2) and c(4 × 2) surface domains with H adsorbed on surface Ga atoms that are exposed due to the H induced loss of As from the surface. At the highest temperature (480 °C) a disordered (2 × 4) reconstruction is formed due to thermal desorption of As from the surface. The results are consistent with the loss of As from the surface, either through direct thermal desorption or as a result of the desorption of volatile compounds which form after reaction with H.     

Wet sulfur passivation of GaSb(1 0 0) surface for optoelectronic applications

A comparative analysis of the properties of the non-passivated and S-passivated GaSb(1 0 0) surfaces has been performed through PL, AFM and RHEED characterization. The samples treated with a 1 M Na₂S aqueous solution demonstrate an increase in the 5 K PL intensity. According to AFM data, the annealing of the S-passivated GaSb(1 0 0) leads to the formation of the clean flat (1 0 0) surface. Moreover, after annealing the PL intensity of the S-passivated GaSb(1 0 0) surfaces decreases by 20%, whereas for the non-passivated samples it drops by more than a factor of 4. The method of wet sulfur passivation has shown great effectiveness in pre-epitaxial processing for LPE and MBE growth of the GaSb-related materials for optoelectronics.     

Structure and composition of chemically prepared and vacuum annealed InSb(0 0 1) surfaces

The InSb(0 0 1) surfaces chemically treated in HCl-isopropanol solution and annealed in vacuum were studied by means of X-ray photoelectron spectroscopy (XPS), low energy electron diffraction (LEED) and electron energy-loss spectroscopy (EELS). The HCl-isopropanol treatment removes indium and antimony oxides and leaves on the surface about 3 ML of physisorbed overlayer, containing indium chlorides and small amounts of antimony, which can be thermally desorbed at 230 °C. The residual carbon contaminations were around 0.2-0.4 ML and consisted of the hydrocarbon molecules. These hydrocarbon contaminations were removed from the surface together with the indium chlorides and antimony overlayer. With increased annealing temperature, a sequence of reconstructions were identified by LEED: (1 × 1), (1 × 3), (4 × 3), and (4 × 1)/c(8 × 2), in the order of decreasing Sb/In ratio. The structural properties of chemically prepared InSb(0 0 1) surface were found to be similar to those obtained by decapping of Sb-capped epitaxial layers.     

Electronic properties of clean unreconstructed 6H-SiC(0 0 0 1) surfaces studied by angle resolved photoelectron spectroscopy

The properties of the clean and unreconstructed 6H-SiC(0 0 0 1) and 6H-SiC surfaces were investigated by means of angle-resolved photoelectron spectroscopy (ARPES). These highly metastable surfaces were prepared by exposing hydrogen terminated surfaces to a high flux of synchrotron radiation. On both surfaces we find a band of surface states with 1 × 1 periodicity assigned to unsaturated Si and C dangling bonds located at 0.8 eV and 0.2 eV above the valence band maximum, respectively. Both states are located below the Fermi level. The dispersion of the surface bands amounts to 0.2 eV for the Si derived band and 0.7 eV for C derived band. It is suggested that the electronic properties of these surfaces are governed by strong correlation effects (Mott-Hubbard metal insulator transition). The results for the (0 0 0 1) surface are directly compared to Si-rich (√3 × √3)R30° reconstructed surface. Distinct differences in electronic structure of the (√3 × √3)R30° and 1 × 1 surfaces are observed.     

Nano-structures in YSZ(1 0 0) surfaces: Implications for metal deposition experiments

The surface morphology of yttria stabilized zirconia (YSZ)(1 0 0) single crystals are examined by AFM and XPS before and after thermal annealing in air to 1000 °C. The surfaces show a large variability in topography which can be categorized in three types: (1) surfaces with well defined terraces, (2) surfaces with etch pits and no visible terraces, (3) surfaces with large square or rectangular holes with flat bottoms. All three types of surfaces show a large number of defects (pits, adatoms, steps) originating from the manufacturing process, and certain samples show large nano-structured arrays of self-organized lines at step edges. The evolution of the surfaces with time at 1000 °C and with higher temperatures was studied. Terraces are ultimately obtained for all sample types at 1300 °C, but the terrace shape is affected by the original defect structure. This history dependence is attributed to defect interactions modifying the annealing process. This is true even for UHV samples prepared using sputter-anneal cycles. The surface type is found to affect the nucleation, growth and sintering behaviour of palladium deposited by electron beam evaporation. For type 3 samples the metal nucleates at step edges outside the holes to particles 6 Å in height, following heating to 135 °C the particles move inside the holes forming agglomerates up to 20 Å.     

GaN nucleation on (0 0 0 1)-sapphire via ion-induced nitridation of gallium

The growth of epitaxial GaN films on (0 0 0 1)-sapphire has been investigated using X-ray photoelectron spectroscopy (XPS) and low energy electron diffraction (LEED). In order to investigate the mechanism of the growth in detail, we have focused on the nitridation of pre-deposited Ga layers (droplets) using ion beam-assisted molecular beam epitaxy (IBA-MBE). Comparative analysis of XPS core-level spectra and LEED patterns reveals, that nitride films nucleate as epitaxial GaN islands. The wetting of the surface by GaN proceeds via reactive spreading of metallic Ga, supplied from the droplets. The discussed growth model confirms, that excess of metallic Ga is beneficial for GaN nucleation.     

GaN/LiNbO3 (0 0 0 1) interface formation calculated from first-principles

The stable adsorption sites for both Ga and N ions on the ideal and on the reconstructed LiNbO₃ (0 0 0 1) surface are determined by means of first-principle total energy calculations. A single N layer is found to be more strongly bound to the substrate than a single Ga layer. The adsorption of a GaN monolayer on the polar substrate within different orientations is then modeled. On the basis of our results, we propose a microscopic model for the GaN/LiNbO₃ interface. The GaN and LiNbO₃ (0 0 0 1) planes are parallel, but rotated by 30° each other, with in-plane epitaxial relationship [1 0 0]_GaN‖ [1 1  0]_LiNbO3. In this way the (0 0 0 1) plane lattice mismatch between GaN and LiNbO₃ is minimal and equal to 6.9% of the GaN lattice constant. The adsorbed GaN and the underlying LiNbO₃ substrate have parallel c-axes.     

Chemically prepared well-ordered InP(0 0 1) surfaces

In the present work HCl-isopropanol treated and vacuum annealed InP(0 0 1) surfaces were studied by means of low-energy electron diffraction (LEED), soft X-ray photoemission (SXPS), and reflectance anisotropy (RAS) spectroscopies. The treatment removes the natural oxide and leaves on the surface a physisorbed overlayer containing InCl_x and phosphorus. Annealing at 230 °C induces desorption of InCl_x overlayer and reveals a P-rich (2 × 1) surface. Subsequent annealing at higher temperature induces In-rich (2 × 4) surface. The structural properties of chemically prepared InP(0 0 1) surfaces were found to be similar to those obtained by decapping of As/P-capped epitaxial layers.     

Growth and structure of vanadium oxide on anatase (1 0 1) terraces

The interaction of vanadium oxide with epitaxial anatase films exposing (1 0 1) terraces was characterized. The TiO₂ films were grown on vicinal LaAlO₃ (1 1 0) substrates by oxygen plasma-assisted molecular beam epitaxy (OPA-MBE); reflection high energy and low energy electron diffraction (RHEED and LEED) indicated that the films exposed (1 0 1) terraces of the anatase TiO₂ polymorph. When a vanadium oxide monolayer was deposited onto the anatase surface by OPA-MBE at 725 K, only (1 × 1) RHEED and LEED patterns were observed. The V X-ray photoelectron spectroscopy (XPS) peak intensities indicated that the monolayer wetted the anatase surface and so the diffraction patterns were attributed to an epitaxial vanadia layer. Analysis of the vanadium oxide monolayer by X-ray and ultraviolet photoelectron spectroscopies revealed that the V was predominantly 5+. When the vanadia coverage was increased at 725 K, Auger electron spectra showed only very slow attenuation of the anatase Ti peaks while spots began to develop in RHEED patterns recorded along the LaAlO₃ direction; both indicative of 3-D cluster formation. In the orthogonal direction, the RHEED patterns showed unusual diagonal streaks. Meanwhile, the (1 × 1) LEED pattern persisted even after 30 nm of vanadia was deposited. This was attributed to gaps between the 3-D clusters exposing the epitaxial monolayer. Core level XPS spectra of the 3-D clusters revealed a broad V 2p_3/2 peak that was centered at the position expected for V⁴⁺ but could be deconvoluted into three peaks corresponding to V³⁺, V⁴⁺, and V⁵⁺. It is shown that crystallographic shear that accommodates such variations in the oxygen content of V oxides can lead to the diagonal streaks in RHEED patterns recorded along the LaAlO₃ [0 0 1] direction even as the pattern in the orthogonal direction shows sharp transmission spots. The results show that vanadia growth on anatase (1 0 1) proceeds through the Stranski-Krastanov mode with a strong vanadia-titania interaction stabilizing a dispersed vanadia monolayer. The results are compared with previous data for vanadia growth on anatase (0 0 1) where smooth, epitaxial VO₂ films grow ad infinitum.     

Growth of oriented crystalline Ag nanoislands on air-exposed Si(0 0 1) surfaces

Growth of Ag islands under ultrahigh vacuum condition on air-exposed Si(0 0 1)-(2 × 1) surfaces has been investigated by in-situ reflection high energy electron diffraction (RHEED). A thin oxide is formed on Si via exposure of the clean Si(0 0 1)-(2 × 1) surface to air. Deposition of Ag on this oxidized surface was carried out at different substrate temperatures. Deposition at room temperature leads to the growth of randomly oriented Ag islands while well-oriented Ag islands, with (0 0 1)_Ag||(0 0 1)_Si, [1 1 0]_Ag||[1 1 0]_Si, have been found to grow at substrate temperatures of ≥350 °C in spite of the presence of the oxide layer between Ag islands and Si. The RHEED patterns show similarities with the case of Ag deposition on H-passivated Si(0 0 1) surfaces.     

Structure and electronic properties of gold adsorbed on Ti(0 0 0 1)

The Au/Ti(0 0 0 1) adsorption system was studied by low energy electron diffraction (LEED) and photoemission spectroscopy with synchrotron radiation after step-wise Au evaporation onto the Ti(0 0 0 1) surface. For adsorption of Au at 300 K, no additional superstructures were observed and the (1 × 1) pattern of the clean surface simply became diffuse. Annealing of gold layers more than 1 ML thick resulted in the formation of an ordered Au-Ti surface alloy. Depending on the temperature and annealing time, three surface reconstructions were observed by LEED: (√3 × √3) R30°, (2 × 2) and a one-dimensional incommensurate (√3 × √3) rectangular pattern. The Au 4f core level and valence band photoemission spectra provided evidence of a strong chemical interaction between gold and titanium. The data indicated formation of an intermetallic interface and associated valence orbital hybridization, together with diffusion of gold into the bulk. Au core-level shifts were found to be dependent on the surface alloy stoichiometry.     

Structure, defects, and impurities at the rutile TiO2(0 1 1)-(2 × 1) surface: A scanning tunneling microscopy study

The titanium dioxide rutile (0 1 1) (equivalent to (1 0 1)) surface reconstructs to a stable (2 × 1) structure upon sputtering and annealing in ultrahigh vacuum. A previously proposed model (T.J. Beck, A. Klust, M. Batzill, U. Diebold, C. Di Valentin, A. Selloni, Phys. Rev. Lett. 93 (2004) 036104/1) containing onefold coordinated oxygen atoms (titanyl groups, TiO) is supported by Scanning Tunneling Microscopy (STM) measurements. These TiO sites are imaged bright in empty-states STM. A few percent of these terminal oxygen atoms are missing at vacuum-annealed surfaces of bulk-reduced samples. These O vacancies are imaged as dark spots. Their number density depends on the reduction state of the bulk. Double vacancies are the most commonly observed defect configuration; single vacancies and vacancies involving several O atoms are present as well. Formation of oxygen vacancies can be suppressed by annealing a sputtered surface first in vacuum and then in oxygen; annealing a sputtered surface in oxygen results in surface restructuring and a (3 × 1) phase. Anti-phase domain boundaries in the (2 × 1) structure are active adsorption sites. Segregation of calcium impurities from the bulk results in an ordered overlayer that exhibits domains with a centered (2 × 1) periodicity in STM.     

The role of antiphase boundaries during ion sputtering and solid phase epitaxy of Si(0 0 1)

The Si(0 0 1) surface morphology during ion sputtering at elevated temperatures and solid phase epitaxy (SPE) following ion sputtering at room temperature has been investigated using scanning tunneling microscopy. Two types of antiphase boundaries form on Si(0 0 1) surfaces during ion sputtering and SPE. One type of antiphase boundary, the AP2 antiphase boundary, contributes to the surface roughening. AP2 antiphase boundaries are stable up to 700 °C, and ion sputtering and SPE performed at 700 °C result in atomically flat Si(0 0 1) surfaces.     

Structural analysis of the c(4 × 2) reconstruction in Si(0 0 1) and Ge(0 0 1) surfaces by low-energy electron diffraction

The c(4 × 2) structures in (0 0 1) surfaces of Si and Ge have been studied by low-energy electron diffraction (LEED). Using a proper cleaning method for the Si surface, we were able to observe clear c(4 × 2) LEED patterns up to incident energy of ∼400 eV as well as the Ge surface. Extensive experimental intensity-voltage curves allowed us to optimize the asymmetric dimer model up to the eighth layer (including the dimer layer) in depth in the dynamical LEED calculation. Optimized structural parameters are almost the same for the Si and Ge except for the height of the buckled-up atom of the asymmetric dimer. For the Ge surface, the structural parameters are in excellent agreement with those obtained by a previous theoretical calculation. The tilt angle and bond length of the dimer are 18 ± 1 (19 ± 1)° and 2.4 ± 0.1 (2.5 ± 0.1) Å for the Si(0 0 1) (Ge(0 0 1)), respectively.     

RHEED studies during growth of TiN/SiNx/TiN trilayers on MgO(0 0 1)

TiN/SiN_x/TiN(0 0 1) trilayers have been deposited on MgO(0 0 1) substrates using ultra-high vacuum based reactive magnetron sputtering and studied by in situ reflection high energy electron diffraction (RHEED). Depositions were carried out at 500 °C and 800 °C, with SiN_x layer thicknesses between 3 and 300 Å. Here, we find that SiN_x(0 0 1) layers grown at 800 °C exhibit 1 × 4 surface reconstructions along orthogonal 〈1 1 0〉 directions up to a critical thickness of ∼9 Å, where an amorphous phase forms. Growth of TiN overlayers on the reconstructed SiN_x(0 0 1) layers yield RHEED patterns indicating the growth of (0 0 1)-oriented epitaxial layers with a 1 × 1 reconstruction. For the case of amorphous SiN_x layers the TiN overlayers grow polycrystalline.     

The role of nitrogen in the preferential chromium segregation on the ferritic stainless steel (1 1 1) surface

The temperature dependence on the segregation behavior of the ferritic stainless steel single crystal (1 1 1) surface morphology has been examined by scanning tunneling microscopy (STM), Auger electron spectroscopy (AES), and low energy electron diffraction (LEED). AES clearly showed the surface segregations of chromium and nitrogen upon annealing. Nanoscale triangular chromium nitride clusters were formed around 650 °C and were regularly aligned in a hexagonal configuration. In contrast, for the ferritic stainless steel (1 1 1) surface with low-nitrogen content, chromium and carbon were found to segregate on the surface upon annealing and Auger spectra of carbon displayed the characteristic carbide peak. For the low-nitrogen surface, LEED identified a facetted surface with (2 × 2) superstructure at 650 °C. High-resolution STM identified a chromium carbide film with segregated carbon atoms randomly located on the surface. The facetted (2 × 2) superstructure changed into a (3 × 3) superstructure with no faceting upon annealing at 750 °C. Also, segregated sulfur seems to contribute to the reconstruction or interfacial relaxation between the ferritic stainless steel (1 1 1) substrate and chromium carbide film.     

Electronic structure of oxidized SiC(0 0 0 1) studied by inverse photoemission spectroscopy

Starting from the silicon rich (3 × 3) reconstruction of SiC(0 0 0 1) we prepared oxidized surfaces by hydrogen etching as well as by exposure to molecular oxygen. LEED pictures show a (1 × 1)-reconstructed surface with a faint structure being more pronounced for the hydrogen-etched surfaces. Auger spectra reveal a distinct change in the shape of the Si_LVV peak indicating the existence of Si-O bonds on the surface. Inverse photoemission (IPE) is employed to study the electronic structure above the Fermi level of the oxidized samples. On the hydrogen-etched surface difference spectra reveal a surface feature at 1 eV above the Fermi level that presumably originates from an isolated dangling bond on ordered patches of the oxidized surface.     

Observation of a (√3 × √3)-R30° reconstruction on GaN(0 0 0 1) by RHEED and LEED

A new reconstruction of √3 × √3-R30° has been observed on a GaN film grown on a 6H-SiC (0 0 0 1)-√3 × √3 surface using RHEED and LEED experimental techniques. The experimental LEED PF shows that the GaN film is Ga-terminated hexagonal. The surface is a mixture of two structures with a single bilayer height difference between them. One is a √3 × √3-R30° reconstruction with Ga-adatoms occupying the T4 sites. Another is a Ga-terminated 1 × 1 with no extra Ga on top. The area ratio of the √3 × √3 part to the 1 × 1 part is slightly larger than 1. The first principle total energy calculations and Tensor-LEED I-V curves simulations further confirm this structure model.