Spin-engineering in the Co75Fe25/Cu(1 1 0) system

We present results on the growth and magnetic anisotropies of Co₇₅Fe₂₅ films grown on a Cu(1 1 0) single crystal. Angular dependent MOKE measurements show a thickness dependent, in-plane rotation of the easy axis of magnetisation of up to 60° from the [0 0 1] direction (towards [−1 1 0]). For a film thickness of 5 ML, just greater than that required for the onset of ferromagnetism, uniaxial anisotropy is observed with the easy axis along the [0 0 1] direction. As the film thickness increases this is seen to rotate in-plane towards the [−1 1 0] direction as the contribution from the cubic anisotropy constant grows. At a film thickness of 9 ML there is predominantly cubic anisotropy and at 10 ML the easy axis is rotated to 150° with respect to the [1 −1 0] axis, where it is stabilised.     

Epitaxial strain-induced magnetic anisotropy in Sm3Fe5O12 thin films grown by pulsed laser deposition

Sm₃Fe₅O₁₂ thin films of various thicknesses were grown on a (0 0 1)-oriented Gd₃Ga₅O₁₂ substrate by pulsed laser deposition. The crystal structure of the films was strongly dependent on film thickness. The lattice was strained for thinner films due to a lattice mismatch between the film and substrate. This lattice strain was relaxed when the film thickness exceeded a critical thickness of around 660 Å. It is suggested that the epitaxial strain induces uniaxial magnetic anisotropy with an out-of-plane magnetic easy axis.     

Magnetic domain structure in Fe78.8−xCoxCu0.6Nb2.6Si9B9 nanocrystalline alloys studied by Lorentz microscopy

The magnetic domain structures of Fe_78.8−xCo_xCu_0.6Nb_2.6Si₉B₉ (x=0, 20, 40, 60) alloys are investigated by Lorentz microscopy coupled with the focused ion beam method. The specimen prepared using the FIB method is found to have a considerably more uniform thickness compared to that prepared using the ion-milling method. In Fe_38.8Co₄₀Cu_0.6Nb_2.6Si₉B₉ and Fe_18.8Co₆₀Cu_0.6Nb_2.6Si₉B₉ alloys, 180° domain walls extending in the direction of the induced magnetic anisotropy are observed. Analysis with Lorentz microscopy reveals that the width of the magnetic domains decreases with an increase in the cobalt content or the induced magnetic anisotropy K_u, that is, the domain width d is proportional to the induced magnetic anisotropy (K_u)^−1/4. On the other hand, in the in situ Lorentz microscopy observation as a function of temperature, magnetic ripple structures are found to appear in a localized area due to the fluctuation of magnetization vectors from 423 K. It is observed that the induced magnetic anisotropy caused by the applied magnetic field at 803 K is not suppressed by the magnetic ripple structures observed at 423–443 K.     

Structure,magnetic properties and magnetostriction of Fe81Ga19 thin films

The structure, magnetic properties and magnetostriction of Fe₈₁Ga₁₉ thin films have been investigated by using X-ray diffraction analysis, scanning electron microscope (SEM), vibrating sample magnetometer and capacitive cantilever method. It was found that the grain size of as-deposited Fe₈₁Ga₁₉ thin films is 50–60 nm and the grain size increases with increase in the annealing temperature. The remanence ratio (M_r/M_s) of the thin films slowly decreases with increase in the annealing temperature. However, the coercivity of the thin films goes the opposite way with increase in the annealing temperature. A preferential orientation of the Fe₈₁Ga₁₉ thin film fabricated under an applied magnetic field exists along 〈1 0 0〉 direction due to the function of magnetic field during sputtering. An in-plane-induced anisotropy of the thin film is well formed by the applied magnetic field during the sputtering and the formation of in-plane-induced anisotropy results in 90° rotations of the magnetic domains during magnetization and in the increase of magnetostriction for the thin film.     

Role of crystal orientation on the magnetic properties of CoFe2O4 thin films grown on Si (1 0 0) and Al2O3 (0 0 0 1) substrates using pulsed laser deposition

We report the influence of crystal orientation on the magnetic properties of CoFe₂O₄ (CFO) thin films grown on single crystal Si (1 0 0) and c-cut sapphire (Al₂O₃) (0 0 0 1) substrates using pulsed laser deposition technique. The thickness was varied from 200 to 50 nm for CFO films grown on Si substrates, while it was fixed at 200 nm for CFO films grown on Al₂O₃ substrates. We observed that the 200 and 100 nm thick CFO-Si films grew in both (1 1 1) and (3 1 1) directions and displayed out-of-plane anisotropy, whereas the 50 nm thick CFO-Si film showed only an (1 1 1) orientation and an in-plane anisotropy. The 200 nm thick CFO film grown on an Al₂O₃ substrate was also found to show a complete (1 1 1) orientation and a strong in-plane anisotropy. These observations pointed to a definite relation between the crystalline orientation and the observed magnetic anisotropy in the CFO thin films.     

Magnetic properties of strontium hexaferrite films prepared by pulsed laser deposition

The magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films fabricated by pulsed laser deposition on the Si(100) substrate with Pt(111) underlayer have been studied as a function of film thickness (50–700 nm). X-ray diffraction patterns confirm that the films have c-axis perpendicular orientation. The coercivities in perpendicular direction are higher than those for in-plane direction which indicates the films have perpendicular magnetic anisotropy. The coercivity was found to decrease with increasing of thickness, due to the increasing of the grain size and relaxation in lattice strain. The 200 nm thick film exhibits hexagonal shape grains of 150 nm and optimum magnetic properties of M_s=298 emu/cm³ and H_c=2540 Oe.     

Dependence of magnetic anisotropy of the La0.67Ca0.33MnO3 films on substrate and film thickness

Strain in the La_0.67Ca_0.33MnO₃ films has been tuned by varying substrate and film thickness, and its effects on magnetic anisotropy are studied based on the measurements of isothermal magnetization. Measuring the strain in the films by the out-of-plane lattice parameter (c), we found a strong dependence of the magnetic anisotropy constant (Ku) on strain. Ku decreases linearly from ∼−1.1×10⁶ erg/cm³ for c=0.763 nm to 1.2×10⁶ erg/cm³ for c=0.776 nm, corresponding to a change from tensile strain to compressive strain. Positive Ku signifies a uniaxial anisotropy with the easy axis perpendicular to the film plane, while negative Ku demonstrates an anisotropy of the easy plane character. Smaller or larger c leads a decrease or increase in Ku, which indicates the presence of other effects in addition to those associated with strain. Three distinctive processes for the magnetization are observed along the hard magnetic axis of the films on (001)SrTiO₃, suggesting a possibility of strain relaxation even in ultra-thin films.     

Effect of nanoscale thin films of Dy2Fe14B on the magnetic hysteresis characteristics of melt-spun ribbons of Nd2Fe14B

The effectiveness of nanoscale Dy₂Fe₁₄B thin films on coercivity and energy product of melt-spun ribbons of Nd₂Fe₁₄B at high temperatures was investigated. It is hypothesized that the nanoscale Dy-thin film will act as an obstacle for the nucleation of reverse domains and also maximize the energy of domain walls and thereby improve the magnetic performance at high temperatures. Pulsed laser deposition (PLD) of amorphous Dy₂Fe₁₄B layers on Nd₂Fe₁₄B melt-spun ribbons was performed for a nominal thickness of 40 nm. The coated ribbons were then annealed in environmentally controlled quartz furnace at two different cycles (750 °C for 15 min and 900 °C for 2 h) to cause crystallization. Magnetic hysteresis tests conducted at 300 and 400 K revealed that there is small but consistent improvement in the magnetic properties of the coated ribbons annealed at 750 °C for 15 min. However, higher temperature annealing (900 °C for 2 h) drastically reduced the magnetic properties. The incomplete recrystallization of amorphous structure at 750 °C for 15 min and large grain growth and formation of non-magnetic phases at 900 °C for 2 h are believed to be responsible for not meeting the expected magnetic performance.     

Effect of oxygen pressure on microstructure and magnetic properties of strontium hexaferrite (SrFe12O19) film prepared by pulsed laser deposition

The effects of oxygen pressure during deposition on microstructure and magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films grown on Si (100) substrate with Pt (111) underlayer by pulsed laser deposition have been investigated. X-ray diffraction pattern confirms that the films have c-axis perpendicular orientation. The c-axis dispersion (Δθ₅₀) increases and c-axis lattice parameter decreases with increasing oxygen pressure. The films have hexagonal shape grains with diameter of 150-250 nm as determined by atomic force microscopy. The coercivities in perpendicular direction are higher than those in in-plane direction, which shows the films have perpendicular magnetic anisotropy. The saturation magnetization and anisotropy field for the film deposited in oxygen pressure of 0.13 mbar are comparable to those of the bulk strontium hexaferrite. Higher oxygen pressure leads to the films having higher coercivity and squareness. The coercivity in perpendicular and in-plane directions of the film deposited in oxygen pressure of 0.13 mbar are 2520 Oe and 870 Oe, respectively.     

Nanoridge domains in α-phase W films

Two types of nanoridge domains oriented with each other with an angle ranging between 109° and 124° were measured by scanning tunneling microscopy on the α-W film sputter deposited on an oxidized Si surface. Each domain contains nanoridges with a period of 7.5 ± 1.0 nm. No such domains were observed on the β-W film surface. We argued that due to the anisotropy of the W(1 1 0) surface, the impinging W atoms diffuse faster along the 〈111〉 directions on the surface to form the nanoridge structure. There are two equivalent 〈111〉 directions, which give rise to two orientational domains with an angle of ∼110°. An isotropic β-W(1 0 0) phase has no preferred diffusion direction for the impinging W atoms and therefore, no nanoridge domain structure was observed.     

Magnetic force microscopy characterization of heat and current treated Fe40Ni38Mo4B18 amorphous ribbons

The domain structure of a magnetostrictive Fe₄₀Ni₃₈Mo₄B₁₈ amorphous ribbon has been studied using magnetic force microscopy (MFM) at room temperature. First, the evolution of the magnetic domain patterns as a function of the annealing temperature has been investigated. In samples heat treated at 250 and 450 °C for 1 h, a transformation from 90° to 180° domain wall has been clearly observed, while the sample heat treated at 700 °C for 1 h showed a magnetic phase fixed by the crystalline anisotropy. Additionally, the evolution of the magnetic domain structure by applying a DC current was recorded by the MFM technique. For current annealed samples at 1 A for 1, 30 and 60 min, a transformation between different domain patterns has been observed. Finally, in samples treated by the current annealing method under simultaneous stress, an increase of the annealing time gives rise to a different magnetic structure arising from the development of transverse magnetic anisotropy.     

Texture development and magnetic properties of [ZrO2/CoPt]n/Ag nanocomposite films

The L1₀ CoPt films with (0 0 1) preferred orientation are achieved by fabricating on the glass substrates and post annealing at 600° C for 30 min. The preferred orientation of [ZrO₂/CoPt]_n/Ag films dependence of the Ag underlayer thickness, ZrO₂ and CoPt interlayer thickness is investigated. A large perpendicular magnetic anisotropy and a nearly perfect L1₀ CoPt (0 0 1) texture are obtained in the [ZrO₂ (3 nm)/CoPt (5 nm)]₃/Ag (10 nm) film. The existence of ZrO₂ plays an important role in reducing the intergranular interactions and in determining the size of CoPt grains. Magnetic reversal in textured CoPt films are close to a Stoner-Wolfarth rotation.     

Magnetic properties of co-sputtered Tb-Co2FeAl films with perpendicular anisotropy

We present a systematic study on magnetic properties of co-sputtered Tb-Co₂FeAl (TCFA) films. The TCFA films with suitable Tb content have perpendicular magnetic anisotropy (PMA). The PMA deteriorates with both decreasing film thickness and high temperature annealing. Under a certain thickness, the perpendicular coercivity of the TCFA films with PMA can be reduced down to 60 Oe, which is comparable with normal soft ferromagnets. After annealing at 100 °C, a large remanence squareness of 0.95 is observed in the TCFA film with 33% Tb and a thickness of 30 nm.     

Tuning magnetic properties of magnetoelectric BiFeO3-NiFe2O4 nanostructures

Multifunctional thin film nanostructures containing soft magnetic materials such as nickel ferrite are interesting for potential applications in microwave signal processing because of the possibility to shrink the size of device architecture and limit device power consumption. An essential prerequisite to future applications of such a system is a firm understanding of its magnetic properties. We show that nanostructures composed of ferrimagnetic NiFe₂O₄ pillars in a multiferroic BiFeO₃ matrix can be tuned magnetically by altering the aspect ratio of the pillars by depositing films of varying thickness. Magnetic anisotropy is studied using ferromagnetic resonance, which shows that the uniaxial magnetic anisotropy in the growth direction changes sign upon increasing the film thickness. The magnitude of this anisotropy contribution can be explained via a combination of shape and magnetostatic effects, using the object-oriented micromagnetic framework (OOMMF). The key factors determining the magnetic properties of the films are shown to be the aspect ratio of individual pillars and magnetostatic interactions between neighboring pillars.     

Effect of nanoparticle size on magnetic damping parameter in Co92Zr8 soft magnetic films

Co₉₂Zr₈(50 nm)/Ag(x) soft magnetic films have been prepared on Si (111) substrates by oblique sputtering at 45°. Nanoparticle size of Co₉₂Zr₈ soft magnetic films can be tuned by thickening Ag buffer layer from 9 nm to 96 nm. The static and dynamic magnetic properties show great dependence on Ag buffer layer thickness. The coercivity and effective damping parameter of Co₉₂Zr₈ films increase with thickening Ag buffer layer. The intrinsic and extrinsic parts of damping were extracted from the effective damping parameter. For x=96 nm film, the extrinsic damping parameter is 0.028, which is significantly larger than 0.004 for x=9 nm film. The origin of the enhancement of extrinsic damping can be explained by increased inhomogeneity of anisotropy. Therefore, it is an effective method to tailor magnetic damping parameter of thin magnetic films, which is desirable for high frequency application.     

Thermomagnetic transitions and coercivity mechanism in bulk composite Nd60Fe30Al10 alloys

The thermomagnetic behaviour (within the temperature range 553-300 K) for the bulk composite Nd₆₀Fe₃₀Al₁₀ alloy is described in terms of a transition from paramagnetic to superferromagnetic state at T=553 K, followed by a ferromagnetic ordering for T<473 K. For the superferromagnetic regime, the alloy thermomagnetic response was associated to a homogeneous distribution of magnetic clusters with mean magnetic moment and size of 1072 μ_B and 2.5 nm, respectively. For T<473 K, a pinning model of domain walls described properly the alloy coercivity dependence with temperature, from which the domain wall width and the magnetic anisotropy constant were estimated as being of ≈8 nm and ≈10⁵ J/m³, typical values of hard magnetic phases. Results are supported by microstructural and magnetic domain observations.     

Anomalous magnetization processes and non-symmetrical domain wall displacements in L10 FePt particulate films

Anomalous magnetization processes and non-symmetrical domain wall displacements in the minor loop of L1₀ FePt particulate films were investigated by magnetization measurements and in situ magnetic force microscopy. Magnetization (M) decreases dramatically on increasing the magnetic field to ∼3 kOe after which M becomes small and constant in the range of 5–20 kOe as observed in the successive measurement of minor loops. The domain wall displacement is non-symmetrical with respect to the field direction. The anomalous magnetization behavior was attributed to the non-symmetrical domain wall displacement and large magnetic field required for domain wall nucleation. Energy calculations from modeling suggest that non-symmetrical domain wall displacement is caused by the existence of metastable domains in which the domain edges are stuck to the particle boundaries.     

Effects of oblique-incidence evaporation on magnetic properties of Fe20Ni80/Fe70Co30 bilayer film

Evaporative deposition at oblique incidence is shown to enhance the magnetic anisotropy of an Fe₂₀Ni₈₀ magnetic film and induce magnetic anisotropy in an overlying, strongly isotropic Fe₇₀Co₃₀ film. This deposition method for the formation of an underlayer of several lattice parameters in thickness and semi-hard overlayer of a few thousands Angstroms in thickness achieves a significant change in the magnetization process and strong suppression of the coercive forces of Fe₇₀Co₃₀ in the hard magnetization direction. Soft magnetization of the Fe₇₀Co₃₀ overlayer is not achieved when one of the layers is deposited at oblique incidence. It is anticipated that shape magnetic anisotropy is responsible in part for the magnetic anisotropy induced in both in Fe₂₀Ni₈₀ under- and Fe₇₀Co₃₀ overlayer by oblique incidence evaporation.     

Demonstration of ultra-high-resolution MFM images using Co90Fe10-coated CNT probes

We demonstrate ultra-high-resolution magnetic force microscopy images of perpendicular magnetic storage media using carbon nanotube probes coated by ferromagnetic Co₉₀Fe₁₀ films (20, 30, 40, and 50 nm). By optimizing ferromagnetic film thickness (effective tip diameter), we obtained best magnetic domain image with an 40 nm-Co₉₀Fe₁₀-coated tip (50 nm tip diameter) about a lateral detect density of 1200 k flux per inch on perpendicular magnetic storage medium, one of the highest resolutions in MFM imaging reported for this material system and structure. The observed dependence of tip dimension on signal contrast and image resolution was successfully explained by a theoretical analysis indicating that the signal contrast, along with the physical probe-tip dimension, should be taken into account to design magnetic probes tips for high-resolution magnetic force microscopy.     

Thickness dependence of microwave magnetic properties in electrodeposited Fe-Co soft magnetic films with in-plane anisotropy

In this work, the thickness effect of Fe₅₂Co₄₈ soft magnetic films with in-plane anisotropy on static and microwave magnetic properties was investigated. The hysteresis loop results indicated that the static in-plane uniaxial anisotropy field increased from almost 0-60 Oe with increasing film thickness from 100 to 540 nm and well-defined in-plane uniaxial magnetic anisotropy can be obtained as the thickness reached 540 nm or larger. Based on Landau-Lifshitz-Gilbert (LLG) equation, the microwave complex permeability spectra were analyzed and well fitted. The LLG curve-fitting results indicated that the initial permeability increased from 106 to 142 and the resonant frequency was shifted from 4.95 to 4.29 GHz as the film thickness was varied from 540 to 1500 nm. Moreover, it was found that there was a discrepancy between the static and the dynamically determined anisotropy field, which can be explained by introducing an additional effective isotropic ripple field. The decreased ripple field was suggested to result in a significant decrease of damping coefficient from 0.109 to 0.038.