Ultramicroporous Building Units as a Path to Bi‐microporous Metal–Organic Frameworks with High Acetylene Storage and Separation Performance

A strategy called ultramicroporous building unit (UBU) is introduced. It allows the creation of hierarchical bi‐porous features that work in tandem to enhance gas uptake capacity and separation. Smaller pores from UBUs promote selectivity, while larger inter‐UBU packing pores increase uptake capacity. The effectiveness of this UBU strategy is shown with a cobalt MOF (denoted SNNU‐45) in which octahedral cages with 4.5 Å pore size serve as UBUs. The C₂H₂ uptake capacity at 1 atm reaches 193.0 cm³ g^?1 (8.6 mmol g^?1) at 273 K and 134.0 cm³ g^?1 (6.0 mmol g^?1) at 298 K. Such high uptake capacity is accompanied by a high C₂H₂/CO₂ selectivity of up to 8.5 at 298 K. Dynamic breakthrough studies at room temperature and 1 atm show a C₂H₂/CO₂ breakthrough time up to 79 min g^?1, among top‐performing MOFs. Grand canonical Monte Carlo simulations agree that ultrahigh C₂H₂/CO₂ selectivity is mainly from UBU ultramicropores, while packing pores promote C₂H₂ uptake capacity.     

Efficient Visible‐Light‐Driven Carbon Dioxide Reduction by a Single‐Atom Implanted Metal–Organic Framework

Modular optimization of metal–organic frameworks (MOFs) was realized by incorporation of coordinatively unsaturated single atoms in a MOF matrix. The newly developed MOF can selectively capture and photoreduce CO₂ with high efficiency under visible‐light irradiation. Mechanistic investigation reveals that the presence of single Co atoms in the MOF can greatly boost the electron–hole separation efficiency in porphyrin units. Directional migration of photogenerated excitons from porphyrin to catalytic Co centers was witnessed, thereby achieving supply of long‐lived electrons for the reduction of CO₂ molecules adsorbed on Co centers. As a direct result, porphyrin MOF comprising atomically dispersed catalytic centers exhibits significantly enhanced photocatalytic conversion of CO₂, which is equivalent to a 3.13‐fold improvement in CO evolution rate (200.6 μmol g^?1 h^?1) and a 5.93‐fold enhancement in CH₄ generation rate (36.67 μmol g^?1 h^?1) compared to the parent MOF.     

Adenine Components in Biomimetic Metal–Organic Frameworks for Efficient CO2 Photoconversion

Visible‐light driven photoconversion of CO₂ into energy carriers is highly important to the natural carbon balance and sustainable development. Demonstrated here is the adenine‐dependent CO₂ photoreduction performance in green biomimetic metal–organic frameworks. Photocatalytic results indicate that AD‐MOF‐2 exhibited a very high HCOOH production rate of 443.2 μmol g^?1 h^?1 in pure aqueous solution, and is more than two times higher than that of AD‐MOF‐1 (179.0 μmol g^?1h^?1) in acetonitrile solution. Significantly, experimental and theoretical evidence reveal that the CO₂ photoreduction reaction mainly takes place at the aromatic nitrogen atom of adenine molecules through a unique o‐amino‐assisted activation rather than at the metal center. This work not only serves as an important case study for the development of green biomimetic photocatalysts used for artificial photosynthesis, but also proposes a new catalytic strategy for efficient CO₂ photoconversion.     

Control of Interpenetration and Gas‐Sorption Properties of Metal–Organic Frameworks by a Simple Change in Ligand Design

In metal–organic framework (MOF) chemistry, interpenetration greatly affects the gas‐sorption properties. However, there is a lack of a systematic study on how to control the interpenetration and whether the interpenetration enhances gas uptake capacities or not. Herein, we report an example of interpenetration that is simply controlled by the presence of a carbon–carbon double or single bond in identical organic building blocks, and provide a comparison of gas‐sorption properties for these similar frameworks, which differ only in their degree of interpenetration. Noninterpenetrated ( SNU‐70 ) and doubly interpenetrated ( SNU‐71 ) cubic nets were prepared by a solvothermal reaction of [Zn(NO₃)₂] ? 6 H₂O in N,N‐diethylformamide (DEF) with 4‐(2‐carboxyvinyl)benzoic acid and 4‐(2‐carboxyethyl)benzoic acid, respectively. They have almost‐identical structures, but the noninterpenetrated framework has a much bigger pore size (ca. 9.0×9.0 Å) than the interpenetrated framework (ca. 2.5×2.5 Å). Activation of the MOFs by using supercritical CO₂ gave SNU‐70′ and SNU‐71′ . The simulation of the PXRD pattern of SNU‐71′ indicates the rearrangement of the interpenetrated networks on guest removal, which increases pore size. SNU‐70′ has a Brunauer–Emmett–Teller (BET) surface area of 5290 m² g^?1, which is the highest value reported to date for a MOF with a cubic‐net structure, whereas SNU‐71′ has a BET surface area of 1770 m² g^?1. In general, noninterpenetrated SNU‐70′ exhibits much higher gas‐adsorption capacities than interpenetrated SNU‐71′ at high pressures, regardless of the temperature. However, at P<1 atm, the gas‐adsorption capacities for N₂ at 77 K and CO₂ at 195 K are higher for noninterpenetrated SNU‐70′ than for interpenetrated SNU‐71′ , but the capacities for H₂ and CH₄ are the opposite; SNU‐71′ has higher uptake capacities than SNU‐70′ due to the higher isosteric heat of gas adsorption that results from the smaller pores. In particular, SNU‐70′ has exceptionally high H₂ and CO₂ uptake capacities. By using a post‐synthetic method, the C?C double bond in SNU‐70 was quantitatively brominated at room temperature, and the MOF still showed very high porosity (BET surface area of 2285 m² g^?1).     

A Polyhedron‐based Metal‐Organic Framework showing high CO2 Adsorption Capacity

A novel porous copper‐based metal‐organic framework {[Cu₂(TTDA)₂]*(DMA)₇}_n ( 1 ) (DMA = N,N‐dimethylacetamide) was designed and synthesized via the combination of a dual‐functional organic linker 5′‐(4‐(4H‐1,2,4‐triazol‐4‐yl)phenyl)‐[1,1′:3′,1′′‐terphenyl]‐4,4′′‐dicarboxylic acid (H₂TTDA) and a dinuclear Cu^II paddle‐wheel cluster. This MOF is characterized by elemental analysis, powder X‐ray diffraction (PXRD), thermo gravimetric analysis (TGA), and single‐crystal X‐ray diffraction. The framework is constructed from two types of cages (octahedral and cuboctahedral cages) and exhibits two types of circular‐shaped channels of approximate size of 5.8 and 11.4 Å along the crystallographic c axis. The gas sorption experiments indicate that it possesses a large surface area (1687 m² · g^–1) and high CO₂ adsorption capacities around room temperature (up to 172 cm³ · g^–1 at 273 K and 124 cm³ · g^–1 at 298 K).     

High‐Performance K–CO2 Batteries Based on Metal‐Free Carbon Electrocatalysts

Metal–CO₂ batteries have attracted much attention owing to their high energy density and use of greenhouse CO₂ waste as the energy source. However, the increasing cost of lithium and the low discharge potential of Na–CO₂ batteries create obstacles for practical applications of Li/Na–CO₂ batteries. Recently, earth‐abundant potassium ions have attracted considerable interest as fast ionic charge carriers for electrochemical energy storage. Herein, we report the first K–CO₂ battery with a carbon‐based metal‐free electrocatalyst. The battery shows a higher theoretical discharge potential (E^?=2.48 V) than that of Na–CO₂ batteries (E^?=2.35 V) and can operate for more than 250 cycles (1500 h) with a cutoff capacity of 300 mA h g^?1. Combined DFT calculations and experimental observations revealed a reaction mechanism involving the reversible formation and decomposition of P12₁/c1‐type K₂CO₃ at the efficient carbon‐based catalyst.     

Porous carbon derived from a metal–organic framework as an efficient adsorbent for the solid‐phase extraction of phthalate esters

A porous carbon designated as MOF‐5‐C was prepared by directly carbonizing a metal–organic framework (MOF‐5). The morphology and microstructure of MOF‐5‐C were characterized by scanning electron microscopy, N₂ adsorption, and powder X‐ray diffraction. The MOF‐5‐C retained the original porous structures of MOF‐5, and showed a high Brunauer–Emmett–Teller surface area (1808 m² g^?1) and large pore volume (3.05 cm³ g^?1). To evaluate its adsorption performance, the MOF‐5‐C was used as an adsorbent for the solid‐phase extraction of four phthalate esters from bottled water, peach juice, and soft drink samples followed by high‐performance liquid chromatographic analysis. Several parameters that could affect the extraction efficiencies were investigated. Under the optimum conditions, a good linearity was achieved in the concentration range of 0.1–50.0 ng mL^?1 for bottled water sample and 0.2–50.0 ng mL^?1 for peach juice and soft drink samples. The limits of detection of the method (S/N = 3) were 0.02 ng mL^?1 for bottled water sample, and 0.04–0.05 ng mL^?1 for peach juice and soft drink samples. The results indicated that the MOF‐5‐C exhibited an excellent adsorption capability for trace levels of phthalate esters, and it could be a promising adsorbent for the preconcentration of other organic compounds.     

Conjugated Copper–Catecholate Framework Electrodes for Efficient Energy Storage

A conjugated copper(II) catecholate based metal–organic framework (namely Cu‐DBC) was prepared using a D₂‐symmetric redox‐active ligand in a copper bis(dihydroxy) coordination geometry. The π‐d conjugated framework exhibits typical semiconducting behavior with a high electrical conductivity of ca. 1.0 S m^?1 at room temperature. Benefiting from the good electrical conductivity and the excellent redox reversibility of both ligand and copper centers, Cu‐DBC electrode features superior capacitor performances with gravimetric capacitance up to 479 F g^?1 at a discharge rate of 0.2 A g^?1. Moreover, the symmetric solid‐state supercapacitor of Cu‐DBC exhibits high areal (879 mF cm^?2) and volumetric (22 F cm^?3) capacitances, as well as good rate capability. These metrics are superior to most reported MOF‐based supercapacitors, demonstrating promising applications in energy‐storage devices.     

A New Synthetic Route to Microporous Silica with Well‐Defined Pores by Replication of a Metal–Organic Framework

Microporous amorphous hydrophobic silica materials with well‐defined pores were synthesized by replication of the metal–organic framework (MOF) [Cu₃(1,3,5‐benzenetricarboxylate)₂] (HKUST‐1). The silica replicas were obtained by using tetramethoxysilane or tetraethoxysilane as silica precursors and have a micro–meso binary pore system. The BET surface area, the micropore volume, and the mesopore volume of the silica replica, obtained by means of hydrothermal treatment at 423 K with tetraethoxysilane, are 620 m²g^?1, 0.18 mL g^?1, and 0.55 mL g^?1, respectively. Interestingly, the silica has micropores with a pore size of 0.55 nm that corresponds to the pore‐wall thickness of the template MOF. The silica replica is hydrophobic, as confirmed by adsorption analyses, although the replica has a certain amount of silanol groups. This hydrophobicity is due to the unique condensation environment of the silica precursors in the template MOF.     

Hierarchically Porous Carbons Derived from Metal–Organic Framework/Chitosan Composites for High‐Performance Supercapacitors

Hierarchically porous carbon materials with high surface areas are promising candidates for energy storage and conversion. Herein, the facile synthesis of hierarchically porous carbons through the calcination of metal–organic framework (MOF)/chitosan composites is reported. The effects of the chitosan (CS) additive on the pore structure of the resultant carbons are discussed. The corresponding MOF/chitosan precursors could be readily converted into hierarchically porous carbons (NPC‐V, V=1, 2, 4, and 6) with much higher ratios of meso‐/macropore volume to micropore volume (V_meso‐macro/V_micro). The derived carbon NPC‐2 with the high ratio of V_meso‐macro/V_micro=1.47 demonstrates a high specific surface area of 2375 m² g^?1, and a high pore volume of 2.49 cm³ g^?1, as well as a high graphitization degree, in comparison to its counterpart (NPC) without chitosan addition. These excellent features are favorable for rapid ion diffusion/transport, endowing NPC‐2 with enhanced electrochemical behavior as supercapacitor electrodes in a symmetric electrode system, corresponding to a high specific capacitance of 199.9 F g^?1 in the aqueous electrolyte and good rate capability. Good cycling stability is also observed after 10 000 cycles.     

Mixed Metal–Organic Framework with Multiple Binding Sites for Efficient C2H2/CO2 Separation

The separation of C₂H₂/CO₂ is particularly challenging owing to their similarities in physical properties and molecular sizes. Reported here is a mixed metal–organic framework (M′MOF), [Fe(pyz)Ni(CN)₄] ( FeNi‐M′MOF , pyz=pyrazine), with multiple functional sites and compact one‐dimensional channels of about 4.0 Å for C₂H₂/CO₂ separation. This MOF shows not only a remarkable volumetric C₂H₂ uptake of 133 cm³ cm^?3, but also an excellent C₂H₂/CO₂ selectivity of 24 under ambient conditions, resulting in the second highest C₂H₂‐capture amount of 4.54 mol L^?1, thus outperforming most previous benchmark materials. The separation performance of this material is driven by π–π stacking and multiple intermolecular interactions between C₂H₂ molecules and the binding sites of FeNi‐M′MOF . This material can be facilely synthesized at room temperature and is water stable, highlighting FeNi‐M′MOF as a promising material for C₂H₂/CO₂ separation.     

Facile Synthesis of Hydroxy‐Modified MOF‐5 for Improving the Adsorption Capacity of Hydrogen by Lithium Doping

A facile synthesis of partially hydroxy‐modified MOF‐5 and its improved H₂‐adsorption capacity by lithium doping are reported. The reaction of Zn(NO₃)₂ ? 6 H₂O with a mixture of terephthalic acid (H₂BDC) and 2‐hydroxyterephthalic acid (H₂BDC‐OH) in DMF gave hydroxy‐modified MOF‐5 (MOF‐5‐OH‐x), in which the molar fraction (x) of BDC‐OH^2? was up to 0.54 of the whole ligand. The MOF‐5‐OH‐x frameworks had high BET surface areas (about 3300 m² g^?1), which were comparable to that of MOF‐5. We suggest that the MOF‐5‐OH‐x frameworks are formed by the secondary growth of BDC^2?‐rich MOF‐5 seed crystals, which are nucleated during the early stage of the reaction. Subsequent Li doping into MOF‐5‐OH‐x results in increased H₂ uptake at 77 K and 0.1 MPa from 1.23 to 1.39 wt. % and an increased isosteric heat of H₂ adsorption from 5.1–4.2 kJ mol^?1 to 5.5–4.4 kJ mol^?1.     

Proton Transport in a Highly Conductive Porous Zirconium‐Based Metal–Organic Framework: Molecular Insight

The water stable UiO‐66(Zr)‐(CO₂H)₂ MOF exhibits a superprotonic conductivity of 2.3×10^?3 S cm^?1 at 90 °C and 95 % relative humidity. Quasi‐elastic neutron scattering measurements combined with aMS‐EVB3 molecular dynamics simulations were able to probe individually the dynamics of both confined protons and water molecules and to further reveal that the proton transport is assisted by the formation of a hydrogen‐bonded water network that spans from the tetrahedral to the octahedral cages of this MOF. This is the first joint experimental/modeling study that unambiguously elucidates the proton‐conduction mechanism at the molecular level in a highly conductive MOF.     

Enhanced CO2 Adsorption Affinity in a NbO‐type MOF Constructed from a Low‐Cost Diisophthalate Ligand with a Piperazine‐Ring Bridge

A metal–organic framework (NPC‐6) with an NbO topology based on a piperazine ring‐bridged diisophthalate ligand was synthesized and characterized. The incorporated piperazine group leads to an enhanced adsorption affinity for CO₂ in NPC‐6, in which the CO₂ uptake is 4.83 mmol g^?1 at 293 K and 1 bar, ranking among the top values of CO₂ uptake on MOF materials. At 0.15 bar and 293 K, the NPC‐6 adsorbs 1.07 mmol g^?1 of CO₂, which is about 55.1 % higher than that of the analogue MOF NOTT‐101 under the same conditions. The enhanced CO₂ uptake combined with comparable uptakes for CH₄ and N₂ leads to much higher selectivities for CO₂/CH₄ and CO₂/N₂ gas mixtures on NPC‐6 than on NOTT‐101. Furthermore, an N‐alkylation is used in the synthesis of the PDIA ligand, leading to a much lower cost compared with that in the synthesis of ligands in the NOTT series, as the former does not require a palladium‐based catalyst and borate esters. Thus, we conclude that NPC‐6 is a promising candidate for CO₂ capture applications.     

Metal–Organic Frameworks Containing Missing‐Linker Defects Leading to High Hydroxide‐Ion Conductivity

The ionic conductivity properties of the face‐centered cubic [Ni₈(OH)₄(H₂O)₂(BDP_X)₆] (H₂BDP_X=1,4‐bis(pyrazol‐4‐yl)benzene‐4‐X with X=H ( 1 ), OH ( 2 ), NH₂ ( 3 )) metal–organic framework (MOF) systems as well as their post‐synthetically modified materials K[Ni₈(OH)₅(EtO)(BDP_X)_5.5] ( 1@KOH , 3@KOH ) and K₃[Ni₈(OH)₃(EtO)(BDP_O)₅] ( 2@KOH ), which contain missing‐linker defects, have been studied by variable temperature AC impedance spectroscopy. It should be noted that these modified materials exhibit up to four orders of magnitude increase in conductivity ^‐values in comparison to pristine 1 – 3 systems. As an example, the conductivity value of 5.86×10^?9 S cm^?1 (activation energy E_a of 0.60 eV) for 2 at 313 K and 22 % relative humidity (RH) increases up to 2.75×10^?5 S cm^?1 (E_a of 0.40 eV) for 2@KOH . Moreover, a further increase of conductivity values up to 1.16×10^?2 S cm^?1 and diminution of E_a down to 0.20 eV is achieved at 100 % RH for 2@KOH . The increased porosity, basicity and hydrophilicity of the 1@KOH – 3@KOH materials compared to the pristine 1 – 3 systems should explain the better performance of the KOH‐modified materials.     

Thermodynamics of Carbon Dioxide Adsorption on the Protonic Zeolite H‐ZSM‐5

Adsorption of carbon dioxide on H‐ZSM‐5 zeolite (Si:Al=11.5:1) was studied by means of variable‐temperature FT‐IR spectroscopy, in the temperature range of 310–365 K. The adsorbed CO₂ molecules interact with the zeolite Brønsted‐acid OH groups bringing about a characteristic red‐shift of the O? H stretching band from 3610 cm^?1 to 3480 cm^?1. Simultaneously, the ν₃ mode of adsorbed CO₂ is observed at 2345 cm^?1. From the variation of integrated intensity of the IR absorption bands at both 3610 and 2345 cm^?1, upon changing temperature (and CO₂ equilibrium pressure), the standard adsorption enthalpy of CO₂ on H‐ZSM‐5 is ΔH⁰=?31.2(±1) kJ mol^?1 and the corresponding entropy change is ΔS⁰=?140(±10) J mol^?1 K^?1. These results are discussed in the context of available data for carbon dioxide adsorption on other protonic, and also alkali‐metal exchanged, zeolites.     

Water‐Stable Zirconium‐Based Metal–Organic Framework Material with High‐Surface Area and Gas‐Storage Capacities

We designed, synthesized, and characterized a new Zr‐based metal–organic framework material, NU‐1100 , with a pore volume of 1.53 ccg^?1 and Brunauer–Emmett–Teller (BET) surface area of 4020 m²g^?1; to our knowledge, currently the highest published for Zr‐based MOFs. CH₄/CO₂/H₂ adsorption isotherms were obtained over a broad range of pressures and temperatures and are in excellent agreement with the computational predictions. The total hydrogen adsorption at 65 bar and 77 K is 0.092 g g^?1, which corresponds to 43 g L^?1. The volumetric and gravimetric methane‐storage capacities at 65 bar and 298 K are approximately 180 v_STP/v and 0.27 g g^?1, respectively.     

Rechargeable Room‐Temperature Na–CO2 Batteries

Developing rechargeable Na–CO₂ batteries is significant for energy conversion and utilization of CO₂. However, the reported batteries in pure CO₂ atmosphere are non‐rechargeable with limited discharge capacity of 200 mAh g^?1. Herein, we realized the rechargeability of a Na–CO₂ battery, with the proposed and demonstrated reversible reaction of 3 CO₂+4 Na?2 Na₂CO₃+C. The battery consists of a Na anode, an ether‐based electrolyte, and a designed cathode with electrolyte‐treated multi‐wall carbon nanotubes, and shows reversible capacity of 60000 mAh g^?1 at 1 A g^?1 (≈1000 Wh kg^?1) and runs for 200 cycles with controlled capacity of 2000 mAh g^?1 at charge voltage <3.7 V. The porous structure, high electro‐conductivity, and good wettability of electrolyte to cathode lead to reduced electrochemical polarization of the battery and further result in high performance. Our work provides an alternative approach towards clean recycling and utilization of CO₂.     

Design and Synthesis of a Water‐Stable Anionic Uranium‐Based Metal–Organic Framework (MOF) with Ultra Large Pores

Ionic metal–organic frameworks (MOFs) are a subclass of porous materials that have the ability to incorporate different charged species in confined nanospace by ion‐exchange. To date, however, very few examples combining mesoporosity and water stability have been realized in ionic MOF chemistry. Herein, we report the rational design and synthesis of a water‐stable anionic mesoporous MOF based on uranium and featuring tbo‐type topology. The resulting tbo MOF exhibits exceptionally large open cavities (3.9 nm) exceeding those of all known anionic MOFs. By supercritical CO₂ activation, a record‐high Brunauer‐Emmett‐Teller (BET) surface area (2100 m² g^?1) for actinide‐based MOFs has been obtained. Most importantly, however, this new uranium‐based MOF is water‐stable and able to absorb positively charged ions selectively over negatively charged ones, enabling the efficient separation of organic dyes and biomolecules.     

Encapsulating Perovskite Quantum Dots in Iron‐Based Metal–Organic Frameworks (MOFs) for Efficient Photocatalytic CO2 Reduction

Improving the stability of lead halide perovskite quantum dots (QDs) in a system containing water is the key for their practical application in artificial photosynthesis. Herein, we encapsulate low‐cost CH₃NH₃PbI₃ (MAPbI₃) perovskite QDs in the pores of earth‐abundant Fe‐porphyrin based metal organic framework (MOF) PCN‐221(Fe_x) by a sequential deposition route, to construct a series of composite photocatalysts of MAPbI₃@PCN‐221(Fe_x) (x=0–1). Protected by the MOF the composite photocatalysts exhibit much improved stability in reaction systems containing water. The close contact of QDs to the Fe catalytic site in the MOF, allows the photogenerated electrons in the QDs to transfer rapidly the Fe catalytic sites to enhance the photocatalytic activity for CO₂ reduction. Using water as an electron source, MAPbI₃@PCN‐221(Fe_0.2) exhibits a record‐high total yield of 1559 μmol g^?1 for photocatalytic CO₂ reduction to CO (34 %) and CH₄ (66 %), 38 times higher than that of PCN‐221(Fe_0.2) in the absence of perovskite QDs.