Magnetic transitions in Ni1−xMox and Ni1−xWx disordered alloys

We present a mean-field study of the magnetic phase diagram of Ni_1−xMo_x and Ni_1−xW_x alloys. The pair energies that enter the internal energy part of the free energy are obtained from a first-principles calculation. We try to understand why spin-glass phase is not observed in these alloys.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Formation mechanism of ferromagnetism in Si1−xMnx diluted magnetic semiconductors

Si_1−xMn_x diluted magnetic semiconductor (DMS) bulks were formed by using an implantation and annealing method. Energy dispersive X-ray fluorescence, transmission electron microscopy (TEM), and double-crystal rocking X-ray diffraction (DCRXD) measurements showed that the grown materials were Si_1−xMn_x crystalline bulks. Hall effect measurements showed that annealed Si_1−xMn_x bulks were p-type semiconductors. The magnetization curve as a function of the magnetic field clearly showed that the ferromagnetism in the annealed Si_1−xMn_x bulks originated from the interaction between interstitial and substitutional Mn⁺ ions, which was confirmed by the DCRXD measurements. The magnetization curve as a function of the temperature showed that the ferromagnetic transition temperature was approximately 75 K. The present results can help to improve understanding of the formation mechanism of ferromagnetism in Si_1−xMn_x DMS bulks.     

Bulk Sn1−xMnxO2 magnetic semiconductors without room-temperature ferromagnetism

Polycrystalline Sn_1−xMn_xO₂ (0≤x≤0.05) diluted magnetic semiconductors were prepared by solid-state reaction method and their structural and magnetic properties had been investigated systematically. The three Mn-doped samples (x=0.01, 0.03, 0.05) undergo paramagnetic to ferromagnetic phase transitions upon cooling, but their Curie temperatures are far lower than room temperature. The magnetization cannot be attributed to any identified impurity phase. It is also found that the magnetization increases with increasing Mn doping, while the ratio of the Mn ions contributing to ferromagnetic ordering to the total Mn ions decreases.     

Magnetic properties of Mn-rich Rh2Mn1+xSn1−x Heusler alloys

X-ray powder diffraction and magnetization measurements have been carried out on Rh₂Mn_1+xSn_1−x (0≤x≤0.3) alloys. The alloys, which crystallize in the L2₁ structure, were found to exhibit ferromagnetic behavior. The lattice constant a at room temperature decreases with increasing x, whereas the Curie temperature T_C decreases linearly. At 5 K the magnetic moment per formula unit first increases with increasing x and then saturates for x≥0.2. The experimental results are discussed in terms of the influence of the Mn-Mn exchange interactions between the Mn atoms on the Sn and Mn sites.     

The large low-field magnetic entropy changes in Ni43Mn46Sn11−xSbx alloys

A series of Ni₄₃Mn₄₆Sn_11−xSb_x (x=0, 1, and 3) alloys were prepared by an arc melting method. The martensitic transition shifts to higher temperature with the increasing Sb content. The isothermal magnetization curves and Arrott plots around martensitic transition temperatures show a typical metamagnetic behavior. Under a low applied magnetic field of 10 kOe, large magnetic entropy changes around the martensitic transition temperature are 10.4, 8.9, and 7.3 J/kg K, for x=0, 1, and 3, respectively. The origin of the large magnetic entropy changes and potential application for Ni₄₃Mn₄₆Sn_11−xSb_x alloys as working substances in magnetic refrigeration are discussed.     

Transport properties and magnetoresistance in CoNb1−xMnxSb half-Heusler alloys with a low temperature localization

The transport properties and magnetoresistance of half-Heusler CoNb_1−xMn_xSb (x=0.0-1.0) alloys have been investigated between 2 and 300 K. In this temperature range, a metallic conductivity has been observed for the alloys with higher (x=1.0) and lower (x=0.0-0.2) Mn contents. However, the middle Mn content alloys (x=0.4-0.8) exhibit non-metallic conductive behavior. Their temperature dependence of resistivity undergoes a Mott localization law ρ=ρ₀exp(T₀/T)^p (p=1/4) rather than a thermal excitation regime ρ=ρ₀exp(E_a/kT) at low temperature (). The localization can be attributed to atomic and magnetic disorder. Resistivity peaks from 25 to 300 K were also observed for these alloys. Magnetotransport investigation reveals that these resistivity peaks result from localization effect as well as spin-disorder scattering.     

Formation of room-temperature ferromagnetic Zn1−xCoxO nanocrystals

Optical and magnetic properties of Co²⁺-doped ZnO nanocrystals were studied. Optical measurements confirm the incorporation of Co²⁺ in ZnO lattice with tetrahedral geometry. Optical absorption spectra also reveal the partial bleaching of the excitonic feature attributable to an increase in electron concentration. Magnetization measurements indicate the ferromagnetic ordering in Co²⁺-doped ZnO nanocrystals with saturation magnetization . No structural changes were observed in lightly doped ZnO nanocrystals. The present investigations are important in obtaining the ferromagnetic Zn_1−xCo_xO nanocrystals.     

The effect of Fe doping on structural, magnetic and electrical transport properties of CaMn1−xFexO3 (x=0-0.35)

A comprehensive study of the effect of Fe doping on CaMnO₃ is carried out by means of experiments on the structural, transport conduction, and magnetic properties of CaMn_1−xFe_xO₃ (0≤x≤0.35). With a sol-gel process for sample preparation, Fe is substituted for Mn up to x=0.35. This substitution substantially brings out the lattice expansion and gradually suppresses the antiferromagnetism. For x=0.08 and 0.10 in particular, the magnetization curves with a field-cooled mode under the field of 1 kOe behave as those of a ferrimagnetic-like system and present low-temperature negative magnetization. For x≥0.15, the negative magnetization phenomenon disappears, and a ferromagnetic component coexists with an antiferromagnetic one, but the antiferromagnetic interaction still dominates in these compounds. Electrical transport measurements show insulating behavior for all compositions. Fe doping, even at a level as low as x=0.02, can cause a marked resistivity increase in the temperature range studied. Further increasing the Fe content causes the resistivity to gradually decrease due to the increasing carrier presence.     

Structure and magnetic properties of Ca1−x−yMgxCu2+yO3 influenced by isoelectronic substitution x

Phases of the composition Ca_1−x−yMg_xCu_2+yO₃ have been prepared for the first time. The compounds are isostructural with the known end-members CaCu₂O₃ and MgCu₂O₃ showing a two-leg spin-ladder-like connection of copper and oxygen atoms within the Cu₂O₃-layer. Opposite the spin ladders this layer is folded, which results in a long-range antiferromagnetic ordering of these phases. The Néel temperature can be adapted by variation of x in Ca_1−x−yMg_xCu_2+yO₃ between 24 and 80 K. Several structural features, which influence the magnetic ordering, are discussed.     

Electronic structure and elastic constants of TiCxN1−x, ZrxNb1−xC and HfCxN1−x alloys: A first-principles study

The structural, electronic and elastic properties of TiC_xN_1−x, Zr_xNb_1−xC and HfC_xN_1−x alloys have been investigated by using the plane-wave pseudopotential method within the density-functional theory. The calculations indicate that the variations of the equilibrium lattice constants and bulk modulus with the composition are found to be linear. The calculated elastic constants C₄₄ and shear constants as a function of alloy concentration reveal the anisotropic hardness of these compounds. The partial and total density of states (DOS) for the binary and ternary compounds had been obtained, and the metallic behavior of these alloys had been confirmed by the analysis of DOS.     

First-principles and Monte Carlo combinational study on Zn1−xCoxO diluted magnetic semiconductor

The electronic structures and magnetic properties of Zn_1−xCo_xO (x=5.55%,8.33%,12.5%) are studied using first-principles calculations in combination with Monte Carlo (MC) simulation. The combinational method makes possible a complete simulation from the microscopic magnetic interaction to macroscopic magnetic behavior. The calculated results from first principles indicate that the ferromagnetic ground state is stabilized by a half-metallic electronic structure which originates from the strong hybridization between Co 3d electrons and O 2p electrons. With the magnetic coupling strengths obtained from first-principles calculations, the MC simulation predicts the ferromagnetism of Zn_1−xCo_xO (x=5.55%,8.33%,12.5%) with , which is consistent with the experimental facts.     

Structural and photoluminescence properties of thermally evaporated Cd1−xMnxS nano-crystalline films

Thin films of Cd_1−xMn_xS (0≤x≤0.5) were formed on glass substrates by resistive vacuum thermal evaporation. All the films were deposited at 300 K and the films were annealed at 373, 473 and 573 K for 1 h in a vacuum of 10⁻⁶ mbar. Atomic force microscopy (AFM) studies showed that all the films investigated were in nano-crystalline form with a grain size in the range 36-82 nm. All the films exhibited a wurtzite structure of the host material. The lattice parameters varied linearly with composition following Vegard’s law in the entire composition range. Photoluminescence studies showed that two distinct emission bands were observed for each Cd_1−xMn_xS compound. One corresponds to internal transition and the other one is due to the transition of Mn²⁺ ions in interstitial sites or in small ‘Mn’ chalcogenic clusters.     

Highly cation-deficient manganese perovskite, La1−xMn1−yO3 with x=y

Oxidative (δ>0) nonstoichiometry in the perovskite ‘LaMnO_3+δ’ has been known to be manifested not with O interstitials but rather with cation vacancies of equal amounts at the two cation sites, La and Mn, i.e. La_1−xMn_1−yO₃ with x=y. Here, we report the fabrication of samples with record-high cation-vacancy concentrations (x>0.12 or δ>0.4) by means of a variety of high-pressure oxygenation techniques. Linear (negative) dependence of the cell volume on x was observed within the whole x range investigated, down to 56.9 Å³ (per formula unit) for a sample oxygenated at 5 GPa and 1100 °C using Ag₂O₂ as an excess oxygen source. With increasing degree of cation deficiency in La_1−xMn_1−xO₃, the ferromagnetic transition temperature was found to follow a bell shape with respect to x exhibiting a maximum of ∼250 K about x≈0.1. For moderately oxygenated samples large magnetoresistance effect was evidenced.     

Magnetic,electronic and structural properties of ZnxFe3−xO4

A series of samples Zn_xFe_3−xO₄ have been prepared by the chemical coprecipitation technique and characterized by X-ray diffraction (XRD), vibrating sample magnetometry (VSM) and X-ray photoelectron spectroscopy (XPS). XRD demonstrates all the samples of Zn_xFe_3−xO₄ have a spinel structure same as Fe₃O₄. The magnetic hysteresis loops of Zn_xFe_3−xO₄ obtained from VSM indicate that the saturation magnetization has a maximum when x is ∼1/3. The chemical states of Fe atoms and Zn atoms in zinc ferrites have been measured using XPS and Auger electron spectroscopy (AES). The Fe 2p core-level XPS spectra and Zn L₃M₄₅M₄₅ Auger peaks have been analyzed and the results have been discussed in correlation with the samples’ magnetic properties. These results suggest most of Zn atoms occupy the tetrahedral sites and a small amount of them occupy the octahedral sites.     

Structural and elastic properties of Ni2+xMn1−xGa alloys

The structural parameters and the energetics of the Ni_2+xMn_1−xGa alloys have been investigated by the first-principles Exact Muffin Tin Orbital-Coherent Potential Approximation (EMTO-CPA) for 0.10<x<0.30. The difference in total energies (δE) between the low-temperature tetragonal phase and the high-temperature cubic phase has been considered as a qualitative indicator of the martensitic transformation temperature T_m. The qualitative behavior of δE with variation of x has been found to be in agreement with the experimentally observed variation of T_m with x. The elastic constants for the entire range of x have also been calculated and the determination of a relationship between δE and the elastic shear modulus has been attempted. It is seen that δE varies linearly with elastic shear modulus C′, qualitatively similar to the relation between T_m and C′. The energetics calculated with the EMTO method agrees quite well with the all-electron full-potential results ensuring the accuracy of the method. These results show that the EMTO-CPA method is one of the most reliable and accurate first-principles methods, in the context of off-stoichiometric alloys which undergo martensitic phase transformations.     

Synthesis and magnetic properties of Zn1−xMnxO films prepared by the sol-gel method

We report on the ferromagnetic characteristics of Zn_1−xMn_xO films (x=0.1-0.3) prepared by the sol-gel method on silicon substrates using transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), X-ray diffractometry (XRD) and superconducting quantum interference device (SQUID) magnetometry at various temperatures. Magnetic measurement show that the Curie temperature (T_C) and the coercive field (H_C) were ∼39 K and ∼2100 Oe for the film of x=0.2, respectively. EDS and TEM measurements indicate that Mn content at the interface is significantly higher than that at the center of the Zn_0.8Mn_0.2O film showing the ratio, Zn:Mn:O≅1:12:15. This experimental evidence suggests that ferromagnetic precipitates containing manganese oxide may be responsible for the observed ferromagnetic behavior of the film.     

The role of oxygen vacancies in magnetism of CoxTi1−xO2−δ films on Si(001) prepared by sol-gel method

Co_xTi_1−xO_2−δ films have been prepared on Si(001) substrates by sol-gel method. When heat treated in air, Co_xTi_1−xO_2−δ films are non-ferromagnetic at room temperature. However, after further vacuum annealing or hydrogenation, Co_xTi_1−xO_2−δ films show room-temperature ferromagnetism (RTFM). When the vacuum annealed Co_xTi_1−xO_2−δ films are reheated in air, the magnetic moments of the films strongly reduce. After these films are vacuum annealed once again, the magnetic moments are greatly enhanced, confirming the role of vacuum annealing in ferromagnetism of Co_xTi_1−xO_2−δ films. The x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) and measurements of magnetization (M) vs temperature (T) fail to detect Co clusters in the vacuum annealed and the hydrogenated Co_xTi_1−xO_2−δ films. Oxygen vacancies are formed in Co_xTi_1−xO_2−δ films after vacuum annealing and hydrogenation, determined by XRD and XPS measurements. These results indicate that oxygen vacancies created by vacuum annealing and hydrogenation play an important role in the generation of RTFM in Co_xTi_1−xO_2−δ films.     

Antiferromagnetism and spin-glass transition in the FeInxCr2−xSe4 series of selenides

The magnetic behavior of the FeIn_xCr_2−xSe₄ system (with x=0.0, 0.2 and 0.4) has been investigated by magnetic and Mössbauer spectroscopy. Hyperfine parameters indicate that iron is in the Fe²⁺ oxidation state, with a minor (∼9%) Fe³⁺ fraction, located at different layers in the structure. Low-field magnetization curves as a function of temperature showed that the antiferromagnetic (AFM) order temperature is T_N=208(2) K for FeCr₂Se₄ and decreases to 174(3) K for FeIn_0.4Cr_1.6Se₄. The effective magnetic moment μ_eff decreases with increasing In contents, and shows agreement with the expected values from the contribution of Fe²⁺ (⁵D) and Cr³⁺ (⁴F) electronic states. A second, low-temperature transition is observed at T_G∼13 K, which has been assigned to the onset of a glassy state.     

Desorption of surfactant and sintering of surface-modified PdxNi1 − x nanoparticles

A series of Pd_xNi_1 − x nanoparticles in a diameter of 6-7 nm were prepared by wet chemical reduction. They were then modified with two surfactants, stearic acid (SA) and polyethylene glycol (PEG). Desorption of the surfactant was studied using a temperature programmed desorption technique, and the sintering behavior of surface-modified Pd_xNi_1 − x nanoparticles was examined. Since surface energy of the nanoparticles depends on the alloy composition, it can be correlated with the desorption temperature of surfactant from the nanoparticle surface. Because Ni has a higher surface energy, the surfactant desorption temperature increases as the Ni content increases. With the same stoichiometry, the desorption temperature of SA is always higher than that of PEG. The SA-modified nanoparticles have higher thermal stability and are less sintered than PEG-modified nanoparticles. The sintering and growth behavior of the nanoparticles can be correlated with variation of surface energy due to different surface modification.