The Fe/ZnO(0 0 0 1) interface: Formation and thermal stability

The room temperature growth mode and the interface reaction of Fe films on single crystalline ZnO(0 0 0 1) substrates prepared in ultra high vacuum (UHV) has been investigated by means of X-ray photoelectron and Auger electron spectroscopy (XPS, AES), low energy electron diffraction (LEED) and low energy ion scattering spectroscopy (LEIS). The results show that Fe grows in the pseudo layer-by-layer mode. At ambient temperature the deposited Fe film reduces the underlying ZnO single crystal resulting in FeO at the interface and metallic Zn, which partially diffuses into the remaining Fe overlayer. Annealing leads to a stepwise oxidation of the Fe to FeO (670 K) and Fe₂O₃ (820 K). The Fe₂O₃ mixes with the substrate resulting in two (1 1 1) oriented textures of a spinel phase found by electron backscatter diffraction analysis (EBSD). Fe-based spin-injection may play a vital role for ZnO-based spintronic devices.     

Structural and morphological evolution of Co on faceted Pt/W(1 1 1) surface upon thermal annealing

The structural and morphological changes of a 1.1 monolayer (ML) Pt deposit on W(1 1 1) have been investigated in situ, in ultra-high vacuum, as a function of the annealing temperature from 700 to 1340 K, by a combination of grazing incidence X-ray diffraction and grazing incidence small-angle X-ray scattering. Before annealing, the thin Pt layer is two-dimensional and lattice-matched to the W(1 1 1) surface. The faceting of Pt/W(1 1 1) towards nanoscale three-sided pyramids with {2 1 1} facets has been detected from 715 K. At this stage, the pyramids, which have a 5-nm average lateral size, cover nearly perfectly the surface. At higher temperatures, they increase in size. The role of the edge energy in the nanofaceting process is discussed. In addition, 4 MLs Co are deposited at room temperature on the smallest Pt/W pyramids. The obtained three-dimensional Co islands are correlated with the Pt/W nanopyramids and Co is relaxed on Pt/W. At approximately 800 K, a CoPt alloy is formed and becomes better ordered as the annealing temperature increases. At 1100 K, both defaceting and phase separation begin; the CoPt alloy segregates on the W(1 1 1) flat surface, while Co forms an epitaxial layer on the {2 1 1} facets. In addition, in the temperature range of 1100-1200 K, a great majority of {2 1 1} large facets coexist with some {1 1 0} small facets. Finally, the surface becomes flat again at 1250 K.     

Core level photoemission and STM characterization of Ta/Si(1 1 1)-7 × 7 interfaces

We present the results of scanning tunneling microscopy (STM) and photoemission spectroscopy (PES) of the Ta/Si(1 1 1)-7 × 7 system after deposition of Ta at substrate temperatures from 300 to 1250 K. The coverage of Ta varied from 0.05 up to 2.5 of a monolayer (ML). STM shows that at 300 K and coverage less than 1 ML, a disordered chemisorbed phase is formed. Deposition on a hot surface (above 500 K) produces round 3D clusters randomly distributed on the surface. Cluster height and their diameter are found to change drastically with annealing temperature and the Ta coverage. Analysis of photoemission data of the Si 2p core levels shows that at room temperature and at coverage ?1 ML core level binding energy shifts and intensity variations of Si surface related components are observed, which clearly indicate that the reaction starts already at 300 K. Shifts in the binding energy, changes of the peak shapes and intensity of the Ta 4f doublet at higher temperatures can be explained by the formation of stable silicide on the surface.     

The growth of ultrathin Au films on Ni{1 1 1}: A study with medium energy ion scattering

The initial growth of Au on Ni{1 1 1} is strongly influenced by the 15.7% difference in bulk lattice parameter between the two fcc metals. At 400 K, the first monolayer of Au grows on the Ni{1 1 1} surface as a (9 × 9) overlayer with 8 Au-Au spacings being equivalent to 9 Ni-Ni spacings. Umezawa et al. [Physical Review B 57 (1998) 8842; Surface Science 426 (1999) 225] reported that the growth of Au overlayers can occur either via a reverse (R)-mode (i.e., incorporating a stacking fault at the Au-Ni interface) or a normal (N)-mode—the relative proportion of each mode being strongly sensitive to growth temperature. Using the technique of medium energy ion scattering, we examine the growth of Au on Ni{1 1 1} at 400 K. We conclude that, at this deposition temperature, there is a preference for growth via the R-mode (74 ± 9%). In addition, we find that the Au overlayer has a considerably higher density than bulk Au being contracted isotropically by 3.1% in the {1 1 1} plane and also by ∼7% perpendicular to the {1 1 1} plane. We discuss possible explanations for our findings.     

Growth and morphology of the epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) Trilayers

Growth and surface morphology of epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) trilayers constituting a magnetic tunnel junction were investigated by low-energy electron diffraction (LEED) and scanning tunneling microscopy (STM). STM reveals a grain-like growth mode of MgO on Fe(1 1 0) resulting in dense MgO(1 1 1) films at room temperature as well as at 250 °C. As observed by STM, initial deposition of MgO leads to a partial oxidation of the Fe(1 1 0) surface which is confirmed by Auger electron spectroscopy. The top Fe layer deposited on MgO(1 1 1) at room temperature is relatively rough consisting of clusters which can be transformed by annealing to an atomically flat epitaxial Fe(1 1 0) film.     

Formation and hydrogenation of p(2 × 2)-N on Pt(1 1 1)

The formation of a well-ordered p(2 × 2) overlayer of atomic nitrogen on the Pt(1 1 1) surface and its reaction with hydrogen were characterized with reflection absorption infrared spectroscopy (RAIRS), temperature programmed desorption (TPD), low energy electron diffraction (LEED), Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS). The p(2 × 2)-N overlayer is formed by exposure of ammonia to a surface at 85 K that is covered with 0.44 monolayer (ML) of molecular oxygen and then heating to 400 K. The reaction between ammonia and oxygen produces water, which desorbs below 400 K. The only desorption product observed above 400 K is molecular nitrogen, which has a peak desorption temperature of 453 K. The absence of oxygen after the 400 K anneal is confirmed with AES. Although atomic nitrogen can also be produced on the surface through the reaction of ammonia with an atomic, rather than molecular, oxygen overlayer at a saturation coverage of 0.25 ML, the yield of surface nitrogen is significantly less, as indicated by the N₂ TPD peak area. Atomic nitrogen readily reacts with hydrogen to produce the NH species, which is characterized with RAIRS by an intense and narrow (FWHM ∼ 4 cm⁻¹) peak at 3322 cm⁻¹. The areas of the H₂ TPD peak associated with NH dissociation and the XPS N 1s peak associated with the NH species indicate that not all of the surface N atoms can be converted to NH by the methods used here.     

Condensation and desorption of nickel tetra-carbonyl on Cu(1 1 0)

The condensation and desorption of nickel tetra-carbonyl (Ni(CO)₄) on Cu(1 1 0) has been studied by thermal desorption spectroscopy. A quite unusual evolution of the desorption spectra is observed. First a desorption peak appears at around 140 K, which disappears with increasing coverage and merges into a clearly separated new desorption peak at around 150 K. This transformation takes place at a coverage of about 10% of a monolayer. It is suggested that the low temperature peak is due to desorption of monomers. With increasing coverage nucleation and growth of multilayer islands starts, from which the desorption energy is higher due to the higher coordination of the carbonyl molecules, compared to that of the monomers. Evaluation of the multilayer desorption spectra yields a desorption energy of 57.9 kJ/mol (0.60 eV) and an unusually high frequency factor of 1.6 × 10¹⁹ s⁻¹.     

Oxidation of Pt(1 0 0)-hex-R0.7° by gas-phase oxygen atoms

We utilized temperature programmed desorption (TPD), X-ray photoelectron spectroscopy (XPS), electron energy loss spectroscopy (ELS), and low energy electron diffraction (LEED) to investigate the oxidation of Pt(1 0 0)-hex-R0.7° at 450 K. Using an oxygen atom beam, we generated atomic oxygen coverages as high as 3.6 ML (monolayers) on Pt(1 0 0) in ultrahigh vacuum (UHV), almost 6 times the maximum coverage obtainable by dissociatively adsorbing O₂. The results show that oxidation occurs through the development of several chemisorbed phases prior to oxide growth above about 1 ML. A weakly bound oxygen state that populates as the coverage increases from approximately 0.50 ML to 1 ML appears to serve as a necessary precursor to Pt oxide growth. We find that increasing the coverage above about 1 ML causes Pt oxide particle growth and significant surface disordering. Decomposition of the Pt oxide particles produces explosive O₂ desorption characterized by a shift of the primary TPD feature to higher temperatures and a dramatic increase in the maximum desorption rate with increasing coverage. Based on thermodynamic considerations, we show that the thermal stability of the surface Pt oxide on Pt single crystal surfaces significantly exceeds that of bulk PtO₂. Furthermore, we attribute the high stability and the acceleratory decomposition rates of the surface oxide to large kinetic barriers that must be overcome during oxide formation and decomposition. Lastly, we present evidence that structurally similar oxides develop on both Pt(1 1 1) and Pt(1 0 0), therefore concluding that the properties of the surface Pt oxide are largely insensitive to the initial structure of the Pt single crystal surface.     

Stability of ZnO{0 0 0 1} against low energy ion bombardment

The steady-state surface compositions of the polar (O and Zn terminated) faces of ZnO{0 0 0 1} produced by low energy (0.3-2 keV) Ar⁺ ion bombardment were studied by Auger electron spectroscopy and electron energy loss spectroscopy. The alterations produced by the ion bombardment using different ion energies were monitored by calculating the intensity ratios of the low and high energy Zn Auger peaks (59 eV and 994 eV, respectively); Zn and O Auger peaks (59 eV and 510 eV, respectively). Based on the dependence of these ratios on the ion energy and termination of the surface, we could conclude that the stability of the Zn face is higher against the low energy argon ion bombardment-induced compositional changes than that of the O face.     

Adsorption of d-alaninol on Cu(1 0 0)

Adsorption of d-alaninol on Cu(1 0 0) at room temperature has been investigated by photoelectron spectroscopy in the soft X-ray and VUV energy range and low energy electron diffraction (LEED). d-Alaninol was found by LEED to self-assemble at full coverage; core and valence photoemission spectra are presented at low and full coverage. Chemisorption occurs at room temperature. The bonding at low coverage takes place at the hydroxylic group; at full coverage there is evidence of bonding for both hydroxylic and amino groups.     

Adsorption and decomposition of NO on O-covered planar and faceted Ir(2 1 0)

We report on the adsorption and decomposition of NO on O-covered planar Ir(2 1 0) and nanofaceted Ir(2 1 0) with variable facet sizes investigated using temperature programmed desorption (TPD), high-resolution electron energy loss spectroscopy (HREELS), and density functional theory (DFT). When pre-covered with up to 0.5 ML O, both planar and faceted Ir(2 1 0) exhibit unexpectedly high reactivity for NO decomposition. Upon increasing the oxygen coverage to 0.7 ML O, planar Ir(2 1 0) has little activity while faceted Ir(2 1 0) still remains active toward NO decomposition, although NO decomposition is completely inhibited when both surfaces are pre-covered by 1 ML O. NO molecularly adsorbs on O-covered Ir at 300 K. At low NO and oxygen coverage, NO adsorbs on the atop sites of planar Ir(2 1 0) while on the bridge and atop sites of faceted Ir(2 1 0) composed of (1 1 0) and {3 1 1} faces. No evidence for size effects in the decomposition of NO on O-covered faceted Ir(2 1 0) is observed for average facet size in the range 5-14 nm. Our findings should be of importance for development of Ir-based catalysts for NO decomposition under oxygen-rich conditions.     

Methanethiolate structural phases on Cu{1 1 1} observed using a novel fibre-optic low-energy electron diffraction instrument

We have used a novel fibre-optic low-energy electron diffraction (FO-LEED) instrument, capable of low flux measurements that minimise electron beam damage to surface overlayers, to study methanethiolate (CH₃-S-) structural phases formed on Cu{1 1 1} at temperatures between 110 and 300 K. Three structural phases were seen: a (√3 × √3)R30° phase that forms at 110-140 K; a (4 × 4) phase which was observed transiently at 110 K; and a pseudo-{1 0 0} reconstructed phase which forms at room temperature. We discuss these in the context of previous studies of this system, and demonstrate the ability of the FO-LEED instrument to record high-quality LEED patterns and intensity data from a strongly beam-sensitive surface.     

Formation and structure of a (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy

An ordered (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy can be formed by vapor depositing one-monolayer Ge on a Pt(1 1 1) substrate at room temperature and subsequently annealing at 900-1200 K. The long-range order of this structure was observed by low energy electron diffraction (LEED) and confirmed by scanning tunneling microscopy (STM). The local structure and alloying of vapor-deposited Ge on Pt(1 1 1) at 300 K was investigated by using X-ray Photoelectron Diffraction (XPD) and low energy alkali ion scattering spectroscopy (ALISS). XPS indicates that Ge adatoms are incorporated to form an alloy surface layer at ∼900 K. Results from XPD and ALISS establish that Ge atoms are substitutionally incorporated into the Pt surface layer and reside exclusively in the topmost layer, with excess Ge diffusing deep into the bulk of the crystal. The incorporated Ge atoms at the surface are located very close to substitutional Pt atomic positions, without any corrugation or “buckling”. Temperature Programmed Desorption (TPD) shows that both CO and NO adsorb more weakly on the Ge/Pt(1 1 1) surface alloy compared to that on the clean Pt(1 1 1) surface.     

Adsorption and decomposition of triethylsilane on Si(1 0 0)

The adsorption and decomposition of triethylsilane (TES) on Si(1 0 0) were studied using temperature programmed desorption (TPD), high resolution electron energy loss spectroscopy (HREELS), electron stimulated desorption (ESD), and X-ray photoelectron spectroscopy (XPS). TPD and HREELS data indicate that carbon is thermally removed from the TES-dosed Si(1 0 0) surface via a β-hydride elimination process. At high exposures, TPD data shows the presence of physisorbed TES on the surface. These species are characterized by desorption of TES fragments at 160 K. Non-thermal decomposition of TES was studied at 100 K by irradiating the surface with 600 eV electrons. ESD of mass 27 strongly suggests that a β-hydride elimination process is a channel for non-thermal desorption of ethylene. TPD data indicated that electron irradiation of physisorbed TES species resulted in decomposition of the parent molecule and deposition of methyl groups on the surface that desorbed thermally at about 900 K. Without electron irradiation, mass 15 was not detected in the TPD spectra, indicating that the production of methyl groups in the TPD spectra was a direct result of electron irradiation. XPS data also showed that following electron irradiation of TES adsorbed on Si(1 0 0), carbon was deposited on the surface and could not be removed thermally.     

Self-organized Fe nanostructures on W(1 1 0)

The magnetic domain structure of Fe wires, ribbons and islands with different shapes that have been prepared under ultra high vacuum conditions on W(1 1 0) are studied with spin polarized low energy electron microscopy. The dimensions of the nanostructures, which are of the order of tens and hundreds of nm, can be controlled by the temperature at which they are produced, by the average Fe coverage and by the substrate morphology. The domain structure of the nanostructures depends on their shape and is determined by the competition between magnetoelastic, shape and magnetocrystalline anisotropies.     

Structure analysis of W(0 0 1)2 × 1-O surface at room and liquid nitrogen temperatures

Surface structure of O-adsorbed W(0 0 1) surface after annealing to 1200 K has been analyzed by low energy electron diffraction at 77 K as well as at room temperature. The optimum structure has tungsten missing rows and oxygen double rows. Furthermore, the R-factor is minimized at the structure that O atoms are adsorbed on one of the two different threefold hollow sites of the (1 1 0) facet appearing on the W(0 0 1)2 × 1 with missing row. However, the results suggest that two domains of O atoms adsorbed on both the two different threefold hollow sites coexist. Then, I-V curves have been analyzed as a function of the mixing ratio of the two domains having different O adsorption sites at room and low temperatures. The energy difference between these two sites has been estimated to be 6.5 meV from the temperature dependence of the mixing ratio.     

FeO(1 1 1) formation by exposure of Fe(1 1 0) to atomic and molecular oxygen

The growth, structure, and morphology of ultrathin iron oxide layers formed on a Fe(1 1 0) single crystal surface are investigated by Auger electron spectroscopy, low energy electron diffraction, and grazing ion scattering. For Fe oxidation by atomic instead of molecular oxygen, the gas exposure can be reduced by almost two orders of magnitude because surface sticking and dissociation are not limiting the growth process. A well-ordered FeO(1 1 1) film with low defect density is only obtained with atomic oxygen. Compared to the bulk, the FeO lattice is laterally compressed by about 5-6% resulting in an in-plane oxygen (Fe) nearest-neighbor distance of 2.87 Å. Independent of the preparation method, long-range structural order is poor if the oxide film thickness is increased to 3-5 layers. This is attributed to the relatively large lattice mismatch between FeO(1 1 1) and Fe(1 1 0).     

CO2 adsorption on the bimetallic Zn-on-Cu(1 1 0) system

Adsorption probability measurements (molecular beam scattering) have been conducted to examine the adsorption dynamics (i.e. the gas-surface energy transfer processes) of CO₂ adsorption on the Zn-on-Cu(1 1 0) bimetallic system. The results indicate surface alloy formation, which is in agreement with prior studies. Depositing Zn at 300 K on Cu(1 1 0), above the condensation temperature of CO₂, leads to a “blocking” of CO₂ adsorption sites by Zn which is incorporated in the Cu(1 1 0) surface. This apparent site blocking effect indicates a lowering of the CO₂ binding energy on the alloyed surface as compared with the clean Cu(1 1 0) support. The Zn coverage has been calibrated by Auger electron spectroscopy and thermal desorption spectroscopy.     

A valence band photoemission study of Pb adsorption on Rh(1 0 0) and Rh(1 1 0)

We have studied the adsorption of Pb on the Rh(1 0 0) and (1 1 0) surfaces by photoemission and low energy electron diffraction (LEED), and tested the chemical properties by adsorption of CO. Pb forms two distinct c(2 × 2) phases on Rh(1 0 0), according to the temperature of the substrate. The phase formed below about 570-620 K, denoted α-c(2 × 2), reduces the coverage of adsorbed CO but does not affect the valence band spectrum of the molecule. The phase formed above this temperature, denoted β-c(2 × 2), also reduces the coverage of adsorbed CO but the valence band spectrum of the adsorbed CO is strongly affected. The two phases are also characterised by a slightly different binding energy of the Pb 5d_5/2 level, 17.54 eV for the α phase and 17.70 for the β phase. The Pb/Rh(1 1 0) surface shows two ordered Pb induced phases, c(2 × 2) and p(3 × 1). CO adsorbs on the first with reduced heat of adsorption and with a valence band spectrum that is strongly altered with respect to CO adsorbed on clean Rh(1 1 0), but does not adsorb on the p(3 × 1) structure at 300 K. We compare the present results with previous results from related systems.     

Study of phase transitions within alumina grown on top of CoAl (1 0 0) surface

The oxidation of CoAl(1 0 0) was investigated by means of Auger electron spectroscopy (AES), low energy electron diffraction (LEED), high resolution electron energy loss spectroscopy (HREELS), and scanning tunneling microscopy (STM). In the case of alumina grown after oxidation with 15,000 L at room temperature, the characteristic EEL spectrum, along with the sharp (2 × 1) LEED pattern observed after annealing at 1000 K, showed that a stable well-ordered θ alumina was formed. The intermediate phase was found after heat treatment at 1150 K. At higher temperatures, the formation of the α-like alumina was observed. The comparative study of as-oxidation versus subsequent annealing of amorphous alumina at high-temperatures revealed a close similarity between the structures of alumina.