Study on the adsorption mechanism of DNA with mesoporous silica nanoparticles in aqueous solution

Among the numerous adsorption strategies for DNA adsorption into mesopores, the salt-solution-induced adsorption method has a great application potential in nucleic acids science; thus, it is important to understand the adsorption mechanism. This work demonstrates the mechanistic aspects underlying the adsorption behaviors of DNA with mesoporous silica nanoparticles (MSNs) in aqueous solution. The driving forces for the adsorption process can be categorized into three parts: the shielded electrostatic force, the dehydration effect, and the intermolecular hydrogen bonds. Compared to the adsorption behaviors of DNA with a solid silica nanosphere, we find some unique features for DNA adsorption into the mesopores, such as increasing the salt concentration or decreasing the pH value can promote DNA adsorption into the mesoporous silica. Further analysis indicates that the entrance of DNA into mesopores is probably controlled by the Debye length in solution and DNA can generate direct and indirect hydrogen bonds in the pores with different diameters. The following desorption study depicts that such types of hydrogen bonds result in different energy barriers for the desorption process. In summary, our study depicts the mechanism of DNA adsorption within mesopores in aqueous solution and sets the stage for formulating MSNs as carriers of nucleic acids.     

Influence of mesoporosity on the sorption of 2,4-dichlorophenoxyacetic acid onto alumina and silica

Two SiO2 and three Al2O3 adsorbents with varying degrees of mesoporosity (pore diameter 2-50 nm) were reacted with 2,4-dichlorophenoxyacetic acid (2,4-D) at pH 6 to investigate the effects of intraparticle mesopores on adsorption/desorption. Anionic 2,4-D did not adsorb onto either SiO2 solid, presumably because of electrostatic repulsion, but it did adsorb onto positively charged Al2O3 adsorbents, resulting in concave isotherms. The Al2O3 adsorbent of highest mesoporosity consistently adsorbed more 2,4-D per unit surface area than did the nonporous and less mesoporous Al2O3 adsorbents over a range of initial 2,4-D solution concentrations (0.025-2.5 mM) and reaction times (30 min-55 d). Differences in adsorption efficiency were observed despite equivalent surface site densities on the three Al2O3 adsorbents. Hysteresis between the adsorption/desorption isotherms was not observed, indicating that adsorption is reversible. Attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy studies confirm that 2,4-D adsorption does not occur via ligand exchange, but rather via electrostatic interaction. The results indicate that adsorbent intraparticle mesopores can result in consistently greater 2,4-D adsorption, but the amount adsorbed is dependent upon surface charge and the presence of adsorbent mesoporosity. The data also suggest that when mineral pores are significantly larger than the adsorbate, they do not contribute to diffusion-limited adsorption/desorption hysteresis. Adsorbent transformations through time are discussed.     

有序介孔二氧化硅对正丁醛的吸附性能

合成了一系列具有不同孔结构与性质的有序介孔二氧化硅材料SBA-15、MCM-41、SBA-16、KIT-6, 同时通过改变水热温度制备了不同孔径大小的SBA-15, 并利用小角X射线散射、透射电镜、扫描电镜和氮气吸附-脱附等手段, 对其介孔结构进行了表征. 以正丁醛为探针分子, 考察了其对有机醛的吸附, 并与Y-沸石的吸附性能做了对比. 结果表明, 材料的介孔比表面积与其对正丁醛的吸附量成正比, 吸附等温线符合Langmuir 模型, 属于单层吸附, 具有最大介孔比表面积的MCM-41对正丁醛的吸附量最大(484 mg·g^-1). 最后将SBA-15添加到卷烟滤嘴中, 实验结果表明, SBA-15能显著降低卷烟烟气中巴豆醛的释放量.     

有序介孔二氧化硅对正丁醛的吸附性能

合成了一系列具有不同孔结构与性质的有序介孔二氧化硅材料SBA-15、MCM-41、SBA-16、KIT-6,同时通过改变水热温度制备了不同孔径大小的SBA-15,并利用小角X射线散射、透射电镜、扫描电镜和氮气吸附-脱附等手段,对其介孔结构进行了表征.以正丁醛为探针分子,考察了其对有机醛的吸附,并与Y-沸石的吸附性能做了对比.结果表明,材料的介孔比表面积与其对正丁醛的吸附量成正比,吸附等温线符合Langmuir模型,属于单层吸附,具有最大介孔比表面积的MCM-41对正丁醛的吸附量最大(484 mg·g-1).最后将SBA-15添加到卷烟滤嘴中,实验结果表明,SBA-15能显著降低卷烟烟气中巴豆醛的释放量.     

Thermodynamic and neutron scattering study of hydrogen adsorption in two mesoporous ordered carbons

Two mesoporous ordered carbon materials (MOCs) have been synthesized from silica templates by using sucrose as the carbon precursor. The textural characterization using Ar, N2, and CO2 adsorption combined with neutron diffraction showed that the two samples exhibit a significant microporous volume close to 0.5 cm3/g and an ordered network of mesopores. For both MCM48 and SBA15 templated carbons, adsorption first proceeds with the filling of micropores and then by the filling of mesopores with an adsorption energy close to the enthalpy of vaporization of bulk hydrogen. The hydrogen isosteric heat of adsorption in the micropores (6-8 kJ/mol) is significantly larger than that on the graphite surface (approximately 4 kJ/mol) but still too small for a reasonable use of these MOCs as hydrogen adsorbents for storage at room temperature. The neutron scattering study showed that the structure at 10 K of the adsorbed deuterium phase is poorly organized; it exhibits short and medium range orders of about 13 angstroms in micropores and about 20 angstroms in mesopores, respectively. The average distance between adsorbed molecules decreases with coverage by about 10%. In the mesopores, the diffracted line is consistent with a pseudohexagonal packing.     

Availability and interconnectivity of pores in mesostructured ZSM-5 zeolites by the adsorption and diffusion of mesitylene

Probing the mesopore architecture in mesoporous zeolites is of importance for large scale applications of the materials. In this work, the adsorption and diffusion of mesitylene with larger molecule size in mesoporous ZSM-5 zeolites were carried out, in order to acquaint the availability and interconnectivity of mesopores in zeolite crystals. The comparisons of the shape of adsorption isotherms and the mesopore volume calculated from mesitylene and N₂ adsorption in mesoporous ZSM-5 zeolites with different mesoporosities can be used to discriminate two cases of mesopores: accessible mesopores connected to external surface of the zeolite crystals and non-accessible meso-voids that are occluded in the microporous matrix. Furthermore, the effective diffusivity and activation energy of mesitylene in mesoporous ZSM-5 extracted from ZLC desorption curves as a function of mesopore volume calculated from mesitylene adsorption reveal the enhancement of mesopore interconnectivity to molecule diffusion in zeolite crystals.     

Dibenzodioxin adsorption on inorganic materials

Dibenzodioxin adsorption/desorption on solid surfaces is an important issue associated with the formation, adsorption, and emission of dioxins. Dibenzodioxin adsorption/desorption behaviors on inorganic materials (amorphous/mesoporous silica, metal oxides, and zeolites) were investigated using in situ FT-IR spectroscopy and thermogravimetric (TG) analysis. Desorption temperatures of adsorbed dibenzodioxin are very different for different kinds of inorganic materials: approximately 200 degrees C for amorphous/mesoporous silica, approximately 230 degrees C for metal oxides, and approximately 450 degrees C for NaY and mordenite zeolites. The adsorption of dibenzodioxin can be grouped into three categories according to the red shifts of the IR band at 1496 cm(-1) of the aromatic ring for the adsorbed dibenzodioxin: a shift of 6 cm(-1) for amorphous/mesoporous silica, a shift of 10 cm(-1) for metal oxides, and a shift of 14 cm(-1) for NaY and mordenite, suggesting that the IR shifts are proposed to associated with the strength of the interaction between adsorbed dibenzodioxin and the inorganic materials. It is proposed that the dibenzodioxin adsorption is mainly via the following three interactions: hydrogen bonding with the surface hydroxyl groups on amorphous/mesoporous silica, complexation with Lewis acid sites on metal oxides, and confinement effect of pores of mordenite and NaY with pore size close to the molecular size of dibenzodioxin.     

Synthesis of temperature-responsive anion exchanger via click reaction

The temperature-responsive anion exchanger was synthesized by immobilizing the poly(N-isopropylacrylamide) (PNIPAM), a kind of the temperature-responsive polymer, on the external surface of mesoporous silica via click reaction. The structure of this synthesized composite was characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), elemental analysis, and nitrogen adsorption experiment. The amount of PNIPAM immobilized on the external surface of mesoporous silica, which was calculated from the weight loss measured by thermogravimetry, increased from 5.3 wt.% to 12.9 wt.% (dry) depending on the amount of PNIPAM added in the click reaction. The adsorption-desorption behavior of methyl orange (MO) ions in this synthesized anion exchanger was affected by the temperature of aqueous solution: the MO ions were adsorbed and desorbed reversibly and repeatedly with changing the pH of the solution at 25 °C, while the amount of adsorbed MO ions remained nearly constant at about 0.05 mmol/g independent of the pH of the solution at 40 °C. Also, the amount of PNIPAM immobilized on the mesoporous silica influenced the adsorption rate of MO ions, suggesting that the adsorption rate in this composite is controlled by the diffusion of MO ions through the PNIPAM layer.     

多重响应性介孔二氧化硅纳米微球的制备及载药研究

采用溶胶凝胶法制备了以油酸稳定的Fe3O4为核, 十六烷基三甲基溴化铵(CTAB)为模板剂的磁响应性的介孔二氧化硅纳米微球; 通过孔道内修饰羧基和巯基, 链转移反应修饰线性的聚(N-异丙基丙烯酰胺-co-N-羟甲基丙烯酰胺)共聚物得到多重响应性的介孔二氧化硅纳米微球P(NIPAM-co-NHMA)@M-MSN(-COOH). 利用Brunauer-Emmett-Teller (BET)、振动样品磁强计(VSM)、透射电子显微镜(TEM)、紫外光谱(UV/Vis)表征了微球的物理化学性质. 阿霉素(DOX)被用作模型药物研究了这种多重响应性的介孔二氧化硅纳米微球作为药物载体的载药及药物释放行为, 结果显示这种纳米微球载药率高达48%, 药物释放呈现对温度和pH的双重响应性, 可以实现对药物的控制释放.     

Growth of porous single-crystal Cr2O3 in a 3-D mesopore system

Single-crystal Cr2O3 with regular mesopores has been synthesized using mesoporous silica KIT-6 as a template and characterized by using XRD, HRTEM and nitrogen adsorption/desorption.     

Diffuse reflectance infrared Fourier transform spectroscopy as a tool to characterise water in adsorption/confinement situations

We present experimental data acquired by diffuse reflectance infrared spectroscopy in the mid-IR (4000-400 cm(-1)), on micrometric-sized mineral grain powders. The spectral evolution of the OH-stretching band is followed when the adsorbed water film is thinned under dry conditions, from high to low hydration states. The IR bands are found to be characteristic of the degree of adsorption/confinement of the liquid water. The OH-stretching band is shifted toward shorter wavenumbers than in bulk water, showing that a significant portion of adsorbed water has a higher intermolecular bonding energy. Complementary treatment of the kinetics of water desorption, varying with the surface forces in the water film, confirms the relationships of these bands with the constrained water state. We distinguish different water types obeying liquid-liquid interactions (free and capillary water) or dominated by solid-water interactions (confined and adsorbed water). Part of this study is devoted to mesoporous silica MCM-41, of interest due to the restricted geometries of its mesopores (4.7 nm) favouring the confined water state. The methodology allows us to distinguish bulk and adsorbed/confined water, using spectral analysis coupled with an understanding of the dynamic behaviour of the desorption process.     

Synthesis and characterization of pore size-tunable magnetic mesoporous silica nanoparticles

Magnetic mesoporous silica nanoparticles (M-MSNs) are emerging as one of the most appealing candidates for theranostic carriers. Herein, a simple synthesis method of M-MSNs with a single Fe(3)O(4) nanocrystal core and a mesoporous shell with radially aligned pores was elaborated using tetraethyl orthosilicate (TEOS) as silica source, cationic surfactant CTAB as template, and 1,3,5-triisopropylbenzene (TMB)/decane as pore swelling agents. Due to the special localization of TMB during the synthesis process, the pore size was increased with added TMB amount within a limited range, while further employment of TMB lead to severe particle coalescence and not well-developed pore structure. On the other hand, when a proper amount of decane was jointly incorporated with limited amounts of TMB, effective pore expansion of M-MSNs similar to that of analogous mesoporous silica nanoparticles was realized. The resultant M-MSN materials possessed smaller particle size (about 40-70 nm in diameter), tunable pore sizes (3.8-6.1 nm), high surface areas (700-1100 m(2)/g), and large pore volumes (0.44-1.54 cm(3)/g). We also demonstrate their high potential in conventional DNA loading. Maximum loading capacity of salmon sperm DNA (375 mg/g) was obtained by the use of the M-MSN sample with the largest pore size of 6.1 nm.     

Adsorption property of congo red from aqueous solution by Cu-BTC/SiO 2 composite

The adsorption behavior of congo red from aqueous solution on Cu-BTC/SiO2 was investigated. Cu-BTC/SiO2 with mesoporous structure and large surface area was prepared by loading Cu-BTC into the mesoporous silica using in-situ synthesis method. The X-ray diffraction, scanning electron microscopy, and nitrogen adsorption–desorption analysis were used to characterize the structure and morphology of the prepared materials. The adsorption studies showed that the adsorption isotherm of congo red on Cu-BTC/SiO2 fitted well with Freundlich adsorption model and congo red is easy to be adsorbed by Cu-BTC/SiO2. The thermodynamic study showed that the adsorption behavior of congo red on Cu-BTC/SiO2 is an exothermic process at temperature under investigation.     

Adsorption of plasmid DNA to a natural organic matter-coated silica surface: kinetics, conformation, and reversibility

A quartz crystal microbalance with dissipation (QCM-D) has been used to determine the adsorption rate of ampicillin-resistant linear and supercoiled plasmid DNA onto a silica surface coated with natural organic matter (NOM). The structure of the resulting adsorbed DNA layer was determined by analyzing the viscoelastic properties of the adsorbed DNA layers as they formed and were then exposed to solutions of different ionic composition. The QCM-D data were complemented by dynamic light scattering measurements of diffusion coefficients of the DNA molecules as a function of solution ionic composition. The obtained results suggest that electrostatic interactions control the adsorption and structural changes of the adsorbed plasmid DNA on the NOM-coated silica surface. The adsorption of DNA molecules to the NOM layer took place at moderately high monovalent (sodium) electrolyte concentrations. A sharp decrease in solution ionic strength did not result in the release of the adsorbed DNA, indicating that DNA adsorption on the NOM-coated silica surface is irreversible under the studied solution conditions. However, the decrease in electrolyte concentration influenced the structure of the adsorbed layer, causing the adsorbed DNA to adopt a less compact conformation. The linear and supercoiled DNA had similar adsorption rates, but the linear DNA formed a thicker and less compact adsorbed layer than the supercoiled DNA.     

Adsorption of DNA into mesoporous silica

In these experiments, double-stranded, linear DNA sequences were adsorbed into the pores of spherically shaped acid-prepared mesoporous silica (APMS). The lengths of the sequences were either 760 base pairs or 2000 base pairs. DNA adsorption into the interior of the mesoporous material was confirmed using confocal microscopy of sequences containing fluorescently labeled DNA molecules. Additional characterization with N(2) physisorption and powder X-ray diffraction supported this finding. The extent of adsorption was measured at various concentrations using UV-visible spectrophotometry to establish adsorption isotherms. APMS alone adsorbed a negligible amount of DNA; however, exchanging divalent cations such as Mg(2+) and Ca(2+) into the pores of APMS prior to DNA uptake was found to cause a significant amount of DNA to be adsorbed. Using Na(+) caused a lower amount of DNA to be adsorbed. DNA adsorption was also dependent on the pore diameter of APMS. Adsorption increased upon expansion of the pore size of the metal ion-exchanged material from 34 to 54 A; however, no additional uptake was measured by further increasing the pore size to 100 A. The amount of DNA adsorbed could also be significantly increased by using (aminopropyl)triethoxysilane to covalently link ammonium ions to the surface. Postsynthetic modification of the silica surface with aminopropyl groups increased the maximum DNA adsorption to 15.7 microg/mg silica, for materials with pore diameters of 100 A, which is 2 to 3 times more adsorbed DNA than for metal ion-exchanged material. This indicated that DNA binds more strongly in the presence of the ammonium group compared to the metal counterions. Finally, calculation and comparison of Freundlich and Langmuir constants for these adsorption processes indicate that intermolecular interactions between the DNA molecules within the pores are significant when the effective pore diameter is small, including materials with larger pores that were modified with organosilane.     

Mechanism of the dimerization of enzymes upon adsorption on silicate adsorbents using the example of lysozyme and β-galactosidase

It is shown by the kinetic analysis of lysozyme and β-galactosidase adsorption on silochrome, silica gel, and mesoporous silica that the adsorption follows a two-stage scheme, including reversible pre-adsorption and the irreversible binding of dimmers. The corresponding rate constants of adsorption, desorption, and dimerization were calculated. It was found that β-galoctosidase adsorbed on silica gel and mesoporous silica retained ∼20% of its activity, while β-galoctosidase adsorbed on silochrome retained more than 30% of its activity.     

β-Cyclodextrin assisted one-pot synthesis of mesoporous magnetic Fe3O4@C and their excellent performance for the removal of Cr Ⅵ from aqueous solutions

Mesoporous magnetic Fe3O4@C nanoparticles have been synthesized by a one-pot approach and used as adsorbents for removal of Cr (Ⅳ) from aqueous solution. Magnetic iron oxide nanostructured materials encapsulated by carbon were characterized by scanning electron microscope (SEM), nitrogen adsorption and desorption, X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The adsorption performance of the nanomaterial adsorbents is tested with the removal of Cr (Ⅳ) from aqueous solution. The results reveal that the mesoporous magnetic Fe3O4@C nanospheres exhibit excellent adsorption efficiency and be easily isolated by an external magnetic field. In comparison with magnetic Fe3O4 nanospheres, the mesoporous magnetic Fe3O4@C exhibited 1.8 times higher removal rate of Cr Ⅵ. Themesoporous structure and an abundance of hydroxy groups on the carbon surfacemay be responsible for high absorbent capability.     

A Stand-Alone Mesoporous Crystal Structure Model from in situ X-ray Diffraction: Nitrogen Adsorption on 3 D Cagelike Mesoporous Silica SBA-16

We present a modeling scheme to analyze cagelike silica mesoporous crystals based on in situ X-ray diffraction (XRD) data collected during gas adsorption-desorption (physisorption) processes. Nitrogen physisorption on a silica mesoporous crystal of SBA-16 was directly monitored by using synchrotron in situ powder XRD measurements conducted at SPring-8. SBA-16 is a well-ordered mesoporous silica in which three-dimensional interconnected cagelike primary mesopores are located at the body-centered cubic lattice points. In addition, the surrounding silica matrix contains random microporous and mesoporous intrawall porosities that are significantly influential to the diffusion properties, and thus important to be quantified for this media. The in situ XRD data exhibits seven Bragg reflections throughout the measurements, and the present method allows one to obtain the maximal and stand-alone information about the pore structure (for example, the mesopore size, the matrix density, the intrawall porosity, and pore surface roughness) together with the nitrogen film evolution in the primary mesopores and the intrawall pore-filling in the silica matrix. We furthermore observe a macroscopic amount of nitrogen adsorbed assuming the density of the fluid, and confirm that the XRD "isotherm" recalculated from the analysis result is consistent with the conventional nitrogen isotherm on a semi-quantitative level; however, these results suggest that the intrawall pores would have a greater contribution to the adsorption than considered based on the conventional isotherm analyses. The present method is readily extendable to any ordered mesopores wrapped by the wall matrix containing a certain intrawall porosity.     

Silica nanoparticle size influences the structure and enzymatic activity of adsorbed lysozyme

Adsorption of chicken egg lysozyme on silica nanoparticles of various diameters has been studied. Special attention has been paid to the effect of nanoparticle size on the structure and function of the adsorbed protein molecules. Both adsorption patterns and protein structure and function are strongly dependent on the size of the nanoparticles. Formation of molecular complexes is observed for adsorption onto 4-nm silica. True adsorptive behavior is evident on 20- and 100-nm particles, with the former resulting in monolayer adsorption and the latter yielding multilayer adsorption. A decrease in the solution pH results in a decrease in lysozyme adsorption. A change of protein structure upon adsorption is observed, as characterized by a loss in alpha-helix content, and this is strongly dependent on the size of the nanoparticle and the solution pH. Generally, greater loss of alpha helicity was observed for the lysozyme adsorbed onto larger nanoparticles under otherwise similar conditions. The activity of lysozyme adsorbed onto silica nanoparticles is lower than that of the free protein, and the fraction of activity lost correlates well with the decrease in alpha-helix content. These results indicate that the size of the nanoparticle, perhaps because of the contributions of surface curvature, influences adsorbed protein structure and function.     

NPE在有序介孔炭上的吸附行为研究

采用有序介孔硅为硬模板制备了具有不同孔径的有序介孔炭(OMCs). 氮气吸附测试表明, 有序介孔炭具有丰富的介孔表面和集中的介孔分布. 以壬基酚聚氧乙烯醚(NPE)为探针分子, 研究了大分子酚类在有序介孔炭上的吸附行为. 吸附研究表明, NPE在有序介孔炭上的吸附满足Langmuir吸附模型. 孔结构分析表明, 大于1.5 nm的孔的表面积是决定NPE吸附量的关键因素, 而有序介孔炭的最可几孔径决定吸附速率的大小. 与吸附量相比, 吸附速率更容易受环境温度的影响. 动力学研究表明, NPE在有序介孔炭上的吸附满足准二级动力学方程.