Influence of treating frequency on microstructure and properties of Al2O3 coating on 304 stainless steel by cathodic plasma electrolytic deposition

Alumina ceramic coatings were fabricated on 304 stainless steel by cathodic plasma electrolytic deposition (CPED). Influence of treating frequency of the power supply on the microstructure and properties of the coatings were studied. The results indicated that coatings obtained at various frequencies on 304 stainless steels were all composed of α-Al₂O₃ and γ-Al₂O₃, and α-Al₂O₃ was the dominant phase. The contents of α-Al₂O₃ decreased gradually in a very small rate with increasing the frequency and γ-Al₂O₃ gradually increased. The surface of alumina ceramic coating was porous. With increasing the frequency, the coating surface gradually became less rough and more compact, resulting in low surface roughness. The bonding strength of Al₂O₃ coating was higher than 22 MPa and was not strongly affected by treating frequency. With increasing the frequency, the alumina coated steels showed better and gradually increasing corrosion resistance than the uncoated one in 3.5% NaCl solution. The coating steel with desirable corrosion resistance was obtained at 800 Hz whose corrosion current potential and corrosion density were −0.237 V and 7.367 × 10⁻⁸ A/cm², respectively.     

Corrosion and wear properties of PEO coatings formed on AM60B alloy in NaAlO2 electrolytes

Coatings with a thickness of 22-32 μm were formed on an AM60B magnesium alloy by plasma electrolytic oxidation (PEO) in electrolytes containing 12.0-24.0 g/l NaAlO₂ and other additives. SEM analyses of the coated samples showed that the coatings were compact with relatively low porosity. X-ray diffraction revealed that the coatings consisted of mainly MgAl₂O₄ and MgO phases. The relative amount of MgAl₂O₄ in the coating increased with increasing NaAlO₂ concentration. The relatively compact and thick coatings provide good corrosion protection for magnesium, as indicated by the results of potentiodynamic polarization tests. In addition, the PEO treatment also significantly improved the wear resistance of the alloy. Pin-on-disk wear tests showed that the PEO treatment reduced the wear volume loss by a factor of 10.     

Effect of α-Al2O3 on the properties of cold sprayed Al/α-Al2O3 composite coatings on AZ91D magnesium alloy

Composite coatings using pure Al powder blended with α-Al₂O₃ as feedstock were deposited on AZ91D magnesium alloy substrates by cold spray (CS). The content of α-Al₂O₃ in the feedstock was 25 wt.% and 50 wt.%, respectively. The effects of α-Al₂O₃ on the porosity, microhardness, adhesion and tensile strength of the coatings were studied. Electrochemical tests were carried out in neutral 3.5 wt.% NaCl solution to evaluate the effect of α-Al₂O₃ on the corrosion behavior of the coatings. The results showed that the composite coatings possessed lower porosity, higher adhesion strength and tensile strength than cold sprayed pure Al coating. The corrosion current densities of the composite coatings were similar to that of the pure Al coating and much higher than that of bare AZ91D magnesium alloy.     

Deposition of duplex Al2O3/aluminum coatings on steel using a combined technique of arc spraying and plasma electrolytic oxidation

Plasma electrolytic oxidation (PEO) is a cost-effective technique that can be used to prepare ceramic coatings on metals such as Ti, Al, Mg, Nb, etc., and their alloys, but this promising technique cannot be used to modify the surface properties of steels, which are the most widely used materials in engineering. In order to prepare metallurgically bonded ceramic coatings on steels, a combined technique of arc spraying and plasma electrolytic oxidation (PEO) was adopted. In this work, metallurgically bonded ceramic coatings on steels were obtained using this method. We firstly prepared aluminum coatings on steels by arc spraying, and then obtained the metallurgically bonded ceramic coatings on aluminum coatings by PEO. The characteristics of duplex coatings were analyzed by X-ray diffractometer (XRD) and scanning electron microscopy (SEM). The corrosion and wear resistance of the ceramic coatings were also studied. The results show that, duplex Al₂O₃/aluminum coatings have been deposited on steel substrate after the combined treatment. The ceramic coatings are mainly composed of α-Al₂O₃, γ-Al₂O₃, θ-Al₂O₃ and some amorphous phase. The duplex coatings show favorable corrosion and wear resistance properties. The investigations indicate that the combination of arc spraying and plasma electrolytic oxidation proves a promising technique for surface modification of steels for protective purposes.     

Ni-Co-TiO2 nanocomposite coating prepared by pulse and pulse reversal methods using acetate bath

Ni-Co/nano TiO₂ (Ni-Co-TiO₂) composite coatings were prepared under pulse current and pulse reverse current methods using acetate bath. The microstructure and corrosion resistance of the coatings were characterized by means of XRD, SEM and EIS. Both the Ni-Co alloy and composite coatings exhibited single phase of Ni matrix with face centered cubic (fcc) crystal structure. The crystal orientation of the Ni-Co-TiO₂ composite coating was transformed from crystal face (2 0 0) to (1 1 1) compared with Ni-Co alloy coatings. The results showed that the microstructure and performances of the coatings were greatly affected by TiO₂ content on the deposits prepared by PC and PRC methods. The microhardness and corrosion resistance were enhanced in the optimum percentage of TiO₂ composite coatings. The PRC composite coatings were exhibited from compact surface, higher microhardness and good corrosion resistance compared with that of the PC composite coating.     

Investigation of the characteristics and corrosion resistance of Al2O3/TiN coatings

Al₂O₃ /TiN double and Al₂O₃/Cr/TiN triple coatings were produced on stainless steel substrates using plasma-detonation techniques. Investigation of the microstructure and characteristics of the coatings after the preparation was performed by X-ray diffraction (XRD), transmission electron microscopy (TEM) and Auger electron spectroscopy (AES). The corrosion resistance of the coatings was studied in several electrolytic solutions (0.5 M H₂SO₄, 1 M HCl, 0.75 M NaCl) using electrochemical techniques (open circuit potential, cyclovoltammetry and potentiodynamic polarization). The obtained results showed, in most of the cases, an improvement of the corrosion resistance, except in NaCl solutions. The effect of the controlled thickness of TiN and Cr layers as well as the additional treatment with a high-current electron beam was also investigated. Nuclear reaction analysis (NRA), Rutherford backscattering spectroscopy (RBS) and scanning electron microscopy (SEM) were applied for the characterization of the samples before and after the corrosion experiments.     

Effects of duty ratio at low frequency on growth mechanism of micro-plasma oxidation ceramic coatings on Ti alloy

The aim of this work is to study the effects of duty ratio on the growth mechanism of the ceramic coatings on Ti-6Al-4V alloy prepared by pulsed single-polar MPO at 50 Hz in NaAlO₂ solution. The phase composition of the coatings was studied by X-ray diffraction, and the morphology and the element distribution in the coating were examined through scanning electron microscopy and energy dispersive spectroscopy. The thickness of the coatings was measured by eddy current coating thickness gauge. The corrosion resistance of the coated samples was examined by linear sweep voltammetry technique in 3.5% NaCl solution. The changes of the duty ratio (D) of the anode process led to the changes of the mode of the spark discharge during the pulsed single-polar MPO process, which further influenced the structure and the morphology of the ceramic coatings. The coatings prepared at D = 10% were composed of a large amount of Al₂TiO₅ and a little γ-Al₂O₃ while the coatings prepared at D = 45% were mainly composed of α-Al₂O₃ and γ-Al₂O₃. The coating thickness and the roughness were both increased with the increasing D due to the formation of Al₂O₃. The formation of Al₂TiO₅ resulted from the spark discharge due to the breakdown of the oxide film, while the formation of Al₂O₃ resulted from the spark discharge due to the breakdown of the vapor envelope. The ceramic coatings improved the corrosion resistance of Ti-6Al-4V alloy. And the surface morphology and the coating thickness determined the corrosion resistance of the coated samples prepared at D = 45% was better than that of the coated samples prepared at D = 10%.     

Preparation and characterization of the electrodeposited Cr-Al2O3/SiC composite coating

To increase the SiC content in Cr-based coatings, Cr-Al₂O₃/SiC composite coatings were plated in Cr(VI) baths which contained Al₂O₃-coated SiC powders. The Al₂O₃-coated SiC composite particles were synthesized by calcining the precursor prepared by heterogeneous deposition method. The transmission electron microscopy analysis of the particles showed that the nano-SiC particle was packaged by alumina. The zeta potential of the particles collected from the bath was up to +23 mV, a favorable condition for the co-deposition of the particles and chromium. Pulse current was used during the electrodeposition. Scanning Electron Microscopy (SEM) indicated that the coating was compact and combined well with the substrate. Energy dispersive X-ray analysis of Cr-Al₂O₃/SiC coatings demonstrated that the concentration of SiC in the coating reached about 2.5 wt.%. The corrosion behavior of the composite coating was studied by potentiodynamic polarization and electrochemical impedance spectroscopy techniques. The data obtained suggested that the Al₂O₃/SiC particles significantly enhanced the corrosion resistance of the composite coating in 0.05 M HCl solution.     

Preparation and characterization of nickel nano-Al2O3 composite coatings by sediment co-deposition

Ni-Al₂O₃ composite coatings were prepared by using sediment co-deposition (SCD) technique and conventional electroplating (CEP) technique from Watt's type electrolyte without any additives. The microstructure, hardness, and wear resistance of resulting composites were investigated. The results show that the incorporation of nano-Al₂O₃ particles changes the surface morphology of nickel matrix. The preferential orientation is modified from (2 0 0) plane to (1 1 1) plane. The microhardness of Ni-Al₂O₃ composite coatings in the SCD technique are higher than that of the CEP technique and pure Ni coating and increase with the increasing of the nano-Al₂O₃ particles concentration in plating solution. The wear rate of the Ni-Al₂O₃ composite coating fabricated via SCD technique with 10 g/l nano-Al₂O₃ particles in plating bath is approximately one order of magnitude lower than that of pure Ni coating. Wear resistance for SCD obtained composite coatings is superior to that obtained by the CEP technique. The wear mechanism of pure Ni and nickel nano-Al₂O₃ composite coatings are adhesive wear and abrasive wear, respectively.     

Ultra-hard ceramic coatings fabricated through microarc oxidation on aluminium alloy

Ultra-hard ceramic coatings with microhardness of 2535 Hv have been synthesized on the Al alloy substrate by microarc oxidation (MAO) technique. The effects of anodic current density (j_a) and the ratio of cathodic to anodic current density (j_c/j_a) on the mechanical and corrosion resistance properties of MAO coatings have been studied by microhardness and pitting corrosion tests, respectively. In addition, the phase composition and microstructure of the coatings were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The results show that the coatings prepared at high anodic current density consist mainly of α-Al₂O₃, while those fabricated at low anodic current density are almost composed of γ-Al₂O₃. Microhardness test shows that the coatings have high microhardness, and the highest one is found in the coating formed at j_a = 15 A/dm² and j_c/j_a = 0.7. Pitting corrosion test shows that the structure of coatings is strongly influenced by the varying j_c/j_a.     

Electrodeposition and characterization of Ni-Y2O3 composite

Nano-sized Y₂O₃ particles were codeposited with nickel by electrolytic plating from a nickel sulfate bath. The effects of the incorporated Y₂O₃ on the structure, morphology and mechanical properties (including microhardness, friction coefficient and wear resistant) of Ni-Y₂O₃ composite coatings were studied. It is observed that the addition of nano-sized Y₂O₃ particles shows apparent influence on the reduction potential and pH of the electrolyte. The incorporated Y₂O₃ increases from 1.56 wt.% to 4.4 wt.% by increasing the Y₂O₃ concentration in the plating bath from 20 to 80 g/l. XRD results reveal that the incorporated Y₂O₃ particles favour the crystal faces (2 0 0) and (2 2 0). SEM and AFM images demonstrate that the addition of Y₂O₃ particles causes a smooth and compact surface. The present study also shows that the codeposited Y₂O₃ particles in deposits decrease the friction coefficient and simultaneously reduce the wear weight loss. Ni-Y₂O₃ composite coatings reach their best microhardness and tribological properties at Y₂O₃ content 4.4 wt.% under the experiment conditions.     

The role of As2O3 on the stability and some physical properties of PbO-Sb2O3 glasses

PbO-Sb₂O₃ glasses added with different concentrations of As₂O₃ (10-55 mol%) were prepared to understand their IR spectra, elastic properties (Young's modulus E, Shear modulus G, microhardness H), optical absorption and dielectric properties (constant ε, loss tan δ, ac conductivity σ_ac over a moderately wide range of frequency and temperature and breakdown strength in air medium at room temperature). Results have indicated that the structure of the PbO-Sb₂O₃-As₂O₃ glass is more rigid when the concentration of As₂O₃ is around 40 mol%.     

Microstructure and interfacial properties of HfO2-Al2O3 nanolaminate films

High-k HfO₂-Al₂O₃ composite gate dielectric thin films on Si(1 0 0) have been deposited by means of magnetron sputtering. The microstructure and interfacial characteristics of the HfO₂-Al₂O₃ films have been investigated by using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and spectroscopic ellipsometry (SE). Analysis by XRD has confirmed that an amorphous structure of the HfO₂-Al₂O₃ composite films is maintained up to an annealing temperature of 800 °C, which is much higher than that of pure HfO₂ thin films. FTIR characterization indicates that the growth of the interfacial SiO₂ layer is effectively suppressed when the annealing temperature is as low as 800 °C, which is also confirmed by spectroscopy ellipsometry measurement. These results clearly show that the crystallization temperature of the nanolaminate HfO₂-Al₂O₃ composite films has been increased compared to pure HfO₂ films. Al₂O₃ as a passivation barrier for HfO₂ high-k dielectrics prevents oxygen diffusion and the interfacial layer growth effectively.     

Synthesis and fine patterning of organic-inorganic composite SiO2-Al2O3 thick films

Organic-inorganic composite SiO₂-Al₂O₃ films have been prepared by sol-gel using methacryloxypropyl trimethoxysilane and aluminum sec-butoxide as the precursors. By introduction of organic groups into the inorganic backbone, the smooth and crack-free films could be readily achieved by a one-step dip-coating process, with the thickness up to 4.6 μm after being post-baked at 200 °C for 2 h. The films presented in an amorphous phase with an acceptable chemical homogeneity. Owing to the formation of chelate rings, the gel films showed a strong photosensitivity to ultraviolet light at 325 nm. The uniform fine patterns of SiO₂-Al₂O₃ thick films could be well defined by ultraviolet light imprinting simply using a mask. These performances of SiO₂-Al₂O₃ films indicate the potential for integrated optical systems.     

Formation of aligned silicon-nanowire on silicon in aqueous HF/(AgNO3 + Na2S2O8) solution

Highly oriented silicon nanowire (SiNW) layer was fabricated by etching Si substrate in HF/(AgNO₃ + Na₂S₂O₈) solution at 50 °C. The morphology and the photoluminescence (PL) of the etched layer as a function of Na₂S₂O₈ concentration were studied. The SiNW layers formed on silicon were investigated by scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX). It was demonstrated that the morphology of the etched layers depends on the Na₂S₂O₈ concentration. Room-temperature photoluminescence (PL) from etched layer was observed. It was found that the utilisation of Na₂S₂O₈ decreases PL peak intensity. Finally, a discussion on the formation process of the silicon nanowires is presented.     

Physical studies on composites Ag7I4VO4-Al2O3

The electrical properties of the solid electrolytes Ag₇I₄VO₄-Al₂O₃ (0-40 mol% Al₂O₃) are investigated. The electrical conductivity, dielectric constant and dielectric loss are increased by increasing the concentration of Al₂O₃; showing a maximum at 30 mol% Al₂O₃. The conductivity is found to be increased by decreasing the particle size of Al₂O₃. The results are explained using the random resistor network model (RRN). This is due to the formation of a highly conducting interface layer along the matrix-particle interface. This layer is destroyed at concentrations higher than 30 mol% Al₂O₃.     

Electrodeposition of nanostructured Pt films from lyotropic liquid crystalline phases on α-Al2O3 supported dense Pd membranes

Using the lyotropic liquid crystalline templating strategy, the nanostructured platinum film was electrochemically deposited on the α-Al₂O₃ supported dense palladium membrane. The XRD and TEM results of the Pt film revealed a hexagonal array of cylindrical pores with a uniform pore diameter of ca. 3.8 nm and a pore-to-pore separation of ca. 7.6 nm. The structure parameters of the Pt film were almost the same as those of the hexagonal liquid crystalline template. Based on SEM observations, the Pt film was featureless, smooth, and tightly adherent to the dense Pd membrane. The specific surface area of the Pt film, measured by using cyclic voltammetry, was ca. 13.8 m² g⁻¹, which was in accord with the theoretical value of 14.5 m² g⁻¹ for a perfect hexagonal nanostructure with the same structure parameters. By combining the dense Pd membrane for selective permeation to hydrogen with the Pt film of high specific surface area for catalysis, the as-synthesized two-layer film will be a promising catalytic membrane to intensify hydrogen-related reaction processes.     

Nickel ion—A structural probe in BaO-Al2O3-P2O5 glass system by means of dielectric, spectroscopic and magnetic studies

BaO-Al₂O₃-P₂O₅ glasses containing different concentrations of NiO (ranging from 0 to 1.0 mol%) were prepared. A number of studies viz., chemical durability, differential thermal analysis, spectroscopic (infrared, optical absorption spectra), magnetic susceptibility and dielectric properties (constant ε′, loss tan δ, AC conductivity σ_AC over a range of frequency and temperature) of these glasses have been carried out. The studies on chemical durability indicate that there is a significant increase in the corrosion resistance of the glasses; where as the results of differential thermal analysis suggests that there is a substantial improvement in the glass forming ability, with increase in the concentration of NiO up to 0.6 mol% in the glass matrix. The optical absorption, magnetic susceptibility and IR spectral studies point out nickel ions occupy both tetrahedral and octahedral positions in the glass network; the later positions seems to be dominant when the concentration of NiO is beyond 0.6 mol% in the glass matrix. The studies of dielectric properties reveal that the presence of nickel oxide in the glass network causes a considerable improvement in the insulating strength of the se glasses when the concentration of NiO?0.6 mol%.     

A comparative study on Zn0.8Cd0.2O films deposited on different substrates

Highly (0 0 2)-oriented Zn_0.8Cd_0.2O crystal films were prepared on different substrates, namely, glass, Si(1 1 1) and α-Al₂O₃(0 0 1) wafers by the dc reactive magnetron sputtering technique. The Zn_0.8Cd_0.2O/α-Al₂O₃ film has the best crystal quality with a FWHM of (0 0 2) peak of 0.3700°, an average grain size of about 200 nm and a root-mean-square surface roughness of about 70 nm; yet the Zn_0.8Cd_0.2O/glass holds the worst crystal quality with a much larger FWHM of 0.6281°. SIMS depth profile shows that the Zn and O compositions change little along the film depth direction; the Cd incorporation also almost holds the line towards the top surface other than an accumulation at the interface between the film and the substrate. The Cd content in the film is nearly consistent with that in target.     

Zn-ZrO2 nanocomposite coatings: Elecrodeposition and evaluation of corrosion resistance

The Zn and Zn-ZrO₂ composite coatings were produced by electrodeposition technique using sulphate bath. ZrO₂ particles were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The ZrO₂ particle size distribution in the plating bath and Zeta potential and the ZrO₂ were measured using dynamic light scattering technique (DLS). The corrosion resistance properties of Zn and Zn-ZrO₂ composite coatings were compared by examining the experimental data acquired through polarization, open circuit potential (OCP) and Tafel measurements. The corrosion environment was 3.5 wt% NaCl solution. The variation of amount of ZrO₂ in the solution on their % wt inclusion in the composite and on composite microhardness was investigated. XRD patterns were recorded for Zn and Zn-ZrO₂ coatings to compare their grain size. The SEM images of coatings before and after corrosion under chemical and electrochemical conditions were presented. The results were analyzed to establish the superiority of Zn-ZrO₂ composite over Zn coating.