(La0.75Sm0.25)2Zr2O7陶瓷的热导率

以Sm2O3、La2O3和ZrO2为原料,用固相反应法制备了(La0.75Sm0.25)2Zr2O7陶瓷材料.采用XRD和FT-IR技术研究了试样的相结构,用SEM分析了试样的微观组织结构,采用激光脉冲法测量试样的热导率.结果表明,所制备的陶瓷材料具有焦绿石晶体结构,其组织结构致密,晶粒大小均匀,晶界清晰.由于La3+和Sm3+质量和离子半径的差别, (La0.75Sm0.25)2Zr2O7具有比La2Zr2O7更低的热导率.其热导率明显低于现役的YSZ陶瓷,可用作新型热障涂层表面陶瓷层候选材料.     

热障涂层用稀土锆酸盐陶瓷材料研究进展

稀土锆酸盐热障涂层材料因具有低热导率,良好的高温相稳定性和隔氧性能等优点而被认为是最具有潜力的新型高温热障涂层材料体系之一.本文主要针对其作为新一代热障涂层在隔热与承载方面的性能需求,分析了热物理性能与力学性能的研究进展,并展望今后稀土锆酸盐的研制方向.     

(Sm1-xAlx)2Ce2O7化合物的热物理性能

以Al2O3、Sm2O3和CeO2为原材料,采用固相反应法制备了(Sm1-xAlx)2Ce2O7化合物.对其相结构,显微组织和热物理性能进行了研究.结果表明,合成的(Sm1-xAlx)2Ce2O7化合物具有单一的萤石型晶格,该化合物致密度均在90;以上,晶粒界面明显.三价铝离子的引入能明显降低其导热性能,热膨胀性能虽虽然有所降低,但高温热膨胀系数大于YSZ,满足热障涂层的要求.     

(Sm0.5Gd0.2Nd0.3)2(Hf0.3Ce0.7)2O7复合氧化物的热物理性能

为寻求新型热障涂层用陶瓷材料,本文采用高温固相烧结法制备了(Sm_0.5Gd_0.2Nd_0.3)₂(Hf_0.3Ce_0.7)₂O₇复合氧化物。利用XRD分析了其晶体结构,SEM分析其显微组织,膨胀仪测试其热膨胀性能,激光热导仪测试其热扩散系数。结果表明,成功制备了具有单一萤石晶体结构的(Sm_0.5Gd_0.2Nd_0.3)₂(Hf_0.3Ce_0.7)₂O₇复合氧化物。其显微组织结构致密,晶界清晰无其他相存在。由于复杂的元素组成和较大的原子量,其热导率明显低于7YSZ和Sm₂Ce₂O₇。其较低的热膨胀系数则归因于B位离子较小的离子半径,但其热膨胀系数依然满足热障涂层的要求。     

添加纳米Ti(C7N3)的ZrO2基纳米陶瓷模具材料

本文针对模具对陶瓷材料的要求,从提高陶瓷模具材料的综合力学性能出发,采用纳米复合方法制备出具有较高综合力学性能的纳米陶瓷模具材料.研究了纳米Ti(C7N3)和Y2O3的组分含量对纳米陶瓷模具材料微观结构和力学性能的影响,结果表明添加纳米Ti(C7N3)和Y2O3的氧化锆纳米陶瓷模具材料的力学性能优于纯氧化锆陶瓷材料,纳米颗粒的添加改善了材料的微观结构和力学性能.当纳米Ti(C7N3)和Y2O3的添加量分别为17.15vol;和5 mol;时,材料的综合性能最好,其抗弯强度为814MPa、断裂韧性6.35 MPa· m1/2、维氏硬度11.87 GPa.     

Hf微量掺杂Sm2Ce2O7固溶体制备及热物理性能

采用高温固相烧结法制备了Sm2(Ge1-xHfx)2O7(x=0,0.025,0.05,0.075,0.1)固溶体,并对其相组成、显微组织及热物理性能进行了分析.结果表明,所合成的固溶体具有单一的萤石结构,其相对致密度均在90;以上.Hf掺杂增强了声子的散射程度,从而使其热导率与Sm2Ce2O7相比明显降低.Hf较小的离子半径使得其热膨胀系数随HfO2掺杂量增加而降低,但仍然满足热障涂层的要求.     

Yb2O3-Y2O3-Gd2O3-ZrO2热障涂层制备及性能研究

以Yb2O3、Y2O3 、Gd2O3稀土氧化物粉末和ZrOCl2·8H2O粉末为原料,采用化学共沉淀法制备了Yb2O3-Y2O3-Gd2O3-ZrO2 (YYGZO)热喷涂用粉末,采用大气等离子喷涂技术制备了YYGZO涂层,利用场发射扫描电镜(FESEM)、X射线衍射(XRD)研究了YYGZO粉末及涂层的微观组织形貌、相结构.结果表明,制备的热喷涂YYGZO粉末大部分呈规则实心球体状,且球形度良好,颗粒粒径均匀,大部分颗粒粒径分布为30～60μm,流动性能较好,满足大气等离子喷涂的要求.YYGZO涂层具有较好的高温相结构稳定性.所制备YYGZO热障涂层组织结构比较致密,涂层各个界面结合紧密,孔隙率约为9.23;,结合强度为35.2 MPa.     

稀土强化Al2O3/Ti(C,N)陶瓷材料的组分设计及其使用性能研究

以稀土强化Al2O3/Ti(C,N)陶瓷材料为基础,进行了基于抗冲击性能、抗热震性能和耐磨性能的组分设计.结果发现,与最佳的抗冲击性能、抗热震性能和耐磨性能相对应,弥散相Ti(C,N)的最优体积含量分别为27.7;、26.5;和30.7;,其最优性能分别比纯Al2O3陶瓷提高约71.4;、40.4;和28.9;.在此基础上,实验研究了稀土强化Al2O3/Ti(C,N)陶瓷材料用于刀具时的切削特性.表明该材料具有良好的耐磨性能,可以作为刀具材料使用.     

Y-Ce-ZrO_2-TiC-Al_2O_3复合陶瓷材料的制备及其摩擦磨损特性研究

从提高陶瓷材料的力学性能出发,采用真空热压工艺,制备了混合稀土氧化物稳定的Y-Ce-ZrO2-TiC-Al2O3复合陶瓷材料。对复合陶瓷材料进行了摩擦磨损性能实验研究,采用扫描电镜对其磨损表面形貌进行了观察,对磨损表面物相进行了X射线衍射分析。并与单相ZrO2陶瓷作对比,探讨了复合陶瓷材料的磨损机理。研究表明,该复合陶瓷材料具有较高的综合力学性能,在法向载荷为140 N、转速为200 r/min干摩擦条件下,Y-Ce-ZrO2-TiC-Al2O3复合陶瓷摩擦系数为0.65,磨损率为2.88×10-7mm3/N.m,明显低于单相ZrO2陶瓷,其磨损机理为机械冷焊和粘着磨损。     

B4C-TiB2复相陶瓷材料的研究进展

往B4C中添加适量TiB2形成B4C-TiB2复相陶瓷既可以保留B4C的超硬、低密度等优良性能,又可通过提高陶瓷材料的致密度来改进材料的力学性能,还可降低材料的电阻率使其满足电火花加工的要求,因此B4C-TiB2复相陶瓷是最具有潜力的一类B4C基复合材料.本文从粉体制备、烧结致密化、显微结构、力学性能、电学及加工性能等方面就B4C-TiB2复相陶瓷的最新研究进展作了系统的阐述并对其发展方向做了展望.     

CsI-LiCl共晶材料的坩埚下降法生长与闪烁性能研究

本文采用坩埚下降法,在真空密封的石英坩埚中成功生长出CsI-LiCl与CsI-LiCl:Na共晶闪烁体。通过扫描电子显微镜(SEM)观察晶体微结构表明该共晶中LiCl相与CsI相存在周期性的层状排列,CsI相的厚度在5 μm左右。共晶样品的X射线激发发射谱显示在CsI-LiCl和CsI-LiCl:Na共晶样品存在缺陷发光,在CsI-LiCl样品中还观察到了纯CsI的自陷激子(STE)发光。CsI-LiCl样品在α粒子激发下的多道能谱中观察到明显的全能峰,这一结果证明CsI-LiCl共晶可用于热中子探测的潜力。     

静电纺丝法制备CeO2微纳米纤维及其除氟性能

以聚丙烯腈(PAN)为载体,六水合硝酸铈[Ce(NO₃)₃·6H₂O]为原料,采用静电纺丝法制备了Ce(NO₃)₃/PAN纤维,在空气中热处理得到CeO₂微纳米纤维,通过XRD、BET和SEM对CeO₂微纳米纤维进行表征。采用静态吸附实验探讨了CeO₂微纳米纤维去除水溶液中氟离子的性能,考察了溶液pH值、初始氟离子浓度及共存阴离子等对吸附性能的影响。结果表明,pH=3时,CeO₂微纳米纤维对F^-的吸附性能最佳,CeO₂吸附量随着F^-浓度的增大呈上升趋势。CeO₂微纳米纤维对F^-的吸附等温线遵循Langmuir模型,二级动力学模型能很好地描述CeO₂微纳米纤维对F^-的吸附过程。CeO₂微纳米纤维的除氟性能优良,可为其实际应用提供理论参考。     

Crystal structures of the cis and trans isomers of a tetrathia[3.3.3.3]cyclophane

Both the cis and trans isomers of 3,11,18,26-tetrathiatricyclo[26.2.2.1^5,9.2^13,16.1^20,24] hexatriaconta-5,7,9,20,22,24-hexene have been prepared and structurally characterized. Each of these centrosymmetric tetrathia dimers includes two cyclohexane rings in chair conformations with either 1,4-cis or 1,4-trans bonding and two meta-substituted benzene rings. The cis isomer packs into the monoclinic space group P2₁/a with a = 10.485(3)Å, b = 10.3956(18)Å, c = 14.1343(10)Å, = 105.200(13)°, Z = 2 and refined to an R factor of 0.046. The trans isomer crystallizes in the monoclinic space group P2₁/c with a = 10.7217(12)Å, b = 5.6797(7)Å, c = 25.415(5)Å, = 96.001(12)°, Z = 2 and refined to an R factor of 0.043. In the cis structure each benzene ring faces a cyclohexane ring while in the trans structure the cyclohexane rings face one another.     

First-principles coexistence simulations of supercooled liquid silicon

We perform first-principles coexistence simulations of the low-density and the high-density phases of supercooled liquid silicon and find a negative slope for the coexisting line in the temperature-pressure plane. Electron density maps and electron-localization function plots of the two phases of silicon show marked differences. The calculated differences suggest more localized electrons in the low-density liquid compared to the high-density liquid, coming from an increased population of covalent bonds, which further explain the calculated negative slope in the two phase coexistence regime. This is consistent with the presence of a pseudo-gap in low-density liquid silicon, absent in the high-density liquid which shows a metallic behavior.     

Triethyl ammonium salt of O,O′-bis(p-tolyl)dithiophosphate, [Et3NH]+[(4-MeC6H4O)2PS2]−

Triethyl ammonium Salt of O,O′-bis(p-tolyl)dithiophosphate and O,O′-bis(m-tolyl)dithiophosphate have been obtained by reaction of p- and m-cresol, respectively with P₂S₅ in toluene and have been characterized by elemental analysis, IR, ¹H and ³¹P NMR spectroscopy. The molecular structure of O,O′-bis(p-tolyl)dithiophosphate has been determined. Crystal data: [Et₃NH]⁺[(4-MeC₆H₄O)₂PS₂]⁻: Monoclinic, P2₁/c, a=15.2441(9) ?, b=10.415(2) ?, c=3.9726(9) ?, β=91.709(7)°, V=2217.5(1) ?⁻³, Z=4.Supplementary materials Additional material available from the Cambridge Crystallographic Data Centre (CCDC no. 600927 for [Et₃NH]⁺[(4-MeC₆H₄O)₂PS₂]⁻ comprises the final atomic coordinates for all atoms, thermal parameters, and a complete listing of bond distances and angles. Copies of this information may be obtained free of charge on application to The Director, 12 Union Road, Cambridge CB2 2EZ, UK (fax: +44-1223-336033; email: deposit@ccdc.cam.ac.uk or www:http://www.ccdc.cam.ac.uk).     

电沉积法制备ZnO纳米棒阵列及其发光特性

本文以掺F的SnO2导电玻璃为基板,以硝酸锌水溶液为电解液,采用三电极恒电位体系电沉积制备ZnO纳米棒阵列,系统考察了硝酸锌浓度和沉积电位等工艺参数对ZnO纳米棒阵列的微观形貌及其发光性能的影响规律.结果表明,硝酸锌浓度和沉积电位对纳米棒阵列的形貌有显著影响,控制适宜的工艺条件可以制备出直径分布均匀、结晶性好且纯度高的六方纤锌矿ZnO纳米棒阵列.荧光光谱分析表明,电沉积制备出的ZnO纳米棒阵列在385 nm附近有一个强荧光发射峰,且发光性能稳定、对纳米棒阵列微观形貌的细微变化不敏感,使其在发光二极管和激光器等领域具有广阔的应用前景.     

Crystal structures of thecis andtrans isomers of dithiahexahydro[3.3]metacyclophane

Structures of both thecis andtrans isomers of dithiahexahydro[3.3]metacyclophane, ?C₆H₄?CH₂SCH₂?C₆H₁₀?CH₂SCH₂?, have been determined, wherecis andtrans refer to the attachments to the cyclohexane ring. Thecis form crystallizes in the monoclinic space groupP2₁/c witha=8.4299(11)Å,b=21.772(2)Å,c=8.9724(13)Å, β=116.574(11)^o, andZ=4. Thetrans isomer packs into the monoclinic space groupP2₁ witha=8.159(16)Å,b=10.185(5)Å,c=9.558(2)Å, β=112.435(18)^o, andZ=2. The cyclohexane ring of thecis isomer is in the chair conformation, while the cyclohexane of thetrans isomer is found in a twisted boat conformation.     

CTAB与SDBS对碳酸锶粒子生长形态调控及机理研究

以表面活性剂CTAB和SDBS为化学添加剂,采用化学共沉淀法对碳酸锶晶体的生长形态进行调控,成功地制备出了实心的树枝状和花瓣为空心的花状碳酸锶粉体,并用X射线衍射(XRD)、扫描电子显微镜(SEM)和傅里叶变换红外光谱(FT-IR)等分析手段对样品进行了表征;最后重点对化学添加剂可能产生的影响机理进行了初步的探讨.结果表明,CTAB和SDBS在晶体生长的过程中能起到显著的影响作用,两者对粒子分散性能的作用效果相反,而且后者对晶体(013)和(213)晶面表面能降低的贡献明显大于前者.     

Phase Properties of Hexanedioldiacrylate/E7 Blends

Abstract

Equilibrium phase diagrams of uncured and UV-cured difunctional hexanedioldiacrylate and the eutectic mixture of low molecular weight liquid crystals E7 are established by polarized optical microscopy and differential scanning calorimetry. Data are analyzed using the Maier-Saupe model of nematic order. In the case of the uncured system the Flory-Huggins free energy of isotropic mixing is applied while for the cured system, the Flory-Rehner elastic free energy model is used. A good correlation between experimental and theoretical phase diagrams is found in both systems.