Transferring CdTe Nanoparticles from Liquid Phase to Polyvinylpyrrolidone Nanofibers by Electrospinning and Detecting Its Photoluminescence Property

The major aim of this work was to synthesize thio-stabilized CdTe nanoparticles(NPs) in an aqueous solution,which was then enwrapped with cetyltrimethylammonium bromide(CTAB),and finally transferred to the polyvinylpyrrolidone(PVP) matrix by electrospinning,The PVP nanofibers containing CdTe NPs were characterized by scanning electron microscopy(SEM) and transmission electron microscopy(TEM),to observe the morphology of the nanofibers and the distribution of CdTe NPs,The selective area electronic diffraction(SAED) pattern verified that CdTe NPs were cubic lattice,The photoluminescence(PL) spectrum indicated that CdTe NPs existed in an optical style in PVP nanofibers,Moreover,X-ray photoelectron spectra(XPS) revealed that thiol-stabilized CdTe NPs were enwrapped by CTAB,and PVP acted as a dispersant in the process of electrospinning.     

SnO2/TiO2复合纳米纤维的制备及光催化性能

采用静电纺丝技术,以聚乙烯吡咯烷酮和钛酸正丁酯为前驱体,制得锐钛矿相TiO2纳米纤维。以TiO2纳米纤维为模板,通过水热合成法,制备了具有异质结构的SnO2/TiO2复合纳米纤维。利用扫描电镜(SEM)、X射线能量色散光谱（EDS）、透射电镜(TEM)和X射线衍射(XRD)等分析测试手段对其形貌和结构进行了表征,结果表明,SnO2纳米粒子均匀地生长在TiO2纳米纤维表面,形成了异质结构的SnO2/TiO2复合纳米纤维材料。通过改变反应物浓度,能有效地实现SnO2/TiO2复合纳米纤维的可控合成。以罗丹明B为模拟污染物,考察了SnO2/TiO2复合纳米纤维的光催化性能,与纯TiO2纳米纤维相比光催化活性明显提高,初步探讨了光催化反应机理。     

聚乙烯吡咯烷酮/四氧化三铁复合纳米纤维的制备与表征

采用静电纺丝方法制备了聚乙烯吡咯烷酮/四氧化三铁复合纳米纤维, 并用透射电子显微镜(TEM)、X射线衍射(XRD)、热失重分析(TGA)和振动磁力分析进行了表征, 探讨了复合物的结构及其性能.     

纳米碳纤维固载TiO_2

采用聚乙烯吡咯烷酮(PVP)溶胶通过静电纺丝法制备了PVP纳米纤维。将PVP纳米纤维直接固载在碳棒上,在250℃预氧化,850℃炭化,得到碳纳米纤维。将碳纤维渍取钛酸丁酯,200℃下热处理后在550℃空气中焙烧,制得负载型纳米TiO2。利用扫描电子显微镜、红外吸收光谱、X射线衍射等测试技术对纳米纤维进行了表征。并把负载型TiO2分散在亚甲基蓝溶液中,分析了TiO2固载纳米碳纤维的光催化活性。结果表明,在100mL20mg/L亚甲基蓝溶液中加入1.0mgTiO2固载碳纳米纤维,光催化降解40min后,亚甲基蓝的分解率接近75%。     

Ag nanoparticle-embedded one-dimensional β-CD/PVP composite nanofibers prepared via electrospinning for use in antibacterial material

Ag nanoparticle-embedded one-dimensional β-CD (β-cyclodextrin)/PVP composite nanofibers were prepared using a one-step electrospinning technique. Ag nanoparticles were obtained in the AgNO₃/β-CD/DMF solution, in which silver nitrate been introduced as the precursor, DMF as solvent, β-CD as reducing and capping agent. After electrospinning of the composite solution at room temperature, the β-CD/PVP nanofibers containing Ag nanoparticles were obtained. The electrospun composite solution containning Ag nsnopsrticles were confirmed by UV-visible absorption spectra; the resulting composite nanofibers were characterized by scanning electron microscopy , transmission electron microscopy, and X-ray diffraction. Ag-β-CD/PVP nanofiber exhibits good antibacterial property for Escherichia coli and Staphylococcus aureus. Consequently, we propose that these Ag nanoparticle-embedded 1D-nanostructures prepared via electrospinning may be used as antibacterial material.     

电纺丝-气相沉积法制备碳包覆TiO_2纳米纤维及其光催化行为的研究

以聚乙烯吡咯烷酮(PVP)溶胶/钛酸正丁酯为前躯体,以静电纺丝法制备了PVP/Ti(OC4H9)4纤维。550℃下,空气氛中焙烧双组分纤维,得到直径60～300nm的TiO2纳米纤维。继而以气相沉积法制得碳包覆TiO2纳米纤维。用红外吸收光谱(FTIR)、X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等对纳米纤维进行了表征。与TiO2纳米纤维、TiO2纳米粉体相比,气相沉积法制备的碳包覆TiO2纳米纤维在光分解亚甲基蓝上表现出更好的催化性能。     

同轴静电纺丝法在纳米中空Ti02纤维中填充Ag的应用

以聚乙烯吡咯烷酮(PVP)溶胶,钛酸四正丁酯和PVP溶胶,银颗粒为前驱体,以共轴静电纺丝法制备了银填充的TiO2中空纳米纤维.将双组分纤维在200℃下热处理去除乙醇与表面吸附水后,继而在空气气氛中焙烧至600℃.可以得到在内表面上沉积银颗粒的TiO2纳米管,银颗粒的直径为5-40 nm,TiO2纳米管的外径150-300 nm.管臂厚10-20 nm.用红外吸收光谱(IR)、X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等测试手段对超细纤维进行了表征.中空纤维的直径和管壁可以通过改变电纺参数来调节.与Ag-TiO2纳米纤维、TiO2纳米中空纤维、TiO2纳米纤维及TiO2纳米粉体相比较,Ag颗粒填充的TiO2纳米中空纤维在光分解亚甲基蓝上表现出了更好的光催化性能.     

The controllable preparation of electrospun carbon fibers supported Pd nanoparticles catalyst and its application in Suzuki and Heck reactions

The palladium nanoparticles/carbon nanofibers(Pd NPs/CNFs) catalyst was prepared by the electrospinning method, the hydrazine hydrate solution reduction in an ice bath environment, the high temperature carbonization. The catalyst was characterized by X-ray diffraction(XRD), fieldemission scanning electron microscope(FE-SEM), and transmission electron microscopy(TEM). The nanofibers are not cross-linked and arranged in order. The surface of Pd NPs/CNFs is smooth, and it can be observed that a large number of particles were loaded and well-dispersed in carbon fiber matrix, and the particle distribution is uniform. The activity center of catalyst is Pd(0). The Pd NPs/CNFs exhibited a high efficiency, good reusability and stability in the Suzuki and Heck reactions. It can be used for at least five consecutive runs without significant loss of its catalytic activity. The good recyclability of Pd NPs/CNFs provides a way to greatly reduce the cost of the catalyst.     

同轴静电纺丝法在纳米中空TiO2纤维中填充Ag的应用

以聚乙烯吡咯烷酮(PVP)溶胶/钛酸四正丁酯和PVP溶胶/银颗粒为前驱体, 以共轴静电纺丝法制备了银填充的TiO2中空纳米纤维. 将双组分纤维在200 ℃下热处理去除乙醇与表面吸附水后, 继而在空气气氛中焙烧至600 ℃, 可以得到在内表面上沉积银颗粒的TiO2纳米管, 银颗粒的直径为5-40 nm, TiO2纳米管的外径150-300 nm, 管臂厚10-20 nm. 用红外吸收光谱(IR)、X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)等测试手段对超细纤维进行了表征. 中空纤维的直径和管壁可以通过改变电纺参数来调节. 与Ag-TiO2纳米纤维、TiO2纳米中空纤维、TiO2纳米纤维及TiO2纳米粉体相比较, Ag颗粒填充的TiO2纳米中空纤维在光分解亚甲基蓝上表现出了更好的光催化性能.     

晶相可控的ZrO2纳米线的无卤制备及表征

采用无卤法制备晶相可控的ZrO₂纳米线. 通过静电纺丝法制备聚乙烯吡咯烷酮(PVP)与Zr(NO₃)₄的复合纤维; 再通过煅烧法在除去聚合物模板的同时制备ZrO₂纳米线. 采用X射线衍射(XRD)、 扫描电子显微镜(SEM)、 透射电子显微镜(TEM)、 傅里叶变换红外光谱(FTIR)仪及热重差热联用热分析仪(DSC-TGA)对材料的晶相结构、 形貌及热稳定性进行表征. 通过改变煅烧温度, 可以实现ZrO₂纳米材料形貌及晶相组成的调控.     

Highly Porous Amidoximed Carbon Nanofibers Supported Palladium(0) Nanoparticle Catalyzed Heck Reaction

Highly porous amidoximed carbon nanofibers(AOCNFs), which were fabricated via a conventional electrospinning technique followed by chemically modification, impregnation-reduction and carbonization process, had been used for the immobilization of palladium nanoparticles(Pd NPs) catalyst. During the carbonization process, polystyrene(PS) was selectively decomposed from bicomponent fibers, generating porous fibers. Fourier transform infrared spectroscopy(FTIR) result revealed the functional groups on PAN-PS fibers(PAN=polyacrylonitrile), AOPAN-PS fibers and AOCNFs; scanning electron microscopy(SEM) was used to observe the morphology of all stages of nanofibers; transmission electron microscopy(TEM) result gave the structure of through-hole morphology clearly visible and the dispersion of Pd NPs on the surface of nanofibers; and X-ray photoelectron spectra(XPS) confirmed that Pd nanoparticles on the surface of AOCNFs was of the metallic state. Moreover, the as-prepared catalyst exhibited high catalytic activity and efficient recycle for Heck coupling reactions between iodobenzene and acrylates.     

Preparation and characterization of porous TiO_2/ZnO composite nanofibers via electrospinning

<正>Porous TiO_2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO_2/ZnCl_2/PVP[PVP:polyvinyl pyrrolidone)]nanofibers,which were electrospun from a mixture solution of TiO_2,ZnCl_2 and PVP.Transmission electron microscopy(TEM) and X-ray diffraction(XRD) analyses were used to identify the morphology of the TiO_2/ZnO nanofibers and a formation of inorganic TiO_2/ZnO fibers.The porous structure of the TiO_2/ZnO fibers was characterized by N_2 adsoption/desorption isotherm.Surface photovoltage spectroscopy(SPS) and photocatalytic activity measurements revealed advance properties of the porous TiO_2/ZnO composite nanofibers and the results were compared with pure TiO_2 nanofibers,pure ZnO nanofibers and TiO_2/ZnO nanoparticles.     

Synthesis of Poly（N-vinylpyrrolidone） Nanofibers Containing Gold Nanoparticles via Electrospinning Technique

Poly(N-vinylpyrrolidone)(PVP)nanofibers containing gold nanoparticles were prepared by electrospinning method.This simple route was used to prepare composites on a large scale,and the syntheses are simple.The optical property of gold nanoparticles in PVP aqueous solution was investigated by UV-Visible absorption spectra.The morphology of the fibers and the distribution of particles were characterized by transmission electron microscopy.The structure of the composite was characterized by Fourier transform infrared spectroscopy.     

速溶电纺载药PVP纳米纤维膜制备与表征

采用电纺工艺制备载豆腐果苷聚乙烯基吡咯烷酮纳米纤维膜.通过偏光显微镜确定电纺条件,利用扫描电镜对纤维膜表面形态进行观察;采用X-射线晶体衍射(XRD)和差示扫描量热分析(DSC)检测纤维膜中药物的存在状态,通过红外光谱分析药物与纤维基材之间的相互作用.结果表明载药纤维直径分布均匀(400~600 nm)、表面光滑无药物颗粒,药物与聚合物之间通过氢键作用、具有良好的相容性,XRD和DSC结果表明药物以无定形态高度分散于纳米纤维中,纤维膜中药物以"聚合物控释"机制在13.7 s左右完全溶解.     

Electrospun nanofibers of poly（vinyl pyrrolidone）/Eu^3＋ and its photoluminescence properties

Nanofibers of poly（vinyl pyrrolidone） （PVP）/Eu^3＋ with diameters of 300-900 nm were prepared by using sol-gel processing and electrospinning technique. The products were characterized by scanning electron microscope （SEM）, Fourier transform infrared spectroscopy （FT-IR）, and photoluminescence （PL）. The results indicated that, Eu^3＋ was successfully embedded in the onedimensional hybrid nanofibers, and the PVP/Eu^3＋ hybrid nanofibers had favorable photoluminescence properties.     

Aligned polymer fibers produced via an additive electric field

Electrospinning is known to be a highly versatile method to produce nanofibers, and several techniques have been developed to align nanofibers. In this paper, poly(vinyl alcohol) (PVA), poly(vinylpyrrolidone) (PVP), poly(propylene carbonate) (PC), poly(ethylene oxide) (PEO), PVA/Chitosan and PVA/Fe₃O₄ uniaxially aligned ultrafine fibers were obtained with electrospinning method by adding another electric field in the collection area. Alignment of the nanofibers was characterized by the use of digital cameras and field emission scanning electron microscopy, polarized Fourier transform infrared spectroscopy (FTIR), and wideangle X-ray diffraction (XRD). The mechanism of fiber alignment was investigated as well.     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

静电纺丝法制备铁酸锌中空纤维及其磁学性能

以锌盐、铁盐和聚乙烯吡咯烷酮(PVP)为原料,通过静电纺丝法先制备PVP/硝酸盐复合纤维,这些复合纤维以5℃·min-1的升温速率加热到500℃并保温3h,最终得到铁酸锌(ZnFe2O4)中空纤维.通过X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)以及振动样品磁强计(VSM)等分析手段对中空纤维的晶体结构、形貌和磁学性能进行了研究.结果显示,ZnFe2O4中空纤维属于尖晶石结构,高温处理后仍能保持一维结构,纤维直径在200-400nm之间,纤维壁由大小为25nm的颗粒堆积而成.室温磁化结果显示制备的ZnFe2O4中空纤维具有超顺磁性,在10kOe的磁化强度为2.03emu·g-1.     

单晶MoO3纳米片：静电纺丝法制备及光催化活性

以聚乙烯基吡咯烷酮(PVP)和钼酸铵((NH4)6Mo7O24.4H2O)为原料,利用静电纺丝技术结合溶胶过程制备了PVP/(NH4)6Mo7O24.4H2O前躯体,对前躯体缓慢控温处理制备MoO3纳米材料。通过X-射线光电子能谱(XPS)﹑红外光谱(FTIR)﹑X射线粉末衍射(XRD)和场发射扫描电子显微镜(FE-SEM)等表征手段研究了热处理温度对MoO3晶体生长和结构的影响。以亚甲基蓝(MB)的光降解为模型反应,研究了MoO3微纳米材料的光催化性能。结果表明,热处理温度500℃时生成的MoO3纳米片光催化活性最好,并探讨了其光催化机理。     

Silver Nanoparticles Filling in TiO2 Hollow Nanofibers by Coaxial Electrospinning

This study investigated the coaxial electrospinning process of silver filling in TiO₂ ultrafine hollow fibers using polyvinyl pyrrolidone (PVP) sol/titanium n-butyloxide (Ti(OC₄H₉)₄) and PVP sol/silver nanoparticles as pore-directing agents. The bicomponent fibers were heat treated at 200 °C and calcined at 600 °C. Silver particles having diameters of 5 to 40 nm were deposited on the inner surface of the long hollow TiO₂ nanofibers (outer diameter of 150.300 nm) with mesoporous walls (thickness of 10.20 nm). The morphological structure of the filled ultrafine hollow fibers has been studied by means of infrared (IR) spectrum, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The diameters and wall thicknesses of the hollow fibers could be tuned by adjusting the electrospinning parameters. Compared with other nanostructured TiO₂ materials, such as mesoporous Ag-TiO₂ blending fibers, TiO₂ hollow nanofibers, TiO₂ nanofibers, and TiO₂ powders, the silver filled TiO₂ hollow fibers exhibited a higher photocatalytic activity toward the degradation of methylene blue.