Preparation and photocatalytic activity of ZnO/TiO2/SnO2 mixture

ZnO/TiO₂/SnO₂ mixture was prepared by mixing its component solid oxides ZnO, TiO₂ and SnO₂ in the molar ratio of 4?1?1, followed by calcining the solid mixture at 200-1300 °C. The products and solid-state reaction process during the calcinations were characterized with powder X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG-DTA), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS) and Brunauer-Emmett-Teller measurement of specific surface area. Neither solid-state reaction nor change of crystal phase composition took place among the ZnO, TiO₂ and SnO₂ powders on the calcinations up to 600 °C. However, formation of the inverse spinel Zn₂TiO₄ and Zn₂SnO₄ was detected at 700-900 and 1100-1200 °C, respectively. Further increase of the calcination temperature enabled the mixture to form a single-phase solid solution Zn₂Ti_0.5Sn_0.5O₄ with an inverse spinel structure in the space group of . The ZnO/TiO₂/SnO₂ mixture was photocatalytically active for the degradation of methyl orange in water; its photocatalytic mass activity was 16.4 times that of SnO₂, 2.0 times that of TiO₂, and 0.92 times that of ZnO after calcination at 500 °C for 2 h. But, the mass activity of the mixture decreased with increasing the calcination temperature at above 700 °C because of the formation of the photoinactive Zn₂TiO₄, Zn₂SnO₄ and Zn₂Ti_0.5Sn_0.5O₄. The sample became completely inert for the photocatalysis after prolonged calcination at 1300 °C (42 h), since all of the active component oxides were reacted to form the solid solution Zn₂Ti_0.5Sn_0.5O₄ with no photocatalytic activity.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Structural models for intergrowth structures in the phase system Al2O3-TiO2

The phase system Al₂O₃-TiO₂ was investigated in the compositional range from 48:52 to 62:38 mol% Al₂O₃:TiO₂. The samples were prepared by melting the binary oxides in an arc-imaging furnace and the obtained samples were examined by powder X-ray diffraction. The recorded powder patterns could be interpreted in terms of intergrowth structures consisting of two basic building blocks, which were deduced from the known crystal structures of β-Al₂TiO₅ and Al₆Ti₂O₁₃. The structure of a new ordered compound with the formula Al₁₆Ti₅O₃₄ is proposed. The thermal stability was estimated from DTA and tempering experiments and showed that all prepared samples decompose at temperatures around 800 °C into the binary oxides corundum and titania.     

Syntheses of TiO2(B) nanowires and TiO2 anatase nanowires by hydrothermal and post-heat treatments

TiO₂(B) nanowires and TiO₂ anatase nanowires were synthesized by the hydrothermal processing in 10 M NaOH aq. at 150 °C followed by the post-heat treatment at 300-800 °C. As-synthesized Na-free titanate nanowires (prepared by the hydrothermal treatment and repeated ion exchanging by HCl (aq.) were transformed into TiO₂(B) structure with maintaining 1-D morphology at 300-500 °C, and further transformed into anatase structure at 600-800 °C with keeping 1-D shape. At 900 °C, they transformed into rod-shaped rutile grains. Microstructure of these 1-D TiO₂ nanomaterials is reported.     

Bi2Ti2O7/TiO2复合纤维：原位水热合成及光催化性能

采用静电纺丝技术制备的TiO2纤维作为模板和反应物,通过原位水热合成了具有异质结构的Bi2Ti2O7/TiO2复合纤维。利用X射线衍射(XRD)、扫描电镜(SEM)、能量散射光谱(EDS)、高分辨透射电镜(HRTEM)和紫外可见吸收光谱(UV-Vis)等分析测试手段对样品的结构和形貌进行表征。以罗丹明B为模拟有机污染物进行光催化降解实验。结果表明:花状Bi2Ti2O7纳米结构均匀地生长在TiO2纤维上,制备了Bi2Ti2O7与TiO2相复合的光催化材料,其光谱响应范围拓宽至可见光区,与纯TiO2纤维相比可见光催化活性显著提高,且易于分离、回收和循环使用。初步探讨了Bi2Ti2O7/TiO2异质结的生长机制和光催化活性提高机理。     

A new structure type of phosphate: Crystal structure of Na2Zn5(PO4)4

A new compound, Na₂Zn₅(PO₄)₄, was identified in the system ZnONa₂OP₂O₅ and high-quality crystal was obtained by the melt method. The crystal structure of this compound was solved by direct method from single crystal X-ray diffraction data. The structure was then refined anisotropically using a full-matrix least square refinement on F² and the refinement converged to R₁=0.0233 and wR₂=0.0544. This compound crystallizes in the orthorhombic system with space group Pbcn, lattice parameters a=10.381(2) Å, b=8.507(1) Å, c=16.568(3) Å and Z=4. The structure is made up of 3D [Zn₅P₄O₁₆]_n²ⁿ⁻ covalent framework consisting of [Zn₄P₄O₁₆]_n⁴ⁿ⁻ layers. The powder diffraction pattern of Na₉Zn₂₁(PO₄)₁₇ is explained by simulating a theoretical pattern with NaZnPO₄ and Na₂Zn₅(PO₄)₄ in the molar ratio of 1:4 and then by Rietveld refinement of experimental pattern. Na₂Zn₅(PO₄)₄ melts congruently at 855 °C and its conductivity is 5.63×10⁻⁹ S/cm.     

Effect of surface fluorination and conductive additives on the electrochemical behavior of lithium titanate (Li4/3Ti5/3O4) for lithium ion battery

Effect of surface fluorination and conductive additives on the charge/discharge behavior of lithium titanate (Li_4/3Ti_5/3O₄) has been investigated using F₂ gas and vapor grown carbon fiber (VGCF). Surface fluorination of Li_4/3Ti_5/3O₄ was made using F₂ gas (3 × 10⁴ Pa) at 25-150 °C for 2 min. Charge capacities of Li_4/3Ti_5/3O₄ samples fluorinated at 70 °C and 100 °C were larger than those for original sample at high current densities of 300 and 600 mA/g. Optimum fluorination temperatures of Li_4/3Ti_5/3O₄ were 70 °C and 100 °C. Fibrous VGCF with a large surface area (17.7 m²/g) increased the utilization of available capacity of Li_4/3Ti_5/3O₄ probably because it provided the better electrical contact than acetylene black (AB) between Li_4/3Ti_5/3O₄ particles and nickel current collector.     

A novel microwave dielectric ceramic Ca2Zn4Ti16O38: Preparation and dielectric properties

A novel microwave dielectric powder with composition of Ca₂Zn₄Ti₁₆O₃₈ was synthesized through a citrate sol-gel process. The development of crystalline phases with heat-treating temperature for the gel derived powders was evaluated by using thermo-gravimetric analysis and X-ray powder diffraction analysis techniques. The pure phase of Ca₂Zn₄Ti₁₆O₃₈ with crichtonite crystal structure was obtained at relatively low temperature of 1000 °C. The synthesized powder has high reactivity and the dense ceramics with single crystalline phase were obtained at low sintering temperature of 1100 °C. Impedance spectroscopy and microwave dielectric measurements on sintered samples showed the present compound to be a modest dielectric insulator with excellent dielectric properties of ε_r∼47-49, Qf value ∼27,800-31,600 GHz and τ_f∼+45 to +50 ppm/°C. It shows comparable microwave dielectric properties to other moderate-permittivity microwave dielectrics, but much lower sintering temperature of 1100 °C.     

稀碱溶液中水热法制备柔性TiO2纳米须薄膜的生长机制及表征

以柔性不锈钢基底上经磁控溅射沉积的钛膜为钛源, 在1 mol·L^-1的低浓度NaOH溶液中水热法制备了朝基底上方取向生长的大长径比柔性TiO₂纳米须薄膜, 考察了钛膜沉积条件对纳米须薄膜的影响, 系统研究了水热反应条件对薄膜生长过程的影响及TiO₂纳米须薄膜的形成机制. 通过场发射扫描电镜(FESEM)、X射线能谱仪(EDS)、高分辨透射电子显微镜(HRTEM)、X射线衍射仪(XRD)等对样品进行了表征. 结果表明, 与室温沉积的钛膜相比, 600 ℃下沉积的钛膜水热后得到的纳米线薄膜与基底的附着力更好. 所得TiO₂纳米须为单晶锐钛矿, 经由Na₂Ti₂O₄(OH)₂、H₂Ti₂O₅·H₂O转变而来. 纳米须形成于水热阶段, 平行于Na₂Ti₂O₄(OH)₂的(100)晶面择优取向生长, 纳米须经历了纳米片→纳米线束→纳米线的裂解生长过程. 朝基底上方取向生长的纳米须薄膜的形成是低浓度NaOH溶液与较高水热温度(220 ℃)协同作用的结果. 进一步在Na₂SO₄溶液中研究了薄膜电极的光电化学性能, 结果表明, TiO₂纳米须薄膜的光电性能明显优于零维纳米颗粒薄膜和二维纳米片薄膜, 显示了良好的应用前景.     

Dependence of nitrogen doping on TiO2 precursor annealed under NH3 flow

N-doped TiO₂ photocatalysts were prepared by annealing two different precursors, P25 and a TiO₂ xerogel powder under NH₃/Ar flow at 500, 550, and 600 °C. The xerogel powder prepared by peptizing Ti(OH)₄ with HNO₃ was composed of nanoparticles and had large specific surface area. During the annealing process, the xerogel powder underwent increase in crystallinity, grain growth and phase transformation, whereas P25 did not show obvious changes. Compared with the N-doped TiO₂ photocatalysts from P25, the N-doped TiO₂ photocatalysts from the xerogel powder possessed higher concentrations of the substitutional nitrogen and exhibited more obvious absorption in the visible light region. The N-doped TiO₂ photocatalysts from the xerogel powder exhibited obvious visible-light activities for photodegrading methylene blue and the sample prepared at 500 °C achieved the best performance with a rate constant (k) about 0.44 h⁻¹, whereas those from P25 did not exhibit improved visible-light activities.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

Synthesis and characterization of sodium titanates Na2Ti3O7 and Na2Ti6O13

Na₂Ti₃O₇ and Na₂Ti₆O₁₃ were synthesized by sol-gel method in order to obtain pure phases. Different heat-treatments were applied on powders and pellets of these materials. The effects were studied by XRD, dilatometry, TGA-DTA, SEM and electrochemical impedance spectroscopy. Pure Na₂Ti₃O₇ was obtained at 973 K. Sintering at 1373 K caused a partial decomposition into Na₂Ti₆O₁₃. The Na₂Ti₃O₇ powder sintered at 1273 K showed polygonal microstructure. Na₂Ti₃O₇ pellets sintered at 1323 K for 10 h exhibited large structures. This latter microstructure decreased the electrical conductivity of Na₂Ti₃O₇. Pure Na₂Ti₆O₁₃ was obtained at 873 K. Sintering at 1073 K caused a partial decomposition into TiO₂ (rutile). Na₂Ti₆O₁₃ pellets sintered at 1323 K for 10 h exhibited common shrinkage behavior. This shrinkage process increased the electrical conductivity of this material. The presence of TiO₂ resulted in a oxygen partial pressure dependence of the electrical conductivity.     

Selective hydrothermal synthesis of BiOBr microflowers and Bi2O3 shuttles with concave surfaces

Through controlling the amount of NaOH added, BiOBr and Bi₂O₃ with different shapes were hydrothermally synthesized in the reaction system of Bi(NO₃)₃-hexadecyl trimethyl ammonium bromide (CTAB)-NaOH. As 8 mmol of NaOH was added, BiOBr microflowers constructed of nanoflakes were synthesized. The thickness of these single-crystal nanoflakes was about 20 nm. In the similar condition, when the amount of NaOH added was 28 mmol, Bi₂O₃ shuttles with concave surfaces were obtained. The length of these shuttles was 100 μm and the diameter at the middle of these shuttles was 50 μm. The photocatalytic activity of as-prepared BiOBr microflowers was evaluated by the degradation of methyl orange (MO) under visible-light irradiation (λ>420 nm), which was up to 96% within 90 min.     

Synthesis and nonlinear optical properties of BaTi(BO3)2 and Ba3Ti3O6(BO3)2 crystals in glasses with high TiO2 contents

The ternary BaO-TiO₂-B₂O₃ glasses containing a large amount of TiO₂ (20-40 mol%) are prepared, and their optical basicities (Λ), the formation, structural features and second-order optical nonlinearities of BaTi(BO₃)₂ and Ba₃Ti₃O₆(BO₃)₂ crystals are examined to develop new nonlinear optical materials. It is found that the glasses with high TiO₂ contents of 30-40 mol% show large optical basicities of Λ=0.81-0.87, suggesting the high polarizabity of TiO_n polyhedra (n=4-6) in the glasses. BaTi(BO₃)₂ and Ba₃Ti₃O₆(BO₃)₂ crystals are found to be formed as main crystalline phases in the glasses. It is found that BaTi(BO₃)₂ crystals tend to orient at the surface of crystallized glasses. The new XRD pattern for the Ba₃Ti₃O₆(BO₃)₂ phase is proposed through Rietvelt analysis. The second harmonic intensities of crystallized glasses were found to be 0.8 times as large as α-quartz powders, i.e., I^2ω(sample)/I^2ω(α-quartz)=0.8, for the sample with BaTi(BO₃)₂ crystals and to be I^2ω(sample)/I^2ω(α-quartz)=68 for the sample with Ba₃Ti₃O₆(BO₃)₂ crystals. The Raman scattering spectra for these two crystalline phases are measured for the first time and their structural features are discussed.     

Synthesis, structure and magnetic properties of new phosphates K2Mn0.5Ti1.5(PO4)3 and K2Co0.5Ti1.5(PO4)3 with the langbeinite structure

New complex phosphates of the general formula K₂M_0.5Ti_1.5(PO₄)₃ (M=Mn, Co) have been obtained from the melting mixture of KPO₃, K₄P₂O₇, TiO₂ and CoCO₃·mCo(OH)₂ or Mn(H₂PO₄)₂ by means of a flux technique. The synthesized phosphates have been characterized by the single-crystal X-ray diffraction and the FTIR-spectroscopy. The compounds crystallize in the cubic system with the space group P2₁3 and cell parameters a=9.9030(14) Å for K₂Mn_0.5Ti_1.5(PO₄)₃ and a=9.8445(12) Å for K₂Co_0.5Ti_1.5(PO₄)₃. Both phosphates are isostructural with the langbeinite mineral and contain four formula unit K₂M_0.5Ti_1.5(PO₄)₃ per unit cell. The structure can be described using [M₂(PO₄)₃] framework composed of two [MO₆] octahedra interlinked via three [PO₄] tetrahedra. The Curie-Weiss-type behavior is observed in the magnetic susceptibility.     

Raman scattering investigations on lanthanum-doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

The ferroelectric ceramics of Bi₄Ti₃O₁₂, SrBi₄Ti₄O₁₅, and lanthanum-doped Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅ were synthesized, and their Raman spectra were investigated. La-doping resulted in the enlargement of remnant polarization of Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The structure of the Bi₂O₂ layers and TiO₆ octahedra of the intergrowth was found to be different from those of Bi₄Ti₃O₁₂ and SrBi₄Ti₄O₁₅. La³⁺ ions exhibit pronounced selectivity for the occupation of A site as La content is lower than 0.50, and tend to be incorporated into Bi₂O₂ layers when the La content is higher than 0.50. Lanthanum substitution brings about the structural phase transition in Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The variation of ferroelectric property may be attributed to combined contribution from the decreasing of the oxygen vacancies, the relaxation of the lattice distortion, the destroying of the insulation and the space charge compensation effects of the Bi₂O₂ slabs.     

The study of Bi3B5O12: synthesis, crystal structure and thermal expansion of oxoborate Bi3B5O12

The paper presents a new data on the crystal structure, thermal expansion and IR spectra of Bi₃B₅O₁₂. The Bi₃B₅O₁₂ single crystals were grown from the melt of the same stoichiometry by Czochralski technique. The crystal structure of Bi₃B₅O₁₂ was refined in anisotropic approximation using single-crystal X-ray diffraction data. It is orthorhombic, Pnma, a=6.530(4), b=7.726(5), c=18.578(5) Å, V=937.2(5) Å³, Z=4, R=3.45%. Bi³⁺ atoms have irregular coordination polyhedra, Bi(1)O₆ (d(B-O)=2.09-2.75 Å) and Bi(2)O₇ (d(B-O)=2.108-2.804 Å). Taking into account the shortest bonds only, these polyhedra are considered here as trigonal Bi(1)O₃ (2.09-2.20 Å) and tetragonal Bi(2)O₄ (2.108-2.331 Å) irregular pyramids with Bi atoms in the tops of both pyramids. The BiO₄ polyhedra form zigzag chains along b-axis. These chains alternate with isolated anions [B₂^IVB₃^IIIO₁₁]⁷⁻ through the common oxygen atoms to form thick layers extended in ab plane. A perfect cleavage of the compound corresponds to these layers and an imperfect one is parallel to the Bi-O chains. The Bi₃B₅O₁₂ thermal expansion is sharply anisotropic (α₁₁≈α₂₂=12, α₃₃=3×10⁻⁶ °C⁻¹) likely due to a straightening of the flexible zigzag chains along b-axis and decreasing of their zigzag along c-axis. Thus the properties like cleavage and thermal expansion correlate to these chains.     

Thermochemistry of NaRb[B4O5(OH)4]·4H2O

The enthalpies of solution of NaRb[B₄O₅(OH)₄]·4H₂O in approximately 1 mol dm⁻³ aqueous hydrochloric acid and of RbCl in aqueous (hydrochloric acid + boric acid + sodium chloride) were determined. From these results and the enthalpy of solution of H₃BO₃ in approximately 1 mol dm⁻³ HCl(aq) and of sodium chloride in aqueous (hydrochloric acid + boric acid), the standard molar enthalpy of formation of −(5128.02 ± 1.94) kJ mol⁻¹ for NaRb[B₄O₅(OH)₄]·4H₂O was obtained from the standard molar enthalpies of formation of NaCl(s), RbCl(s), H₃BO₃(s) and H₂O(l). The standard molar entropy of formation of NaRb[B₄O₅(OH)₄]·4H₂O was calculated from the Gibbs free energy of formation of NaRb[B₄O₅(OH)₄]·4H₂O computed from a group contribution method.     

Hydrothermal synthesis, characterization and thermochemistry of Ca2[B2O4(OH)2]·0.5H2O

A pure calcium borate Ca₂[B₂O₄(OH)₂]·0.5H₂O has been synthesized under hydrothermal condition and characterized by XRD, FT-IR and TG as well as by chemical analysis. The molar enthalpy of solution of Ca₂[B₂O₄(OH)₂]·0.5H₂O in HC1·54.582H₂O was determined. From a combination of this result with measured enthalpies of solution of H₃BO₃ in HC1·54.561H₂O and of CaO in (HCl + H₃BO₃) solution, together with the standard molar enthalpies of formation of CaO(s), H₃BO₃(s) and H₂O(l), the standard molar enthalpy of formation of −(3172.5 ± 2.5) kJ mol⁻¹ of Ca₂[B₂O₄(OH)₂]·0.5H₂O was obtained.     

Hydrothermal preparation and visible-light photocatalytic activity of Bi2WO6 powders

Bi₂WO₆ powder photocatalyst was prepared using Bi(NO₃)₃ and Na₂WO₄ as raw materials by a simple hydrothermal method at 150 °C for 24 h, and then calcined at 300, 400, 500, 600 and 700 °C for 2 h, respectively. The as-prepared samples were characterized with UV-visible diffuse reflectance spectra, fourier transform infrared spectra (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and N₂ adsorption-desorption measurement. The photocatalytic activity of the samples was evaluated using the photocatalytic oxidation of formaldehyde at room temperature under visible light irradiation. It was found that post-treatment temperature obviously influenced the visible-light photocatalytic activity and physical properties of Bi₂WO₆ powders. At 500 °C, Bi₂WO₆ powder photocatalyst showed the highest visible-light photocatalytic activity due to the samples with good crystallization and high BET surface area.