Synthesis and structural investigation of the compounds containing HF2 anions: Ca(HF2)2, Ba4F4(HF2)(PF6)3 and Pb2F2(HF2)(PF6)

Three new compounds Ca(HF₂)₂, Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) were obtained in the system metal(II) fluoride and anhydrous HF (aHF) acidified with excessive PF₅. The obtained polymeric solids are slightly soluble in aHF and they crystallize out of their aHF solutions. Ca(HF₂)₂ was prepared by simply dissolving CaF₂ in a neutral aHF. It represents the second known compound with homoleptic HF environment of the central atom besides Ba(H₃F₄)₂. The compounds Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) represent two additional examples of the formation of a polymeric zigzag ladder or ribbon composed of metal cation and fluoride anion (MF⁺)_n besides PbF(AsF₆), the first isolated compound with such zigzag ladder. The obtained new compounds were characterized by X-ray single crystal diffraction method and partly by Raman spectroscopy. Ba₄F₄(HF₂)(PF₆)₃ crystallizes in a triclinic space group P1¯ with a=4.5870(2) Å, b=8.8327(3) Å, c=11.2489(3) Å, α=67.758(9)°, β=84.722(12), γ=78.283(12)°, V=413.00(3) Å³ at 200 K, Z=1 and R=0.0588. Pb₂F₂(HF₂)(PF₆) at 200 K: space group P1¯, a=4.5722(19) Å, b=4.763(2) Å, c=8.818(4) Å, α=86.967(10)°, β=76.774(10)°, γ=83.230(12)°, V=185.55(14) ų, Z=1 and R=0.0937. Pb₂F₂(HF₂)(PF₆) at 293 K: space group P1¯, a=4.586(2) Å, b=4.781(3) Å, c=8.831(5) Å, α=87.106(13)°, β=76.830(13)°, γ=83.531(11)°, V=187.27(18) Å³, Z=1 and R=0.072. Ca(HF₂)₂ crystallizes in an orthorhombic Fddd space group with a=5.5709(6) Å, b=10.1111(9) Å, c=10.5945(10) Å, V=596.77(10) Å³ at 200 K, Z=8 and R=0.028.     

Order-disorder in In perovskites: The example of A(In2/3B″1/3)O3 (A=Ba, Sr; B″=W, U)

We describe the preparation and structural characterization of four In-containing perovskites from neutron powder diffraction (NPD) and X-ray powder diffraction (XRPD) data. Sr₃In₂B″O₉ and Ba(In_2/3B″_1/3)O₃ (B″=W, U) were synthesized by standard ceramic procedures. The crystal structure of the W-containing perovskites and Ba(In_2/3U_1/3)O₃ have been revisited based on our high-resolution NPD and XRPD data, while for the new U-containing perovskite Sr₃In₂UO₉ the structural refinement was carried out from high-resolution XRPD data. At room temperature, the crystal structure for the two Sr phases is monoclinic, space group P2₁/n, where the In atoms occupy two different sites Sr₂[In]_2d[In_1/3B″_2/3]_2cO₆, with a=5.7548(2) Å, b=5.7706(2) Å, c=8.1432(3) Å, β=90.01(1)° for B″=W and a=5.861(1) Å, b=5.908(1) Å, c=8.315(2) Å, β=89.98(1)° for B″=U. The two phases with A=Ba should be described in a simple cubic perovskite unit cell (S.G. Pm3¯m) with In and B″ distributed at random at the octahedral sites, with a=4.16111(1) Å and 4.24941(1) Å for W and U compounds, respectively.     

Two new octahedral/pyramidal frameworks containing both cation channels and lone-pair channels: syntheses and structures of Ba2MnMn2(SeO3)6 and PbFe2(SeO3)4

The hydrothermal syntheses, single crystal structures, and some properties of Ba₂Mn^IIMn₂^III(SeO₃)₆ and PbFe₂(SeO₃)₄ are reported. These related phases contain three-dimensional frameworks of vertex (FeO₆) and vertex/edge linked (MnO₆) octahedra and SeO₃ pyramids. In each case, the MO₆/SeO₃ framework encloses two types of 8 ring channels, one of which encapsulates the extra-framework cations and one of which provides space for the Se^IV lone pairs. Crystal data: Ba₂Mn₃(SeO₃)₆, M_r=1201.22, monoclinic, P2₁/c (No. 14), a=5.4717 (3) Å, b=9.0636 (4) Å, c=17.6586 (9) Å, β=94.519 (1)°, V=873.03 (8) Å³, Z=2, R(F)=0.031, wR(F²)=0.070; PbFe₂(SeO₃)₄, M_r=826.73, triclinic, (No. 2), a=5.2318 (5) Å, b=6.7925 (6) Å, c=7.6445 (7) Å, α=94.300 (2)°, β=90.613 (2)°, γ=95.224 (2)°, V=269.73 (4) Å³, Z=1, R(F)=0.051, wR(F²)=0.131.     

Hydrothermal synthesis and structural characterization of two organically templated zincophosphites with three-dimensional frameworks, (C6H14N2)·[Zn3(HPO3)4] and (C4H12N2)·[Zn3(HPO3)4]

Two organically templated zincophosphites, (C₆H₁₄N₂)·[Zn₃(HPO₃)₄] and (C₄H₁₄N₂)·[Zn₃(HPO₃)₄] have been prepared under hydrothermal conditions and characterized by single-crystal X-ray diffraction. (C₆H₁₄N₂)·[Zn₃(HPO₃)₄] crystallizes in the triclinic space group , with cell parameters, a=9.363(4) Å, b=10.051(4) Å, c=10.051(4) Å, α=85.777(13)°, β=82.091(9)°, and γ=79.783(9)°. (C₄H₁₄N₂)·[Zn₃(HPO₃)₄] crystallizes in the monoclinic space group P2₁/c, with cell parameters, a=9.9512(3) Å, b=10.1508(3) Å, c=17.8105(5) Å, and β=95.6510(10)°. Although the two structures are different, they have the same anionic framework compositions of [Zn₃(HPO₃)₄]²⁻. Their frameworks are built up from strictly alternating ZnO₄ tetrahedra and HPO₃ pseudo pyramids by sharing vertexes. There exist channels with an eight-membered ring window along the a- and c-axis. Powder X-ray diffraction, IR spectroscopy, ³¹P MAS solid-state NMR, thermogravimetric and differential thermal analyses were also carried out.     

New one-dimensional uranyl and neptunyl iodates: crystal structures of K3[(UO2)2(IO3)6](IO3)·H2O and K[NpO2(IO3)3]·1.5H2O

The uranyl and neptunyl(VI) iodates, K₃[(UO₂)₂(IO₃)₆](IO₃)·H₂O (1) and K[NpO₂(IO₃)₃]·1.5H₂O (2), have been prepared and crystallized under mild hydrothermal conditions. The structures of 1 and 2 both contain one-dimensional _∞¹[AnO₂(IO₃)₃]¹⁻(An=U,Np) ribbons that consist of approximately linear actinyl(VI) cations bound by iodate anions to yield AnO₇ pentagonal bipyramids. The AnO₇ units are linked by bridging iodate anions to yield chains that are in turn coupled by additional iodate anions to yield ribbons. The edges of the ribbons are terminated by monodentate iodate anions. For 1 and 2, K⁺ cations and water molecules separate the ribbons from one another. In addition, isolated iodate anions are also found between _∞¹[UO₂(IO₃)₃]¹⁻ ribbons in 1. In order to aid in the assignment of oxidation states in neptunyl containing compounds, a bond-valence sum parameter of 2.018 Å for Np(VI) bound exclusively to oxygen has been developed with b=0.37 Å. Crystallographic data (193 K, MoKα, λ=0.71073): 1, triclinic, , a=7.0609(4) Å, b=14.5686(8)  Å, c=14.7047(8)  Å, α=119.547(1)°, β=95.256(1)°, γ=93.206(1)°, Z=2, R(F)=2.49% for 353 parameters with 6414 reflections with I>2σ(I); (203 K, MoKα, λ=0.71073): 2, monoclinic, P2₁/c, a=7.796(4)  Å, b=7.151(3)  Å, c=21.79(1)  Å, β=97.399(7)°, Z=4, R(F)=6.33% for 183 parameters with 2451 reflections with I>2σ(I).     

K2Li(NH2)3 and K2Na(NH2)3—synthesis and crystal structure of two crystal-chemically isotypic mixed-cationic amides

K₂Li(NH₂)₃ (1) was the only crystalline product obtained from the reaction of potassium with dilithium decahydro-closo-decaborate Li₂B₁₀H₁₀ in liquid ammonia at −38 °C. The compound crystallizes in the space group P4₂/m with Z=4, a=6.8720(5) Å, c=11.706(1) Å and V=552.81(7) Å³. The investigated crystal-chemically isotypic sodium compound K₂Na(NH₂)₃ (2) was merohedrally twinned and crystallized from a reaction mixture containing potassium and disodium decahydro-closo-decaborate Na₂B₁₀H₁₀ in liquid ammonia with a=7.0044(5) Å, c=12.362(1) Å and V=606.48(9) Å³. The compounds contain pairs of edge sharing tetraamidolithium or tetraamidosodium tetrahedra which are interconnected by potassium ions forming three-dimensional infinite networks.     

Crystal structure and phase transitions in perovskite-like C(NH2)3SnCl3

X-ray single-crystal diffraction, high-temperature powder diffraction and differential thermal analysis at ambient and high pressure have been employed to study the crystal structure and phase transitions of guanidinium trichlorostannate, C(NH₂)₃SnCl₃. At 295 K the crystal structure is orthorhombic, space group Pbca, Z=8, a=7.7506(2) Å, b=12.0958(4) Å and c=17.8049(6) Å, solved from single-crystal data. It is perovskite-like with distorted corner-linked SnCl₆ octahedra and with ordered guanidinium cations in the distorted cuboctahedral voids. At 400 K the structure shows a first-order order-disorder phase transition. The space group is changed to Pnma with Z=4, a=12.1552(2) Å, b=8.8590(2) Å and c=8.0175(1) Å, solved from powder diffraction data and showing disordering of the guanidinium cations. At 419 K, the structure shows yet another first-order order-disorder transformation with disordering of the SnCl₃⁻ part. The space group symmetry is maintained as Pnma, with a=12.1786(2) Å, b=8.8642(2) Å and c=8.0821(2) Å. The thermodynamic parameters of these transitions and the p-T phase diagram have been determined and described.     

Subsolidus phase relations and crystal structures of the mixed-oxide phases in the In2O3-WO3 system

Subsolidus phase relationships in the In₂O₃-WO₃ system at 800-1400°C were investigated using X-ray diffraction. Two binary-oxide phases—In₆WO₁₂ and In₂(WO₄)₃—were found to be stable over the range 800-1200°C. Heating the binary-oxide phases above 1200°C resulted in the preferential volatilization of WO₃. Rietveld refinement was performed on three structures using X-ray diffraction data from nominally phase-pure In₆WO₁₂ at room temperature and from nominally phase-pure In₂(WO₄)₃ at 225°C and 310°C. The indium-rich phase, In₆WO₁₂, is rhombohedral, space group (rhombohedral), with Z=1, a=6.22390(4) Å, α=99.0338(2)° [hexagonal axes: a_H=9.48298(6) Å, c=8.94276(6) Å, a_H/c=0.9430(9)]. In₆WO₁₂ can be viewed as an anion-deficient fluorite structure in which 1/7 of the fluorite anion sites are vacant. Indium tungstate, In₂(WO₄)₃, undergoes a monoclinic-orthorhombic transition around 250°C. The high-temperature polymorph is orthorhombic, space group Pnca, with a=9.7126(5) Å, b=13.3824(7) Å, c=9.6141(5) Å, and Z=4. The low-temperature polymorph is monoclinic, space group P2₁/a, with a=16.406(2) Å, b=9.9663(1) Å, c=19.099(2) Å, β=125.411(2)°, and Z=8. The structures of the two In₂(WO₄)₃ polymorphs are similar, consisting of a network of corner sharing InO₆ octahedra and WO₄ tetrahedra.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Synthesis, structure, and characterization of hybrid materials: [Ce(H2O)]2[O2C(CH2)2CO2]3 and [Sm(H2O)]2[O2C(CH2)2CO2]3·H2O

The rare-earth dicarboxylate hybrid materials [Ce(H₂O)]₂[O₂C(CH₂)₂CO₂]₃ ([Ce(Suc)]) and [Sm(H₂O)]₂[O₂C(CH₂)₂CO₂]₃·H₂O ([Sm(Suc)]) have been hydrothermally synthesized (200°C, 3 days) under autogenus pressure. [Ce(Suc)] is triclinic, a=7.961 (3) Å, b=8.176 (5) Å, c=14.32 (2) Å, α=97.07° (7), β=96.75° (8), γ=103.73° (6), and z=2. The crystal structure of this compound has been determined using 3120 unique single crystal data. The final refinements let the agreement factors R₁ and wR₂(F²) converge to 0.0138 and 0.0363, respectively. [Ce(Suc)] is built up from infinite chains of edge-sharing nine-fold coordinated cerium atoms running along [100]. These chains are interconnected by the carbon atoms of the succinate anions, leading to a three-dimensional hybrid framework. The cell constants of [Sm(Suc)], isotypic with monoclinic C2/c [Pr(H₂O)]₂[O₂C(CH₂)₂CO₂]₃·H₂O ([Pr(Suc)]), were refined starting from X-ray powder data: a=20.275 (3) Å, b=7.919 (6) Å, c=14.130 (3) Å, and β=121.45° (1). Despite its lower symmetry, [Ce(Suc)] presents an important structural filiation with [Sm(Suc)]     

New members of ternary rare-earth metal boride carbides containing finite boron-carbon chains: RE25B14C26 (RE=Pr, Nd) and Nd25B12C28

New ternary rare-earth metal boride carbides RE₂₅B₁₄C₂₆ (RE=Pr, Nd) and Nd₂₅B₁₂C₂₈ were synthesized by co-melting the elements. Nd₂₅B₁₂C₂₈ is stable up to 1440 K. RE₂₅B₁₄C₂₆ (RE=Pr, Nd) exist above 1270 K. The crystal structures were investigated by means of single-crystal X-ray diffraction. Nd₂₅B₁₂C₂₈: space group P, a=8.3209(7) Å, b=8.3231(6) Å, c=29.888(2) Å, α=83.730(9)°, β=83.294(9)°, γ=89.764(9)°. Pr₂₅B₁₄C₂₆: space group P2₁/c, a=8.4243(5) Å, b=8.4095(6) Å, c=30.828(1) Å, β=105.879(4)°, V=2100.6(2) Å³, (R1=0.048 (wR2=0.088) from 2961 reflections with I_o>2σ(I_o)); for Nd₂₅B₁₄C₂₆ space group P2₁/c, Z=2, a=8.3404(6) Å, b=8.3096(6) Å, c=30.599(2) Å, β=106.065(1)°. Their structures consist of a three-dimensional framework of rare-earth metal atoms resulting from the stacking of slightly corrugated and distorted square nets, leading to cavities filled with cumulene-like molecules [B₂C₄]⁶⁻ and [B₃C₃]⁷⁻, nearly linear [BC₂]⁵⁻ and bent [BC₂]⁷⁻ units and isolated carbon atoms. Structural and theoretical analysis suggests the ionic formulation for RE₂₅B₁₄C₂₆: (RE³⁺)₂₅[B₂C₄]⁶⁻([B₃C₃]⁷⁻)₂([BC₂]⁵⁻)₄([BC₂]⁷⁻)₂(C⁴⁻)₄·5e⁻ and for Nd₂₅B₁₂C₂₈: (Nd³⁺)₂₅([B₂C₄]⁶⁻)₃([BC₂]⁵⁻)₄([BC₂]⁷⁻)₂(C⁴⁻)₄·7e⁻. Accordingly, extended Hückel tight-binding calculations indicate that the compounds are metallic in character.     

Syntheses, crystal structures and optical spectroscopy of Ln2(SO4)3·8H2O (Ln=Ho, Tm) and Pr2(SO4)3·4H2O

The lanthanide sulphate octahydrates Ln₂(SO₄)₃·8H₂O (Ln=Ho, Tm) and the respective tetrahydrate Pr₂(SO₄)₃·4H₂O were obtained by evaporation of aqueous reaction mixtures of trivalent rare earth oxides and sulphuric acid at 300 K. Ln₂(SO₄)₃·8H₂O (Ln=Ho, Tm) crystallise in space group C2/c (Z=4, a_Ho=13.4421(4) Å, b_Ho=6.6745(2) Å, c_Ho=18.1642(5) Å, β_Ho=102.006(1) Å³ and a_Tm=13.4118(14) Å, b_Tm=6.6402(6) Å, c_Tm=18.1040(16) Å, β_Tm=101.980(8) Å³), Pr₂(SO₄)₃·4H₂O adopts space group P2₁/n (a=13.051(3) Å, b=7.2047(14) Å, c=13.316(3) Å, β=92.55(3) Å³). The vibrational and optical spectra of Ho₂(SO₄)₃·8H₂O and Pr₂(SO₄)₃·4H₂O are also reported.     

High-pressure high-temperature synthesis and crystal structure of the isotypic rare earth (RE)-thioborate-sulfides RE9[BS3]2[BS4]3S3, (RE=Dy-Lu)

Application of high-pressure high-temperature conditions (3.5 GPa at 1673 K for 5 h) to mixtures of the elements (RE:B:S=1:3:6) yielded crystalline samples of the isotypic rare earth-thioborate-sulfides RE₉[BS₃]₂[BS₄]₃S₃, (RE=Dy-Lu), which crystallize in space group P6₃ (Z=2/3) and adopt the Ce₆Al_3.33S₁₄ structure type. The crystal structures were refined from X-ray powder diffraction data by applying the Rietveld method. Dy: a=9.4044(2) Å, c=5.8855(3) Å; Ho: a=9.3703(1) Å, c=5.8826(1) Å; Er: a=9.3279(12) Å, c=5.8793(8) Å; Tm: a=9.2869(3) Å, c=5.8781(3) Å; Yb: a=9.2514(5) Å, c=5.8805(6) Å; Lu: a=9.2162(3) Å, c=5.8911(3) Å. The crystal structure is characterized by the presence of two isolated complex ions [BS₃]^3- and [BS₄]^5- as well as [□(S^2-)₃] units.     

Synthesis and crystal structure of new uranyl tungstates M2(UO2)(W2O8) (M=Na, K), M2(UO2)2(WO5)O (M=K, Rb), and Na10(UO2)8(W5O20)O8

The solid-state reactions of UO₃ and WO₃ with M₂CO₃ (M=Na, K, Rb) at 650°C for 5 days result, accordingly the starting stoichiometry, in the formation of M₂(UO₂)(W₂O₈) (M=Na (1), K (2)), M₂(UO₂)₂(WO₅)O (M=K (3), Rb (4)), and Na₁₀(UO₂)₈(W₅O₂₀)O₈ (5). The crystal structures of compounds 2, 3, 4, and 5 have been determined by single-crystal X-ray diffraction using Mo(Kα) radiation and a charge-coupled device detector. The crystal structures were solved by direct methods and Fourier difference techniques, and refined by a least-squares method on the basis of F² for all unique reflections. For (1), unit-cell parameters were determined from powder X-ray diffraction data. Crystallographic data: 1, monoclinic, a=12.736(4) Å, b=7.531(3) Å, c=8.493(3) Å, β=93.96(2)°, ρ_cal=6.62(2) g/cm³, ρ_mes=6.64(1) g/cm³, Z=4; 2, orthorhombic, space group Pmcn, a=7.5884(16) Å, b=8.6157(18) Å, c=13.946(3) Å, ρ_cal=6.15(2) g/cm³, ρ_mes=6.22(1) g/cm³, Z=8, R1=0.029 for 80 parameters with 1069 independent reflections; 3, monoclinic, space group P2₁/n, a=8.083(4) Å, b=28.724(5) Å, c=9.012(4) Å, β=102.14(1)°, ρ_cal=5.83(2) g/cm³, ρ_mes=5.90(2) g/cm³, Z=8, R1=0.037 for 171 parameters with 1471 reflections; 4, monoclinic, space group P2₁/n, a=8.234(1) Å, b=28.740(3) Å, c=9.378(1) Å, β=104.59(1)°, ρ_cal=6.13(2) g/cm³,  g/cm³, Z=8, R1=0.037 for 171 parameters with 1452 reflections; 5, monoclinic, space group C2/c, a=24.359(5) Å, b=23.506(5) Å, c=6.8068(14) Å, β=94.85(3)°, ρ_cal=6.42(2) g/cm³,  g/cm³, Z=8, R1=0.036 for 306 parameters with 5190 independent reflections. The crystal structure of 2 contains linear one-dimensional chains formed from edge-sharing UO₇ pentagonal bipyramids connected by two octahedra wide (W₂O₈) ribbons formed from two edge-sharing WO₆ octahedra connected together by corners. This arrangement leads to [UW₂O₁₀]²⁻ corrugated layers parallel to (001). Owing to the unit-cell parameters, compound 1 probably contains similar sheets parallel to (100). Compounds 3 and 4 are isostructural and the structure consists of bi-dimensional networks built from the edge- and corner-sharing UO₇ pentagonal bipyramids. This arrangement creates square sites occupied by W atoms, a fifth oxygen atom completes the coordination of W atoms to form WO₅ distorted square pyramids. The interspaces between the resulting [U₂WO₁₀]²⁻ layers parallel to plane are occupied by K or Rb atoms. The crystal structure of compound 5 is particularly original. It is based upon layers formed from UO₇ pentagonal bipyramids and two edge-shared octahedra units, W₂O₁₀, by the sharing of edges and corners. Two successive layers stacked along the [100] direction are pillared by WO₄ tetrahedra resulting in sheets of double layers. The sheets are separated by Na⁺ ions. The other Na⁺ ions occupy the rectangular tunnels created within the sheets. In fact complex anions W₅O₂₀¹⁰⁻ are built by the sharing of the four corners of a WO₄ tetrahedron with two W₂O₁₀ dimmers, so, the formula of compound 5 can be written Na₁₀(UO₂)₈(W₅O₂₀)O₈.     

High-pressure synthesis and structural characterization of three new polyphosphides, α-SrP3, BaP8, and LaP5

Three novel metal polyphosphides, α-SrP₃, BaP₈, and LaP₅, were prepared in BN crucibles by the reaction of the respective stoichiometric mixtures under a high pressure of 3 GPa at 950-1000°C. Their crystal structures were determined from single-crystal X-ray data (α-SrP₃: space group C2/m, a=9.199(6) Å, b=7.288(3) Å, c=5.690(3) Å, β=113.45(4)°, Z=4, R₁/wR₂=0.0684/0.1180 for 471 observed reflections and 22 variables; BaP₈: space group P−1, a=6.762(2) Å, b=7.233(2) Å, c=8.567(2) Å, α=86.32(2)°, β=84.31(2)°, γ=70.40(2)°, Z=2, R₁/wR₂=0.0476/0.1255 for 2702 observed reflections and 82 variables; LaP₅: space group P2₁/m, a=4.885(1) Å, b=9.673(3) Å, c=5.577(2) Å, β=105.32(2)°, Z=2, R₁/wR₂=0.0391/0.1034 for 1272 observed reflections and 31 variables). α-SrP₃ is isostructural with SrAs₃ and the crystal structure consists of two-dimensional puckered polyanionic layers _∞²[P₃]²⁻ that stack along the c-axis yielding channels occupied by Sr²⁺ counterions. BaP₈ crystallizes in a new structure type which contains a three-dimensional infinite polyanionic framework _∞³[P₃]²⁻, with large channels hosting the barium cations. LaP₅ is a layered compound containing _∞²[P₅]³⁻ polyanionic layers separated by La³⁺ ions. All three compounds exhibit expected diamagnetic behaviors.     

Crystal structures of CsFe2S3 and RbFe2S3: synthetic analogs of rasvumite KFe2S3

The isostructural alkali thioferrate compounds CsFe₂S₃, RbFe₂S₃ and KFe₂S₃ have been synthesized by reacting Fe and S with their corresponding AFeS₂ (A=K, Rb, Cs) precursors. The crystal structures of these and binary compounds of intermediate composition were determined by Rietveld analysis of laboratory powder X-ray diffraction patterns. All of the synthesized compounds adopt the space group Cmcm (#63), Z=4 with: a=9.5193(8) Å, b=11.5826(10) Å, c=5.4820(4) Å for CsFe₂S₃; a=9.2202(7) Å, b=11.2429(9) Å, c=5.4450(3) Å for RbFe₂S₃; and a=9.0415(13) Å, b=11.0298(17) Å, c=5.4177(6) Å for KFe₂S₃. These mixed valence alkali thioferrates show regular changes in cell dimensions, AS₁₀ (A=K, Rb, Cs) polyhedron volumes, polyhedron distortion parameters, and calculated oxidation state of Fe with respect to increasing size of the alkali element cation. The calculated empirical oxidation state of iron varies from +2.618 (CsFe₂S₃), through +2.666 (RbFe₂S₃) to +2.77 (KFe₂S₃).     

Hydrothermal synthesis, thermal, structural, spectroscopic and magnetic studies of the Mn5−xCox(HPO4)2(PO4)2(H2O)4 (x=1.25, 2, 2.5 and 3) finite solid solution

The Mn_5−xCo_x(HPO₄)₂(PO₄)₂(H₂O)₄ (x=1.25, 2, 2.5, 3) finite solid solution has been synthesized by mild hydrothermal conditions under autogeneous pressure. The phases crystallize in the C2/c space group with Z=4, belonging to the monoclinic system. The unit-cell parameters obtained from single crystal X-ray diffraction are: a=17.525(1), b=9.0535(6), c=9.4517(7) Å, β=96.633(5) ° being R1=0.0436, wR2=0.0454 for Mn75Co25; a=17.444(2), b=9.0093(9), c=9.400(1) Å, β=96.76(1) ° being R1=0.0381, wR2=0.0490 for Mn60Co40; a=17.433(2), b=8.9989(9), c=9.405(1) Å, β=96.662(9) ° being R1=0.0438, wR2=0.0515 for Mn50Co50 and a=17.4257(9), b=8.9869(5), c=9.3935(5) Å, β=96.685(4) ° being R1=0.0296, wR2=0.0460 for Mn40Co60. The structure consists of a three dimensional network formed by octahedral pentameric entities (Mn,Co)₅O₁₆(H₂O)₆ sharing vertices with the (PO₄)³⁻ and (HPO₄)²⁻ tetrahedra. The limit of thermal stability of these compounds is, approximately, 165 °C, near to this mean temperature the phases loose their water content in two successive steps. IR spectra show the characteristic bands of the water molecules and the phosphate and hydrogen-phosphate oxoanions. The diffuse reflectance spectra are consistent with the presence of MO₆ octahedra environments in slightly distorted octahedral geometry, except for the M(3)O₆ octahedron which presents a remarkable distortion and so a higher Dq parameter. The mean value for the Dq and B-Racah parameter for the M(1),(2)O₆ octahedra is 685 and 850 cm⁻¹, respectively. These parameters for the most distorted M(3)O₆ polyhedron are 825 and 880 cm⁻¹, respectively. The four phases exhibit antiferromagnetic couplings as the major magnetic interactions. However, a small spin canting phenomenon is observed at low temperatures for the two phases with major content in the anisotropic-Co(II) cation.     

Formation and structural refinements of tunneled intergrowth phases in the Ga2O3-In2O3-SnO2-TiO2 system

Over 100 samples were prepared as (Ga,In)₄(Sn,Ti)_n−4O_2n−2, n=6, 7, and 9 by solid-state reaction at 1400 °C and characterized by X-ray diffraction. Nominally phase-pure beta-gallia-rutile intergrowths were observed in samples prepared with n=9 (0.17?x?0.35 and 0?y?0.4) as well as in a few samples prepared with n=6 and 7. Rietveld analysis of neutron time-of-flight powder diffraction data were conducted for three phase-pure samples. The n=6 phase Ga_3.24In_0.76Sn_1.6Ti_0.4O₁₀ is monoclinic, P2/m, with Z=2 and a=11.5934(3) Å, b=3.12529(9) Å, c=10.6549(3) Å, β=99.146(1)°. The n=7 phase Ga_3.24In_0.76Sn_2.4Ti_0.6O₁₂ is monoclinic, C2/m, with Z=2 and a=14.2644(1) Å, b=3.12751(2) Å, c=10.6251(8) Å, β=108.405(1)°. The n=9 phase Ga_3.16In_0.84Sn₄TiO₁₆ is monoclinic, C2/m, with Z=2 a=18.1754(2) Å, b=3.13388(3) Å, c=10.60671(9) Å, β=102.657(1)°. All of the structures are similar in that they possess distorted hexagonal tunnels parallel to the [010] vector.     

The study of Bi3B5O12: synthesis, crystal structure and thermal expansion of oxoborate Bi3B5O12

The paper presents a new data on the crystal structure, thermal expansion and IR spectra of Bi₃B₅O₁₂. The Bi₃B₅O₁₂ single crystals were grown from the melt of the same stoichiometry by Czochralski technique. The crystal structure of Bi₃B₅O₁₂ was refined in anisotropic approximation using single-crystal X-ray diffraction data. It is orthorhombic, Pnma, a=6.530(4), b=7.726(5), c=18.578(5) Å, V=937.2(5) Å³, Z=4, R=3.45%. Bi³⁺ atoms have irregular coordination polyhedra, Bi(1)O₆ (d(B-O)=2.09-2.75 Å) and Bi(2)O₇ (d(B-O)=2.108-2.804 Å). Taking into account the shortest bonds only, these polyhedra are considered here as trigonal Bi(1)O₃ (2.09-2.20 Å) and tetragonal Bi(2)O₄ (2.108-2.331 Å) irregular pyramids with Bi atoms in the tops of both pyramids. The BiO₄ polyhedra form zigzag chains along b-axis. These chains alternate with isolated anions [B₂^IVB₃^IIIO₁₁]⁷⁻ through the common oxygen atoms to form thick layers extended in ab plane. A perfect cleavage of the compound corresponds to these layers and an imperfect one is parallel to the Bi-O chains. The Bi₃B₅O₁₂ thermal expansion is sharply anisotropic (α₁₁≈α₂₂=12, α₃₃=3×10⁻⁶ °C⁻¹) likely due to a straightening of the flexible zigzag chains along b-axis and decreasing of their zigzag along c-axis. Thus the properties like cleavage and thermal expansion correlate to these chains.     

Synthesis and characterization of organic-inorganic hybrid compounds with a pillared layer structure: Ga2(4,4′-bpy)(XO4)2 (X=P, As)

Two organic-inorganic hybrid compounds, Ga₂(4,4′-bpy)(PO₄)₂, 1, and Ga₂(4,4′-bpy)(AsO₄)₂, 2, have been synthesized under hydrothermal conditions and structurally characterized by single-crystal X-ray diffraction. The two compounds are isostructural and crystallize in the triclinic space group (No. 2) with a=4.9723(9) Å, b=5.770(1) Å, c=11.812(2) Å, α=78.268(3)°, β=89.159(3)° γ=88.344(3)°, V=331.7(2) Å³, Z=1, and R1=0.0377 for 1, and a=5.1111(7) Å, b=5.9327(8) Å, c=11.788(2) Å, α=79.497(2)°, β=88.870(2)°, γ=88.784(2)°, V=351.3(2) Å³, and R1=0.0264 for 2. The structure consists of neutral sheets of GaXO₄ (X=P or As) which are pillared through 4,4′-bipyridine ligands. Each oxide layer, which is formed only by four-membered rings, is constructed from corner-sharing GaO₄N trigonal bipyramids and XO₄ tetrahedra. The title compounds are two of the few examples in which the gallium atoms are exclusively five-coordinate.