Preparation and properties of electroless Ni-P-SiO2 composite coatings

Dispersible SiO₂ nanoparticles were co-deposited with electroless Ni-P coating onto AISI-1045 steel substrates in the absence of any surfactants in plating bath. The resulting Ni-P/nano-SiO₂ composite coatings were heat-treated for 1 h at 200 °C, 400 °C, and 600 °C, respectively. The hardness and wear resistance of the heat-treated composite coatings were measured. Moreover, the structural changes of the composite coatings before and after heat treatment were investigated by means of X-ray diffraction (XRD), while their elemental composition and morphology were analyzed using an energy dispersive spectrometer (EDS) and a scanning electron microscope (SEM). Results show that co-deposited SiO₂ particles contributed to increase the hardness and wear resistance of electroless Ni-P coating, and the composite coating heat-treated at about 400 °C had the maximum hardness and wear resistance.     

Influences of laser remelting on microstructure of nanostructured Al2O3-13 wt.% TiO2 coatings fabricated by plasma spraying

The effects of laser remelting on microstructure of nanostructured Al₂O₃-13 wt.% TiO₂ ceramic coatings prepared by plasma spraying with agglomerated powders were studied. The microstructure of the feedstock, as-sprayed and laser-remelted coatings were investigated by using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffractometry (XRD). The results indicate that the plasma-sprayed ceramic coating consists of both fully melted regions and partially melted regions. The totally ceramic coating, especially the fully melted regions, has a typical plasma-sprayed lamellar-like structure as the conventional coating, and has some pores. According to the difference of microstructures, the partially melted regions can be divided into liquid-phase sintered regions (a three-dimensional net or skeleton-like structure: Al₂O₃-rich submicron particles embedded in the TiO₂-rich matrix) and solid-phase sintered regions (remained nanoparticles). The lamellar defect of the as-sprayed coating is erased, and the compactness of the coating is improved significantly after laser remelting. The laser-remelted region composed of fine equiaxed grains, which are different from the conventional column-like crystals along the direction of the heat current. Due to the rapid solidification of laser remelting process, there are still some nanoparticles in the remelted region because of an insufficient time for grains growth.     

Cycle oxidation behavior of nanostructured Ni60-TiB2 composite coating sprayed by HVOF technique

Cycle oxidation resistance at 800 °C in static air was investigated for a nanostructured Ni60-TiB₂ composite coating sprayed by high velocity oxy-fuel (HVOF). For comparison, a Ni60-TiB₂ conventional composite coating was also studied. The results indicate that, the oxidation processes of both composite coatings are controlled by diffusion mechanism, and the nanostructured composite coating has better cycle oxidation resistance than that of the conventional composite coating. The reasons for this improvement can be attributed to the formation of the intact SiO₂ and Cr₂O₃ protective layer, and the enhanced adhesion between oxide film and nanostructure coating.     

Microstructure and wear behaviors of laser clad NiCr/Cr3C2-WS2 high temperature self-lubricating wear-resistant composite coating

The high temperature self-lubricating wear-resistant NiCr/Cr₃C₂-30%WS₂ coating and wear-resistant NiCr/Cr₃C₂ coating were fabricated on 0Cr18Ni9 austenitic stainless steel by laser cladding. Phase constitutions and microstructures were investigated, and the tribological properties were evaluated using a ball-on-disc wear tester under dry sliding condition at room-temperature (17 °C), 300 °C and 600 °C, respectively. Results indicated that the laser clad NiCr/Cr₃C₂ coating consisted of Cr₇C₃ primary phase and γ-(Fe,Ni)/Cr₇C₃ eutectic colony, while the coating added with WS₂ was mainly composed of Cr₇C₃ and (Cr,W)C carbides, with the lubricating WS₂ and CrS sulfides as the minor phases. The wear tests showed that the friction coefficients of two coatings both decrease with the increasing temperature, while the both wear rates increase. The friction coefficient of laser clad NiCr/Cr₃C₂-30%WS₂ is lower than the coating without WS₂ whatever at room-temperature, 300 °C, 600 °C, but its wear rate is only lower at 300 °C. It is considered that the laser clad NiCr/Cr₃C₂-30%WS₂ composite coating has good combination of anti-wear and friction-reducing capabilities at room-temperature up to 300 °C.     

Magnetic and electrical properties of bulk BaTiO3+MgFe2O4 composite

BaTiO₃+MgFe₂O₄ material system was synthesized by hybrid chemical process using chlorides and nitrates of barium, titanium, iron, and magnesium. Magnetic properties of the composite samples measured as a function of annealing conditions indicated soft magnetic behavior. Saturation specific magnetization from 8 21 emu/g was observed for samples annealed at temperature between 950 and 1150 °C. Variation of specific saturation magnetization with respect to annealing temperature was related with the distribution of Fe cations in the tetrahedral and octahedral sites of MgFe₂O₄. Electrical properties of the samples annealed at different temperatures were measured to analyze the coexistence of ferroelectric phase. Dielectric constant varying from 15 to 200 with respect to frequency was observed for samples annealed from 950 to 1150 °C.     

Laser surface remelting of plasma sprayed nanostructured Al2O3-13wt%TiO2 coatings on titanium alloy

Plasma sprayed nanostructured coatings were successfully fabricated on a titanium alloy (Ti-6Al-4V) substrate using the as-prepared nanostructured Al₂O₃-13wt%TiO₂ feedstock. A CO₂ laser was used to remelt the plasma sprayed coatings. The effects of laser remelting on the phase constituents, microstructure and properties of the ceramic coatings were investigated. The laser remelted coatings (LRmC) possessed a much denser and more homogenous structure and excellent metallurgical bonding to the substrate. The average porosity of the LRmC was reduced to 0.9%, compared with 6.2% of the as-sprayed coatings. The net-like structure in the as-prepared feedstock remained in the coatings before and after laser remelting. The metastable γ-Al₂O₃ phase in the as-sprayed coatings transformed to stable α-Al₂O₃ during laser remelting. The LRmC could remain nanostructure. The microhardness of the coatings was enhanced to 1000-1400 HV_0.3 after laser remelting, which was much higher than that of the plasma sprayed coatings and 2-3 times higher that of the substrate. Significant decreases in surface roughness were also found in the LRmC.     

TiO2 thick films supported on reticulated macroporous Al2O3 foams and their photoactivity in phenol mineralization

TiO₂ thick films deposited on macroporous reticulated Al₂O₃ foams with pore size of 10 ppi and 15 ppi were prepared using dip coating from slurries of Aeroxide^® P25 nanopowder and precipitated titania. All prepared films have sufficiently good adhesion to the surface of the substrate also in case of strongly cracked films. No measurable release of deposited TiO₂ after repeated photocatalytic cycles was observed. The photocatalytic activity was characterized as the rate of mineralization of aqueous phenol solution under irradiation of UVA light by TOC technique. The best activity was obtained with Aeroxide^® P25 coated Al₂O₃ foam with the pore size of 10 ppi, annealed at 600 °C. The optimal annealing temperature for preparation of films from precipitated titania could be determined at 700 °C. Films prepared by sol-gel deposition technique were considerably thinner compared to coatings made of suspensions and their photocatalytic activity was significantly smaller.     

Interfacial reactions and oxidation behavior of Al2O3 and Al2O3/Al coatings on an orthorhombic Ti2AlNb alloy

The uniform and dense Al₂O₃ and Al₂O₃/Al coatings were deposited on an orthorhombic Ti₂AlNb alloy by filtered arc ion plating. The interfacial reactions of the Al₂O₃/Ti₂AlNb and Al₂O₃/Al/Ti₂AlNb specimens after vacuum annealing at 750 °C were studied. In the Al₂O₃/Ti₂AlNb specimens, the Al₂O₃ coating decomposed significantly due to reaction between the Al₂O₃ coating and the O-Ti₂AlNb substrate. In the Al₂O₃/Al/Ti₂AlNb specimens, a γ-TiAl layer and an Nb-rich zone came into being by interdiffusion between the Al layer and the O-Ti₂AlNb substrate. The γ-TiAl layer is chemically compatible with Al₂O₃, with no decomposition of Al₂O₃ being detected. No internal oxidation or oxygen and nitrogen dissolution zone was observed in the O-Ti₂AlNb alloy. The Al₂O₃/Al/Ti₂AlNb specimens exhibited excellent oxidation resistance at 750 °C.     

Characteristics and heat treatment of cold-sprayed Al-Sn binary alloy coatings

In this study, Al-Sn binary alloy coatings were prepared with Al-5 wt.% Sn (Al-5Sn) and Al-10 wt.% Sn (Al-10Sn) gas atomized powders by low pressure and high pressure cold spray process. The microstructure and microhardness of the coatings were characterized. To understand the coarsening of tin in the coating, the as-sprayed coatings were annealed at 150, 200, 250 and 300 °C for 1 h, respectively. The effect of annealing on microstructure and the bond strength of the coatings were investigated. The results show that Al-5Sn coating can be deposited by high pressure cold spray with nitrogen while Al-10Sn can only be deposited by low pressure cold spray with helium gas. Both Al-5Sn and Al-10Sn coatings present dense structures. The fraction of Sn in as-sprayed coatings is consistent with that in feed stock powders. The coarsening and/or migration of Sn phase in the coatings were observed when the annealing temperature exceeds 200 °C. Furthermore, the microhardness of the coatings decreased significantly at the annealing temperature of 250 °C. EDXA analysis shows that the heat treatment has no significant effect on fraction of Sn phase in Al-5Sn coatings. Bonding strength of as-sprayed Al-10Sn coating is slightly higher than that of Al-5Sn coating. Annealing at 200 °C can increase the bonding strength of Al-5Sn coatings.     

High performance nanostructured ZrO2 based thermal barrier coatings deposited by high efficiency supersonic plasma spraying

In this paper, the nanostructured zirconia (ZrO₂) based thermal barrier coatings (TBCs) deposited by high efficiency supersonic atmospheric plasma spraying (SAPS), were described. The phase composition, microstructure, thermal conductivity and thermal shock resistance of as-sprayed coating were studied. The results revealed that the as-sprayed coating was composed of tetragonal zirconia and consisted of some unmelted nanoparticles (30-50 nm) and nanograins (60-110 nm), and the latter was the main microstructure of the coating. The nanograins and homogeneously distributed micro-cracks of coating resulted in not only low thermal conductivity, but also high thermal cycling lives. Besides, the failure process of coating during thermal cycles was also investigated in the present work.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Electrical properties vs. microstructure of nanocrystallized V2O5-P2O5 glasses — An extended temperature range study

An electronically conducting nanomaterial was synthesized by nanocrystallization of a 90V₂O₅·10P₂O₅ glass and its electrical properties were studied in an extended temperature range from − 170 to + 400 °C. The conductivity of the prepared nanomaterial reaches 2 ? 10^− 1 S cm^− 1 at 400 °C and 2 ? 10^− 3 S cm^− 1 at room temperature. It is higher than that of the original glass by a factor of 25 at room temperature and more than 100 below − 80 °C. A key role in the conductivity enhancement was ascribed to the material's microstructure, and in particular to the presence of the large number of small (ca. 20 nm) grains of crystalline V₂O₅. The observed conductivity dependencies are discussed in terms of the Mott's theory of the electronic hopping transport in disordered systems. Since V₂O₅ is known for its ability to intercalate lithium, the presented results might be helpful in the development of cathode materials for Li-ion batteries.     

Immobilization of glucose oxidase using CoFe2O4/SiO2 nanoparticles as carrier

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. Glucose oxidase (GOD) was immobilized on CoFe₂O₄/SiO₂ NPs via cross-linking with glutaraldehyde (GA). The optimal immobilization condition was achieved with 1% (v/v) GA, cross-linking time of 3 h, solution pH of 7.0 and 0.4 mg GOD (in 3.0 mg carrier). The immobilized GOD showed maximal catalytic activity at pH 6.5 and 40 °C. After immobilization, the GOD exhibited improved thermal, storage and operation stability. The immobilized GOD still maintained 80% of its initial activity after the incubation at 50 °C for 25 min, whereas free enzyme had only 20% of initial activity after the same incubation. After kept at 4 °C for 28 days, the immobilized and free enzyme retained 87% and 40% of initial activity, respectively. The immobilized GOD maintained approximately 57% of initial activity after reused 7 times. The K_M (Michaelis-Menten constant) values for immobilized GOD and free GOD were 14.6 mM and 27.1 mM, respectively.     

Plasma sprayed Al2O3/FeCrAl composite coatings for electromagnetic wave absorption application

Al₂O₃/FeCrAl composite coatings were fabricated by atmosphere plasma spraying technique. Microstructure and dielectric properties in the frequency range from 8.2 to 12.4 GHz were investigated. The microstructure of composite coatings shows a uniform dispersion of metal particles with litter pores and microcracks in the composite coatings. The relaxation polarization and interfacial polarization in the coatings would contribute to enhance ?′ with rising FeCrAl content, and the associated loss could be considered as a dominating factor enhancing ?″. By calculating the microwave-absorption as a single-layer absorber, for the composite coatings with 41 wt.% FeCrAl content, the reflection loss values exceeding −10 dB are achieved in the frequency range of 9.1-10.6 GHz when the coating thickness is 1.3 mm.     

Correlation between Al2O3 particles and interface of Al-Al2O3 coatings by cold spray

Al-Al₂O₃ composite coatings with different Al₂O₃ particle shapes were prepared on Si and Al substrate by cold spray. The powder compositions of metal (Al) and ceramic (Al₂O₃) having different sizes and agglomerations were varied into ratios of 10:1 wt% and 1:1 wt%. Al₂O₃ particles were successfully incorporated into the soft metal matrix of Al. It was found that crater formation between the coatings and substrate, which is typical characteristic signature of cold spray could be affected by initial starting Al₂O₃ particles. In addition, when the large hard particles of fused Al₂O₃ were employed, the deep and big craters were generated at the interface between coatings and hard substrates. In the case of pure soft metal coating such as Al on hard substrate, it is very hard to get proper adhesion due to lack of crater formation. Therefore, the composite coating would have certain advantages.     

Stabilization of a very high-k crystalline ZrO2 phase by post deposition annealing of atomic layer deposited ZrO2/La2O3 dielectrics on germanium

The impact of the ZrO₂/La₂O₃ film thickness ratio and the post deposition annealing in the temperature range between 400 °C and 600 °C on the electrical properties of ultrathin ZrO₂/La₂O₃ high-k dielectrics grown by atomic layer deposition on (1 0 0) germanium is investigated. As-deposited stacks have a relative dielectric constant of 24 which is increased to a value of 35 after annealing at 500 °C due to the stabilization of tetragonal/cubic ZrO₂ phases. This effect depends on the absolute thickness of ZrO₂ within the dielectric stack and is limited due to possible interfacial reactions at the oxide/Ge interface. We show that adequate processing leads to very high-k dielectrics with EOT values below 1 nm, leakage current densities in the range of 0.01 A/cm², and interface trap densities in the range of 2-5 × 10¹² eV⁻¹ cm⁻².     

Effect of vacuum heat treatment on tensile strength and fracture performance of cold-sprayed Cu-4Cr-2Nb coatings

The previous study [1] indicated that dense thick Cu-4Cr-2Nb coatings could be formed by cold spraying, and the post-spray heat treatment could significantly influence the microstructure and microhardness of the as-sprayed Cu-4Cr-2Nb coatings. In this study, the tensile strength and fracture performance of the Cu-4Cr-2Nb coatings after annealing were investigated. The vacuum heat treatment was conducted under 10⁻² Pa at 850 °C for 4 h. Results showed that the heat treatment had a great contribution to the healing-up of the incompleteness of the interfaces between the deposited particles. In addition, the coating microhardness decreased from 156.8 ± 4.6 Hv_0.2 for the as-sprayed coatings to 101.7 ± 4.5 Hv_0.2 for the annealed ones. The mean tensile strength of the annealed coatings was approximately 294.1 ± 36.1 MPa compared to that of 45.0 ± 10.5 MPa for the as-sprayed ones, which results from the partially metallurgically bonded zones between the deposited particles inducing by the heat treatment process.     

Double-ceramic-layer thermal barrier coatings based on La2(Zr0.7Ce0.3)2O7/La2Ce2O7 deposited by electron beam-physical vapor deposition

Double-ceramic-layer (DCL) thermal barrier coatings (TBCs) of La₂(Zr_0.7Ce_0.3)₂O₇ (LZ7C3) and La₂Ce₂O₇ (LC) were deposited by electron beam-physical vapor deposition (EB-PVD). The composition, interdiffusion, surface and cross-sectional morphologies, cyclic oxidation behavior of DCL coating were studied. Energy dispersive spectroscopy and X-ray diffraction analyses indicate that both LZ7C3 and LC coatings are effectively fabricated by a single LZ7C3 ingot with properly controlling the deposition energy. The chemical compatibility of LC coating and thermally grown oxide (TGO) layer is unstable. LaAlO₃ is formed due to the chemical reaction between LC and Al₂O₃ which is the main composition of TGO layer. Additionally, the thermal cycling behavior of DCL coating is influenced by the interdiffusion of Zr and Ce between LZ7C3 and LC coatings. The failure of DCL coating is a result of the sintering of LZ7C3 coating surface, the chemical incompatibility of LC coating and TGO layer and the abnormal oxidation of bond coat. Since no single material that has been studied so far satisfies all the requirements for high temperature applications, DCL coating is an important development direction of TBCs.     

Structural and optical properties of SrCu2O2 films deposited on sapphire substrates by pulsed laser deposition

We deposited SrCu₂O₂ (SCO) films on sapphire (Al₂O₃) (0 0 0 1) substrates by pulsed laser deposition. The crystallographic orientation of the SCO thin film showed clear dependence on the growth temperature. X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis showed that the film deposited at 400 °C was mainly oriented in the SCO [2 0 0] direction, whereas when the growth temperature was increased to 600 °C, the SCO film showed a dominant orientation of SCO [1 1 2]. The SCO film deposited at 500 °C was obvious polycrystalline, showing multi peaks from (2 0 0), (1 1 2), and (2 1 1) diffraction in the XRD spectrum. The SCO film deposited at 600 °C showed a band gap energy of 3.3 eV and transparency up to 80% around 500 nm. The photoluminescence (PL) spectra of the SCO films grown at 500 °C and 600 °C mainly showed blue-green emission, which was attributed to the intra-band transition of the isolated Cu⁺ and Cu⁺–Cu⁺ pairs according to the temperature dependent-PL analysis.     

Surface study of fine MgFe2O4 ferrite powder prepared by chemical methods

To study surface behaviors, MgFe₂O₄ ferrite materials having different grain sizes were synthesized by two different chemical methods, i.e., a polymerization method and a reverse coprecipitation method. The single phase of the cubic MgFe₂O₄ was confirmed by the X-ray diffraction method for both the precursors decomposed at 600-1000 °C except for a very small peak of Fe₂O₃ was detected for the samples calcined at 600 and 700 °C by the polymerization method. The crystal size and particle size increased with an increase in the sintering temperature using both methods. The conductance of the MgFe₂O₄ decreased when the atmosphere was changed from ambient air to air containing 10.0 ppm NO₂. The conductance change, C = G(air)/G(10 ppm NO₂), was reduced with an increase in the operating temperature. For the polymerization method, the maximum C-value was ca. 40 at 300 °C for the samples sintered at 900 °C. However, the samples sintered at 1000 °C showed a low conductance change in the 10 ppm NO₂ gas, because the ratio of the O₂ gas adsorption sites on the particle surface is smaller than those of the samples having a high C-value. The low Mg content on the surface affects the low ratio of the gas adsorption sites. For the reverse coprecipitation method, the particle size was smaller than that of the polymerization method. Although a stable conductance was obtained for the sample sintered at 900 and 1000 °C, its conductance change was less than that of the polymerization method.