Synthesis and near-infrared luminescence properties of LaOCl:Nd3+/Yb3+

Near-infrared emitting phosphors LaOCl:Nd³⁺/Yb³⁺ were prepared by the solid-state method, and their structures and luminescent properties were investigated by using X-ray diffraction and photoluminescence analysis, respectively. The studies shows that tetragonal LaOCl:Nd³⁺/Yb³⁺ can be synthesized by the solid-state reaction at 600 °C for 3 h. Upon 353 nm UV excitation, LaOCl:Nd³⁺/Yb³⁺ sample shows strong near-infrared emission lines in the region of 1060–1150 nm (corresponding to ⁴F_3/2 → ⁴I_J′ transition of Nd³⁺, J′ = 9/2, 11/2, 13/2, 15/2) and 980–1050 nm (corresponding to ²F_5/2 → ²F_7/2 transition of Yb³⁺). The decreasing emission intensity of Nd³⁺ with increasing doping concentration of Yb³⁺ proved the energy transfer in LaOCl:Nd³⁺/Yb³⁺. The possible near-infrared emission and energy transfer mechanism between Nd³⁺ and Yb³⁺, as well as the energy transfer efficiency of LaOCl:Nd³⁺/Yb³⁺ were discussed.     

磷酸盐玻璃中Yb3+和Nd3+之间的声子参助能量转移

本文中报道了磷酸盐玻璃中Nd³⁺,Yb³⁺的时间分辨谱和激发能量的转移。通过实验确定了在不同温度下的转移速率。证实了Nd³⁺→Yb³⁺的能量转移机构为从⁴F_3/2(Nd³⁺)到²F_5/2(Yb³⁺)并同时产生单声子发射的过程;而从Yb³⁺到Nd³⁺关键词：     

Microstructural and Radioluminescence Characteristics of Nd<Superscript>3+</Superscript> Doped Columbite-Type SrNb<Subscript>2</Subscript>O<Subscript>6</Subscript> Phosphor

Undoped and different concentration Nd³⁺ doped SrNb₂O₆ powders with columbite structure were synthesized by molten salt process using a mixture of strontium nitrate and niobium (V) oxide and NaCl-KCl salt mixture as a flux under relatively low calcining temperature. X-ray diffraction analysis results indicated that SrNb₂O₆ phases found to be orthorhombic columbite single phase for undoped, 0.5 and 3 mol% Nd³⁺ doping concentrations. Phase composition of the powders was examined by SEM-EDS analyses. Radioluminescence properties of Nd³⁺ doped samples from UV to near-IR spectral region were studied. The emissions increased with the doping concentration of up to 3 mol%, and then decreased due to concentration quenching effect. There is a sharp emission peak around 880 nm associated with ⁴F_5/2 → ⁴I_9/2 transition in the Nd³⁺ ion between 300 and 1100 nm. The broad emission band intensity was observed from 400 to 650 nm where the peak intensities increased by increasing Nd³⁺ doping concentration. All the measurements were taken under the room temperature.     

Towards efficient upconversion and downconversion of NaYF4:Ho3+,Yb3+ phosphors

NaYF₄ microcrystals co-doped with Ho³⁺ and Yb³⁺ were prepared by a facile hydrothermal synthesis. The products were characterized by X-ray diffractometer, scanning electron microscopy, and photoluminescence spectroscopy. Upon excitation with a 980 nm laser diode, the sample shows an intense green upconversion emission centered at 540 nm corresponding to the ⁵S₂→⁵I₈ transition of Ho³⁺. The quadratic dependence of the green emission intensity on the excitation power reveals a two-phonon upconversion process. On the contrary, upon excitation with 448 nm, both visible and near-infrared emissions peaked at 483, 540, 644, 749, and 978 nm are simultaneously observed, which could be assigned to the electronic transitions of Ho³⁺: ⁵F₃→⁵I₈, ⁵S₂→⁵I₈, ⁵F₅→⁵I₈, ⁵S₂→⁵I₇, and Yb³⁺: ²F_5/2→²F_7/2, respectively. The energy transfer processes between Ho³⁺ and Yb³⁺ ions and the involved mechanisms have been investigated and discussed.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Nd3+ → Yb3+ energy transfer in a codoped metaphosphate glass as a model for Yb3+ laser operation around 980 nm

A complete spectroscopic investigation of a metaphosphate glass with composition Pb(PO₃)₂ doped with various amounts of Nd³⁺ and Yb³⁺ (1 up to 10 at.%) is reported. Efficient Nd³⁺ → Yb³⁺ energy transfers occur both radiatively and non-radiatively, the latter being dominant and partly resonant and partly phonon-assisted by phonons of the order of 950 cm⁻¹, which fits well with the reported Raman spectrum of the material. These transfers mainly concern the ⁴F_3/2 → ⁴I_9/2 emission and the ²F_7/2 → ²F_5/2 absorption transitions of the Nd³⁺ and Yb³⁺ ions around 900 nm, respectively. They are analysed both via spectral and temporal data. The results show that about 5% Nd³⁺ and 5% Yb³⁺ ions have to be incorporated to reach energy transfers exceeding about 65%, which is in agreement with data recently reported in the case of a YAl₃(BO₃)₄ crystal. Simulations based on the obtained data show that laser thresholds of a few tens of mW should be easily attainable by operating the materials in a channel waveguide configuration.     

Spectroscopic investigations of Nd-, Er-, Er/Yb-, and Tm-ions doped SiO2-Al2O3-CaF2-GdF3 glasses

This paper reports on the absorption, visible and near-infrared luminescence properties of Nd³⁺, Er³⁺, Er³⁺/2Yb³⁺, and Tm³⁺ doped oxyfluoride aluminosilicate glasses. From the measured absorption spectra, Judd-Ofelt (J-O) intensity parameters (Ω₂, Ω₄ and Ω₆) have been calculated for all the studied ions. Decay lifetime curves were measured for the visible emissions of Er³⁺ (558 nm, green), and Tm³⁺ (650 and 795 nm), respectively. The near infrared emission spectrum of Nd³⁺ doped glass has shown full width at half maximum (FWHM) around 45 nm (for the ⁴F_3/2→⁴I_9/2 transition), 45 nm (for the ⁴F_3/2→⁴I_11/2 transition), and 60 nm (for the ⁴F_3/2→⁴I_13/2 transition), respectively, with 800 nm laser diode (LD) excitation. For Er³⁺, and Er³⁺/2Yb³⁺ co-doped glasses, the characteristic near infrared emission bands were spectrally centered at 1532 and 1544 nm, respectively, with 980 nm laser diode excitation, exhibiting full width at half maximum around 50 and 90 nm for the erbium ⁴I_13/2→⁴I_15/2 transition. The measured maximum decay times of ⁴I_13/2→⁴I_15/2 transition (at wavelength 1532 and 1544 nm) are about 5.280 and 5.719 ms for 1Er³⁺ and 1Er³⁺/2Yb³⁺ (mol%) co-doped glasses, respectively. The maximum stimulated emission cross sections for ⁴I_13/2→⁴I_15/2 transition of Er³⁺ and Er³⁺/Yb³⁺ are 10.81×10⁻²¹ and 5.723×10^-21 cm². These glasses with better thermal stability, bright visible emissions and broad near-infrared emissions should have potential applications in broadly tunable laser sources, interesting optical luminescent materials and broadband optical amplification at low-loss telecommunication windows.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Optical Analysis of Er3+:Boro-Fluoro-Phosphate Glasses

This paper deals with the preparation and optical analysis of Er³⁺ (0.2 mol%) boro-fluoro-phosphate glasses in the following glass compositions:

• Series A: 69.8 B₂O₃–10 P₂O₅–10(ZnO/CdO/TeO₂)–10 AlF₃

• Series B: 69.8 B₂O₃–10 P₂O₅–10(ZnO/CdO/TeO₂)–10 LiF

Measured Vis-NIR absorption spectra of Er³⁺:boro-fluoro-phosphate glasses have revealed nine absorption bands at 377 nm, 405 nm, 450 nm, 486 nm, 519 nm, 543 nm, 649 nm, 973 nm and 1529 nm, which correspond with the transitions of ⁴I_15/2 → ⁴G_11/2, (²G_9/2,⁴H_9/2), ⁴F_5/2, ⁴F_7/2, ²H_11/2, ⁴S_3/2, ⁴F_9/2, ⁴I_11/2, and ⁴I_13/2, respectively. With an excitation at λ _exci = 375 nm, a bright green emission (⁴S_3/2 → ⁴I_15/2) at 547 nm has been observed from these erbium glasses. Judd–Ofelt characteristic intensity Ω_λ (λ = 2, 4, 6) parameters are obtained from the absorption spectra, and these results were used to compute the radiative properties of Er³⁺:boro-fluoro-phosphate glasses. The NIR emission (⁴I_13/2 → ⁴I_15/2) at 1547 nm from these glasses was measured with an Ar⁺ laser (514.5 nm) as an excitation source.     

Up conversion luminescence of Yb3+–Er3+ codoped CeO2 nanocrystals with imaging applications

The effects of Yb³⁺ doping on up conversion in Yb³⁺–Er³⁺ co-doped cerium oxide nanocrystals are reported. Green emission around 545 and 560 nm attributed to the ²H_11/2, ⁴S_3/2→⁴I_15/2 transitions and red emission around 660 and 680 nm due to ⁴F_9/2→ ⁴I_15/2 transitions under 975 nm excitation were studied at room temperature. Both green and red emission intensities increase as the Yb³⁺ concentration increases from 0%. Emission strength starts to decrease after the Yb³⁺ concentration exceeds a critical amount. The green emission strength peaks around 1% Yb³⁺ concentration while the red emission strength peaks around 4%. An explanation of competition between different decay mechanisms is presented to account for the luminescence dependence on Yb³⁺ concentration. Also, the application of up converting nanoparticles in biomedical imaging is demonstrated.     

The upconversion luminescence and magnetism in Yb<Superscript>3+</Superscript>/Ho<Superscript>3+</Superscript> co-doped LaF<Subscript>3</Subscript> nanocrystals for potential bimodal imaging

Biocompatible upconversion nanoparticles with multifunctional properties can serve as potential nanoprobes for multimodal imaging. Herein, we report an upconversion nanocrystal based on lanthanum fluoride which is developed to address the imaging modalities, upconversion luminescence imaging and magnetic resonance imaging (MRI). Lanthanide ions (Yb³⁺ and Ho³⁺) doped LaF₃ nanocrystals (LaF₃ Yb³⁺/Ho³⁺) are fabricated through a rapid microwave-assisted synthesis. The hexagonal phase LaF₃ nanocrystals exhibit nearly spherical morphology with average diameter of 9.8 nm. The inductively coupled plasma mass spectrometry (ICP-MS) analysis estimated the doping concentration of Yb³⁺ and Ho³⁺ as 3.99 and 0.41%, respectively. The nanocrystals show upconversion luminescence when irradiated with near-infrared (NIR) photons of wavelength 980 nm. The emission spectrum consists of bands centred at 542, 645 and 658 nm. The stronger green emission at 542 nm and the weak red emissions at 645 and 658 nm are assigned to ⁵S₂ → ⁵I₈ and ⁵F₅ → ⁵I₈ transitions of Ho³⁺, respectively. The pump power dependence of luminescence intensity confirmed the two-photon upconversion process. The nanocrystals exhibit paramagnetism due to the presence of lanthanide ion dopant Ho³⁺ and the magnetization is 19.81 emu/g at room temperature. The nanocrystals exhibit a longitudinal relaxivity (r ₁) of 0.12 s^?1 mM^?1 and transverse relaxivity (r ₂) of 28.18 s^?1 mM^?1, which makes the system suitable for developing T2 MRI contrast agents based on holmium. The LaF₃ Yb³⁺/Ho³⁺ nanocrystals are surface modified by PEGylation to improve biocompatibility and enhance further functionalisation. The PEGylated nanocrystals are found to be non-toxic up to 50 μg/mL for 48 h of incubation, which is confirmed by the MTT assay as well as morphological studies in HeLa cells. The upconversion luminescence and magnetism together with biocompatibility enables the adaptability of the present system as a nanoprobe for potential bimodal imaging.     

The fluorescence properties of Yb3+ and Er3+ Co-doped YAl3(BO3)4 powders prepared by sol-gel method

Yb³⁺ and Er³⁺ co-doped YAB powders were prepared by sol-gel method. The structure and fluorescence properties were investigated. XRD pattern indicated that the single phase was obtained at 1150°C and the structure belonged to rhombohedral. Under 379 nm excitation, two emissions around 983 nm and 1531 nm were observed and the effect of Yb³⁺ ion concentration on the emission intensity was discussed. The energy transfer was observed under 930 nm excitation and the energy transfer efficiencies for all samples were calculated. The lifetimes of ² F _5/2 level of Yb³⁺ ion and ⁴ I _13/2 level of Er³⁺ ion were measured and the effect of Yb³⁺ ion concentration on the lifetime was also discussed. The results indicated that there was an additional mechanism for the decay of ⁴ I _13/2 level in powder samples. The Yb³⁺ and Er³⁺ co-doped YAB powders should be a potential candidate for ceramic laser materials.     

Improvement of thermal and spectroscopic behavior of Er<Superscript>3+</Superscript>/Ce<Superscript>3+</Superscript> co-doped tellurite glass for lasing materials

Tellurite glasses (TeO₂–ZnO–Nb₂O₅) mono-doped Er³⁺ and co-doped Er³⁺/Ce³⁺ have been prepared using the melt-quenching technique. To evaluate the effect of Ce³⁺ on the structural, thermal stability of glass hosts and fluorescence properties of Er³⁺, X-ray diffraction patterns, Ftir spectra, differential scanning calorimeter curves, absorption spectra, fluorescence emission spectra, fluorescence lifetimes, up-conversion emission spectra of glass samples were measured and investigated. Using Judd–Ofelt theory, we calculated intensity parameters (Ω₂, Ω₄ and Ω₆), spontaneous emission probabilities, the radiative lifetime, luminescence branching factors and the quantum yield of luminescence for ⁴I_13/2 → ⁴I_15/2 transition. The co-doping with Ce³⁺ was effective on the suppression of up-conversion emission of Er³⁺ owing to the phonon-assisted energy transfer: Er³⁺:⁴I_11/2 + Ce³⁺:²F_5/2 → Er³⁺:⁴I_13/2 + Ce³⁺:²F_7/2 which contributed the effective enhancement of 1.53 µm fluorescence emission. The change in optical properties with the addition of Ce³⁺ ions have been discussed and compared with other glasses. Using the Mc Cumber method for the ⁴I_13/2 → ⁴I_15/2 transition, absorption cross-section, calculated emission cross-section, and gain cross-section values support that TZNEr1Ce1 glass is a potential material for developing broad-band and high-gain erbium-doped fiber amplifiers applied for 1.53 µm.     

A study of energy transfer phenomenon leading to photon up-conversion in Ho3+:Yb3+:CaF2 crystalline powders and its temperature sensing properties

When Ho³⁺:Yb³⁺:CaF₂ crystalline powders prepared by combustion synthesis were exposed to near-infrared (λ ～ 975 nm) radiation, intense photon up-conversion (UC) was observed at the visible with emission bands peaked at ～ 545, ～650 and ～750 nm identified as 4f-4f transitions from higher levels (⁵F₄, ⁵S₂) and ⁵F₅ to lower levels ⁵I₈ and ⁵I₇ of Ho³⁺. The emission bands at the green and red, in particular, have been demonstrated to be useful for temperature sensing based on luminescence intensity ratio technique. However, no model is available in literature to explain the change of the electronic populations of states (⁵F₄, ⁵S₂) and ⁵F₅ with temperature. The UC phenomenon was studied from both theoretical and experimental points of view. A rate equation model with temperature dependent parameters for Ho³⁺ and Yb³⁺ electronic populations considering a high sensitization of Ho³⁺ ions by Yb³⁺ ions was used. High Yb³⁺ → Ho³⁺ energy transfer efficiency was found (～88% at room temperature). The change with temperature predicted by the model for the luminescence intensity ratio of the UC green and red emission lines agrees well with the experimental data.     

A novel scheme to acquire enhanced up-conversion emissions of Ho3+ and Yb3+ co-doped Sc2O3

A detailed investigation about the effect of Sc₂O₃: 1 mol%Ho³⁺/5 mol%Yb³⁺ co-doped with Ce⁴⁺ ions prepared by sol-gel methods was performed systematically. Under the excitation of 980 nm laser diode, both green emission (553 nm, ⁵F₄/⁵S₂→⁵I₈) and red emission (672 nm, ⁵F₅→⁵I₈) were both observed in the emission spectra of the samples, which were found to be two-photon process and sensitized by Yb³⁺ ions. With the increasing of Ce⁴⁺ ions, the up-conversion green emission intensity are increased by 6.52, 8.69, 10.85, 13.92 and 16.66 fold, corresponding to the Ce⁴⁺ ions concentrations from 5 mol% to 13 mol%, respectively. The number of photons are necessary to populate the upper emitting state decreases to 2 and the infrared absorption coefficient is reduced, when the Ce⁴⁺ ions concentration increase to 13 mol%. Ce⁴⁺ ions play an important role in tailoring the local crystal field around Ho³⁺ ions, lowering the highest phonon cut-off energy of matrix and reducing the infrared absorption coefficient, thus hindering the non-radiative processes, which contribute to the increased emission intensity. The excellent enhancement makes it a promising multifunctional optical luminescence material.     

Synthesis and up-conversion luminescence properties of Ho3+, Yb3+ co-doped BaLa2ZnO5

Up-conversion phosphors BaLa₂ZnO₅ co-doped with Ho³⁺/Yb³⁺ were synthesized by high temperature solid-state reaction method. The phase composition of the phosphors was characterized by X-ray diffraction (XRD). The structure of BaLa₂ZnO₅: 0.75% Ho/15% Yb phosphor was refined by the Rietveld method and results showed the decreased unit cell parameters and cell volume after doping Ho³⁺ and Yb³⁺, indicating Ho³⁺ and Yb³⁺ have successfully replaced La³⁺. Under the excitation of 980 nm diode laser, the strong green and weak red up-conversion emissions centered at 548 nm, 664 nm and 758 nm were observed, which originating from ⁵S₂, ⁵F₂→⁵I₈, ⁵F₄→⁵I₈ and ⁵S₂, ⁵F₂→⁵I₇ transitions of Ho³⁺ ions, respectively. The optimum doping concentrations of Ho³⁺ and Yb³⁺ were determined to be 0.75% and 15%, and the corresponding Commission International de L'Eclairage (CIE) coordinates are calculated to be x=0.298 and y=0.692. The related UC mechanism of Ho³⁺/Yb³⁺ co-doped BaLa₂ZnO₅ depending on pump power was studied in detail. The results indicate that BaLa₂ZnO₅: Ho³⁺/Yb³⁺ can be an effective candidate for up-conversion yellowish-green light emitter.     

Structural and Upconversion Studies of Er3+ Codoped with CdS Nanoparticles in Sol-Gel Glasses

The Er³⁺ codoped with CdS nanoparticles in sol-gel glass with an average particle size of about 10 nm have been synthesized by sol-gel method. The green and red up-conversion emissions centered at about 534, 560 and 680 nm, corresponding to the ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺, respectively; were detected by a 800 nm excitation. The two-photon absorption process is involved in the green and red up-conversion emissions.     

Spectroscopic properties of Nd—doped phosphate glass with a high emission cross section

Neodymium doped phosphate glasses have been prepared by the semi-continuous melting technique. Their absorption and emission spectra have been recorded at room temperature. The Judd－Ofelt theory has been applied to evaluate the stimulated emission cross sections of ⁴F_3/2→⁴I_11/2 transition for Nd³⁺. The higher stimulated emission cross section, 4.0×10^-20cm², is obtained. The fluorescence decays of the ⁴F_3/2→⁴I_11/2 transition of Nd³⁺ are measured for the samples doped (0.7－10) wt% of Nd₂O₃ at room temperature. The concentration quenching of Nd-doped phosphate glass is mainly attributed to cross-relaxation and energy migration. The site-dependent properties of fluorescence spectra and the fluorescence lifetime of the Nd³⁺-doped phosphate glass (with 2.2wt%Nd₂O₃) are studied using laser-induced fluorescence line narrowing techniques, and the site-to-site variations of optical properties are observed at low temperature.     

Downconversion for Solar Cells in YF3:Pr3+, Yb3+

ABSTRACT

Energy losses in solar cells caused by the spectral mismatch can be reduced by adapting the solar spectrum using a downconversion material where one higher energy visible photon is ‘cut' into two lower energy near-infrared photons that both can be absorbed by the solar cell. Downconversion with the (Pr³⁺, Yb³⁺) couple in YF₃ is investigated. Based on analysis of luminescence and diffuse reflectance spectra it is evident that two-step energy transfer takes place from the ³P₀ level of Pr³⁺ (around 490 nm) exciting two Yb³⁺ to the ²F_5/2 level giving emission around 980 nm. The transfer efficiency increases with Yb³⁺ concentration and is 86% for YF₃ doped with 0.5% Pr³⁺ and 30% Yb³⁺. Due to concentration quenching the intensity of emission from Yb³⁺ is strongly reduced and the ²F_5/2 emission intensity reaches a maximum for the sample with 0.5% Pr³⁺ and 2–5% Yb³⁺ at 300 K. Temperature dependent measurements reveal the role of the Pr^{3+ 1}G₄ level in the energy transfer between Pr³⁺ and Yb³⁺. Back-transfer of excitation energy from the Yb^{3+ 2}F_5/2 level to the ¹G₄ level of Pr³⁺ occurs and quenches the Yb³⁺ emission. The quenching is shown to become more efficient between 4 and 50 K due to faster phonon-assisted energy transfer between the Yb³⁺ donors. Upon raising the temperature from 50 to 300 K, the luminescence life time of the Yb³⁺ emission increases again because the small energy difference between the Pr³⁺ (¹G₄) level and the Yb³⁺ (²F_5/2) level (～300 cm^?1) which makes the ¹G₄ less efficient as a trap for the excitation energy. The present results give insight into factors involved in the concentration quenching in downconversion materials based on the (Pr³⁺, Yb³⁺) couple.     

Upconversion luminescence in Tm3+/Yb3+co-doped lead tungstate tellurite glasses

This work reports the upconversion luminescence properties of Tm³⁺/Yb³⁺ ions in lead tungstate tellurite (LTT) glasses. Judd–Oflet intensity parameters have been obtained from the absorption band intensities of Tm³⁺ singly-doped and Tm³⁺/Yb³⁺ co-doped LTT glasses. The spontaneous emission probabilities, radiative lifetimes and branching ratios for ¹G₄ and ³H₄ emission levels of Tm³⁺ have been determined. Upconversion luminescence has been observed by exciting the samples at 980 nm (Yb³⁺:²F_7/2→²F_5/2) at room temperature. Four upconversion emission bands corresponding to the ¹G₄→³H₆ (477 nm), ¹G₄→³F₄ (651 nm), ¹G₄→³H₅ (702 nm) and ³H₄→³H₆ (810 nm) transitions have been identified. The relative variation in the intensities of upconversion bands, the different channels responsible for upconversion spectra and the effect of Yb³⁺ ions concentration on the upconversion luminescence of Tm³⁺ ions have also been discussed.