Surface‐Confined Electropolymerization of Methylene Blue on Gold Electrodes

We report on the electrochemical behaviour and electropolymerization of self‐assembled monolayers (SAMs) of methylene blue (MB) on gold electrodes. The SAMs of MB on gold electrodes were prepared by immersing the substrates into a solution of 1.0 mM MB in absolute ethanol for different times at room temperature. Cyclic voltammetry experiments exhibited that reductive desorption of MB monolayer takes place at three different potentials on polycrystalline gold electrodes, while reductive desorption of MB monolayer consists of only one peak on single crystal Au(111) substrates. Calculated charge densities for different immersion times indicated that optimal immersion time for self‐assembly of MB is 96 h. Electropolymerization of SAMs of MB on gold electrode was achieved by applying 0.95 V for 1 s in 0.1 M borate buffer solution (pH: 9.0). It was observed that poly(MB) monolayers are highly stable in acidic media. ATR‐FTIR and UV‐vis spectra exhibited differences between monomer and polymer monolayers, which are attributed to surface‐confined electropolymerization. STM image of poly(MB) monolayer on Au(111) substrate revealed a surface that is covered by well‐ordered, collateral nanowires with an average size of 3 nm.     

Electroanalysis of Norepinephrine at Bare Gold Electrode Pure and Modified with Gold Nanoparticles and S‐Functionalized Self‐Assembled Layers in Aqueous Solution

Gold nanoparticles (Au‐NPs), cystamine (CA) and 3,3′‐dithiodipropionic acid (DTDPA) modified gold bare electrodes were applied in voltammetric sensors for simultaneous detection of norepinephrine (NEP), ascorbic (AA) and uric (UA) acids. A linear relationship between norepinephrine concentration and current response was obtained in the range of 0.1 μM to 600 μM M with the detection limit ≤0.091 μM for the electrodes modified at 2D template and in the range of 0.1 μM to 700 μM M with the detection limit ≤0.087 μM for the electrodes modified at 3D template The results have shown that using modified electrodes it is possible to perform electrochemical analysis of norepinephrine without interference of ascorbic and uric acids, whose presence is the major limitation in norepinephrine determination at a bare gold electrode. The modified SAMs electrodes show good selectivity, sensitivity, reproducibility and high stability.     

Enhanced Electrocatalytic Oxidation of Paracetamol at DNA Modified Gold Electrode

Cysteine monolayer has been assembled onto bare gold electrode (SAM/Au), and subsequently deoxyribonucleic acid (DNA) has been successfully immobilized at the SAM/Au electrode. The thus modified electrode is assigned DNA/SAM/Au. Modification steps of the electrode were followed electrochemically using K₄[Fe(CN₆)] electrochemical marker. Also, the build‐up of the modified electrode composition is followed using EDX and the crystallographic orientation is inspected using XRD. The electrochemical behavior of paracetamol (PC) at DNA/SAM/Au electrode is investigated. Interestingly, the sluggish irreversible behavior of PC at the bare gold electrode is converted to a quasi‐reversible one at DNA/SAM/Au electrode pointing to some interaction between the immobilized DNA and PC. The enhanced electrochemical behavior of PC at modified DNA/SAM/Au electrode is successfully used for a sensitive electrochemical determination of PC. Square wave voltammetry (SWV) was used for this purpose. The concentration of PC was in linear relation with the peak current at the optimum conditions within the range 10.0–110.0 μg mL^?1 with correlation coefficient (R²) of 0.998. Also, the standard deviation (SD) and relative standard deviation (RSD) were calculated and found to be 0.817 and 1.52, respectively, indicating the significance of the present method.     

Voltammetric Determination of Epinephrine with a 3‐Mercaptopropionic Acid Self‐Assembled Monolayer Modified Gold Electrode

Epinephrine (EP) could exhibit an anodic peak at a bare gold electrode, but it was very insensitive. However, when the bare gold electrode was modified with 3‐mercaptopropionic acid (3MPA) self‐assembled monolayer (3MPA SAM), the peaks of EP became more reversible and sensitive due to the accumulation and mediate efficiency of 3MPA SAM. Conditions such as solution pH, concentration of supporting electrolyte and accumulation time were optimized. Under the selected conditions (i.e., 0.02 M pH 6.8 sodium phosphate buffer, accumulation time: 2 min under open‐ circuit.), the height of the anodic peak at about 0.18 V (vs. SCE) was linear to EP concentration in the range of 2×10^?7 ?1×10^?6 M and 1×10^?6?5×10^?4 M with correlation coefficient of 0.995 and 0.999, respectively. When the 3MPA/Au was further modified with cysteamine, the interference of H₂O₂ and BrO₃^? was eliminated. But the resulting electrode still suffered from the interference of ascorbic acid. This method was used to determine the content of EP in adrenaline hydrochloride injections, and the recovery was in the range of 97.0% to 105.1%.     

Electrochemical Studies of Chemically Modified Nanometer‐Sized Electrodes

Self‐assembled monolayers (SAMs) of 4‐aminothiophenol (4‐ATP) has been successfully deposited onto nanometer‐sized gold (Au) electrodes. The cyclic voltammograms obtained on a 4‐ATP SAMs modified electrode show peaks and the peak height is proportional to the scan rate, which is similar to that on an electroactive SAMs modified macro electrode. The electrochemical behavior and mechanism of outer‐sphere electron transfer reaction on the 4‐ATP SAMs modified nanometer‐sized electrode has also been studied. The 4‐ATP SAMs modified electrode is further modified with platinum (Pt) nanoparticles. Electrochemical behaviors show that there is electrical communication between Pt nanoparticles and Au metal on the Pt nanoparticles/4‐ATP SAMs/Au electrode. However, scanning electron microscopic image shows that the Pt nanoparticles are not evenly covered the electrode.     

DNA-modified electrodes; part 4: optimization of covalent immobilization of DNA on self-assembled monolayers

The covalent immobilization of DNA onto self-assembled monolayer (SAM) modified gold electrodes (SAM/Au) was studied by X-ray photoelectron spectrometry and electrochemical method so as to optimize its covalent immobilization on SAMs. Three types of SAMs with hydroxyl, amino, and carboxyl terminal groups, respectively, were examined. Results obtained by both X-ray photoelectron spectrometry and cyclic voltammetry show that the largest covalent immobilization amount of dsDNA could be gained on hydroxyl-terminated SAM/Au. The ratio of amount of dsDNA immobilized on hydroxyl-terminated SAMs to that on carboxyl-terminated SAMs and to that on amino-terminated SAMs is (3-3.5): (1-1.5): 1. The dsDNA immobilized covalently on hydroxyl-terminated SAMs accounts for 82.8-87.6% of its total surface amount (including small amount of dsDNA adsorbed). So the hydroxyl-terminated SAM is a good substrate for the covalent immobilization of dsDNA on gold surfaces.     

Electroanalytical applications of cationic self-assembled monolayers: square-wave voltammetric determination of dopamine and ascorbate

Gold electrodes modified with cationic self-assembled monolayers (SAMs) of 2,2'-dithiobisethaneamine (CYST) and 6,6'-dithiobishexaneamine (DTH) were used for the simultaneous determination of dopamine (DA) and ascorbate (AA). The cationic SAM modified electrodes have several advantages over the bare electrode for the oxidation of AA. A very large (approximately 450 mV) decrease in the overpotential for the oxidation of AA when compared with the bare electrode has been observed at the cationic monolayer-modified electrode. The electrostatic interaction of negatively charged AA with the monolayer shift the oxidation peak potential of AA to less positive potential and enhances the peak current. On the other hand, the positively charged DA is repelled from the monolayer and the oxidation potential shifts to more positive potential when compared to the bare electrode. The electrochemical oxidation of AA at the mixed monolayer of CYST and diethyl disulfide (DEDS) supports the influence of cationic terminal group of the monolayer on the oxidation of AA. Since the oxidation of AA occurs well before the oxidation potential of DA is reached, the homogeneous catalytic oxidation of AA by the oxidized DA has been advantageously eliminated at the monolayer-modified electrode. The cationic self-assembled monolayers successfully detect DA in the presence of high concentration of AA. The sensitivity of the electrode modified with CYST monolayer was found to be 0.036 and 0.021 microA/microM towards AA and DA, respectively.     

Study of the immobilization of alcohol dehydrogenase on Au-colloid modified gold electrode by piezoelectric quartz crystal sensor,cyclic voltammetry,and electrochemical impedance techniques

The immobilization of alcohol dehydrogenase (ADH) on Au-colloid modified gold electrodes has been investigated. Colloidal Au was first self-assembled onto gold electrodes through the thiol groups of an 1,6-hexanedithiol monolayer. Piezoelectric quartz crystal sensor, cyclic voltammetry, and electrochemical impedance techniques were used to investigate the immobilization of ADH on Au colloids. The cyclic voltammogram tends to be more irreversible with increased ADH concentration. In the impedance spectroscopic study, an obvious difference of the electron transfer resistance between the Au-colloid modified electrode and the bare gold electrode was observed. Using the piezoelectric quartz crystal sensor, the Michaelis constant, K(m), and the maximum initial rate, V(max), of the immobilized ADH were estimated as 6.03 x 10(-4) M and 0.63 Hzs (-1), respectively. The binding constant of ADH with nicotinamide adenine dinucleotide (NAD) was also determined as 1.87 x 10(4) M(-1). Experimental results showed that colloidal Au can be used as a biocompatible matrix for enzyme immobilization.     

Determination of acetaminophen by square wave voltammetry at a gold electrode modified by 4-amino-2-mercaptopyrimidine self-assembled monolayers

A 4-Amino-2-mercaptopyrimidine self-assembled monolayer (AMP SAMs/Au) modified gold electrode was prepared. The electrochemical behavior of acetaminophen on the AMP SAMs/Au was studied in Britton-Robinson (BR) buffer solution. Compared to a bare gold electrode, the modified electrode exhibits a significant enhancement in the oxidation current response for acetaminophen. The modified electrode was used for the determination of acetaminophen by square wave voltammetry. The oxidation current increased linearly with the concentration of acetaminophen in the range of 2.0 × 10⁻⁶−4.0 × 10⁻³ M. The modified electrode made it possible to eliminate the interference of dopamine (DA), brucine, epinephrine (EP), and norepinephrine (NE). The practical analytical utility was illustrated by the determination of acetaminophen in a commercially available drug. The text was submitted by the authors in English.     

Quasi-reversible two-electron reduction of oxygen at gold electrodes modified with a self-assembled submonolayer of cysteine

The electrochemical reduction of molecular oxygen (O₂) has been performed at gold electrodes modified with a submonolayer of a self-assembly (sub-SAM/Au) of a thiol compound (typically cysteine (CYST)) in O₂-saturated 0.5 M KOH. At bare gold electrode O₂ reduction reaction proceeds irreversibly, while this reaction is totally hindered at gold electrodes with a compact structure of CYST over its surface. The partial reductive desorption of the compact CYST monolayer was achieved by controlling the potential of the CYST/Au electrode, leading to the formation of a submonolayer coverage of the thiol compound over the Au electrode surface (sub-SAM/Au), at which the CYST molecules selectively block the Au(1 0 0) and Au(1 1 0) fractions (the so-called rough domains) of the polycrystalline Au while the Au(1 1 1) component (the so-called smooth domains) remains bare (i.e., uncovered with CYST). This sub-SAM/Au electrode extraordinarily exhibits a quasi-reversible two-electron reduction of molecular oxygen (O₂) in alkaline medium with a peak separation (ΔE_p) between the cathodic and anodic peak potentials (E_p^c,E_p^a) of about 60 mV. The ratio of the anodic current to the cathodic one is close to unity. The formal potential (E^o′) of this reaction is found to equal −150 mV vs. Ag/AgCl/KCl(sat.).     

Stripping voltammetry of copper and lead using gold electrodes modified with self-assembled monolayers

One problem associated with using bare solid metal electrodes, such as gold and platinum, in stripping analysis to determine heavy metal ions such as lead and copper ions in dilute solutions is that underpotential deposition (UPD) gives multiple stripping peaks in the analysis of mixtures. These peaks are often overlapped and cannot be conveniently used for analytical purposes. Bifunctional alkylthiols, such as 3-mercaptopropionic acid, with an ionizable group on the other terminal end of the thiol can form self-assembled monolayers (SAMs) on the surface of the gold electrode. It is shown that such an SAM-modified gold electrode minimizes the UPD effects for the stripping analysis of lead and copper. The anodic peak potential shifts and the peak shape changes, indicating that the SAM changes the deposition and stripping steps of these heavy metal ions. Thus, the sensitivity levels for both single species and mixtures can be significantly improved for the conventional solid electrodes. The mechanism of the deposition reaction at the SAM-modified gold electrodes is discussed. Received: 29 May 1997 / Accepted: 24 June 1997     

维生素B_1自组装膜修饰金电极对多巴胺、尿酸的电催化作用

用维生素B1(VB1)在金电极上进行自组装,制备了VB1自组装膜修饰金电极(VB1-Au/SAMs/CME).利用循环伏安法初步研究了此自组装单分子膜修饰电极的电化学行为.结果表明: VB1在金电极表面具有特性吸附.以\3-/ 4-氧化还原电对为探针,考察了VB1自组装膜修饰金电极的电化学性质, VB1自组装膜的存在对\3-/4-的电子转移具有明显的阻碍作用.研究了多巴胺(DA)和尿酸(UA)在此电极上的电化学行为.实验结果表明, DA和UA在此电极上均可被电催化氧化.差分脉冲伏安(DPV)氧化峰电流与DA浓度在2.0×10-5～4.0×10-4 mol/L范围内呈线性关系;测定UA的线性范围为6.0×10-5～2.2×10-4 mol/L,而且可实现这两种物质的同时测定.     

Electorchemical Studies of Cytochrome c on Electodes Modified by Single—Wall Carbon Naotubes

Single-wall carbon nanotubes(SWNTs) modified gold electrodes were prepared by using two different methods.The electrochemical behavior of cytochrome c on the modified gold electrodes was investigated.The first kind of SWNT-modified electrode (noted as SWNT/Au electrode)was prepared by the adsorption of carboxylterminated SWNTs from DMF dispersion on the gold electrode.The oxidatively processed SWNT tips were covalently modified by coupling with amines (AET) to form amide linkage.Via Au-S chemical bonding,the self-assembled monolayer of thiol-unctionalized nanotubes on gold surface was fabricated so as to prepare the others SWNT-modified electrode (noted as SWNT/AET/Au electrode).It was shown from cyclic voltammetry cxperiments that cytochrome c exhibited direct electrochemical responses on the both electrodes, but only the current of controlled diffusion existed on the SWNT/Au electrode while both the currents of controlled diffusion and adsorption of cytochrome c occurred on the SWNT/AET/Au electrode.Photoelastic Modulation Infared Reflection Absorpthion Spectroscopy (PEM-IRRAS) and Quartz Crystal Microbalance (QCM) were employed to verify the adsorption of SWNTs on the gold electrodes.The results proved that SWNTs could enhance the direct electron transfer proecss between the electrodes and redox proteins.     

亚硒酸钠在L-半胱氨酸自组装类生物膜修饰电极上的电化学行为

利用L-半胱氨酸自组装膜修饰金电极(L-Cys,Au/SAMs), 在0.05mol/L H_2SO_4 底液中研究了 Na_2SeO_3 的电化学特性.在0.00～1.30 V (vs. SCE) 电位范围内对微量Na_2SeO_3进行循环伏安扫描,发现L-Cys, Au/SAMs修饰电极在峰电位0.89 V处有灵敏的Se的氧化溶出峰.通过比较裸金电极和修饰电极在Na_2SeO_3 溶液中的电化学特性发现,修饰电极通过巯基中的S与Na_2SeO_3发生氧化还原作用生成Se,且修饰电极对沉积在电极表面的Se的氧化过程具有催化作用.根据Na_2SeO_3在单分子膜上的电化学行为,提出了单分子膜中硫(Au-S)与Se(Ⅳ)作用生成Se的反应机理、Se电化学催化氧化机理及巯基化合物通过生成纳米硒生物吸收Se的类生物膜模型.     

Electrochemical study and detection of perphenazine using a gold electrode modified with decanethiol SAM

A novel method for the determination of perphenazine has been developed. The method is based on the accumulation of perphenazine at a gold electrode modified with decanethiol (DEC) self-assembled monolayer (SAM) and its oxidation at about 0.6 V (vs. saturated calomel electrode (SCE)). Because some coexistent electroactives were blocked and perphenazine was selectively accumulated by the SAM, the electrode exhibited good selectivity and sensitivity. Various conditions were optimized for practical application. Under the selected conditions (i.e. 0.05 M pH 10 sodium borate buffer, accumulation time: 120 s, accumulation potential: −0.4 V, scan rate: 100 mV s⁻¹), the anodic stripping peak current was linear to perphenazine concentration in the ranges of 6×10⁻⁹–5×l0⁻⁷ and 5×10⁻⁷–5×10⁻⁶ M with correlation coefficients of 0.998 and 0.995, respectively. For a 1.0×10⁻⁶ M perphenazine solution, the relative standard deviation of peak height was 2.3% (n=8). This method was applied to the determination of perphenazine in some drugs and the recovery was 92–101%. In addition, it was found that in the presence of perphenazine, the SAM structure changed a little and more needle holes appeared. However, the SAM could recover the original form when perphenazine and its redox product were removed from the monolayer by repeatedly cycling the electrode in a blank solution for a minute. The modified electrode was characterized by alternating current impedance and electrochemical probe.     

Epinephrine Oxidation in the Presence of Interfering Molecules on Gold and Gold Electrodes modified with Gold Nanoparticles and Thiodipropionic Acid in Aqueous Solution. A Comparative Study

Thiodipropionoc acid (TDPA), cysteamine (CA) and gold nanoparticles (Au‐NPs) modified gold pure electrodes have been applied in voltammetric sensors for simultaneous detection of epinephrine (EP), ascorbic (AA) and uric (UA) acids. Modified electrodes with self assembled layers (SAMs) show high selectivity, sensitivity, reproducibility and stability. A linear relationship between the epinephrine concentration and the current response is obtained in the range of 0.1 μM to 0.65 μM with the detection limit ≤0.065 μM for the electrodes modified at 2D surface and in the range of 0.1 μM to 0.75 μM with the detection limit ≤0.082 μM for the electrodes modified at the 3D surface.     

Exploring three-dimensional nanosystems with Raman spectroscopy: methylene blue adsorbed on thiol and sulfur monolayers on gold

Resonant Raman and surface-enhanced Raman scattering (SERS) spectroscopies, complemented with scanning tunnel microscopy and electrochemical techniques, have been used to obtain information about the amount and spatial distribution of methylene blue (MB) molecules immobilized on sulfur and four ultrathin molecular alkanethiolate films self-assembled on Au(111) and rough Au electrodes. The intensity of the Raman signals allow one to estimate the amount of immobilized MB at different organic films, whereas the decrease in the SERS intensity as a function of distance for the rough Au electrodes is used to locate the average position of the MB species with respect to the Au substrate. We found that significant amounts of cationic MB species are able to diffuse into methyl-terminated thiols, but they are stopped at the outer plane of the self-assembled monolayer (SAM) by negatively charged carboxylate groups. The relative shift of C-N stretching Raman modes indicates that the binding of MB to S is different from that found for MB on thiols. Most of the molecules immobilized on methyl- and carboxylate-terminated thiols are electrochemically inactive, suggesting that strong coupling between the Au electrode and the MB molecules is needed for charge transfer. Our results are consistent with a small population of electrochemically active MB species very close to the Au surface that reach this position driven by their lipophilic (hydrophobic) character through defects at SAMs.     

Electrochemical response of dopamine at a penicillamine self-assembled gold electrode.

The penicillamine (Pen) self-assembled monolayer (SAM) modified gold electrode (Pen/Au) is demonstrated to catalyze the electrochemical response of dopamine (DA) by cyclic voltammetry. A pair of well-defined redox waves was obtained and the calculated standard rate constant (k(s)) is 3.88 x 10(-3) cm/s at the self-assembled electrode. The electrode reaction is a quasi-reversible process. The oxidation peak of DA can be used to determine the concentration of DA. The peak current and the concentration of DA are a linear relationship in the range of 2.0 x 10(-5) M to 8.0 x 10(-4) M. The detection limit is 4.0 x 10(-6) M. By ac impedance spectroscopy the apparent electron transfer rate constant (k(app)) of Fe(CN)(3-)/Fe(CN)(4-) at the Pen/Au electrode was obtained as 2.08 x 10(-5) cm/s. The Pen SAM was characterized with X-ray photoelectron spectroscopy (XPS), grazing angle FT-IR spectroscopy and contact angle goniometer.     

EQCM and Fluoroelectrochemical Studies on the Catalytic Oxidation of NADH at a Pencil 8B‐Scrawled Gold Electrode with High Detection Sensitivity

We report for the first time the effective catalytic electrooxidation of nicotinamide adenine dinucleotide (NADH) on the pencil 8B‐scrawled gold electrode of an electrochemical quartz crystal microbalance (EQCM). The EQCM allowed us to quantitatively evaluate the catalytic activity of the pencil‐scrawled Au electrode. With increasing the mass of modified pencil powders, the peak potential for NADH oxidation shifted negatively, with maximum shift of ?0.35 V at saturated pencil modification; the NADH‐oxidation peak current density (j_p) was also notably increased, and the j_p at saturated pencil modification was found to be larger than those at conventional pencil 8B and bare Au electrodes. Sensitive amperometric detection of NADH was achieved at the gold electrode with saturated pencil modification, with low detection potential (0.4 V versus SCE), low detection limit (0.08 μmol L^?1) and wide linear range (0.2–710 μmol L^?1). The fluoroelectrochemical measurements of NADH at bare and pencil‐modified gold electrodes were also conducted with satisfactory results. The convenient and low‐cost modification of pencil powders on the Au electrode may have presented a new functional surface of the EQCM, which is recommended for wider applications to bioelectrochemical studies, especially in view of the EQCM's capability of providing abundant in situ information in relevant processes.